key: cord-0933105-121xcnsg authors: Feng, Bin; Zhang, Sibo; Wang, Di; Li, Yalong; Zheng, Pai; Gao, Long; Huo, Da; Cheng, Lei; Wei, Shuangying title: Study on antibacterial wood coatings with soybean protein isolate nano-silver hydrosol date: 2022-02-14 journal: Prog Org Coat DOI: 10.1016/j.porgcoat.2022.106766 sha: 2e96c9abac38b165d43131e805c49b7178699282 doc_id: 933105 cord_uid: 121xcnsg As the new coronavirus pneumonia swept the world in 2020, the demand for antibacterial products significantly increased. In this study, a soy protein isolate nano-silver hydrosol was prepared using an environmentally friendly Ag(+) in situ reduction process, where the soy protein was ultrasonically blended with polyacrylic resin to obtain a polyacrylate-nano silver antibacterial wood coating. The structure of the soy protein isolate nano-silver hydrosol was assessed, and the structure and antibacterial and mechanical properties of the film were characterized. The results showed that the silver nanoparticles (AgNPs) exhibited good crystallinity and were evenly distributed in the emulsion. The composite film had good antibacterial properties against gram-negative bacteria represented by Escherichia coli and gram-positive bacteria represented by Staphylococcus aureus. With increased nano-silver content, the diameter of the inhibition zone increased from 0 to 30 mm, and from 18 to 50 mm for the two bacteria, respectively. Moreover, the elastic modulus of the film increased from 8.173 to 97.912 MPa, and the elongation at break decreased from 240.601 to 41.038% as the content of AgNPs changed from 0.1 to 1%, respectively. Thus, this study provides a new method for preparing waterborne polyacrylate coatings with excellent antibacterial properties. waterborne wood coatings With increasing interest in environmental protection, water-based wood coatings have received widespread attention because of their low toxicity and excellent performance [1] [2] [3] . Polyacrylate waterborne coatings are one of the main varieties of wood coatings, with advantages such as strong adhesion, high transparency, and high solid content [4] . The new coronavirus pneumonia in 2020 became a global health crisis, and drastically affected individuals and the world economy. Thus, applying antibacterial coatings on material surfaces may not only effectively protect the base material, but also eliminate disease transmittance between people and objects, caused by the spread of microorganisms. This type of mitigation technique is important but is currently less utilized for wood furniture coatings. Antibacterial coatings can be divided into natural antibacterial coatings, organic antibacterial coatings, inorganic antibacterial coatings, and composite antibacterial coatings, according to the types of antibacterial agents added. Natural antibacterial agents, such as chitosan, have spectral antibacterial properties and good biocompatibility, but begin to carbonize and decompose at 160˚C-180˚C and thus cannot be mass-produced [5] [6] [7] . Organic antibacterial agents have strong color permanence and short-term antibacterial effects, with good performance, but utilize small molecules that are toxic [8] . Therefore, researchers are increasingly investigating inorganic antibacterial agents, as they hold potential for development [9] . Among them, silver nanoparticles (AgNPs) combine the advantages of inorganic antibacterial materials and nano-antibacterial materials and exhibit low toxicity, high antifouling and broad-spectrum antibacterial performance, and strong adsorption capacities. Thus, these materials hold promise as super antibacterial materials [10] [11] [12] [13] [14] . The biocidal activity of AgNPs is caused by the sustained release of Ag + ions, and their surfaces have photocatalytic properties, which can promote oxidative damage to neighboring cells [15] [16] [17] . Current methods for preparing nano-silver can be classified according to physical or chemical preparation. Physical preparation methods include laser ablation, microwave reduction, quenching, and mechanical grinding [18] [19] [20] . Physical methods provide high purity and a simple process but have additional equipment requirements and high production costs [21] . Chemical reduction methods require the addition of a reducing agent, such as sodium borohydride or sodium zirconate, to a silver precursor to reduce the precursor into elemental silver, which further grows into silver particles [22] [23] [24] . Silver particles can easily agglomerate, thus stabilizers or dispersants, such as polyethylene glycol, mercaptan derivatives, aniline, long-chain amines, and surfactants, are often added to reduce silver particle agglomeration [25] . Traditional chemical methods have low cost and high yield, but the reagents used therein are harmful to humans and the environment, and some stabilizers and dispersants are even carcinogenic [26] . Therefore, there is a growing demand for non-toxic preparation compounds [27] [28] [29] . Soy protein has received extensive attention from researchers because it is J o u r n a l P r e -p r o o f non-toxic, inexpensive, biodegradable, and environmentally friendly [30] [31] [32] . Soy glycinin (11S globulin) and glycinin (7S globulin) are two important components of soy protein, which are predominant in soy protein [33] [34] [35] . In addition, special amino acids such as tyrosine and cysteine from soy protein isolate (SPI) can be used as reducing agents for metal ion precursors. Furthermore, the amino and carboxyl groups on the SPI surface have a strong affinity for silver particles and can be used to stabilize and disperse silver nanoparticles, and stabilize reduced silver nanoparticles in solution [36] . In this study, the soybean protein isolate was used as the raw material, and the flavor protease hydrolysis reaction, which is a mild reaction with few side reactions, was used to break the peptide bonds in soybean protein isolate and maintain its structure and amino acid configurations. AgNPs were prepared in situ using tyrosine to reduce silver ions and stabilize elemental silver, and were then blended with a polyacrylic resin emulsion under ultrasonication. The corresponding antibacterial coating was then prepared by ultraviolet curing, and its antibacterial performance was evaluated. This green preparation of soybean protein isolate nano-silver hydrosols for antibacterial wood coatings possesses potential and broad development prospects. Soy protein isolate was obtained from Shansong Biological Products Co., Ltd. (Linyi, China) (protein (%) ≥ 90). The flavor protease was obtained from Novozymes (China) Biotechnology Co., Ltd. Methyl methacrylate, n-butyl acrylate (BA), ammonium persulfate, sodium dodecyl sulfate (SDS), sodium hydroxide, pentaerythritol triacrylate, and bromelain were obtained from Shanghai Macklin (China). In addition, 2-(methacryloyloxy)ethyl acetoacetate (AAEM), OP-10 emulsifier, and silver nitrate were obtained from Shanghai Aladdin (Shanghai, China). Ten grams of soy protein isolate and 0.3 g of bromelain were dissolved in 175 mL of distilled water and stirred at 50˚C for 8 h until the solution was clear and uniform. The obtained liquid was then transferred to a dialysis bag, and after dialysis in an 11.5 pH sodium oxide solution for two days, the dialysate was exchanged with deionized water for one day, and the dialysate was changed every 2 h. After dialysis, the solution was centrifuged at 9000 r/min for 10 min to remove small amounts of insoluble matter. The concentration of the soy protein isolate, which was measured by the weighing method, was about 1%. The isolate was then stored at 4˚C. The soy protein isolate solution prepared above was diluted to 0.25 wt.%. Then, 20 mmol/L of sodium hydroxide was added to 5 mL of the isolate solution, to adjust the pH to 10. While stirring, 20 mmol/L of silver nitrate solution was added dropwise until different concentrations of silver nitrate formed. The solution was stirred for 10 min until fully mixed, and then the mixed solution was exposed under a 100-W white light. A 100-mL alkaline aqueous solution containing 0.4 wt.% of NaOH was prepared. MMA, BA, and AAEM were washed with the alkaline aqueous solution three times to remove the acrylic monomer inhibitor. The monomer was then washed with 100 mL of distilled water three times to remove the alkaline aqueous solution from the monomer. An ammonium persulfate initiator (0.042 g) was dissolved in 15 g of distilled water. Then, SDS (0.60 g) and OP-10 (0.30 g) were dissolved in 45 g of deionized water, to form an emulsifier solution for later use. The MMA (18 g), AAEM (5.9 g), and BA (15 g) were then mixed together. The emulsification solution was added to a four-necked flask, and the water bath temperature was adjusted to 80˚C. Then, the flask was filled with nitrogen, and 10 wt.% of the monomer and initiator were poured into the four-necked flask and mechanically stirred at 360 rpm for pre-emulsification for 15 min. The monomer and initiator were added dropwise to the four-necked flask at a rate of one drop every three seconds, and one drop every thirty seconds, respectively. The soy protein isolate nano-silver hydrosol was added to the polyacrylate emulsion, and nano-silver content was controlled to 0.1, 0.2, 0.5, and 1 wt.% of the polyacrylate. Then, the 819 L photoinitiator (3 wt.% of solid content) and the PETA active diluent monomer (5 wt.% of emulsion mass) were mixed with the above antibacterial emulsion, sonicated for 5 min, and then stirred with a magnetic stir bar for 15 min. To prepare the resin film, the emulsion solution was cast into 45 × 12 × 1 mm polytetrafluoroethylene molds. After removing the water at room temperature for 24 h, the film was irradiated under a 395-nm UV-LED light for 10-15 s. When the films were cooled to room temperature, the corresponding numbers were S2, S3, S4, and S5, and the corresponding nano-silver content was 0.1, 0.2, 0.5, and 1 wt.%, respectively. To prepare the wood coatings, the emulsion was coated on a wooden board by brush coating. Subsequently, the wooden board was placed in an 80˚C oven for about 30 s. After removing the water, the wood coating was irradiated with a 395 nm UV-LED light for 10-15 s. The above steps were then repeated two times, and then we tested the performance of the paint film after 10 days, after it was completely dry. The soy protein isolate solutions containing different concentrations of AgNO 3 were reacted under a 100 W incandescent lamp for 24 h. Then, the solution was diluted 10 times, and the fluorescence was measured using a fluorescence J o u r n a l P r e -p r o o f spectrophotometer (Hitachi, Japan) with an excitation wavelength of 280 nm. The soy protein isolate nano-silver hydrosol was analyzed by a Hitachi u-3010 UV spectrophotometer. Wavelength detection was 300-600 nm, the scanning speed was 300 nm/min, and the step length was 1 nm. Deionized water was used as the blank control. The morphologies of the AgNPs were observed using a JEM-2100 transmission electron microscope (TEM, JEOL, Japan) at an operating voltage of 200 kV. The hydrosol was diluted to about 0.5 wt.% with deionized water and coated on carbon thin-film-modified copper grids. A selected area electron diffraction (SAED) was used for crystal structure analysis, and energy dispersive X-Ray spectroscopy (EDX) was used for elemental analysis. The surface morphologies of the polyacrylate and composite films were assessed by a scanning electron microscope (SEM) (Se3400N, Hitachi Ltd., Tokyo, Japan), at a voltage of 20 kV, after coating with gold. S. aureus and E. coli were selected as the representative gram-positive bacteria and gram-negative bacteria, respectively, to test the antibacterial properties of the polyacrylate nano-silver composite film. Tensile tests were conducted using an electronic universal testing machine (UTM 2203, Sansi Zongheng Technology Co., Ltd.), where 45 × 10 mm (length × width) rectangular films were tested at a rate of 10 mm/min. The performance of the wood coating was assessed according to its abrasion resistance, hardness, adhesion, and glossiness, in accordance with the GBT4893.8-2013, GB/T 6739-2006, GBT4893.4-2013, and GBT4893.6-2013 standards, respectively. Figure 1 shows the fluorescence spectrum analysis results of the SPI-AgNPs hydrosols with different AgNO 3 concentrations. The fluorescence intensity of the sol reflected the tyrosine content, and the phenolic hydroxyl group on the tyrosine residue had a strong electron-donating ability, reducing silver ions in situ to obtain silver nanoparticles. When the AgNO 3 concentration in the mixed solution increased from 0.10 to 2.00 mmol/L, fluorescence intensity gradually decreased. In addition, the fluorescence intensity was unchanged after reaching 1.60 mmol/L, indicating that the reducing ability of tyrosine reached its limit at this time. Therefore, when the AgNO 3 concentration was 1.40 mmol/L, the Ag + in the system could be completely reduced to Ag 0 . In the follow-up study, we uniformly used 1.40 mmol/L of AgNO 3 to prepare the corresponding polyacrylate nano-silver composite material. was colorless and transparent. After adjusting the pH to 10, and adding 1.40 mmol/L of the silver nitrate solution, the solution became milky white. After the solution was irradiated under a 100 W incandescent lamp for 1 h, the solution changed from milky white to light yellow. The solution became bright yellow after 3 h, dark gray after 4 h, and dark brown after 6 h. After further illumination, the color of the hydrosol did not change significantly. The observed solution color changes were caused by the surface plasmon resonance (SPR) of the silver nanoparticles in the visible light range [37] . This was due to the deepening of the solution color, as the number of AgNPs increased with increased light time, and the absorption peak of the silver nanoparticles tended to increase with exposure time. Studies have also shown that the shape and size of AgNPs will affect the position of the characteristic peaks [38] . Thus, characteristic peaks between 320 and 450 nm are generally associated with spherical nano-silver, which was verified in the nano-silver transmission diagram in this study. In addition, in the spectrum, no peaks near 335 and 560 nm, were observed, indicating no aggregation of nanoparticles [39] . As shown in Figure 3(a) , the silver nanoparticles were about 10 nm in size, and the morphology was spherical, with uniform dispersion and no agglomeration. This indicated that the silver nanoparticles exhibited good stability. The lattice parameters, observed by HRTEM, showed that the interlayer spacing was 0.23 nm, which corresponded to the lattice constant of the (101) plane of nano-silver. The SAED pattern was clear, indicating that the nanoparticles were highly crystalline. The rings were also attributed to the diffraction of the (111), (200), (220), and (311) planes of face-centered cubic (FCC) silver [40] . The EDX spectra showed obvious characteristic absorption peaks for silver, which further confirmed that the product was nano-silver. The micro-morphologies of the film surfaces were further observed by SEM, and the results are shown in Figure 4 . The surface of the polyacrylate film was smooth, with almost no phase separation or cracking. The results showed that the film exhibited a high crosslinking density and good phase mixing between the soft and hard segments when cured by ultraviolet light [41] . Furthermore, the AgNPs did not affect the smoothness of the film. Figure 5 shows that the nano-silver was uniformly dispersed on the surface of the polyacrylate nano-silver composite film without large-scale agglomeration. The contact antibacterial method was used to test the antibacterial performance of the polyacrylic resin-nano silver composite film. Pure polyacrylic resin was used as a reference material to test the antibacterial ability of the composite film for at least 24 h. As shown in Figure 6 , the prepared polyacrylic resin-nano silver composite film had excellent resistance to both E. coli (gram-negative bacteria) and S. aureus (gram-positive bacteria). This was the result of bacterial structural damage and death, caused by the interactions of the nano-silver with the cell membrane, which destroyed the respiratory chain binding enzymes, inhibited the ribosomal subunit proteins, and ATP production processes related to enzyme expression, which consequently affected DNA replication. In addition, with increased nano-silver content, the antibacterial effect of the composite film on E. coli and S. aureus improved. In this study, a higher inhibition zone was observed for gram-positive S. aureus compared to gram-negative E.coli. This observation was in excellent agreement with earlier studies [42] [43] [44] . This was attributed to the cell wall structure of gram-negative bacteria, which consists of an outer membrane composed of lipids, proteins, and lipopolysaccharides (LPS), and acts as a barrier, providing effective protection against antibacterial agents. By contrast, the walls of gram-positive bacteria do not contain an outer membrane [45, 46] . The mechanical properties of the films were evaluated and the results are shown in Figure 7 and Table 1 . With increased AgNP content, the elastic modulus and tensile strength increased from 8.173 and 5.311 MPa to 97.912 and 6.092 MPa, respectively, while the elongation at break decreased from 240.601 to 41.038%. These results were mainly attributed to the small average particle size and large specific surface area of the nanoparticles. In addition, the dispersed nano-silver particles acted as reinforcement sites for the film, effectively improving the strength and modulus of the film. Thus, the introduction of AgNPs significantly enhanced the mechanical properties of the polyacrylate films. The performance results of the wood coatings with different AgNP content, such as abrasion resistance, adhesion, glossiness, and pencil hardness, are shown in Table 2 . There were no significant changes in abrasion resistance and pencil hardness of the wood coatings. However, the glossiness of the coatings slightly improved with increased AgNP content. In addition, the adhesion properties of the polyacrylate nano-silver coatings with different AgNP content reached level 1 or higher. This was attributed to the hydrophilic groups in the water-based acrylic resin in the coating, which chemically reacted with the hydroxyl groups of the wood surface, providing good adhesion strength [47] . Owing to the excellent reduction properties of tyrosine in green and natural soybean protein isolate under alkaline and light conditions, a silver precursor was reduced to elemental silver in situ. It was then ultrasonically blended with polyacrylate to obtain an antibacterial coating with excellent mechanical properties. The optimal feeding concentration of the silver ions was 1.4 mmol/L, according to the fluorescence intensity of the solution. The UV-Vis spectrum indicated that as the illumination time increased, the absorption peak gradually increased, and more nano-silver was generated. In addition, the 320-450 nm absorption peak corresponded to spherical nano-silver, which was in good agreement with the subsequent TEM images. The SEM images also showed that the nano-silver was uniformly distributed in the polyacrylate film, and its surface morphology was not affected. The polyacrylic resin nano-silver composite film thus showed excellent resistance to both E. coli and S. aureus bacteria. With increased AgNP content, the tensile strength and elastic modulus gradually increased, while the elongation at break gradually decreased. When AgNP content was 0.5 wt.%, the film exhibited ideal properties, with an elastic modulus, tensile strength, and elongation at break of 62.946 MPa, 7.463 MPa, and 175.789%, respectively. In addition, the wear loss, adhesion, glossiness, and pencil hardness values after 100 revolutions were 0.003 g, 0, 26.9, and 5H, respectively. UV-curable waterborne polyurethane-acrylate: preparation, characterization and properties Biobased reactive diluent for UV-curable urethane acrylate oligomers for wood coating Recent advances in vegetable oils based environment friendly coatings: A review Study on waterborne acrylate coatings modified with biomass silicon Wound dressing from polyvinyl alcohol/chitosan electrospun fiber membrane loaded with OH-CATH30 nanoparticles Porous Cellulose Membranes with Chitosan-Coated Nanofibers for Visualized Cutaneous Wound Healing Dressing Wound dressing based on electrospun PVA/chitosan/starch nanofibrous mats: Fabrication, antibacterial and cytocompatibility evaluation and in vitro healing assay Synthesis of Ag modified vanadium oxide nanotubes and their antibacterial properties Antimicrobial Silver Nanoparticles: Future of Nanomaterials, Microbial Nanobionics Synergy of bioinspired chimeric protein and silver nanoparticles for fabricating "kill-release" antibacterial coating A sol-gel based silver nanoparticle/polytetrafluorethylene (AgNP/PTFE) coating with enhanced antibacterial and anti-corrosive properties Silver nanoparticles: partial oxidation and antibacterial activities Synergistic antibacterial effects of β-lactam antibiotic combined with silver nanoparticles Development of Silver-Zein Composites as a Promising Antimicrobial Agent Antibacterial activity of glutathione-coated silver nanoparticles against Gram positive and Gram negative bacteria Antibacterial hybrid hydrogels loaded with nano silver Assessment of silver release and biocidal capacity from silver nanocomposite food packaging materials Shape-Controlled Synthesis of Silver Nanoparticles by Production of silver nanoparticles by laser ablation in open air Microwave-assisted synthesis of silver nanoparticles using sodium alginate and their antibacterial activity Enhanced Raman scattering and photocatalytic activity of TiO2 films with embedded Ag nanoparticles deposited by magnetron sputtering Uniform Silver Nanowires Synthesis by Reducing AgNO3 with Ethylene Glycol in the Presence of Seeds and Poly(Vinyl Pyrrolidone) Synthesis and characterization of a silver nanoparticle-containing polymer composite with antimicrobial abilities for application in prosthetic and orthotic devices Development of Ag nanoparticles on the surface of Ti powders by chemical reduction method and investigation of their antibacterial properties Biosynthesis of Silver Nanoparticles using Lemon Extract and its Antibacterial Activity Silver as antibacterial agent: ion, nanoparticle, and metal Synthesis and characterization of silver nanoparticles using Gmelina asiatica leaf extract against filariasis, dengue, and malaria vector mosquitoes Green synthesis and characterization of silver nanoparticles using Enicostemma axillare (Lam.) leaf extract Low-cost and eco-friendly phyto-synthesis of silver nanoparticles using Cocos nucifera coir extract and its larvicidal activity Synthesis and Applications of Biodegradable Soy Based Graft Copolymers: A Review PMMA-g-SOY as a sustainable novel dielectric material Properties and Structure of Soy Protein Isolate-Ethylene Glycol Sheets Obtained by Compression Molding Comparative study of encapsulation of vitamins J o u r n a l P r e -p r o o f with native and modified soy protein, Food Hydrocoll Preparation of Soy Protein Isolate (SPI)-Pectin Complex Film Containing Cinnamon Oil and Its Effects on Microbial Growth of Dehydrated Soybean Curd (Dry Tofu) Biodegradable soy protein isolate-based materials: a review Green Synthesis of Silver Nanoparticles Using Nymphae odorata Extract Incorporated Films and Antimicrobial Activity Superior bactericidal activity of SDS capped silver nanoparticles: Synthesis and characterization Controlling the Synthesis and Assembly of Silver Nanostructures for Plasmonic Applications Preparation of acacia-stabilized silver nanoparticles: A green approach Gum kondagogu (Cochlospermum gossypium): A template for the green synthesis and stabilization of silver nanoparticles with antibacterial application Synthesis of UV-curing waterborne polyurethane-acrylate coating and its photopolymerization kinetics using FT-IR and photo-DSC methods The study of antimicrobial activity and preservative effects of nanosilver ingredient Silver nanoparticles: green synthesis and their antimicrobial activities Green synthesis of silver nanoparticles using olive leaf extract and its antibacterial activity Impregnation of silver nanoparticles into bacterial cellulose for antimicrobial wound dressing Biodegradable electrospun poly(l-lactide) fibers containing antibacterial silver nanoparticles Structural analysis of photodegraded wood by means of FTIR spectroscopy ). We thank LetPub (www.letpub.com) for its linguistic assistance during the preparation of this manuscript.