key: cord-1000386-70eoiedf
authors: Rubino, Ilaria; Oh, Euna; Han, Sumin; Kaleem, Sana; Hornig, Alex; Lee, Su-Hwa; Kang, Hae-Ji; Lee, Dong-Hun; Chu, Ki-Back; Kumaran, Surjith; Armstrong, Sarah; Lalani, Romani; Choudhry, Shivanjali; Kim, Chun Il; Quan, Fu-Shi; Jeon, Byeonghwa; Choi, Hyo-Jick
title: Salt coatings functionalize inert membranes into high-performing filters against infectious respiratory diseases
date: 2020-08-17
journal: Sci Rep
DOI: 10.1038/s41598-020-70623-9
sha: ce0001b7025e972ed141f2cce2d3c730b87752c5
doc_id: 1000386
cord_uid: 70eoiedf

Respiratory protection is key in infection prevention of airborne diseases, as highlighted by the COVID-19 pandemic for instance. Conventional technologies have several drawbacks (i.e., cross-infection risk, filtration efficiency improvements limited by difficulty in breathing, and no safe reusability), which have yet to be addressed in a single device. Here, we report the development of a filter overcoming the major technical challenges of respiratory protective devices. Large-pore membranes, offering high breathability but low bacteria capture, were functionalized to have a uniform salt layer on the fibers. The salt-functionalized membranes achieved high filtration efficiency as opposed to the bare membrane, with differences of up to 48%, while maintaining high breathability (> 60% increase compared to commercial surgical masks even for the thickest salt filters tested). The salt-functionalized filters quickly killed Gram-positive and Gram-negative bacteria aerosols in vitro, with CFU reductions observed as early as within 5 min, and in vivo by causing structural damage due to salt recrystallization. The salt coatings retained the pathogen inactivation capability at harsh environmental conditions (37 °C and a relative humidity of 70%, 80% and 90%). Combination of these properties in one filter will lead to the production of an effective device, comprehensibly mitigating infection transmission globally.

www.nature.com/scientificreports/ additionally, the WHO has reported global resistance to third-generation cephalosporins and carbapenem in 30-60% and up to 50% of cases, respectively 10 . Methicillin-resistant S. aureus (MRSA), also transmissible through the air 11 , constitutes another major pathogen in nosocomial infections, causing 20% to above 80% of S. aureus nosocomial infections worldwide 10 . The most commonly used respiratory protective device in health care is the N95 respirator, which is designed to capture aerosols. Surgical masks, commonly used to block large droplets during surgeries, were historically utilized against bioaerosols. Surgical masks have seen a continued use for this purpose in the general public during more recent outbreaks, in spite of the improper application [12] [13] [14] [15] . This is due to their high availability, affordability and comfort. Although respirators and masks play a critical role in the protection against bioaerosols, they are limited by four major technical issues of the filters: (i) cross-infection, (ii) filtration efficiency, (iii) breathability, and (iv) recyclability 16 . When respirators/masks capture bioaerosols, they become contaminated, since pathogens survive on the surface of the filters. This presents a threat to the wearer and people they come in contact with. As the devices can easily become a source of infection, commercial respirators/masks are limited to a single use. Additionally, in the traditional technologies, it is well-known that increasing the filtration efficiency leads to filters that cause higher pressure drop across the masks, with consequent difficulty in breathing. Some efforts have been directed towards production of filters that can overcome the burden of decreased breathability 17, 18 . However, these methods cannot address the risks arising from the survival of pathogens captured on the filters.

We envisioned the development of a technology that could solve all major technical challenges simultaneously, which cannot be addressed by conventional respiratory protective devices. The mechanism we developed consists of functionalizing the polypropylene (PP) fibers of large-pore (~ 60 μm) membranes with salt. Large-pore membranes have high breathability compared to commercial respirators/masks, but no pathogen filtration activity. We hypothesized that the salt coating would: (i) increase the filtration efficiency of the breathable membranes, turning them into an active filtration unit, and (ii) inactivate bacteria. Our previous report showed that coating the filters of surgical masks with sodium chloride (NaCl) salt kills multiple strains of influenza virus; additionally, a significant increase in the filtration efficiency of viral aerosols on the NaCl-coated filters compared to the bare surgical mask filters was observed 19 . In this work, non-functional large-pore membranes were coated with three types of salt [NaCl, potassium sulfate (K 2 SO 4 ) and potassium chloride (KCl)]. We demonstrate that salt functionalization greatly increases the filtration efficiency of large-pore membranes, while at the same time exhibiting no significant increase in pressure drop. The proposed filtration mechanism is non-mechanical in nature, which is evidenced by the insensitivity of filtration efficiency with respect to increasing layer numbers and the high filtration efficiency of the top layer (the first layer interacting with aerosols) of salt-functionalized filters even with presence of large-pore fiber mesh. Additionally, the salt recrystallization upon exposure of the salt-functionalized filters to infectious aerosols caused the physical damage of the bacteria independent of strain (K. pneumoniae, MRSA, P. aeruginosa, S. pyogenes and E. coli), leading to their inactivation. As such, we report a diverse respiratory protection system that is manufactured without extensive engineering efforts, and achieves quick universal pathogen inactivation, high filtration efficiency, high breathability, and safe recyclability, all in one platform.

Production and characterization of salt-coated filters. Development of environment-resistant filters is key to their universal application. Thus, when designing the salt-functionalized filters, fine-tuning of the properties of the pathogen-inactivating mask to satisfy different temperature/humidity conditions during use and storage was considered. To this end, safe and inexpensive salt types with different critical relative humidity (RH) were selected. At a given temperature, if a salt is exposed to an RH above its critical RH, it will take up water from the atmosphere. NaCl, KCl and K 2 SO 4 have critical RH of 74.7%, 81.2% and 95.7% at 40 °C, respectively 20 , and were investigated in this study. The salt coatings were applied onto the PP microfibers of large-pore membranes, which were not designed to provide protection against bacteria aerosols. The membranes (bare membranes) were dried in different volumes of coating solution (V salt ; NaCl, K 2 SO 4 or KCl), to produce filters coated with different amounts of salts per unit area (W salt ). The linear relationship between W salt and V salt for each salt type at different thicknesses can be found in Supplementary Fig. S1a -c (Pearson test, P values on graphs).

By stacking different numbers of membrane layers during drying, the overall thickness was varied. This allows for control over the final design of the salt-functionalized filters based on application needs. The formation of NaCl, K 2 SO 4 or KCl salt coatings was analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) mapping. Homogenous coating formation on the surface of the fibers and throughout the cross section of multi-layer filters was observed ( Fig. 1a and Supplementary Fig. S1d ). These results show the successful fabrication of filters uniformly functionalized with NaCl, K 2 SO 4 or KCl salts at controlled thicknesses.

Filtration efficiency against bacteria aerosols. The bacteria filtration performance of the salt-coated filters was probed against K. pneumoniae aerosols at 0 and 15 Lpm air flow rates. Overall, at 0 Lpm air flow, salt-coated filters showed significantly higher filtration efficiency than bare membranes at all conditions of salt type (NaCl, K 2 SO 4 and KCl), thickness (1, 3 or 5 layers), and salt amount (3, 6 or 7 mg/cm 2 ) (two-way ANOVA, P values on graphs) (Fig. 1b,c) . In particular, the NaCl, K 2 SO 4 and KCl filters exhibited an increase in filtration efficiency from 50 to 79%, 98% and 81%, respectively, as compared to bare membranes (Fig. 1b) . Even when the K. pneumoniae aerosols were passed through the filters at 15 Lpm, NaCl and KCl salt filters still captured significantly more bacteria than bare membranes; 5-layered K 2 SO 4 filters showed a significant increase in filtration efficiency compared to bare membranes as well (two-way ANOVA, P values on graphs) (Fig. 1d ). Interestingly, with the sole exception of K 2 SO 4 filters tested at 15 Lpm air flow, the filtration efficiency of the salt-coated filters did not depend on the filter thickness (two-way ANOVA, P > 0.05) (Fig. 1b,d) . This led us to hypothesize that Scientific RepoRtS | (2020) 10:13875 | https://doi.org/10.1038/s41598-020-70623-9

www.nature.com/scientificreports/ www.nature.com/scientificreports/ the top layer (first layer to interact with the aerosols) is mainly responsible for the increased filtration efficiency observed in salt-coated filters. Considering the relatively large size of pores against aerosols, the collection of aerosols possibly occurs via the absorption mechanisms of coated dry-salt agents (mainly those applied on the top layer), as opposed to the conventional filtration mechanism where the collection efficiency is governed by the fine mesh size and the number of added layers.

Pressure drop across the salt-coated filters. As traditional technologies that enhance capture of pathogens/particles negatively affect the breathability of the filters, the pressure drop of the salt-coated filters at an air flow rate of 8 Lpm was measured next. Pressure drop levels evaluate the perceived resistance breathing through the filters. Notably, the pressure drop across NaCl, K 2 SO 4 and KCl filters did not significantly change as compared to bare membranes, irrespective of the amount of coated salt (one-way ANOVA, P > 0.05) (Fig. 1e ) and the thickness of the filters (two-way ANOVA, P > 0.05) (Fig. 1f ). Since the pore size of the fiber mesh remains sufficiently large after the salt coating treatment (Supplementary Fig. S1e and Supplementary Table S2) , the above results further suggest that the proposed filtration mechanism is non-mechanical in nature, ensuring maximum filtration efficiency with high breathability.

To represent the overall filter performance, the quality factors (QF) of the salt-coated filters were compared with those of the bare membranes at 15 Lpm. The QF values are reported in Supplementary Table S1 and represent the ratio between the filtration efficiency and the pressure drop of filters 1 . The QF of NaCl, K 2 SO 4 and KCl filters increased by 107%, 26% and 103%, respectively, compared with bare membranes at 1-layer thickness, 16%, 23% and 57% for 3 layers and 23%, 66% and 51% for 5 layers. The increase in QF of the salt-functionalized filters compared to bare membranes indicates an overall enhancement in performance. It is also important to note that, in theory, the QF is independent of the filter thickness. However, NaCl and KCl filters show differences in QF at different thicknesses. This is related to the fact that the top layer constitutes the main capture medium responsible for increased filtration efficiency of the salt-coated filters compared to bare membranes, as mentioned. Overall, these performance test results indicate that functionalizing large-pore membranes with salts leads to a substantial increase of the amount of captured bacteria, without increasing the resistance to air flow, yielding improved filter quality.

inactivation of K. pneumoniae on the salt-coated filters and protective efficacy in vivo. The pathogen inactivation on NaCl, K 2 SO 4 and KCl filters was investigated by exposing them to K. pneumoniae bacterial aerosols. Time-dependent inactivation of bacteria incubated on filters coated with all salt types was observed (General Linear Model, P < 0.001) (Fig. 2a) . In particular, the KCl-coated filters exhibited significant colony forming units (CFU) reduction compared to bare membranes even within 5 min from aerosol exposure (two-way ANOVA, P ≤ 0.0001). As shown in Fig. 2b and Supplementary Fig. S2a , in contrast to intact bacteria in the control and on bare membranes, bacteria recovered from the salt-coated filters were found to be severely damaged due to the salt growth during the evaporation process. This explains the destabilization of the bacteria measured by CFU. Furthermore, the effect of different amounts of NaCl coated on the filters on the stability of K. pneumoniae aerosols was investigated. NaCl-coated filters showed rapid time-dependent bacteria inactivation (General Linear Model, P < 0.001) (Fig. 2c) . Notably, NaCl × 3 1200 caused a 4 log CFU reduction within 30 min from aerosol exposure. The TEM analysis revealed the rapture, structural damage and morphological changes incurred by the bacteria due to the salt recrystallization ( Supplementary Fig. S2b ). Similarly, when K. pneumoniae aerosols were exposed to the K 2 SO 4 and KCl filters prepared to contain a lower amount of salt (K 2 SO 4 × 3 0 and KCl × 3 0 ), quick time-dependent CFU reduction was still measured (General Linear Model, P < 0.001) (Supplementary Fig. S3a,b) . The bacteria inactivation on K 2 SO 4 × 3 0 and KCl × 3 0 was also confirmed in the TEM analysis ( Supplementary Fig. S3c ). In general, it is worth noting that the actual infectious aerosols will have significantly lower levels of bacterial concentration than the exposure aerosols used in the tests; as such, it is expected that further pathogen inactivation will be observed in real-life scenarios. Overall, the bacteria stability results indicate that the NaCl, K 2 SO 4 and KCl coatings rapidly neutralize bacteria by physical damage induced during the salt recrystallization process.

The bacteria inactivation findings were confirmed in vivo. Mice were infected with K. pneumoniae recovered from NaCl × 3 600 , K 2 SO 4 × 3 600 and KCl × 3 600 at 5 and 30 min incubation. At 30-min incubation, the bare membrane group reached a body weight loss that was significantly higher than that of NaCl, K 2 SO 4 and KCl filter groups by 10% (Fig. 2d-f ) (two-way ANOVA, P ≤ 0.05). As shown in Fig. 2g , OD 600 measured from the lungs of salt filter group mice were significantly lower than those of the control groups (bare membranes) (one-way ANOVA, P values on graph). Furthermore, the OD 600 levels decreased with incubation time (General Linear Model, P < 0.001). After 2-4 days, all salt filter mice groups showed a significant rapid recovery in body weight Figure 2 . Pathogen inactivation on salt-coated filters due to salt recrystallization. (a) CFU change showing the effect of incubation time on K. pneumoniae exposed to bare membranes and NaCl, K 2 SO 4 , and KCl filters (n = 5-38, mean ± SD). (b) TEM images of K. pneumoniae incubated on Bare × 3, NaCl × 3 600 , K 2 SO 4 × 3 600 , and KCl × 3 600 for 5 and 30 min (top), and of K. pneumoniae suspension as control (bottom). (c) CFU change showing the effect of incubation time on K. pneumoniae exposed to NaCl filters coated with different amount of salt (n = 5-38, mean ± SD). (d-g) Mice body weight change after infection with bacteria incubated on bare membranes, and NaCl × 3 600 (d), K 2 SO 4 × 3 600 (e), and KCl × 3 600 (f) for 5 and 30 min (n = 3-8, mean ± SD), and OD 600 of lungs (n = 3-8, mean ± SD; §: below detection limit) (g). **P < 0.01; ****P < 0.0001, by one-way ANOVA. (h-k) Mice body weight change after infection with bacteria incubated on bare membranes, NaCl × 3 0 , and K 2 SO 4 × 3 0 for 5 min (h), 15 min (i), and 30 min (j) (n = 4-8, mean ± SD), and OD 600 of lungs (n = 3-4, mean ± SD; §: below detection limit) (k). www.nature.com/scientificreports/ www.nature.com/scientificreports/ as opposed to the bacteria aerosol control group (two-way ANOVA, P ≤ 0.05), unlike bare membrane groups (Fig. 2d-f) . Additionally, the in vivo response to K. pneumoniae was investigated after incubation on the NaCl × 3 0 and K 2 SO 4 × 3 0 for 5, 15 and 30 min. At day 2 post-infection, the salt filter groups exhibited a significantly lower body weight loss than the bacteria aerosol control group (two-way ANOVA, P ≤ 0.05), unlike the bare membrane group (Fig. 2h-j) . The lung OD 600 measurements further supported these results by showing significantly lower levels in NaCl × 3 0 and K 2 SO 4 × 3 0 mice groups than bare membrane groups (one-way ANOVA, P ≤ 0.0001) (Fig. 2k) . In general, a decrease in lung OD 600 was also observed with the increase in incubation time on the filters (General Linear Model, P < 0.001). Thus, these studies support the in vitro results, indicating that protection of the mice was obtained by the NaCl, K 2 SO 4 and KCl salt coatings due to inactivation of the aerosolized bacteria.

Strain-nonspecific bacteria inactivation on NaCl, K 2 SO 4 and KCl coated filters was tested by exposure to four further bacteria strains (MRSA, P. aeruginosa, S. pyogenes and E. coli). Similar to K. pneumoniae, the salt filters exhibited inactivation capabilities irrespective of pathogen strain (Fig. 3a-d) . In particular, in the case of E. coli, P. aeruginosa and S. pyogenes, the bacteria showed significant decrease in CFU on all salt filters compared to bare membranes, even within 5 min (General Linear Model, P < 0.001 for E. coli, P < 0.001 for P. aeruginosa, P < 0.05 for S. pyogenes) (Fig. 3a-c) . NaCl-coated filters showed effective time-dependent MRSA inactivation (General Linear Model, P < 0.001) (Fig. 3d) . Therefore, these data indicate that, due to exploitation of a physical mechanism to inactivate the pathogens (i.e., evaporation-induced salt recrystallization), the salt-coated filters offer a universal infection prevention unit.

Exposure of salt coatings to harsh environmental conditions. Next, the environmental stability of the salt-functionalized filters was investigated. The filters were stored at 37 °C and 70%, 80% and 90% RH for 5 days. The SEM analysis showed that all salt types remained coated on the surface of the filter fibers (Fig. 3e) . Additionally, the salt coatings showed morphological changes and increased roughness due to recrystallization at the conditions above the respective critical RH (i.e., at 80% and 90% RH for NaCl, and at 90% RH for KCl). The salt-functionalized filters retained their ability to inactivate K. pneumoniae (Fig. 3f) . Interestingly, the saltcoated filters showed a significant increase in inactivation properties after exposure to the humid environment, and no bacteria were detected from the filters after storage at 90% RH (t test, P values on graph). This phenomenon is due to the morphological change of the salt coatings after storage, leading to increased surface roughness which affects viability of bacteria 21 . Additionally, bare membranes showed the opposite trend, where the bacteria recovered from filters stored at higher RH levels yielded significantly higher CFU counts as compared to the ambient condition (t test, P values on graph). This is due to remaining humidity trapped in the membranes, protecting the bacteria. Altogether, these findings indicate that prolonged exposure of the salt-coated filters to harsh environmental conditions does not compromise the stability of the coating, while inducing further antimicrobial activity. Notably, two important conclusions come from these findings: (i) the salt-based coatings can be safely used at different environmental conditions of use and storage, and (ii) the salt-coated filters will remain highly effective against pathogens after exposure to the humidity levels generated while breathing, ensuring reusability of the filters.

In summary, we developed an antimicrobial respiratory protective system with high filtering performance and improved breathability levels compared to regular masks, based on the salt functionalization technology of largepore membranes. The filters coated with different salt types are able to capture more pathogens than the bare membranes, converting a non-functional system into an active respiratory protection unit. Since the infectious aerosols tested in this work have a small particle size (2.5-4 µm), high filtration efficiency can also be expected against bigger particles responsible for disease transmission through large droplets. Additionally, commercial mask filters are produced by melt-blowing; by converting the more inexpensive spunbond large-pore PP membranes into functional filters by salt coating and controlling the final mask design, the production cost of masks will be reduced. Simultaneously, the enhancement in filtration efficiency does not cause any decrease in the breathability of the large-pore membranes, which is not achievable by traditional technologies. Due to the natural salt recrystallization process physically neutralizing both Gram-positive and Gram-negative bacteria within a short time, the salt-coated filters offer broad-spectrum protection. This results in no risk of cross infection, safe reusability of the device without further processing, reduced amounts of biohazardous waste and no risk of shortage of respirators during outbreaks. Additionally, the salt coatings remained stable on the filters following prolonged exposure to high temperature and humidity. This offers complete protection at varying environmental conditions of use or storage as well as ensures the recyclability of the filters. Overall, the results indicate that our technology can be used to fabricate respiratory protective devices with high filtration and breathability performance, which achieve strain-nonspecific protective efficacy. Notably, the simple and cost-effective functionalization process with salt addresses all major technical challenges of respiratory protection devices in a single system and could be readily applied to other devices that are already in use, such as filters in buildings and hospitals. This comprehensive technology could lead to an enhanced and timely response to epidemics and pandemics, such as the case of COVID-19, and provides a safe and effective solution to prevent diseases globally.

Filters preparation. Large-pore membranes were obtained from three-ply surgical masks (Fisherbrand Facemasks; Fisher Scientific, Pittsburgh, PA, USA). The middle membrane (active filtration unit) and outer protective membrane were discarded; the innermost PP membrane (typically used against the wearer's face Scientific RepoRtS | (2020) 10:13875 | https://doi.org/10.1038/s41598-020-70623-9

www.nature.com/scientificreports/ for mechanical protection of the middle filter; ~ 25 g/m 2 ) was used to produce the salt filter samples. As the innermost mask membrane has higher porosity than the middle filter, it was selected for the study; by stacking different numbers of layers, the performance of the salt filter samples was controlled by varying the thickness. Circular samples (3-cm radius) of the mask innermost large-pore membrane were cut (bare membranes, labelled Bare × # where # is the number of stacked layers). The membranes were coated with different salt types to obtain the salt-functionalized filters: sodium chloride (NaCl; Sigma Aldrich, St. Louis, MO, USA), potassium sulfate (K 2 SO 4 ; Sigma Aldrich), and potassium chloride (KCl; Sigma Aldrich). To prepare the coating solutions, the salts were dissolved in filtered (0.22 µm pore size; Corning, Tewksbury, MA, USA) DI water under stirring at 400 rpm and 90 °C for NaCl, and 400 rpm and room temperature (RT) for K 2 SO 4 and KCl (final salt concentrations: 29.03 w/v%, 9.72 w/v% and 26.31 w/v% for NaCl, K 2 SO 4 and KCl, respectively). Surfactant (Tween 20, Fisher Scientific) was added at 1 v/v%. The salt filters were prepared by completely pre-wetting the membrane samples with ~ 350 μL of a given coating solution (pre-wet membranes). The amount of coated salt was controlled by varying the volume of coating solution (0, 300, 600, or 1,200 µL) in which the pre-wet membranes were deposited in 60 × 15 mm petri dishes; more layers of pre-wet membrane samples were added on top based on the desired total number of layers (1, 3 or 5), and any air bubbles were carefully removed. The salt filter samples were dried overnight in an incubator (Thermolyne 42000; Thermolyne, Dubuque, IA, USA) at 45 °C. 24 . The detailed operation of the filtration efficiency test apparatus is in the Supplementary Methods. Briefly, the filter samples (4.9 cm 2 exposed area) were exposed to 60 µL of aerosolized (diameter = 2.5-4 μm) K. pneumoniae DI water suspension (OD 600 = 10), under an air flow rate of 0 or 15 Lpm. The bacteria were reconstituted from the filter samples as follows. The filter samples were incubated in PBS for 30 s-1 min. After vortexing, the filters were centrifuged (6,000 rpm, RT, 1 min) in a new tube to collect any remaining bacteria. The recovered bacteria were centrifuged (14,000 rpm, 15 min, 4 °C) to discard any salt/ surfactant dissolved from the filters, and then resuspended in 1.2 mL of fresh PBS, eliminating any interference with assays.

The total amount of bacteria contained in the exposure aerosols was determined by aerosolizing 60 µL of K. pneumoniae suspension into a 15-mL tube containing 1.5 mL of PBS for 30 s, followed by 1-min aerosolization of DI water to avoid drying of the bacteria condensed against the tube wall. After vortexing, the bacteria were centrifuged (14,000 rpm, 15 min, 4 °C) and resuspended in 1.2 mL of fresh PBS.

The filtration efficiency was calculated as the ratio of the amount of bacteria recovered from the filter sample to the total amount of bacteria contained in the exposure aerosols. The amount of bacteria was determined as the protein concentration measured with bicinchoninic acid assay (Micro BCA protein assay kit; Thermo Fischer Scientific, Waltham, IL, USA), with bovine serum albumin (BSA) standard.

Pressure drop tests were designed by adapting the MIL-M-36945C standard test 25 , recommended by the FDA 24 . The detailed operation of the pressure drop test apparatus is in the Supplementary Methods. Differential pressure measurements were conducted at an air flow rate of 8 Lpm (breathing condition 26 ) for 15 s, with (P 1 ) and without (P 0 ) loaded filter samples. The final pressure drop was calculated as ΔP = (P 1 -P 0 )/A, where A is the area of filter sample exposed to the air flow (6.6 cm 2 ). The quality factors (QF) of the bare membranes and salt-coated filters were calculated at 15 Lpm (QF = -ln(1 -F))/(P 1 -P 0 ), where F is the fraction of captured bacteria 1 ); notably, filtration efficiency and pressure drop tests were conducted separately.

Aerosols of multiple bacteria were exposed to the bare membranes (3 layers) and salt-functionalized filters (3 layers; NaCl, K 2 SO 4 , KCl). After washing, the bacteria were resuspended in DI water to an OD 600 of 12.5 (K. pneumoniae, P. aeruginosa and E. coli) or 100 (MRSA and S. pyogenes). Highly concentrated bacteria stocks were used to ensure that the bacteria recovered from the filters were detectable, due to the low filtration efficiency of the bare membranes and the inactivation of the bacteria occurring on the salt filters. For reference, the K. pneumoniae stock used is 5 × 10 8 CFU/mL, as opposed to the 3 × 10 0 -5 × 10 1 CFU/mL of bacteria detected in hospitals (assuming 50% RH indoors) 27 .

The nebulizer unit was placed on top of the filter samples (radius = 1.2 cm), which were loaded on a porous support, and 20 μL of bacteria suspension were aerosolized (30 s). After 3, 5, 15 or 30 min incubation on the filter samples, the bacteria were reconstituted as described above. After removing the supernatant containing salt/ surfactant, the bacteria were resuspended in 100 μL of PBS. The amount of bacteria contained in the exposure aerosols (0 min incubation on the filters) was determined by aerosolizing 40 µL of bacteria suspension into a 15-mL tube, similar to above; the bacteria were resuspended in 100 μL of PBS. CFU measurements were obtained by incubating 5 μL of 10 × dilutions onto MH II agar plates (K. pneumoniae, MRSA and E. coli), TSA plates (P. aeruginosa) or BHI agar plates (S. pyogenes) at 37 °C overnight. CFU were divided by the amount of bacteria www.nature.com/scientificreports/ recovered from the filters (determined as protein concentration). The measurements were expressed relative to the CFU at 0 min incubation on the filters (Relative CFU = CFU sample /CFU 0 min ).

Test of bacteria stability change on filters in vivo. 20 μL of K. pneumoniae DI water suspension (OD 600 = 10.5) were aerosolized on the filter samples and incubated for 5, 15 and 30 min. A lethal dose of bacteria reconstituted from the filters was used to infect 8 7-week old BALB/c mice (KOATECH, Pyeongtaek, Republic of Korea) per group by the intranasal route. As negative controls, two mice groups were infected with the bacteria before and after aerosolization, respectively. The body weight change was measured daily for 10 days. The mice were euthanized if the body weight reached below 75% of the starting weight. Kyung Hee University (KHU) Institutional Animal Care and Use Committee (IACUC), which operates under National Veterinary Research and Quarantine Service (NVRQS) and animal welfare law and regulations of the WOAH-OIE (World organization for animal health), provided approval for all animal protocols (KHUASP(SE)-18-085). The approved protocols and guidelines of KHU IACUC were followed for all animal experiments and husbandry related to this study. At day 3 post-infection, 4 mice per group were sacrificed to collect the lung tissues. The lung supernatants from the homogenizing process were used to measure OD 600 (NanoDrop One C; Thermo Fisher Scientific).

Performance of filters at different environmental conditions. Bare membranes (Bare × 3) and saltfunctionalized filters (NaCl × 3 600 , K 2 SO 4 × 3 600 , KCl × 3 600 ) were stored in an environmental chamber (Memmert HPP260; Memmert, Buchenbach, Germany) at 37 °C, and 70%, 80% and 90% RH. The bacteria stability change on filters in vitro was tested against K. pneumoniae aerosols at day 5 of storage, by measuring the CFU after 30 min incubation of the bacteria on the filters, as described above.

Electron microscopy analysis. SEM analysis (secondary electron mode at 20 kV, Hitachi S-3000N;

Hitachi, Toronto, Canada) was performed on the salt filters (NaCl, K 2 SO 4 , KCl) coated with a gold layer (thickness = 10 nm), and an EDX detector (Oxford Instruments, Concord, MA, USA) was used for the EDX analysis. The pore size of bare membranes and salt filters was determined from SEM images. TEM analysis (200 kV, JEOL JEM 2100; JEOL, Peabody, MA, USA) was performed on K. pneumoniae reconstituted after incubation on the bare membranes and salt-functionalized filters, as described above. The bacteria were deposited on copper grids (Electron Microscopy Sciences, Hatfield, PA, USA) and negatively stained with tungsten using a solution of 1.5 w/v% phosphotungstic acid hydrate (pH = 7.0) (Sigma Aldrich).

Pearson correlation coefficients basis of correlations was conducted between levels of salt weight and volume. The statistical analysis was performed by using one-way analysis of variance (ANOVA), two-way ANOVA, General Linear Model, t test, and chi-square analysis for multiple comparisons. SPSS ver. 21 (IBM, Armonk, NY, USA) and Minitab (Minitab, State College, PA) were used. The significance of multiple comparisons was considered by P value; P value of less than 0.05 was considered significant.

All data generated or analysed during this study are included in this published article (and its Supplementary Information files).

Received: 17 April 2020; Accepted: 30 July 2020

Aerosol Technology: Properties, Behavior, and Measurement of Airborne Particles

Inactivation of influenza A viruses in the environment and modes of transmission: a critical review

World Health Organization. Urgent Health Challenges for the Next Decade

Nosocomial infection and its molecular mechanisms of antibiotic resistance

Medical and microbiological problems arising from airborne infection in hospitals

The role of airborne bacteria in the contamination of fine particle nebulizers and the development of nosocomial pneumonia

The effect of increased bed numbers on MRSA transmission in acute medical wards

Chute-hydropulping waste disposal system: a reservoir of enteric bacilli and pseudomonas in a modern hospital

The airborne transmission of infection in hospital buildings: fact or fiction?

Significance of airborne transmission of methicillin-resistant Staphylococcus aureus in an otolaryngology-head and neck surgery unit

Effectiveness of precautions against droplets and contact in prevention of nosocomial transmission of severe acute respiratory syndrome (SARS)

Do N95 respirators provide 95% protection level against airborne viruses, and how adequate are surgical masks?

Surgical mask vs N95 respirator for preventing influenza among health care workers: a randomized trial

Respiratory and facial protection: a critical review of recent literature

(1234567890) Scientific RepoRtS | (2020) 10:13875 |

Respiratory protection against pandemic and epidemic diseases

Plasma modification of filter nonwovens used for the protection of respiratory tracts

A new material for airborne virus filtration

Universal and reusable virus deactivation system for respiratory protection

Hygroscopicity of fertilizer materials and mixtures

Multi-scale surface topography to minimize adherence and viability of nosocomial drug-resistant bacteria

ASTM F2101-14 Standard Test Method for Evaluating the Bacterial Filtration Efficiency (BFE) of Medical Face Mask Materials, Using a Biological Aerosol of Staphylococcus aureus

ASTM F2101-19, Standard Test Method for Evaluating the Bacterial Filtration Efficiency (BFE) of Medical Face Mask Materials, Using a Biological Aerosol of Staphylococcus aureus

Surgical Masks-Premarket Notification

Military Specification. MIL-M

Lung Function: Assessment and Application in Medicine

Microbial contamination on used surgical masks among hospital personnel and microbial air quality in their working wards: a hospital in Bangkok

The authors wish to thank Mr. Ankit Kumar at the University of Alberta for technical assistance on the SEM/ EDX, and Ms. Sally Fung, Ms. Iryna Roever and Ms. Miyoung Park at the University of Alberta for assistance in the sample preparation. This research was financially supported by the Natural Sciences and Engineering Research Council of Canada (NSERC) Discovery Grant, University of Alberta Faculty of Engineering, and Mitacs Globalink Research Award.

The authors declare the following financial interests/personal relationships which may be considered as potential competing interests: H.J.C is an inventor of the salt-coated pathogen deactivation technology and the patent application has been filed.

Supplementary information is available for this paper at https ://doi.org/10.1038/s4159 8-020-70623 -9.Correspondence and requests for materials should be addressed to H.-J.C.

Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creat iveco mmons .org/licen ses/by/4.0/.