key: cord-0873674-e55wiwu0 authors: Rasul, Shahriar Bin; Som, Uday; Hossain, Md. Shameem; Rahman, Md. Wasikur title: Liquid fuel oil produced from plastic based medical wastes by thermal cracking date: 2021-08-23 journal: Sci Rep DOI: 10.1038/s41598-021-96424-2 sha: 4adbcb2a97cc35d44fed8aeab03f23f3d63396f5 doc_id: 873674 cord_uid: e55wiwu0 The present work is an effort to produce liquid fuel oil from plastic based medical wastes through thermal cracking process under oxidizing conditions. The mixed plastics from medical wastes were considered as a feedstock, shredded into small pieces and heated at 773 ± 10 K for 40 min with a heating rate of 20 K/min in a batch reactor for thermal cracking process. The feedstock was characterized by proximate and ultimate analysis along with thermogravimetric investigation. Moreover, chemical compositions of the liquid fuel oil were examined by FTIR and GC–MS spectroscopy. The properties of liquid product were also examined and compared to the commercial fuel oil. The average yield of brownish and sticky liquid fuel was obtained to be 52 wt% and the gross calorific value of the liquid was found 41.32 MJ/kg which is comparable to that of commercial diesel. FTIR spectrum showed characteristic absorption bands of C–H and =CH(2) groups indicating presence of alkane and alkene compounds. GC–MS study demonstrated the chemical constituents of the liquid product that is mostly aliphatic compounds of mainly alkanes (16.28%), alkenes (10.67%), alcohols (14.65%) and ester groups (10.38%) including iso-phthalate (40.02%) as a predominant product. This experiment concludes that the liquid oil derived from thermal cracking of mixed plastics comprised of a composite mixture of organic components. A significant amount of non-degraded constituents like plasticizers, precursors, etc. remained in the product having some economic values with human health and environmental impacts during burning has been addressed in the current issue. www.nature.com/scientificreports/ level, homogeneity of the kinds and color similarity 9 . The foremost remarkable plastic waste management method is chemical recycling. Incineration and pyrolysis are usually employed to obtain biofuel from plastic materials. Nonetheless, pyrolysis is the key process to alter plastics into liquid oil effectively that comprises heat 10 . Incineration is a crucial procedure from which hydrocarbons are altered into combustion products; whereas, pyrolysis is often employed to change them into inferior hydrocarbons can be employed as biofuel and different materials having economic values. An important magnitude of hazardous pollutants, like HCl, furans, dioxins and heavy metals including Hg, Cd and Pb, are formed from the incineration of medical wastes 11 . Pyrolysis is a process of thermal cracking that occurred in the absence of oxygen. By pyrolysis method, the organic constituents of the decomposable material yield various products of liquid oil, syngas and char as potential sources of energy 12 . The composition of the products depends upon process parameters just as temperatures of the consequent steps of condensation 13 . Various research outcomes reported in the literature that pyrolysis method is usually operated at temperature ranges of 623 and1173 K for 15 to 120 min 14 . Products obtained by pyrolysis of waste plastics lay on the characteristics of plastics, duration, feeding plan, reactor type, condensation arrangement and temperatures employed 15 . The excellence of liquids resulting from the pyrolysis of waste plastics extensively depends on the procedure and therefore the load 16 . Now, the reclamation fuel gas is castoff inside the plant as supplementary fuel for the source of energy to the gas-triggered boiler 17 . The physico-chemical performance of plastics for the amount of thermal pyrolysis acting a crucial role in reactor design 18 . Various reactors are set up and utilized, for example, batch or semi-batch, fluidized bed, screw kiln, spouted bed, microwave and fixed bed 19 . Semi-batch, batch and fixed bed devices are cast off by many investigators as a result of its modest design and informal procedure. In general, the waste plastics are being recycled especially polypropylene (PP), low density polyethylene (LDPE) and high density polyethylene (HDPE) and polyvinyl chloride (PVC) based plastics. Due to hazardous and infectious contents in medical plastics, these need to be incinerated. However, burning plastic releases toxins, like furans and dioxins, persistent organic pollutants (POPs), polycyclic aromatic hydrocarbons (PAHs), etc. results in air and environmental pollution 20 . Emission of polychlorinated dioxins and dibenzofurans like toxins was quantified from medical waste incinerators (MWI) in China and the residents nearby the MWI are at high health risk 21 . In fact, the direct combustion of organo-chloride compounds like PVC is the main cause of those toxic releases 22, 23 . Mechanical recycling is one of the alternative eco-friendly options for PVC based plastic waste management but it is necessary to separate out from other types of plastics 24 . In case of infectious hazardous medical wastes, the separation process of PVC materials is at risk for human health. It has been reported that dehydrochlorination is a predominant process for decomposition of PVC at low temperature 25 and no harmful dioxin or furan compounds were found in pyrolytic yield from PVC and mixed plastics which was carried out at higher temperature 26, 27 . Catalytic degradation of plastic waste polymers and compared the results to catalytic and non-catalytic degradation 28 , have examined the thermal cracking of plastic waste 29 . A study on thermal decomposition of LDPE operated at 623 K in oxidizing atmosphere showed that linear aliphatic compounds mostly low carbon alcohols and carboxylic acids were obtained 30 . Butler et al. showed the pyrolysis of plastic syringe as medical wastes to produce valuable fuel oil 31 . Therefore, energy recovery from medical-based plastic wastes is one of the alternative solutions. A few pieces of scientific literature were reported on the thermal treatment of the medical wastes in oxygen free atmosphere and the characteristics of the liquid fuel oil 32 . Nonetheless, no one investigated the current issues in details as of transformation of medical based mixed plastic-wastes into energy through oxidative thermal degradation. In medical sector, a huge amount of plastics based disposable medical supplies, made of HDPE, PP, PS, PVC etc., are discarded, which are a great source of mixed engineered plastics 33 . Since the natures of such medical grade plastics are specialized due to its high heat resistance, more durable, impact strength and highly stable under UV irradiation, there may have impact on the yield of liquid fraction from thermal treatment. Likewise, these outstanding properties of medical-grade plastics contain various additives, plasticizers, slip and curing agent etc. that may influence the characteristics of the thermally cracking fuel oil 34 . Moreover, disposable medical-based plastic wastes are disposed of every day from the hospitals, clinics and the diagnostic centres, which perform as a vector of spreading of communication diseases. Due to application of high temperature (> 573 K) in thermal treatment all germs even viruses are destroyed. A recent study shows that high temperature pyrolysis technique is one of the alternative technology in-practice to deal with the current pandemic COVID-19 based waste management 35 . So, the thermal treatment of mixed plastic wastes either the pyrolysis or the oxidative thermal cracking process could be a potential alternative medical waste management along with a resource recovery option. In Bangladesh, incinerator is used for managing all sort of medical wastes in few big cities whereas in urban/peri-urban areas the decomposable wastes are dumped or buried at the landfill site and the plastic wastes go to the recycler which is alarming for public health 36 . Under these circumstances, the present work is an effort to produce liquid fuel oil from plastic based mixed medical wastes through thermal cracking in a batch reactor under oxidizing atmosphere and its characterization (Fig. 1) . In order to ensure the quality of the derived fuel oil, the properties of the fuel has been studied and compared to the commercial fuels. Besides, the chemical characteristics has been undertaken to find out the nature and types of degraded constituents from the waste plastics and whether any harmful volatile compounds exist that have environmental and health effects. This work additionally contributes in developing proper management of plastic based medical wastes in order to reduce harmful environmental emissions other than a potential feedstock for liquid fuels. Feedstock. Plastic based medical wastes, mostly medical disposable supplies, were collected from the local hospitals and clinics of Bangladesh. This includes syringes, surgical gloves and infusion bags and sets that have been used as feed materials throughout the experiment. The composition of the medical supplies was identified from the specification of the manufacturers available in the literatures 33 , respectively. In addition, most of these medical grade plastics contain various additives like plasticizer, precursor, slip agent, curing agent, stabilizer, etc. to make them transparent, flexible, resistant to kinking and non-reactive to the fluids and medicines. So, the feedstock, selected for this experiment, is a composite and heterogeneous polymeric-additive compound. The collected plastic based medical wastes were cleaned successively by water, methanol and hydrochloric acid and eventually rinsed with distilled water and air-dried. This pre-cleaning approach was followed as a precaution for the researchers ensuring safe handling of the samples and avoiding communication disease or any pathogenic contamination. It is assumed that this pre-cleaning process does not necessarily important for large scale application of thermal cracking because all pathogens are killed at high temperatures. The washed materials were shredded to an average particle size of 1 cm and mixed thoroughly preparing as about 12 kg feedstock for a series of thermal cracking experiments. The size of the feedstock was predetermined based on the previous work of the research group 2 . Characterization of raw materials. Proximate and ultimate analysis of the feedstock was administered by a muffle furnace (Barnstead) and an elemental (CHNS) analyzer (Vario MICRO, Model EA 1108), respectively. The high calorific value (HCV) of the feedstock was measured by a Bomb Calorimeter. Degradation characteristics of the plastic based mixed medical wastes were measured by Thermogravimetric Analyzer (TGA) using Perkin-Elmer TGA7 (Detector TGA-50H, Cell Al). The TGA experiment was investigated at three altered heating rates of 10, 20 and 30 K/min with constant flow of air (oxidizing environment) at a rate of 10 mL/min from room temperature to 1073 K. Experimental procedure. The apparatus used in this experiment was a batch reactor which was cylindrical in shape, made of carbon steel, having 45.7 cm and 25.4 cm inner depth and diameter, respectively. Four electrical heating coils with a power of 500 W each were used as a source of heating energy, placed inside the reactor. A type K thermocouple connected with a temperature recorder was used for measuring temperature of the inside reactor. At the top of the reactor, a tubing system was connected with a valve through which the volatile fractions were flown in two successive condensers. The condensed product was stored in the oil collector and the residual non-condensable fraction was allowed to flow through a column of activated carbon and was exhausted to the air by controlling the exit valve. A schematic illustration of the thermal cracking experiment is shown in the Fig. 2 . The preliminary experiment was intended to discover the impact of temperature on the yield of fuel oil and char from thermal cracking of plastic based medical wastes. To this effect, the thermal cracking was carried out at four temperatures settings of 523 K, 623 K, 723 K and 773 K (± 10 K each) and a fixed amount of feedstock was loaded each time into the reactor. The thermal reaction was completed at a heating rate of 20 K/min under the normal oxidizing conditions for 25 to 40 min in different temperature settings. The derived liquid oil was collected after each reaction step and weighed. The char products, after each reaction step, were also collected Due to the objective of this study, the non-condensable fraction was not collected for its characteristic investigation; however, creative works of current researchers of the related area are referred to understand its compositions. The liquid fraction obtained from the experiment repeated for three times at 773 ± 10 K was stored for measuring chemical features. To determine the physical properties (gross calorific value, density and flash point) of the derived liquid oil, the subsequent standard methods are followed: American Standard for Testing and Materials (ASTM), Density 4052 (ASTM: D4052), ASTM: D445-11, ASTM: D93, ASTM D97 and Oxygen-Bomb Calorimeter. Fourier Transform Infrared (FTIR) was employed to analyse surface properties of the sample using FTIR spectrophotometer (Model: IRAffinity-1S, Shimadzu Co., Japan). An analytical method of Gas Chromatography-Mass Spectroscopy (GC-MS) (GCMS-TQ8040) was carried out to identify the composition of the as-prepared liquid sample and works with a coupling of GC (column and injection temperatures 50 and 300 °C, respectively) and MS (acquisition time 3.5 to 36.5 min with an scan speed of 2000/sec). Elemental and proximate analysis of feedstock. The proximate analysis interprets that the feedstock contains 87.2% volatile matter, i.e., the bulk of the raw material is organic compounds which were burnt in the gaseous state. The fixed carbon in the feedstock is 7.8% that was burnt in the solid state. Higher volatile components quantified higher liquid product during the thermal cracking process. The volatile components and the high calorific value (HCV) are the crucial factors for the thermal treatment of plastic based medical wastes. It was found that 33.3 MJ of heat energy can be liberated from the combustion of 1 kg of medical wastes, indicated a good source of energy valorisation. The HCV value of the current study was found to be a little bit lower than those reported some other researchers as shown in Table 1 , which might be due to the presence of some impurities, need to be further purified. The www.nature.com/scientificreports/ due to its presence in PDMS and various chemical additives (e.g., plasticizer, precursor and stabilizers, etc.) used in the processing of medical-grade plastics 40, 41 . Sulphur may be found from sulphur containing antioxidant, which is used as a thermal stabilizer during the processing of polymeric materials 39 . The ultimate and proximate analyses of plastic medical wastes presented in Table 1 are compared to some other results reported elsewhere 20, 42 . Characterization by TGA . The TGA result supports to understand the thermal stability of the feedstock and the behaviour of the degradation under controlled atmosphere like either in inert or in oxidizing environment. In this research, the plastic based mixed medical wastes (PE, PP, PVC, etc.) were considered for TGA at three heating rates of 10 K/min, 20 K/min and 30 K/min under oxidizing conditions. The Thermogravimetric (TG) curves (3a, 3b and 3c in Fig. 3 ) interpret the weight loss as a function of temperature at different heating rates corresponded to Differential Thermogravimetric (DTG) peaks (3d, 3e and 3f in Fig. 3 ) which construe the weight reduction of the feed sample with time. Figure 3 clearly indicates that both TG curves and DTG peaks moved to the elevated temperatures with increasing trial heating rates. The DTG peaks also indicate wide degradation temperature spans which is due to mixed polymeric components in the plastic wastes 42 . The mixed plastics started decomposition from 360 K, 548 K and 555 K at the heating rates of 10 K/min, 20 K/min and 30 K/min, respectively under constant air flow. The degradation process was completed at 730 K, 740 K and 809 K with no residuals of significant level of char product. It was comprehended that degradation temperature was quite low at the minimum heating rate but it showed maximum ranges of temperature span. This TGA study revealed that the degradation temperatures at the heating rates was found significantly lower than those of individual virgin materials (like PE, PP, etc.) as reported by the researchers. This might be due to the presence of various additives, plasticizers, stabilizers, etc. in the plastic materials 42 . The degradation temperatures at which the weight loss became half of the feedstock were found to be 548 K, 621 K and 704 K corresponded to the successively increased heating rates. The DTG peak at 20 K/min heating rate (Fig. 3e ) also showed two steps degradation at the temperatures of 621 K and 645 K results in possibly mixture of polymeric components in the plastic wastes. Based on the TGA data, finally, the liquid fuel oil was derived from the mixed plastic wastes by thermal cracking in the range of 500-773 K at a heating rate of 20 K/min under oxidizing environment. Effect of temperature on thermally degraded yield. In thermal cracking process, the degraded plastic materials are mainly char, condensate/liquid oil and a fraction of non-condensable product or gaseous fraction. The amounts of these degraded yields depend on the temperature applied during the thermal cracking. In Table 1 . Proximate and ultimate analysis of plastic based medical wastes. Ultimate analysis (wt%) www.nature.com/scientificreports/ this experiment, the effect of temperature was examined on the thermally degraded yields from plastic based mixed medical wastes as shown in Fig. 4 . It was observed during the experiment that the maximum yield of liquid oil was found to be 61% with an optimum temperature of 623 K and the rate of yield was further decreased to 52% with the increasing in temperature at 773 K. Simultaneously, the yield of char was decreased successively and at the maximum temperature of 773 K, the amount of char became negligible. The calculated non-condensable fractions were found to be increased with temperature rises. Dash et al. 37 showed that 83.3 wt% of liquid oil was acquired from the pyrolysis of medical wastes (e.g., plastic syringe, a mixture of PP and PE). On the other hand, Hossain et al. 2 showed that 39.89 wt% liquid yield was derived from the waste plastics (PP, PE, etc.) through pyrolysis process at 773 ± 10 K. Hence, there was a variation in product yields among the researchers in pyrolysis (in absence of oxygen) process. In this experiment, the maximum yields of liquid oil obtained through thermal cracking in oxidizing conditions do not differ significantly from the pyrolysis process. The obtained liquid product was brownish and sticky. It is depicted that thermal cracking of plastic materials depends on their distributions, range of temperature, composition of feedstock, types and dimensions of reactor, effectiveness of heat transfer from hot reactor surface to raw material, particle size of feedstock and residence time of vapor, etc. In the current experiment, the liquid oil derived from the maximum temperature setting at 773 ± 10 K was considered for chemical characterization because at this stage, the char production was negligible and the fraction of non-condensate was maximum value. fuel was researched to comprehend the nature and kind of the composites in thermally degraded liquid oil. The Total Ion Chromatogram (TIC) of the liquid oil from GC-MS study is shown in Fig. 6 . The GC-MS data shows a list of different organic compounds having the functional groups quite similar to FTIR shown in Table 2 . According to the TIC peak area, the amount of the types of compounds in percentage is presented in Fig. 7 . It was perceived that the thermally degraded liquid oil consisted of aliphatic compounds, mainly of alkane (16.28%), alcohol (14.65%), alkene (10.67%), esters (10.38%), cycloalkane (2.56%) and phenolic compounds (3.32%). The predominant form of major compounds was identified as phthalate group (42.13%) which is widely used as plasticizer in plastic materials. The chemicals found within alkanes, alkenes and cycloalkane groups have high carbon content (C 10 to C 26 ) and these are possibly the degraded products from the mixed polymeric medical wastes. Some other researchers 37,43 also found similar groups of organic compounds having high carbon contents. The chemical constituent of phthalate group was found as dioctyl isophthalate (DOIP) and diethyl hexyl phthalate (DEHP) which are used as plasticizers in polymeric formulations; especially, in the medical-grade PVC and the typical range of amount used 10-70% (w/w) 44 for improving the flexibility, durability and stretch ability of the plastics. Shuqi et al. 43 also found dibutyl phthalate (1.54%) as a plasticizer in the chemical list of GC-MS data in pyrolytic yield. The boiling points of these plasticizers are high (658-673 K) and thus it is expected that such chemicals are not degradable product under the condition applied in this investigation. Analogous chemicals of high boiling point have been found in ester groups which are almost fatty acid ester used as a lubricant or slip agent to reduce the surface coefficient of friction of plastic materials 33, 44 . The chemical constituents, found in alcohol group, are used as precursor for the synthesis of DEHP and so it is presumed that the chemicals within ester and alcohol groups are not the thermally degraded product 41 . A small portion of phenol (1.89%) was found in the liquid oil which may produce during thermal degradation of plastics under oxidizing environment 20 . It is concluded from the GC-MS data analysis that the mixed plastic wastes from medical source, which are made from mostly of engineered polymeric resins, are not degraded fully through thermal cracking under oxidizing conditions at a maximum temperature 773 K and various chemical additives used in plastic materials are released in the thermally degraded liquid oil product and there may have environmental effect if such liquid oil is burnt as fuel. Properties of liquid fraction as fuel. The characteristics of the as prepared liquid oil are compared to some commercial fuel oils like gasoline and diesel as shown in Table 3 . The viscosity of the liquid product (4.0 cSt) is higher than that of diesel (2.8 cSt) and lower than gasoline (6.2 cSt). The density (840 kg/m 3 ), flash point (312 K) and gross calorific value (GCV) (41.32 MJ/kg) of the liquid oil are almost similar to liquid fuels reported elsewhere 45 . This liquid fraction can be utilized by blending with commercial fuel oil or this can be further refined to improve the fuel properties. Merits and demerits of thermal cracking of medical based plastic wastes. In a nutshell, the application of the thermal cracking process in the management of medically-based plastic wastes is useful in recovering fuel energy. It has been proved that the procedure breaks down the mixed engineering plastics-based disposable medical supplies having polymers or long-chain hydrocarbons and complex organic molecules as www.nature.com/scientificreports/ additives. In contrast, it produces a portion of light hydrocarbons alkane and alkene products lower to medium boiling point hydrocarbons, which are useful as a substitute for fossil fuel. Besides, the non-degraded plastic additives that remain in the liquid fraction have a strong influence on fuel properties. The advantage of a thermal cracking process of medical waste is that the batch reactor and associated equipment to maintain the temperature range 723-773 K can be easily commissioned using locally available materials comparatively instead of the high-cost incinerator. The liquid product comprises a composite mixture of various organic components as described in the GC-MS study. The list of constituents from the GC-MS study showed that no harmful polychlorinated dibenzo-p-dioxins, Polychlorinated dibenzofurans, Polychlorinated biphenyls, and any other hazardous organochlorine products were formed in the liquid fraction, though a significant portion of PVC materials was present in the feedstock. So, the oxidative thermal cracking process could be an alternative to an incinerator for the management of medicalbased mixed plastic waste. Moreover, the process will be an alternative thermal technique to disinfect hazardous medical-based plastic wastes without any pre-treatment due to apply high temperature reaction condition and simultaneously to recover clean fuel energy. In addition, the non-condensate, which is mostly composed of syngas (CO, CO 2 and H 2 ) having economic importance due to its high calorific value used in most chemical and polymer industries. The gas is applied for www.nature.com/scientificreports/ the generation of power and heat. It can be burned directly as fuel or it is used to produce ethanol and hydrogen. Syngas are also used in the Fischer-Tropsch process to produce liquid hydrocarbons. The disadvantage of the thermal cracking process is the low yield of product due to the oxidizing condition. Besides, there are some non-degraded and high boiling point compounds that remain in the liquid fraction which has human health and environmental impact. The thermal cracking liquids need further treatments, for instance, centrifugation, filtration, hydro-treating, decanting and desulphurization for use as clean fuels. Plastic based medical wastes were successfully employed as a potential feedstock of liquid fuel oil by thermal cracking process in oxidizing conditions. In order to recover liquid oil from the medical waste, the feedstock was thermally cracked at a temperature of 773 ± 10 K and the product yield was found to be 52 wt%. The gross calorific value of the derived liquid oil was found to be 41 MJ/kg that is analogous to the commercial fuel oils. The functional groups of the chemical constituents in the derived liquid fuel oil were examined by using FTIR spectroscopy. The spectrum showed strong absorption bands of both stretching and bending vibrations for alkane, alkene, methylene, alcohol and ester groups. The chemical characteristics of the as prepared liquid oil demonstrate the constituents of a composite mixture of degraded and non-degraded organic compounds derived from the medical based mixed plastic wastes. GC-MS study showed that both degraded polymeric components and non-degraded products existed in the derived fuel oil. The chemical constituents of degraded yield were mostly aliphatic compounds that are mainly of alkane (16.28%), alkene (10.67%), and non-degraded yield was classified as alcohol (14.65%) and ester (10.38%) and predominant compound of phthalate (42.02%) group. The degraded fractions are medium to heavy hydrocarbons having carbon numbers C 8 to C 26 and the non-degraded constituents were found mostly as phthalate group. The non-degraded constituents present in the liquid oil may release gases into the environment while burning and harmful to human health. In fact, thermal cracking, pyrolysis or gasification techniques are appraised for the preparation of liquid fuel from plastic based medical waste materials; nonetheless, the liquid fuel needs further treatment or separation techniques, for instance, centrifugation, filtration, hydro-treating, decanting, etc. to be used for the clean fuels in the near future. Finally, it can be concluded that the oxidative thermal cracking process could be an alternative technology instead of an incinerator for not only treating hazardous plastic based medical waste but also to produce clean fuel energy. Postconsumer plastic waste over post-use cracking catalysts for producing hydrocarbon fuels Recovery of alternative fuel from thermal pyrolysis of medical wastes Thermal pyrolysis of polyethylene in fluidized beds: Review of the influence of process parameters on product distribution Thermolysis of waste plastics to liquid fuel: A suitable method for plastic waste management and manufacture of value added products: A world prospective Medical waste management at Upazila level in Bangladesh Pattern of medical waste management: existing scenario in Dhaka City & Team IPSU. Medical waste management at Rajshahi city corporation public private partnership model development: A collaborative effort on medical waste Management in Bangladesh Mechanistic implications of plastic degradation Feedstock Recycling of Plastic Wastes Application of sustainability assessment to a novel plastic recycling process Metals leachability from medical waste incinerator fly ash: A case study on particle size comparison Influence of time and temperature on pyrolysis of plastic wastes in a semi-batch reactor Novel catalytic systems for waste tires pyrolysis: Optimization of gas fraction Liquefaction process for a hydrothermally treated waste mixture containing plastics Pyrolysis of high-density polyethylene in a fluidised bed reactor. Influence of the temperature and residence time A comparative analysis of the kinetic experiments in polyethylene pyrolysis Fuel production from plastic wastes pyrolysis: Fluids engineering division summer meeting Pyrolysis of municipal solid waste in Japan Thermal degradation of medical plastic waste by in-situ FTIR, TG-MS and TG-GC/MS coupled analyses Emission characteristic of polychlorinated dibenzo-p-dioxins and polychlorinated dibenzofurans (PCDD/Fs) from medical waste incinerators (MWIs) in China in 2016: A comparison between higher emission levels of MWIs and lower emission levels of MWIs Dioxins and polyvinyl chloride in combustion and fires Waste incineration, PVC, and dioxins Recycling of PVC wastes Thermal degradation of polyvinyl chloride Pyrolysis of polyvinyl chloride (PVC)-containing mixed plastic wastes for recovery of hydrocarbons Thermal degradation of PVC: A review The conversion of waste polystyrene into useful hydrocarbons by microwave-metal interaction pyrolysis A comparative study of liquid product on non-catalytic and catalytic degradation of waste plastics using spent FCC catalyst A factorial experimental design for oxidative thermal decomposition of lowdensity polyethylene waste Waste polyolefins to liquid fuels via pyrolysis: Review of commercial state-of-the-art and recent laboratory research Pyrolysis characteristics of Municipal solid waste in oxygen-free Circumstance Handbook of Polymer Applications in Medicine and Medical Devices Syringes as medical devices Disinfection technology and strategies for COVID-19 hospital and bio-medical waste management Hospital waste management: Bangladesh Thermolysis of medical waste (waste syringe) to liquid fuel using semi batch reactor Application of synthetic polymers in clinical medicine Susianto: Production of liquid fuel from plastic waste using integrated pyrolysis method with refinery distillation bubble cap plate column The vacuum pyrolysis of used tires: End-uses for oil and carbon black products Brydon's Plastic Materials 8th edn Thermal degradation of waste plastics under non-sweeping atmosphere: Part-1: Effect of temperature, product optimization, and degradation mechanism Study on pyrolysis products characteristics of medical waste and fractional condensation of the pyrolysis oil An overview of chemical additives present in plastics: Migration, release, fate and environmental impact during their use, disposal and recycling Physicochemical and structural analysis of biodiesel produced from linseed oil by microwave method This research didn't get a particular award from subsidizing organizations in general society, business, or notrevenue driven areas. All authors contributed significantly to do the experiments, write and reviewed the manuscript. The authors declare no competing interests. Correspondence and requests for materials should be addressed to M.S.H. or M.W.R.Reprints and permissions information is available at www.nature.com/reprints.Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.