key: cord-0819361-upnen752
authors: Badica, Petre; Batalu, Nicolae Dan; Chifiriuc, Mariana Carmen; Burdusel, Mihail; Grigoroscuta, Mihai Alexandru; Aldica, Gheorghe Virgil; Pasuk, Iuliana; Kuncser, Andrei; Popa, Marcela; Agostino, Angelo; Operti, Lorenza; Padhi, Santanu Kumar; Bonino, Valentina; Truccato, Marco
title: Sintered and 3D-Printed Bulks of MgB(2)-Based Materials with Antimicrobial Properties
date: 2021-10-06
journal: Molecules
DOI: 10.3390/molecules26196045
sha: df29fe3124e37314d36935173c2cc974cabe1d26
doc_id: 819361
cord_uid: upnen752

Pristine high-density bulk disks of MgB(2) with added hexagonal BN (10 wt.%) were prepared using spark plasma sintering. The BN-added samples are machinable by chipping them into desired geometries. Complex shapes of different sizes can also be obtained by the 3D printing of polylactic acid filaments embedded with MgB(2) powder particles (10 wt.%). Our present work aims to assess antimicrobial activity quantified as viable cells (CFU/mL) vs. time of sintered and 3D-printed materials. In vitro antimicrobial tests were performed against the bacterial strains Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, Staphylococcus aureus ATCC 25923, Enterococcus faecium DSM 13590, and Enterococcus faecalis ATCC 29212; and the yeast strain Candida parapsilosis ATCC 22019. The antimicrobial effects were found to depend on the tested samples and microbes, with E. faecium being the most resistant and E. coli the most susceptible.

Planktonic and biofilm-forming microbes are among the most important threats to human health. In the EU, 25,000 people die every year due to infections with antibiotic-resistant bacteria, and the management of these infections costs about 1.5 billion EUR/year [1]. This problem could be considered a crisis, because the rate of development and commercialization of novel effective antibiotics has slowed [2] . Moreover, government funds and efforts have recently been focused on other urgent problems, such as the COVID-19 pandemic crisis. From 1930 to 1962, 20 new types of antibiotics were developed; meanwhile, from 1962 to the present, only 2 new types of antibiotics have gone into production [3] [4] [5] . Modern antimicrobial strategies are needed [6] , and among them, nanostructured materials such as powders, coatings, and bulks are promising candidates [7] [8] [9] . The literature also offers examples of many bioactive metals including Ag, Cu, Zn, Mg, Ce, Ti, Al, Si, Au, Bi, Ca, Fe, Pt, Sn, Hg, Cd, Cr, Tl, Al, Co, In, Ni, Mn, and Cr [10] [11] [12] [13] [14] . The first two, Ag and Cu [15] , are the most popular, being already used in many antimicrobial applications. Metals are often used as oxides, hydroxides, halides, and sulfates [10, 16] or they are introduced as active components in alloys (e.g., brasses, bronzes, copper-nickel-zinc) and in composite materials (e.g., steels, hydroxyapatite, polymer/resin matrices, and textiles [15, 17] ). Antimicrobial non-metals such as C (e.g., fullerene, carbon nanotubes, graphene oxide) [18] [19] [20] [21] [22] or B [23, 24] and their compounds have also been reported to display antimicrobial functions. Other antimicrobial materials include quaternary ammonium compounds and synthetic or natural polymers (e.g., peptides, lactoferrin, chitosan) [11, 15] . However, synthetic polymers often need physical, chemical, or mechanical surface modifications [15] to optimize their efficiency against microbes.

Magnesium diboride (MgB 2 ) is well-known for its superconducting properties [25] . MgB 2 can be prepared by a variety of methods, including spark plasma sintering (SPS) [26] [27] [28] [29] [30] [31] . Our research group has recently reported for the first time in the scientific literature the potential for the antimicrobial applications of MgB 2 materials (powders and biodegradable coatings based on polyvinylpyrrolidone) for the clinical field and for combating the negative impact of microbial colonization in different environments, as with the biodeterioration of heritage buildings [26, [32] [33] [34] [35] . We have previously shown that the antimicrobial activity of MgB 2 powders depends on the fabrication process (e.g., MgB 2 powders produced by reactive liquid infiltration (RLI) show superior performance to commercial powders) as well as their purity, microstructure, and pH behavior in water. Another important aspect revealed by our results was the good performance of these materials against a large spectrum of bacterial and fungal strains and their similar efficiency against microbes, both in the planktonic and the biofilm growth state. Biofilms are known to be significantly more resilient than individual microbes, and thus pose a higher health threat [36] .

Considering the acute need for developing novel solutions to prevent and combat biofilms and the promising results reported in our previous papers for the antibiofilm potential of MgB 2 coatings, we have continued our research in this direction. In the present paper, we focus on the bulk of this material to assess its in vitro antimicrobial activity against Gram-negative and Gram-positive bacteria, as well as yeast strains.

The bulk materials investigated in this work are sintered MgB 2 high-density massive samples obtained by SPS and 3D printed samples of a polylactic acid (PLA) with the addition of MgB 2 powder. For our study, we selected PLA for its wide availability, low price, biodegradability, and readiness for 3D printing [37] [38] [39] . PLA has great biocompatibility [39] , and some of its applications are already in use (bone fixation screws, stent coating, bioresorbable suture threads, etc.). The advantage of using the 3D-printing approach is that it allows the fabrication of functional medical devices with antimicrobial properties in diverse and complex shapes at low costs, and it is adapted for small series production. Bulks of sintered MgB 2 were shown to have mechanical properties close to conventional structural SiC or Al 2 O 3 ceramic (i.e., they are relatively hard and brittle) [40] . This makes it difficult to fabricate pristine MgB 2 into precise and complex geometries by mechanical processing. Therefore, machinable MgB 2 [41] sintered bulks with added hexagonal BN and 3D-printed materials with embedded MgB 2 can provide the needed (complex) shape and size for applications.

The bulk materials based on MgB 2 in this work that allow processing into complex shapes are envisioned for applications such as medical devices (artificial prosthetics and biodegradable implants [42, 43] , drug delivery systems) and self-sterilizing medical instruments with time-and space-controlled activity. Apart from the degradation and release of the active components with antimicrobial activity, the proposed bulks are also expected to allow mechanical support control. Other possible applications could be found in the packaging industry [44] , such as for food transportation, preservation, and the enhancement of shelf life complimented by eco-friendly packaging with high levels of water biodegradability and biocompatibility. Other applications of bulk bioactive materials based on MgB 2 could be found in industries where free surfaces of biological materials are necessary. The management of potable water could become a viable application [24] , but other biofouling applications are also expected to emerge.

High-density (>95%, Table 1 ) bulk samples of MgB 2 ( Figure 1a ) and MgB 2 -added with 10 wt.% hexagonal BN (hBN) were prepared by SPS in a vacuum at 1150 • C for 3 min, under a maximum uniaxial pressure of 95 MPa. The raw powders were MgB 2 (LTS Research Laboratories Inc, 99.5% purity, <44 µm) and hBN (High Purity Chemicals, >99%, 10 µm). The details of sample fabrication by SPS were reported in [41, 45] . The hBN-added MgB 2 was demonstrated to be machinable by chipping in [41] . Composite filaments of PLA ( Figure 1b ) with embedded MgB 2 particles (LTS Research Laboratories Inc, Orangeburg, NY, USA, 99.5% purity, <44 µm) were prepared in two steps. In the first step, commercial PLA was dissolved in chloroform and mixed with MgB 2 powder (10 wt.%). In the second step, after the evaporation of chloroform, the PLA+MgB 2 solid layer was cut into small pellets and extruded as filaments [46] with a Noztek extruder. The composite polymer-ceramic filaments had an average diameter of 1.65 mm (±0.05). Printing into square shapes (~10 mm × 10 mm) with a thickness of~3 mm (Figure 1c ) was performed with a WASP 2040 Turbo 2 3D printer (based on fused filament fabrication, FFF) with a 0.7 mm nozzle diameter. The printing temperature was 210 • C and the bed temperature was 60 • C, with 100% infill and a printing speed of 20 mm/s.

The antimicrobial activity of the MgB 2 -hBN sintered bulk and PLA-MgB 2 3D-printed samples was tested by using reference bacterial and fungal strains: Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, Staphylococcus aureus ATCC 25923, Enterococcus faecium DSM 13590, Enterococcus faecalis ATCC 29212, and Candida parapsilosis ATCC 22019.

The MgB 2 bulk disks were incubated in a humid atmosphere at 37 • C for 6 and 24 h, in contact with microbial suspensions of 10 5 CFU (colony-forming units)/mL density. After incubation, the materials were washed with distilled water to remove unadhered microorganisms and sonicated for 15 s at maximum power. Next, they were vortexed for 15 s at 3000 rpm to recover the adherent microorganisms that were quantified by determining the viable cells expressed as CFU/mL.

The antimicrobial activity of the bulk sintered MgB 2 -hBN was tested using a final inoculum density of 5 × 10 5 CFU/mL prepared in a 10 mL saline solution, with the microbial viability being assessed after different contact times (0.5 h, 1 h, 2 h, 3 h, 4 h, 5 h, 6 h, 24 h) and expressed as CFU/mL. The antibacterial activity of PLA samples with embedded MgB 2 particles was assessed by the direct contact method: A~10 8 CFU/mL microbial suspension was distributed over the sterile material samples and incubated in a humid atmosphere for 2 h, 4 h, and 24 h at 37 • C. After incubation, the colonized samples were placed in 2 mL of sterile saline and were vigorously shaken to detach the adherent bacterial cells. The harvested bacterial suspension was further used to prepare serial dilutions to quantify bacterial growth by counting the resulting colonies and calculating the colony-forming units (CFU/mL).

All the assays were performed in duplicate, and the statistical analysis of the obtained materials was performed using a paired t test with GraphPad Prism (version 8.0.0 for Windows, GraphPad Software, San Diego, CA, USA, www.graphpad.com, accessed on 4 October 2020).

The raw MgB 2 powder and sintered bulk samples were subjected to X-ray diffraction (Bruker AXS D8 Advance diffractometer, CuKα radiation). Rietveld analysis (MAUD 2.31 [47] ) was applied to determine the weight fraction of the phases, a and c lattice parameters of MgB 2 , the crystallite size, and the residual strain for different phases (Table 1) . The amount of carbon (denoted y, Table 1 ) substituting boron in the crystal lattice of MgB 2 (Mg(B 1−y C y ) 2 ) was calculated with the empirical formula: y = −21.9·a + 6.76 (a in nm)

(1)

considering mediated data from [48] [49] [50] .

The apparent bulk density of the sintered samples (r a ) was measured by the Archimedes method. The relative density, R = (r a /r t ) × 100 (%), where r t is the theoretical mass density [51] , was calculated by considering all identified phases (MgB 2 , MgO, MgB 4 , and Mg) as determined by Rietveld analysis [47] . The microstructure of the samples was observed using scanning electron microscopy (SEM, Lyra 3XMU/Tescan). Metallographic polishing of the sintered samples was made with different oil-based emulsions of Al 2 O 3 down to a particle size of 1 µm. Saline suspensions with cultures (see Section 2.2) were placed on the as-polished surfaces.

We obtained, characterized, and bio-assessed the anti-biofilm activity of various types of samples based on MgB 2 fabricated by SPS (pristine MgB 2 and hBN-added MgB 2 ) and FFF 3D printing. The obtained samples exhibited significant antimicrobial activity against adherent strains at short incubation times (less than 6 h) and against subsequently formed biofilms at longer incubation times of 24 h. This behavior represents an important advantage: the early occurrence of an inhibitory effect on bacterial growth prevents the development of bacterial biofilms on the surface of medical devices. The antimicrobial activity of MgB 2 , its good biodegradability and biocompatibility, as well as its anti-inflammatory properties promote this material as a useful candidate for a wide range of biomedical applications.

XRD spectra and the results of Rietveld analysis on as-sintered pristine MgB 2 samples are presented in Figure 2a and Table 1 . The MgB 2 raw powder was 97 wt.% MgB 2 phase, and the impurity phases were MgO and metallic Mg (Table 1) . After sintering, the MgB 2 phase decreased by about 10 wt.% in the pristine sample, and the newly formed secondary phases were MgB 4 and MgO. In the hBN-added sample, the amount of MgB 2 was 78 wt.%. If~10 wt.% of hBN is not taken into consideration, the maximum amount in the added sample would be~88 wt.%, which is comparable to the 87.5% value in the pristine sample. As previously reported, hBN has little influence, if any, on the decomposition reactions of MgB 2 during SPS [45] . The crystallite size of MgB 2 during SPS showed some increase, but it was within the range of experimental error. The crystallite sizes of MgB 2 , MgO, and MgB 4 for pristine and hBN-added SPS-processed samples can be considered similar. This result also supports the inertness of hBN compared to MgB 2 . In addition, there was little difference in the carbon intake during SPS between the pristine and hBN-added samples. As presented in Section 2.3, insertion of carbon in the crystal lattice of MgB 2 decreased the a-axis lattice parameter, while the c-axis lattice parameter remained almost constant (Table 1 ). In addition, this is usually accompanied by an increase in microstrain. This trend can be observed when raw powder and sintered samples are compared. However, in the sintered samples, this correlation did not hold up, since the higher y-carbon level in sample LTS SPS (0.0114) than in the sample LTS + (hBN) 0.01 SPS (0.0076) induced a lower microstrain of 0.12% vs. 0.14%, respectively. The amount of carbon, a biocompatible material, was very low in the sintered samples [52] . The results of in vitro antimicrobial activity are presented in Figures 3-5 . The results demonstrate significant antimicrobial activity for the pristine MgB 2 bulk material. Both the initial phase of adhesion of microorganisms quantified after 6 h of contact and the mature biofilm growth quantified after 24 h of incubation were inhibited. For pristine MgB 2 sintered bulks, after 6 h of incubation there was a significant decrease in microbial growth for E. coli and S. aureus ( Figure 3 ) and a total growth inhibition of the P. aeruginosa strain. After 24 h of incubation, the samples had completely inhibited the growth of four out of the five tested microbial strains (i.e., E. coli, P. aeruginosa, S. aureus, and C. parapsilosis). These results demonstrate significant antimicrobial activity of the pristine MgB 2 bulk material. The initial phase of the microorganisms' adhesion was quantified after 6 h of contact (statistically significant for E. coli and P. aeruginosa, P < 0.0005), and the mature biofilms' growth was quantified after 24 h of contact. The results for pristine MgB 2 bulks were reproduced in machinable hBN-added MgB 2 sintered samples (Figure 4) . The results for the hBN-added samples showed that MgB 2 had inhibitory and microbicidal effects on the microbial strains included in the study. Its efficacy was more pronounced for the Gram-negative strains E. coli and P. aeruginosa, which were no longer viable after 1 and 2 h of contact, respectively. Regarding the Gram-positive bacteria, the inhibitory effect of MgB 2 against S. aureus started after 3 h of incubation and against E. faecalis after 6 h, and it was complete after 4 h and 24 h of incubation for S. aureus and E. faecalis, respectively. C. parapsilosis fungal strains are among the most frequently isolated fungi on human skin [53] , and in our study the tested strain was the most resistant to the inhibitory effects of the tested samples. However, the fungicidal effect was initiated at 24 h. No viable cells of P. aeruginosa survived after 2 h of incubation. The comparison of the antimicrobial activity of the two types of sintered materials (i.e., pristine MgB 2 bulk and hBN-added MgB 2 sintered samples) reveals a higher efficacy of the latter against E. faecium after 6 h and 24 h of incubation, and similar activity against the other four tested microbial strains for those two incubation periods.

The 3D-printed PLA+10 wt.% MgB 2 samples were tested for their anti-biofilm activity against two strains: the Gram-negative E. coli and the Gram-positive S. aureus ( Figure 5 ). Statistical analysis was not performed for the polymer-MgB 2 results. These results are preliminary, and more experiments are needed. The pristine PLA polymer is inert with respect to microbes [54] , and therefore, if there is an antimicrobial effect it could likely be ascribed to the MgB 2 from the 3D-printed samples. Analysis of the biofilm dynamics evidenced that the 3D-printed samples had an inhibitory effect on microbial cell adhesion after 2 h of incubation. At 24 h of incubation, the number of viable bacteria cells decreased by 5 log units, and no viable cells were observed at 48 h of incubation. These results suggest that it is necessary to carefully select the type and concentration of the composite components to improve and control antimicrobial activity over space and time.

The antimicrobial activity efficiency over time for a given material depends on the microbial strain. This raises the question of whether the adherent strains affect the surface structure of the colonized material over time. If this were the case, it could partially explain the differences observed in the intensity of the antimicrobial effect exhibited by different surfaces in contact with different strains for different contact times. Figure 2b shows the XRD spectra of the surface of the pristine MgB 2 sintered bulk samples after removing the E. coli, E. faecium, and S. aureus biofilms. There are no notable differences among the samples. A similar result can be inferred from the microscopy data (Figure 6) , where, to avoid redundancy, only the samples that were in contact with E. faecium are shown. When surfaces of samples in contact with other strains were investigated (not shown here) no particularities were revealed. Table 1 ) after being in contact with E. faecium, and RGB images obtained by overlapping the EDS maps. The presence of Cl and Na on the surface is from the saline solution used for the in vitro tests.

We conclude that the process of surface corrosion develops independently of the microbial strain, and it could be influenced by the saline solution. Corrosion-specific features are similar to those reported in [35] . More research is needed on corrosion vs. the antimicrobial effect of MgB 2 -based materials.

Taken together, the biological assays suggest significant antimicrobial activity of MgB 2 materials (pristine, added, or composite), making them promising candidates for the development of novel antimicrobial strategies. Further studies are required to establish the detailed mechanisms of the antimicrobial activity revealed by the tested MgB 2 -based materials. However, we could speculate that the antimicrobial activity may be due to the release of Mg 2+ ions, which could affect the integrity of microbial cell membranes or disrupt mem-brane potential and cause the leakage of cellular contents and eventually cell lysis [54] [55] [56] [57] [58] . The anti-biofilm effect of Mg 2+ ions could result from downregulation of extracellular matrix gene expression [59] or from the enhancement of c-di-GMP degradation, which would decrease biofilm formation [60] . Moreover, considering the anti-inflammatory effects of magnesium, we expect that the use of these materials in antimicrobial formulations could lead to the attenuation of tissue lesions caused by an increased inflammatory response to the presence of pathogens [61] .

In this paper, we outlined how we obtained, characterized, and bio-evaluated the anti-biofilm activity of samples based on MgB 2 fabricated by SPS (pristine MgB 2 and hBNadded MgB 2 ) and as 3D-printed composite (PLA embedded with 10 wt.% MgB 2 particles). These samples inhibited both the initial phases of biofilm development quantified after 6 h of incubation and the mature biofilms at 24 h. The antimicrobial activity of MgB 2 , its good biodegradability and biocompatibility, as well as its anti-inflammatory properties promote this material as a useful candidate for a wide range of biomedical applications, including the development of novel biomaterials resistant to microbial colonization that would present a low risk for developing medical device biofilm-associated infections. Data Availability Statement: The raw/processed data required to reproduce these findings cannot be shared at this time as the data also form part of an ongoing study. Data are available from the corresponding authors on request.

The Quest for Novel Antimicrobial Compounds: Emerging Trends in Research, Development, and Technologies. Antibiotics

Bad bugs, no drugs: No ESKAPE! An update from the Infectious Diseases Society of America

Where will new antibiotics come from?

Platforms for antibiotic discovery

Bacterial biofilm formation on implantable devices and approaches to its treatment and prevention

Metallic-based micro and nanostructures with antimicrobial activity

Robust Hierarchical Porous PTFE Film Fabricated via Femtosecond Laser for Self-Cleaning Passive Cooling

Solar-driven thermal-wind synergistic effect on laser-textured superhydrophilic copper foam architectures for ultrahigh efficient vapor generation

5-Antibacterial bioactive materials

The role of magnesium in biomaterials related infections

Antimicrobial materials with medical applications

Escherichia coli damage by ceramic powder slurries

Antibacterial activity of copper monodispersed nanoparticles into sepiolite

Review on the antimicrobial properties of Carbon nanostructures

Inactivation of bacteriophages via photosensitization of fullerol nanoparticles

Bacterial cell association and antimicrobial activity of a C60 water suspension

Antibacterial effects of carbon nanotubes: Size does matter

Synthesis, characterization, and bactericidal evaluation of chitosan/guanidine functionalized graphene oxide composites

The importance of boron in biological systems

Minimum inhibitory and minimum bactericidal concentrations of boron compounds against several bacterial strains. Turk

Superconductivity at 39 K in magnesium diboride

Spark plasma sintering of MgB 2 in the two-temperature route. Phys. C

Microwave Synthesis of Fullerene-Doped MgB 2

Synthesis of bulk MgB 2 superconductors by pulsed electric current

The influence of HIP on the homogeneity, Jc, Birr, Tc and Fp in MgB 2 wires

A New Generation of In Situ MgB 2 Wires With Improved J(c) and B-irr Values Obtained by Cold Densification (CHPD)

Trapped magnetic field of dense MgB 2 bulks fabricated under high pressure. Phys. Procedia

MgB 2 powders and bioevaluation of their interaction with planktonic microbes, biofilms, and tumor cells

Antibacterial composite coatings of MgB 2 powders embedded in PVP matrix

In Vitro Evaluation of MgB 2 Powders as Novel Tools to Fight Fungal Biodeterioration of Heritage Buildings and Objects

Evaluation of pristine and Eu 2 O 3 -added MgB 2 ceramics for medical applications: Hardness, corrosion resistance, cytotoxicity and antibacterial activity

Understanding biofilm resistance to antibacterial agents

A literature review of Poly(lactic acid)

3D printed mesh reinforced geopolymer: Notched prism bending

A perspective of polylactic acid-based polymers use for nanoparticles synthesis and applications

Compressive properties of pristine and SiC-Te-added MgB 2 powders, green compacts and spark-plasma-sintered bulks

Machinable Superconducting Material and Magnetic Field Concentrator/Storer Made of a Superconducting Material Based on MgB 2 , Machinable by Chip Remova. Patent No. RO130252-B1

Biomechanical comparison of biodegradable magnesium screws and titanium screws for operative stabilization of displaced capitellar fractures

Magnesium-Based Compression Screws: A Novelty in the Clinical Use of Implants

Review of antimicrobial food packaging

Significant enhancement of the critical current density for cubic BN addition into ex situ spark plasma sintered MgB 2

Functional Composite Material with Matrix of Polymer and MgB 2 Powder Addition. Patent Request No. RO134554-A0

Total pattern fitting for the combined size-strain-stress-texture determination in thin film diffraction

Dwell time influence on spark plasma-sintered MgB 2

Crystal chemistry of carbon-substituted MgB 2 . Phys. C

Crystal growth of C-doped MgB 2 superconductors: Accidental doping and inhomogeneity. Phys. C

Effect of certain group IV oxides on dielectric constant and dissipation factor of barium titanate

Graphene as an Enabling Strategy for Dental Implant and Tissue Regeneration

Candida parapsilosis, an Emerging Fungal Pathogen

Antimicrobial PLA films from environment friendly additives

Calcium and Magnesium Ions Are Membrane-Active against Stationary-Phase Staphylococcus aureus with High Specificity

In vitro antibiofilm and anti-Adhesion effects of magnesium oxide nanoparticles against antibiotic resistant bacteria

Thin magnesium layer confirmed as an antibacterial and biocompatible implant coating in a coculture model

Fast corroding, thin magnesium coating displays antibacterial effects and low cytotoxicity

Antibiofilm activity of nanosized magnesium fluoride

Antimicrobial Properties of Magnesium Open Opportunities to Develop Healthier Food

Magnesium deficiency and increased inflammation: Current perspectives

Acknowledgments: S.K.P., V.B. and M.T. also acknowledge partial support from the "Departments of Excellence" (L. 232/2016) grant, funded by MIUR. The funders had no role in the study, design, data collection and analysis, decision to publish, or preparation of the manuscript. Authors acknowledge MIUR, UEFISCDI, and EU for financial support. S.K.P., N.B., V.B. and M.T. also acknowledge partial support fromthe "Departments of Excellence" (L. 232/2016) grant, funded by MIUR.

The authors declare no conflict of interest.