key: cord-0922353-7mbz0pis authors: Ding, Zhanlin; Wang, Hong; Feng, Zhe; Sun, Meiqing title: Synthesis of dual-phase Ti(3)O(5)/Ti(4)O(7) nanofibers for efficient adsorption of SARS-CoV-2 date: 2021-06-02 journal: Mater Lett DOI: 10.1016/j.matlet.2021.130167 sha: fb1d0e794f0b0ce9c45fb23a088439210652a7df doc_id: 922353 cord_uid: 7mbz0pis In this study, we synthesized the dual-phase Ti(3)O(5)/Ti(4)O(7) nanofibers for efficient adsorption of the severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2), a life-threatening virus being taking millions of people lives. The Ti(3)O(5)/Ti(4)O(7) nanofibers were synthesized by preparation of H(2)Ti(3)O(7) precursor, polydopamine coating and furnace calcination. Protein and phospholipid adsorption assays showed that the dual-phase nanofibers had much higher affinity to both the model molecules bovine serum album (BSA) and phosphatidylethanolamine (PE) than the control single-phase Ti(6)O(11) nanofibers. Consistently, the dual-phase nanofibers exhibited much stronger adsorption ability to SARS-CoV-2 pseudovirus than Ti(6)O(11). This study sheds a light on titanium oxide nanomaterials to adsorb SARS-CoV-2 for avoiding its infection and for enriching it during rapid virus detection. The severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2), which causes worldwid e COVID-19 pandamic, is a great threat that has taken millions of the people lives [1] [2] [3] . This virus, similar to other kinds of coronaviruses (e.g., SARS-CoV-1, MERS), is a respiratory RNA virus spreading in population by abundant mediators, such as air, water, food, touched things, and so on [4] [5] [6] . It is very important to develop efficient strategies to remove this virus and to enrich it for detection from these mediators, especially from air and water. Nanomaterials exhibited high surface areas and adjustable surface affinity to viruses. Adsorption of viruses by nanomaterials is an exciting topic to remove viruses for protecting human bodies from lifethreatening infections, and to enrich them for sensitive detection [7, 8] . A series of nanomaterials, such as polymer-based nanomaterials, natural nanofibers, graphene nanofilms, and so on [9] [10] [11] . However, it remains a great challenge to develop inorganic nanomaterials for efficient adsorption of viruses, especially SARS-CoV-2. In this study, we synthesized a series of titanium oxide nanofibers, including dual-phase Ti3O5/Ti4O7 nanofibers and single-phase Ti6O11 nanofibers, by using hydrothermal methods and electrospinninghydrogen reduction method. Protein and phospholipid adsorption assays were performed to evaluate the affinity of the nanofibers to model biomolecules. Adsorption of the nanofibers to SARS-Co V-2 pseudovirus was further detected to investigate the virus adsorption ability of the nanofibers. This study revealed that the dual-phase Ti3O5/Ti4O7 nanofibers are promising nanoplatforms capturing the dangerous SARS-CoV-2 to avoid its infection and to enrich it for virus detection. The Ti3O5/Ti4O7 nanofibers were synthesized using the Shi's hydrothermal method with modificatio n [12] . Briefly, 20 mL NaOH solution (containing 12 g NaOH in dH2O) and 8 mL Ti(SO4)2 solution (containing 1.07 g Ti(SO4)2 in dH2O) were mixed by magnetic stirring. The mixture was added in a 50 -mL Teflon-lined stainless-steel reactor, followed by heated at 180 °C for 48 h, obtaining the Na2Ti3O7 nanofibers. The nanofibers were then treated by 1 mol/L HCl for 1 h, obtaining the H2Ti3O7 precursor. 100 mg of the precursor were mixed with 100 mg of polydopamine at Tris buffer (pH=8.5) by magnetic stirring for 24 h. The coated precursor was then harvested by centrifugation and calcinated at 1000 °C for 1 h at a tube furnace, obtaining the final Ti3O5/Ti4O7 nanofibers. The Ti6O11 single-phase nanofibers were synthesized by electrospinning-hydrogen reduction method [13] . The synthesized nanofibers were characterized by transmission electron microscopy (TEM, Tecnai G 2 F-20, FEI, USA), X-ray diffraction The adsorption ability of the nanofibers to BSA and PE was evaluated according to our previous methods [14] . BSA adsorption was performed in 10 mL of distilled water, with the initial nanofiber concentration and BSA concentration of 500 mg/L in 40-mL vials. The vials were gently shaken at 37 °C for 24 h, followed by centrifugation to remove the nanofibers. BSA concentration of the supernatants were measured by a Coomassie brilliant blue assay. PE adsorption was performed in 10 mL of 1:1 chloroform/methanol, with the initial nanofiber and PE concentration of 500 mg/L in 40-mL vials. After 24 h of shaking at 37 °C, the suspensions were centrifuged, and PE concentration of the supernatants were measured using a LC-MS system (LCMS-2020, Shimadzu, Japan). To evaluate the adsorption ability of the nanofibers to SARS-CoV-2 pseudovirus, 100 μL of SARS- The Ti3O5/Ti4O7 titanium oxides were synthesized by calcination of the polydopamine-coated H2Ti3O7 precursor. Both SEM and TEM observation showed that the products had regular nanofiber morphology, with the diameter of 50~100 nm, and the length of 3-10 μm (Figure 1a, 1b (Table S1 ). As the control nanofibers, two kinds of Ti6O11 single-phase nanofibers (i.e., Ti6O11-1 and Ti6O11-2) were prepared by the electrospinning method. TEM observation, XRD and XPS characterization indicated that both kinds of the control titanium oxides had the similar nanofiber morphology ( Figure S2a ), the XRD pattern of Ti6O11 (JCSPD# 85-1058, Figure S2b ), and the main composition of Ti and O ( Figure S2c) . BET) analysis further revealed that Ti6O11-1 and Ti6O11-2 had a BET surface of 235.9 m 2 /g and 36.0 m 2 /g (Table S1 ), respectively. Proteins and phospholipids are two main components on the surface of SARS-CoV-2. To compare the affinity between the nanofibers and biomolecules, two model molecules, i.e., the model protein BSA and the model phospholipids were chosen for adsorption assays . After co-incubation of the nanofibers and BSA, the Ti3O5/Ti4O7 nanofibers adsorbed much higher levels of BSA than the two kinds of control Ti6O11 nanofibers (155 mg/g versus 44~81 mg/g, Figure 2a) . Similarly, the Ti3O5/Ti4O7 nanofibers also adsorbed much PE than the two kinds of Ti6O11 nanofibers (420 mg/g versus 128~255 mg/L, Figure 2b ). These results indicated that the dual-phase nanofibers had high affinity to both proteins and phospholipids, which may facilitate their adsorption to virus particles. The high affinity of the dual-phase nanofibers may be attributed to their surface vacancies that facilitate the nanofiber surfaces strongly binding the biomolecules. PE adsorption by the nanofibers. * indicates significant difference between the groups (P < 0.05). The high affinity of the dual-phase nanofibers suggested its high adsorption ability to the SARS-CoV-2 virus. To confirm this, a SARS-CoV-2 pseudovirus, which exposes the critical spike protein (S protein) on the virus surface and has similar surface properties of the real SARS-CoV-2, was used to assess the capacity of the nanofibers to adsorb SARS-CoV-2. After co-incubation of the nanofibers with the SARS -CoV-2 pseudovirus, the nanofibers were filtered and stained by FITC-tagged anti-S protein antibodies. Confocal microscopy revealed that the Ti3O5/Ti4O7 nanofibers displayed strong FITC fluorescence on the surface (Figure 3a ). In contrast, the two kinds of control Ti6O11 nanofibers had only weak FITC fluorescence ( Figure 3a) . These results revealed that the Ti3O5/Ti4O7 nanofibers had much higher virus -adsorption capacity than Ti6O11. Besides, since abundant viruses had similar protein and lipid compositions to SARS-CoV-2, the Ti3O5/Ti4O7 nanofibers may also have high adsorption capacity to other kinds of viruses. In conclusion, this study synthesized the dual-phase Ti3O5/Ti4O7 nanofibers by precursor preparation, polydopamine coating and furnace calcination for efficient adsorption of the SARS-CoV-2 virus. The obtained dual-phase nanofibers exhibited much higher affinity to both the model molecules BSA and PE, and to the SARS-CoV-2 pseudovirus than the single-phase Ti6O11 nanofibers. This study provided a novel strategy of SARS-CoV-2 adsorption by inorganic titanium oxide nanomaterials for avoiding its infection and for enrichment it during rapid detection. Proc. Nat. Acad. Sci Experimental & molecular medic This work is supported by Project of Science and Technology Development in Wuqing District , Tianjin (WQKJ202067).