key: cord-0974807-jeaz5sh3 authors: Mohammadamini, Fatemeh; Rahbar Shahrouzi, Javad; Samadi, Mitra title: A suspended polymeric microfluidic sensor for liquid flow rate measurement in microchannels date: 2022-02-16 journal: Sci Rep DOI: 10.1038/s41598-022-06656-z sha: 75271054d76b625980e64e6bfdc79c21a0b07f30 doc_id: 974807 cord_uid: jeaz5sh3 In this study, a microfluidic cantilever flow sensor was designed and manufactured to monitor liquid flow rate within the range of 100–1000 µl/min. System simulation was also performed to determine the influential optimal parameters and compare the results with experimental data. A flowmeter was constructed as a curved cantilever with dimensions of 6.9 × 0.5 × 0.6 mm(3) and a microchannel carved with a CO(2) laser inside the cantilever beam. The fabrication substance was Polydimethylsiloxane. Different flow rates were injected using a syringe pump to test the performance of the flowmeter. Vertical displacement of the cantilever was measured in each flowrate using a digital microscope. According to the results, the full-scale overall device accuracy was up to ± 1.39%, and the response time of the sensor was measured to be 6.3 s. The microchip sensitivity was 0.126 µm/(µl/min) in the range of measured flow rates. The sensor could also be utilized multiple times with an acceptable error value. The experimental data obtained by the constructed microchip had a linear trend (R(2) = 0.995) and were of good consistency with simulation results. Furthermore, according to the experimental and the simulation data, the initially curved cantilever structure had a higher bending and sensitivity level than a perfectly straight cantilever construction. www.nature.com/scientificreports/ cantilever is made of a thin membrane, a beam, or a plate with one side attached to a support and the other free to bend. A cantilever flow sensor is a type of pressure flowmeter in which flow is in contact with the surface of the cantilever, causing the cantilever to bend in the direction of acting force. In order to calculate the flow rate using a calibration curve, deflection must be measured using optical, piezoelectric, piezoresistive, or capacitive methods 13 . As an example of flow measurement with a cantilever structure, Naveen et al. 14 created a stainless-steel cantilever along the pipeline to measure the flow rate at high volumes. Image analysis was employed to determine the cantilever's deflection. Hamdollahi et al. 15 also studied a cantilever-based air flowmeter that calculates gas flow rate through image processing. Due to its simple structure and function, the cantilever is of the favorable capability to be used as a flow sensor in microfluidic systems. Microcantilevers are reported to be used in microfluidic systems, including analyte detection 16 , biosensing of DNA 17 , detection of heavy metal ions 18 , and viscometers 19 . In this regard, some initial works were carried out in the microfluidic systems flow metering field. Aiyar et al. 20 developed a micromachined airflow sensor in aerial vehicles to perceive an artificial skin by measuring air velocity. In their work, polyimide film (Kapton) was used as the base material of the sensor. Quist et al. 21 developed a piezoresistive cantilever sensor to measure flowrate and viscosity in microchannel and refined the beam structure to measure fluid speed in terms of cm/s. Lien et al. 22 also manufactured a fiber-optic cantilever flow sensor for liquid flow in a microchannel with high sensitivity and dynamic range of 0-1500 µl/min. Afterward, as technology progressed, more intricate forms of flowmeters were proposed to measure flow characteristics in microchannels. Ju et al. 23 , for instance, studied a flow-induced vibrating sensor for flow monitoring. The sensor was an etched fiber-optic cantilever with a diameter of 9 µm for flow sensing inside a microchannel with dimensions of 100 × 70 µm 2 , which could also be used to analyze properties of non-Newtonian liquids. Sanati Nezhad et al. 5 constructed a multilayer polydimethylsiloxane (PDMS) microcantilever incorporated within a microfluidic device and used an optic microscope to assess the cantilever bending. In another work, Neoth et al. 6 designed two microcantilever flow sensors made of SU-8 and SiN materials to indicate the effect of surface holes on cantilever deformation using a position-sensitive detector (PSD) system that monitors the ending level. Cheri et al. 1 manufactured a cantilever-based optofluidic flow sensor integrated with optical fibers for real-time flowrate measurement. Instead of a time-consuming multilayer lithography method, the fabrication process was carried by casting method using laser engraving of PMMA. Wang et al. 24 designed a free-standing piezoresistive-based cantilever to measure airflow velocity. In their study, the resistance of the platinum pizeoresistor affected the cantilever beam as the airflow changed. Platinum resistance was also determined using an external LCR meter. Verlinden et al. 25 proposed a two-channel microfluidic AFM cantilever to enable multiple reagents dosing inside another liquid environment as an application to highlight the importance of flow metric in (bio) chemical reactions. This device was capable of controlling flow rates ranging from femtoliters to pico-liters per second. Garrett et al. 26 also proposed a biocompatible microfluidic flow sensor to assess the cerebrospinal fluid shunt as a functional sensor in the medical industry. This PDMS cantilever could detect the flow rates within the range of 20-120 mL/h, which is the particular range for cerebral spinal fluid. Fabrication and characterization of a polymeric micro cantilever liquid flow sensor were carried out in this study. The design of this sensor was inspired by suspended polymeric microfluidic (SPMF) systems, which are commonly employed for particle detection in biological applications 27 or monitoring the density and viscosity of fluids 19 . In this field, the cantilever is not exposed to flow, but rather, the liquid passes through the embedded microchannel inside the cantilever, and the flow force acting on the interior walls causes it to bend. Before the fabrication process, a 3D computational fluid dynamic (CFD) simulation was performed to design an appropriate size for microchannel and cantilever construction. The simulation results on the system are required to determine the dynamic flowrate range within which the cantilever has a linear response 28 . In order to skip the conventional lithography steps, the microchannel was encarved by a CO 2 laser on a prepared PDMS polymeric layer to fabricate the sensor. In this research, the effect of the initially curved geometry of the cantilever on flowmeter performance was assessed and compared with the initially straight one. Afterward, a comparison was made between simulation results and experimental data, and conformity degree was assessed. Simulation and design. As mentioned earlier, the change in the direction of the fluid inside the microchannel applies force on the cantilever and makes it deform. The fundamental operation of the flowmeter is shown in Fig. 1a . The force on the cantilever wall acts in the vertical and horizontal directions. Fluid pressure is the source of the vertically applied force, while the horizontal force stems from shear stress 29 . However, cantilever deformation is governed by the Stoney equation indicated below 13 . where δ is the vertical cantilever deformation, E and ν respectively are Young's modulus and the Poisson's coefficient of the substrate used in the beam structure. σ indicates the normal stress applied to the material. F is the applied force to the cantilever, µ is fluid viscosity, u indicates the velocity change, A is the surface of the cantilever perpendicular to the fluid, and k m is the stiffness factor for a cantilever with the length of l and thickness of t. Scientific Reports | (2022) 12:2642 | https://doi.org/10.1038/s41598-022-06656-z www.nature.com/scientificreports/ The sensitivity of a cantilever sensor is determined by its physical dimensions and mechanical properties of the material it is made of 30 . The system's preliminary design was carried out by simulation to achieve appropriate dimensions for constructing a high-sensitivity sensor in the range of the required flow rate. High sensitivity here refers to high cantilever deflection over the required flowrate range. The parameters that affect the cantilever deflection must be optimized, such as material type, cantilever and microchannel dimensions, microchannel geometry, and placement coordinates inside the cantilever. Accordingly, a coupled solid mechanic and laminar flow phenomena were used to simulate the interaction between fluid and solid structure in COMSOL Multiphysics 5.3. Assumptions used to simplify the problem include steady-state, fully developed, laminar fluid flow, non-slip boundary condition, the square cross-section perpendicular to fluid, and smooth wall surface. Mass and momentum balances for fluid and solid elastic equations at steady-state conditions are expressed as follows: where ρ(kg/m 3 ) represents fluid density, u (m/s) is fluid velocity vector, p (Pa) is the pressure, I is the identity matrix, η kg/ms is the fluid viscosity, F is the acceleration force density, F ν is the applied force to solid per space unit, and σ (N/m 2 ) is the total stress applied to microchannel interior wall. The equations were solved using the boundary conditions listed as follows. • The fluid stable inlet flow rate was in the range of 100-1000 µl/min. • Relative outlet fluid pressure is equal to 0 due to entering the atmospheric environment. • No-slip boundary condition for microchannel interior walls • Definition of fixed constraint for microcantilever at the inlet base • Definition of the cantilever as a linear elastic material The sensor performance depends on the amount of total displacement taking place in the free end of the cantilever due to different flow rates. In this regard, the cantilever bending level was optimized in the desired range by software. After simulation and investigation of all factors affecting cantilever bending, the optimal value for each parameter was obtained, as shown in Table 1 . Furthermore, according to simulation results, the www.nature.com/scientificreports/ construction of a curved cantilever plays a determining role in increasing bending. For this purpose, the effect of the different initial shapes (curvature) of the cantilever on the bending values was compared, as shown in Fig. 1b . According to this diagram, the bending value of the curved cantilever is greater than that of the straight one for the same range of flowrate. Therefore, fabricating a cantilever with a curved construction is preferable in increasing the sensitivity of the sensor. It is worth mentioning that raising the curvature value of the cantilever has a positive effect on the deflection. Preparation of cantilever and microchannel. Figure 2 illustrates the schematic of the microcantilever fabrication process. In order to to provide a polymeric layer for cantilever sensor fabrication, a mixture of Polydimethylsiloxane (PDMS) was prepared with a ratio of 1:10 (cross-linker:base) and poured into a glass base to cast a smooth layer with applicator device. After the degasification process through a vacuum pump (GEC BS500011, England), the casted films were baked at 70 °C for 24 h. Then, the resulting polymeric film was peeled off from the glass. In order to fabricate a cantilever with an overall thickness of 600 µm, two films were prepared with thicknesses of 100 and 500 µm. Afterward, the shape designed for microchannel and cantilever in optimal dimensions was drawn with CorelDRAW v.X7 software and prepared for engraving on a polymer layer with Bonding process. After the engraving process, the prepared films were washed with isopropanol to remove extra particles from lasering. Then, clean films were prepared for bonding to form the microchannel. This step was carried out by applying an adhesive layer, which was prepared by mixing PDMS and toluene with a ratio of 1:2 on both polymeric films 31 (see Fig. 2f ). It should be noted that plasma treatment on the surface increases the hydrophilic level of PDMS films and improves surface coverage with the adhesive layer 32, 33 . Therefore, before coating the films with glue, one of them was treated with corona plasma radiation. After applying adhesive on both 100 and 500 μm films, they were gently placed on each other, heated for 15 min at 70 °C for initial bake, and left at room temperature for 24 h without any displacement. Afterward, the films were completely stuck to each other and were ready for fluid injection. In order to fix one side of the cantilever, the polymeric microchip was sandwiched between PMMA sheets except for the cantilever part. For this purpose, an adhesive of the same type was prepared, and plasma corona irradiation was used. A vacuum pumping step was also required to remove the trapped air between PDMS and PMMA sheets. Figure 3d -f demonstrates the corona treatment of PDMS surface and final micro flow sensor after the fixation process. The experimental setup is demonstrated in Fig. 4a -c. In order to inject liquid into the microchannel, a high precise calibrated syringe pump (SP125, Iran) was employed. Silicon tube with a diameter of 1 mm were used to connect the chip to the syringe pump. In addition, a small piece of a rigid Teflon tube with a diameter of 1 mm was used to connect the silicone tube and the PMMA sheet. It is worth noting that the connections were sealed via waterproof glue to prevent fluid leakage from the connections. A digital CMOS microscope (1600x, China) was applied to measure the vertical bending value of the microcantilever. The microscope was placed perpendicular to the cantilever, and the measurement was performed through HiView v.1.4 software. An example of the measuring process is shown in Fig. 4d . Repeatability of responses. Bending performance is the critical feature of a sensor after it is used several times. Therefore, the repeatability of the flow sensor was examined by comparing the vertical deformation of the cantilever at multiple applications. Figure 5a , b shows the vertical deformation data for three different tests performed on one day under the same laboratory conditions and at equal time intervals to assess the repeatability characteristic of the flowmeter. According to the data, the average standard deviation of sensor response was www.nature.com/scientificreports/ approximately 1.9. It is worth mentioning that the instrument cannot accurately measure the amount of deformation at flow rates lower than 200 L/min due to the low resolution of the displacement measurement camera. Besides, the test was repeated after one week to study the effect of time interval on the vertical displacement of the cantilever under the same laboratory conditions. According to this comparison, as the number of times, the microchip is used to measure flow rate increases, the final value of vertical displacement significantly changes and deviates from the original value, especially at higher flow rates. Accordingly, it can be deduced that the sensor requires re-calibration for long-term uses. Flowmeter reversibility. Another essential feature of mechanical sensors is their mechanical ability to return to their original position after multiple uses. In order to study this feature of the sensor, two independent tests were conducted: constant input flowrate and increasing input flowrate. In either case, the initial position of the cantilever pertinent to the vertical axis was measured using a digital camera. The cantilever displacement due to the force exerted by fluid was measured at the beginning of fluid injection into the microchannel, and its value was recorded in one minute. The cantilever was then returned to its original state by terminating the fluid injection into the microchannel. Then, after a one-minute pause, the measurement procedure was repeated in the same way. This experiment was carried out on the manufactured sensor in two different constant and increasing input flow rate modes. The results are presented in Fig. 5c , d, respectively. According to the results of these tests, the probability of sensor reversibility may deviate up to 15% from the initial position at the constant flow rate, especially at higher input flow rate values. This deviation was reduced to 5% as the input flow rate increased. As an elastic polymer, PDMS shows excellent robustness against fatigue. According to the reported result in Figs. 5c, d, only a small amount of tension remained inside the polymeric layers of the cantilever after the sensor was used several times. Thereby, the robustness of the sensor against fatigue is acceptable. However, the cantilever will be back to its original position if enough time is given. While using this sensor, a serious failure is that the bond between the bonded layers might break due to the pressure of the fluid created by the over ranged fluid flow. In this case, the bond between the layers will break, and the leakage will take place. Consequently, the measurement will fail. Accuracy. It is feasible to quantify the amount of device error in each repetition relative to the average performance using the data gathered from numerous usages to determine the accuracy of the sensor. For this purpose, two types of relative and full-scale error were calculated. The relative error result is shown in Fig. 6a . According to the results, at low flow rates, the error of the device is much more significant than that at high flow www.nature.com/scientificreports/ rates, which can be attributed to the low accuracy of the microscope in measuring the displacement at low flow ranges. Eventually, the average full-scale error percentage of the sensor was determined to be ± 1.39%. The shorter the response time of a flowmeter, the more instantaneously it can be used. System response time refers to the time it takes from the cantilever to be stable in a fixed position after turning on the syringe pump. In general, the degree of material elasticity used in manufacturing a cantilever sensor can affect its response time, in addition to the intensity of the input fluid. Therefore, using a more elastic material for manufacturing a cantilever sensor causes rapid position changes. Ultimately, after analyzing system response time at different input flow rates, the average response time of the flowmeter was determined to be 6.3 s. Figure 6b illustrates the vertical deformation value of the cantilever at 800 µl/min input flow rate. Simulation results. The results of the comparison between the average value of cantilever vertical displacement at different flow rates and the simulation results for the same microchip are remarkable, as shown in Fig. 6c . According to this result, as the input flow rate increases, the deviation between the simulation and experimental results rises so that a relative error of 25.8% is observed between them. Therefore, normalizing each data set and calculating P value is an excellent way to compare the degree of conformity between results. Figure 6d indicates the normalized experimental and simulation data with a calculated P value of 0.328, indicating good conformity between them. The deviation between results can be attributed to microchannel surface roughness caused by laser engraving on polymer, leading to increased friction between surface and fluid. Subsequently, the flow regime inside the microchannel becomes a little bit turbulent. In contrast, in the simulation assumptions, the inner surface of the microchannel is considered completely smooth with hydrodynamic laminar flow. Fig. 7 . According to the results obtained by the simulation at a flow rate of 700 µl/min, the flow hydrodynamic inside the microchannel is laminar, and no turbulency is observed along the flow path. At a given area of the cantilever, the maximum velocity was observed in the center of the microchannel, whose approximate value equals 0.3 m/s (Fig. 7a) . Nevertheless, as the vertical cross-section changes, fluid velocity reduces due to the flexibility of the material. The momentum force resulting from this velocity change leads to cantilever deformation, as can be seen in Fig. 7b -d. Given that a cantilever is a type of pressure flowmeter whose performance relies on applied force, overall stress distribution must be studied. For this purpose, the distribution of fluid stress on the upper surface of the microchannel wall in a two-dimensional diagram for both straight and curved cantilevers is shown in Fig. 7e , f. According to the diagram, it is evident that the total stress applied by fluid will increase by making a curved cantilever. According to the results, the maximum shear stress belongs to change in the fluid direction, whose value is equal to 2000 and 4500 N/m 2 in straight microcantilever and curved microcantilever, respectively. A fluid exerts stress on the microchannel walls in both normal and tangent directions. This stress emerges due to changes in velocity (shear stress) and pressure (normal stress) inside the microchannel. In a straight cantilever, stress exerted by fluid is tangent to the wall, while by making a curved cantilever, the stress is applied to the surface of the wall at a certain angle and causes the cantilever to push along the flow direction and bend. In this study, a suspended polymeric microfluidic system was fabricated to monitor the liquid flow rate in a microchannel. Prior to the fabrication process, a simulation analysis was performed to optimize the dimensions and other contributing factors. According to the simulation results, the larger the surface perpendicular to the flow, the higher rate of fluid will enter the cantilever, which causes the bending to increase. The fabricated polymeric suspended flowmeter with a sensitivity of 0.126 µm/(µl/min) measures flow rate within the range of 100-1000 µl/min. Ultimately, according to the comparison between the experimental results and simulation data, an acceptable consistency was obtained. The main result of this work refers to the curvature of the cantilever, stating that for accurate measuring, a curved structure is preferred to a straight one. Moreover, many www.nature.com/scientificreports/ conventional commercial flowmeters are not suitable for measuring low flow rates. Despite the low number of studies conducted in this field, the present paper was an attempt to provide a suitable flowmeter at the microfluidic scale. The advantages of the proposed flowmeter include its reasonable price and simple manufacturing method because of its simple structure consisting of only two thin layers of polymer and the laser engraving method required for its fabrication. High sensitivity and linear cantilever deflection based on different fluid flows are other advantages. The results were acceptable in terms of accuracy and repeatability, and an error of less than 2% was obtained. On the other hand, for its commercialization, a more appropriate detection method, such as resistance or capacitive technique, should be employed. Real-time measurement of flow rate in microfluidic devices using a cantilever-based optofluidic sensor Fabrication and applications of microfluidic devices: A review Microfluidic flow sensing approaches in Advances in micro-and manofluidics Noncontact and nonintrusive microwave-microfluidic flow sensor for energy and biomedical engineering PDMS microcantilever-based flow sensor integration for lab-on-a-chip Integrated cantilever-based flow sensors with tunable sensitivity for in-line monitoring of flow fluctuations in microfluidic systems A microfluidic flow meter with micromachined thermal sensing elements A disposable microfluidic flow sensor with a reusable sensing substrate Novel electrochemical flow sensor based on sensing the convective-diffusive ionic concentration layer Simple and convenient microfluidic flow rate measurement based on microbubble image velocimetry Optical micro/nanofibre embedded soft film enables multifunctional flow sensing in microfluidic chips Digital nanoliter to milliliter flow rate sensor with in vivo demonstration for continuous sweat rate measurement Design and fabrication of a graphene-based microcantilever flow sensor for liquid flow measurement Design and development of a low-cost cantilever-based flow sensor Fabrication and evaluation of a graphene oxide-based cantilever-type flow-meter for subsonic gas flow rate measurement Enhanced quality factor label-free biosensing with micro-cantilevers integrated into microfluidic systems Label-free biosensing of DNA in microfluidics using amorphous silicon capacitive microcantilevers Design of microfluidic experimental setup for the detection of heavy metal ions using piezoresistive biomems sensor Parametric study on fluid structure interaction of a 3D suspended polymeric microfluidics (SPMF 3) An all-polymer airflow sensor using a piezoresistive composite elastomer Piezoresistive cantilever based nanoflow and viscosity sensor for microchannels Microfluidic flow rate detection based on integrated optical fiber cantilever 2011 16th International Solid-State Sensors, Actuators and Microsystems Conference A MEMS-based air flow sensor with a free-standing micro-cantilever structure Volume and concentration dosing in picolitres using a two-channel microfluidic AFM cantilever A passive, biocompatible microfluidic flow sensor to assess flows in a cerebral spinal fluid shunt Nano-integrated suspended polymeric microfluidics (SPMF) platform for ultra-sensitive biomolecular recognition of bovine growth hormones PDMS microcantilever-based flow sensor integration for lab-on-a-chip 3D suspended polymeric microfluidics (SPMF3) with flow orthogonal to bending (FOB) for fluid analysis through kinematic viscosity A review on surface stress-based miniaturized piezoresistive SU-8 polymeric cantilever sensors Fabrication of two-layered channel system with embedded electrodes to measure resistance across epithelial and endothelial barriers Bonding of thermoplastic polymer microfluidics 4th IEEE International Conference on Nano/Micro Engineered and Molecular Systems All authors contributed equally to this work. The authors declare no competing interests. Correspondence and requests for materials should be addressed to J.R.S.Reprints and permissions information is available at www.nature.com/reprints.Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.