key: cord-0870985-yck9ueey authors: Wang, Hong; Wu, Yanjin; Wang, Jiang title: Triboelectric charging of melt-blown nonwoven filters with high filtration efficiency date: 2022-01-21 journal: Sci Rep DOI: 10.1038/s41598-022-04838-3 sha: b2db9d44e35355babffe34ff660711bbdbe5cba1 doc_id: 870985 cord_uid: yck9ueey As a novel technology to convert low-frequency energy into electric power, the triboelectric nanogenerator is a hot research topic recently. However, the nature of charge carriers and their transfer mechanisms still remain poorly understood, especially for the cases of liquid–solid triboelectric nanogenerator. In this paper, charges produced by a triboelectric charging process were designed to provide melt-blown nonwoven fabrics with high filtration efficiency by making full use of the electrostatic attraction filtration mechanism. Influences of water conductivity and drying temperature on the filtration efficiency of melt-blown nonwoven fabrics were investigated. And the corresponding properties such as the surface charge potential and charge stability were analyzed by using the electrostatic voltmeter, bio atomic force microscope and thermally stimulated discharge technique. In addition, metal and inorganic elements in the masterbatch and water before and after triboelectric charging were measured in order to uncover the charge transfer mechanism. Melt-blown nonwoven fabrics with filtration efficiency as high as 96.8% was obtained through the triboelectric charging treatment by using water with the conductivity as low as 1.1 μS/cm for the first time. Negative and positive surface charge density appeared randomly on both sides of melt-blown nonwoven fabrics after the triboelectric charging treatment from the bio atomic force microscope measurement while only one kind of surface charge density can be achieved in the research of TENG, that is, negative or positive. It seems there are both electron and ion transfers during the triboelectric charging process and electron transfer seems to have more important contribution for the generation of charges. Since the outbreak of COVID-19 at the beginning of 2020, face masks have attracted great attention worldwide and hydro charging technique has been widely used to produce MNF with higher filtration efficiency and long-term stability as the key layer of face masks while remain the same pressure drop, although the underlying mechanism is still not yet understood. In addition, since invented in 2012, much research is now focused on triboelectric nanogenerator (TENG) which exhibits potential application as a power source, self powered sensor, capacitor and blue energy harvester [11] [12] [13] [14] [15] . Among them, TENG based on liquid-solid triboelectrification is proposed with new strategies toward harnessing water kinetic energy [16] [17] [18] . Although triboelectrification is a well known phenomenon for more than 2600 years, its scientific understanding is still under debate, especially for the cases of liquid-solid contact electrification 19 . Based on the above background and our previous study, in this paper, MNF with high filtration efficiency was prepared in our lab by using a simulating triboelectric charging equipment. The corresponding properties such as the surface charge potential and charge stability were analyzed. And metal and inorganic elements in the masterbatch and water before and after triboelectric charging treatment were measured with the aim to uncover the charge transfer mechanism of the triboelectric charging treatment which is helpful to explore the mechanism of water-solid TENG as well. Triboelectric charging experiment. In this paper, a simulating triboelectric charging equipment was set up in our lab with a portable petrol powered sprayer (the water pressure is in the range of 1 ~ 3 MPa) to generate water jets with desired speed, as illustrated in Fig. 1 . Deionized water with different conductivity was sprayed out of the nozzle of the portable sprayer and continuously impinged on up and down sides of MNF repeatedly for 1 min, which was put on a shelf with wheels and could be moved forward and back manually.Then the wet MNF was dried in an oven for 2 min under certain temperature, as shown in Fig. 2 . MNF used in the experiment was composited with 2.5% electret masterbatch which was added during the melt-blowing process of polypropylene, with the basis weight of 25 g/m 2 . An electrostatic voltmeter (Model 542, TREK Inc., USA) was used to determine the surface charge potential of MNF with the size of 12 cm × 12 cm which was laid on an insulating desk. The values of surface charge potential at different areas on the MNF were recorded one by one when the sensor hold by hand was moving over the MNF 15 mm away. In order to reflect the charge potential distribution, each sample was tested for three times, with 30 points were recorded on the front side and back side, respectively. The Dimension FastScan Bio Atomic Force Microscope (Bruker Co., USA) was used to measure the surface potential of MNF before and after triboelectric charging treatment. The model of the conducting probe was OMCL-AC240TM-R3 with the spring constant and resonance range of 2 N/m and 2 V, respectively. The lift-off distance of the probe was 200 nm. The open circuit thermally stimulated discharge (TSD) measurements of MNF were carried out in a system consisting of a temperature controlled oven with a linear heating rate of 3℃/min, an electrometer (Model6514, Keithley), and a data processing computer. The linear temperature range of the TSD test was 30 − 150℃. Metal and inorganic elements in the electret masterbatch and water before and after triboelectric charging treatment were measured by using inductively coupled plasma analysis (Prodigy, Leeman, America) with argon as the carrier gas. The influence of water conductivity on the filtration efficiency of MNF. The electrical conductivity of water is used in many industries as an indication of the purity of water. The conductivity of tap water is in the range of 125 ~ 1250 μS/cm while the conductivity of distilled water used widely in the study of solid-liquid contact electrification is only 0.18μS/cm (the resistivity is 18.2 MΩ·cm) 20 . As we know, excessive purification of water will increase the cost of production unnecessarily. Hence, in this paper, the influence of the electrical conductivity of water on the effect of triboelectric charging was studied at first. MNF were triboelectric charging treated by using water with the electrical conductivity of 1.1, 6.9, 18.0 and 72.9 μS/cm, respectively, while keeping other experimental conditions the same. Effects of the electrical conductivity of water on the filtration efficiency of the obtained MNF were shown in Table 1 and Fig. 3 . In addition, in order to rule out the influence of physical filtration effects, the mean pore size of MNF before and after triboelectric charging treatment were measured as well, as shown in Table 1 . www.nature.com/scientificreports/ It can be found from Table 1 and Fig. 3 that the filtration efficiency of MNF decreased with the increase of the conductivity of water significantly. As we know, the pore size of filters has a great influence on the filtration efficiency according to the physical filtration mechanism. However, as presented in the Table 1 , the mean pore size of triboelectric charging treated MNF by using water with different conductivity did not change obviously. It is believed that the variation was mainly due to the compression being employed during the triboelectric charging process. Therefore, it is believed that static charges on fiber surface of MNF generated after the triboelectric charging treatment have important contribution to the filtration efficiency of MNF by making use of the electrostatic attraction filtration mechanism, consistent with the findings in the study of solid-liquid TENG which is reported that solutes in the solution, pH value of the solution and the hydrophilicity of the solid affect the ratio of electron transfers to ion transfers 21 . Based on the coupling between the triboelectric effect and electrostatic induction, TENG has proven to be a cost-effective and environmentally friendly technology for mechanical energy harvesting, self-powered devices and systems, and air filter. A triboelectric air filter consisting of five layers of the polytetrafluoroethylene (PTFE) and nylon fabrics can be charged by simply rubbing the PTFE and nylon fabrics against each other. After charging, the air filter has a removal efficiency of 84.7% for PM0.5, 96.0% for PM2.5 22 . A face mask based on the Poly(vinylidene fluoride) electrospun nanofiber film and TENG driven by respiration is developed. The face mask can continually provide electrostatic charges by respiration and shows a removal efficiency of coarse and fine particulates as high as 99.2wt%, and its removal efficiency of ultrafine particulates is as high as 86.9wt% 23 . In this study, MNF with filtration efficiency of NaCl particles with diameter of 0.3 μm is as high as 96.8% through the triboelectric charging treatment by using water with the conductivity as low as 1.1 μS/cm, much higher than all the above reports. The influence of drying temperature on the filtration efficiency of MNF. In order to understand influences of the drying temperature on the filtration efficiency of MNF, the wet MNF was dried in an oven under 110℃, 130℃, 150℃ and 160℃ respectively, after the triboelectric charging treatment by using deionized water with the conductivity of 1.1μS/cm, and the results were shown in Fig. 3 . In comparison, the filtration efficiency of triboelectric charging treated MNF dried under room temperature (25℃) was measured as well. It can be found from Fig. 4 that triboelectric charged MNF dried under different temperature exhibited similar filtration efficiency, suggesting that the drying temperature does not influence the filtration efficiency of MNF, and static charges on fiber surface of MNF generated after the triboelectric charging treatment have good thermal stability as well. On the other hand, it was found that MNF dried under 160℃ shrank obviously, suggesting that the drying temperature should not be higher than 150℃. Surface charge potential of MNF. In order to verify if the filtration efficiency improvement of triboelectric charged MNF is due to the extra electrostatic charges obtained by the triboelectric charging treatment, the surface electrostatic potential of triboelectric charged MNF (sample 1 in Table 1 ) and the original MNF were measured by using a non-contacting voltmeter and the results were shown in Fig. 3 . In order to reflect the charge distribution, each sample was tested for 90 times and the corresponding surface charge potential distribution diagram was performed by plotting the surface charge potential as the vertical y-axis against the sequence number of each surface charge potential as the horizontal x-axis, as shown in Fig. 5 . As shown in Fig. 5 , the surface charge potential of triboelectric charged MNF was much higher than that of the original MNF, suggesting that the triboelectric charging treatment could generate charges on the fiber surface of MNF, resulting in the higher filtration efficiency consequently. Negative and positive charges appeared randomly on both sides of MNF treated by triboelectric charging process as shown in Fig. 5a while only one kind of surface charge density can be achieved in the research of TENG, that is, negative or positive 24 . In addition, it is believed that the surface charge potential of the original MNF is due to the polarization of additives and impurities in the polymer melt during the spinning and drawing process 25 . To double check the nature of charges on MNF, the surface charge densities of sample 1 listed in Table 1 was measured by using a FastScan Bio Atomic Force Microscope (AFM) and the results were shown in Fig. 6 . www.nature.com/scientificreports/ It can be found from Fig. 6 that negative and positive charges appeared simultaneously on triboelectric charged MNF. To the best of our knowledge, the mean fiber diameter of MNF is in the range of 1 ~ 4 μm. Hence it can be concluded from Fig. 4 that a single fiber of MNF can be negatively and positively charged simultaneously during the triboelectric charging process, which is quite different from the charges widely reported in the study of TENG. Charge storage stability of triboelectric charged MNF. The thermally stimulated discharge (TSD) current measurement is often applied to study the stable behavior of charge storage 26 , which is helpful to uncover the nature of charge carriers and their transfer mechanism to some extent. In this paper, the charge stability of MNF before and after triboelectric charged treatment was investigated by TSD technique, as shown in Fig. 7 . It is reported that the medium-temperature peak between 100 and 130℃ on TSD spectra of charged polypropylene is attributed to the release of both inherent and injected charge carriers 27 . As demonstrated in Fig. 7 , a peak at about 130℃appeared obviously on the TSD current spectra of triboelectric charged MNF, while the discharged current of virgin MNF over the entire temperature range was negligible, suggesting that a great amount of charges were injected into MNF by triboelectric charging treatment, which is consistent with the surface charge potential analysis as shown in Fig.6. Composition analysis of the triboelectric charging masterbatch and water before and after triboelectric charging treatment. As we know, only MNF added with functional masterbatch can achieve higher filtration efficiency by triboelectric charging treatments. Hence it is necessary to study the composition and function of the functional masterbatch which might be helpful to identity charge carriers (electrons or/and ions) and further understand the mechanisms underlying the triboelectric charging process. In this paper, metal www.nature.com/scientificreports/ and inorganic elements of the masterbatch used in the experiment were measured by using ICP and the results were shown in Table 2 . In comparison, a commercial corona charging masterbatch was measured as well. It can be found from Table 2 that the metal and inorganic elements content of the triboelectric charging masterbatch was quite different from that of corona charging masterbatch. Mg content of the triboelectric charging masterbatch was much lower than that of the corona charging masterbatch while there were more Ba and B in it. In addition, the content of Ca was similar in the two kinds of masterbatches, which might help to improve the charge stability of MNF. In the corona charging process, meltblown nonwoven fabrics are often prepared by blending with dielectric additives such as SiO 2 , Al 2 O 3 , BaTiO 3 , boehmite, and boron nitride nanosheets, which will develop a quasipermanent polarized electrical charge when they are subjected to a high voltage electric field. In addition, it is believed that the charge traps mainly originate from the interfaces between crystallite and amorphous region of MNF. As a kind of nucleating agent, MgSt can improve the crystallinity of MNF with more fine-grained crystallite. Hence it is often added as the charge enhancer as well 28, 29 . However, it is impossible for the triboelectric charging masterbatch to polarize electrically because the triboelectric charging treatment doesn't operate necessarily in a high voltage electric field. Hence, it is believed that the masterbatch used in this paper is able to lose and/or receive electrons from the water spray during the triboelectric charging process. In order to verify whether the ion transfer also appears during the triboelectric charging process as those described in the research of TENG, metal and inorganic elements in the water before and after triboelectric charging treatment were examined by using ICP which is a promising technique for analysis of trace elements in solutions and has been rated as the most powerful tool in analytical chemistry. Metal and inorganic elements in the water before and after triboelectric charging process were shown in Table 3 . It can be found from Table 3 that the metal and inorganic elements in the triboelectric charged water were not higher obviously than those in the original water, suggesting that metal and inorganic elements on the fiber surface of MNF didn't dissolve in the water during the triboelectric charging process. The content of B and Si in the original water was much higher than we expected because the apparatus for producing deionized water can't remove them from the tap water. It is believed that electron transfer between the water jet and fibers of MNF is Table 3 . Metal and inorganic elements in the water before and after triboelectric charging process. www.nature.com/scientificreports/ the main phenomenon during the triboelectric charging process. In other words, ion transfer between the MNF and water is not the main origin of static charges on fiber surface. The charge transfer mechanism of triboelectric charging process. Although the contact electrification phenomenon has been known since antiquity, the nature of charge carriers and their transfer mechanisms still remain poorly understood, especially for the cases of liquid-solid contact electrification. In the past few decades, at least three mechanisms have been proposed: electron transfer, ion transfer and material transfer 25 . On the other hand, other studies proposed that ions, instead of electrons, are transferred during contact electrification 30 . In addition, Pandey and co-workers studied the charge transferred and the amount of material transferred during the contact electrification by varying the degree of softness of a polymer and believe that material transfer seems to have an important contribution for the generation of charge by contact, especially for materials that are soft 31 . As the developer of TENG, Wang and co-workers proposed a Wang's hybrid layer model to explain the solid-liquid contact electrification 24 . In Wang's hybrid layer model, the water is assumed to be neutral before it contact with the solid. The water droplet gently separated from the grounded needle and instantly came into contact with the polymer surface in the drop-TENG experiment. However, in other study, it is reported that the water movement and impact can lead to an extensive accumulation of electrical charge in water due to the charge separation of water 16, 32 . Based on the above experimental results and research on charge transfer mechanisms of liquid-solid contact electrification, a diagram of charge transfer mechanism of the triboelectric charging process is established, as illustrated in Fig. 8 , and a charge transfer mechanism is proposed as follows. Similar to the solid-liquid TENG, in the triboelectric charging process, it is believed that the water has been positively charged due to the lost of electrons caused by the friction with the pipeline. After spraying out of the nozzle, more charge separation happens due to the splashing and bubbling movement. Therefore, water droplets become positively, negatively, or neutrally charged before they contact with MNF. When positively and negatively charged water droplets come into contact with MNF, they will be neutralized after receiving electrons or transferring electrons to fibers of MNF. At the same time, neutral droplets will lose the lone pair electrons from the oxygen atoms caused by the contact electrification between water and fiber surface. Correspondingly, fibers of MNF will be charged positively and negatively as shown in Fig. 6 , and the negative and positive surface potential of MNF is distributed randomly as shown in Fig. 5 as well. It is believed that electron transfer between the water jet and fibers of MNF is the main phenomenon during the triboelectric charging process. In addition, with functional materbatch added, electron transfer between the water droplet and fiber surface become more efficiently and more available charge densities are filled, resulting in MNF with higher static surface potential consequently. For producing electret filters, triboelectrification generally needs more than one components to be present in order to make full use of the electrostatic attraction filtration mechanism. That is, one kind of fibers from the more negative side of the triboelectric series, and one from the more positive side. However, MNF used for the hydro charging treatment is composed with only one kind of fibers which was blended with 2.5% electret masterbatch. In the study of the solid-liquid TENG 19 , as shown in Fig. 9 , when a water drop falls down and contacts with the thin film, the ionization of surface groups on the film will cause it to be negatively charged and cause a positively charged electrical double layer (EDL) on the contact surface of the water drop to maintain electrical neutrality. As the water drop is leaving the thin film, a negative electric potential difference will be established between the electrode and ground. In the short-circuit case, electrons are transferred from the electrode to ground. In the study of solid-liquid electrification 33 , as shown in Fig. 10 , when water (initially uncharged) flows across, and then falls off a solid surface under its own weight, it acquires a net positive charge. Consequently, the solid acquires a net negative charge. In conclusion, solid with different charge property is obtained after the solid-liquid electrification/TENG and triboelectric charging treatment studied in this paper. The solid surface is negatively charged in the solid-liquid In conclusion, a meltblown nonwoven filter with high filtration efficiency was developed by triboelectric charging process and the charge origin mechanism was analyzed for the first time. The effect of the water conductivity and drying temperature on the filtration efficiency of MNF was investigated. In addition, metal and inorganic elements in the masterbatch and water before and after triboelectric charging treatment were measured in order to uncover the charge transfer mechanism. More details are summarized as follows: The conductivity of water played a significant role on the filtration efficiency of triboelectric charged MNF which decreased with the increase of the conductivity of water significantly. MNF with filtration efficiency as high as 96.8% was obtained by using water with the conductivity as low as 1.1 μS/cm. On the other hand, the drying temperature didn't have obvious influence on the filtration efficiency of triboelectric charged MNF. The metal and inorganic elements content of the masterbatch used in this paper was quite different from the corona charging masterbatch, in which the Mg content was much lower than that of the corona charging masterbatch while more Ba and B elements appeared. On other hand, metal and inorganic elements in the triboelectric charged water were not higher obviously than those in the original water, suggesting that ion transfer between the MNF and water is not the main origin of static charges on fiber surface. It is found that negative and positive charges generated simultaneously on fiber surface of MNF after triboelectric charging treatment which is more desirable as a filter. In contrast, only one kind of surface charges can be achieved in the study of solid-liquid TENG. It is believed that electron transfer between the water jet and fibers of MNF during the triboelectric charging process is the main origin of charge carriers, rather than originating from ions transfer. All data generated or analysed during this study are included in this published article and its supplementary information file. Nonwoven fabrics and its application Charging characteristics for electret filter materials Electrostatic capture efficiency enhancement of polypropylene electret filters with barium titanate Boehmite nanoparticles incorporated electrospun Nylon-6 nanofiber web for new electret filter media Theory and techniques of electrostatic charging of melt-blown nonwoven webs Meltblown fiber web with staple fibers Method of charging electret filter media The effect of water-quenching on the electrostatic charging of fibers and fabrics during the melt-blowing process Development of a melt-blown nonwoven filter for medical masks by hydro charging All-plastic-materials based self-charging power system composed of triboelectric nanogenerators and supercapacitors All-in-one 3D acceleration sensor based on coded liquid-metal triboelectric nanogenerator for vehicle restraint system Additive manufacturing-based recycling of laboratory waste into energy harvesting device for self-powered applications Porosity modulated piezo-triboelectric hybridized nanogenerator for sensing small energy impacts A green metal-organic framework-cyclodextrin MOF: a novel multifuntional material based triboelectric nanogenerator for highly efficient mechanical energy harvesting Using the gravitational energy of water to generate power by separation of charge at interfaces A study of sustainable green current generated by the fluid-based triboelectric nanogenerator (FluTENG) with a comparison of contact and sliding mode Spontaneous occurrence of liquid-solid contact electrification in nature: toward a robust triboelectric nanogenerator inspired by the natural lotus leaf Harvesting water drop energy by sequential contact-electrification and electrostatic-induction process Quantifying electron-transfer in liquid-solid contact electrification and the formation of electric double-layer Water behavior based electric generation via charge separation Washable multilayer triboelectric air filter for efficient particulate matter PM2.5 removal A self-powered electrostatic adsorption face mask based on triboelectric nanogenerator A droplet-based electricity generator with high instantaneous power density Electrostatic electrochemistry at insulators Study on correlation of filtration performance and charge behavior and crystalline structure for melt-blown polypropylene electret fabrics Fibrous filter media Design of electret polypropylene melt blown air filtration material containing nucleating agent for effective PM2.5 capture Electret stability related to spherulites in polypropylene Electrostatic charging due to separation of ions at interfaces: contact electrification of ionic electrets Correlating material transfer and charge transfer in contact electrification Water behavior based electric generation via charge separation Spontaneous electrical charging of droplets by conventional pipetting H.W. wrote the main manuscript text and Y.W. prepared all figures except figure 3 which was prepared by J.W. All authors reviewed the manuscript. The authors declare no competing interests. The online version contains supplementary material available at https:// doi. org/ 10. 1038/ s41598-022-04838-3.Correspondence and requests for materials should be addressed to H.W.Reprints and permissions information is available at www.nature.com/reprints.Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.