key: cord-1017949-oa8xzgat
authors: Oude Vrielink, Timo J. C.; Meijer, Johanna H.
title: Using surgical wrapping material for the fabrication of respirator masks
date: 2020-07-21
journal: PLoS One
DOI: 10.1371/journal.pone.0236239
sha: f86a8dcd5ac6d666718af1a1a19e6219c9b00481
doc_id: 1017949
cord_uid: oa8xzgat

Given the current shortage of respirator masks and the resulting lack of personal protective equipment for use by clinical staff, we examined bottom-up solutions that would allow hospitals to fabricate respirator masks that: (i) meet requirements in terms of filtering capacities, (ii) are easy to produce rapidly and locally, and (iii) can be constructed using materials commonly available in hospitals worldwide. We found that Halyard H300 material used for wrapping of surgical instruments and routinely available in hospitals, met these criteria. Specifically, three layers of material achieved a filter efficiency of 94%, 99%, and 100% for 0.3 μm, 0.5 μm, and 3.0 μm particles, respectively; importantly, these values are close to the efficiency provided by FFP2 and N95 masks. After re-sterilization up to 5 times, the filter’s efficiency remains sufficiently high for use as an FFP1 respirator mask. Finally, using only one layer of the material satisfies the criteria for use as a ‘surgical mask’. This material can therefore be used to help protect hospital staff and other healthcare professionals who require access to high quality masks but lack commercially available solutions.

The SARS-CoV-2 pandemic, which began in late 2019 and rapidly spread throughout the world in early 2020, has led to a severe shortage of basic personal protective equipment for people working in high-risk occupations, including hospitals and extended care homes. Because SARS-CoV-2 can be transmitted via respiratory droplets, and potentially including aerosols [1] [2] [3] , the demand for high-quality, well tested respirator masks has increased dramatically. In an attempt to help provide access to personal protective equipment against SARS-CoV-2, particularly in locations currently experiencing a shortage of masks [4] , we investigated whether sterilization wrapping material is suitability for use in the production of FFP2 or N95 masks. We chose to use this material because of its filter properties, and its current availability in most hospitals, and the near-global sales market. The wrapping material Halyard Quick check H300 (manufactured by Owens & Minor) is commonly used to wrap surgical instruments for sterilization with steam or ethylene oxide gas; after sterilization, the material provides a sterile barrier against pathogens. Thus, the filter properties of this a1111111111 a1111111111 a1111111111 a1111111111 a1111111111 wrapping material are similar to the materials used in respirator masks. Moreover, the surgical wrapping material is composed of polypropylene, a material commonly used in air filters. Although sterilization wrapping has previously been suggested as an alternative material for the local production of respirator masks [5] [6] [7] , it has not been tested.

A series of industrial standards are currently used to classify the filter efficiency of respirators. The European Norm (EN) 149 standard [8] classifies respirators using FFP (Filtering Facemask against Particles) values, while World Health Organisation (WHO) guidelines require that healthcare workers-particularly those working under aerosol-generating conditions-wear a mask that provides at least FFP2 protection or equivalent [9] , with FFP2 corresponding to a filter efficiency of at least 94%. Providing a filter efficiency of at least 95%, similar standards are used for N95 and NK95 masks, corresponding to regulation NIOSH 42 CFR 84 in the US and norm GB2626-2006 in China, respectively. For respirator masks, the material's efficiency at filtering particles 0.3 μm in size is considered the most relevant, as particles of this size are difficult to filter out [10] .

In addition to the above-mentioned EN 149 norm, several commercially available respirators are also classified using the EN 14683 standard [11] ; the equivalent classification in the US is the ASTM F2100 standard. This standard is specific to masks used for medical purposes, primarily to protect patients from contamination, for example during surgery. In light of the SARS-CoV-2 pandemic, the WHO now recommends the use of surgical masks by patients who are potentially infected with the virus and hospital staff who work with these patients [12] . As an alternative to surgical masks, FFP1 respirators have also been suggested; however, although FFP1 respirator masks provide better particle protection than surgical masks, they are less splash-resistant than surgical masks [13] .

Here, we investigated whether Halyard wrapping material can be used to create masks in order to help protect healthcare workers under various conditions. We used standardized equipment to measure the transmission of various particle sizes, and we also measured splash resistance. Finally, we used standard sterilization procedures in order to investigate whether the material can be re-used while still providing sufficient protection. Moreover, we developed a prototype for a complete, functional respirator mask, with the aim of facilitating its rapid onsite fabrication. Importantly, we also identified additional materials that allow for the production of high quantities of respirator masks using basic workshop instruments and found that the masks can be produced in at the relatively rapid rate of under 10 minutes per mask.

The filter properties of the surgical isolation and wrapping material Halyard Quickcheck H300 (Owens & Minor, Inc.) was tested using a Solair 3100 air particle counter (Lighthouse Worldwide Solutions Benelux B.V.) as shown in Fig 1. The flow rate was set at 1.0 CFM (cubic feet per minute)cfm, which is well above (4x) normal breathing, and the filter efficiency of the material for 0.3 μm, 0.5 μm, and 3.0 μm particles was measured. The particles were collected from ambient air and background measurements were used to determine the filter efficiency of the material. The filter efficiency (FE) for a given particle size was determined using the particles measured after filtering (P f ) with a background measurement performed without the filter (P BG ), using the following equation:

In addition, the pressure differential was measured over the sample to provide a measure of breathing resistance. The surface of the material through which the air passes is a circle with 33 mm diameter; this surface area was used to normalize the measured pressure to Pa/cm 2 . For comparison, we also measured the differential pressure of commercially available FFP2 respirators and surgical masks.

Splash resistance was measured using a water column pressure test (Fig 1) . In brief, the water column is filled gradually, increasing the pressure at the sample, and the height of water in the column withheld by the material sample is defined as the sample's splash resistance.

We tested 1, 2, and 3 layers of Halyard Quick Check H300 material and performed each measurement four times. All tests were then repeated following each subsequent round of steam sterilization (15 min at 121 degrees Celsius under 2.0 atm of pressure). In addition, these tests were repeated with the material reversed and after the mask was worn for 20 min. Finally, three commercially available masks were tested as a control and for comparison with the custom-made masks: (1) Surgical Mask, Henan Gore Medical Instruments Co. Ltd (2) Disposable FFP2 mask, (3) 3820 FFP2 NR D, 3M.

This study did not involve any human subjects, and therefore was exempt from ethical approval. The data from the Particle Counter was downloaded and stored into a .xslx worksheet. The data of the differential pressure test and the water column test was manually inserted in separate .xlsx files. The data analyses was performed using Microsoft Excel, including the independent t-tests required for statistical analysis. Table 1 , and the complete results are provided in the S1 and S5 Data). Two layers resulted in 86.60±1.91%, 98.02±0.46%, and 99.97±0.01%, respectively, was satisfies the criteria for an FFP1 respirator mask. Importantly, the triple-layer material's efficiency at filtering 0.5 μm and 3.0 μm particles remained above the FFP2 standards even after five rounds of sterilization cycles; however, the filter efficiency for 0.3 μm particles decreased below the requirements for an FFP2 mask, but was still sufficient for use an as FFP1 mask. Table 1 shows the filtering efficiencies for the wrapping material. Based on the tests with the double layer material it is shown that the filter efficiency did not significantly change when reversing the material or after wearing the respirator mask for 20 min (p = 0.233 for 0.3μm particle size). After sterilization of the wrapping material the filter efficiency at the 0.3 μm decreased significantly after 1 round of sterilization for single, double and triple layers of materials (p = 0.019, p = 0.026 and p = 0.000, respectively). The filter efficiency for 3.0μm particles in triple layer material significantly changed after 4 sterilization cycles (p = 0.049).

As shown in Fig 3 (S2 Data) , the pressure differential across the wrapping material, which provides an approximation of the material's breathability, increases with each additional layer). No significant difference in pressure differential was observed after the sterilization (p 1 = 0.099, p 2 = 0.540, p 3 = 0.327, p 4 = 0.961, p 5 = 0.577 for the 1-5 sterilization cycles compared to unsterilized material, respectively). Fig 4 summarizes the results of the water column test, which provides an approximate measure of the materials' splash resistance (S3 Data). With two and three layers of wrapping material, the mean column pressure was 92 and 105 cm H 2 O, respectively; similar results were obtained when the material was reversed. A single layer of non-sterilized wrapping material provided similar or better results compared to a surgical mask in terms of filter efficiency (p = 0.001), and splash resistance (p = 0.002). On the other hand, the breathability of the surgical mask was better than the wrapping material (p = 0.000, one-tailed independent t-test).

As a comparison Halyard Quickcheck H500, which is used for wrapping heavier instrumentation, was tested (S4 Data). The material shows improved splash resistance and filter efficiencies, also for 0.3 μm, however, the material has considerable higher breathing resistance than the H300 material.

Here, we report that the Halyard Quickcheck H300 surgical wrapping material, which is commonly available in most hospitals for use in sterilizing surgical instruments, provides high filtration efficiency for all three particle sizes measured. Specifically, three layers of the material filtered approximately 94% of 0.3 μm particles, which is similar to the requirements established for N95 (95%) and FFP2 (94%) respirator masks [14, 15] . In addition, the three-layer provided a filter efficiency of 99.5% and 100% for 0.5 and 3.0 μm particles, respectively. Moreover, we found that the wrapping material provides high splash resistance; although this is not a requirement for respirator masks, this property helps protect against transmission due to coughing and sneezing. After several sterilization rounds, the masks were suitable for use as FFP1 respirators.

In addition, we found that a single layer of wrapping material is suitable for use as a highquality alternative for splash resistant surgical mask. Of note, our testing method differed from the method recommended by EN 14683; specifically, we did not test bacterial pathogens. The filter efficiency of surgical masks is determined specifically based on the ability to filter the Staphylococcus aureus bacterium, which has a diameter of 0.5-1.5 μm [13, 16] . Although we measured particles, rather than bacteria, we found that even a single layer of H300 provides higher filter efficiencies than is required for surgical masks and moreover a better splash resistance. A limitation of this study is that the SARS-CoV-2 pathogen is not used for the determination of the filter efficiencies. Rather, the method used in this study is focused on particles in the air, making our approach similar to the once used for commercially available and qualified respirators. These respirators have also not been subjected to SARS-CoV-2 pathogens. This may be taken into account in the context of the current pandemic.

The precise particle size that is most critical in the transmission of SARS-CoV-2 is currently under debate and subject to change as new information becomes available. One view is that especially larger-diameter aerosols play a role in the virus' transmission [17] . These aerosols can reach the ACE-2 receptor proteins abundantly expressed in the upper respiratory tract The sheet is folded to provide alignment with the face, and thereby ensure the respirator mask has an adequate fit when worn. The elastics (Resistance Band, Matchu Sport BV) is laser-cut to a width of 13/32 inch (10mm), and a length of 7 7/8 inch (200mm) and attached at the inside of the respirator mask. A single stitch line at the bottom ensures that the surface of the respirator mask stays separated from the mouth and allows to adjust the size of the respirator mask for -and by-anybody. (B) For the nose clip a 0.5mm thick aluminum strips (Al 99.5%, 1050A) is used, cut to a length of 3 1/2 inch (90mm) and a width of 5/32 inch (4mm). A neoprene strip with adhesive is used to hold the noseclip in place, and adhered to the inner-top side of the respirator mask. The fit of the mask was tested using an FT-30 Fit Test from 3M.

https://doi.org/10.1371/journal.pone.0236239.g005 [18, 19] , and coughing and sneezing are believed to be one of the major routes of transmission [1] . In this respect, the high splash resistance of H300 material -being better than that of N95 or FFP masks-seems particularly important.

The breathability of the H300 material decreased with each layer added, which can be considered a drawback of this solution. With three layers of material, the breathing resistance -per surface area-is higher than for FFP2 respirators (�180 cm/Pa vs �100 cm/Pa). The breathability for N95 or FFP2 respirator masks is, according to the standard, not specified for the material but for the entire mask, making it dependent on the design and surface area. We therefore purposely designed a mask in which the entire surface size is utilized for breathing.

We constructed a complete respiratory mask in order to facilitate production locally in hospitals. We identified a basic set of conventional materials (aluminum, neoprene rubber, and elastic material) with suitable specifications (see Fig 5) , recognizing that many other designs will also work [5] [6] [7] . Most hospitals-even in rural areas-have a basic workshop. The only key requirement for our design is a machine to cut aluminum and elastic strips out of larger sheets. The model that we propose is relatively easy to make, and we intentionally designed the mask in such a way that the wearer can breathe through the entire surface of the mask, increasing breathability and thereby comfort.

In other studies, the suitability of alternative materials for use as respirator masks has been investigated. For instance, a regular tea cloth provides some protection, but remains a factor 50 below the FFP2 requirements [20] . A recent study analyzed the filtering efficiencies of various conventional fabrics to assess possible materials for the SARS-CoV-2 pandemic [21] . The results from this study contributed to understand the efficiencies for alternative materials for home-made masks and showed that widely available materials such as cotton and chiffon displayed filtering efficiencies above 95%, for larger, but not for smaller particles. Our study was specifically aimed to allow for solutions in hospitals and other critical environments and provide a solution in case of a limited supply of high quality protective respirator masks. grateful to Nuri Cano (tailor) for pointing us in the right direction, and without whom this work had not been undertaken.

Airborne transmission of SARS-CoV-2: The world should face the reality

Consideration of the Aerosol Transmission for COVID-19 and Public Health

Aerosol and surface stability of SARS-CoV-2 as compared with SARS-CoV-1

Centers for Disease Control and Prevention. Strategies for Optimizing the Supply of Facemasks

WVU engineers, designers partner tot test material for surgical masks

A simple method for making surgical masks from operating room sterilization wrap. https:// medium.com/@GundleMD/a-simple-method-for-making-surgical-masks-from-operating-roomsterilization-wrap-6aaaf5e6b041

Respiratory protective devices-Filtering half masks to protect against particles-Requirements, testing, marking

Infection prevention and control during health care when novel coronavirus (nCoV) infection is suspected Interim guidance

Centers for Disease Control and Prevention. N95 Respirators and Surgical Masks

Medical face masks-Requirements and test methods

Advice on the use of masks in the context of COVID-19: interim guidance

World Health Organization. Rational use of personal protective equipment for coronavirus disease (COVID-19) and considerations during severe shortages: interim guidance

Centers for Disease Control and Prevention. 42 CFR Part 84 Respiratory Protective Devices

Respiratory protective devices-Filtering half masks to protect against particles-Requirements, testing, marking

An introduction to Staphylococcus aureus, and techniques for identifying and quantifying S. aureus adhesins in relation to adhesion to biomaterials: review

Reducing transmission of SARS-COV-2

Structure of the SARS-CoV-2 spike receptor-binding domain bound to the ACE2 receptor

Structure, function, and antigenicity of the SARS-CoV-2 spike glycoprotein

Professional and home-made face masks reduce exposure to respiratory infections among the general population

Aerosol filtration efficiency of common fabrics used in respiratory cloth masks

The authors would like to thank the Development Department of the LUMC, Huybert van der Stadt (for photography), and André van der Zee (for assistance on measurements). We thank G.D. Block (UCLA), J.S. Takahashi (Southwestern University), and G.A. Fitzgerald (University of Pennsylvania) for providing general comments regarding the paper. We are particularly