key: cord-0905710-5ti1gapx authors: Musselman, Kevin P.; Delumeau, Louis-Vincent; Araujo, Roy; Wang, Haiyan; MacManus-Driscoll, Judith title: Electrochemical removal of anodic aluminium oxide templates for the production of phase-pure cuprous oxide nanorods for antimicrobial surfaces date: 2020-09-18 journal: Electrochem commun DOI: 10.1016/j.elecom.2020.106833 sha: 725061334c853c907566c2df76c4e34d48cda96a doc_id: 905710 cord_uid: 5ti1gapx Antimicrobial surfaces are ones that incapacitate or kill pathogens landing on them, which could allow for self-sanitising surfaces for hospitals or implants, ensuring healthier stays and procedures. Cuprous compounds such as Cu(2)O are especially effective at incapacitating both viruses and bacteria, and nanorod arrays have been shown to prevent the adhesion of pathogens and mechanically deform bacteria to the point that their cell walls rupture. A Cu(2)O nanorod array should therefore allow for the exploitation of these effects. In the present work, an electrochemical method is introduced, where Cu(2)O nanorods formed in a substrate-supported anodic aluminium oxide (AAO) template are held at a stable electrochemical potential throughout the removal of the AAO template. This avoids the partial reduction of the nanorods from Cu(2)O to Cu that was observed during chemical removal of the template, which was attributed to the presence of residual aluminium from the template fabrication process that reacts with the etchant and lowers the electrochemical potential of the nanorods to a value that favours reduction. Using the electrochemical removal method, the reliable production of phase-pure, free-standing, crystalline Cu(2)O nanorod arrays on ITO/glass substrates is demonstrated. This simple method is compatible with nanorod arrays of any size. Anodic aluminium oxide (AAO) templates have proven to be a useful tool for producing arrays of nanorods, nanowires, and nanotubes (both semiconducting and metallic), for applications in sensing, energy generation and storage, and catalysis [1] [2] [3] . These templates have been produced on aluminium (Al) foils, as well as different substrates, including silicon and indium-tin-oxide (ITO)/glass [3] [4] [5] [6] [7] [8] [9] . With the rise in antibiotic resistance in bacteria and the recent difficulty in tackling the COVID-19 viral pandemic, there is an urgent need for enhanced antimicrobial surfaces, and template-created arrays are a promising architecture for such surfaces. Nanorod or nanowire arrays can impart antimicrobial properties to a surface by preventing the adhesion of pathogens and/or incapacitating them once they reach it [10, 11] . Poor adhesion follows from the fact that nanotextured surfaces are hydrophobic, due to the air they retain between the nano-features, which minimises contact area between pathogens and the surface [11] . Incapacitation of adhered pathogens may follow from physical and/or chemical effects. Arrays of nearly parallel nanorods have been developed as bactericidal "beds of nails", inspired from the bactericidal nanorod-rich surfaces of certain insect wings [10, [12] [13] [14] . Evidence has indicated that the SARS-CoV-2 virus is less viable on copper (Cu) surfaces than on other common surfaces [15] , and more generally, cuprous compounds are among the most effective materials known to incapacitate pathogens, including SARS-CoV-2 [16] [17] [18] . In a study using human coronavirus 229E on Cu/Zn brass samples for example, it was found that Cu(I) may play a more significant role in virus incapacitation than Cu(II) in the longer term [19] . In another study, cuprous oxide (Cu 2 O) powders reduced the infectious activity of bacteriophage T4 and Qβ viruses by 4 and 5 orders of magnitude in 30 min and the infectious activity of gram-negative and gram-positive bacteria by 3 orders of magnitude in 1 hour. These reductions were significantly larger than for CuO or silver powders, and it was concluded that the mode of action to degrade pathogen biomolecules must be direct contact with cuprous compound surfaces [16] . Thus, the ability to control the chemical composition of antimicrobial surfaces is critical. In the case of nanorod fabrication with AAO templates, the templates are typically removed by chemically etching the AAO in a basic solution. However, little consideration has been given to the influence of etching on the embedded materials. In this work we examine the chemical stability of Cu 2 O nanorods, a promising antimicrobial surface due to the combined effect of Cu 2 O and of nano-features, during the chemical removal of a surrounding AAO template. Cu 2 O nanorod arrays were fabricated using AAO templates on ITO/glass by a procedure reported previously [3] , as illustrated in Figure 1 . Briefly, Al films approximately 500 nm thick were deposited onto ITO/glass substrates (Praezisions Glas & Optik) by DC magnetron sputtering with thin titanium (Ti) and tungsten (W) adhesion and barrier layers between the ITO and Al. The Al films were then anodised in 0.3M oxalic acid at 40 V to produce AAO templates approximately 800 nm thick. The edges of the samples were masked with Crystal bond adhesive to prevent delamination from the edges during anodisation. After anodisation, the AAO templates were soaked in 5 wt% phosphoric acid to widen the pores slightly and remove the oxide layer from the base of the pores, exposing the underlying conductive substrate. Cu 2 O was then electrochemically deposited into the AAO pores to produce arrays of Cu 2 O nanorods with approximate dimensions of 60 nm in diameter and 300 nm in length. All details for the nanorod fabrication can be found in a previous report [3] . Cu 2 O films were also produced using identical electrochemical deposition conditions by using bare ITO/glass substrates as the working electrode. [PLACEHOLDER FOR FIGURE 1] The AAO templates were chemically removed to leave free-standing nanorod arrays by soaking in an aqueous 0.1M NaOH solution for 30 min, as illustrated in Figure 1 . After template removal, the nanorod samples were rinsed in purified water to remove any remaining NaOH and dried with a light flow of nitrogen. To monitor the electrochemical potential of a nanorod array during the chemical template removal process, an insulated Cu wire was attached to the underlying ITO substrate with silver (Ag) paste and masked with Kapton polyimide tape. The potential of the sample was measured using a Keithley 2400 Sourcemeter, relative to an Ag/AgCl (in saturated KCl) reference electrode, which was also inserted into the etching solution. For the electrochemical template removal procedure, an insulated Cu wire was attached with Ag paste to the underlying ITO substrate of the sample to be etched, and masked with Kapton polyimide tape. The sample was then attached to a Princeton Applied Research Model 363 Potentiostat/Galvanostat in a standard three-electrode configuration with a reference electrode like the one described in Section 2.2 and a 6.25 cm 2 platinum counter electrode, as illustrated in Figure 1 . The electrodes (including the sample to be etched) were immersed in 0.1M aqueous NaOH at room temperature, at which point the potentiostat was turned on immediately. After template removal, the nanorod samples were rinsed in purified water to remove any remaining NaOH and dried with a light flow of nitrogen. Scanning electron microscopy (SEM) was performed with a a LEO VP1530 field emission SEM. Phase identification was performed using a Bruker D8 theta/theta X-ray diffraction (XRD) system with Cu Kα radiation (λ=0.15418 nm) and a LynxEye position-sensitive detector. The transmission electron microscopy (TEM) cross-sectional specimen was prepared by conventional mechanical thinning, grinding, polishing, and a final ion polishing step. The TEM images were taken using a FEI Tecnai F20 electron microscope. Cyclic voltammetry of Cu 2 O films was performed using the same potentiostat/galvanostat and three-electrode cell noted in Section 2.3, together with custom-made Labview software. Top-view SEM images of the fabricated AAO templates are shown in Figure 2a -b. The pore diameters are observed to range in size from approximately 30 to 60 nm. Figure 2c shows a topview SEM image of a nanorod array produced by pore-widening the AAO template for 30 min in the 5 wt% phosphoric acid, followed by electrochemical deposition of Cu 2 O and chemical removal of the AAO template. Image analysis indicated an average nanorod diameter of 538 nm. The bactericidal efficiency has been reported to depend on the dimensions of the nanostructures, and the nanorod arrays produced here fall well within the recommended dimensions for bactericidal nanostructures [12, 14] . The XRD data for an AAO template on ITO/glass, containing an array of Cu 2 O nanorods approximately 275 nm long is shown in Figure 3a . The XRD data indicates that the nanorods are phase pure. Other than signals associated with the ITO substrate and AAO template, the only peaks present in the as-deposited sample correspond to Cu 2 O. Moreover, the intensity and sharpness of the peaks indicate a good degree of crystallinity of the Cu 2 O phase grown by the electrodeposition technique. Figure 3b shows the XRD data for a similar nanorod array after template removal by chemical etching. The intensity of all Cu 2 O peaks was reduced by the chemical template removal procedure and a Cu peak appeared. Removal of the AAO template by chemical etching was seen to result in discolouration of the nanorods from bright yellow to brown, as shown in Figure 3d , consistent with partial reduction of the Cu 2 O nanorods to elemental copper. The Cu peak in Figure 3b is broad, indicating small crystallites of Cu are formed during the reduction process. From the breadth of the peak, the Cu crystallite size was estimated to be approximately 20 nm using the Scherrer equation. This was confirmed by TEM imaging. Figure 4a shows a cross-sectional TEM image of 300 nm-tall nanorods for which discolouration was observed during template removal. The nanorods are seen to be composed of many small grains. The electrochemical potential of a Cu 2 O nanorod array during the chemical template removal process was measured and is shown in Figure 5a . The potential of the nanorod array was observed to drop to a value significantly lower than -0.5 V within the first few minutes of etching, before returning to a more positive potential, after approximately 16 minutes. The lower half of the inset in Figure 5 displays pictures taken of the sample surface during chemical template removal, at intervals of 1 min. Significant discolouration of the Cu 2 O nanorods is seen, particularly after 11 minutes, when the potential dropped to a value less than -1.1 V. Chemical removal of AAO is performed at room temperature in a simple aqueous NaOH solution, such that the etching conditions are well described by the electrochemical stability diagram of Pourbaix [20] , reproduced in Figure 6 . For the copper system in aqueous solutions at 25°C and a pH of 13, the reduction of Cu 2 O to Cu is favoured at potentials of approximately -0.5 V (versus Ag/AgCl in KCl(sat)) or lower [20] . This is consistent with the reduction to metallic copper observed in the inset of Figure 5a , particularly when the electrochemical potential dropped below -1.1 V. We attribute the negative potential observed during the initial stage of the chemical template It is crucial to be able to remove AAO template without altering the properties of the nanostructures contained therein, particularly for surface-sensitive applications such as antimicrobial coatings. This necessitates the ability to maintain the electrochemical potential of the nanorod array at a level within the stability region throughout the template removal process. Using the setup detailed in Section 2.3, the electrochemical potential of the ITO substrate and Cu 2 O nanorod array was held at a fixed value of -0.4 V, which corresponds to the middle of the Cu 2 O stability region at a pH of 13 ( Figure 6 ). Figure 5b shows the constant potential maintained throughout the electrochemical template removal, and the upper portion of the inset in Figure 5 displays pictures of a Cu 2 O nanorod sample at 1 min intervals during the electrochemical template removal. In contrast to the chemical template removal (lower portion of inset), no change in colour was observed. Nanorod arrays were maintained in these electrochemical conditions for over 3 hours with no visible change in colour. Figure 5c shows a Cu 2 O nanorod array produced via this electrochemical template removal approach. It is seen in Figure 6 that the Cu 2 O stability region is equally narrow across the entire pH range, so the electrochemical template removal is expected to be advantageous regardless of the pH of the etching solution used. The nanorods subjected to this prolonged 3-hour template removal process were examined by TEM and XRD. The XRD data of the electrochemically treated nanorods is shown in Figure 3c and was identical to that of the as-deposited nanorods (Figure 3a) , except for the absence of an AAO-related peak, indicating that phase-pure Cu 2 O remained. TEM images of the nanorods removed from the AAO using the electrochemical method are shown in Figures 4b-c . Compared to the nanorods produced by chemical removal of the AAO in Figure 4a , the electrochemicallyremoved nanorods display large crystalline grains with dimensions similar to the nanorods themselves. This is consistent with the sharper Cu 2 O XRD peaks from Figure 3a and c. The reliable production of pure, crystalline nanorod arrays on supporting substrates via the removal of AAO is critical for the realisation of many of the proposed applications of these nanostructures. To prevent reduction of nanorods in AAO templates upon template dissolution, Cu 2 O nanorods were studied. An easy-to-implement electrochemical template removal method was employed, in which the Cu 2 O nanorods were held at a stable electrochemical potential throughout the AAO etching process, guaranteeing Cu 2 O nanorods as a final product. It was found that the presence of residual aluminium in the AAO template leads to a negative electrochemical potential on the sample and partial reduction of the Cu 2 O to metallic Cu during chemical template removal. By introducing this simple electrochemical procedure to remove the ITO-supported AAO, we demonstrate the ability to produce phase-pure Cu 2 O nanorod arrays. To our knowledge, there has been no previous report of a similar electrochemical technique for the removal of AAO templates. This technique would be similarly useful for other materials with limited electrochemical stability, such as iron, zinc, chromium, and manganese oxides. Moreover, it is compatible with conductive substrates of any size, and could have applications in mass production of nanostructures. Notably, these phase-pure Cu 2 O nanorod arrays are promising as antimicrobial surfaces that may prevent the adhesion of pathogens and/or incapacitate them through morphological mechanisms and the material effects of Cu 2 O. This could be very useful in applications such as antimicrobial surfaces in hospitals. The synthesis method developed in this work will facilitate future investigation of the antimicrobial behavior of these and other types of nanorod arrays. The authors have no competing interests to declare. transparent substrates via sol-gel electrophoresis Low temperature synthesis of large-area, free-standing nanorod arrays on ITO/glass and other conducting substrates Origin of the bottlenecks in preparing anodized aluminum oxide (AAO) templates on ITO glass Highly ordered nanoporous alumina on conducting substrates with adhesion enhanced by surface modification: universal templates for ultrahighdensity arrays of nanorods Nanoporous aluminum oxide thin films on Si substrate: structural changes as a function of interfacial stress Anodic aluminum oxide (AAO) templates on transparent conducting glass (TCO) coated glass: new prospects for a mature nano-fabrication tool Development of nanoporous anodic aluminum oxide AAO) thin template on PET/Ti flexible substrate for flexible liquid cristal display (flexible-LCD) application Preparation of large-area porous anodic alumina on insulating substrates Nanosciencebased strategies to engineer antimicrobial surfaces Surface alterations to impart antiviral properties to combat COVID-19 transmission Bio-mimicking nano and microstructured surface fabrication for antibacterial properties in medical implants Quantitative evaluation of the antibacterial factors of ZnO nanorod arrays under dark conditions: physical and chemical effects on Escherichia coli inactivation Natural and bioinspired nanostructured bactericidal surfaces Aerosol and surface stability of SARS-CoV-2 as compared with SARS-CoV-1 Highly efficient antiviral and antibacterial activities of solid-state cuprous compounds Deactivation of human immunodeficiency virus type 1 in medium by copper oxide-containing filters A surface coating that rapidly inactivates SARS-CoV-2 Human coronavirus 229E remains infectious on common touch surface materials Atlas of electrochemical equilibria in aqueous solutions  Chemical removal of anodic aluminium oxide templates can damage embedded structures  Anodic aluminium oxide templates were used to grow cuprous oxide nanorod arrays  Electrochemical removal technique prevented reduction of cuprous oxide nanorods  Reported procedure is useful in production of antimicrobial surfaces