key: cord-0886646-doylzohq
authors: Stelmakova, M.; Streckova, M.; Orinakova, R.; Guboova, A.; Balaz, M.; Girman, V.; Mudra, E.; Bera, C.; Batkova, M.
title: Effect of heat treatment on the morphology of carbon fibers doped with Co(2)p nanoparticles
date: 2021-10-07
journal: Chem Zvesti
DOI: 10.1007/s11696-021-01897-0
sha: 8f212e1a90194ce66e9c6fe280b7a190ee0fe258
doc_id: 886646
cord_uid: doylzohq

ABSTRACT: Carbon fibers (CFs) decorated by Co(2)P nanoparticles and carbon nanotubes were prepared via needle-less electrospinning technique. Formation of catalytically active Co(2)P nanoparticles and growth of carbon nanotubes were monitored in open and closed sintering environment at different sintering exposure times. Higher porosity, important in the catalytic reaction for easier penetration of electrolyte into the CFs, was achieved by mixing two immiscible polymers with natrium dodecyl sulfate and subsequent heat treatment process. Structure and morphology of the prepared modified carbon fibers were characterized by XRD, SEM and TEM. The time of heat exposure at the sintering temperature of 1200 °C and closure of the sintering space showed distinct effect on the growth and shape of carbon nanotubes. SEM and Raman spectroscopy revealed that closure of the system led to the formation of carbon nanotubes with smaller diameters and less structural disorder. Comparing of as-prepared CFs revealed that CFs with Co(2)P sintered in the closed system exhibited the best electrocatalytic activity for hydrogen evolution reaction due to lower overpotential and smaller Tafel slope in acidic solution. GRAPHIC ABSTRACT: [Image: see text]

The high costs of coal and gas, together with negative impact of fossil fuels on the environment and human life, have led to increased interest in the use of renewable energy. Moreover, according to the "Global Energy Review" published in April 2020 by the International Energy Agency, as one of many global world`s associations for shaping, secure and sustainable energy for future, in the, renewable energy has so far been the energy source most resilient to Covid-19 lockdown measures. According to this review, which examines the impact of the Covid-19 crisis on overall energy demand and CO 2 emissions, global use of renewable energy in all sectors increased in the first quarter of 2020 by about 1.5% relative to the same quarter of 2019 (emissions 2020). Despite supply chain disruptions that have paused or delayed activity in many regions, the expansion of solar, wind and hydropower was expected to help renewable electricity generation to rise by nearly 5% in 2020 (emissions 2020). Unfortunately, fossil fuels still cover almost 60% of global electricity supply, so water, wind and solar energy as alternative energy sources present new challenges in the field of safety of energy transfer kinetics, etc.) and DFT (density functional theory) calculated from the Gibbs free energy ΔG H of the adsorbed atomic hydrogen, three most perspective alternatives for catalysts are: metals and alloys, transition metal compounds, and carbonaceous compounds Greeley and Nørskov 2005; Wang and Johnson 2009; Zhang et al. 2018; Andrews and Citra 2002; Zeng and Li 2015; Kibsgaard et al. 2015) .

Distinctive properties of carbon materials, such as wide operating potential, large variability of modifications by shaping or easy incorporation into other materials, low cost and inertness against most electrolytes, make them suitable catalysts for HER. However, amorphous carbon is an electroactive inert and possesses poor catalytic activity . Therefore, it is necessary to supplement other catalysts into the carbonaceous materials that increase their electrocatalytic activity. Alternatively, one may design more suitable carbon structures such as carbon fibers (CFs), carbon nanotubes (CNTs) single-walled CNTs (SWCNTs), graphene, or glassy paper. It is known that the incorporation of transition metal nanoparticles (TMN), such as Co, Cu, Ni, Fe, significantly increases the electrocatalytic activity, the efficiency of catalysts (Zhou et al. 2016; Shi and Zhang 2016; Kong et al. 2013) , and also initiates the growth of carbon nanotubes (CNTs) . Carbon with tubular nanostructures such as CNTs and SWNTs has attracted considerable attention not only because of its fascinating, unique physicochemical properties, but also due to its promising applications in transistors (Bachtold et al. 2001) , field-emission tips (Iijima 1991) , sensors (Zhu et al. 2002 ), supercapacitors (An et al. 2001 , and bio-medical fields (Zanello et al. 2006) . Various established methods are used to prepare carbon fibers and CNTs, such as electric-arc discharge, laser ablation synthesis techniques and catalytic pyrolysis of carbon-containing gases via catalytic chemical vapor deposition (CCVD) (Hernadi et al. 2000; Lyu et al. 2004; Bonard et al. 2002; Wei et al. 2003) .

Needle electrostatic spinning (NLE) is the most suitable method for production of fibers from polymer solutions (Jirsak and Petrik 2012). The principle of electrospinning is based on the generation of free charges on the surface of a polymer solution with a high voltage potential (in tens of kV) (Garg and Bowlin 2011; Inagaki et al. 2012) . A Taylor cone is formed at the end of the needle, from which fibers are formed after overcoming the surface tension and are trapped on the collecting counter electrode. By this technique, the continual fibers can be created and modified by nanoparticles directly in the spinning process. Needle-less electrospinning (NLES) or electrospinning of free liquid surfaces can simultaneously generate a number of streams from the solution surface, which increases the amount of fibers prepared by an order of magnitude, thus significantly reducing the time required to produce fibers (Niu et al. 2019) .

NLES is a promising technology for mass-scale production of nanofibers. Although there are some issues with the practical application, NLES is still the first choice for industrial production of nanofibers, considering its advantages and potential for continual improvement. Thanks to close collaboration between electrospinners, chemists, designers, machinery, electricians and automation controls engineers, NLES will produce high-quality nanofibers in a well-controlled way at low cost and be beneficial to our daily life, health care and various industrial sectors (Ding et al. 2019) .

According to the literature and authors' knowledge, three main factors affect the catalytic behavior of carbon fibers prepared by needle-less electrospinning: i. structure of CF ) morphology and porosity of the fibers (size and diameters of CF, defect-less structure, distribution of incorporated nanoparticles, etc.); ii. modification of CF )-surface or interior modification by additional nanoparticles or additives (CNT growth on the surface, type of TMN, etc.); iii. final heat treatment, which can influence the building of the carbon matrix and affect the distribution of TMN and growth of CNTs (Streckova et al. 2016) .

The type and dispersion of the catalyst are key factors for the formation and controlling the growth of CNTs. Therefore, a great effort has been paid to explore the optimal catalysts to enhance reactivity and efficiency for HER. It was found that the growth and structure of CNTs was greatly influenced by the form and occurrence of Co in the substrate structure (Xiang et al. 2009 ). The role of cobalt catalyst in the Co-MCM-41 material at different pretreatment stages of the SWCNT synthesis was investigated by Chen et al. (Chen et al. 2004a (Chen et al. , 2004b (Chen et al. , 2006 . During the SWCNT growth process, cobalt in Co-MCM-41 substrate becomes more active after partial reduction by hydrogen prior to CO exposure. A narrow distribution of SWNT diameter can be achieved by optimized prereduction (500-600 °C) and reaction temperature (750-800 °C) and by control of cobalt cluster sizes (Chen et al. 2004a ). The experimental results showed that the effect of CO pressure and reaction time controls synthesis of SWCNTs depending on three competitive processes: reduction in cobalt, nucleation of the reduced cobalt atoms into clusters, and initiation and growth of the carbon nanotubes (Chen et al. 2004b ). The concentration and size of Co nanoparticles also affected the growth of SWCNTs. The uniform SWCNT diameters were achieved at a cobalt cluster size of approximately 6 -8 Å with concentration of Co catalytic nanoparticles of 3 wt.% (Chen et al. 2006) .

In this article, the main goal is the investigation of the effect of heat treatment on the morphology and electrocatalytic activity of CFs modified by cobalt phosphide nanoparticles (CoP, Co 2 P) for HER. Polymeric fibers containing the source compounds for Co 2 P nanoparticles formation have been produced by NLES. These compounds are represented by cobalt nitride and phosphoric acid. The further main step of modified carbon fibers preparation is sintering at 1200 °C in Ar atmosphere. The heat treatment process is responsible for carbon ladder matrix formation with incorporated Co 2 P nanoparticles (Streckova et al. 2018) . Cobalt phosphate nanoparticles have been incorporated into the carbon matrix in situ in the heat treatment process and act as the catalysts for CNT growth during sintering. The growth of CNT was performed according to the "Tip growth model" .

No additional surface modification was necessary. The used sintering conditions had a great influence on the morphology, porosity and growth of CNTs on the CF surface, which had a positive effect on the active surface area for HER. CNT growth was catalyzed by the presence of CoP nanoparticles. Fiber morphology and CNT growth were observed by SEM and TEM. The type of phosphides was determined by XRD, and the amount of Co in the fibers was determined by atomic absorption spectroscopy (AAS). The electrocatalytic activity of fibers and the effect on hydrogen evolution were analyzed using linear sweep voltammetry and Tafel slopes. The turnover frequencies (TOF) were calculated to further assess the electrocatalytic activity of two most active samples.

The solutions used to prepare the precursor fibers were composed of two polymers: polyacrylonitrile (PAN, Mw = 150 000 g.mol −1 , Sigma-Aldrich) and polyvinylpyrrolidone (PVP, Mw = 55000 g.mol −1 , Sigma-Aldrich). Phosphoric acid (H 3 PO 4 , Merck, 85%) was employed to enhance the viscosity and conductivity and hence, the spinnability of the precursor solution. Sodium dodecyl sulfate (SDS, Merck, 90%) was used as a surfactant to improve porosity. N,Ndimethylformamide (DMF, Acros Organic, 99.8%) was used as a solvent. Cobalt nitrate hexahydrate [Co(NO 3 ) 2 ·6H 2 O, Sigma-Aldrich, p.a.] was added as a source of Co nanoparticles. Electrochemical measurements were performed in 0.5 M sulfuric acid (H 2 SO 4 , Centralchem, 96%).

Precursor solutions were prepared by dissolving PAN, PVP, SDS and Co(NO 3 ) 2 in DMF for two hours at 80 °C. Then, H 3 PO 4 was added dropwise, and the solutions were stirred vigorously for another 1 h at 90 °C until homogenization was complete. The notation of the as-prepared CF samples with the composition of the precursor polymer solutions and the sintering exposure times at 1200 °C is given in Table 1 Carbon fibers (CFs) were prepared by needle-less electrospinning (NLES) using Nanospider™ NS LAB (Elmarco, Czech Republic) from precursor solutions. The precursor solutions were poured into a spinning bath (30 ml vessel and a rotating electrode), and the spinning distance between the electrodes was kept at 180 -190 mm. The rotation speed . 1 Schematic diagram of the needle-less electrospinning system (Yalcinkaya et al. 2016) of the spinning electrode was adjusted to 8 rpm, and a high voltage of 50 -60 kV was applied to the surface of the spinning drum. A schematic diagram of the needle-less electrospinning system is depicted in Fig. 1 (Yalcinkaya et al. 2016 ).

The heat treatment optimization of PAN-based fibers is the key factor, especially in such composite systems as modified CFs with cobalt phosphide nanoparticles (Rahaman et al. 2007 ). The sintering of the CFs was carried out at 1200 °C in Ar atmosphere in an open system (referred to as -o), which means free access of Ar into the sample with the possibility of releasing gases to the environment. Another way was sintering in a closed system (referred to as -c) where the gases originated during sintering process (H 2 , CO 2 , CO and Ar) stayed in the system and were prevented from escaping. The sintering time at the maximum temperature is referred to as "-t" (e.g., -0t means no exposure time, -1t means 1 h). The complete notation of the samples sintered in a closed and open system is summarized in (Table 1) .

Structural characterization of the prepared fibrous samples was done by XRD analysis (PhilipsX' PertPro, CuKα radiation). The morphology, size and shape of modified CFs were visualized by scanning electron microscope (SEM, JSM-7000F, JEOL, Japan) and transmission electron microscope (TEM, JEM-2100F, JEOL, Japan). Active surface area for HER was determined from adsorption/desorption isotherms using the NOVA 1200e Surface Area & Pore Size Analyzer (Quantachrome Instruments, USA). The values of specific surface area (S BET ) were determined by ethe Brunauer-Emmett-Teller method (S t ). Atomic absorption spectroscopy (AAS, Atomic Absorption Spectrometer PerkinElmer) was used to determine the cobalt content in the fibers. The Raman spectra were measured by the Raman spectroscopy (HORIBA -BX41TF).

The electrocatalytic HER performance was evaluated by linear sweep voltammetry (LSV) method in a three-electrode cell configuration connected to the Autolab potentiostat (PGSTAT302N, Metrohm, Switzerland) at ambient conditions. LSV measurements were performed in 0.5 M H 2 SO 4 aqueous solution at a scan rate of 1 mVs −1 in the potential range from + 600 mV to -1200 mV (vs. Ag/AgCl/3 M KCl). A silver chloride electrode (Ag/AgCl/3 M KCl) and a large area platinum foil were used as the reference and the counter electrode, respectively. All potentials were calibrated to a reversible hydrogen electrode (RHE). The carbon fibers in the form of carbon foam, used as compact electrode for electrochemical measurement, were weighted and directly used as working electrodes without further modification. All polarization curves were measured without IR correction.

The phase structure and crystallinity of carbon fibers modified by cobalt phosphides CFCo 0t-o, CFCo 0.5t-o, CFCo 1t-o, CFCo 0t-c with different heat treatment conditions were first identified by XRD. The obtained XRD pattern is shown in Fig. 2 

, (301), (020), (322), (314) planes,. The characteristic diffraction of graphite/graphene oxide (GO) peak at ~ 2Θ = 12.4° corresponding to the oxidation of the carbon structure and the formation of an oxygenated functional groups was identified (Johra et al. 2017; Kartick et al. 2013) . Increasing GO peak intensity was detected with increasing exposure time at high temperature (the order, starting from 

Bare carbon fibers were prepared from a mixture of PAN and PVP polymers in combination with SDS as a surfactant according to Table 1 . The use of these two immiscible polymers in combination with SDS led to the creation of micelle structure . Ionic surfactants play an important role in the fabrication of carbon-based fibers, because they facilitate the processability of carbon precursors and allow controlled alteration of carbon properties. It has been found that the microporosity of the electrospun carbon nanofibers is promoted in the presence of anionic sodium dodecyl sulfate (SDS) surfactant, regardless of whether metal particles are presented or not (Aykut et al. 2016 ). According to our previous studies , heat treatment and extraction of the micelles from the porous structure of PAN matrix is suitable for better penetration of the electrolyte during the HER process; therefore, the formed micelles were extracted at high carbonization temperatures.

Regarding the evolution of hydrogen during the polymer ladder building, two different ways of the carbonization process were studied. The first was the sintering process in an open system (CF 0t-o), where the precursor fibers were loosely carbonized and all by-products could evolve into the environment. The second one was realized in a closed system (CF 0t-c), where the fibers were carbonized in closed crucibles to prevent the release of hydrogen from the system, which also prevented the surface of the fibers being disturbed and thus, the porosity was increased. A comparison of the morphological characteristics of the two pure carbon fibers CF 0t-o and CF 0t-c calcined in an Ar atmosphere at 1200 °C is shown in the SEM images in Fig. 3 . The continuous fibrous structure was observed for CF 0t-o sample with a diameter of 1.2 to 2.5 µm with a fine wrinkled surface (Fig. 3a,b) . A lot of small spherical particles were dispersed outside and inside the carbon fibers, which were identified by EDX analysis as sodium phosphate particles created after the heat treatment process (Fig. 3c) . Figure 3d shows the structure of the sample sintered in the closed system. As evident, the accumulation of the heat and hydrogen (as a by-product of the PAN pyrolysis) in the fibrous environment led to the deterioration and collapse of the fibrous structure (Fig. 3d) . The closure of the system assumed accumulation and re-spilling of hydrogen into the carbon structure, which is expected to increase the porosity. However, the effect of hydrogen in a closed system is destructive and does not produce the desired fiber properties; in the case of bare carbon fibers, this is reflected a specific surface area as low as 13.5 m 2 /g.

Co 2 P phosphides belong to the family of materials, which enhance the electrocatalysis of hydrogen from water. CNTs increase the active surface area and support the conductivity of the final material. Therefore, the prepared bare CFs were subsequently modified with both Co 2 P nanoparticles and CNTs. It should be noted that Co 2 P nanoparticles were formed in carbon fibers spontaneously at high temperature and in an inert atmosphere from polymer precursor fibers containing Co(NO 3 ) 2 . Effect of the sintering temperature and time of exposure in the open system on the microstructure of (Fig. 4) . As can be seen, the continuous fibrous structure was maintained in all cases of different exposure times. The rough and wrinkled surface with a fiber diameter of 0.8 -3.9 µm contained Co 2 P nanoparticles densely distributed outside as well as inside the carbon fiber matrix (Fig. 4a,c,e) . SEM images at larger magnifications confirmed a homogeneous distribution of CNTs and Co 2 P nanoparticles (Fig. 4b,d,f) . Moreover, the presence of CNTs was observed on the surface of the samples, and their growth and amount were influenced by the sintering exposure time. As shown in Fig. 4 , sintering of CFs upon thermal exposure led to a reduction in the amount of CNTs and metal phosphide nanoparticles. A significant amount of CNTs was observed on the carbon surface matrix of the CFCo 0t-o sample (Fig. 4a,b) . TEM proved the growth of CNTs initiated by Co 2 P nanoparticles (zoom in Fig. 4b ). The prolonged time of exposure at high temperatures resulted in decrease CNT growth (Fig. 4c,d) . Due to the long exposure of heat treatment, the CNTs disintegrate and disappear, whereas agglomeration of Co 2 P occurs (Fig. 4e,f) .

The effect of the closed sintering system on the morphology of CFs modified by Co 2 P nanoparticles was also observed (Fig. 5) . By comparing of carbon fibers sintered in the open system, both samples exhibited fibrous structure, but the surface of CFCo0t-c was more wrinkled with irregular cylindrical structure and distribution of soft CNTs. TEM images confirmed the higher amount of thinner and finer CNTs (Fig. 5c ). Extending the time of heat treatment at 1 200 °C to 0.5 h led to the extinction of fine CNT fibers; therefore, it was not appropriate to further prolong the sintering time. The deteriorated fibrous structure indicated the possibility of an overall collapse of the carbon fibers as in the case of pure carbon fibers (Fig. 3) . A reduced amount of carbon nanotubes with extended sintering time is indicated in Fig. 5d . The CNT structure in CFCo 0t-o and CFCo 0t-c was confirmed by the Raman spectra (Fig. 6a,b) . Both CFCo 0t-o and CFCo 0t-c samples had D-, G-and 2D peaks characteristic of graphene-based materials, which confirms the presence of CNTs. Relatively high defect-activated Raman D peak indicates more disordered structure of CNTs. In addition, the small width of the 2D peak indicates the multilayer configuration of Co-initiated CNTs, as confirmed by (Fig. 6b) . The D to G peak intensity ratio (ID/IG) is often employed to evaluate the level of disorder in CNTs. The lower ID/IG value (0.62) for the CFCo 0t-c sample indicates that the closure of the system led to a more ordered structure with higher amount of thinner CNTs. The mechanism of CNTs growth has been previously discussed by many other authors; however, the upraise of CNTs in situ by affecting temperature is very rare (Kumar and Ando 2010; Pérez-Cabero et al. 2004; Zhao et al. 2006; Yuan et al. 2003; Mo et al. 2001; Vinciguerra et al. 2003) . As mentioned in the authors' previous work, Co and Co 2 P nanoparticles can initiate the growth of CNTs as described in the "tip growth model" . The suggested mechanism of growth and deterioration of carbon nanotubes affected by the prolongation of exposure times at 1200 °C is depicted in Scheme 1. First, the high temperature causes the growth of CNTs that has been catalyzed by Co 2 P nanoparticles immersed on the surface of CFs. The prolonged exposure time causes the falling out of Co 2 P nanoparticles and degradation of carbon nanotubes. Finally, long exposure at the high temperature leads to the aggregation of Co 2 P nanoparticles on the surface of carbon matrix and the subsequent penetration of Co 2 P nanoparticles into the interior of the fibers. The collapse of CNTs is evident.

The chemical composition of Co 2 P nanoparticles encapsulated in the carbon matrix was proved by the EDX mapping analysis shown in Fig. 7 . It is evident that the 

The HER activity measurements were carried out in an acidic medium of 0.5 mol.dm −3 H 2 SO 4 using a three-electrode system. The electrocatalytic activity of carbon fibers was evaluated electrochemically on a compact fibrous sample. The fibers were not affected in any way prior to measurements to preserve the porosity, structure of CNTs and active sites for HER. The structure of fibers was maintained during the measurements. The HER activity of all studied fibrous samples was derived from the values of electrocatalytic activity parameters, such as onset potential (E onset ), overpotentials to achieve cathodic current density of 10 mAcm −2 (η10) and 20 mAcm −2 (η20), exchange current density (j 0 ) and Tafel slope (b) calculated from LSV curves. The data are summarized in Table 2 . As can be seen in Fig. 8 ., the polarization curves revealed that the catalyst CFCo 0t-c produced in the closed sintering system without exposure exhibits the highest HER activity with the overpotential of -280.86 mV at the cathodic current density of 10 mA.cm −2 (η 10 ) and -380.99 mV at the cathodic current density of 20 mA.cm −2 (η 20 ) (Fig. 8) . In contrast, catalysts prepared in the open system exhibit higher overpotentials with prolonged time of exposure at high temperatures. The worse HER performance of the samples sintered in the open system at longer exposure times could be associated with agglomeration of Co 2 P nanoparticles and degradation of CNTs, resulting in lower active surface area (only55 m 2 /g for the CFCo 1t-o sample). The catalyst without active cobalt phosphide nanoparticles CF 0t-o exhibits the lowest electrocatalytic activity among all studied samples, which is in good agreement with previous studies . The poor HER activity of bare CFs indicates that incorporation of Co 2 P nanoparticles into samples significantly enhances the catalytic activity, which may be related to the fact that the Co 2 P nanoparticles present in the fibers not only catalyze HER but also initiate the growth of CNTs. Tafel slopes (Fig. 9) were calculated using Tafel plots derived from the polarization curves. Smaller Tafel slope usually corresponds to a steep rise of the electrocatalytic current density and indicates a fast reaction rate. The lowest values of Tafel slopes were obtained for catalysts fabricated in the closed system without exposure at high temperature (b = 67.03 and 73.15 for CFCo 0t-c and CFCo 0t-o, respectively). This indicates that HER took place via Volmer and Heyrovsky pathway. A long-term stability test was performed to assess the stability and durability of the best-performing CFCo fibers produced with zero time of exposure in closed and open systems (CFCo 0t-c, CFCo 0t-o). The undeniable stability of these samples can be seen from the time-dependent current density curves (Fig. 10) for a static overpotential of 200 mV and a catalytic activity sustained for over 22 h.

The turnover frequencies (TOF) were calculated to further assess the electrocatalytic activity of two the most active samples (CFCo 0t-o and CFCo 0t-c). TOF estimation for the HER in 0.5 M H 2 SO 4 was performed conceding that each individual Co and P atom on the outermost surface layer is a potentially active site due to the vagueness of the hydrogen binding sites Chen et al. 2014) . Both theoretical and experimental surface areas were used for TOF calculations. Experimental surface areas were derived from S BET values, supposing that the surface area of Co 2 P nanoparticles represents 10% and 12% of experimentally determined surface area for CFCo 0t-o and CFCo 0t-c samples, respectively, based on the Co content (Table 2) . Theoretical surface areas were calculated assuming 70 nm (d) spherical Co 2 P particles. The TOF values for CFCo 0t-c sample calculated utilizing the theoretical surface area are 67.77 s −1 at η = 100 mV and 91.41 s −1 at η = 200 mV. The TOF values estimated for this sample using experimental surface area are 73.73 s −1 at η = 100 mV and 99.45 s −1 at η = 200 mV. The TOFs obtained by both methods are in good agreement. The TOF values for CFCo 0t-o sample determined by use of the theoretical surface area are 9.46 s −1 at η = 100 mV and 12.96 s −1 at η = 200 mV, and TOFs calculated from experimental surface area are 3.87 s −1 at η = 100 mV and 4.11 s −1 at η = 200 mV. The obtained TOF values represent only an approximation of the real TOFs, as the actual hydrogen binding sites are not exactly identified. However, it is possible to conclude that the intrinsic catalytic activity of the CFCo 0t-c sample is about 10 times higher than the activity of the CFCo 0t-o catalyst. The obtained TOF values proved the beneficial effect of the use of a closed sintering system during the production of the catalyst on its catalytic activity.

In summary, carbon micro-fibers modified with Co 2 P nanoparticles and decorated by CNTs were prepared by needle-less electrospinning technique. As expected, after optimization of sintering conditions and the structural and compositional metrics, carbon fibers with cobalt phosphides sintered in closed systems exhibited better electrochemical performance for HER than bare carbon fibers or carbon fibers with cobalt phosphides sintered freely. On the other hand, carbon fibers sintered in open system without prolonged exposure time at the 1200 °C showed better electrochemical activity than the same carbon fibers held in the furnace at high temperature for longer time. More specifically, fibers CFCo 0t-c calcined in the closed system require an overpotential of -280 mV to afford a current density of 10 mA.cm −2 with a low Tafel slope of 67.03 mV.dec −1 , while the samples CFCo 0t-o calcined in the open system showed the overpotential of -345.07 mV for the same current density with the Tafel slope of 73.15 mV.dec −1 . Both electrodes exhibit excellent stability under operating conditions.

Supercapacitors using single-walled carbon nanotube electrodes

Infrared spectra and density functional theory calculations on transition metal nitrosyls, Vibrational frequencies of unsaturated transition metal nitrosyls

Effects of surfactants on the microstructures of electrospun polyacrylonitrile nanofibers and their carbonized analogs

Logic Circuits with

Monodisperse multiwall carbon nanotubes obtained with ferritin as catalyst

Synthesis of uniform diameter single-wall carbon nanotubes in Co-MCM-41: effects of the catalyst prereduction and nanotube growth temperatures

Synthesis of uniform diameter single wall carbon nanotubes in Co-MCM-41: Effects of CO pressure and reaction time

The effect of the cobalt loading on the growth of single wall carbon nanotubes by CO disproportionation on Co-MCM-41 catalysts

Molybdenum phosphide: a new highly efficient catalyst for the electrochemical hydrogen evolution reaction

Global Energy Review 2020, IEA, Paris, The impacts of the Covid-19 crisis on global energy demand and CO 2 emissions

A general scheme for the estimation of oxygen binding energies on binary transition metal surface alloys

Porous carbon fibers for effective hydrogen evolution

Production of nanotubes by the catalytic decomposition of different carboncontaining compounds

Helical microtubules of graphitic carbon

Carbon nanofibers prepared via electrospinning

Recent Advances in Nanofibre Technology

Facile and safe graphene preparation on solution based platform

Green synthesis of graphene

Designing an improved transition metal phosphide catalyst for hydrogen evolution using experimental and theoretical trends

First-row transition metal dichalcogenide catalysts for hydrogen evolution reaction

Future energy systems: Integrating renewable energy sources into the smart power grid through industrial electronics

Large-scale synthesis of high-quality double-walled carbon nanotubes by catalytic decomposition of n-Hexane

The growth mechanism of carbon nanotubes from thermal cracking of acetylene over nickel catalyst supported on alumina

Electrospinning: an advanced nanofiber production technology electrospinning: an advanced nanofiber production technology. In: Energy harvesting properties of electrospun nanofibers

Trends in the Exchange Current for Hydrogen Evolution

Growing mechanism of CNTs: a kinetic approach

A review of heat treatment on polyacrylonitrile fiber

Recent advances in transition metal phosphide nanomaterials: synthesis and applications in hydrogen evolution reaction

Social acceptance of renewable energy sources: a review of contingent valuation applications

Nickel and nickel phosphide nanoparticles embedded in electrospun carbon fibers as favourable electrocatalysts for hydrogen evolution

Design of electroactive carbon fibers decorated with metal and metal-phosphide nanoparticles for hydrogen evolution technology

Novel electrocatalysts for hydrogen evolution based on carbon fibers modified by cobalt phosphides

Growth mechanisms in chemical vapour deposited carbon nanotubes

Predicted Trends of Core−Shell Preferences for 132 Late Transition-Metal Binary-Alloy Nanoparticles

Assembly of highly organized carbon nanotube architectures by chemical vapor deposition

Co-based catalysts from Co/Fe/Al layered double hydroxides for preparation of carbon nanotubes

Dependent and Independent Parameters of Needleless Electrospinning. Electrospinning -Material, Techniques, and Biomedical Applications, Sajjad Haider and Adnan Haider

Growth mechanism of carbon nanotubes in methane diffusion flames

Recent advances in heterogeneous electrocatalysts for the hydrogen evolution reaction

Progress and Perspective of Electrocatalytic CO 2 Reduction for Renewable Carbonaceous Fuels and Chemicals

Fabrication and growth mechanism of carbon nanotubes by catalytic chemical vapor deposition

Recent developments of carbon-based electrocatalysts for hydrogen evolution reaction

Direct synthesis of long single-walled carbon nanotube strands