key: cord-0886303-3zi6wix9 authors: Skotadis, Evangelos; Kanaris, Aris; Aslanidis, Evangelos; Kalatzis, Nikos; Chatzipapadopoulos, Fotis; Marianos, Nikolaos; Tsoukalas, Dimitris title: Identification of Two Commercial Pesticides by a Nanoparticle Gas-Sensing Array date: 2021-08-28 journal: Sensors (Basel) DOI: 10.3390/s21175803 sha: 9cc354839a3234e060360cad32f1f5e105f8034f doc_id: 886303 cord_uid: 3zi6wix9 This study presents the experimental testing of a gas-sensing array, for the detection of two commercially available pesticides (i.e., Chloract 48 EC and Nimrod), towards its eventual use along a commercial smart-farming system. The array is comprised of four distinctive sensing devices based on nanoparticles, each functionalized with a different gas-absorbing polymeric layer. As discussed herein, the sensing array is able to identify as well as quantify three gas-analytes, two pesticide solutions, and relative humidity, which acts as a reference analyte. All of the evaluation experiments were conducted in close to real-life conditions; specifically, the sensors response towards the three analytes was tested in three relative humidity backgrounds while the effect of temperature was also considered. The unique response patterns generated after the exposure of the sensing-array to the two gas-analytes were analyzed using the common statistical analysis tool Principal Component Analysis (PCA). The sensing array, being compact, low-cost, and highly sensitive, can be easily integrated with pre-existing crop-monitoring solutions. Given that there are limited reports for effective pesticide gas-sensing solutions, the proposed gas-sensing technology would significantly upgrade the added-value of the integrated system, providing it with unique advantages. In the field of pesticide detection, pollutants are usually identified and quantified via analytical methods and techniques such as chromatographic and coupled chromatographicspectrometric procedures [1, 2] or electroanalytical/voltammetric techniques [3] ; bupirimate as well as chlorpyrifos are usually quantified using all aforementioned methods. The need, however, for fast, remote, and automated in-the-field determination of pesticides is increasing. Miniaturized, cost-effective, low-power, and sensitive sensors are in high demand, with the main technologies in the field of pesticide detection being Electrochemical, optical, and piezoelectric biosensors [4] [5] [6] as well as molecularly imprinted polymer sensors [7] . Gas-sensing of environmental pollutants is also on the rise since gas-sensors in general fulfil all of the aforementioned criteria by usually being low cost, compact, accurate, fast, and able to simultaneously determine multiple gas-analytes, and, contrary to most biosensors, they show reversible responses to their gas-target, thus making them reusable. The majority of the available solutions for gas-sensing of environmental pollutants deal with metal oxide sensors, which typically operate in elevated temperatures. Many solutions have been proposed if the field of micro and Nano gas-sensors in particular, where different nanomaterials have been discussed as potential active materials for gas-sensing. Sensors employing metal oxide semiconductors (MOS) usually rely on p-type or n-type MOS materials fabricated in the nanoscale [8] . Sensors based on Carbon Nanotubes (CNT) are a identification, and quantification of two commercially available pesticides (Nimrod and Chloract 48 EC) over the ever-present in any farming application R.H. In addition, the current study highlights the challenges that the proposed system should overcome, towards its implementation in the field. Previous attempts in detecting pesticide vapours have resulted in successful active ingredient identification (chlorpyrifos) over its solvent for a laboratory prepared standard solution [28] . Results discussed herein showcase the capacity of the array in detecting and differentiating between all three gas-analytes (two of which are commercial pesticides), by optimizing environmental conditions such as R.H. and temperature and employing a common statistical analysis tool (i.e., principal component analysis (PCA)). In addition, instead of initializing and operating the sensors in a close to "zero-humidity" environment as in previously reported results [24] [25] [26] [27] [28] , the sensors are now tested in elevated R.H., in an effort to facilitate their incorporation in commercial crop-monitoring systems for actual in-the-field applications. The hybrid polymer/nanomaterial-based device is ultimately optimized towards the detection of 2 commercially available pesticides at room temperature, proving that it can successfully identify and quantify between three gas targets; the proposed gas-sensing technology could therefore evolve to an e-nose system capable of separating between an expanded number of available gas targets and environmental pollutants. It's also worth noting that, to the authors' knowledge, there are no reports on the gas detection of any of the two commercially available pesticides, while, as far as Nimrod and bupirimate are concerned (Nimrod's active ingredient), there are no reports on its detection, regardless of the choice in sensing technology (analytical methods aside). Given the overall scarcity of available publications in the field of pesticide gas sensing as well as the array's important advantages related to competing gas-sensing technologies (reusable, fast, reversible, highly sensitive, cost-effective, low-power, and reliable), the proposed device is a unique solution that is also suitable for easy integration in commercial, advanced, and remote monitoring systems. The chemical sensing array combines two-dimensional (2D) conductive metallic nanoparticle (NP) films and gas-sensitive polymeric films. The NP layer of the device is responsible for its conductivity while the polymer films, being susceptible to volatile organic compounds (VOCs), act as the gas-sensitive layer. Device fabrication begins by patterning oxidized silicon substrates with gold interdigitated electrodes (IDEs). IDEs are patterned by employing photolithography and the e-gun deposition of 5 nm of Ti (acting as an adhesion layer) and 30 nm of gold; IDEs inter-finger spacing has been selected to be 10 µm. As a second step, Pt NPs are deposited and fabricated in a single step on top of the silicon substrates, utilizing the DC sputtering technique, as described in previous publications by this group [24, 26] . The surface coverage of the devices reported in the current paper has been selected for optimized device-sensitivity (devices with a mean resistance in the range of 700 kΩ). It is important to note that all fabrication steps were performed at room temperature (25 • C). Device fabrication was finalized by spin-coating 4 distinctive polymers on top of the Pt functionalised substrates. Polymeric solutions were prepared using the following materials that were bought from Merck: poly (ethyl methacrylate) (PEMA), poly (2-hydroxyethyl methacrylate) (PHEMA), poly (isobutyl methacrylate) (PIBMA), and poly (butyl methacrylate) (PBMA). The selection of the polymeric materials was based on their performance regarding the detection of a laboratory synthesized Chlorpyrifos solution [28] . All polymers were bought as powders and have been fabricated using a high precision micro-balance; PGMEA and methanol have been used as solvents for PEMA, PIBMA, PBMA, and PHEMA, respectively. As a final step, the fabricated polymeric solutions were spin-coated on top of the device-substrates in order to obtain a polymeric film of 500 nm in thickness. Film thickness has been confirmed via profiling measurements. Two commercially available pesticides were purchased from a local agricultural supply store and used as target gases in the current study: Chloract 48 EC and Nimrod. Chloract 48 EC solution, a chlorpyrifos (CPS) based insecticide, was used according to Sensors 2021, 21, 5803 4 of 12 its respective guidelines; for general use in crops, it is recommended that 100-250 c.c. of Chloract should be used per acre. It is also recommended that 65 L of Chloract solution (with water as a solvent) must be used per acre. All experiments in the current paper used a Chloract test-solution that was fabricated as follows: 175 c.c. of Chloract in 65 L of water. Our finalized Chloract-test solutions were 50 mL in volume, containing 0.081 c.c. of Chloract; this results in a Chloract test-solution composition of 0.12% CPS, 0.15% auxiliary substances, and 99.73% water (according to the manufacturer's documentation). Nimrod solutions (a bupirimate-based fungicide) were also prepared according to the manufacturer's guidelines; specifically, 250 c.c. of Nimrod should be used for 100 L of Nimrod/water solution, while 75 L of the finalised Nimrod/water solution should be used per acre. A Nimrod solution of 50 mL was used throughout the following experiments, corresponding to 0.125 c.c. of Nimrod. According to Nimrod documentation, its actual synthesis corresponds to 27.5% bupirimate, while the rest corresponds to auxiliary substances. This translates to a solution that is 0.069% bupirimate, 0.18% auxiliary substances, and 99.75% H 2 O in concentration. All gas-sensing experiments were conducted in the gas-sensing characterization setup that is available at the School of Applied Physics of the NTUA; a schematic of the specific setup used for the gas-sensing experiments is provided in Figure 1 . Notably, the sensors are exposed to varying concentrations of one of the two pesticides/analytes vs. humidity. Specifically, 50 mL of either Chloract or Nimrod test-solutions were placed inside Bubbler 3, while 50 mL of DI water (reference analyte) were placed inside bubbler 2. Their respective vapours were collected by feeding the bubblers with a separate Nitrogen gas-line, externally controlled by two Nitrogen Mass Flow Controllers (MFCs). The Nitrogen gas-flow can be directed in either bubbler (2 or 3), by opening the respective valves (V2 and V3), as demonstrated in Figure 1 . Chlorpyrifos or bupirimate solutions were prepared according to the manufacturer's guidelines; the composite gas-mixture that is eventually introduced inside the sensing-array's measuring chamber has a composition that depends on the partial vapour pressures of each solution-ingredient (water, auxiliary substances, and chlorpyrifos or bupirimate). In order to calculate the actual concentration of each activeingredient (chlorpyrifos or bupirimate), Raoult's law was employed (a good approximation for dilute solutions). In order to apply Raoult's law effectively, the partial vapour pressure of each substance inside the water-mixtures must be known. However, in the case of proprietary commercial pesticides, there is a great number of unknown auxiliary substances whose vapour pressure needs to be approximated; herein, we have approximated the vapour pressure of the auxiliary substances with p-xylene, which is a common solute for pesticides [29] . Varying concentrations of Chloract, Nimrod, or humidity (corresponding to varying Nitrogen flow-rates) were superimposed over a continuous background-flow of nitrogen and humidity (originating from Bubbler 1), which eventually flowed inside the sensors' measurement chamber. The purpose of the background-flow is to create a stable, artificial atmosphere of constant relative humidity (R.H.) so as to record the performance of the sensing-array in realistic conditions. R.H. is an ever-present "background" gas in any greenhouse and farming environment; any sensing-array that aspires to successfully detect pesticides and other environmental pollutants in the gaseous state should be able to distinguish such pollutants from any other gas over a constant background value of environmental R.H. For all experimental results reported in this paper, a comparison of the sensing-array's response between Chloract, Nimrod, and humidity has been conducted. This comparison was for identical carrier-gas (Nitrogen) flows. For the sensors' packaging, a small volume plastic chamber was 3D printed, ensuring efficient isolation between the sensing array and its environment; ultimately, R.H. was controlled within 0.1% and temperature within 0.1 • C. A commercial sensor was also used to track R.H. and temperature inside the array's packaging, while the array's resistance was monitored using a Keithley 2400 multimeter. Finally, that identical nitrogen flows of each pesticide and R.H. were introduced successively and in alternating order inside the sensing-array chamber (e.g., the introduction of the array's packaging, while the array's resistance was monitored using a Keithley 2400 multimeter. Finally, that identical nitrogen flows of each pesticide and R.H. were introduced successively and in alternating order inside the sensing-array chamber (e.g., the introduction of 32 mL/min of a pesticide analyte would be followed by the introduction of 32 mL/min of R.H. or vice versa). Schematic of the experimental gas-sensor characterization setup, for the detection of Chlorpyrifos and Bupirimate (chemical structure as shown herein). Three mass flow controllers (MFCs) are responsible for distributing the carrier-gas (N2) within the system. The MFCs are controlled via a PC and a Labview program; the same PC records the output (resistance) of the sensors via a home-made software. A schematic of the four interdigitated electrodes functionalised with four distinctive thin-polymer films (gas-sensing array), as well as a TEM image of the Pt NP film, are also included. The idea behind hybrid NP/polymer-based sensors has been discussed extensively by this group in previous publications, where humidity and other VOCs (including CPS) have been successfully detected [24] [25] [26] [27] [28] . Furthermore, the sensors have been optimized in relation to all available fabrication parameters (i.e., IDEs geometry, NP surface coverage, device conductivity etc.); the devices discussed in the current paper were fabricated according to previous optimization studies [24, 26] . Such sensors rely on the polymer layer for interacting with any VOC in the vicinity of the sensor; this interaction in turn modifies the conductivity (or resistance) of the NP layer. The four polymers selected in the current study are susceptible to most VOC and partially selective; by absorbing gaseous compounds, the polymer films begin to swell and therefore induce a strain in the underlying NP layer. This strain ultimately translates to an increase in the average inter-particle distance and, hence, an increase in the resistance of the device. One must bear in mind that the poor selectivity of all polymer coatings is an inherent disadvantage that is prominent when sensing composite gas mixtures. This partial selectivity leads to increased confusion over the identity of the measured gas target. However, such obstacles can usually be surpassed by employing statistical analysis techniques such as principal component analysis (PCA), which is commonly used for analysing gas-sensing responses for composite gas mixtures [30, 31] . Previous publications regarding the detection of CPS vapours have focused on an analytical approach that investigated the sensors' ability to detect the active ingredient (namely CPS) of a laboratory-synthesized, CPS based standard solution [28] . More recent results have reported on the detection of a commercially available CPS product [29] , Figure 1 . Schematic of the experimental gas-sensor characterization setup, for the detection of Chlorpyrifos and Bupirimate (chemical structure as shown herein). Three mass flow controllers (MFCs) are responsible for distributing the carrier-gas (N 2 ) within the system. The MFCs are controlled via a PC and a Labview program; the same PC records the output (resistance) of the sensors via a home-made software. A schematic of the four interdigitated electrodes functionalised with four distinctive thin-polymer films (gas-sensing array), as well as a TEM image of the Pt NP film, are also included. The idea behind hybrid NP/polymer-based sensors has been discussed extensively by this group in previous publications, where humidity and other VOCs (including CPS) have been successfully detected [24] [25] [26] [27] [28] . Furthermore, the sensors have been optimized in relation to all available fabrication parameters (i.e., IDEs geometry, NP surface coverage, device conductivity etc.); the devices discussed in the current paper were fabricated according to previous optimization studies [24, 26] . Such sensors rely on the polymer layer for interacting with any VOC in the vicinity of the sensor; this interaction in turn modifies the conductivity (or resistance) of the NP layer. The four polymers selected in the current study are susceptible to most VOC and partially selective; by absorbing gaseous compounds, the polymer films begin to swell and therefore induce a strain in the underlying NP layer. This strain ultimately translates to an increase in the average inter-particle distance and, hence, an increase in the resistance of the device. One must bear in mind that the poor selectivity of all polymer coatings is an inherent disadvantage that is prominent when sensing composite gas mixtures. This partial selectivity leads to increased confusion over the identity of the measured gas target. However, such obstacles can usually be surpassed by employing statistical analysis techniques such as principal component analysis (PCA), which is commonly used for analysing gas-sensing responses for composite gas mixtures [30, 31] . Previous publications regarding the detection of CPS vapours have focused on an analytical approach that investigated the sensors' ability to detect the active ingredient (namely CPS) of a laboratory-synthesized, CPS based standard solution [28] . More recent results have reported on the detection of a commercially available CPS product [29] , where the sensors have been always tested in a laboratory "zero-humidity" environment. In that case, a constant background Nitrogen flow of 1000 mL/min was applied inside the gas-measuring chamber, keeping R.H. close to 0% according to a commercial R.H. sensor; any other target-analyte had to be superimposed on-top of this constant Nitrogen flow. On the other hand, results discussed herein show the response of the sensing array in close to actual in-the-field conditions, where R.H. is not close to a "zero-humidity" environment. This especially holds true for greenhouse applications as well as in open crops. The sensors were initially tested in four different R.H. backgrounds (10%, 20%, 30%, and 40%). After calibrating the sensors towards background R.H., the sensingarray was submitted to a constant R.H. background and introduced to a range of varying concentrations of two commercially available pesticides (Chloract 48 EC and Nimrod) with different active ingredients (CPS and bupirimate, respectively). Each of the two pesticides has been also compared to varying concentration of R.H. (by successively feeding bubblers 2 and 3 with identical Nitrogen flows, as illustrated in Figure 1) ; specifically, the nitrogen flow-rate values that were employed to achieve R.H. concentrations in the range of 50-80% were also used in the case of Chloract and Nimrod solutions. In addition to the above, the sensors have also been tested in three different temperatures (20, 25 , and 30 • C) so as to investigate the effect of temperature in sensor performance. For all experiments discussed below, twenty sensors have been employed in total (five for each distinctive polymeric coating). In order to study the effect of background humidity on sensor response, the sensingarray was tested in four different humidity backgrounds: 10%, 20%, 30%, and 40% of R.H; the temperature was kept constant at 25 • C. It has been suggested in previous publications that polymer-based R.H. chemo-resistors should incorporate polymers that are insoluble in water but sensitive to humidity [32] ; this can be achieved through graft-polymerization of porous polymer films or through the formation of an interpenetrating polymer network of cross-linked hydrophilic and hydrophobic polymers. The degree of cross-linking can also play an integral role in sensor resistance towards water and its overall performance [33] ; by using appropriate solutes and cross-linking polymer films in elevated temperatures, durable and robust humidity sensors can be produced. For each of the four R.H. backgrounds, the nitrogen gas flows feeding the pesticide or the DI water bubbler were selected so that, when combined with the background R.H., a total R.H. of 50%, 60%, 70%, and 80% would be achieved. For this series of experiments, only one of the two gas target-analytes, namely Nimrod, was used. In Figure 2a , the transient sensing response of a single PEMA coated sensor in Nimrod and R.H, for 20% and 30% R.H. backgrounds, is presented; the sensor's response is typical, resembling the response of PHEMA, PBMA, and PIBMA coated sensors. For all polymeric coatings, the sensors systematically demonstrate an increased response towards the Nimrod solution. In Figure 2b ,c, the ∆R/R 0 (%) response of all 5 PEMA sensors in Nimrod and R.H., for 4 different R.H. backgrounds, is presented. By increasing the R.H. background, the response of the gas-sensing array for both pesticide analytes (measured as ∆R/R 0 %, where R 0 is the resistance of the sensor prior to its exposure to any gas target concentration) is reduced. Figure 2a clearly demonstrates that, by increasing the background R.H. from 20% to 30%, the baseline resistance of the sensors is increased; this in turn translates to a reduced response to any of the gas analytes. The change in R.H. background also affects the sensors' differentiation between Nimrod and R.H., making the R.H. background of 20% the one for maximum separation (Figure 2b,c) . It is envisioned that the eventual integration of the sensing-array in a smart-farming tool will be accompanied by commercial humidity sensors as well as air-drying solutions (e.g., membrane air drying, vacuum drying etc.) in order to control ambient conditions inside the array's packaging. Air drying solutions should be examined in parallel with the packaging development of the array. A feedback loop that will monitor the R.H. inside the packaging via commercial R.H. sensors will be able to provide an environment of 20% R.H. by mixing ambient air with partially dried air. the packaging via commercial R.H. sensors will be able to provide an environment of 20% R.H. by mixing ambient air with partially dried air. As a second step, the effect of temperature on sensing performance has been studied. The sensing array has been exposed to humidity and one of the target analytes of the study (i.e., Nimrod) in three different temperatures: 20, 25, and 30 °C. It is worth noting that our experimental setup can provide temperatures between 20 and 30 °C. Results provided in paragraph 3.1 regarding the effect of ambient R.H. in sensing performance were also taken into account: background R.H. was adjusted to 20% throughout this study (maximum Nimrod to R.H. differentiation). Additionally, the DI water and Nimrod bubblers were fed with Nitrogen flows that are equivalent to R.H. values between 50% and 70%; the acquired data set was adequate so as to establish the effect of temperature on sensor response. As demonstrated in Figure 3 , and for all polymeric coatings, a rise in temperature also signals a rise in sensitivity of the sensors. A change in the response of the sensors is to be expected since the nanoparticle-based sensors discussed in this study were designed for optimum sensitivity, which corresponds to specific nanoparticle surface coverage and therefore device resistance. Optimized devices feature nanoparticle surface coverage that Relative resistance response (measured as ∆R/R0) for PEMA coated sensors and in four different R.H. backgrounds (backgr.). Data points correspond to the mean response of five sensors, while standard deviations are presented as error bars (from 0.56% to 0.87%). (c) Typical relative resistance response for PIBMA sensors, focusing on 2 R.H. backgrounds (20% and 30%). Data points correspond to the mean response of five sensors, while standard deviations are presented as error bars (0.61% to 0.94%). Linear fitting was performed and is presented as dashed lines. The adjusted R-square value for the linear fit regression was found to be between 0.98926 and 0.99559. As a second step, the effect of temperature on sensing performance has been studied. The sensing array has been exposed to humidity and one of the target analytes of the study (i.e., Nimrod) in three different temperatures: 20, 25, and 30 • C. It is worth noting that our experimental setup can provide temperatures between 20 and 30 • C. Results provided in paragraph 3.1 regarding the effect of ambient R.H. in sensing performance were also taken into account: background R.H. was adjusted to 20% throughout this study (maximum Nimrod to R.H. differentiation). Additionally, the DI water and Nimrod bubblers were fed with Nitrogen flows that are equivalent to R.H. values between 50% and 70%; the acquired data set was adequate so as to establish the effect of temperature on sensor response. As demonstrated in Figure 3 , and for all polymeric coatings, a rise in temperature also signals a rise in sensitivity of the sensors. A change in the response of the sensors is to be expected since the nanoparticle-based sensors discussed in this study were designed for optimum sensitivity, which corresponds to specific nanoparticle surface coverage and therefore device resistance. Optimized devices feature nanoparticle surface coverage that lies just below the percolation threshold, while their conductivity is governed by a thermally activated tunneling mechanism [29] . A rise in temperature is expected to contribute to a drop in resistance, which was validated in the results discussed herein. However, the increase in sensitivity observed in Figure 3 should be mainly attributed to the polymeric coatings. Various reports indicate that polymers increase in terms of hole-free volume (volume stemming from volume relaxation and plasticization upon heating and cooling of the polymer and accessible for penetrant transport) for increasing temperature [34] ; in addition, the diffusion coefficient for polymers increases for increasing temperature [35] . The overall increase in the swelling of the polymer coatings (temperature as well as vapour induced), as well as enhanced diffusion, translates to increased sensor response, in accordance with our already reported gas-sensing mechanism. The time needed for reaching 70% of equilibrium state (mean response time) for all 16 sensors, was 17 s. A quasi-linear response towards Nimrod was recorded for all sensors, while the minimum detectable change in R.H. gas analytes (sensors' resolution) was 0.48% (or 150 ppm). Finally, experimental results suggest that for 20 • C the sensors exhibit maximum differentiation in terms of sensing response for the two analytes (Nimrod and humidity). Controlling the temperature of a small footprint sensing array (single sensor dimensions are 1 mm by 0.8 mm) can be achieved using thermoelectric modules [36] ; such modules can operate as heat pumps, providing heating or cooling of an object connected to one side of a thermoelectric module if a DC current is applied to the module's input terminals, and are widely used in MEMS technology. lies just below the percolation threshold, while their conductivity is governed by a thermally activated tunneling mechanism [29] . A rise in temperature is expected to contribute to a drop in resistance, which was validated in the results discussed herein. However, the increase in sensitivity observed in Figure 3 should be mainly attributed to the polymeric coatings. Various reports indicate that polymers increase in terms of hole-free volume (volume stemming from volume relaxation and plasticization upon heating and cooling of the polymer and accessible for penetrant transport) for increasing temperature [34] ; in addition, the diffusion coefficient for polymers increases for increasing temperature [35] . The overall increase in the swelling of the polymer coatings (temperature as well as vapour induced), as well as enhanced diffusion, translates to increased sensor response, in accordance with our already reported gas-sensing mechanism. The time needed for reaching 70% of equilibrium state (mean response time) for all 16 sensors, was 17 s. A quasilinear response towards Nimrod was recorded for all sensors, while the minimum detectable change in R.H. gas analytes (sensors' resolution) was 0.48% (or 150 ppm). Finally, experimental results suggest that for 20 °C the sensors exhibit maximum differentiation in terms of sensing response for the two analytes (Nimrod and humidity). Controlling the temperature of a small footprint sensing array (single sensor dimensions are 1 mm by 0.8 mm) can be achieved using thermoelectric modules [36] ; such modules can operate as heat pumps, providing heating or cooling of an object connected to one side of a thermoelectric module if a DC current is applied to the module's input terminals, and are widely used in MEMS technology. As a final step, the sensing array has been examined as a potential "e-nose" for discerning between Nimrod, Chloract 48 EC, and R.H. The ability of the array to discern between CPS (Chloract's active ingredient) and its solvent [21] , as well as between a commercial CPS product and R.H. in a close to "zero R.H. environment" was demonstrated in the past by this group [29] . However, the ability of the array to discern between two commercially available pesticides and R.H. in elevated levels of background R.H. is an even more challenging task. In Figure 4a, to a total R.H of 22%, as illustrated in Figure 4d . This flow rate corresponds to a humidity concentration of 500 ppm (and a R.H. of 2%), a chlorpyrifos concentration of 10.9 ppb, and a bupirimate concentration of 9 ppb (approximated using Raoult's law, as described in Section 2). A hybrid gas-sensing array based on platinum nanoparticles and functionalized with four distinctive polymeric films, was tested as a potential "e-nose" for detecting, quantifying, and separating between two commercially available pesticides (Nimrod and Chloract 48 EC) and relative humidity (R.H.). The effect of environmental parameters such as The successful operation of a gas-sensing array as a potential e-nose system lies in the ability of the distinctive sensing devices to produce unique response patterns. The gas-sensitive elements of this device are the four polymeric coatings; each coating is characterized by its own unique diffusion rate, hence the swelling towards separate analytes [37] . In this way, unique gas sensing patterns are generated. However, the capability of the array to differentiate between various gas targets, as well as to quantify them, can only be validated by implementing statistical analysis tools or pattern recognition algorithms in the post-processing of the array's read-out. Principal component analysis (PCA) is a statistical tool commonly used to analyze the output of gas-sensing arrays [30, 31] to discriminate between target analytes in a composite gas mixture. To that end, PCA has been applied over our existing data-set (array's response to Nimrod, Chloract 48 EC, and R.H.), in an effort to validate its use as a potential "e-nose" system. In Figure 4 , PCA results are provided after the array's response to Chloract vs. R.H., Nimrod vs. R.H., as well as Chloract vs. Nimrod vs. R.H., respectively, always in the presence of a fixed R.H. background of 20% and for a temperature of 20 • C. PCA of the array's response results, using only 2 or 3 distinctive polymeric coatings, was also executed in all possible combinations; this revealed that a necessary condition for successful PCA separation between R.H. and Chloract is to include in the PCA the response of PHEMA coated sensors, while in the case of Nimrod: PEMA coated sensors. PHEMA and PEMA must be included in the PCA for successful separation between the analytes when applying the method in data-sets originating from the response of two or three polymeric films. By including the response of all four polymeric coatings, PCA results in even better separation between the analytes; Figure 4 illustrates this by introducing three target analytes on top of the fixed R.H. background. The array can differentiate not only between gas targets of identical flow-rate (data sets within the same dotted ellipses) but also between varying flow rates (distinctive dotted ellipses); this is due to the fact that PCA data points do not overlap for identical or varying flow rates of the three target analytes. The need for including R.H. as an additional gas target in Figure 4 arises from the fact that, in a real-case scenario, the array must be able to distinguish between short-term R.H. increases (caused e.g., after plant watering) and the event of applying a water-based solution that contains pesticides. Finally, the minimum concentration for which the array can separate between the three analytes was also investigated. As illustrated in Figure 4d , the sensing array can successfully separate between Chloract, Nimrod, and R.H. for a flow rate that is no less than 3.4 mL/min, and is superimposed over a background R.H. of 20% (flow rate of 24.2 mL/min), corresponding to a total R.H of 22%, as illustrated in Figure 4d . This flow rate corresponds to a humidity concentration of 500 ppm (and a R.H. of 2%), a chlorpyrifos concentration of 10.9 ppb, and a bupirimate concentration of 9 ppb (approximated using Raoult's law, as described in Section 2). A hybrid gas-sensing array based on platinum nanoparticles and functionalized with four distinctive polymeric films, was tested as a potential "e-nose" for detecting, quantifying, and separating between two commercially available pesticides (Nimrod and Chloract 48 EC) and relative humidity (R.H.). The effect of environmental parameters such as background R.H. and temperature on the performance of the sensors was evaluated, identifying a background R.H. of 20% and a temperature of 20 • C as optimal conditions for maximum separation between R.H. and pesticides. As a final step, the response data obtained for exposing the array to all three analytes were post-processed using principal component analysis (PCA). PCA validated the array's capacity for discriminating and identifying between the three test gases, as well as for successfully operating for the first time in an environment of elevated background R.H. The importance of the results reported in the current study is further highlighted if the number of existing pesticide gas-sensing reports, as well as the detection of commercially available pesticides and bupirimate, are also taken into account. The proposed sensing array emerges as an appealing pesticide-sensing solution for seamless integration in portable and remote smart-farming monitoring tools [38] , being low-cost, compact, low-power, highly sensitive, fast reversible/reusable, and reliable. Future plans include further investigation of the effect of environmental conditions on sensor response, investigation of possible solutions in order to control temperature and R.H. inside the gas-sensing chamber during measurements, the eventual integration of the proposed sensing technology with the "gaiasense" smart-farming tool [39] , and its performance evaluation in an operational environment. Finally, the expansion of the number of potential environmental pollutants that can be identified by the array, as well as expanding the degrees of freedom of the system by adding more polymeric films, are amongst our future goals. Funding: This research was conducted with the co-financing of Greece and the European Union (European Regional Development Fund) in context with Operation Program "Competitiveness, Entrepreneurship and Innovation (EΠANEK)" of the NSRF 2014-2020-(AcID project code: T2EDK-01949). Review of analytical methods for the determination of pesticide residues in grapes Liquid chromatography-mass spectrometry in the analysis of pesticide residues in food Voltammetric behavior of bupirimate fungicide and its square wave voltammetric determination An ultra-sensitive acetylcholinesterase biosensor based on reduced graphene oxide-Au nanoparticles-ß-cyclodextrin/Prussian blue-chitosan nanocomposites for organophosphorus pesticides detection A ratiometric fluorescent quantum dots based biosensor for organophosphorus pesticides detection by inner-filter effect A rapid detection of pesticide residue based on piezoelectric biosensor A molecularly imprinted polymer based lab-on-paper chemiluminescence device for the detection of dichlorvos Highly sensitive and selective gas sensors using p-type oxide semiconductors Chemically functionalized single-walled carbon nanotubes as ammonia sensors Metal oxides nanowires chemical/gas sensors: Recent advances. Mater Gas sensor by direct growth and functionalization of metal oxide/metal sulfide core-shell nanowires on flexible substrates Bimetallic Pd/Pt nanoparticle functionalized SnO 2 nanowires for fast response and recovery to NO 2 Acetone sensing of Au and Pd-decorated WO 3 nanorod sensors Design and control of gas diffusion process in a nanoporous soft crystal Emerging strategies for enhancing detection of explosives by artificial olfaction Polymers in sensor applications Polymer-based technologies for sensing applications Multiplexed nanomaterial-based sensor array for detection of COVID-19 in exhaled breath Chemical sensors based on metal oxides Length-extensional resonating gas sensors with IC foundry compatible low-cost fabrication in non-SOI single-wafer Organophosphate vapour detection on gold electrodes using peptide nanotubes Qualitative and quantitative analysis of organophosphorus pesticide residues using temperature modulated SnO 2 gas sensor Pesticide vapor sensing using an aptamer Chemiresistive sensor fabricated by the sequential ink-jet printing deposition of a gold nanoparticle and polymer layer Chemical sensing based on double layer PHEMA 18 polymer and platinum nanoparticle films PHEMA functionalization of gold nanoparticles for vapor sensing: Chemi-resistance, chemi-capacitance and chemi-impedance Flexible polyimide chemical sensors using platinum nanoparticles Nanoparticle based gas-sensing array for pesticide detection A sensing approach for automated and real-time pesticide detection in the scope of smart-farming Detection of trace levels of organophosphate pesticides using an electronic tongue based on graphene hybrid nanocomposites Colorimetric sensor arrays based on pattern recognition for the detection of nitroaromatic molecules Humidity sensors based on polymer thin films Properties of a polyethyleneimine-based sensor for measuring medium and high relative humidity Mechanics of moisture for polymers: Fundamental concepts and model study Measurement Good Practice Guide No. 102-Absorption and Diffusion of Moisture in Polymeric Materials A Review of Thermoelectric MEMS Devices for Micro-power Generation-Heating and Cooling Applications Vapor-induced swelling of supported methacrylic and siloxane polymer films: Determination of interaction parameters IoT in agriculture: Designing a Europe-widelarge-scale pilot Smart farming techniques for climate change adaptation in Cyprus Informed Consent Statement: Not applicable. The data presented in this study are available on request from the corresponding author. The data are not publicly available due to privacy restrictions. The authors declare no conflict of interest.