key: cord-0976921-ascj25nw authors: Liu, Li; Xu, Wenhui; Ding, Yichun; Agarwal, Seema; Greiner, Andreas; Duan, Gaigai title: A review of smart electrospun fibers toward textiles date: 2020-09-17 journal: nan DOI: 10.1016/j.coco.2020.100506 sha: abd63a21af1866b4d4a5239aec925d8d485a524c doc_id: 976921 cord_uid: ascj25nw Electrospinning as a versatile technology has attracted a large amount of attention in the past few decades due to the facile way to produce micro- and nano-scale fibers featuring flexibility, large specific surface area and high porosity. Stimuli-responsive polymers are a class of smart materials that are capable of sensing surround environment and interacting with them. Therefore, the combination of electrospinning and smart materials could have a great deal of benefits over the development of smart fibers. In this review, it offers a comprehensive understanding of smart electrospun fibers towards textile applications. Firstly, the definition of smart fibers and the differences between interactive fibers and passive interactive fibers are briefly introduced. Then some interactive fibers made from temperature-, pH-, light-, electric field/electricity-, magnetic field-, multi-responsive polymers, as well as some polymers featuring piezoelectric and triboelectric effect which are suitable flexible electrics, are emphasized with their applications in the form of electrospun fibers. Afterwards, some passive and hybrid smart electrospun fibers are introduced. Finally, associated challenges and perspectives are summarized and discussed. behavior is mainly attributed to the coil state, at which the expanded polymer chains keep a hydrophilic coil conformation [69] [70] [71] . However, the collapsed hydrophobic globule state indicates a shrinkage. According to this temperature-dependent shifting property, temperature-responsive polymers can be characterized as lower critical solution temperature (LCST) and upper critical solution temperature UCST. As illustrated in the temperature-composition diagram, shown in Figure 3a , LCST and UCST polymers can display a miscibility gap upon a high temperature and/or a low temperature, respectively. And the LCST and the UCST, reflected in the temperature-composition diagram, are the minimum and maximum temperatures, respectively. In terms of LCST polymers, they are soluble or swellable upon cross-linked in aqueous solution below the LCST points, whereas they turn into insolubility or show shrinkage behavior above their LCST, and vice versa for UCST polymers [72] [73] [74] . Poly(N-isopropylacrylamide) (P(NIPAM)) whose chemical structure is presented in Figure 3b , as a typical example of LCST polymers, has been widely investigated in the past decades. It is well known that P(NIPAM) has a LCST near 32 o C at which the phase transition can be triggered in the physiological range, so that, it can be used with great benefits as a smart resource to develop fibers. In one study, an anti-cancer drug doxorubincin (DOX) was encapsulated into cross-linked P(NIPAM)/gelatin electrospun nanofibers. After heating up the nanofibers from RT to 37 o C, the nanofibers shrunk nearly half its original diameter. The in Vitro test implies an on-demand drug release profile upon the rising temperature above LCST, consequently lower the viability of human cervical cancer Hela cells [75] . In another study, Ma et al [76] . reported a core-shell fibrous structure designed by coaxial electrospinning. In this unique structure, the thermoresponsive polymer P(NIPAM) and biodegradable material polylactic acid (PLA) were applied as shell and core components, respectively. And the temperature-dependent state of P(NIPAM) shell has a great impact in the drug release of Combretastatin A4 (CA4) from PLA core. More importantly, P(NIPAM) copolymers, which can be synthesized easily just by radical polymerization due to the existing of double bond in NIPAM monomer, are able to provide P(NIPAM) some interesting properties and further introduce them to a broader spectrum of diverse applications. For instance, some introduced moieties designed to exhibit crosslinking function can provide P(NIPAM) with insolubility even in an environment with lower temperature than LCST. In one study, Chen et al [77] . selected N-hydroxymethyl-acrylamide (NMA) cross-linked P(NIPAM) electrospun nanofibers as the carrier doped with an 1,10-phenanthroline-based fluorescent sensor (F-phen) for detection of metal ions. The insolubility after crosslinked makes it possible for reuse and the effectively enhanced sensing J o u r n a l P r e -p r o o f performance is contributed to high specific surface are of nanofibers which is 1-2 orders of magnitude the deep-coated films, leading to high sensitivity. Furthermore, the temperature-dependent swell-shrunk P(NIPAM) fibers could be played as a switch by which the ability to approach the sensors could be adjusted. Besides, thermoresponsive electrospun nanofibers can be served as actuator as well [78, 79] . As shown in Figure 3c , Agarwal et al. demonstrated a superfast reversible actuating behavior of a bilayered fibrous structure composed of a 4-benzoylphenyl acrylate (ABP) crosslinked P(NIPAM) fibrous membrane and a thermoplastic fibrous membrane (TPU) by electrospinning upon cooling and heating cycle between 0 o C and 40 o C. This superfast responsive ability and versatile actuation is attributed to the aligned fibers at nanoscale which can offer sufficient surface area for energy exchange. In addition, recently, some scientists reported a facile way to fabricate surgical mesh with 4D response by coating a copolymer of N,N'-methylene bis(acrylamide) (MBA) crosslinked P(NIPAM) on a cold-plasma treated surface of PP fibers in a knitted fabric [80] . The resultant coated knitted fabric showed a 4D response upon temperature change, which may indicate one of the new generations of surgical meshes. However, compared with other thermoresponsive actuators from electrospun nanofibers [78] , it is quite insensitive to the temperature, whose response time was in the range of 2 to 15 mins. This is caused by the different specific surface area between traditional textile fibers and electrospun nanofibers. pH-responsive polymers are a series of stimuli-responsive polymers that can respond to external pH changes by conducting physical and chemical nature changes. In terms of the mechanism, pHresponsive polymers can be defined as polyelectrolytes that contain, in their polymer chains, either weak acidic groups or basic groups which favor protonation or deprotonation varied from surround pH values. The corresponding ability to accept protons under low pH condition and release them under high pH condition of these functional groups is associated with their pKa. At pH lower than its pKa, they prefer to accepting more protons; otherwise, they are willing to releasing more protons. However, the performance the pH-responsive polymers undergone could be distinct from their classifications. Generally, there are two types of pH-responsive polymers depending on the acidic groups or the basic groups they have. Polymer having acidic groups possesses negatively charged polymer chains after releasing protons at high pH, featuring dissolution or swelling behavior, such as poly (acrylic acid) [81] , poly(methacrylic acid) [82] . Those basic group-based pH-responsive polymers, such as poly((2dimethylamino)ethyl methacrylate) (PDMA) [83] , poly((2-diethylamino)ethyl methacrylate) (PEDA) [84] , form positively charged polymer chains upon capturing protons at low pH, leading to dissolution or swelling behavior. These dissolutions or swelling behaviors are attributed to the electrostatic repulsive force between the same charged polymer chains. Such a unique pH-dependent transition and the ability to capture and release counter ions make pH-responsive polymers very popular in scientific area in recent years [85] . Particularly, the introduction of electrospinning makes pH-responsive polymers a promising field in a broader spectrum of applications. The high specific surface area of pHresponsive polymers electrospun fibers facilitate the interaction between two oppositely charged groups resulting from the enhancement of diffusion of ions from surrounding aqueous environment. All these distinct properties make pH-responsive polymers incorporated with electrospinning wellsuited for a broad spectrum of fields. In efforts to pack poly(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA), two kinds of oppositely charged polyelectrolytes, into highly confined macromolecular, Zussman et al [86] . fabricated nanofibers from an adjusted stoichiometric ration of PAA-PAH low-pH solution by electrospinning. The results demonstrated that the polyelectrolyte complexes nanofibers exhibit a high pH-responsive ability featuring high dependency on the pH surroundings. The reversible swelling-shrinkage performance of these obtained nanofibers varied from pH 1.8 to pH 5.5, in accordance with the degree of ionization of the polyelectrolyte complexes, implying great potential in tailoring and manipulating fiber properties. The nature of interaction between charged polymer chains with counter ions could be reflected in the switchable wettability states, featuring hydrophilicity and hydrophobicity determined by the surrounding pH values. With the help of electrospinning, one of the applications regarding to this nature is oil/water separation. Stemming from the high porosity and specific surface area, poly-(dimethyl siloxane)-blockpoly(4-vinylpyridine) (PDMS-b-P4VP) electrospun mat was endowed with effective pH-responsive J o u r n a l P r e -p r o o f oil/water surface wettability as a result of the protonation and deprotonation of pyridyl groups in the P4VP segments [87] . Another important application of the pH-responsive polymers incorporated with electrospinning is to apply electrospun mat as a platform. Due to the ability of pH-responsive polymers to interact with counter ions, the electrospun pH-responsive polymeric nanofibers could be utilized as a carrier to capture, detection and detachment. Poly((2-(dimethyl amino) ethyl methacrylate) PDMAEMA as a positive charged polymer is capable of capturing negative charged groups as a result of protonation of MDAEMA segment, which could be modulated by regulating the pH value of surroundings. Owing to highly sensitive to micro-environment, pyrene-based materials are always considered to be a good candidate as a fluorescent probe. Chen et al [88] . synthesized a copolymer poly((2-(dimethyl amino) ethyl methacrylate)-co-(stearyl acrylate)-co-((1-pyrene) methyl 2-methyl-2-propenoate)) (poly (DMAEMA-co-SA-co-Py)) via free radical polymerization, followed by electrospinning into nanofibers. As illustrated in Figure 4 , the multifunctional capture, detection and detachment of DNA were integrated in this all-in-one nanofiber carrier. The low pH surrounding leads to the electrostatic repulsion between MDAEMA segments, in accordance with the ionization of MDAEMA segments, and causes the separation of pyrene excimer, featuring the decrease in excimer-to-monomer ratio. Upon the presence of DNA, the pronated fibers perform the interaction with the counter charged group from DNA, capturing the DNA. Correspondingly, as compared to the absence of DNA, the addition of DNA contributes to more pyrene segments in proximity through electrostatic interaction, thus resulting in the increase in excimer-to-monomer ratio. Furthermore, the detachment of DNA could be conducted by modulating the pH value to 7. As compared to other stimulus, light has been considered as a desirable stimulus in terms of easy-get, safe, clean, precise and flexible. Under the illumination, the light-responsive polymers have the capability to undergo physical or chemical property change. The mechanism behind this is that the light, as a kind of energy, after absorbed by the photo sensitive molecules or moieties in the polymer chains, causes a large structure change. Light responsive polymers can be roughly categorized into either photochemical or photothermal type. The photochemical effect is often triggered by the light-induced moieties photoreaction, for instance, photo induced isomerization and dimerization. Photoisomerization is a behavior at molecular level, at which a conformational change between isomers is generated by light irradiation. Usually, it consists of ring opening-closing transition and trans-cis isomerization. The compounds of the former one undergoes bond reaction or cleavage in response to light irradiation at particular wavelengths, like fulgide and diarylethene. The example of latter one is endowed with the switch ability between the two states that compounds rotating or inversing around the double bond, such as azobenzene and stilbene. Among the photo-responsive groups, azobenzenes are one of the most widely used type of functional molecules. Typically, at molecular level, the azobenzene group undergoes two states, trans vs cis isomers, as shown in Figure 5a . These two states are able to be interconverted by particular light wavelengths: a UV wavelength of 300-400 nm for trans-cis conversion, to a less stable state, higher energy cis isomer and visible light > 400 nm for the cis-trans conversion, back to a relaxed trans isomer [89] . In one demonstration, an azobenzene-functionalized PCL electrospun nano fibrous mat exhibit a light-dependent wettability-controlled surface, whose hydrophilic and hydrophobic behavior was tuned by the alternating UV irradiation and visible light irradiation, corresponding to cis isomer and trans isomer, respectively [90] , as shown in Figure 5b . Owing to this special transition of azobenzene group, it is attractive in the application of remotecontrol drug release system in combination with the host-guest interaction between α-cyclodextrins (CDs) and trans isomer of azobenzene. Therefore, upon UV irradiation, the host-guest interaction would be suppressed during the trans-cis transition, leading to a light triggered remote α-cyclodextrin based drug release profile [91] . Based on this mechanism, in another demonstration, the introduction of CDsbased drug into poly (vinyl benzyl chloride-block-glycidyl methacrylate) poly (PVBC-b-PGMA) electrospun nanofibers realize a fast light-triggered on-demand drug release. In response to UV irradiation, a well-regulated drug release profile was obtained, whereas the same phenomenon in dark condition was hindered [92] . Beside photochemical classes, generally, regarding light-responsive polymers, they are probably associated with photothermal effect which can convert light into heat. This effect can be enabled by the photothermal polymers, including polydopamine (PDA), polypyrrole (PPy) and polyaniline, or the photothermal components as the key switch embedded in polymer forming photothermal objectives or composites, such as Au nanocages (AuNCs), carbon nanotube (CNTs), indocyanine green (ICG), reduced graphene (rGO), Fe 3 O 4 particles and black phosphorus. And the incorporation of photothermal component into polymer fabricating hybrids or composites is considered as a frequently versatile strategy. AuNCs as a considerably greater photothermal effect material with low-cost advantage has been employed in many applications already [93] . Xia et al. Electrical responsive materials that respond to electrical field, other than other smart materials, sparked research interest in mainly developing actuators. Electroactive polymers (EAPs), which are highly flexible plastics, are a field of polymers that perform a change in size or shape during an electrical stimulation of electric field. In comparison with electronic EAPs actuator, driven by Coulomb force, those ionic EAPs-based ones offer an obvious advantage of lower voltage as low as 1-2 V. In a particular case of actuator design, ionic EAPs based actuators are driven by the diffusion or displacement of ions when stimulated by an electric field. The mechanism has been common suggested that, although still no definitively clear, upon a simulation of electric field, the negative ions fixed to the polymer chains are subjected to an attractive force from the anode, while the movement of cations J o u r n a l P r e -p r o o f toward the cathode taking place, therefore resulting in actuation. Polypyrrole (PPy) is such an ionic EAP, which is usually considered one of ideal candidates for ionic EAP actuators. In one study, as shown in nanoparticles chopped cellulose acetate electrospun fibrous mat and studied its bending behavior as a function of dopant concentration under external electrical input. As the increased concentration of PANI particles, the displacement of the composite actuator was shown much larger, since the main reason that the charged PANI particles interact with free ions inside the cellulose acetate [99] . To a certain extent, these reversible actuators paved the way to the design of artificial muscles. Not only the design in actuator but also the application in drug release can ionic EAPs be employed. Upon the stimulation of electric field, a volume change can be induced in an ion-doped conductive polymer of poly(3,4-ethylenedioxythiophene) (PEDOT). For instance, as illustrated in Figure 6d , owing to this electrical induced volume change property, a drug of dexamethasone controlled-release profile from PEDOT-coated PLGA electrospun fibers was achieved by applying external potential [100] . Much like other EAPs, in general, pH sensitive polymer such as poly (acrylic acid) (PAA), whose ionization feature varied from surrounding pH, is expected to be sensitive to electric field. As the deprotonation taking place, the protons or the negatively charged polymer chains of PAA prefer to moving towards the cathode or the anode, respectively, under the electric field stimulation. PAA, therefore, may particularly offer a unique advantage of electric field dependent volume change [101] . In a drug release system, it demonstrated that the swelling ratio and rate of the multiwalled carbon nanotubes (MWCN) incorporated PVA and PAA electrospun fibers are positively correlated to the applied voltage [102] . However, since the diffusion of ions inside electrolyte, these ionic EAPs need to maintain the wetness all time, which could limit the applications. Apart from the actuator, using a hybrid approach, functionality of smart fibers can also be indirectly obtained. To generate heat from wearable fabrics, in one study, a sandwich configuration of Ag an H2 atmosphere at 550 o C for 5 h, featuring magnetic properties [104] . In addition, magnetic sensitive polymers, that in particular are organometallic copolymers or composites, are of great scientific interests and have broad potential applications in numerous fields due to their shared features with metals and organic polymers. To make a magnetic sensitive electrospun fibrous mat, in comparison with the former approach, the later one of constructing composites by embedding magnetic ingredients into fibers is a simpler and more direct way. In one study, Guo et al. found that the polyacrylonitrile (PAN) electrospun fibrous mat were endowed with magnetic properties after the incorporation of Fe 3 O 4 particles, and the enhanced magnetization was attributed to weaker dipolar interaction arisen from the increased space distance between Fe 3 O 4 nanoparticles [105] . In fact, electrospun fibers can be provided with multifunctionality after the introduction of superparamagnetic particles due to the magneto-thermal effect that of oscillatory magnetic field induced heat from superparamagnetic particles. In a study of cancer treatment, as presented in Figure 7 , compared with the warm water bath method, cancer cells were killed in a more effective way by the oscillatory magnetic field induced heat from the loaded Fe 3 O 4 particles in the polystyrene (PS) electrospun fibers [106] . Magnetic hyperthermia, rather than photo hyperthermia, is considered to have a brighter future in the cancer treatment field, although both of them belong to remote triggering mechanisms. This is attributed to the fact that the access to the magnetothermal is more feasible in practical settings without the concern of photo path. Moreover, owing to their electrical and magnetic properties [107] [108] [109] . Fe 3 O 4 particles have been incorporated into electrospun nanofibers aiming to develop lightweight microwave absorption absorber. A Fe 3 O 4 particle embedded PVC composite electrospun nanofiber was demonstrated to be a good candidate for electromagnetic radiation protection material as a result of its low microwave transmission coefficient values, transmission loss below -16 dB in the microwave frequency range of X-band [110] . Using a similar approach, Yoon et al. constructed a core-shell nanofibrous mat with Fe 3 O 4 particles and polyamide (PA6) as core and shell, respectively, by coaxial electrospinning technology. The combination of Fe 3 O 4 particles and PA6 shows a property of electromagnetic shielding [111] . However, the electrospinning process is always interrupted by the particle agglomeration in the needle, thus causing the undesirable morphology of the mats. To address this issue, scientists have made numerous efforts to separate particles and then prepare well-dispersed nanoparticles suspension. In general, two J o u r n a l P r e -p r o o f main approaches have been pursued; the first involves the addition of surfactant in the particle suspension and the second relies on the surface modification of particles. Ultrasonic treatment is always employed to separate pure particles so that those individual particles could be capped possibly better by surfactant. As a matter of fact, both of the surfactant approach and the surface modification method are associated with "coating". The same as surfactant, the primary role of surface modification by polymer capping the particles is to prevent agglomeration as a result of the interparticle van der Waals attraction in a dispersion medium by offering either electrostatic repulsion or steric [112] . KGaA, Weinheim. To design smart fibers, the stimuli-responsive materials must fulfill the requirement in terms of multiresponsive ability. The materials are needed to be sensitive to not only one stimulus, but also, most time, multi-stimulus as well. Generally, the approaches to create multi-responsive ability involve constructing block polymer and loading functional ingredients into stimuli-responsive materials etc. Poly (Nisopropylacrylamide-co-acrylic acid) (P(NIPAM-co-AA)) is a typical dual responsive polymer, that comprising thermoresponsive and pH-responsive segments, are sensitive to external temperature and surrounding pH value change. Therefore, the properties of electrospun fibrous mat made of (P(NIPAMco-AA) can be adjusted by both temperature and pH. As one study we did before, in which (P(NIPAM-co-AA) was selected as the materials to fabricate a dual-responsive electrospun fibrous actuator whose actuation could be fast precisely controlled by changing temperature and pH value, which expand the application in compared with the thermoresponsive or pH-responsive actuator [81] , as illustrated in Figure 8 . This study only showed only dual responsive ability, but we believe it could be also stimulated by the electric field due to the protonization/deprotonization process of acrylic acid segment. Similarly, as described above, dual responsive materials could be created as well as by the loading of functional ingredient into smart materials [116, 117] . In another study, an ion-, pH-and temperatureresponsive random copolymer, poly(2-(2-hydroxyl-4-(5-(acryloxy) hexyloxy]phenyl)benzoxazole)-co-(N-isopropylacrylamide)-co-(stearyl acrylate)) (poly(HPBO-co-NIPAAm-co-SA)), was synthesized by radical polymerization. Besides the thermoresponsive ability coming from NIPAAM moiety, the ion and pH-responsive functionality are attributed to the HPBO segment which would turn into zinc complex or phenolate anion with regarding to aqueous Zn 2+ solution or basic condition, respectively. The electrospun fibrous mat from this multi-responsive polymer solution showed a thermo-, metal ion-and pH-responsive ability featuring hydrophilicity-hydrophobicity transition and fluorescent emission [118] . Numerous of multi-responsive fibrous mats fabricated by electrospinning have been created either through constructing multi-responsive copolymers, or combining several responsive polymers, or embedded functional ingredients into responsive polymers [119] [120] [121] [122] . J o u r n a l P r e -p r o o f It is very well known that carbon nanofibers by the carbonization of polyacrylonitrile by calcination, [123] and the way of electrospinning conductive agents, like carbon nanotube, graphite, can give insolate fibers conductivity. However, a key challenge to the widespread application in this field is the brittle property of the carbon fibers and unstable fabrication process caused by the aggregation of particles, respectively. [124] Instead, blending conductive nanofibers with general insolate electrospun fibers is one possibility to fabricate conductive fibrous mat. In one study, the reduced graphene oxide (rGO) as conductive path was localized uniformly on the surface of electrospun polyurethane (TPU) fibrous mat through ultrasonication. This constructed flexible composite structure possessing both of good stretchability and high sensitivity was used as a good candidate for sensor in human motion monitoring [125] . Apart from the deposition of conductive materials on the surface, conductive fibers could be assembled with other conventional base fibers as well. Greiner et al. fabricated a composite with the metal-like electrical conductivity of 750,000 S/m by homogeneously distributing silver nanowires (AgNWs) among electrospun short poly(ε-caprolactone) (PCL) fibers through the filtration of AgNWs and PCL fiber suspension, as shown in Figure 9 . This research provided a promising in portable applications [126] . From an open access article [127] . According to the piezoelectric effect and triboelectric effect, scientists have carried a tremendous amount of research work in energy harvesting/storage, self-powered and heater generator systems in combination of electrospun fibrous mats. Piezoelectric materials are a certain class of materials that has the capability to generate electric charges upon the mechanical stress. As one of the most important semi-crystalline materials, it is able to convert mechanical force into electricity due to the β crystalline phase who features the piezoelectric sensitivity. In 2011, Lin's group discovered that the electricity could be generated directly from electrospun PVDF fibrous mat even without the procedure of any extra poling treatment upon receiving a mechanical impact [128] . And in another study, Zhu et al. conducted electrospun PVDF fibrous mat, on the surface of which a secondary rough nanostructure is constructed, as active layer in insole. As the mechanical to electricity conversion during the human walking procedure, the maximum generated voltage could reach 210 v [129] . Triboelectric nanogenerator is capable of harvesting energy from external mechanical motions and Figure 11 , PAN & PVDF and silver wires were fabricated as core and shell components, respectively, by electrospinning followed by the formation of yarn. When conducting 2.5 Hz mechanical drive, this yarn is able to generate high output of 40.8 V, 0.705 μA cm -2 and 9.513 nC cm -2 and the resulting smart electrospun fibrous mats present the biomechanical sensing features. [130] J o u r n a l P r e -p r o o f Similarly, Ding's group has also succeeded in developing a triboelectric effect dependent wearable fabrics generator, by which the mechanical energy from human motions can be harvested and converted to electricity. This fabric generator was fabricated by the deposition of PTFE particles and PVDF nanofibers on traditional textiles, such as cotton, silk, PP, PET, through simultaneously sprayed and electrospun technology. Owing to the roughness surface of the fabric (PET), which is attributed to the modification of PTFE particles and PVDF nanofibers, the triboelectric effect is therefore enhanced. And then the electric output performance of the fabric generator is significantly boosted, by which serious of LEDs could be lighted up. [131] Conversely, passive fibrous mats possess less motivation when carrying out the interactive behavior with external environment. Compared with the communication process of interactive fibrous mat with external environment by changing their chemical/physical properties actively, the passive ones prefer to J o u r n a l P r e -p r o o f doing nothing but rely on the intrinsic characterizations without the change of their chemical/physical properties, such as waterproof and breathable fibrous mat and antibacterial fibrous mat. The air permeability, a critical parameter for clothing, is tightly related to the porosity which of electrospun mats can easily reach up to 90%. Higher porosity can provide more channels for air to go through the textile. The diameters of rain droplets are between around 18 and 28 μm or even larger [132] . And the pore sizes among those intersecting fibers can be controlled in the range from 0.1 to 0.8 μm by adjusting the process parameters during electrospinning and the overall porosity of the mat [55] . Therefore, the high porosity and the well-designed pores guarantee the possibility of waterproof and moisture permeable textiles by offering them the selective permeability for water droplet or vapor, as shown in Figure 12a . Consequently, it is to conclude that the pore size of an electrospun mat can be well fabricated for moisture-permeable but impervious to water droplets on rainy days. In a fabric system, the electrospun PU nano-fibrous mat showed better performance in the situation of water vaporand air-permeability than that PU and PTFT coated fabrics [133] . Furthermore, the performance of textiles in waterproof feature, that of hydrophobicity, can be enhanced by introducing hydrophobic rough surface, as illustrated in Figure 12b . And electrospinning has been demonstrated as such a kind of versatile tool for fabricating superhydrophobic mats, which is attributed to the wide selection of hydrophobic polymers with low-surface energy [134] [135] [136] and the facile way to construct rough surface with ability to trap amount of air [137] [138] [139] [140] [141] [142] . A simultaneous electrospraying of silica particles was employed during the electrospinning of PVDF and the resulting mat, that exhibited superhydrophilicity with the water contact angle of 163 o C and a high porosity of 85%, is considered as a good candidates of filter and waterproof and moisture permeable textiles [143] , as presented in Figure 12c The key to impart antimicrobial activity to the fibrous mat is creating an antimicrobial surface on the fibrous mat, which can be functionalized in a diversity of ways. Except constructing antibacterial polymers terminated with quaternary amine groups which are able to kill bacterial by the cation formation, [145] the other common way to fabricate antibacterial fibrous mat is the incorporation of antibacterial components into fibers. Silver ions have been demonstrated to kill bacterial due to the ability of reaction with thiol group that most of bacterial has in enzymes. [146] Similarly, copper as one of nature antimicrobial materials has also shown the same property as well, although the mechanism is not very clear. [147] When the silver or copper agent is engineered into nanofibers by electrospinning, the resultant fibrous mat, as a carrier, can offer thousands of loading spots due to the large specific surface area and high porosity. In one study, silver and copper nanoparticles originated from AgNO 3 and J o u r n a l P r e -p r o o f Cu(CH 3 COO) 2 ), respectively, are incorporated into cellulose electrospun nanofibers, and the resulting fibrous mats shows superior antibacterial activity. [148] When discussing the characterizations of interactive and passive smart fibers, it should be noticeable that there is not a sharp boundary between them. Sometimes there are always some types of smart fibers neither from stimuli responsive nor from piezoelectric and triboelectric effect polymers, that we cannot just simply term them as either interactive or passive ones. Shape Memory Polymers (SMP) feature a shape shift between the temporary shape and the permanent shape upon receiving stimulus from surrounding environment, such as heat. The fibrous conformation guaranteeing an effective heat transfer due to their porous structure can allow a fibrous SMP to perform a faster response. The large specific surface area of electrospun fibers endow them with versatile surface functionality, therefore, electrospun fibrous structure can be designed to act as a promising platform to construct structural colouration to mimic the natural colour of some insects, like butterfly wings, without using any dye by manipulating the nano-, micro-structures on the fibers according to the Bragg's Law. Electrospinning also make it possible to fabricate coaxial structure at nanoscale, consequently, different functional components or reaction agents can be incorporated into nanofibers acting as core part and separated by the shell materials. When these functional agents leak out from the core and touch with each other, some "smart" action probably starts showing some smart properties, like self-healing fibers. Be different from those smart fibers made by stimuli-responsive polymers or conductive ones, generally, these hybrid smart electrospun fibers have to rely on fiber assemblies including other introduced materials to show a "smart" response. Shape Memory Polymers (SMP) are an emerging class of materials that allow the shape to be a reversible transition between a deformed state and an original state upon exposure to an external stimulus, like temperature. In general, the SMP effect mechanism relies on two inherent incompatible phases in the polymer. These two phases, a reversible soft phase and a frozen hard phase acting as a competition, account for the shift between the temporary shape and the permanent shape, respectively. Upon an external stimulus, generally, like temperature, a temporary shape is created and subsequently frozen when a mechanical deformation is employed due to the compromised polymer chains movement of reversible soft phase, while the frozen hard phase still keeping its stiff state. And the transition from a temporary state back to a permanent state is attributed to the resulting strain during the deformation from J o u r n a l P r e -p r o o f the frozen hard phase [149] [150] [151] [152] [153] [154] [155] [156] . A typical polymer meeting these requirements is polyurethane (PU) which is composed of soft and hard segments respectively corresponding to the reversible soft phase and the frozen hard phase. As the temperature exceeding the glass or melting transition, the recovery actuation will be triggered. Rather than bulk film, the Shape Memory Effect (SME) employed in fibers at the micro-or nano-scale probably promotes the research of textiles in situations of immediate control due to the high porosity [157] . In an early study, PCL based shape memory PU fibrous mat was produced by electrospinning, which showed excellent shape recovery with 98% and 80% shape fixity [158] . In another study, as shown in Figure 13 Color gives human the sense of beauty in life. Dye, either natural or synthetic one, enables the coloration of textiles by the manipulation of light in the form of reflecting and absorbing etc. Even so, the pollution of dyeing procedure brought about by the chemical process cannot be ignored as well as the undegradable residual colorants. As an alternative to dye, structural coloration which is easy to be found in nature, such as butterfly wings, provides another route for the textile color generation [161, 162] . The color generated from structure, rather than from dye, is more environment friendly due to its unique nature of dye-free and fadeless process. Be analogous to the colorful butterfly wings, structural coloration arises from photonic band gap of ordered photonic-crystal structure [163, 164] . According to the Bragg's Law, the corresponding mechanism relies on the ability of the periodic micro-or nanostructure to manipulate the incident light, that of light refraction, scattering and diffraction as a result of the interaction between light waves and tailored configurations possessing the same order of size as the wavelength [165, 166] . Electrospinning, featuring the easy access to the desirable morphology and structure of nanofibers, has been subject to intensive study in structurally colored textiles by scientists. In one work, presented in Figure 14 , the colors of the samples were tuned by tailoring the nanostructure of electrospun colloidal nano fibers through employing various size of poly-(styrene-methyl methacrylate-acrylic acid) (P(St-MMA-AA)) particles from 220 nm, 246 nm to 280 nm, leading to green, red and purplish-red, respectively [167] . Another strategy is referred to as core-shell structure in which the thickness of shell accounts for the color. For example, the colors of blue, green and red were constructed by controlling the thickness of polystyrene/poly(N-isopropylacrylamide-co-acrylic-acid) core-shell particles which have the potential to enable the colorful textiles by coating them on textiles [168] . American Chemical Society. Self-healing is an effective and innovative function to address the issues that materials are most of time vulnerable to damage and the crack sites are hard to be localized. The self-healing materials can J o u r n a l P r e -p r o o f automatically detect and repair the cracks upon the damage. Considering this remarkable property, the long-term durability of materials during the application are supposed to be easily achieved. The mechanism relied on the reaction happening to the cracks suggests that two reagents not ought to meet each other until the cracks are created [169, 170] . For instance, the nutrients are not supposed to be delivered towards the wound site to encounter the injured cells and tissues initiating the healing process until a cut or a wound on human skin [171] . Some typical strategies have been developed to accomplish self-healing materials by constructing the healing agent fluid flow, as a key feature, to mimic that nature process. The melting polymer flow can be generated easily by employing PCL with low-melting point at 60 o C. In one study, a cut crack on a PCL electrospun fibrous mat was healed by the re-bonding process at the crack point as a result of the melting PCL fluid flow, serving as healing agent, upon the temperature at 80 o C [172] . Alternatively, healing agents which start reacting once they encounter each other, are separated by the shell structure, generally, in the form of core-shell configuration. When one of the agents is released from the crack site, caused by the deformation or the broken of shell, touching the other one outside the shell, then the reaction will be initiated automatically in situ, thus starting the self-healing. In one demonstration, a cut-induced polymerization was initiated in an electrospun nanofibrous mat reinforced composite by the meeting and the reaction of two reagents, that of curing agent (dimethyl methylhydrogen siloxane) and liquid monomer (dimethyl siloxane), respectively, from the core of PAN electrospun fibers and the epoxy matrix. As a consequence, the cut spot was repaired by this effective healing process after 2 days [173] . Similarly, healing agents could be fabricated into different core-shell structures as well. As illustrated in Figure 15 , Khorasani et al. encapsulated two healing agents, including two ingredients composed of a low viscosity epoxy resin and its amine-based curing agent, into nanofibers with the shell of styrene acrylonitrile (SAN) by electrospinning, respectively. These two types of core-shell nanofibers were loaded into resin region covered by two carbon fabric layers creating a self-healing composite whose crack was repaired and the mechanical properties were restored back to its original performance after a damage was employed [174] . In summary, smart electrospun fibers have a great potential towards textile applications. As the development of science and technology, fibrous structure like fibrous mats are taking more responsibilities to meet the development requirements of textiles in future which are not only regarded as the roles of protection, insulation and decoration. In terms of fibers, understanding the differences between interactive and passive fibers will dramatically aid in our ability to establish the concept of smart textiles, to identify them and to pave the way for the design of novel textiles. Nano fibrous mats, which have unique larger specific surface area, higher porosity and more flexibility, to a certain extent, can serve as a man-made skin against external harsh environment. Electrospinning provide a facile way to produce nanofibers with a broad selection of materials from inorganic to organic matters [175, 176] . And the combination of electrospinning technology and smart materials open a new window for the fabrication of smart fibers and their innovative applications in drug release system, actuator, selfpowered matters, wearable electronic devices, human motion monitors and sensors. Although many researches on these smart electrospun fiebrs have been proceeding, more efforts should be carried forward in practical usage. For example, in the battle against coronavirus starting at the end of 2019, a variety of masks are suggested being worn to prevent the spread of disease caused by the coronavirus, but most of them are the old-fashioned surgical masks and anti-smog face mask N95, which, relying on the passive functionalities in their short life service, are failing to adapt to the virus mutation. Therefore, the electrospinning technology combined with novel smart materials probably access the fibers including fiber, yarn, mat or textile with passive or interactive ability which suggests a bright future. Additionally, with the aid of development of computer science, smart electrospun fibers would be endowed with a new role in the applications of artificial intelligence (AI), man-machine interaction and soft electronic devices. However, the other confronting challenge for the smart electrospun fibers, which is the low production of electrospun fibers, is hindering their commercialization. There are already some companies, such as Jiangxi Xiancai Nanofibers Technology Co., Ltd. and MANN-HUMMEL, etc., which have dedicated to the industrial-scale mass production of electrospinning and showed actual perspectives, but the work toward high yields and industrialization all over the world should be kept on carrying out. And on the way of this work, anther new challenges should be addressed, that of the industrial-scale mass production of smart materials and the massive toxic solvents used in the electrospinning process. Other than the rather simplistic way to synthesize and employ materials in the laboratories, the economic cost plays a significant role in the commercialization process of materials. Moreover, most of time, it is inevitable to apply organic solvents for electrospinning which are toxic and harmful to our environment. Therefore, it is necessary to select low-toxic even non-toxic solvent to minimize the related negative effect. Anyway, smart electrospun fibers, serving as functional parts, are unnecessary to taking the place of every areas of those traditional textiles, but preferably integrated into them. electrospun nanofibers with high modulus and electric conductivity, Mater. Lett Understanding of passive smart electrospun fibers and interactive smart electrospun fibers The recent progress in flexible electronics from electrospun fibers The recent progress in stimuli-responsive polymers applied The loss of functional body hair in man: the influence of thermal environment, body form and bipedality Regenerated cellulose fibres early Indian cotton textiles from Berenike Alkylene ester of polybasic acids Linear condensation polymers Superior mechanical enhancement of epoxy composites reinforced by polyimide nanofibers via a vacuum-assisted hot-pressing Production of submicrometer diameter fibers by two-fluid electrospinning A Review of Recent Results on Superhydrophobic Materials Based on Micro-and Nanofibers Hierarchical composites of NiCo2S4 nanorods grown on carbon nanofibers as anodes for high-performance lithium ion batteries Nanofibers with diameter below one nanometer from electrospinning High strength and high breaking load of single electrospun polyimide microfiber from water soluble precursor Electrospun nanofibers for high-performance air filtration Ultralight, thermally insulating, compressible polyimide fiber assembled sponges Low Density, Thermally Stable, and Intrinsic Flame Retardant Poly(bis(benzimidazo)Benzophenanthroline-dione) Sponge High-density Fibrous Polyimide Sponges with Superior Mechanical and Thermal Properties Electrospun nanofibrous materials: A versatile platform for enzyme mimicking and their sensing applications Low-Density Open Cellular Sponges as Functional Materials Synthesis of stimuli-responsive polymers by living polymerization: poly (N-isopropylacrylamide) and poly (vinyl ether) s, Wax crystal control· nanocomposites· stimuliresponsive polymers Low-Density Self-Assembled Poly(N-Isopropyl Acrylamide) Sponges with Ultrahigh and Extremely Fast Water Uptake and Release Thioetherimide-Modified Cyanate Ester Resin with Better Molding Performance for Glass Fiber Reinforced Composites How to Modulate the Chemical Structure of Polyoxazolines by Appropriate Functionalization Recent development of pH-responsive polymers for cancer nanomedicine Polydopamine free radical scavengers Poly(amino acid)-Based Gel Fibers with pH Responsivity by Coaxial Reactive Electrospinning Synthesis and application of photo-responsive polymers Photo-responsive polymeric structures based on spiropyran Superlithiation of non-conductive polyimide toward high-performance lithium-ion batteries Ultrafine hollow TiO2 nanofibers from coreshell composite fibers and their photocatalytic properties Electrically-responsive deformation of polyelectrolyte complex (PEC) fibrous membrane Light and electrically responsive materials based on aligned carbon nanotubes Carbonization: A feasible route for reutilization of plastic wastes Flexible and refractory tantalum carbide Dielectric, mechanical and thermal properties of all-organic PI/PSF composite films by in situ polymerization, e-Polym Flexible hdC-G reinforced polyimide composites with high dielectric permittivity Highly foldable PANi@ CNTs/PU dielectric composites toward thin-film capacitor application Design and fabrication of microfluidic mixer from carbonyl iron-PDMS composite membrane Smart Polymers and Their Applications Robust superamphiphobic coatings based on raspberry-like hollow SnO2 composites Rewritable superhydrophobic coatings fabricated using water-soluble polyvinyl alcohol Base-Mediated Amination of Alcohols Using Amidines Multi-walled carbon nanotubes decrease neuronal NO synthase in 3D brain organoids MnO2 mediated sequential oxidation/olefination of alkyl-substituted heteroarenes with alcohols Ionic liquid-induced nanoporous structures of polymer films Unusual and Superfast Temperature-Triggered Actuators Sustainable development of smart textiles: A review of 'selffunctioning'abilities which makes textiles alive Highly effective antibacterial textiles containing green synthesized silver nanoparticles Superhydrophobicity from composite nano/microstructures: Carbon fabrics coated with silica nanoparticles Solar light induced and TiO2 assisted degradation of textile dye reactive blue 4 Effect of asymmetric wettability on directional transport of water through Janus fabrics prepared by an electrospinning technique Novel biocompatible electrospun gelatin fiber mats with antibiotic drug delivery properties Transport properties of porous membranes based on electrospun nanofibers High strength in combination with high toughness in robust and sustainable polymeric materials Ditungsten carbide nanoparticles embedded in electrospun carbon nanofiber membranes as flexible and high-performance supercapacitor electrodes Introduction to nanofiber materials Long-term drug delivery using implantable electrospun woven polymeric nanotextiles Electrospinning and electrospun nanofibers: Methods, materials, and applications Electrospinning: a fascinating method for the preparation of ultrathin fibers Electrospinning: a fascinating fiber fabrication technique Smart'polymers and what they could do in biotechnology and medicine Stimuli-responsive polymers and their applications Synthesis of temperature-sensitive poly (N-isopropylacrylamide) hydrogel with improved surface property An instant multi-responsive porous polymer actuator driven by solvent molecule sorption Porous materials for sound absorption Polymer gels, Fundamentals and Biomedical Applications Comparison of the coil-to-globule and the globule-to-coil transitions of a single poly (N-isopropylacrylamide) homopolymer chain in water Upper critical solution temperature of poly (Nacryloyl glycinamide) in water: a concealed property Globule-to-coil transition of a single homopolymer chain in solution Thermo-responsive polymers and their application as smart biomaterials Polymers with upper critical solution temperature in aqueous solution Studies on thermoresponsive polymers: Phase behaviour, drug delivery and biomedical applications Situ Cross-Linked PNIPAM/Gelatin Nanofibers for Thermo-Responsive Drug Release Thermo-sensitive drug controlled release PLA core/PNIPAM shell fibers fabricated using a combination of electrospinning and UV photopolymerization Thermo-responsive electrospun nanofibers doped with 1, 10-phenanthrolinebased fluorescent sensor for metal ion detection Giving Direction to Motion and Surface with Ultra-Fast Speed Using Oriented Hydrogel Fibers Tailoring the Morphology of Responsive Bioinspired Bicomponent Fibers Toward the New Generation of Surgical Meshes with 4D Response: Soft, Dynamic, and Adaptable Composite Polymeric Membranes with Directionally Embedded Fibers for Controlled Dual Actuation Poly (vinyl chloride) catheters modified with pH-responsive poly (methacrylic acid) with affinity for antimicrobial agents Reversible assembly of pH responsive branched copolymer-stabilised emulsion via electrostatic forces Polymers with tertiary amine groups for drug delivery and bioimaging pH-Responsive polymers Electrospinning polyelectrolyte complexes: pH-responsive fibers Electrospun fibrous mat with pH-switchable superwettability that can separate layered oil/water mixtures pH-Responsive and pyrene based electrospun nanofibers for DNA adsorption and detection Light-Driven Wettability Changes on a Photoresponsive Electrospun Mat Photocontrolled reversible supramolecular assemblies of an azobenzene-containing surfactant with α-cyclodextrin Smart nanofibers with a photoresponsive surface for controlled release Gold nanocages covered by smart polymers for controlled release with near-infrared light Incorporation of gold nanocages into electrospun nanofibers for efficient water evaporation through photothermal heating Electrospun PLA/MWCNTs composite nanofibers for combined chemo-and photothermal therapy Reduced Graphene-Oxide-Embedded Polymeric Nanofiber Mats: An Photothermally Triggered Antibiotic Release Platform Photothermal Welding, Melting, and Patterned Expansion of Nonwoven Mats of Polymer Nanofibers for Biomedical and Printing Applications Polypyrrole actuator based on electrospun microribbons Electro-active polymer actuator based on PVDF with bacterial cellulose nano-whiskers (BCNW) via electrospinning method Conducting-Polymer Nanotubes for Controlled Drug Release pH-and electro-response characteristics of bacterial cellulose nanofiber/sodium alginate hybrid hydrogels for dual controlled drug delivery Electro-responsive transdermal drug delivery behavior of PVA/PAA/MWCNT nanofibers An integrated smart heating control system based on sandwich-structural textiles Magnetically anisotropic cobalt and iron nanofibers via electrospinning Electrospun polyacrylonitrile nanocomposite fibers reinforced with Fe3O4 nanoparticles: Fabrication and property analysis Magnetic electrospun fibers for cancer therapy Synthesis and electromagnetic wave absorption properties of matrimony vine-like iron oxide/reduced graphene oxide prepared by a facile method Shapedependent magnetic and microwave absorption properties of iron oxide nanocrystals Fabrication of porous graphene-Fe3O4 hybrid composites with outstanding microwave absorption performance Electrospun PVC/Fe3O4 composite nanofibers for microwave absorption applications Core/shell PA6@ Fe3O4 nanofibers: Magnetic and shielding behavior Water-based magnetic fluids as extractants for synthetic organic compounds Structure of polymer-stabilized magnetic fluids: small-angle neutron scattering and mean-field lattice modeling Field-responsive superparamagnetic composite nanofibers by electrospinning Multiresponsive actuators based on modified electrospun films Artificial phototropism for omnidirectional tracking and harvesting of light Ultra metal ions and pH sensing characteristics of thermoresponsive luminescent electrospun nanofibers prepared from poly (HPBO-co-NIPAAm-co-SA) Chemical Dual-Responsive Wettability of Superhydrophobic PANI-PAN Coaxial Nanofibers Dual pHand ammonia-vapor-responsive electrospun nanofibrous membranes for oil-water separations Ultrafine hydrogel fibers with dual temperature-and pH-responsive swelling behaviors Multi-stimuli responsive supramolecular polymers and their electrospun nanofibers Controlling the composition, morphology, porosity and surface chemistry of lignin-based electrospun carbon materials Fabrication of conductive polymer nanofibers through SWNT supramolecular functionalization and aqueous solution processing Flexible electrically resistive-type strain sensors based on reduced graphene oxide-decorated electrospun polymer fibrous mats for human motion monitoring Polymer nanofibre composite nonwovens with metal-like electrical conductivity Multifunctional flexible membranes from sponge-like porous carbon nanofibers with high conductivity Electrical power generator from randomly oriented electrospun poly (vinylidene fluoride) nanofibre membranes Human walking-driven wearable all-fiber triboelectric nanogenerator containing electrospun polyvinylidene fluoride piezoelectric nanofibers Continuous and Scalable Manufacture of Hybridized Nano-Micro Triboelectric Yarns for Energy Harvesting and Signal Sensing Highly flexible, breathable, tailorable and washable power generation fabrics for wearable electronics The Effect of Smoke Particles on Clouds and Climate Forcing Functional Nanofibre: Enabling Material for the Next Generations Smart Textiles Morphology and hydroscopic properties of acrylic/thermoplastic polyurethane core-shell electrospun micro/nano fibrous mats with tunable porosity A novel multinozzle electrospinning process for preparing superhydrophobic PS films with controllable bead-onstring/microfiber morphology Coaxially Electrospun PVDF− Teflon AF and Teflon AF− PVDF Core− Sheath Nanofiber Mats with Superhydrophobic Properties Preparation of superhydrophobic polystyrene membranes by electrospinning Superhydrophobic films of electrospun fibers with multiple-scale surface morphology Superhydrophobicity of PHBV fibrous surface with bead-on-string structure Superhydrophobic titania membranes of different adhesive forces fabricated by electrospinning Superhydrophobicity of cellulose triacetate fibrous mats produced by electrospinning and plasma treatment Decorated electrospun fibers exhibiting superhydrophobicity Fabrication of three-dimensional superhydrophobic membranes with high porosity via simultaneous electrospraying and electrospinning Waterproof breathable layers-A review Quaternary ammonium chitosan/polyvinyl alcohol composites prepared by electrospinning with high antibacterial properties and filtration efficiency Interaction of silver nitrate with readily identifiable groups: relationship to the antibacterialaction of silver ions Copper, an ancient remedy returning to fight microbial, fungal and viral infections Synthesis and attachment of silver and copper nanoparticles on cellulose nanofibers and comparative antibacterial study Shape-memory polymers Cold, warm, and hot programming of shape memory polymers A review of shape memory polymers bearing reversible binding groups Fabrication of free-standing octagon-shaped carbon nanofibre assembly for electrical actuation of shape memory polymer nanocomposites Recent progress in shape memory polymer: New behavior, enabling materials, and mechanistic understanding Temperature sensing and actuating capabilities of polymeric shape memory composite containing thermochromic particles A phenomenological and quantitative model for shape/temperature memory effect in polypyrrole undergoing relaxation transition Phenomenological model and working mechanism of bio-inspired polymeric composites driven by water gradient Shape memory polymer nanofibers and their composites: electrospinning, structure, performance, and applications Electrospun polyurethane nanofibres having shape memory effect Electrospun biomimetic fibrous scaffold from shape memory polymer of PDLLA-co-TMC for bone tissue engineering Remotely actuated shape memory effect of electrospun composite nanofibers Light and color on the wing: structural colors in butterflies and moths Coloration strategies in peacock feathers Effect of macroscopic structure in iridescent color of the peacock feathers Structural color of Morpho butterflies Review on fabrication of structurally colored fibers by electrospinning Ten Eyck, Structural color production by constructive reflection from ordered collagen arrays in a bird (Philepitta castanea: Eurylaimidae) Structural Coloration of Colloidal Fiber by Photonic Band Gap and Resonant Mie Scattering Study on the high hydrophobicity and its possible mechanism of textile fabric with structural colors of three-dimensional poly(styrenemethacrylic acid) photonic crystals Superhydrophobic PDMS/wax coated polyester textiles with self-healing ability via inlaying method Intelligent nanofiber composites: Dynamic communication between materials and their environment Self-healing materials with microvascular networks Shape Memory Assisted Self-Healing Coating Hybrid self-healing matrix using coreshell nanofibers and capsuleless microdroplets Towards the development of selfhealing carbon/epoxy composites with improved potential provided by efficient encapsulation of healing agents in core-shell nanofibers Chapter 21 -Electrospun Nanofiber Electrodes: A Promising Platform for Electrospinning: Nanofabrication and Applications Conductive carbon nanofiber interpenetrated graphene architecture for ultra-stable sodium ion battery The authors declare that they have no conflict of interest.