key: cord-0970647-tsgnnza5 authors: de Sousa Iwamoto, Luciana Aparecida; Duailibi, Mônica Talarico; Iwamoto, Gerson Yoshinobu; de Oliveira, Débora Cristina; Duailibi, Silvio Eduardo title: Evaluation of ethylene oxide, gamma radiation, dry heat and autoclave sterilization processes on extracellular matrix of biomaterial dental scaffolds date: 2022-03-11 journal: Sci Rep DOI: 10.1038/s41598-022-08258-1 sha: 0e9fdff32ca2cef58c1ccd62cdd0e546a798265d doc_id: 970647 cord_uid: tsgnnza5 Scaffolds used to receive stem cells are a promising perspective of tissue regeneration research, and one of the most effective solutions to rebuild organs. In the near future will be possible to reconstruct a natural tooth using stems cells, but to avoid an immune-defensive response, sterilize the scaffold is not only desired, but also essential to be successful. A study confirmed stem cells extracted from rat’s natural teeth, and implanted into the alveolar bone, could differentiate themselves in dental cells, but the scaffold’s chemistry, geometry, density, morphology, adherence, biocompatibility and mechanical properties remained an issue. This study intended to produce a completely sterilized dental scaffold with preserved extracellular matrix. Fifty-one samples were collected, kept in formaldehyde, submitted to partial demineralization and decellularization processes and sterilized using four different methods: dry heating; autoclave; ethylene-oxide and gamma-radiation. They were characterized through optical images, micro-hardness, XRD, EDS, XRF, SEM, histology and sterility test. The results evidenced the four sterilization methods were fully effective with preservation of ECM molecular arrangements, variation on chemical composition (proportion of Ca/P) was compatible with Ca/P proportional variation between enamel and dentine regions. Gamma irradiation and ethylene oxide presents excellent results, but their viability are compromised by the costs and technology’s accessibility (requires very expensive equipment and/or consumables). Excepted gamma irradiation, all the sterilization methods more than sterilizing also reduced the remaining pulp. Autoclave presents easy equipment accessibility, lower cost consumables, higher reduction of remaining pulp and complete sterilization, reason why was considered the most promising technique. www.nature.com/scientificreports/ sterilization of the organs, but was not found a definitive process for the dental scaffold. Dentistry aims not only on restoration but also on its regeneration, justifying the need of advancing on studies to mimic the teeth enabling it as biomaterial scaffold, what also will demand an efficient sterilization process. In the first phase of this study 31 , after partial demineralization-decellularization, presented remaining pulp on almost 30% of the samples. Would be possible to reach 100% of pulp removal, using higher concentration or time extension of exposition to demineralization solution, an alternative could be an endodontic intervention to access the pulp chamber, both avoided because they could interfere on the samples' structural integrity. failure rates because of bacterial colonization are still high The existence of remaining pulp could provide conditions to cell proliferation 38 and represent a considerable risk of rejection or inflammatory response 32, 39 , reason why the sterilization methods were introduced in this phase of the study. The aim of this study was to obtain a viable dental scaffold, with preservation of structural properties, were compared commonly used sterilization methods (AS and DH) and high efficiency techniques (Gamma and EO), Mechanical resistance (micro-hardness), preservation of layers (enamel, dentine, cement and pulp chamber were analyzed and also the sterilization efficacy of the four methods proposed and analyze their efficacy to sterilize extracted natural teeth, enabling them as biomaterial scaffolds to posterior reception of stem cells. The research protocol is performed in accordance with the relevant guidelines, is in accordance with Declaration of Helsinki, and was approved by the Ethics Committee in Research of Federal University of São Paulo (UNIFESP) under number 1529/2015. This study was conceptualized as primary, experimental, prospective, analytic and comparative design. Informed consent obtained from all patients and/or their legal guardian(s). In this design, 51 pre-molar teeth were obtained from healthy patients through orthodontic extraction procedure. The inclusion criteria for teeth selection were: healthy subjects without chronic use of any kind of drugs, radicular complete formation and signed written consent. Exclusion criteria were sectioned or bleached teeth, dental anomaly or dental whitening 16 . Premolars were kept at room temperature in Falcon tubes at 10% formaldehyde solution before the use, then washed in de-ionized water, dried at room temperature (24 h). To make easier the access of cleaning substances to pulp chamber, teeth were emerged in a 500 ml of Phosphate Saline Buffer (PBS), with addition of 28 g of EDTA kept at 60C up to translucence (Ph4), then placed in individual recipients for 30 days at room temperature. Second step, were kept 30 days on 9% hydrogen peroxide to clean up the teeth, and final 30 days emerged in enzymatic detergent solution (Riozyme)/distillated water 50% each) to remove the biological residues. They were washed on deionized running water, dried at room temperature for 24 h and packaged in surgical grade paper to be sterilized. The first tooth was cut is 10 slices (~ 1.5 mm), washed, dried, packed and separated in pairs, these slices were intended to be grinded into powder for analisys at X-Ray Diffractometer (XRD) equipment. The 50 teeth + 10 slices were randomly separated into 5 groups of 10 + 2 slice each, named as groups for decellularization (GD) to avoid direct identification during analysis, and finally submitted to sterilization: DH (group GD1)-170 °C by 120 min; AS (group GD2)-from 60 to 129 °C, and pressure between 1.7 and 1.8 kgf/cm 2 . In two steps, the first 20 min sterilizing, and 30 min drying; EO (group GD3)-packed samples were sterilized through exposition to an ethylene-oxide (30%) + CO 2 (70%) atmosphere at a relative humidity from 40 to 70%, pressure range 0.4 to 0.5 kgf/cm 2 , exposure time of 4 h with temperature range from 45 to 55 °C. Gamma (group GD5)-packed and sealed samples were exposed to radiation of 25 kGy with multipurpose irradiator of 60 CO (CTR / IPEN / CNEN-SP), at room temperature and pressure. The samples were characterized to confirm the preservation of ECM (shape, atomic composition and mechanical resistance) and determine the efficacy of sterilization processes. The teeth were photographed (digital camera cannon model EOS Rebel T100) and radiographed in the longitudinal plane, before and after sterilization processes, using a positioning device to keep uniform distance. On radiographs were used an aluminum scale in order to standardize the different shades of gray observed, where the colorimeter Chroma Meter CR-400-Konica Minolta Camera Co., provided a quantitative measurement to evaluate the color variation after sterilization processes. To verify the micro-structural interfaces (enamel, dentin, cement and pulp chamber), the samples were carefully sliced, and analyzed at SEM equipment (EVO MA 15 Zeiss equipment), the samples were fixed on stubs and covered with exploded carbon tape, a thin carbon tape established the electrical contact between the sample surface and the sample-holder, allowing the images generation on SEM. The same equipment has an EDS probe included, where was possible to confirm the variation on atomic composition. An additional composition analysis was proceeded using an X-Ray Fluorescence (XRF) equipment, Bruker S2 Ranger, adjusted to analyze a 10 mm diameter and calibrated using pure Cu standard, the equipment has the limitation of analyzing the components through oxide, and Hydrogen is not detectable by the sensors. As the Hydroxyapatite formula is Ca 10 (PO 4 ) 6 (OH) 2 (denoting the crystal unit cell comprises two entities of Ca 5 (PO 4 ) 3 (OH)), was decided to confirm the proportionality of Ca (Calcium) and P (Phosphorus) in order to analyze if the sterilization treatments could cause a structural variation caused by temperature, pressure, exposition to ethylene oxide + CO 2 or gamma irradiation. If existing, this variation could cause an atomic rearrangement crystallographic structure or adsorption of atoms from gas composition of controlled atmosphere (for Example on EO). The samples were ground into powder using pistil and mortar and measured in the XRD equipment D8 diffractometer, with linear position detector type LynxEye from Bruker. The powder was carefully positioned at sample-holder (PPMMA-Poly-methylmethacrylate) and measured at room temperature under Cu kα radiation, wavelength 1 = 15,406 Å, 2θ scanning from 20° to 120°, step of 0.02° and exposition time of 1.2 s. The data were analyzed through Rietveld Method 40 at Topas 4.2 software from Bruker AXS, and CIF (Crystallographic Information Files) were obtained from ICSD www.nature.com/scientificreports/ (Inorganic Crystal Structure Database). Mechanical Resistance-The samples were previously embedded in acrylic resin and polished, and then micro-hardness was measured at Shimadzu HMV 2 T equipment, using 490.3 mN, 0.05 load, and 10 s. Thioglycolate (THIO) and for aerobic bacteria, fungi and yeast, was chosen Tryptone Soya Broth (TSB). Negative control sterilization tests were proceeded using two sterilized tubes only with THIO and TSB, The positive tests were performed on 2 inoculated tubes, one only with THIO and the other with TSB solution with no teeth. From the control group GD4 (with no sterilization) one tooth was introduced in the tube with THIO, the second was placed into an inoculated tube with THIO, the third was introduced into a tube with TSB and the fourth into a tube with inoculated TSB. This procedure was done to warranty the cleaning substances residues are not enough to inhibit the microbial growth. The other groups had 2 teeth for each solution (GD1, GD2, GD3 and GD5). All tubes were incubated at 37.5° C for 14 days. The microorganisms were Staphylococcus Aureus (ATCC6538), Bacilus subtilis (ATCC6633), Pseudomonas aeruginosa (ATCC 9027), Clostridium sporogenes (ATCC 11437), Candida albicans (ATCC 10231) and Aspergillus niger (ATCC16404). The concentration was 1 ml for each 15 ml of solution, with 10 to 100 viable microorganisms, in accord to Brazilian Pharmacopeia. Histology-The dental organs were included in resin block, sliced (2 elements of each group), polished and identified. The samples were colored with Hematoxiline Eosine (HE), Masson Goldner (MG) and Steven Blue (SB), and the pictures were obtained using Inverted Optical Microscopy Axiovert 40C (Carl Zeiss) through Axio Vision 4.1 software. The data were treated with Kruskal-Wallis (EDS), ANOVA 1 factor (Microhardness) and ANOVA double factor (mass weight losses) tests for statistical validation, in all cases the nullity hypothesis level was set at 0.05 or 5%. ECM preservation-The characterization techniques were used to confirm the preservation of ECM in terms of shape, atomic composition, diffractive information about atoms arrangement in the crystalline structure and the micro-hardness of the samples. The mass losses, optical images (photography, radiographies), absence of detected fractures, and minor changes on color suggest the different sterilization methods represents low impact on ECM, supposedly not compromising the scaffolds' viability. As soon the sterilization processes were completed all the teeth were fractioned using sterilized cutting pliers, where was verified presence of pulp in 30% of the control group (GD1) and also on Gamma group (GD5), 20% of DH (GD1) and EO (GD3), and 10% of AS (GD2). Observing SEM's image, Fig. 1 , details of teeth's structure do not evidence visible variations on hard tissues (cement, dentine and enamel) when comparing the different sterilization processes, however, the same was not observed on soft tissue (pulp). While, sterilization at GD1 and GD5 caused almost no modification, on GD3 and mainly GD2 caused a significant degradation on teeth with remaining pulp. All sterilization techniques caused significant elevation on hardness, where Gamma Radiation (GD5) is the least impacting, while the most impacting one was dry heat (Fig. 2 presents the comparative measurements). All samples presented small cracking lines, a further study should be interesting to confirm if it would influence the resistance, cells adhesion or even reconstruction of the tissue. Apparently, the temperature has higher influence on hardness, mainly above the water boiling temperature. The control group presented micro-hardness slightly below indicated by Garcia-Garcia 41 (45.69, varying from 38 to 53HVN), GD5 presented the expected hardness (69.53, varying from 50 to 67HVN), GD2 (69.53 HVN), GD3 (70.61 HVN) and GD1 (77.55 HVN) these results, associated to statistical validation indicates the sterilization method interfere directly on the micro-hardness of teeth, it is important to confirm if this hardness increase can interfere on cell adhesion or not. The Rietveld analysis of XRD data suggests the crystalline structures of hydroxyapatite (HA) do not change significantly, although presenting small intensity variation, mainly on angles range of 32-34 degrees; this variation is probably related to different region of sliced teeth analysis (enamel has higher proportion of HA, in sequence are dentine, cement and absent at pulp, the layers were also differently affected by the sterilization process). The reminiscence of peaks on same angles indicates the structural arrangement was not modified, even after the sterilization processes. The refining parameters GOF (Goodness of Fit) 1.40 and weighted profile R-factor (RwP) = 8.51 reinforces the refinement is very close to expected HA's data. On Fig. 3a ) the peaks variation pointed as enamel % variance reflects the technique used, although no change on the 2 theta angles was registered, there was an intensity variation, correlated to higher presence of enamel on some slices. The tooth was cut on crosswise sectioning, where the crown region, with higher presence of enamel, have sharper and more intense peaks than the ones from dentine or cement, in good agreement with reported XRD of enamel and dentine regions 41, 42 . The XRF data, Fig. 3b , indicates a small variation on proportion of Calcium (Ca) and Phosphorus (P), being GD3 the more affected, in proportional balance of Ca/P, followed by Gamma Irradiation (GD5), and, apparently, GD1 and GD2 methods did not affect the chemical composition. The hypothesis of structural arrangement modification on HA was not confirmed by XRD analysis, reinforced by the mass losses in every single sterilizing methods (Table 1) . Considering the chemical composition of enamel (96% HA and 4% water), dentine (70% HA, 20% organic material and 10% water), and cement (40% HA, 33% proteins and 22% water), the deeper effect of EO (GD3) and Gamma (GD5) were probably because the impact of water, organic material, or slice of tooth analyzed (crown, dentine region or cement). The " Table 1 " presents the mass variation caused by the sterilization methods, GD4 didn't varied because was the control group and was not submitted to any sterilization, but also was weighted when the samples were submitted to sterilization and when they returned. Using "Anova double factor without repetition" statistic tool, www.nature.com/scientificreports/ Figure 1 . SEM images, obtained at EVO MA ZEISS equipment from UNIFESP, did not evidence visual changes on dentine structure, but presented an apparent smoothing on enamel surface (GD1, GD2, GD3 and GD5), and also some cracks on the cement at GD2 and GD3 (the possibility of being caused by cutting process is not discarded). (Table 2a -c). The last line of each table is the proportional weight composition of HA, they are very close to GD4 composition on dentine and enamel (justified by the fact dentine has 70% of HA and enamel 90% approximately). The sterilization methods affects more intensively the pulp (Table 2a) , probably because this tissue is softer and easier to be modified by pressure or temperature. The significant growth of "others" on GD3, is probably related to adsorption of Ethylene Oxide gas by the pulp; Kruskal-Wallis (KW) statistical analysis: H = 9.217143 and p = 0.026539 validate the hypothesis of different sterilization method interfere on the chemical composition. Dentine (Table 2b) , has intermediate levels of HA (~ 70%), organic tissue (20%) and water (10%) being less affected than pulp, but here the Oxygen was the most affected compound, although in lower scales the growth of "others" can indicate adsorption of Ethylene Oxide, probably at teeth canaliculated channels; also using KW, H = 16.72686 and p = 0.000804 confirms the hypothesis of interference of sterilization method on chemical composition on dentine. Enamel (Table 2c) , was the least affected, probably related to the highest level of HA (near 90%), reinforcing the low effect of the sterilization methods on the HA matrix, the same confirmation on Enamel through KW statistic tool, indicates H = 16.71429 and p = 0.000809, also confirming the sterilization method interfere on final chemical composition. Histology images (Fig. 4) , using three different standards (Hematoxiline-Eosine (HE), color cell nuclei blue, cytoplasm and collagen fibers pink, the dentine region of GD4 appears darker colored, probably because of miscegenation of nuclei inside the caniculated channels. The sterilized samples presented lighter pink coloration, indicating the sterilization partially eliminated soft tissue, but enamel didn't present reactive coloration, meaning absence of this kind of cells; Masson Goldner (MG) color cell nuclei black, cytoplasm red and collagen green, the images indicate higher concentration of collagen on dentine region, in special on dentine of GD4 and GD5 groups, enamel didn't present reactive coloration; and Stevenel's Blue (SB) color in blue collagen and fibers, and red-pink the calcified tissues; The coloration at dentine and enamel evidenced calcified structure, not being possible to affirm nuclei or soft tissue are present, dark dots and lines are apparently the canaliculated channels. The images with HE and MG colorants suggests GD1, GD2 and GD3 were more efficient on removing soft tissue from the teeth. CIFs obtained from ICSD-https:// icsd. produ cts. fiz-karls ruhe. de/), treated at Topas 4.2 also from Bruker, and plotted using Origin 2015. As it is a complex multi-atomic molecular structure, several angles are represented, but with higher incidence on angles near 26, 32-33, and 40 degrees, the reminiscence of angles positions means no molecular arrangement modification was detected. (b) XRF's data obtained at Bruker's S2 Ranger equipment the graphic was generated at Excel 2013-the sterilization methods present different effects on the composition balance (Ca/P), indicating GD3 (EO) affects more the Ca portion of Hydroxyapatite and GD2 (DH) interacts more intensively with P portion. www.nature.com/scientificreports/ Although the sterility tests are very well known techniques, with large application to several materials, their usage on dental scaffolds is not frequently reported, to reduce the possibility of rejection of these scaffolds the sterilization methods are the central core of this research. Here, the negative control (NC) test, with THIO and TSB solutions, confirmed there were no contamination on solutions or tubes. Two empty tubes were inoculated, and presented microorganisms proliferation, showing the effectiveness of THIO and TSB solutions. In sequence were run the positive control (PC) tests, preparing 20 falcon tubes, 4 for each sterilized group and control group (GD1, GD2, GD3, GD4 and GD5). The absence of microorganisms, after incubation process, evidenced Table 3 . The use of sterilization procedures on medical or dental devices is a common practice, even on artificial implants as titanium teeth implants, the study of Manea 43 44 reports the importance of sterilization when proceeding these tissues, some methods cited include moist heat (autoclaving), ethylene oxide and gamma irradiation. The study does not recommend ethylene oxide because of a toxic gas production (ethylene chlorohydrin) what could cause synovial inflammation, and focuses on gamma irradiation. Fölsch 45 studied the thermo-disinfection on cancellous bones reporting the tensile strength was preserved, agreeing to supposed preservation of structural resistance on ECM. In this study, after partial decellularization process, almost 30% of samples still presented biological residues at the pulp chamber, repeating the results previously obtained on the partial demineralization study 31 . When submitted to sterilization, the results suggest the influence of temperature and pressure variation on reduction of remaining pulp. Except by GD5 process, all the others presented a significant reduction; GD5 was run at room temperature (~ 20 °C) and pressure (~ 1kgf/cm2) still presented 30% of remaining pulp; GD1 at room pressure and 170 °C, reduced from 30 to 20%; GD3, at pressure between 0.4 and 0.5 kgf/cm2 and temperature 45-50 °C, also reduced from 30 to 20%; GD2, with pressure between 1.7 and 1.8 kgf/cm 2 and temperature from 60 to 129 °C, reduced from 30 to 10%, indicating the combination of higher pressure and temperature have stronger impact on the reduction of remaining pulp. As the aim of this research was to evaluate the four sterilization methods, could be said the four methods were well succeeded, as all of them are suitable to produce sterilized scaffold. None of methods impacted on structural molecular arrangement (XRD), although, caused impact on chemical composition (XRF and EDS), and also caused higher micro-hardness. Considering the cost-benefit criteria associated to reduction of remaining pulp, the results suggest the Autoclave Sterilization (GD2) has some advantages in terms of competitive appeal. However, a deeper study to confirm the compatibility with stem cells should be proceeded previously to discard dry heat (GD1), ethylene oxide (GD3) or gamma radiation (GD5). The results evidenced the decellularization alone is not enough to eliminate microorganisms from dental scaffolds, and the four sterilization methods were fully effective with preservation of ECM molecular arrangements, but with some variation on chemical composition (mainly proportion of Ca/P). Gamma irradiation (GD5) and ethylene oxide (GD3) presents excellent results, but their viability are compromised by the costs and mainly the technology's accessibility (requires very expensive equipment and/or consumables), exception to gamma irradiation (GD5), all the others also reduced the remaining pulp. Autoclave (GD2) presented easy equipment accessibility (with lower cost consumables), higher reduction of remaining pulp and complete sterilization, reason why was considered the most promising technique. Table 3 . Sterility test-the signals " + " indicates the presence of microorganisms, and "−" absence, PC and NC are abbreviations of "Positive Control" and "Negative Control". Managementof dental caries asa chronic infectious disease Ciência e Engenharia de Materiais -Uma introdução Teeth and bones: applications of surface science to dental materials and related biomaterials Analysis of the electron-beam radiation damage of TEM samples in the acceleration energy range from 0.1 to 2MeV using the standard theory for fast electrons In vitro and in vivo degradation of porous poly(DL-lactic-co-glycolic acid) foams Novel bioactive materials with different mechanical properties Polyurethane/poly(lactic-co-glycolic) acid composite scaffolds fabricated by thermally induced phase separation Developing bioactive composite materials for tissue replacement In vitro and in vivo characteristics of PCL scaffolds with pore size gradient fabricated by a centrifugation method Biomaterials and strategies for nerve regeneration Effect of ceramic filler content on the mechanical and thermal behaviour of poly-l-lactic acid and poly-llactic-co-glycolic acid composites for medical applications Influence of the extracellular matrix on the regulation of cardiac fibroblast behavior by mechanical stretch Intrinsic mechanical properties of the extracellular matrix affect the behavior of pre-osteoblastic MC3T3-E1 cells Bioengineered teeth from cultured rat tooth bud cells APIC guideline for selection and use of disinfectants Nanofibrous scaffolds for dental and craniofacial applications Culturally sensitive oral health educational materials for older African Americans Stem cells and tooth tissue engineering Biological matrices and bionanotechnology Performance of collagen sponge as a 3-D scaffold for tooth-tissue engineering Chick embryo model for homing and host interactions of tissue engineering-purposed human dental stem cells In vivo generation of dental pulp-like tissue by using dental pulp stem cells, a collagen scaffold, and dentin matrix protein 1 after subcutaneous transplantation in mice The performance of human dental pulp stem cells on different three-dimensional scaffold materials Tissue engineering: the hope, the hype, and the future Vascularization strategies for tissue engineering The rapid anastomosis between prevascularized networks on silk fibroin scaffolds generated in vitro with cocultures of human microvascular endothelial and osteoblast cells and the host vasculature Engineered vascularized bone grafts supplimenary information Decellularization of tissues and organs Tooth tissue engineering: tooth decellularization for natural scaffold Nucleotide sequences of complementary deoxyribonucleic acids for the Proal Chain of Human Type I procollagen. statistical evaluation of structures that are conserved during evolution D o s s i ê t é c n i c o: Controle de esterilização em produtos odonto-médico hospitalares Effect of different human tissue processing techniques on SARS-CoV-2 inactivationreview Sterilization techniques for biodegradable scaffolds in tissue engineering applications Which is the best method of sterilization of tumour bone for reimplantation? a biomechanical and histopathological study Avaliação da biocompatibilidade de implantes mamários de silicone esterilizados por calor seco e pelo óxido de etileno. Rev. Bras. Ciencias Farm Culture of human dental pulp cells at variable times post-tooth extraction Systematic review on sterilization methods of implants and medical devices Rietveld refinement guidelines Estudio Del Comportamiento Térmico De La Hidroxiapatita Mediante Las Técnicas De Espectroscopia Infrarroja Y Análisis Térmico Diferencial The use of new materials for pulp capping (hydroxyapatite-HAp and tricalcium phosphate-β-TCP) Sterilization protocol for porous dental implants made by selective laser melting Radiation sterilization of tissue allografts: a review Influence of thermodisinfection and duration of cryopreservation at different temperatures on pull out strength of cancellous bone L.I.: Contributed to conception, design, data acquisition, analysis and interpretation, performed all statistical analysis, drafted, critically revised the manuscript and gave final approval; M.D.: Contributed to conception, design, analysis and interpretation, performed all statistical analysis, drafted, critically revised the manuscript and gave final approval; G.I.: Contributed to conception, design, data acquisition, analysis, interpretation and critically revised the manuscript and gave final approval; D.O.: Contributed to design, data acquisition, analysis, interpretation and critically revised the manuscript and gave final approval; S.D.: Contributed to conception, design, analysis, interpretation, critically revised the manuscript and gave final approval; All authors gave their final approval and agree to be accountable for all aspects of the work. The authors declare no competing interests. Correspondence and requests for materials should be addressed to L.A.S.I. Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.