key: cord-0842729-b5zxmr10 authors: Hurtado, Alejandro; Aljabali, Alaa A. A.; Mishra, Vijay; Tambuwala, Murtaza M.; Serrano-Aroca, Ángel title: Alginate: Enhancement Strategies for Advanced Applications date: 2022-04-19 journal: Int J Mol Sci DOI: 10.3390/ijms23094486 sha: a8dc0ba06bc7cff0a6f9d39c887556ab1d0cebe8 doc_id: 842729 cord_uid: b5zxmr10 Alginate is an excellent biodegradable and renewable material that is already used for a broad range of industrial applications, including advanced fields, such as biomedicine and bioengineering, due to its excellent biodegradable and biocompatible properties. This biopolymer can be produced from brown algae or a microorganism culture. This review presents the principles, chemical structures, gelation properties, chemical interactions, production, sterilization, purification, types, and alginate-based hydrogels developed so far. We present all of the advanced strategies used to remarkably enhance this biopolymer’s physicochemical and biological characteristics in various forms, such as injectable gels, fibers, films, hydrogels, and scaffolds. Thus, we present here all of the material engineering enhancement approaches achieved so far in this biopolymer in terms of mechanical reinforcement, thermal and electrical performance, wettability, water sorption and diffusion, antimicrobial activity, in vivo and in vitro biological behavior, including toxicity, cell adhesion, proliferation, and differentiation, immunological response, biodegradation, porosity, and its use as scaffolds for tissue engineering applications. These improvements to overcome the drawbacks of the alginate biopolymer could exponentially increase the significant number of alginate applications that go from the paper industry to the bioprinting of organs. Alginate has established itself as an excellent biodegradable, renewable, and biocompatible material with non-immunogenicity and easy gelation capacity [1, 2] . This biopolymer can be produced from brown algae or microorganism culture [3, 4] . Alginate is a U.S. FDA-approved product currently used in several medical applications, such as thickening stabilizing agents for dental impression materials and wound healing treatments in gel form [5] . Alginate currently possesses an immense number of industrial applications in a wide range of fields, such as biotechnology, bioengineering, biomedicine, and clinical applications, the pharmaceutical industry, chemical, textile, packaging and construction industry, food and drinks, aquaculture, dentistry, paper industry, arts and crafts, and the leisure industry (Table 1) . Table 1 . Application areas of alginate and its specific uses. Biotechnology, bioengineering, biomedicine, and clinical Dressings for wounds and burns [6, 7] Heavy metal chelator [8, 9] Scaffolding in tissue engineering [10] [11] [12] [13] Controlled release [14, 15] 3D bio-printing [16, 17] Prosthesis, dental molds and impression materials [18] [19] [20] [21] Immobilization of enzymes and cells [2, 22] Pharmaceutical industry 45] Confectionery and gastronomy in general [46, 47] Aquaculture Binder for food [48, 49] Paper industry Thickener [39] Arts and crafts Taxidermy molds [44, 50] Leisure industry Protective masks [51, 52] Biotechnology, bioengineering, biomedicine, and clinical areas include dressings for wound healing [6, 7] , heavy metal chelators [8, 9] , tissue engineering [10] [11] [12] [13] , control drug delivery [14, 15] , 3D bio-printing [16, 17] , prosthesis, dental molds and impression materials [18, 19] , and cell immobilization [2, 22] . In drug delivery, alginate hydrogels can efficiently encapsulate compounds such as insulin [53] or diverse enzymes [54] to be released because they possess adequate porosity for these purposes. Alginate can be used as a carrier of proteins to protect them from degradation and minimize denaturation [55] . There is an increasing use of alginate hydrogels in the human body, resulting in no adverse effects [56] ; these gels have great potential in tissue regeneration, such as bone, muscle, nerve, pancreatic, or hepatic tissue, in combination with cell transplantation and/or delivery of growth factors [57] [58] [59] . The pharmaceutical industry includes food supplements [23], treatment for gastric reflux [24, 25] , and cancer therapy [26, 27] . Alginate can be combined with drugs (e.g., ketoprofen) in mixtures to exhibit anti-inflammatory effects after oral administration for colon diseases [60] . Alginate has also shown great potential in the chemical, textile, packaging, and construction industry, including cosmetics [28, 29] Alginate polymer chains can generate gels that can be manufactured by acid precipitation or ionic reticulation, called ionotropic gelation [94] . Precipitation of acids to form alginate gels occurs as soon as the pH is reduced to parameters lower than the pKa or a dissociation coefficient of the biomaterial. Alginate has a negative charge over a fairly large pH spectrum [95] . The lowering of the pH rate impacts the alginate mixture in a couple of ways: (1) the precipitation of alginate generating those aggregates is caused when the pH is rapidly reduced; (2) the alginate gel is generated with a gradual and more stable reduction of pH [96] . Another factor is the consistency of the alginate achieved by molecular bonding of hydrogen and having the M-block residue factor in as they act appropriately in the mechanism of gel formation. However, gelation by ionic cross-linking to form ionic gels is caused when carboxylic group residues possessing a negative charge interact with divalent or trivalent cations or cationic materials [97, 98] . The formation of alginate gels is mainly due to abundant GG blocks, which are responsible for the specific anionic bond, and the gelling properties of alginate hydrogels come from there [99] . It should be noted that the units of the MM block form a linear polymer, whereas those of the GG block form loop-shaped or rotational groups (see Figure 1a ) [100] . The ability of SA to form gels when it is immersed in a solution containing divalent cations such as Ca 2+ is the fundamental concept for using this biomaterial in different fields, including biological and technological fields [101] . Alginate has many carboxyl and hydroxyl groups in its polymeric structure, making alginate a suitable precursor, since it acts as a chelating agent [102] . Gelation by ionic crosslinking is generated by applying two external or internal techniques. These two vary in the divalent cations applied and in the gel formation in terms of kinetics. First, the external way is based on introducing the ions with an external base Alginate polymer chains can generate gels that can be manufactured by acid precipitation or ionic reticulation, called ionotropic gelation [94] . Precipitation of acids to form alginate gels occurs as soon as the pH is reduced to parameters lower than the pKa or a dissociation coefficient of the biomaterial. Alginate has a negative charge over a fairly large pH spectrum [95] . The lowering of the pH rate impacts the alginate mixture in a couple of ways: (1) the precipitation of alginate generating those aggregates is caused when the pH is rapidly reduced; (2) the alginate gel is generated with a gradual and more stable reduction of pH [96] . Another factor is the consistency of the alginate achieved by molecular bonding of hydrogen and having the M-block residue factor in as they act appropriately in the mechanism of gel formation. However, gelation by ionic cross-linking to form ionic gels is caused when carboxylic group residues possessing a negative charge interact with divalent or trivalent cations or cationic materials [97, 98] . The formation of alginate gels is mainly due to abundant GG blocks, which are responsible for the specific anionic bond, and the gelling properties of alginate hydrogels come from there [99] . It should be noted that the units of the MM block form a linear polymer, whereas those of the GG block form loop-shaped or rotational groups (see Figure 1a ) [100] . The ability of SA to form gels when it is immersed in a solution containing divalent cations such as Ca 2+ is the fundamental concept for using this biomaterial in different fields, including biological and technological fields [101] . Alginate has many carboxyl and hydroxyl groups in its polymeric structure, making alginate a suitable precursor, since it acts as a chelating agent [102] . Gelation by ionic crosslinking is generated by applying two external or internal techniques. These two vary in the divalent cations applied and in the gel formation in terms of kinetics. First, the external way is based on introducing the ions with an external base to generate the gels, The physicochemical properties of alginate may be modified because they depend on the conformation of the biopolymer [113] . The mannuronic and guluronic building blocks that make up the alginate structure and the conformation and partitioning in the alginate structure must be considered to vary the alginate characteristics [39] . There are up to 200 different types of alginate with different molecular mass and/or chemical compositions of the associated elements [114] . Alginates show different percentages of glycosidic monomers that make up the alginate structure [115] . Therefore, its applications depend on its properties and are directly proportional to its structure type. On the other hand, alginates are non-toxic, biocompatible, and biodegradable materials [116] . The ability to degrade alginate is impossible in mammals, mainly because the enzyme necessary for the process is not present [117] . However, degradation does occur in alginate hydrogels crosslinked with ions as there is an outflow of ions into the environment with exchange reactions. The degradation rate of alginates can be controlled and may be very slow, preventing degradation in the short-term [118] . Other important physicochemical properties of alginate involve selective bonding of divalent cations, the basis of hydrogel formation [119] . The pH is essential for the solubility of alginates [119] . Thus, a very low pH causes the precipitation of alginate chains [120] . Any variation in ionic strength is likely to affect solubility and viscosity; dispersion and solubility will vary with different ionic strengths [121] . Thus, alginate will have another state depending on pH: alginate becomes a gel at neutral pH, alginate swells at pH 3, and alginate becomes more viscous at pH 8 [122] . The principles of the properties of alginate gelling are based on this simple characteristic [123] . The selectivity of alginate blocks is very relevant as G-blocks are more efficiently bound to divalent ions than M-blocks [124] . In addition, G-blocks have a significant value because they have an overall characteristic that they can be presented as regulators or modulators of gelation when dissolved with gelling alginates [125] . The selectivity of this polysaccharide for positive ions with double valence is precise to the number of ions in the natural biomaterial hydrogel [126] . The control mechanism for the union of alginates with ions becomes a procedure of great importance for its final structure [127] . The mediated introduction of binding cations is made possible by two mechanisms for preparing an alginate natural biomaterial hydrogel: the dissemination and the inner fixation methods [119] . The dissemination process differs because it allows the introduction of a crosslinking cation from a large external reservoir into an alginate solution [128] . The diffusion setting is characterized by a much faster gel rate and is applied for immobilization purposes, where each of the polysaccharide dissolution droplets makes a single drop of gel with an active agent included within it [127] . The internal method differs from diffusion by the mediated secretion of the cross-linking ion already inside the hydrogel [129] . Properties of the material, such as stability and ionically cross-linked gels, are essential for biological use [130] . Alginate is sensitive to depolymerization because it is composed of simple chain polymeric material [130] . Thus, the stability of glycosidic bonds is variable but can be broken by techniques that apply pH variation or oxidation with free radicals [131] . Hydrolysis of the gel occurs when complex stability is reduced to a pH below 5 because there is a higher concentration of protons; instead, decomposition is generated at a pH above 5. Autoclaving should not be used to sterilize SA. γ-radiation leads to irreversible alginate damage with hydroxyl free radical (OH*) formation [132] . Since this polymer can be dissolved in water at ambient temperature, sterile filtration is recommended. Crosslinked alginate in the form of films can be sterilized by cleaning with absolute ethanol and subsequent UV irradiation for 1 h per side [68, 71, 104, [133] [134] [135] . Currently, alginate biosynthesis can arise from brown algae, such as Laminaria Hyperborea, or bacteria, such as Pseudomonas aeruginosa [136] . The generation of brown algae began in California in 1929; soon after, in 1939, it was developed in some European countries and Japan [137] . At present, there is a high regional imbalance in seaweed production [138] . Thus, 35.8 million tons of global seaweed production is contributed to by 49 countries/territories and 97% of the world production production is contributed to by 49 countries/territories and 97% of the world product comes from Asia. Thus, the major producer countries per area are China, Indonesia, public of Korea, and Philippines in Asia. In Americas, Chile is the major producer at same level of Japan. In Europe, Norway and France are the major producers but w production rates three and eight times lower than that of Japan, respectively. Algina are derived from brown seaweed and are produced mainly in the USA, Norway, Chi Canada, France, and Japan [139] . Among the advantages of obtaining alginate from bro algae is that most alginophytes have large quantities of the product and generate la areas on the rocky shores with little depth [140, 141] . Figure 2 shows the areas where so algae used for alginate production are found throughout the world [142] . Alginate is found in algae, mainly in the cell wall and especially in species such brown algae [143] . Alginate extraction from brown algae is carried out based on vario mechanisms, such as applying various centrifuges, variations in pH, and allowing prec itation [99] . The yield of alginate extracted from brown algae is about 44.32% on avera [144] . More than 200 types of alginate are commercially available, and most of them extracted from wild brown seaweed [58] . Among the species of brown algae from wh alginate is extracted, Macrocystis pyrifera is one of the most essential [145] . Among the s cies that produce alginate, from the industrial point of view, the most relevant Ascophyllum nodosum, Macrocystis pyrifera, and Laminaria hyperborea [142] . A novel meth is used to cultivate brown algae in the laboratory using free-living gametophytes, as th have advantages in terms of genetic selection capacity, clone generation, and product of large quantities [142, 146] . The relative molecular mass of alginate ranges from 32 to kg/mol [147] , and the leading causes of variability are the algae's species and age [14 Table 2 shows the main types of alginate extracted from different brown algae. Alginate is found in algae, mainly in the cell wall and especially in species such as brown algae [143] . Alginate extraction from brown algae is carried out based on various mechanisms, such as applying various centrifuges, variations in pH, and allowing precipitation [99] . The yield of alginate extracted from brown algae is about 44.32% on average [144] . More than 200 types of alginate are commercially available, and most of them are extracted from wild brown seaweed [58] . Among the species of brown algae from which alginate is extracted, Macrocystis pyrifera is one of the most essential [145] . Among the species that produce alginate, from the industrial point of view, the most relevant are Ascophyllum nodosum, Macrocystis pyrifera, and Laminaria hyperborea [142] . A novel method is used to cultivate brown algae in the laboratory using free-living gametophytes, as they have advantages in terms of genetic selection capacity, clone generation, and production of large quantities [142, 146] . The relative molecular mass of alginate ranges from 32 to 400 kg/mol [147] , and the leading causes of variability are the algae's species and age [148] . Table 2 shows the main types of alginate extracted from different brown algae. Alginate is a bio-polysaccharide that was first isolated from marine macroalgae, but later, this sugar was observed in differentiated bacteria [161] . Alginate is an essential component of the biofilm of bacteria that produce pulmonary fibrosis disease [162] . Of the bacterial types, the most relevant for alginate production are the species Pseudomonas aeruginosa [163] and Azotobacter vinelandii [164] ; they are capable of producing large amounts of this biopolymer as an excretion polysaccharide in the bacterial biofilm [163] . In the first bacterium, alginate has a relevant role in the biofilm structure, and A. vinelandii uses alginates that possess high G-block and low M-block concentrations to be more persistent in cysts [165] . The PMI-GMP isomerase enzyme is fully involved in different early and late alginate production processes in these bacteria [166] . Multiple genes are found in the alginate generation pathway necessary for its production ( Table 3) , some of which are responsible for the proper functioning of alginate polymerase [163] . Table 3 . Genes involved in the production of alginate by bacteria and their gene products. Product Reference algA Phosphomannose isomerase/GDP-mannose pyrophosphorylase [167] [168] [169] algB ntrC [170, 171] Some genes are not directly related to alginate synthesis but produce alternative proteins [180] . Alginate acts as an inducer of increased alginate production in a positive feedback reaction at the gene promoter of the biosynthesis pathway [170] . These genes could be used for molecular modifications in genetic engineering [181] . Alginate matrix is governed by an enzyme called mannuronan-C-5 epimerase that interconnects stereospecific epimers [182] . Thus, alginate can be chemically modified by acetylation and epimerization, located in the time interval in which they are transferred to the periplasmatic space [183] . Genetic engineering and protein engineering can be used to produce bacterial alginates by modeling bacterial genetics [165] . Finally, it should be noted that only alginates produced from bacterial cultures have a greater capacity to interact with water molecules because the glycosidic product is found with acetylation at carbon positions 2 and 3 [164] . The main alginate types produced from different bacterial cultures, M/G ratios, and bacteria features from bacteria are shown in Table 4 . Mucoid biofilms [186, 188] As mentioned above, there are multiple genes involved in synthesizing these genes; up to 24 stand out in the bacterium P. aeruginosa [167] . Most of these genes are found on the bacterial chromosome, and so far, there are no studies that show that it is located in plasmids [180] . There is a tremendous advantage in alginates produced by bacteria over alginates produced by algae because the quality generated is much better, and their characteristics and activities have been studied in detail [97, 189] . However, alginate produced from bacterial culture presents several disadvantages concerning alginate extracted from brown algae. Thus, in the first place, the production of bacterial alginate is much more expensive than that produced from brown algae [190] . Furthermore, extraction is interrupted by the enzyme alginate lyase, and, in addition, the mucoid strains of P. aeruginosa often stop producing alginate when grown in the laboratory [136] . Furthermore, the alginate produced by bacteria has the existence of the enzyme epimerase that hinders the procedure [136, 191] . After extraction, the alginate contains residues, such as heavy metals, protein compounds, toxins, and polyphenols [97] that compromise the biocompatibility of this biopolymer [147, 165] . Therefore, accurate extraction techniques must be performed, eliminating upstream and unnecessary compounds, and purification must be performed to eliminate downstream compounds, avoiding an immunogenic response in biomedical applications [83] . Alginate used in medicine and introduced into the body without purification leads to cell overgrowth around the capsules of this biopolymer, so purification techniques must be used to reduce contaminants such as immunogenic proteins [192, 193] . Unpurified alginate, raw alginate, in a sphere for directed microencapsulation introduced into living organisms, is also known to produce characteristic pathogen-associated molecular patterns (PAMPs) and damage-associated molecular patterns (DAMPS) that stimulate the immune response [53] . The viscosity must also be considered within alginate purification, as this parameter is affected after purification [194] . Alginate can be purified by filtration, extraction, and precipitation [195] . A novel alginate purification method is the chemical purification procedure applied to alginates with variations in the proportions of M-monomers and G-monomers [196] . It improves stability and reduces diffusion, permeability, and increases the practical defense of quiescent cells against the body's response to the immune process in such a case [197] . Correct elimination of downstream compounds decreases immunogenic factors promoting the non-activation of the immune system [198] . Some of these impurities include endotoxins, certain proteins, and polyphenols [198] . Polyphenols can be dangerous for humans as reported by the World Health Organization, and can possibly accumulate in the body. Endotoxins and proteins have been associated with a reduced biocompatibility of the alginate. Thus, a considerable reduction of proteinic contaminants is obtained using size exclusion chromatography for alginate purification [199] . Another technique for alginate purification is the removal of mitogenic compounds by free-flowing electrophoresis [200] . The purification of alginate for clinical use has increased biocompatibility [201] . Many researchers prefer to buy ultrapure alginate directly from specialized companies, such as NovaMatrix-DuPont [202] , to reduce work time. These companies offer well-characterized ultra-purified alginates with different molecular weighs and M/G rations in sterile conditions. Peptide-coupled alginates with enhanced cell adhesion properties can also be purchased. A broad range of material engineering enhancement approaches have been achieved so far in the alginate biopolymer, in terms of mechanical reinforcement, thermal and electrical properties, wettability, and water sorption and diffusion. The mechanical performance of alginate increases at higher concentrations [197] and higher G block contents with respect to the amount of M blocks [203] . Even though alginates possess excellent properties, such as biodegradability, biocompatibility, etc., their mechanical performance is relatively poor, especially in the hydrated state [204] . In this regard, many material engineering approaches have been developed, such as reinforcement combining alginate with other compounds, polymers, by nanofilling advanced materials such as nanofibers, carbon nanomaterials, nanometals, nanocellulose, or nanoclay, among others. Several multicomponent polymer structures using alginate have been developed, such as mixtures [205] , graft copolymers [206, 207] , semi-interpenetrating polymer networks (semi-IPNs), such as alginate/chitosan [65] , calcium alginate/polycaprolactone [208] , or sodium alginate-g-poly(sodium acrylate) [64] , and the full interpenetrated polymer network (IPN), such as alginate/poly(acrylic acid) [62, 63] or sterculia gum/calcium alginate [61] . In addition, to achieve mechanical reinforcement, other enhancements of properties can be achieved by these multicomponent systems, such as heat-resistant capacity [209] , cell adhesive properties [65] , sensibility as drug delivery systems [95] , etc. Different polymers such as cellulose acetate phthalate (CAP), polyphosphate (PP), sodium carboxymethylcellulose (CMC), cellulose sulphate (CS), and dextran sulfate (DS) have mixed with alginate to enhance its mechanical properties [210, 211] . The microcapsules formed with alginate that are loaded with insulin were reinforced with another polymer, such as chitosan to increase insulin protection [211] . The mucoadhesive properties of chitosan have been combined with alginate [212] . Alginate can also be mixed with polymers of different chemical nature, such as those belonging to or derived from cellulose, acrylic polymers, pectins, and polyvinylpyrrolidone [213] . The mixture of polyethylene glycol acrylate with alginate has successfully promoted chemical stability for Langerhans microencapsulation of the islets for insulin release [214] . In recent reports, benzoyl peroxide has generated a polymerized matrix of itaconic acid with SA as an improvement [206] . Other investigations highlighted that using alginate with other compounds to generate a stable polymeric matrix has a significant value. Polymers such as poly(N-isopropylacrylamide) (PIPAAm) and poly (acrylic acid) (PAA) have been used to generate spheres by processes such as microwave-mediated secretion of indomethacin (IND) [207] . Hydrogels formed by semi-IPN have been developed using alginate and other common polysaccharides, hyaluronic acid [215] or chitosan [65] . Other semi-IPNs able to trap glucose isomerase consist of hydrogels that intertwine polyacrylamide and alginate chains [216] . A very recent study has reported the use of alginate and xanthan gum to produce a heart patch [217] . The mechanical properties of alginate-based hydrogels can be improved with the incorporation of fibers and nanofibers. Bonding with fibers and nanofibers promotes the improvement of properties, such as tensile strength, elongation, breakage, and compression resistance [218] . Sodium alginate-polyvinyl alcohol hydrogels have been reinforced with cellulose nanofibers [219] . These composites showed enhanced density, viscoelasticity, and mechanical strength: 79.5 kPa in compressive strength, 3.2 times higher than that of the neat hydrogel. Cellulose nanofibers and bio-extracts showed synergistic effects for fabricating high strength sodium alginate-based composite bio-sponges with antibacterial properties [220] . Cellulose fibers have been used to reinforce a bioadhesive formulation based on a combination of gelatin and alginate crosslinked with water-soluble carbodiimide [221] . These composite materials showed a dramatic increase in the viscosity and in the burst strength. Cellulose fibers and cellulose nanowhiskers isolated from mulberry pulp were used with alginate hydrogels to increase mechanical properties and tensile strength [222] . The bonding of alginate hydrogels with cellulose nanofibers (NFC) and microfibrillated cellulose (MFC) reinforced mechanical properties, tensile strength, and reduced water vapor permeability [223, 224] . Nanocrystalline nanocellulose were used with alginate hydrogel films to significantly increase tensile strength, water vapor permeability, and molecular interactions [225] . Alginate hydrogels bonded with nanocellulose to provide excellent thermal stability and high water resistance have also been reported [226] . Improved mechanical performance of alginate hydrogels can be achieved with cellulose nanocrystal(s) (CNC) and cellulose nanocrystal oxide (OCNC) [73] . Hydrogel alginate spheres, together with magnetic nanocellulose, were used to improve drug delivery and release, mechanical reinforcement, and specific physicochemical characteristics of the final complex [227] . The mechanical properties of an alginate hydrogel were improved by reinforcement with ethanol-treated polycaprolactone nanofibers [228] and with aligned electrospun gelatin nanofibers [229] . Thus, the alginate/gelatin nanofiber hydrogel increased up to 541% in tensile modulus and 1690% in tensile strength, while keeping good transparency. Fiber reinforcement is also used in additive manufacturing. Thus, a 3D-printed fiber-reinforced hydrogel composite consisting of a combination of alginate/acrylamide gel precursor solution and an epoxy-based UV-curable adhesive can be fabricated [230] . Alginate was mixed with nanocellulose to allow 3D printing as a high-printability ink for fabric scaffolds [75, 76] and 3D bioprinting with NFC [17,77]. Calcium alginate films were synthesized with the incorporation of several amounts of carbon nanomaterials (CNMs), such as carbon nanofibers (CNFs) and graphene oxide (GO) [4, [66] [67] [68] [69] . These composite structures showed enhanced mechanical performance and much faster water diffusion through the carbon nanochannels formed in the alginate polymeric matrices. Thus, reinforced calcium alginate/GO composites have been developed ( Figure 3 ) [71] . Compared with calcium alginate without any reinforcing agent, a nine-fold increase in the compression modulus of calcium alginate is seen when dry and up to a six-fold increase when hydrated for 1% w/w of GO. According to Figure 3 , the opacity of alginate films with GO increases with the addition of GO to the composite. When little GO loading Compared with calcium alginate without any reinforcing agent, a nine-fold increase in the compression modulus of calcium alginate is seen when dry and up to a six-fold increase when hydrated for 1% w/w of GO. According to Figure 3 , the opacity of alginate films with GO increases with the addition of GO to the composite. When little GO loading (0.1% w/w) is introduced into the alginate, the compressive modulus significantly increases. The addition of GO with an increase of calcium ions allows to generate alginate gels with a significant improvement in the mechanical reinforcement characteristic, which can be up to a multiple of four times the increase of this parameter [4] . A similar effect is presented when CNFs are used to reinforce calcium alginate [66] . In addition, the water absorption of the final composite increases with a very low amount of CNFs introduced into the alginate polymeric matrix. However, GO nanomaterial is more expensive than CNFs, so it is a factor that must be considered to produce these materials at a large scale. Carbon nanofibers are CBNs with a high degree of hydrophobicity [231] . Therefore, the composite structure generated by incorporating CNFs into the hydrophilic alginate polymer is not homogeneous (Figure 4 ) [68] . . Film composite structures formed by calcium alginate and graphene oxide (GO). Increasing concentrations of GO in the range of 0-1% w/w. The opacity is presented as mean ± standard deviation in the base part of the samples. Reprinted with permission from Elsevier [71] . Compared with calcium alginate without any reinforcing agent, a nine-fold increase in the compression modulus of calcium alginate is seen when dry and up to a six-fold increase when hydrated for 1% w/w of GO. According to Figure 3 , the opacity of alginate films with GO increases with the addition of GO to the composite. When little GO loading (0.1% w/w) is introduced into the alginate, the compressive modulus significantly increases. The addition of GO with an increase of calcium ions allows to generate alginate gels with a significant improvement in the mechanical reinforcement characteristic, which can be up to a multiple of four times the increase of this parameter [4] . A similar effect is presented when CNFs are used to reinforce calcium alginate [66] . In addition, the water absorption of the final composite increases with a very low amount of CNFs introduced into the alginate polymeric matrix. However, GO nanomaterial is more expensive than CNFs, so it is a factor that must be considered to produce these materials at a large scale. Carbon nanofibers are CBNs with a high degree of hydrophobicity [231] . Therefore, the composite structure generated by incorporating CNFs into the hydrophilic alginate polymer is not homogeneous (Figure 4 ) [68] . ultrathin sections of calcium-cross-linked alginate with CNFs at 1% w/w ratio (b); cryo-scanning electron microscopy (cryoSEM) of calcium-crosslinked alginate films, neat (c,e) and with CNFs (d,f), hydrated at 26 ± 0.5 • C and 37 ± 0.5 • C for 1 day, respectively. Reprinted with permission from Elsevier [68] . Figure 4 shows that in the swollen state, when the alginate gels are immersed in pure water, the pores undergo opening to introduce this water into the interior of the composite. It is of note that swelling at the body temperature (37 ± 0.5 • C) produces a morphology with larger pores than swelling at 26 ± 0.5 • C (Figure 4 ) [68] . With the addition of more CNFs, higher tensile properties are achieved and high resistance when they are not in the swollen state [66] . The combination of zinc cations with GO presents itself as an exciting mixture for the medical industry and increases properties, such as thermal characteristics, degradation, and exact dielectric properties [104, 232] . Single-walled carbon nanotubes (SWCNT) are used to promote breakage reinforcement and mechanical traction of many hydrogels [233, 234] . Thus, alginate combined with SWCNTs also showed increased mechanical reinforcement, making these composites ideal candidates for many biomedical applications [235] . Carbon nanotubes (CNTs), in combination with alginate, can be used for drug portability due to greater flexural strength, more excellent stability, less drug leakage, and a much more sustainable release profile [236] . Multi-walled carbon nanotubes (MWCNTs) in alginate hydrogels increase porosity and decrease the degree of the degradability of this hydrogel [237] . However, CNFs have recently shown to be capable of accelerating the biodegradability of the hydrophobic poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) biopolymer [238] . CNTs, similar to other CBNS, reinforced the dehydration and swelling of alginate hydrogels [239] . The addition of GO into SA has increased structural, morphological, and thermal stability and improved mechanical and traction properties [240, 241] . Moreover, 3D cross-linked networks of GO in the form of irregular tubes incorporated into alginate hydrogels showed mechanical improvements due to microstructural changes [69] . Reduced GO (rGO) increases properties just like normal GO or Gr, making it a good alternative material [242, 243] . GO improves the compression performances of alginate hydrogels when applied in a small concentration (0.1% w/w) [4] . The physical properties of alginate can significantly change depending on the green synthesis followed [67] . Thus, novel routes to synthesize alginate using small concentrations of GO have been proposed to generate a measurable increase in water diffusion capacity and different mechanical traction characteristics, among other properties [67] . In addition to CBNs, a broad range of nanoparticles of different chemical nature, such as ceramic, metal/metal oxide, and polymeric nanoparticles can be dispersed in alginate matrix to form blends in the form of hydrogels, films, mats, fibers, or microcapsules with superior properties [244] . These composites with nanofillers have tailored functionality and promising physical, chemical, electrical, and biological properties than pristine ones. Thus, an enhancement strategy consisting of in situ reduction of silver nanoparticles (AgNPs) by sodium alginate to obtain a silver-loaded composite with enhanced mechanical and antimicrobial properties has been reported recently [245] . Alginate biofunctional films modified with melanin and zinc oxide/AgNPs showed enhanced tensile strength [246] . Alginate-based mats reinforced with ZnO nanoparticles were prepared via an electrospinning technique and subjected to a washing-cross-linking process composed of homogeneous nanofibers with a diameter of 100 ± 30 nm [247] . Nanocomposite films based on sodium alginate and polyaniline and TiO 2 nanoceramic, synthesized by the solution casting method, showed promising mechanical, electrical, and antimicrobial activity for food packaging applications [248] . Preparation and characterization of polyaniline/sodium alginate-doped TiO 2 nanoparticles showed promising mechanical and electrical properties and antimicrobial activity for food packaging applications [248] . ZnO and ZnO/CaO nanoparticles in alginate films were characterized mechanically to be used for food packaging [249] . Hydroxyapatite nanoparticles have also been used to enhance the mechanical performance and provide antibacterial properties to alginate films [250] . The use of titanium in combination with calcium alginate is a procedure that promotes immobilization efficiency, increasing the mechanical properties of the hydrogel up to three times compared to pure calcium alginate [251] . Montmorillonite nanoclay (MMT) and CaCl 2 -reinforced alginate-based nanocomposite film was prepared by the solvent casting method to increase internal mechanical and physicochemical properties [252, 253] . The use of different nanoclays, such as MMT, laponite (LP), and sumecton (SUM), together with alginate, can be used as reinforcing agents for biomedical applications [74] . Biopolymers, such as alginate, are often combined with two types of nanoclays, such as kaolinite sheets and halloysite nanotubes, to enhance mechanical performance [254, 255] . Incorporating nano-silica into an IPN produced with poly(acrylic acid) and alginate by UV polymerization increased its compressive strength and fracture resistance [63] . In bioprinting applications, cell-laden alginate-gelatin composite bio-ink with bioactive glass nanoparticles showed enhanced mechanical and biological properties [256] . The thermal properties of alginate can be improved by incorporating nanomaterials with excellent thermal properties, such as CBNs or metallic nanoparticles, among others [257, 258] . Thus, GO provides enhanced thermal resistance and stability to sodium alginate [240] , and this enhancement increases with GO content [259] . Moreover, 3D crosslinked networks of GO showed enhanced thermal properties than single GO nanosheets when incorporated into calcium alginate composite hydrogels [69] . Furthermore, the thermal properties of calcium alginate/GO composites can be tailored following different chemical routes [67] . The introduction of other CBNs, such as rGO into calcium alginate, can efficiently improve its thermal stability [260] . Alginate-CuO nanocomposite showed enhanced thermal stability with respect to neat alginate. In addition, these composites exhibited antifungal activity [261] . Thermogravimetric analysis (TGA) showed that the thermal stability of alginate/AgNPs composite films increased distinctively compared with neat alginate films [262] . The addition of inorganic and organic nanofillers, such as MMT and cellulose nanocrystals, has improved the thermal capacity of the alginate [263, 264] . The carboxymethyl konjac glucomannan polymer increased the physical properties, especially the thermal stability of SA hydrogels due to the intermolecular hydrogen bonds between both polymers [265] . The combination of SA, Gr, and polyvinyl alcohol (PVA) increased the thermal stability of the final composite [266, 267] . Thermal stability can be improved by combining halloysite and alginate [268] . However, the union of alginate with glycerol decreased the thermal decomposition capacity of the final composite [269] . Zinc crosslinked alginate improved thermal stability compared to that of SA [270] . Molybdenum disulfide nanoleafs incorporated into alginate hydrogels can provide enhanced thermal resistance [271] . The thermomechanical properties of alginate films were improved by incorporating SiO 2 , PVA, and glycerol [272] . Many materials, such as Gr, CNTs, CNFs, AgNPs, polypyrrole (PPy), among others, are excellent electrical conductive materials [257, 273, 274] . Therefore, they can provide electrical conductivity to alginate when they are incorporated into its biopolymer matrix. However, in these composites, the percolation threshold; that is, the connectivity between the conductive nanomaterials incorporated into the biopolymer, plays a very important role [275] . Parameters, such as nanoparticle types and forms, synthesis methods, treatments, and dimensionality, as well as polymer types and dispersion methods, have impact on the percolation threshold and, thus, on the maximum conductivity of the composite. The development of conductive composites has great potential in biomedical applications that allow the application of electrostimulation [276, 277] . In this context, various CNTs have been successfully applied to increase the electrical conductivity of alginate hydrogels [278] . Nanofibers composed of alginate and CNTs produced by electrospinning showed increased mechanical and electrical properties when a large amount of CNTs were added [279] . Oher graphene-based materials have been proposed to enhance the electrical properties of alginate [280] [281] [282] [283] [284] [285] . Thus, very recently, rGO, which has an electrical conductivity close to that of graphene, has been used to be produce electroactive calcium-alginate/polycaprolactone/rGO nanohybrid hydrogels for skeletal muscle tissue engineering [208] . Alginate complexes with metals, such as Ba 2+ , Sr 2+ , Pb 2+ , Cd 2+ , or Zn 2+ , present electrical properties similar to semiconductor materials [286] . Other strategies followed to increase the electrical properties of alginate consisting of incorporating bentonite (BNT) clay into the alginate matrix to form SA/BNT composites [287] . These composites showed increased conductivity and dielectric constants with an increasing percentage of BNT in the SA matrix [287] . SA, PVA, and graphene nanospheres bonded by the electrospection technique provided improved electrical properties suitable for the fabrication of conductive scaffolds for nervous tissue engineering application [277] . Aligned and random fibers made of Gr, SA, and PVA have been proposed as conductive scaffolds for peripheral nerve engineering [276] . The results of this study revealed that the aligned fibrous scaffolds closely mimicked the anisotropic structure of the native sciatic nerve and electrical stimulation significantly enhanced PC12 cell proliferation. Another approach to increase the electrical properties of alginate consisted of adding PPy, by chemical polymerization [288] . This conductive polymer achieved an improvement of up to more than 10 times the electrical conductance compared to natural alginate. The wettability of a material surface is usually characterized by contact angle (CA) measurements between solid and liquid interfaces [67, 289, 290] . Hydrophilicity or wettability of biomaterials is considered a very important parameter for certain applications, such as cell adhesion in tissue engineering [291] . Alginate hydrogels have a high degree of hydrophilicity, so water droplets extend along the alginate film surface, with an average CA of less than 15 • [292] . The incorporation of CBNs, such as GO nanosheets into calcium alginate, increases wettability [71] . The hydrophilicity of calcium alginate/GO composites can be tailored following different chemical routes [67] . Hydrophilic alginate-based multidentate biopolymers have been proposed for surface modification of CdS quantum dots [293] . A coating structure formed by alginate/Bioglass ® [294] and the addition of the water-soluble PVA polymer [295] showed suitable hydrophilic behavior for dental and orthopedic applications [296] . A study with alginate microcapsules showed that the smaller the size, the greater the wettability [297] . The addition of inulin increased wettability of microcapsules. Hydrophilic membranes consisting of an active alginate layer and supporting the chitosan layer on top of the base porous blended polyvinylidene fluoride (PVDF) membrane were prepared for pervaporation dehydration applications [298] . The blend of PVDF with 1% PMMA was shown useful in giving better surface properties for adhesion of the alginate and chitosan top layers. In addition, the high mechanical strength of PMMA [299] enhanced the mechanical performance of the alginate-based composite. The enhancement of water sorption and diffusion properties is very desirable in certain fields, such as biomedical engineering and industrial bioprocesses that employ immobilized cells or enzymes in calcium alginate hydrogels (biocatalysts) [4] . The improvement of water diffusion in bioprocesses implies the enhancement of mass transport and, thus, the increase of industrial productivity. This enhancement is also very desirable in many biomedical applications, such as tissue engineering, which, due to mass transport, plays an important role in cell survival [300] . One of the strategies to improve water diffusion (up to more than six times) consists of adding a minuscule amount of GO (0.1% w/w) to calcium alginate, simultaneously improving its compression modulus by a multiple of four-fold [4] . It has been reported that the transport of water through graphene-based nanochannels is ultrafast [301, 302] . However, the addition of GO produced a reduction in the swelling properties of the calcium alginate/GO hydrogel generated. The incorporation of low amounts of GO are desirable in order to reduce production costs as much as possible [4, 71] . Significant improvement in liquid water diffusion is also achieved by adding CNFs to crosslinked calcium alginate [66] . However, the incorporation of CNFs also reduce the water sorption of calcium alginate. Swelling of the alginate hydrogel was considerably inhibited by the union of GO or CNF nanoparticles, the alginate polymer chains and divalent ions of Ca 2+ [4, 66] . Swelling biomaterials can considerably increase membrane permeability but have an adverse effect and significantly decrease membrane selectivity [303] . Water absorption by SA can be significantly reduced by introducing GO nanosheets [304, 305] . This phenomenon is attributed to the formation of hydrogen bonds between oxygenated compounds, which produces improved resistance to swelling. In addition, the interaction between divalent metal ions, such as Ca 2+ and oxygenated functional groups in the basal plane and edges of the GO nanosheets in the alginate composite, considerably reduces the water absorption capacity [67] . PVA biopolymer is added to alginate to reduce swelling because it is hydrophilic, compact, and has a high degree of crystallinity [303] . Therefore, a small amount of PVA improves swelling resistance and reduces the entry of water into the alginate structure. Swelling measurements can be used as indicators of the degree of crosslinking of alginate [306] . Even though alginate possesses excellent biological performance, the enhancement of biological properties, such as biodegradation, antimicrobial activity, cell adhesion, proliferation, differentiation, and immunological challenges is very desirable in a wide variety of industrial fields. The biodegradation of alginate can be enhanced because the biopolymer strands may be relatively oxidized after the addition of sodium periodate ( Figure 5 ), breaking the bonds between the carbons of the cis-diol group and converting the chair conformation into an open chain. This reaction helps the degradation of the biopolymer backbone [307] . based nanochannels is ultrafast [301, 302] . However, the addition of GO produced a reduction in the swelling properties of the calcium alginate/GO hydrogel generated. The incorporation of low amounts of GO are desirable in order to reduce production costs as much as possible [4, 71] . Significant improvement in liquid water diffusion is also achieved by adding CNFs to cross-linked calcium alginate [66] . However, the incorporation of CNFs also reduce the water sorption of calcium alginate. Swelling of the alginate hydrogel was considerably inhibited by the union of GO or CNF nanoparticles, the alginate polymer chains and divalent ions of Ca 2+ [4, 66] . Swelling biomaterials can considerably increase membrane permeability but have an adverse effect and significantly decrease membrane selectivity [303] . Water absorption by SA can be significantly reduced by introducing GO nanosheets [304, 305] . This phenomenon is attributed to the formation of hydrogen bonds between oxygenated compounds, which produces improved resistance to swelling. In addition, the interaction between divalent metal ions, such as Ca 2+ and oxygenated functional groups in the basal plane and edges of the GO nanosheets in the alginate composite, considerably reduces the water absorption capacity [67] . PVA biopolymer is added to alginate to reduce swelling because it is hydrophilic, compact, and has a high degree of crystallinity [303] . Therefore, a small amount of PVA improves swelling resistance and reduces the entry of water into the alginate structure. Swelling measurements can be used as indicators of the degree of crosslinking of alginate [306] . Even though alginate possesses excellent biological performance, the enhancement of biological properties, such as biodegradation, antimicrobial activity, cell adhesion, proliferation, differentiation, and immunological challenges is very desirable in a wide variety of industrial fields. The biodegradation of alginate can be enhanced because the biopolymer strands may be relatively oxidized after the addition of sodium periodate ( Figure 5 ), breaking the bonds between the carbons of the cis-diol group and converting the chair conformation into an open chain. This reaction helps the degradation of the biopolymer backbone [307] . This oxidation, however, does not affect the alginate's ability to produce alginate hydrogels by crosslinking with divalent ions, such as calcium [118] . The degradation behavior of the gel highly depends on the degree of oxidation, in addition to pH and media temperature. Poly(aldehyde guluronate) (PAG) hydrogels can be prepared from alginate by acid hydrolysis and oxidation, followed by covalent cross-linking with adipic acid dihydrazide (AAD) (Figure 6 ) [308] . drogels by crosslinking with divalent ions, such as calcium [118] . The degradation behavior of the gel highly depends on the degree of oxidation, in addition to pH and media temperature. Poly(aldehyde guluronate) (PAG) hydrogels can be prepared from alginate by acid hydrolysis and oxidation, followed by covalent cross-linking with adipic acid dihydrazide (AAD) (Figure 6 ) [308] . These hydrogels were degradable in aqueous media due to the hydrolysis of hydrazone bonds formed between the aldehyde of PAG and the hydrazide of AAD [308] . Furthermore, with the increase of the AAD crosslinker, a slow degradation process of the hydrogel is achieved. An alternative approach to control the degradation of alginate hydrogels consists of adjusting the molecular weight distribution [309] . Another strategy to regulate the degradation rates of hydrogels is by the modulation of the dissociation rates of the polymer chains via a size mismatch in the crosslinking zones [310] . The degradation of the alginate gel can also be regulated using a combination of partial oxidation of polymer chains and a bimodal molecular weight distribution of polymer [311] . The oxidation rate can modify many parameters of alginate hydrogels other than biodegradability, especially the photocrosslinked hydrogels formed by alginate oxidation and methacrylation (OMA) [112] . These OMAs can be used for tissue engineering and other biomedical applications because they are biodegrade and do not show any cytotoxic effects in human cells, such as human bone marrow-derived mesenchymal stem cells (hBMMSCs). Therefore, in the biomedical field, these enhancement strategies are critical. Thus, alginate oxidation increased the cell viability of corneal epithelial cells, which was even more improved with the additional introduction of type IV collagen [307] . When partially oxidized alginate is applied, it promotes the generation of structures that resemble cartilage, unlike gels that are not partially oxidized [118] . Another example is the more rapidly degrading oxidized binary hydrogels facilitating the formation of new bone tissues from transplanted bone marrow stromal cells, as compared with the non-oxidized hydrogels [309] . Encapsulation of fibroblasts has been shown to cause accelerated degradation of the alginate hydrogel [312] . Reprinted with permission from [308] . Copyright 2013 American Chemical Society. These hydrogels were degradable in aqueous media due to the hydrolysis of hydrazone bonds formed between the aldehyde of PAG and the hydrazide of AAD [308] . Furthermore, with the increase of the AAD crosslinker, a slow degradation process of the hydrogel is achieved. An alternative approach to control the degradation of alginate hydrogels consists of adjusting the molecular weight distribution [309] . Another strategy to regulate the degradation rates of hydrogels is by the modulation of the dissociation rates of the polymer chains via a size mismatch in the crosslinking zones [310] . The degradation of the alginate gel can also be regulated using a combination of partial oxidation of polymer chains and a bimodal molecular weight distribution of polymer [311] . The oxidation rate can modify many parameters of alginate hydrogels other than biodegradability, especially the photocrosslinked hydrogels formed by alginate oxidation and methacrylation (OMA) [112] . These OMAs can be used for tissue engineering and other biomedical applications because they are biodegrade and do not show any cytotoxic effects in human cells, such as human bone marrow-derived mesenchymal stem cells (hBMMSCs). Therefore, in the biomedical field, these enhancement strategies are critical. Thus, alginate oxidation increased the cell viability of corneal epithelial cells, which was even more improved with the additional introduction of type IV collagen [307] . When partially oxidized alginate is applied, it promotes the generation of structures that resemble cartilage, unlike gels that are not partially oxidized [118] . Another example is the more rapidly degrading oxidized binary hydrogels facilitating the formation of new bone tissues from transplanted bone marrow stromal cells, as compared with the non-oxidized hydrogels [309] . Encapsulation of fibroblasts has been shown to cause accelerated degradation of the alginate hydrogel [312] . Alginate-based materials possess low or no toxicity and are capable of inactivating a wide variety of viruses affecting different organisms: in humans by the human immunodeficiency virus type 1, the hepatitis A, B, and C viruses, Sindbis virus, herpes simplex virus type 1 and 2, poliovirus type 1, rabies virus, rubella virus, and influenza virus; in mice by murine norovirus; in bacteria by the T4 coliphage, and in plants by the tobacco mosaic virus and the potato virus X [313] . Furthermore, biocompatible calcium alginate films, prepared by solvent casting and subsequent crosslinking with calcium cations, have recently shown antiviral activity against enveloped viruses, such as SARS-CoV-2 Delta variant [314] . The antiviral activity of these calcium alginate films is attributed to its compacted negative charges that may bind to viral envelopes inactivating membrane receptors. However, calcium alginate does not have antibacterial activity [71, 133] . The antibacterial capacity of alginate-based materials is very desirable for certain biomedical applications, for example, to heal wounds, such as dressings, and for their introduction into the organism in the form of scaffolds for tissue engineering [315] . Combining alginate with materials with intrinsic antimicrobial properties such as zinc, silver, copper, or carbon nanomaterials, among others, constitutes an advanced strategy to achieve this goal. The combination of zinc-based materials, such as ZnO nanoparticles with alginate, exhibited high antimicrobial capacities, of up to 99% efficiency in Gram-positive pathogens, such as Staphylococcus aureus, or 100% in Gram-negative bacteria, such as Escherichia coli [316] . This antibacterial capacity provides a tremendous advantage for food and clinical use [317] . Nano zinc oxide was impregnated effectively over cellulose fibers through sodium alginate matrix to produce next generation fibers with antibacterial activity [318] . Other preparations consisted of flexible and porous bandages made of alginate hydrogels with ZnO for healing wounds [319] . These bandages showed a directed biodegradable profile, antibacterial capacity, and rapid healing. Novel zinc alginate hydrogels prepared by internal setting method showed intrinsic antibacterial activity [320] . In addition, Zn can be used for alginate encapsulation to avoid infections [321] . However, it should be noted that the use of high concentrations of Zn 2+ [104] or ZnO [319] produces remarkable cytotoxicity. Silver ions and silver nanoparticles are often used as an antimicrobial agents [322, 323] . In fact, AgNPs are currently used in a broad range of industrial applications such as wound healing in biomedicine, food and textile industries, paints, household products, catheters, implants, cosmetics, and in combination with many types of materials to prevent infections [273] . Silver containing alginate shows antimicrobial activity, improves antioxidant capacity active, and reduces pro-inflammatory cytokine concentration [324, 325] . In addition, the amount of free radicals and the use of this silver alginate in wound healing increase its effectiveness in infected wounds [326] . This hybrid material considerably reduced the growth of S. aureus [324] . Silver can be released from alginate into ions to kill bacteria [326] . A porous complex made of chitosan, alginate, and AgNP showed antimicrobial and anticancer properties [327] . However, extensive use of this metallic antimicrobial agent has produced bacterial resistance [328, 329] . A compound formed by SA hydrogels and PVA and silver showed antibacterial activity [330] . Beads generated from a dual crosslinked PVA/SA/silver nanocomposite present a new structure that is cheap and exploits antimicrobial capability for food preservation [331] . AgNPs in sodium alginate and PVA increased mechanical capacity, and IC 50 dose showed an increase in antibacterial and antifungal effects [332] . Copper nanoparticles (CuNPs) incorporated into alginate provides antibacterial activity to neat alginate [333] . Therefore, recent studies have shown that the union of CuO with alginate increases structural properties and antibacterial activity, especially against S. aureus and E. coli [334] . The incorporation of copper-based materials, such as dendritic copper microparticles in the alginate biopolymer matrix, is low cost compared to other metals and ease of use [335] . Nanocomposites based on polypropylene nonwoven fabric, alginate and copper oxides nanoparticles showed maximum reduction of tested microorganisms [336] . Other proposed antimicrobial platforms consisted of sev-eral combination of materials, such as bacterial cellulose/alginate/chitosan composites incorporating copper (II) sulfate [337] , wool fabric treated with alginate/Cu 2+ [31], polylactide/alginate/copper [338] , alginate/copper systems on cotton and bamboo fabrics [339] , or copper-doped bioglass/alginate [340] . In the field of additive manufacturing, porous materials made of copper-tungsten-silver alloys showed antiviral activity against a viral model of SARS-CoV-2 [341] and 3D-printed alginate/bacterial cellulose composite hydrogels with incorporated copper nanostructures showed antimicrobial capacity [342] . However, it is essential to be aware that several metals, such as Cu, have certain cytotoxicity, producing oxidative stress, so the concentration introduced into alginate hydrogels must be controlled [343] . Carbon-based nanomaterials are next generation materials that have recently been proposed to treat COVID-19 because they have shown antibacterial and antiviral activity against 13 enveloped positive-sense single-stranded RNA viruses, including SARS-CoV-2 [344] . They are broad-spectrum antimicrobial materials, capable of inducing tissue regeneration and characterized by a low risk of microbial resistance. Thus, the incorporation of a low amount (0.1% w/w) of a CBN, such as CNFs, into calcium alginate films showed antibacterial activity against the life-threatening methicillin-resistant Staphylococcus epidermidis, or MRSE (see antimicrobial inhibition zone in Figure 7b ), and no cytotoxicity was observed in human keratinocyte HaCaT cells [133] . metals and ease of use [335] . Nanocomposites based on polypropylene non-woven alginate and copper oxides nanoparticles showed maximum reduction of tested m ganisms [336] . Other proposed antimicrobial platforms consisted of several comb of materials, such as bacterial cellulose/alginate/chitosan composites incorporating (II) sulfate [337] , wool fabric treated with alginate/Cu 2+ [31], polylactide/alginate [338] , alginate/copper systems on cotton and bamboo fabrics [339] , or copper-dop glass/alginate [340] . In the field of additive manufacturing, porous materials made per-tungsten-silver alloys showed antiviral activity against a viral model of SAR 2 [341] and 3D-printed alginate/bacterial cellulose composite hydrogels with incor copper nanostructures showed antimicrobial capacity [342] . However, it is essent aware that several metals, such as Cu, have certain cytotoxicity, producing ox stress, so the concentration introduced into alginate hydrogels must be controlled Carbon-based nanomaterials are next generation materials that have recent proposed to treat COVID-19 because they have shown antibacterial and antiviral against 13 enveloped positive-sense single-stranded RNA viruses, including SAR 2 [344] . They are broad-spectrum antimicrobial materials, capable of inducing ti generation and characterized by a low risk of microbial resistance. Thus, the incorp of a low amount (0.1% w/w) of a CBN, such as CNFs, into calcium alginate films antibacterial activity against the life-threatening methicillin-resistant Staphylococcu midis, or MRSE (see antimicrobial inhibition zone in Figure 7b ), and no cytotoxic observed in human keratinocyte HaCaT cells [133] . Other CNBs, such as GO (0.5% or 1% w/w) combined with alginate, exhibited high antibacterial properties against multidrug-resistant bacteria, such as MRSE, and other relevant pathogens, such as S. aureus, ensuring no cytotoxicity in human HaCaT cells [71] . CNFs incorporated into calcium alginate films enhanced its antiviral properties against bacteriophage T4 [345] . Furthermore, GO and CNFs combined with LED irradiation increased the antibacterial activity of these two nanomaterials [346] . Contrary to the above, incorporating GO at 1% concentration into zinc alginate films did not increase the bacteriakilling properties [104] . The antimicrobial activity of CNMs are attributed to different antimicrobial mechanisms, such as membrane stress, oxidative stress, entrapment, electron transfer, and photothermal hypotheses [347] . Other alternative materials that can provide antimicrobial properties to alginate gels include nanoclays, quaternary ammonium compounds, lactoperoxidase systems, κ-carrageenan, chitosan, and cobalt (II), among others. Thus, alginate combined with two types of nanoclays leaves and halloysite nanotubes may promote the antimicrobial activity of the final complex [348, 349] . Another antimicrobial method consists of complex binding of the alginate-quaternary ammonium complex by reaction of SA bound to (trimethoxysilyl)propyl-octadecyl dimethyl ammonium (TSA) with subsequent crosslinking with CaCl 2 [350] . The lactoperoxidase system and cross-linked alginate hydrogels generate a characteristic antimicrobial activity [351] . Antimicrobial films have been developed based on alginate crosslinked with calcium and κ-carrageenan [352] . Antimicrobial chitosan-SA polyion complexes [353] and nanoparticles [354] have been developed. Alginate/chitosan particles with diclofenac by dropwise addition to the CaCl 2 solution have been developed for biomedical applications [355] . Furthermore, a novel alginate derived cationic surfactant-cobalt(II) complex through the reaction of alginate with cationic surfactant showed good antimicrobial activity against Gram-positive and Gram-negative bacteria and fungi. Although, the antiviral properties of this complex have not been tested, in the field of additive manufacturing, porous materials made of cobalt-based superalloys showed potent antiviral activity against a viral model of SARS-CoV-2 [356] . Cell adhesion on alginate structures has been studied, and this characteristic is generally very low [68, 135, 357, 358] . In this regard, several strategies have been developed to overcome this drawback of alginate gels for biomedical applications requiring cell adhesion, such as regenerative medicine and tissue engineering. Thus, peptide-coupled alginates obtained by chemical functionalization of alginates have shown to increase cell adhesion [359, 360] . Sulfated alginates that resemble heparin have been developed for biomedical applications [361] [362] [363] . Heparin is a sulfated compound with a negative charge, formed via uronic acid dimers linked to glucosamine molecules through a bond that engages carbons 1,4 [364] . Heparin can mediate with different proteins and factors relevant to biological development [365] . Hydrogels presenting heparin are applied in an injectable form and can mediate different processes, such as those mentioned above, or deliver factors that aid cell growth in target tissues [365] . Cell adhesion and proliferation can also be increased with the incorporation of CNM into different biomaterials, such as PHBV [290, 366] . Examples of these carbon nanomaterials are GO and CNFs, which, added in low concentrations, significantly increase cell adhesion and the proliferation capacity of the biomaterials. Other materials used in biomedicine that exhibited improved cell adhesion with the incorporation of GO are polycaprolactone [367] and gelatin [368] . However, alginate-based films with CNFs [68] or GO [135] showed non-cytotoxic effects in human HaCaT cells used, but did not significantly enhance cell adhesion, unlike the other biomaterials. Alginate supports do not produce an increase in cell adhesion capacity when non-hydrophilic CNFs or hydrophilic GO are introduced. However, the incorporation of these CBNs into alginate is capable of enhancing many other physicochemical and antibacterial properties [4, 66, 67, 71, 133] . Alginate-catechol is an adhesive gel capable of remaining adherent to endothelial cells under flow above physiological shear stress [369] . Furthermore, the alginate-catechol matrix exhibits enhanced mechanical stress strengthening and chemical stability that does not change its morphology even if the pH values vary over a large pH spectrum [370] . Recent studies have shown that enhancing properties, such as cell adhesion, cell spreading, and neurite outgrowth, are achieved by binding alginate with up to three laminin-active proteins [371] . Mouse embryonic stem cell culture using alginate hydrogels as 3D scaffolds efficiently supports neural differentiation [372] . However, enhancement strategies combining alginate with other biomaterials has shown successful results in this research area. Thus, human adipose-derived stem cells encapsulated in alginate/gelatin microspheres showed much higher cell proliferation as well as adipogenic differentiation compared with encapsulation in pure alginate [373] . Mineralized alginate matrices have also shown osteogenic differentiation of human mesenchymal stem cells [374] . Alginate-gelatin with mouse planta dermis bio-ink facilitates the proliferation, migration, and sweat gland cell differentiation of mouse mesenchymal stem cells (MSCs) [375] . That study demonstrated that the chemical constituents of a bio-ink play a critical role in promoting the migration and development of MSCs. Furthermore, the physical properties of a bio-ink and spatial conformation can promote the differentiation of MSCs into sweat gland cells [375] . Alginate-gelatin microcapsules have also shown to enhance bone differentiation of mesenchymal stem cells [376] . The combination of alginate with another natural hydrogel, agarose, improved the in vitro differentiation of human dental pulp stem cells in chondrocytes [377] . Therefore, further research must be performed to continue developing new advanced alginate-based materials with enhanced cell adhesion, proliferation, and differentiation. SA has potential application in enhancing immunity in biomedicine [378, 379] . Although cell encapsulation in alginate gels is a very promising therapy for cell transplantation according to the research performed so far in this field, the few clinical trials based on cell encapsulation are still under evaluation [380] . Encapsulation of the transplanted cells can solve the problem of immune rejection, by providing a physical barrier between the transplanted cells and the recipient's immune cells [381, 382] . However, due to the difficulties encountered when trying to prevent the immune responses generated by the various microcapsule components, progress in the area has been slow [380] . In this regard, the immune responses produced by the alginate polymer can be minimized using ultrapure alginates [381] . A strategy consisting of incorporating fucoidan from Fucus vesiculosus in ultrapure alginate for microencapsulation of primary rat islets showed that both viability and glucose responsiveness of rat islets in these gel microcapsules were significantly higher compared to islets encapsulated in alginate alone [383] . Encapsulation and immunoengineering strategies combined with cell therapy have been applied as enhanced strategies to improve cell replacement therapies for management of type 1 diabetes (T1D) [381] . For example, a potential novel strategy to improve long-term survival of pancreatic islet grafts for T1D treatment consists of an immune regulatory 3D-printed alginate-pectin construct for immunoisolation of insulin producing β-cells [384] . The incorporation of immunomodulatory molecules in alginate capsules demonstrated to be for long-term engraftment and functioning of insulin-producing cells [385] . Thus, for example, the combination of alginate with crystalline GW2580, a colony-stimulating factor-1 receptor inhibitor, showed longterm release of the immunomodulator, which reduced fibrosis and facilitated glycemic control for xenogeneic islets transplantation in mice [386] . The fabrication of polymer supports, usually called scaffolds, with a high degree of interconnected porosity, is required for tissue engineering applications [387] [388] [389] [390] [391] [392] [393] [394] . Alginate scaffolds can be produced following several strategies, which include gas foaming and microfluidic gas foaming [395] , electrospinning [396] , the leaching technique [397] , freezedrying [398] , and 3D printing of biomaterials with cells (bioprinting) or without cells [399] , among other methods [400, 401] . Figure 8 presents a summary illustration of alginate extraction from brown algae or microbial culture, crosslinking, and primary techniques for alginate manipulation, encapsulation, and scaffold fabrication methods. nation of alginate with crystalline GW2580, a colony-stimulating factor-1 receptor inhibitor, showed long-term release of the immunomodulator, which reduced fibrosis and facilitated glycemic control for xenogeneic islets transplantation in mice [386] . The fabrication of polymer supports, usually called scaffolds, with a high degree of interconnected porosity, is required for tissue engineering applications [387] [388] [389] [390] [391] [392] [393] [394] . Alginate scaffolds can be produced following several strategies, which include gas foaming and microfluidic gas foaming [395] , electrospinning [396] , the leaching technique [397] , freeze-drying [398] , and 3D printing of biomaterials with cells (bioprinting) or without cells [399] , among other methods [400, 401] . Figure 8 presents a summary illustration of alginate extraction from brown algae or microbial culture, crosslinking, and primary techniques for alginate manipulation, encapsulation, and scaffold fabrication methods. The enhancement strategies developed so far to improve the physicochemical and biological properties of alginate are very important for the fabrication of next generation alginate scaffolds for tissue engineering applications. In this regard, for example, novel alginate scaffolds composed of porous alginate that incorporate tiny poly(lactic-co-glycolic acid) microspheres capable of controlling the release of angiogenic factors, such as a basic fibroblast growth factor, have been developed [402] . Alginate/hydroxyapatite (HAp) scaffolds have also been developed with 82% porosity to allow the growth of osteoblastic cell lines favoring a promising approach for bone tissue engineering applications [403] . The fabrication of alginate scaffolds by the electrospun technique is inexpensive and easy to process and build [404] . In this technique, it is possible to modify the sizes of the structures and the diameter of strands depending on the properties of the natural biopolymer alginate used [10] . Electrospinning of pure alginate is a well-known technique to produce alginate scaffolds with potential applications in tissue engineering [405] . However, enhancement strategies, such as the introduction of gelatin to reinforce alginate electrospun nanofibers, can be applied to achieve improved scaffolding and transplantation in corneal tissue engineering [406] . The structure formed by electrospun alginate/poly(ethylene) oxide (PEO) and Pluronic F127 as a surfactant generated a scaffold with marked porosity for tissue engineering [407] . The use of alginate has been proposed The enhancement strategies developed so far to improve the physicochemical and biological properties of alginate are very important for the fabrication of next generation alginate scaffolds for tissue engineering applications. In this regard, for example, novel alginate scaffolds composed of porous alginate that incorporate tiny poly(lactic-co-glycolic acid) microspheres capable of controlling the release of angiogenic factors, such as a basic fibroblast growth factor, have been developed [402] . Alginate/hydroxyapatite (HAp) scaffolds have also been developed with 82% porosity to allow the growth of osteoblastic cell lines favoring a promising approach for bone tissue engineering applications [403] . The fabrication of alginate scaffolds by the electrospun technique is inexpensive and easy to process and build [404] . In this technique, it is possible to modify the sizes of the structures and the diameter of strands depending on the properties of the natural biopolymer alginate used [10] . Electrospinning of pure alginate is a well-known technique to produce alginate scaffolds with potential applications in tissue engineering [405] . However, enhancement strategies, such as the introduction of gelatin to reinforce alginate electrospun nanofibers, can be applied to achieve improved scaffolding and transplantation in corneal tissue engineering [406] . The structure formed by electrospun alginate/poly(ethylene) oxide (PEO) and Pluronic F127 as a surfactant generated a scaffold with marked porosity for tissue engineering [407] . The use of alginate has been proposed in conjunction with PEO and peptides to improve cell adhesion, which is essential for tissue engineering applications [408] . However, the problems begin when the alginate concentration increases because the structure becomes viscous and cannot be injected, and the solution needs to then introduce surfactants or cosolvents to mediate in the phase transition [404] . If only alginate-based materials are desired, the water-soluble PEO of the nanofibers formed can be eliminated by incubation in water [409] . Three-dimensional electrospun alginate can be produced in combination with another biodegradable polymer, poly (ε-caprolactone) (PCL). These composite scaffolds can be produced with determined pore sizes to allow enhanced viability and tissue regeneration [410] . Electrospun nanofibrous scaffolds reinforced with magnesium oxide nanoparticles showed improved physicochemical properties, such as resistance to traction and elasticity [411] . Improving the resistance and durability of alginate hydrogels by the application of a method based on the layer-by-layer electrospinning of nanofibers showed very promising results at a structural level for tissue engineering [228] . An innovative 3D nanofiber hydrogel composed of alginate bonded with polyaniline in nanofiber form to promote a more stable and reinforced structure for lithium-ion battery applications have been reported via in situ polymerizations instead of electrospinning [412] . The particle leaching method, or porogen technique, and the freeze-drying method were combined with calcium alginate beads and keratin was used to create a flexible structure for fibroblast proliferation [413] . This process is fast and easy, and porosity and size can be controlled to generate various scaffolds with these biopolymers [414] . Alginate-chitosan/hydroxyapatite polyelectrolyte complex porous scaffolds with mechanical resistance and thermal stability were developed by combining the formation of the polyelectrolyte complex (PEC) with freeze-drying [415] . A porous matrix, a scaffold of calcium alginate/gelatin with enhanced properties, was generated by combining porogen leaching and lyophilization, generating a microenvironment for cell adhesion, generation, and tissue regeneration [13] . The mixture of freeze-drying and leaching can increase the pore size of the final alginate scaffold [416] . Alginate can also be used in the form of microsphere porogens to produce porous scaffolds with another biopolymers, such as collagen [417] . Moreover, 3D printing technologies or additive manufacturing techniques are broadly used to fabricate scaffolds, such as fused deposition modeling (FDM) [418] . Thus, 3D printing was used to fabricate porous alginate/gelatin hydrogel scaffolds for tissue engineering [419] . Moreover, 3D printing can handle materials and cells, such as human chondrocytes with nanocellulose-alginate, while moving in the three axes allowing structures with volume for bioengineering applications [77] . Furthermore, 3D printing has been investigated as a promising technique to build tissues by applying microscopic structure control and macroscopic layer by layer production [420] . The 3D tracing technique is also applied to form cell-loaded porous alginate, and this technique is used to form scaffolds for bone problems or cartilaginous tissues [421] . PCL and alginate were combined to form a three-dimensional structure capable of withstanding cell activity and providing a mechanically stable material [422] . Alginate-based heart valves as scaffolding fabricated by the 3D bioprinting technique showed increased viability, correct dispersion, and cell retention [423] . Bioprinting or 3D bioprinting is a technique that allows the direct manufacturing of an artificial living tissue by combining biomaterials, cells, and growth factors using optical and different computational methods and NMR technology data of the tissue or organ to be copied [17] . The structural matrices are multicellular (bio-links) in a sequential layer-by-layer methodology based on these advanced technologies. Moreover, 3D printing can be used to obtain an automatic and reproducible production of living and functional 3D tissues that are more practical tools when carrying out drug experiments, toxicological studies, and even transplants [16]. However, not any material can be used for this purpose since it must meet specific biocompatibility requirements and basic structural and/or mechanical properties for which the most recommended are hydrogels such as alginate [424] . Thus, alginate-based hydrogels are the main biomaterials applied in generating 3D structures because they are polymer of natural origin, biodegradable, non-cytotoxic, and do not generate a response from the immune system, they are also economical compared to other biopolymers. Furthermore, this polymer is obtained from renewable sources, such as brown algae or microorganism culture [4] . Nevertheless, alginate also has its drawbacks. Thus, alginate degradation is slow and difficult to control [425] . This is a serious problem because, for a suitable tissue regeneration, the material must be degraded and allow the cells to generate extracellular components themselves that promote the surface matrix. In addition, the properties required for the manufacturing of different tissues are different, so it is usually necessary to combine alginate with other biomaterials to achieve optimal mechanical and structural properties in each case [424] . Thus, alginate combined with other biomaterials has a fundamental role in tissue regeneration, highlighting cartilage, bone [426] , and vascular tissue [427] . Among the main peculiarities, it is still a challenge for the scientific community to reduce the "bench-to-bedside" gap for the proper functionality of bioprinted tissue. To this end, several research groups have been working in alginate constructions, such as alginate scaffolds with sustained release of the BMP-2 protein for osteogenicity by bioprinting [428] , mesoporous bioglass/alginate scaffolds with porosity up to 70% [429] , alginate scaffolds with calcium phosphate for osteochondral regeneration [430] , and alginate scaffolds with CBNs such as GO [431] . Freeze-drying is an easy method to produce three-dimensional porous materials for regenerative purposes [432] . In-process freeze monitoring is essential for pore formation during scaffold production [433] . Many scaffolds are produced by this technique, such as alginate scaffolds with immobilized Arg-Gly-Asp (RGD) peptide [434, 435] , curcuminloaded chitosan nanoparticles impregnated into collagen-alginate scaffolds [436] , and alginate/poly (lactic-co-glycolic acid)/calcium phosphate cement scaffolds [437] . Sophisticated methods, such as the four-step process that consists of applying a preparation followed by crosslinking, and a step similar to freeze drying, freezing, and lyophilization, has been used to prepared chitosan-alginate as scaffolding material for cartilage tissue engineering [438] . Chitosan/alginate-based scaffolds have also been produced by thermally-induced phase separation and subsequent sublimation of the solvent [439] , by in-situ co-precipitation containing different amounts (0, 10, and 30 wt.%) of HAp [440] . A coaxial structured collagen-alginate scaffolds was designed with an outer collagen and an inner alginate part [441] . These biocompatible scaffolds showed good structural stability and increased mechanical performance compared to pure collagen scaffold under a similar pore structure. Furthermore, they showed good cytotoxicity. Porous bony scaffolds coated with alginate-hydroxyapatite have been recently developed by a combination of several techniques that include coating, 3D printing and freeze-drying for femoral applications [442] . Alginate sulfate-based hydrogel/nanofiber composite scaffolds with controlled Kartogenin delivery have been proposed for tissue engineering [443] . Very recently, chitosan/alginate/hydroxyapatite hybrid scaffolds have been developed using 3D printing and impregnating techniques for potential cartilage regeneration [444] . Table 5 summarizes the most relevant alginate-based scaffolds showing the fabrication method, materials combined with alginate, pore size/shape, porosity, regenerative field, year of publication, and reference. In this review, alginate biopolymer's most relevant enhancement strategies, including the principles, chemical structure, gelation properties, chemical interactions, production, sterilization, purification, types, and alginate-based hydrogels developed so far, and scaffolds for regenerative medicine, have been exposed. Emphasis was placed on the materials and compounds combined with alginate to develop novel composite and nanocomposite materials with improved physicochemical and biological properties that solve the drawbacks of this well-known natural biomaterial. Alginate has been proposed as a natural antiviral material capable of inactivating enveloped viruses, such as SARS-CoV-2 for the current coronavirus pandemic. Therefore, the excellent properties and the increasing amount of enhancement strategies of this biopolymer render alginate-based materials a family with great potential in a broad range of fields, from the food industry to the most sophisticated biomedical technologies. Alginate hydrogels as biomaterials Entrapment in Calcium Alginate Green Composites Films with Antibacterial Properties Llorens-Gámez, M. Enhancement of water diffusion and compression performance of crosslinked alginate with a minuscule amount of graphene oxide Alginate application for heart and cardiovascular diseases An alginate hydrogel matrix for the localised delivery of a fibroblast/keratinocyte co-culture Evaluation of an in situ forming hydrogel wound dressing based on oxidized alginate and gelatin Integrative medicine and the role of modified citrus pectin/alginates in heavy metal chelation and detoxification-Five case reports Reactivity and Heavy Metal Removal Capacity of Calcium Alginate Beads Loaded with Ca-Al Layered Double Hydroxides Alginate-Based Biomaterials for A highly organized three-dimensional alginate scaffold for cartilage tissue engineering prepared by microfluidic technology Alginate in corneal tissue engineering Porous matrix of calcium alginate/gelatin with enhanced properties as scaffold for cell culture Mechanism of beer foam stabilization by propylene glycol alginate Alginate-based edible films and coatings for food packaging applications Alginate as a versatile polymer matrix with biomedical and food applications Binders in fish feeds Binders and Pellet Stability in Development of Crustacean Diets1 Casts of fluid preserved specimens Facilitating Consumer Involvement in Design for Additive Manufacturing/3D Printing Products Customised design and manufacture of protective face masks combining a practitioner-friendly modelling approach and low-cost devices for digitising and additive manufacturing: This paper analyses the viability of replacing conventional practice with AM me Immunological and technical considerations in application of alginate-based microencapsulation systems Matryoshka enzyme encapsulation: Development of zymoactive hydrogel particles with efficient lactose hydrolysis capability. Food Hydrocoll Perspectives of biodegradable natural polysaccharides for site-specific drug delivery to the colon Enhancement of cell viability by fabrication of macroscopic 3D hydrogel scaffolds using an innovative cell-dispensing technique supplemented by preosteoblast-laden micro-beads Skeletal myogenic differentiation of urine-derived stem cells and angiogenesis using microbeads loaded with growth factors Alginate: Properties and biomedical applications Mass transfers in a fluidized bed bioreactor using alginate beads for a future bioartificial liver Alginate microparticles as oral colon drug delivery device: A review In vitro and in vivo evaluation of novel interpenetrated polymer network microparticles containing repaglinide Synthesis, characterization and bending behavior of electroresponsive sodium alginate/poly(acrylic acid) interpenetrating network films under an electric field stimulus High strength and low friction of a PAA-alginate-silica hydrogel as potential material for artificial soft tissues Synthesis and swelling properties of pH-sensitive semi-IPN superabsorbent hydrogels based on sodium alginate-g-poly(sodium acrylate) and polyvinylpyrrolidone Evaluation of alginate-chitosan semi IPNs as cartilage scaffolds Low-Cost Advanced Hydrogels of Calcium Alginate/Carbon Nanofibers with Enhanced Water Diffusion and Compression Properties Green synthetic routes to alginate-graphene oxide composite hydrogels with enhanced physical properties for bioengineering applications Serrano-Aroca, Á. Physical and biological properties of alginate/carbon nanofibers hydrogel films Synthesis of irregular graphene oxide tubes using green chemistry and their potential use as reinforcement materials for biomedical applications Preparation and characterization of alginate/gelatin blend fibers Calcium alginate/graphene oxide films: Reinforced composites able to prevent Staphylococcus aureus and methicillin-resistant Staphylococcus epidermidis infections with no cytotoxicity for human keratinocyte HaCaT cells Effects of alginate on stability and ecotoxicity of nano-TiO 2 in artificial seawater Secrecy throughput optimization for the wpcns with non-linear eh model Combinatorial Screening of Nanoclay-Reinforced Hydrogels: A Glimpse of the "holy Grail" in Orthopedic Stem Cell Therapy? Alginate Sulfate-Nanocellulose Bioinks for Cartilage Bioprinting Applications Cartilage Tissue Engineering by the 3D Bioprinting of iPS Cells in a Nanocellulose/Alginate Bioink 3D bioprinting human chondrocytes with nanocellulose-alginate bioink for cartilage tissue engineering applications Alginate-based composites for environmental applications: A critical review Alginate: From food industry to biomedical applications and management of metabolic disorders Alginate-based adsorbents for removal of metal ions and radionuclides from aqueous solutions: A review Alginate and alginate composites for biomedical applications Alginate-based composite materials for wound dressing application:A mini review Fabrication of alginate microspheres for drug delivery: A review Alginate hydrogels for bone tissue engineering, from injectables to bioprinting: A review Review of alginate-based hydrogel bioprinting for application in tissue engineering Oxidized Alginate-Based Hydrogels for Tissue Engineering Applications: A Review Development of edible films and coatings from alginates and carrageenans Similarities and differences between alginic acid gels and ionically crosslinked alginate gels. Food Hydrocoll A New Process for Extracting Alginates from Laminaria digitata: Reactive Extrusion Exopolysaccharide production in biofilms: Substratum activation of alginate gene expression by Pseudomonas aeruginosa Production and characterization of guluronate lyase from Klebsiella pneumoniae for applications in seaweed biotechnology Evidence for egg-box-compatible interactions in calcium-alginate gels from fiber X-ray diffraction Alginate gel particles-A review of production techniques and physical properties pH/temperature-responsive semi-IPN hydrogels composed of alginate and poly(Nisopropylacrylamide) Food Stabilisers, Thickeners and Gelling Agents Alginate Microcapsules for Drug Delivery Formulation and stability evaluation of 3D alginate beads potentially useful for cumulus-oocyte complexes culture Characterization of the alginates from five madagascan brown algae Alginate based new materials Molecular basis of Ca 2+ -induced gelation in alginates and pectins: The egg-box model revisited Egg-box structure in cobalt alginate: A new approach to multifunctional hierarchical mesoporous N-doped carbon nanofibers for efficient catalysis and energy storage Biological interactions between polysaccharides and divalent cations: The egg-box model Graphene oxide in zinc alginate films: Antibacterial activity, cytotoxicity, zinc release, water sorption/diffusion, wettability and opacity Reexamining the egg-box model in calcium-Alginate gels with X-ray diffraction On the initial binding of alginate by calcium ions the tilted egg-box hypothesis Molecular basis for some physical properties of alginates in the gel state Alginate derivatization: A review of chemistry, properties and applications Fabrication and characterization of macroporous epichlorohydrin cross-linked alginate beads as protein adsorbent Towards a fully-synthetic substitute of alginate: Development of a new process using thermal gelation and chemical cross-linking Novel crosslinking methods to design hydrogels The effect of oxidation on the degradation of photocrosslinkable alginate hydrogels Extraction and characterization of sodium alginate from Moroccan Laminaria digitata brown seaweed Rheological evaluation of inter-grade and inter-batch variability of sodium alginate Alginate as Immobilization Material: I. Correlation between Chemical and Physical Properties of Alginate Gel Beads Photocrosslinked alginate hydrogels with tunable biodegradation rates and mechanical properties Polysaccharide as renewable responsive biopolymer for in situ gel in the delivery of drug through ocular route Degradation of partially oxidized alginate and its potential application for tissue engineering Alginic acid gels: The effect of alginate chemical composition and molecular weight Studies on the Solubility of Alginic Acid from Ascophyllum Nodosum at Low pH Fractionation of Alginates by Precipitation with Calcium and Magnesium Ions The effect of erosion and swelling on the dissolution of theophylline from low and high viscosity sodium alginate matrices Selectivity of Some Anionic Polymers for Divalent Metal Ions Biological interactions between polysaccharides Use of anionic polysaccharides in the development of 3D bioprinting technology Inhomogeneous polysaccharide ionic gels Degradation of Alginate in the Presence of Reducing Compounds Gel strength of Ca-limited alginate gels made in situ Preparation of biodegradable nanoporous microspherical aerogel based on alginate Alginates from Algae Kinetics and mechanisms of depolymerization of alginate and chitosan in aqueous solution Effects of Sterilization Treatments on Some Properties of Alginate Solutions and Gels Serrano-Aroca, Á. Carbon nanofibers in pure form and in calcium alginate composites films: New cost-effective antibacterial biomaterials against the life-threatening multidrug-resistant Staphylococcus epidermidis Antimicrobial Characterization of Advanced Materials for Bioengineering Applications Study of 1D and 2D carbon nanomaterial in alginate films Biosynthesis and applications of alginates Seaweeds uses as Human Foods. In A Guide to the Seaweed Industry FAO-Food and Agriculture Organization of United States Global status of seaweed production, trade and utilization Seaweed in the UK and abroad-status, products, limitations, gaps and Cefas role Treatment of Resistant Hypertension: An Update in Device Therapy A decade of change in the seaweed hydrocolloids industry Alginate Production from Marine Macroalgae, with Emphasis on Kelp Farming Others Aquatic Biopolymers International Conference on Recent Trends in Physics Biosynthesis of alginate. Part I. Composition and structure of alginate produced by Azotobacter vinelandii (Lipman) Culture expérimentale de l' algue Undaria pinnatifida sur les côtes de France Alginate Particles as Platform for Drug Delivery by the Oral Route: State-of-the-Art. ISRN Pharm Ionotropic Gelation and Polyelectrolyte Complexation Technique: Novel Approach to Drug Encapsulation Decrease in dynamic viscosity and average molecular weight of alginate from Laminaria digitata during alkaline extraction Extraction and physicochemical characterization of Sargassum vulgare alginate from Brazil Changes in the functional properties and molecular weight of sodium alginate following γ irradiation Protective effect of sodium alginates against bacterial infection in common carp, Cyprinus carpio L Rheology of Alginate from Azotobacter vinelandii in Aqueous Dispersions Alginate Properties and Heavy Metal Biosorption by Marine Algae Characterization of polysaccharides extracted from brown seaweeds Extraction and characterisation of alginate from brown seaweeds (Fucales, Phaeophyceae) collected from Port Dickson, Peninsular Malaysia Extracted and depolymerized alginates from brown algae Sargassum vulgare of Lebanese origin: Chemical, rheological, and antioxidant properties The renal effects of alginates isolated from brown seaweed Sargassum vulgare Enzymatic modification of alginates with the mannuronan C-5epimerase AlgE4 enhances their solubility at low pH the Penetration of Antibiotics through Sodium Alginate and Through the Exopolysaccharide of a Mucoid Strain of Pseudomonas Aeruginosa Cloning of genes controlling alginate biosynthesis from a mucoid cystic fibrosis isolate of Pseudomonas aeruginosa Bacterial alginates: Biosynthesis and applications Alginate production by Azotobacter vinelandii Bacterial biosynthesis of alginates Enzyme Organization in DNA Precursor Biosynthesis Bacterial alginate biosynthesis-Recent progress and future prospects Cloning of Escherichia coli and Pseudomonas aeruginosa phosphomannose isomerase genes and their expression in alginate-negative mutants of Pseudomonas aeruginosa Pseudomonas aeruginosa AlgB, which modulates the expression of alginate, is a member of the NtrC subclass of prokaryotic regulators Pseudomonas aeruginosa AlgB, a two-component response regulator of the NtrC family, is required for algD transcription The Pseudomonas aeruginosa algC gene encodes phosphoglucomutase, required for the synthesis of a complete lipopolysaccharide core High osmolarity is a signal for enhanced algD transcription in mucoid and nonmucoid Pseudomonas aeruginosa strains Gene algD coding for GDPmannose dehydrogenase is transcriptionally activated in mucoid Pseudomonas aeruginosa Identification of algI and algI in the Pseudomonas aeruginosa alginate biosynthetic gene cluster which are required for alginate O acetylation Pseudomonas aeruginosa AlgG is a polymer level alginate C5-mannuronan epimerase Characterization of the Pseudomonas aeruginosa alginate lyase gene (algL): Cloning, sequencing, and expression in Escherichia coli Alginate synthesis in Pseudomonas aeruginosa: Environmental regulation of the algC promoter Signal transduction in exopolysaccharide alginate synthesis: Phosphorylation of the response regulator AlgR1 in Pseudomonas aeruginosa and Escherichia coli Conversion to mucoidy in Pseudomonas aeruginosa infecting cystic fibrosis patients Identification of Pseudomonas aeruginosa glpM, whose gene product is required for efficient alginate biosynthesis from various carbon sources Genetics of Bacterial Alginate: Alginate Genes Distribution, Organization and Biosynthesis in Bacteria Characteristics of alginate from Laminaria digitata cultivated in a high-phosphate environment Microbial alginate production, modification and its applications Alginate polymerization and modification are linked in pseudomonas aeruginosa Alginate from Pseudomonas fluorescens and P. putida: Production and properties Isolation of alginate-producing mutants of Pseudomonas fluorescens, Pseudomonas putida and Pseudomonas mendocina Applications of alginate microspheres in therapeutics delivery and cell culture: Past, present and future The Use of Biopolymers in Food Packaging Enzymes involved in the biosynthesis of alginate by Pseudomonas aeruginosa Evaluation of alginate purification methods: Effect on polyphenol, endotoxin, and protein contamination Direct effect of alginate purification on the survival of islets immobilized in alginate-based microcapsules Studies on small (<300 µm) microcapsules: II-Parameters governing the production of alginate beads by high voltage electrostatic pulses Improved biocompatibility but limited graft survival after purification of alginate for microencapsulation of pancreatic islets Production of purified alginates suitable for use in immunoisolated transplantation Biocompatibility of mannuronic acid-rich alginates Biocompatibility of alginate-poly-l-lysine microcapsules for cell therapy Role of protein contaminants in the immunogenicity of alginates Original papers Production of mitogen-contamination free alginates with variable ratios of mannuronic acid to guluronic acid by free flow electrophoresis Effect of poly-L-lysine coating on macrophage activation by alginatebased microcapsules: Assessment using a new in vitro method Calcium alginate gel: A biocompatible and mechanically stable polymer for endovascular embolization Biomedical and Pharmaceutical Applications of Alginate and Chitosan Study of the mechanical properties and self-healing ability of asphalt mixture containing calcium-alginate capsules Graft copolymerization of itaconic acid onto sodium alginate using benzoyl peroxide Synthesis and characterization of pH-and temperature-sensitive materials based on alginate and poly(N-isopropylacrylamide/acrylic acid) for drug delivery Electroactive calcium-alginate/polycaprolactone/reduced graphene oxide nanohybrid hydrogels for skeletal muscle tissue engineering Thermoresponsive hydrogels from alginate-based graft copolymers Recent developments of carboxymethyl cellulose Insulin encapsulation in reinforced alginate microspheres prepared by internal gelation In vitro evaluation of mucoadhesive properties of chitosan and some other natural polymers A crosslinked calcium-alginate-pectinate-cellulose acetophthalate gelisphere system for linear drug release Soon-Shiong, P. Interpenetrating polymer networks of alginate and polyethylene glycol for encapsulation of islets of Langerhans Interpenetrating polymer networks polysaccharide hydrogels for drug delivery and tissue engineering Semi-interpenetrating polymer networks (IPNs) for entrapment of glucose isomerase 3D Printing of Personalized Thick and Perfusable Cardiac Patches and Hearts Nanofiber-reinforced bulk hydrogel: Preparation and structural, mechanical, and biological properties Cellulose nanofibers reinforced sodium alginate-polyvinyl alcohol hydrogels: Core-shell structure formation and property characterization Synergistic effect of cellulose nanofibres and bio-extracts for fabricating high strength sodium alginate based composite bio-sponges with antibacterial properties Fiber-reinforced composite hydrogels for bioadhesive and sealant applications Properties of alginate-based films reinforced with cellulose fibers and cellulose nanowhiskers isolated from mulberry pulp Biocomposite cellulose-alginate films: Promising packaging materials Biodegradable nanocomposite films based on sodium alginate and cellulose nanofibrils Nanocrystalline cellulose (NCC) reinforced alginate based biodegradable nanocomposite film Phase equilibria and charge fractionation in polydisperse polyelectrolyte solutions Magnetic nanocellulose alginate hydrogel beads as potential drug delivery system Improving mechanical properties of alginate hydrogel by reinforcement with ethanol treated polycaprolactone nanofibers Composite electrospun gelatin fiber-alginate gel scaffolds for mechanically robust tissue engineered cornea Three-dimensional printing fiber reinforced hydrogel composites Preparation of V2O5-ZnO coated carbon nanofibers: Application for removal of selected antibiotics in environmental matrices Bio-Nanocomposite hydrogel based on zinc alginate/graphene oxide: Morphology, structural conformation, thermal behavior/degradation, and dielectric properties Distribution and alignment of carbon nanotubes and nanofibrils Carbon nanotubes reinforced chitosan films: Mechanical properties and cell response of a novel biomaterial for cardiovascular tissue engineering Fabrication, characterization, and biocompatibility of single-walled carbon nanotubereinforced alginate composite scaffolds manufactured using freeform fabrication technique Alginate microsphere filled with carbon nanotube as drug carrier Development of functionalized multi-walled carbon-nanotube-based alginate hydrogels for enabling biomimetic technologies Graphene Oxide versus Carbon Nanofibers in Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) Films: Degradation in Simulated Intestinal Environments Effect of multiwall carbon nanotube reinforcement on coaxially extruded cellular vascular conduits Sodium alginate/graphene oxide composite films with enhanced thermal and mechanical properties Alginate/graphene oxide fibers with enhanced mechanical strength prepared by wet spinning Biodegradable biopolymer-graphene nanocomposites Reinforcing nanomedicine using graphene family nanomaterials Alginate-nanoparticles composites: Kinds, reactions and applications In situ reduction of silver nanoparticles by sodium alginate to obtain silver-loaded composite wound dressing with enhanced mechanical and antimicrobial property Alginate Biofunctional Films Modified with Melanin from Watermelon Seeds and Zinc Oxide/Silver Nanoparticles Alginate-Based Electrospun Membranes Containing ZnO Nanoparticles as Potential Wound Healing Patches: Biological, Mechanical, and Physicochemical Characterization Preparation and characterization of polyaniline/sodium alginate-doped TiO2 nanoparticles with promising mechanical and electrical properties and antimicrobial activity for food packaging applications ZnO and ZnO/CaO nanoparticles in alginate films. Synthesis, mechanical characterization, barrier properties and release kinetics Enhanced antibacterial activity, mechanical and physical properties of alginate/hydroxyapatite bionanocomposite film Dopamine-modified alginate beads reinforced by cross-linking via titanium coordination or self-polymerization and its application in enzyme immobilization Effect of nanoclay and cross-linking degree on the properties of alginate-based nanocomposite film Preparation and characterization of bio-nanocomposite films based on soy protein isolate and montmorillonite using melt extrusion Effect of the biopolymer charge and the nanoclay morphology on nanocomposite materials Effect of montmorillonite clay and biopolymer concentration on the physical and mechanical properties of alginate nanocomposite films An approach for mechanical property optimization of cell-laden alginate-gelatin composite bioink with bioactive glass nanoparticles A roadmap for graphene Personal thermal management by thermally conductive composites: A review Effects of graphene oxides on the cure behaviors of a tetrafunctional epoxy resin Morphology and thermal properties of calcium alginate/reduced graphene oxide composites Preparation, structural characterization, thermal properties and antifungal activity of alginate-CuO bionanocomposite Preparations and characterization of alginate/silver composite films: Effect of types of silver particles Comparing physico-mechanical and thermal properties of alginate nanocomposite films reinforced with organic and/or inorganic nanofillers. Food Hydrocoll Effect of moisture on electrospun nanofiber composites of poly(vinyl alcohol) and cellulose nanocrystals Improvement of physical properties of crosslinked alginate and carboxymethyl konjac glucomannan blend films Effect of sodium alginate modification of graphene (by anion-π type of interaction) on the mechanical and thermal properties of polyvinyl alcohol (PVA) nanocomposites Effect of surfactant and sodium alginate modification of Graphene on the mechanical and thermal properties of polyvinyl alcohol (PVA) nanocomposites Physicochemical characterization of halloysite/alginate bionanocomposite hydrogel Properties of glycerol-plasticized alginate films obtained by thermo-mechanical mixing. Food Hydrocoll The flame retardancy, thermal properties, and degradation mechanism of zinc alginate films Sodium alginate-assisted exfoliation of MoS2 and its reinforcement in polymer nanocomposites Effect of SiO2, PVA and glycerol concentrations on chemical and mechanical properties of alginate-based films Carbon Nanofibers versus Silver Nanoparticles: Time-Dependent Cytotoxicity, Proliferation, and Gene Expression Vivo and In Vitro Toxicity A review and analysis of electrical percolation in carbon nanotube polymer composites Anisotropic architecture and electrical stimulation enhance neuron cell behaviour on a tough graphene embedded PVA: Alginate fibrous scaffold Tough and conductive hybrid graphene-PVA: Alginate fibrous scaffolds for engineering neural construct Hybrid hydrogels containing vertically aligned carbon nanotubes with anisotropic electrical conductivity for muscle myofiber fabrication Mechanical and Electrical Properties: Electrospun Alginate/Carbon Nanotube Composite Nanofiber. Dhaka Univ Bio-inspired and lanthanide-induced hierarchical sodium alginate/graphene oxide composite paper with enhanced physicochemical properties Graphene oxide reinforced alginate/PVA double network hydrogels for efficient dye removal Conductive core-sheath calcium alginate/graphene composite fibers with polymeric ionic liquids as an intermediate Synergistic effect and characterization of graphene/carbon nanotubes/polyvinyl alcohol/sodium alginate nanofibrous membranes formed using continuous needleless dynamic linear electrospinning Bio-based graphene/sodium alginate aerogels for strain sensors Graphene oxide increases the viability of C 2 C1 2 myoblasts microencapsulated in alginate Relative permittivity and electrical conductivity of some divalent metal alginate complexes Preparation and characterization of an alginate/clay nanocomposite for optoelectronic application Polypyrrole/Alginate Hybrid Hydrogels: Electrically Conductive and Soft Biomaterials for Human Mesenchymal Stem Cell Culture and Potential Neural Tissue Engineering Applications Water wettability/non-wettability of polymer materials by molecular orbital studies Graphene oxide nanosheets versus carbon nanofibers: Enhancement of physical and biological properties of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) films for biomedical applications Improvement of cell adhesion on poly(L-lactide) by atmospheric plasma treatment Biocompatibility and physicochemical characteristics of alginate-polycation microcapsules Hydrophilic alginate based multidentate biopolymers for surface modification of CdS quantum dots Alginate/Bioglass ® composite coatings on stainless steel deposited by direct current and alternating current electrophoretic deposition Review of the oral toxicity of polyvinyl alcohol (PVA)-PDF Free Download Electrophoretic co-deposition of polyvinyl alcohol (PVA) reinforced alginate-Bioglass ® composite coating on stainless steel: Mechanical properties and in-vitro bioactivity assessment The kinetics of the swelling process and the release mechanisms of Coriandrum sativum L. essential oil from chitosan/alginate/inulin microcapsules Pervaporation dehydration of aqueous ethanol and isopropanol mixtures through alginate/chitosan two ply composite membranes supported by poly(vinylidene fluoride) porous membrane Dynamic mechanical analysis and water vapour sorption of highly porous poly(methyl methacrylate) Ultrafast liquid water transport through graphene-based nanochannels measured by isotope labelling Fast diffusion of water nanodroplets on graphene Enhanced anti-swelling property and dehumidification performance by sodium alginate-poly(vinyl alcohol)/polysulfone composite hollow fiber membranes Water Sorption and Diffusion in (Reduced) Graphene Oxide-Alginate Biopolymer Nanocomposites Hybrid membrane biomaterials from self-assembly in polysaccharide and peptide amphiphile mixtures: Controllable structural and mechanical properties and antimicrobial activity Preparation and characterization of alginate hydrogel membranes crosslinked using a water-soluble carbodiimide Oxidized alginate hydrogels as niche environments for corneal epithelial cells Degradation behavior of covalently cross-linked poly(aldehyde guluronate) hydrogels Controlling rigidity and degradation of alginate hydrogels via molecular weight distribution Controlling degradation of hydrogels via the size of cross-linked junctions Controlling alginate gel degradation utilizing partial oxidation and bimodal molecular weight distribution Encapsulation of fibroblasts causes accelerated alginate hydrogel degradation Antiviral Properties of Alginate-Based Biomaterials: Promising Antiviral Agents against SARS-CoV-2 Biocompatible Films of Calcium Alginate Inactivate Enveloped Viruses such as SARS-CoV-2 Bio-based materials with novel characteristics for tissue engineering applications-A review Fabrication and antibacterial properties of ZnO-alginate nanocomposites Nano Zinc Oxide-Loaded Calcium Alginate Films with Potential Antibacterial Properties Nano zinc oxide-sodium alginate antibacterial cellulose fibres Exploration of alginate hydrogel/nano zinc oxide composite bandages for infected wounds Novel zinc alginate hydrogels prepared by internal setting method with intrinsic antibacterial activity Alginate/gum acacia bipolymeric nanohydrogels-Promising carrier for Zinc oxide nanopartic les Historical review of the use of silver in the treatment of burns.I. Early uses Prosthetic meshes for hernia repair: State of art, classification, biomaterials, antimicrobial approaches, and fabrication methods Comparative in vitro study on cytotoxicity, antimicrobial activity, and binding capacity for pathophysiological factors in chronic wounds of alginate and silver-containing alginate Development of silver sulfadiazine loaded bacterial cellulose/sodium alginate composite films with enhanced antibacterial property Silver-containing alginate fibres and dressings Antimicrobial and Anticancer Activities of Porous Chitosan-Alginate Biosynthesized Silver Nanoparticles Amsterdam, The Neitherlands Bacterial resistance to silver in wound care Poly (vinyl alcohol)-alginate physically crosslinked hydrogel membranes for wound dressing applications: Characterization and bio-evaluation Antimicrobial alginate/PVA silver nanocomposite hydrogel, synthesis and characterization Dual-crosslinked poly(vinyl alcohol)/sodium alginate/silver nanocomposite beads-A promising antimicrobial material Polyvinyl alcohol/Sodium alginate integrated silver nanoparticles as probable solution for decontamination of microbes contaminated water Study on antibacterial alginate-stabilized copper nanoparticles by FT-IR and 2D-IR correlation spectroscopy Optimized synthesis, characterization, and antibacterial activity of an alginate-cupric oxide bionanocomposite The bactericidal effect of dendritic copper microparticles, contained in an alginate matrix, on Escherichia coli Novel antimicrobial nanocomposite based on polypropylene non-woven fabric, biopolymer alginate and copper oxides nanoparticles Development of bacterial cellulose/alginate/chitosan composites incorporating copper (II) sulfate as an antibacterial wound dressing Physical Properties, Chemical Analysis, and Evaluation of Antimicrobial Response of New Polylactide/Alginate/Copper Composite Materials Interaction of Alginate/Copper System on Cotton and Bamboo Fabrics Development of copper-doped bioglass/alginate composite membranes: Preliminary results on their characterization and antimicrobial properties Additive manufacturing of anti-SARS-CoV-2 Copper-Tungsten-Silver alloy 3D Printing of Antimicrobial Alginate/Bacterial-Cellulose Composite Hydrogels by Incorporating Copper Nanostructures Copper oxide nanoparticles induce oxidative stress and cytotoxicity in airway epithelial cells Carbon-Based Nanomaterials: Promising Antiviral Agents to Combat COVID-19 in the Microbial-Resistant Era Enhancement of Antimicrobial Activity of Alginate Films with a Low Amount of Carbon Nanofibers (0.1% w/w) Serrano-Aroca, Á. Carbon Nanomaterials and LED Irradiation as Antibacterial Strategies against Gram-Positive Multidrug-Resistant Pathogens The Antibacterial Applications of Graphene and Its Derivatives Antimicrobial activity of alginate/clay nanocomposite films enriched with essential oils against three common foodborne pathogens Production and characterization of a new biodegradable fenugreek seed gum based active nanocomposite film reinforced with nanoclays Preparation of alginate-quaternary ammonium complex beads and evaluation of their antimicrobial activity Antimicrobial activity of lactoperoxidase system incorporated into cross-linked alginate films Antimicrobial films based on Na-alginate and κ-carrageenan Chitosan-sodium alginate polyion complexes as fuel cell membranes Chitosan-sodium alginate nanoparticles as submicroscopic reservoirs for ocular delivery: Formulation, optimisation and in vitro characterisation 1-3 mm Alginate/Chitosan Particles with Diclofenac by Dropwise Addition to CaCl 2 Solution 3D printed cobalt-chromium-molybdenum porous superalloy with superior antiviral activity Biomaterials Science: An Introduction to Materials in Medicine Hydrogel: Preparation, characterization, and applications: A review Efficient functionalization of alginate biomaterials RGD-peptide modified alginate by a chemoenzymatic strategy for tissue engineering applications Heparin as a prophylactic against thrombosis Heparin-like properties of sulfated alginates with defined sequences and sulfation degrees Polyvinyl alcohol/sulfated alginate nanofibers induced the neuronal differentiation of human bone marrow stem cells Heparin-functionalized polymeric biomaterials in tissue engineering and drug delivery applications Injectable hydrogels for cartilage and bone tissue engineering Poly(3-Hydroxybutyrate-co-3-Hydroxyvalerate): Enhancement strategies for advanced applications The preparation and characterization of polycaprolactone/graphene oxide biocomposite nanofiber scaffolds and their application for directing cell behaviors Graphene oxide decorated electrospun gelatin nanofibers: Fabrication, properties and applications Painting blood vessels and atherosclerotic plaques with an adhesive drug depot Alginate-catechol cross-linking interferes with insulin secretion capacity in isolated murine islet cells Biological activity of laminin peptide-conjugated alginate and chitosan matrices Neural differentiation of pluripotent cells in 3D alginate-based cultures Alginate and alginate/gelatin microspheres for human adipose-derived stem cell encapsulation and differentiation Osteogenic differentiation of human mesenchymal stem cells in mineralized alginate matrices Properties of an alginate-gelatinbased bioink and its potential impact on cell migration, proliferation, and differentiation A novel alginate-gelatin microcapsule to enhance bone differentiation of mesenchymal stem cells Alginateagarose hydrogels improve the in vitro differentiation of human dental pulp stem cells in chondrocytes. A histological study Sodium Alginate Modulates Immunity, Intestinal Mucosal Barrier Function, and Gut Microbiota in Cyclophosphamide-Induced Immunosuppressed BALB/c Mice Advanced oral vaccine delivery strategies for improving the immunity Cell Encapsulation Within Alginate Microcapsules: Immunological Challenges and Outlook Immunoengineering Biomaterials in Cell-Based Therapy for Type 1 Diabetes Selected topics in nanomedicine: Regenerative Medicine Fucoidan Hydrogels Significantly Alleviate Oxidative Stress and Enhance the Endocrine Function of Encapsulated Beta Cells An immune regulatory 3D-printed alginate-pectin construct for immunoisolation of insulin producing β-cells Advanced strategies to thwart foreign body response to implantable devices Long-term implant fibrosis prevention in rodents and non-human primates using crystallized drug formulations Characterisation of macroporous poly(methyl methacrylate) coated with plasma-polymerised poly(2-hydroxyethyl acrylate) Plasma-induced polymerisation of hydrophilic coatings onto macroporous hydrophobic scaffolds Effect of crosslinking on porous poly(methyl methacrylate) produced by phase separation Three-dimensional nanocomposite scaffolds with ordered cylindrical orthogonal pores Additive Manufacturing of 3D Aerogels and Porous Scaffolds: A Review Bioactive alginate/carrageenan/calcium silicate porous scaffolds for bone tissue engineering Cardiac tissue engineering, biomaterial scaffolds, and their fabrication techniques Scaffold Fabrication Technologies and Structure/Function Properties in Bone Tissue Engineering Correlation between porous texture and cell seeding efficiency of gas foaming and microfluidic foaming scaffolds Fabrication challenges and trends in biomedical applications of alginate electrospun nanofibers Porous Alginate Scaffolds Designed by Calcium Carbonate Leaching Technique Effect of heat-transfer capability on micropore structure of freeze-drying alginate scaffold State-of-the-art of 3D printing technology of alginate-based hydrogels-An emerging technique for industrial applications Recent progress in the fabrication techniques of 3D scaffolds for tissue engineering Enhancing the vascularization of three-dimensional porous alginate scaffolds by incorporating controlled release basic fibroblast growth factor microspheres Porous alginate/hydroxyapatite composite scaffolds for bone tissue engineering: Preparation, characterization, and in vitro studies Alginate-based nanofibrous scaffolds: Structural, mechanical, and biological properties Effects of chain conformation and entanglement on the electrospinning of pure alginate Gelatin nanofiber-reinforced alginate gel scaffolds for corneal tissue engineering Three-dimensional electrospun alginate nanofiber mats via tailored charge repulsions Electrospun alginate nanofibers with controlled cell adhesion for tissue engineering Electrospun chitosan-alginate nanofibers with in situ polyelectrolyte complexation for use as tissue engineering scaffolds Three-dimensional electrospun polycaprolactone (PCL)/alginate hybrid composite scaffolds Magnesium Oxide Nanoparticles Reinforced Electrospun Alginate-Based Nanofibrous Scaffolds with Improved Physical Properties Facile synthesis of three-dimensional reinforced Sn@polyaniline/sodium alginate nanofiber hydrogel network for high performance lithium-ion battery Fabrication of highly porous keratin sponges by freeze-drying in the presence of calcium alginate beads Fabrication of porous biodegradable polymer scaffolds using a solvent merging/particulate leaching method Alginate-chitosan/hydroxyapatite polyelectrolyte complex porous scaffolds: Preparation and characterization Novel porous, polysaccharide scaffolds for tissue engineering applications Developing highly porous collagen scaffolds by using alginate microsphere porogens for stem cell cultures Fused deposition modelling: Current status, methodology, applications and future prospects 3D printing of porous alginate/gelatin hydrogel scaffolds and their mechanical property characterization 3D printing for tissue engineering 3D Printing of Porous Cell-Laden Hydrogel Constructs for Potential Applications in Cartilage Tissue Engineering Cell(MC3T3-E1)-printed poly(ϵ-caprolactone)/alginate hybrid scaffolds for tissue regeneration 3D Bioprinting of heterogeneous aortic valve conduits with alginate/gelatin hydrogels Bioink properties before, during and after 3D bioprinting Engineering alginate as bioink for bioprinting Tunable hydrogel composite with two-step processing in combination with innovative hardware upgrade for cell-based three-dimensional bioprinting Characterization of printable cellular micro-fluidic channels for tissue engineering Sustained release of BMP-2 in bioprinted alginate for osteogenicity in mice and rats Hierarchical mesoporous bioactive glass/alginate composite scaffolds fabricated by three-dimensional plotting for bone tissue engineering Well-ordered biphasic calcium phosphate-alginate scaffolds fabricated by multi-channel 3D plotting under mild conditions Chondroinductive Alginate-Based Hydrogels Having Graphene Oxide for 3D Printed Scaffold Fabrication Preparation of 3-D regenerated fibroin scaffolds with freeze drying method and freeze drying/foaming technique Tailoring the pore architecture in 3-D alginate scaffolds by controlling the freezing regime during fabrication The effect of immobilized RGD peptide in macroporous alginate scaffolds on TGFβ1-induced chondrogenesis of human mesenchymal stem cells The effect of immobilized RGD peptide in alginate scaffolds on cardiac tissue engineering Curcumin loaded chitosan nanoparticles impregnated into collagen-alginate scaffolds for diabetic wound healing Alginate/poly (lactic-co-glycolic acid)/calcium phosphate cement scaffold with oriented pore structure for bone tissue engineering Chitosan-alginate as scaffolding material for cartilage tissue engineering Chitosan-alginate hybrid scaffolds for bone tissue engineering In-situ formation of the hydroxyapatite/chitosan-alginate composite scaffolds Coaxial structured collagen-alginate scaffolds: Fabrication, physical properties, and biomedical application for skin tissue regeneration Experimental measurement and simulation of mechanical strength and biological behavior of porous bony scaffold coated with alginate-hydroxyapatite for femoral applications Alginate sulfate-based hydrogel/nanofiber composite scaffold with controlled Kartogenin delivery for tissue engineering Fabrication of chitosan/alginate/hydroxyapatite hybrid scaffolds using 3D printing and impregnating techniques for potential cartilage regeneration The influence of the sequential delivery of angiogenic factors from affinity-binding alginate scaffolds on vascularization Manufacture of β-TCP/alginate scaffolds through a Fab@home model for application in bone tissue engineering Production of new 3D scaffolds for bone tissue regeneration by rapid prototyping 3D Bioplotting of Gelatin/Alginate Scaffolds for Tissue Engineering: Influence of Crosslinking Degree and Pore Architecture on Physicochemical Properties Novel 3D printed alginate-BFP1 hybrid scaffolds for enhanced bone regeneration Bioprinting of three-dimensional scaffold based on alginate-gelatin as soft and hard tissue regeneration In vitro and in vivo evaluation of 3D printed sodium alginate/polyethylene glycol scaffolds for sublingual delivery of insulin: Preparation, characterization, and pharmacokinetics Preparation of poly(D,L-lactic acid) scaffolds using alginate particles 3D porous gelatin/PVA hydrogel as meniscus substitute using alginate micro-particles as porogens Porous alginate scaffolds assembled using vaterite CaCO 3 crystals. Micromachines Three-dimensional porous alginate scaffolds provide a conducive environment for generation of well-vascularized embryoid bodies from human embryonic stem cells Physical and cytocompatibility properties of bioactive glass-polyvinyl alcohol-sodium alginate biocomposite foams prepared via sol-gel processing for trabecular bone regeneration Heparin-functionalized chitosan-alginate scaffolds for controlled release of growth factor Cells (MC3T3-E1)-laden alginate scaffolds fabricated by a modified solid-freeform fabrication process supplemented with an aerosol spraying Rapid prototyping of chitosan-coated alginate scaffolds through the use of a 3D fiber deposition technique Fibroin-Alginate Scaffold for Design of Floating Microspheres Containing Felodipine Biomimetic TiO 2 -chitosan/sodium alginate blended nanocomposite scaffolds for tissue engineering applications The authors acknowledge the support given by the Fundación Universidad Católica de Valencia San Vicente Mártir and the Spanish Ministry of Science and Innovation. The authors declare no conflict of interest.