key: cord-1036107-lt4wu69t
authors: Marchenko, Roman D.; Sukhikh, Taisiya S.; Ryadun, Alexey A.; Potapov, Andrei S.
title: Synthesis, Crystal Structure, and Luminescence of Cadmium(II) and Silver(I) Coordination Polymers Based on 1,3-Bis(1,2,4-triazol-1-yl)adamantane
date: 2021-09-05
journal: Molecules
DOI: 10.3390/molecules26175400
sha: 782a05721887f7b724ed9242d22f4b63b89e3c6b
doc_id: 1036107
cord_uid: lt4wu69t

Coordination polymers with a new rigid ligand 1,3-bis(1,2,4-triazol-1-yl)adamantane (L) were prepared by its reaction with cadmium(II) or silver(I) nitrates. Crystal structure of the coordination polymers was determined using single-crystal X-ray diffraction analysis. Silver formed two-dimensional coordination polymer [Ag(L)NO(3)](n), in which metal ions are linked by 1,3-bis(1,2,4-triazol-1-yl)adamantane ligands, coordinated by nitrogen atoms at positions 2 and 4 of 1,2,4-triazole rings. Layers of the coordination polymer consist of rare 18- and 30-membered {Ag(2)L(2)} and {Ag(4)L(4)} metallocycles. Cadmium(II) nitrate formed two kinds of one-dimensional coordination polymers depending on the metal-to-ligand ratio used in the synthesis. Coordination polymer [Cd(L)(2)(NO(3))(2)](n) was obtained in case of a 1:2 M:L ratio, while for M:L = 2:1 product {[Cd(L)(NO(3))(2)(CH(3)OH)]·0.5CH(3)OH}(n) was isolated. All coordination polymers demonstrated ligand-centered emission near 450 nm upon excitation at 370 nm.

Since its discovery adamantane has gained a wide spectrum of applications-from polymer design to biological activity. As a rigid building unit, mono-, di-, tri-, and tetrasubstituted adamantanes are used to construct covalent organic frameworks, hydrogen bounded networks, and metal-organic frameworks [1, 2] . Similar to aromatic ligands, adamantane retains the rigidity, but it exhibits additional benefits: its tetrahedral structure offers access to unique node geometry, the non-polar backbone introduces hydrophobicity, and the conformational stability provides a pool of multiple ligand geometries in solution [1] . Adamantane derivatives are promising materials for porous recyclable catalytically active metal-containing polymers, in which they prevent metal leaching, polymer matrix loss, intercalation, and porosity deterioration [2] .

Natural and synthetic adamantanes possess a wide range of biological activity. Amantadine, memantine, rimantadine, tromantadine, vildagliptin, saxagliptin, and adapalen are used in worldwide clinical practice for treatment of viral infections, acne, neurodegenerative disorders, and type 2 diabetes [3] [4] [5] [6] . Amantadine and memantine demonstrated significant benefits in preventing and treating COVID-19 [7] .

1,2,4-Triazole is a versatile nitrogen-donor ligand capable of forming strong coordination bonds with various metal ions [8, 9] . Derivatives of 1,2,4-triazole are known as anticancer, antiproliferative, anti-inflammatory, anticonvulsant, analgesic, antioxidant agents, and possess activity against wide, but specific spectrum of living organisms [10] . 1,2,4-Triazole cycles and rigid adamantane structures can be combined in bis (1,2,4-triazolyl) 1,2,4-Triazole cycles and rigid adamantane structures can be combined in bis (1,2,4zolyl) adamantane ligands, which could be useful N,N'-linkers for constructing coord tion polymers. Coordination polymers and metal-organic frameworks in particular promising materials with a wide range of potential applications-gas storage and sep tion [11, 12] , enantioselective catalysis [13, 14] , supramolecular systems design [15] , p tant sensing [16, 17] , water purification [18] , fabrication of electrochemical devices [19 and biological activity [21] . Coordination polymers based on 1,3-bis(1,2,4-triazol-4-y amantane with Mo(IV), Cu(II), Zn(II), Cd(II), Ag(I), bimetallic Ag(I)/V(V), Cu(II)/Mo(IV) were successfully synthesized and characterized by Domasevitch rese group [22] [23] [24] [25] [26] [27] [28] [29] [30] [31] , but the coordination chemistry of its isomer, 1,3-bis(1,2,4-triazol-1-yl) mantane remained unexplored.

Following interest in the coordination chemistry of heterocyclic adamantane de tives [32] [33] [34] , we have prepared a new ligand 1,3-bis(1,2,4-triazol-1-yl)adamantane (L) explored its reactions with Cd(II) and Ag(I) ions. As a result, three new Ag(I) and C coordination polymers were synthesized and characterized.

Silver coordination polymer [Ag(L)NO3]n (1) was synthesized from silver nitra and L in methanol at room temperature (Scheme 1). Molar ratio Ag:L = 1:1 was used the same product formed with Ag:L = 1:2 or 2:1.

Coordination polymers [Cd(L)2(NO3)2]n (2) and {[Cd(L)(NO3)2(CH3OH)]·0.5CH3O (3) were obtained by the reaction of cadmium(II) nitrate and L in methanol solutio solvothermal conditions (80 °C). The molar ratio of reagents was Cd:L = 1:2 for 2 and for 3. With the ratio Cd:L = 1:1 the mixture of crystals of 2 and 3 was obtained. Scheme 1. Synthesis of silver(I) and cadmium(II) coordination polymers with 1,3-bis(1,2,4-triazol-1-yl)adamantane.

Coordination polymer 1 crystallizes in monoclinic crystal system, P21/c space gr The elementary unit consists of one Ag(I) ion, one L ligand, and one nitrate ion. Each ver(I) ion coordinates three L ligands-two of them via nitrogen atoms at positions 1,2,4-triazole rings and one ligand via nitrogen atoms at position 2 ( Figure 1 ). Bridgi ligands and Ag(I) ions forms 2D layers parallel to the (-102) crystallographic plane (Fi 2). The layers are composed from two types of metallocycles-18-membered {Ag2L2 cles and 30-membered {Ag4L4} cycles. Nitrate ions are disordered over two positions ure S1), in one of them (occupancy 0.53), a bridging coordination mode is observed Ag-O distances of 2.640(2) and 2.801(2) Å . For the second position (occupancy 0.47 coordination mode should be considered as monodentate with the shortest Ag-O dist of 2.852(3) Å. The observed coordination modes of the nitrate ions are consistent Kleywegt's geometrical criteria calculated from interatomic distances and angles (T S1) [35] . The bridging nitrate ions join the adjacent layers into a 3D structure ( Figure  S3 ). Scheme 1. Synthesis of silver(I) and cadmium(II) coordination polymers with 1,3-bis(1,2,4-triazol-1yl)adamantane.

Coordination polymers [Cd(L) 2 (NO 3 ) 2 ] n (2) and {[Cd(L)(NO 3 ) 2 (CH 3 OH)]·0.5CH 3 OH} n (3) were obtained by the reaction of cadmium(II) nitrate and L in methanol solution at solvothermal conditions (80 • C). The molar ratio of reagents was Cd:L = 1:2 for 2 and 2:1 for 3. With the ratio Cd:L = 1:1 the mixture of crystals of 2 and 3 was obtained.

Coordination polymer 1 crystallizes in monoclinic crystal system, P2 1 /c space group. The elementary unit consists of one Ag(I) ion, one L ligand, and one nitrate ion. Each silver(I) ion coordinates three L ligands-two of them via nitrogen atoms at positions 4 of 1,2,4-triazole rings and one ligand via nitrogen atoms at position 2 ( Figure 1 ). Bridging L ligands and Ag(I) ions forms 2D layers parallel to the (-102) crystallographic plane ( Figure 2 ). The layers are composed from two types of metallocycles-18-membered {Ag 2 L 2 } cycles and 30-membered {Ag 4 L 4 } cycles. Nitrate ions are disordered over two positions ( Figure S1 ), in one of them (occupancy 0.53), a bridging coordination mode is observed with Ag-O distances of 2.640(2) and 2.801(2) Å. For the second position (occupancy 0.47) the coordination mode should be considered as monodentate with the shortest Ag-O distance of 2.852(3) Å. The observed coordination modes of the nitrate ions are consistent with Kleywegt's geometrical criteria calculated from interatomic distances and angles (Table S1 ) [35] . The bridging nitrate ions join the adjacent layers into a 3D structure ( Figures S2 and S3 ). Compound 2 is a 1D coordination polymer, the asymmetric unit consists of one Cd(II) ion, two nitrate ions, and two L ligands ( Figure 3 ). Cd(II) ions are in a seven-coordinated environment, which can be best described as distorted pentagonal bipyramidal, according to calculated minimal distortion paths listed in Table S2 . Two equatorial coordination places are occupied by nitrogen atoms at position 4 of triazole rings and the remaining three by oxygen atoms of nitrate ions ( Figure S4 ). According to Kleywegt's criteria (Table  S1 ), one of the nitrate ions is coordinated in a monodentate fashion (Cd-O distance 2.388(2) Å ), while the other is bidentate with Cd-O distances 2.524(2) and 2.627(2) Å . Compound 2 is a 1D coordination polymer, the asymmetric unit consists of one Cd(II) ion, two nitrate ions, and two L ligands ( Figure 3 ). Cd(II) ions are in a seven-coordinated environment, which can be best described as distorted pentagonal bipyramidal, according to calculated minimal distortion paths listed in Table S2 . Two equatorial coordination places are occupied by nitrogen atoms at position 4 of triazole rings and the remaining three by oxygen atoms of nitrate ions ( Figure S4 ). According to Kleywegt's criteria (Table  S1 ), one of the nitrate ions is coordinated in a monodentate fashion (Cd-O distance 2.388(2) Å ), while the other is bidentate with Cd-O distances 2.524(2) and 2.627(2) Å . Compound 2 is a 1D coordination polymer, the asymmetric unit consists of one Cd(II) ion, two nitrate ions, and two L ligands ( Figure 3 ). Cd(II) ions are in a seven-coordinated environment, which can be best described as distorted pentagonal bipyramidal, according to calculated minimal distortion paths listed in Table S2 . Two equatorial coordination places are occupied by nitrogen atoms at position 4 of triazole rings and the remaining three by oxygen atoms of nitrate ions ( Figure S4 ). According to Kleywegt's criteria (Table S1) Compound 3 crystallizes in a monoclinic P21/c space group, the asymmetric tains two crystallographically independent Cd(II) cations, four nitrate ions, two molecules, and three CH3OH molecules (two of which are coordinated to Cd 2+ , Cd(II) ions are seven-coordinated and their coordination polyhedra resemble a pentagonal bipyramid ( Figure S7 , Table S2 ). The equatorial coordination places pied by four oxygen atoms of the nitrate ions, and one position 4 nitrogen atom triazole ring. The axial positions are occupied by a 1,2,4-triazole nitrogen atom o L molecule and an oxygen atom of a coordinated methanol molecule. Both of t ions coordinated to each of independent Cd(II) ions can be considered as biden the shortest and the longest N-O distances of 2.330(7) Å and 2.602(7) Å (Table S cations are linked by bridging L molecules into 1D chains {Cd(NO3)2(L)(CH3OH) along crystallographic axis b (Figure 6 ). The chains are involved in intermolecul close contacts between the nitrate ions and 1,2,4-triazole hydrogen atoms at p (2.699 Å ) or between the methanol molecules and the 1,2,4-triazole hydrogen ato Å , Figure 6 ). These contacts join the chains into supramolecular 2D layers oriente to ab plane ( Figure S8) . Compound 3 crystallizes in a monoclinic P21/c space group, the asymmetric unit contains two crystallographically independent Cd(II) cations, four nitrate ions, two ligand L molecules, and three CH3OH molecules (two of which are coordinated to Cd 2+ , Figure 5 ). Cd(II) ions are seven-coordinated and their coordination polyhedra resemble a distorted pentagonal bipyramid ( Figure S7 , Table S2 ). The equatorial coordination places are occupied by four oxygen atoms of the nitrate ions, and one position 4 nitrogen atom of 1,2,4triazole ring. The axial positions are occupied by a 1,2,4-triazole nitrogen atom of another L molecule and an oxygen atom of a coordinated methanol molecule. Both of the nitrate ions coordinated to each of independent Cd(II) ions can be considered as bidentate with the shortest and the longest N-O distances of 2.330(7) Å and 2.602(7) Å (Table S1 ). Cd(II) cations are linked by bridging L molecules into 1D chains {Cd(NO3)2(L)(CH3OH)} oriented along crystallographic axis b ( Figure 6 ). The chains are involved in intermolecular CH···O close contacts between the nitrate ions and 1,2,4-triazole hydrogen atoms at position 5 (2.699 Å ) or between the methanol molecules and the 1,2,4-triazole hydrogen atoms (2.694 Å , Figure 6 ). These contacts join the chains into supramolecular 2D layers oriented parallel to ab plane ( Figure S8 ). Compound 3 crystallizes in a monoclinic P2 1 /c space group, the asymmetric unit contains two crystallographically independent Cd(II) cations, four nitrate ions, two ligand L molecules, and three CH 3 OH molecules (two of which are coordinated to Cd 2+ , Figure 5 ). Cd(II) ions are seven-coordinated and their coordination polyhedra resemble a distorted pentagonal bipyramid ( Figure S7 , Table S2 ). The equatorial coordination places are occupied by four oxygen atoms of the nitrate ions, and one position 4 nitrogen atom of 1,2,4-triazole ring. The axial positions are occupied by a 1,2,4-triazole nitrogen atom of another L molecule and an oxygen atom of a coordinated methanol molecule. Both of the nitrate ions coordinated to each of independent Cd(II) ions can be considered as bidentate with the shortest and the longest N-O distances of 2.330(7) Å and 2.602(7) Å (Table S1 ). Cd(II) cations are linked by bridging L molecules into 1D chains {Cd(NO 3 ) 2 (L)(CH 3 OH)} oriented along crystallographic axis b (Figure 6 ). The chains are involved in intermolecular CH···O close contacts between the nitrate ions and 1,2,4-triazole hydrogen atoms at position 5 (2.699 Å) or between the methanol molecules and the 1,2,4-triazole hydrogen atoms (2.694 Å, Figure 6 ). These contacts join the chains into supramolecular 2D layers oriented parallel to ab plane ( Figure S8 ). 

The phase and chemical purity of compounds 1-3 were confirmed by powder X-ray diffraction (powder XRD, Figures S9-S11) and elemental (CHN) analyses.

Thermal stability of the complexes was evaluated by thermogravimetric analysis (TGA) coupled with differential scanning calorimetry (DSC). Coordination polymer 1 shows only a slight weight loss up to 285 °C , after which it undergoes a rapid decomposition in the range of 285-325 °C, followed by a graduate weight loss ( Figure S12 ). The residual mass at 700 °C (24%) corresponds well to silver content in compound 1 (24.5%), indicative of complete loss of nitrate ions and decomposition of the organic ligand.

Coordination polymer 2 is stable up to 290 °C, after which a decomposition process similar to the one observed for compound 1 takes place ( Figure S13 ). Thermal behavior of the coordination polymer 3 is different because of the presence of solvate CH3OH molecules. It demonstrates an early weight loss of about 4% at 35-75 °C, attributable to removal of uncoordinated methanol molecules (calculated weight loss 3%). The formed product is 

The phase and chemical purity of compounds 1-3 were confirmed by powder X-ray diffraction (powder XRD, Figures S9-S11) and elemental (CHN) analyses.

Thermal stability of the complexes was evaluated by thermogravimetric analysis (TGA) coupled with differential scanning calorimetry (DSC). Coordination polymer 1 shows only a slight weight loss up to 285 °C , after which it undergoes a rapid decomposition in the range of 285-325 °C, followed by a graduate weight loss ( Figure S12 ). The residual mass at 700 °C (24%) corresponds well to silver content in compound 1 (24.5%), indicative of complete loss of nitrate ions and decomposition of the organic ligand.

Coordination polymer 2 is stable up to 290 °C, after which a decomposition process similar to the one observed for compound 1 takes place ( Figure S13 ). Thermal behavior of the coordination polymer 3 is different because of the presence of solvate CH3OH molecules. It demonstrates an early weight loss of about 4% at 35-75 °C, attributable to removal of uncoordinated methanol molecules (calculated weight loss 3%). The formed product is 

The phase and chemical purity of compounds 1-3 were confirmed by powder X-ray diffraction (powder XRD, Figures S9-S11) and elemental (CHN) analyses.

Thermal stability of the complexes was evaluated by thermogravimetric analysis (TGA) coupled with differential scanning calorimetry (DSC). Coordination polymer 1 shows only a slight weight loss up to 285 • C, after which it undergoes a rapid decomposition in the range of 285-325 • C, followed by a graduate weight loss ( Figure S12 ). The residual mass at 700 • C (24%) corresponds well to silver content in compound 1 (24.5%), indicative of complete loss of nitrate ions and decomposition of the organic ligand.

Coordination polymer 2 is stable up to 290 • C, after which a decomposition process similar to the one observed for compound 1 takes place ( Figure S13 ). Thermal behavior of the coordination polymer 3 is different because of the presence of solvate CH 3 OH molecules. It demonstrates an early weight loss of about 4% at 35-75 • C, attributable to removal of uncoordinated methanol molecules (calculated weight loss 3%). The formed product is stable in the range of 75-305 • C, after which it decomposes in two steps-rapid at 305-345 • C (55% weight loss) and gradual up to 685 • C, both attributable to loss of coordinated methanol, and decomposition of the organic ligand and cadmium nitrate ( Figure S14 ). Compounds 1-3 were studied by FT-IR spectroscopy in the solid state ( Figures S15-S18) . Bands in the IR spectra of the coordination polymers 1-3 associated with 1,2,4-triazole ring vibrations in the range 1507-1517 cm −1 are shifted to higher frequencies compared to the spectrum of the free L ligand consistent with the participation of the heterocyclic rings in coordination.

Nitrate ion vibration bands in the spectrum of coordination polymer 1 were found near 1438 and 1337 cm −1 , the separation of 101 cm −1 between them is consistent with the monodentate coordination of the nitrate ions. FT-IR spectra of compounds 2 and 3 demonstrate different patterns in the region of NO 3 vibrations. Thus, bands of asymmetric and symmetric NO 3 stretching vibrations are found at 1436 and 1283 cm −1 for compound 2 and 1448 and 1276 cm −1 for compound 3 (Figures S16 and S17) . Higher separation between these bands (172 cm −1 versus 153 cm −1 ) is consistent with a more bidentate character of coordination of nitrate ions in compound 3.

The luminescent properties of the ligand L and the coordination polymers 1-3 were studied for polycrystalline samples in the solid state. The excitation and emission spectra of the free ligand contain a single band near 350 nm and 410 nm associated with π-π* transitions in 1,2,4-triazole rings [36] (Figure 7a) . The excitation and emission spectra of the coordination polymers 1-3 are very similar, consistent with the intraligand nature of the luminescence. In contrast to the spectrum of the free ligand L, two excitation bands were detected in the spectra of the coordination polymers 1-3 (Figure 7b,c) , the lower energy band demonstrates a bathochromic shift to 370 nm relatively to the free ligand, in addition, high-energy bands appear at 270 nm, associated with n-π* transitions in 1,2,4-triazole rings. The emission band also undergoes a bathochromic shift of 40 nm upon excitation at 370 nm. Excitation at 270 nm leads to the appearance of a higher-energy shoulder near 400 nm, probably associated with the π*-n emission pathway (Figure 7b ). Similar photophysical behavior was observed previously for cadmium complexes with structurally similar 1-(1,2,4-triazol-1-yl)adamantane [32] .

Molecules 2021, 26, x FOR PEER REVIEW 6 of 10 stable in the range of 75-305 °C, after which it decomposes in two steps-rapid at 305-345 °C (55% weight loss) and gradual up to 685 °C, both attributable to loss of coordinated methanol, and decomposition of the organic ligand and cadmium nitrate ( Figure S14 ). Compounds 1-3 were studied by FT-IR spectroscopy in the solid state (Figures S15-S18). Bands in the IR spectra of the coordination polymers 1-3 associated with 1,2,4-triazole ring vibrations in the range 1507-1517 cm −1 are shifted to higher frequencies compared to the spectrum of the free L ligand consistent with the participation of the heterocyclic rings in coordination.

Nitrate ion vibration bands in the spectrum of coordination polymer 1 were found near 1438 and 1337 cm −1 , the separation of 101 cm −1 between them is consistent with the monodentate coordination of the nitrate ions. FT-IR spectra of compounds 2 and 3 demonstrate different patterns in the region of NO3 -vibrations. Thus, bands of asymmetric and symmetric NO3 -stretching vibrations are found at 1436 and 1283 cm −1 for compound 2 and 1448 and 1276 cm −1 for compound 3 (Figures S16 and S17) . Higher separation between these bands (172 cm −1 versus 153 cm −1 ) is consistent with a more bidentate character of coordination of nitrate ions in compound 3.

The luminescent properties of the ligand L and the coordination polymers 1-3 were studied for polycrystalline samples in the solid state. The excitation and emission spectra of the free ligand contain a single band near 350 nm and 410 nm associated with π-π* transitions in 1,2,4-triazole rings [36] (Figure 7a ). The excitation and emission spectra of the coordination polymers 1-3 are very similar, consistent with the intraligand nature of the luminescence. In contrast to the spectrum of the free ligand L, two excitation bands were detected in the spectra of the coordination polymers 1-3 (Figure 7b,c) , the lower energy band demonstrates a bathochromic shift to 370 nm relatively to the free ligand, in addition, high-energy bands appear at 270 nm, associated with n-π* transitions in 1,2,4triazole rings. The emission band also undergoes a bathochromic shift of 40 nm upon excitation at 370 nm. Excitation at 270 nm leads to the appearance of a higher-energy shoulder near 400 nm, probably associated with the π*-n emission pathway (Figure 7b ). Similar photophysical behavior was observed previously for cadmium complexes with structurally similar 1-(1,2,4-triazol-1-yl)adamantane [32] . 

All reagents were of reagent grade and used as received without further purification. 1,3-Bis(1,2,4-triazol-1-yl)adamantane (L) was synthesized according to a previously reported procedure [37] . 

Thermogravimetric analysis (TGA) coupled to differential scanning calorimetry (DSC) was carried out with a NETZSCH 449F3 instrument (NETZSCH TAURUS Instruments GmbH, Weimar, Germany) at a heating rate of 10 • C/min in a stream of helium, scanning range-30-750 • C. IR spectra were recorded on Agilent Cary 630 FT-IR spectrometer (Agilent Technologies, Santa Clara, CA, USA) equipped with a diamond ATR (attenuated total reflectance) tool (Agilent Technologies, Santa Clara, CA, USA). Elemental analyses were carried out on Carlo Erba CHNS analyser (Carlo Erba, Barcelona, Spain). The photoluminescence spectra were recorded on Horiba Jobin Yvon Fluorolog 3 Photoluminescence (HORIBA Jobin Yvon SAS, Edison, NJ, UAS) Spectrometer, equipped with 450 W xenon lamp, excitation/emission monochromator, and FL-1073 PMT detector. The powder Xray diffraction data were obtained on a Shimadzu XRD 7000S powder diffractometer (Shimadzu Corporation, Kyoto, Japan) (Co-Kα radiation).

Continuous shape measures were calculated by the SHAPE 2.1 program [38] for seven-coordinated reference polyhedra [39] .

Single-crystal X-ray diffraction data were collected at 150 K (compound 2) or 298 K (compounds 1 and 3) on a Bruker-DUO APEX CCD diffractometer (Bruker Corporation, Billerica, MA, USA) (graphite monochromatized Mo Kα radiation, λ = 0.71073 Å, ϕ and ω scans of narrow frames) equipped with a 4K CCD area detector (Table 1) . Absorption corrections were applied using the SADABS program [40] . The crystal structures were solved by direct methods and refined by full-matrix least-squares techniques with the use of the SHELXTL package [41] and Olex2 GUI [42] . Atomic thermal displacement parameters for non-hydrogen atoms were refined anisotropically. The positions of H atoms were calculated corresponding to their geometrical conditions and refined using the riding model. 

In summary, coordination chemistry of a new ligand, 1,3-bis(1,2,4-triazol-1-yl) adamantane, was explored through the examples of silver(I) and cadmium(II) nitrates. Depending on the metal-to-ligand ratio, cadmium formed 1D coordination polymers with chains of different composition, while in the case of silver(I) ions, a 2D coordination polymer was obtained independently of the ratio of the reagents used. All three coordination polymers demonstrated ligand-centered emission.

Supplementary Materials: The following are available online, Figure S1 . Disorder of nitrate ions in the structure of the coordination polymer 1 (a) and the asymmetric unit of the coordination polymer 1 showing both positions of the nitrate ions (b), Figure S2 . Bridging nitrate ions in the structure of the coordination polymer 1. View along crystallographic axis b, Figure S3 . Packing of layers of the coordination polymer 1. View along crystallographic axis b, Figure S4 . Coordination polyhedron of Cd(II) ion in the coordination polymer 2, Figure S5 . Close CH···O contacts between the chains of the coordination polymer 2, Figure S6 . Packing of chains of the coordination polymer 1. View along crystallographic Compound 3 axis a, Figure S7 . Coordination polyhedra of two crystallographically independent Cd(II) ions in the coordination polymer 3, Figure S8 . Packing of chains of the coordination polymer 3 into supramolecular layers. View along crystallographic axis a, Figure S9 . Powder X-ray diffraction plots for the coordination polymer 1, Figure S10 . Powder X-ray diffraction plots for the coordination polymer 2, Figure S11 . Powder X-ray diffraction plots for the coordination polymer 3, Figure S12 . TG and DTA curves for the coordination polymer 1, Figure S13 . TG and DTA curves for the coordination polymer 2, Figure S14 . TG and DTA curves for the coordination polymer 3, Figure S15 . FT-IR spectrum of the coordination polymer 1, Figure S16 . FT-IR spectrum of the coordination polymer 2, Figure S17 . FT-IR spectrum of the coordination polymer 3, Figure S18 . FT-IR spectrum of the ligand L, Table S1 . Interatomic distances, angles, and geometrical criteria for nitrate coordination in compounds 1-3, Table S2 . Continuous shape measures criteria for seven-coordinated Cd(II) centers in compounds 2 and 3. 

Cyclic Aliphatic Hydrocarbons as Linkers in Metal-Organic Frameworks: New Frontiers for Ligand Design

Porous Materials Based on 3-Dimensional Td-Directing Functionalized Adamantane Scaffolds and Applied as Recyclable Catalysts

Pharmacological profile of natural and synthetic compounds with rigid adamantane-based scaffolds as potential agents for the treatment of neurodegenerative diseases

Adamantane-A Lead Structure for Drugs in Clinical Practice

Influenza and antiviral resistance: An overview

Adamantane in Drug Delivery Systems and Surface Recognition

Potential for the Repurposing of Adamantane Antivirals for COVID-19

Homocoupling Reactions of Azoles and Their Applications in Coordination Chemistry

Lanthanide azolecarboxylate compounds: Structure, luminescent properties and applications

Exploring recent developments on 1,2,4-triazole: Synthesis and biological applications

Micro-and mesoporous metal-organic coordination polymers for separation of hydrocarbons

Microporous Metal-Organic Framework Materials for Gas Separation

Metal-Organic Frameworks in Heterogeneous Catalysis: Recent Progress, New Trends, and Future Perspectives

Asymmetric catalysis using metal-organic frameworks

Functional supramolecular systems: Design and applications

Coordination Polymers Based on Highly Emissive Ligands: Synthesis and Functional Properties

Metal ion detection using luminescent-MOFs: Principles, strategies and roadmap

Metal-Organic Frameworks for the Removal of Emerging Organic Contaminants in Water

Synthesis Protocols, and Energy Applications of MOF-Derived Electrocatalysts

Recent progress in Co-based metal-organic framework derivatives for advanced batteries

New Coordination Polymers of Zinc(II), Copper(II) and Cadmium(II) with 1,3-Bis(1,2,4-triazol-4-yl)adamantane

Triazolyl-Based Copper-Molybdate Hybrids: From Composition Space Diagram to Magnetism and Catalytic Performance

Functionalized adamantane tectons used in the design of mixed-ligand copper(II) 1,2,4-triazolyl/carboxylate metal-organic frameworks

AgI/VV Heterobimetallic Frameworks Generated from Novel-Type {Ag2(VO2F2)2(triazole)4} Secondary Building Blocks: A New Aspect in the Design of SVOF Hybrids

1,2,4-Triazole functionalized adamantanes: A new library of polydentate tectons for designing structures of coordination polymers

Fluoride molecular scissors": A rational construction of new Mo(VI) oxofluorido/1,2,4-triazole MOFs

Multiple anion···π interactions with a soft selenium atom: Accommodation of NCSe− anions inside hydrophobic pockets of adamantane/1,2,4-triazole coordination framework

Metal oxide-organic frameworks (MOOFs), a new series of coordination hybrids constructed from molybdenum(VI) oxide and bitopic 1,2,4-triazole linkers

Polynuclear and polymeric metal complexes based upon 1,2,4-triazolyl functionalized adamantanes

A dihydroxidotetracopper(II) framework supported by 4,4'-(adamantane-1,3-diyl)bis-(1,2,4-triazole) and benzene-1,3,5-tricarboxylate bridges

Synthesis, crystal structures, and luminescence properties of coordination polymers and a discrete complex of cadmium(II) halides with 1-(1,2,4-triazol-1-yl)adamantane

Synthesis of azolyl-substituted adamantane derivatives and their coordination compounds

Facile Synthesis of 3-(Azol-1-yl)-1-adamantanecarboxylic Acids-New Bifunctional Angle-Shaped Building Blocks for Coordination Polymers

Unidentate versus symmetrically and unsymmetrically bidentate nitrate co-ordination in pyrazole-containing chelates. The crystal and molecular structures of (nitrato-O)[tris (3, 5-dimethylpyrazol-1-ylmethyl) amine] copper (II) nitrate,(nitrato-O, O')[tris (3, 5-dimethylpyrazol-1-ylmethyl) amine] nickel (II) nitrate, and (nitrato-O)(nitrato-O, O')[tris (3, 5-dimethylpyrazol-1-ylmethyl) amine] cadmium (II)

Cadmium coordination compounds with flexible ligand 1,3-bis(1,2,4-triazol-1-yl)propane: Synthesis, structure and luminescent properties

1,3-Bis(1,2,4-triazol-1-yl)adamantane

Continuous Symmetry Measures: A New Tool in Quantum Chemistry

Shape and Symmetry of Heptacoordinate Transition-Metal Complexes: Structural Trends

APEX2 (Version 2.0), SAINT (Version 8.18c), and SADABS (Version 2.11), Bruker Advanced X-Ray Solutions

IUCr Crystal structure refinement with SHELXL

OLEX2: A complete structure solution, refinement and analysis program

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.Sample Availability: Samples of the compounds L, 1-3 are available from the authors.