key: cord-0817256-k72c2psi authors: Liu, Kai-Hsi; Lin, Hung-Yin; Thomas, James L.; Chen, Chen-Yuan; Chen, Yen-Ting; Chen, Chuen-Yau; Yang, Chien-Hsin; Lee, Mei-Hwa title: Sensing of C-Reactive Protein Using an Extended-Gate Field-Effect Transistor with a Tungsten Disulfide-Doped Peptide-Imprinted Conductive Polymer Coating date: 2022-01-07 journal: Biosensors (Basel) DOI: 10.3390/bios12010031 sha: 68a772c0662277442dba27ad014c43da9e95b63d doc_id: 817256 cord_uid: k72c2psi C-reactive protein (CRP) is a non-specific biomarker of inflammation and may be associated with cardiovascular disease. In recent studies, systemic inflammatory responses have also been observed in cases of coronavirus disease 2019 (COVID-19). Molecularly imprinted polymers (MIPs) have been developed to replace natural antibodies with polymeric materials that have low cost and high stability and could thus be suitable for use in a home-care system. In this work, a MIP-based electrochemical sensing system for measuring CRP was developed. Such a system can be integrated with microfluidics and electronics for lab-on-a-chip technology. MIP composition was optimized using various imprinting template (CRP peptide) concentrations. Tungsten disulfide (WS(2)) was doped into the MIPs. Doping not only enhances the electrochemical response accompanying the recognition of the template molecules but also raises the top of the sensing range from 1.0 pg/mL to 1.0 ng/mL of the imprinted peptide. The calibration curve of the WS(2)-doped peptide-imprinted polymer-coated electrodes in the extended-gate field-effect transistor platform was obtained and used for the measurement of CRP concentration in real human serum. C-reactive protein (CRP) is a ring-shaped pentameric protein that is found in blood plasma. Elevated serum levels of CRP are associated with inflammation and severe disease in bacterial or viral infections [1] . Low-grade inflammation has recently been discovered to increase the risk of cardiovascular disease [2] . A systemic inflammatory response has been observed in cases of coronavirus disease 2019 (COVID- 19) , and 97.8% of patients with that disease have CRP concentrations above the normal range [1] . A CRP test may be used to find or monitor conditions that cause inflammation, such as sepsis [3] , bowel disease [4] , lupus or rheumatoid arthritis [5] , and osteomyelitis [6] . CRP has also been implicated in the breakdown of important biological barriers. For example, monomeric CRP can cross the retinal pigment endothelium and may cause macular degeneration through the disruption of the outer blood-retinal barrier [7] . Moreover, C-reactive protein (CRP) has been demonstrated to induce blood brain barrier (BBB) disruption in a process involving NAD(P)H-oxidase dependent oxidative stress [8] . BBB disruption in patients deceased from sepsis was found to correlate with elevated CRP levels [9] . Molecularly imprinted polymers (MIPs) were developed to generate artificial antibodies at low cost and comparatively high stability for the recognition of biomolecules [10] . Two approaches can be used in preparing MIPs that recognize CRP: The whole protein may be used, or specific peptide epitopes derived from the protein sequence. When using the whole protein, it has been important to recognize that the physiological role of CRP is to bind to lysophosphatidylcholine (lysoPC) expressed on the surface of dead or dying cells, and some types of bacteria (by which CRP activates the complement system via C1q [11] ). Thus, using functional monomers that mimic lysoPC is important [12] [13] [14] [15] . For example, o-(4-nitrophenylphosphoryl) choline (4NPPC) has been employed as the functional monomer in microcontact imprinting CRP [12] , 3(4)-vinylbenzyl 12-phosphorylcholine-dodecanoate was designed and synthesized specifically to form CRP-recognizing MIPs [13] . Notably, the template used in all of the aforementioned approaches was whole CRP, not peptide fragments. When using a peptide epitope, there is no reason to expect that a lysoPC mimic would improve performance (since the peptide alone does not bind lysoPC). In this work, we have taken this approach, using a peptide (KESDTSYVSLKAPL, designated pK) as the imprinted epitope. One decade ago, the chemistry [16] , electronic and optoelectronic properties of twodimensional layered transition metal dichalcogenide (TMDC) nanosheets were reviewed [17] . The structure of the TMDC tungsten disulfide (WS 2 ) is based on a hexagonal crystal in which each tungsten (W) atom is six-fold coordinated and hexagonally packed between two trigonally coordinated sulfur (S) atoms [18] . It forms layers that are bound by weak van der Waals' interactions [16] , and these layered structures usually exhibit strongly anisotropic electrical, chemical, mechanical, and thermal properties [17] . Biological sensing [19] and medical diagnosis [20] using TMDCs were both recently reviewed. Tungsten disulfide has also been used in the detection of small molecules (such as H 2 O 2 and glucose) [20] , DNA, and RNA [19] . Our previous studies have demonstrated the utility of doping TMDCs into MIPs for the ultrasensitive determination of 17β-estradiol concentration [21] . TMDCs have also been added to optimize the performance of peptide-imprinted conductive polymers as electrochemical sensors [22] . In the present work, CRP peptide-imprinted polymers were synthesized and optimized using various imprinting concentrations of template peptide molecules and doping concentrations of WS 2 (Scheme 1). CRP concentrations in real human serum were measured using the extended gate field-effect transistor (EGFET) platform [23, 24] . Biosensors 2022, 12, x FOR PEER REVIEW 2 of 8 been implicated in the breakdown of important biological barriers. For example, monomeric CRP can cross the retinal pigment endothelium and may cause macular degeneration through the disruption of the outer blood-retinal barrier [7] . Moreover, Creactive protein (CRP) has been demonstrated to induce blood brain barrier (BBB) disruption in a process involving NAD(P)H-oxidase dependent oxidative stress [8] . BBB disruption in patients deceased from sepsis was found to correlate with elevated CRP levels [9] . Molecularly imprinted polymers (MIPs) were developed to generate artificial antibodies at low cost and comparatively high stability for the recognition of biomolecules [10] . Two approaches can be used in preparing MIPs that recognize CRP: The whole protein may be used, or specific peptide epitopes derived from the protein sequence. When using the whole protein, it has been important to recognize that the physiological role of CRP is to bind to lysophosphatidylcholine (lysoPC) expressed on the surface of dead or dying cells, and some types of bacteria (by which CRP activates the complement system via C1q [11] ). Thus, using functional monomers that mimic lysoPC is important [12] [13] [14] [15] . For example, o-(4-nitrophenylphosphoryl) choline (4NPPC) has been employed as the functional monomer in microcontact imprinting CRP [12] , 3(4)-vinylbenzyl 12phosphorylcholine-dodecanoate was designed and synthesized specifically to form CRPrecognizing MIPs [13] . Notably, the template used in all of the aforementioned approaches was whole CRP, not peptide fragments. When using a peptide epitope, there is no reason to expect that a lysoPC mimic would improve performance (since the peptide alone does not bind lysoPC). In this work, we have taken this approach, using a peptide (KESDTSYVSLKAPL, designated pK) as the imprinted epitope. One decade ago, the chemistry [16] , electronic and optoelectronic properties of twodimensional layered transition metal dichalcogenide (TMDC) nanosheets were reviewed [17] . The structure of the TMDC tungsten disulfide (WS2) is based on a hexagonal crystal in which each tungsten (W) atom is six-fold coordinated and hexagonally packed between two trigonally coordinated sulfur (S) atoms [18] . It forms layers that are bound by weak van der Waals' interactions [16] , and these layered structures usually exhibit strongly anisotropic electrical, chemical, mechanical, and thermal properties [17] . Biological sensing [19] and medical diagnosis [20] using TMDCs were both recently reviewed. Tungsten disulfide has also been used in the detection of small molecules (such as H2O2 and glucose) [20] , DNA, and RNA [19] . Our previous studies have demonstrated the utility of doping TMDCs into MIPs for the ultrasensitive determination of 17β-estradiol concentration [21] . TMDCs have also been added to optimize the performance of peptideimprinted conductive polymers as electrochemical sensors [22] . In the present work, CRP peptide-imprinted polymers were synthesized and optimized using various imprinting concentrations of template peptide molecules and doping concentrations of WS2 (Scheme 1). CRP concentrations in real human serum were measured using the extended gate fieldeffect transistor (EGFET) platform [23, 24] . Scheme 1. Sensing of C-reactive protein using a tungsten disulfide-doped peptide-imprinted conductive polymer-coated electrode in an extended-gate field-effect transistor. Scheme 1. Sensing of C-reactive protein using a tungsten disulfide-doped peptide-imprinted conductive polymer-coated electrode in an extended-gate field-effect transistor. Figure 1a ,b presents the electropolymerization curves that show the effects of doping 90 nm WS 2 flakes into poly(AN-co-MSAN), from 0 and 0.5 wt%. There is broad oxidation peak at 0.20-0.25 V and slightly narrower reduction peak at −0.05 V. All curves were with a target pK concentration of 0.5 wt%. The peak currents (both oxidation and reduction) decreased slightly with the increasing concentration of the dopant WS 2 . Figure 1c shows that higher target (pK) concentrations lead to lower polymerization current (at the 20th polymerization cycle). The current intensity of the oxidation peak decreased approximately exponentially as the amount of added peptide increased, as expected when the peptide competes with AN for binding to SO 3− on MSAN. Figure 1d shows that higher WS 2 dopant concentrations have the same effect and also greatly reduce polymerization currents at the 20th cycle. In previous work, we have shown that there is an anticorrelation between polymerization current and sensing current [25] . Therefore, the lower polymerization current should give greater sensing current changes, and thus we selected pK and WS 2 concentrations of 0.5 wt% for subsequent MIP preparation. Moreover, our previous work also demonstrated the relationship of polymerization duration and the imprinting effectiveness [26] and showed that the thickness of the MIP layer is related to recognition capacity [27] . Figure 1a ,b presents the electropolymerization curves that show the effects of doping 90 nm WS2 flakes into poly(AN-co-MSAN), from 0 and 0.5 wt%. There is broad oxidation peak at 0.20-0.25 V and slightly narrower reduction peak at −0.05 V. All curves were with a target pK concentration of 0.5 wt%. The peak currents (both oxidation and reduction) decreased slightly with the increasing concentration of the dopant WS2. Figure 1c shows that higher target (pK) concentrations lead to lower polymerization current (at the 20th polymerization cycle). The current intensity of the oxidation peak decreased approximately exponentially as the amount of added peptide increased, as expected when the peptide competes with AN for binding to SO 3− on MSAN. Figure 1d shows that higher WS2 dopant concentrations have the same effect and also greatly reduce polymerization currents at the 20th cycle. In previous work, we have shown that there is an anticorrelation between polymerization current and sensing current [25] . Therefore, the lower polymerization current should give greater sensing current changes, and thus we selected pK and WS2 concentrations of 0.5 wt% for subsequent MIP preparation. Moreover, our previous work also demonstrated the relationship of polymerization duration and the imprinting effectiveness [26] and showed that the thickness of the MIP layer is related to recognition capacity [27] . Figure 2c shows the calibration curves obtained from the voltammograms in Figure 2a ,b. The calibration curves plot the difference between the peak current obtained in a pK (target) solution and that obtained in buffer alone for pK concentrations varying over seven orders of magnitude. The pKIP-and NIP-coated electrodes began to show an onset of saturation (i.e., a leveling-off of the response) beginning at about 1.0 pg/mL, Figure 2c . Doping with WS 2 increases the amplitude of the response but also extends the (log)-linearity and useful sensing range up to at least 1.0 ng/mL. Figure 2d shows the responses of WS 2 -doped pK-imprinted electrodes to other peptides taken from CRP sequences. The response of the electrode to these irrelevant peptides is very similar to the responses obtained with non-imprinted electrodes to pK. This is an important result that we will discuss further, vide infra. 20th polymerization cycles during the preparation of peptide-imprinted polymer electrodes with various concentrations of (c) peptides K or (d) 90 nm WS2. Figure 2a ,b display the cyclic voltammograms of WS2/NIPs-and WS2/pKIPs-coated electrodes used to sense various peptide K concentrations in an aqueous solution. The oxidation and reduction current peaks were at 0.2 and −0.1 V, respectively, possibly corresponding to the oxidation and reduction of coupled Fe(CN)6 3+ and Fe(CN)6 4+ . Figure 2c shows the calibration curves obtained from the voltammograms in Figure 2a ,b. The calibration curves plot the difference between the peak current obtained in a pK (target) solution and that obtained in buffer alone for pK concentrations varying over seven orders of magnitude. The pKIP-and NIP-coated electrodes began to show an onset of saturation (i.e., a leveling-off of the response) beginning at about 1.0 pg/mL, Figure 2c . Doping with WS2 increases the amplitude of the response but also extends the (log)-linearity and useful sensing range up to at least 1.0 ng/mL. Figure 2d shows the responses of WS2-doped pKimprinted electrodes to other peptides taken from CRP sequences. The response of the electrode to these irrelevant peptides is very similar to the responses obtained with nonimprinted electrodes to pK. This is an important result that we will discuss further, vide infra. Figure S1 , from top to bottom, displays the surface morphologies of WS 2 /NIPs-(left column) and WS 2 /pKIPs-(right column) coated electrodes before and after template removal and upon rebinding with 1.0 pg/mL of pK. The sizes of aggregates of poly(ANco-MSAN) is approximately 50 to 100 nm. Figure S2a ,b plot the electrochemical responses of WS 2 /NIPs-and WS 2 /pKIPs-coated electrodes in buffer, 1.0 pg/mL of peptide K and 1.0 pg/mL of CRP at various scan rates. These were fit using the Randles-Sevcik equation. Interestingly, the gradients of the fitted curves for WS 2 /pKIPs exceed those for WS 2 /NIPs, possibly indicating that the binding of pK or CRP increased the surface area of the electrodes. The larger surface area raises the concern that the higher responses in Figure 2c arise from non-specific binding to a larger surface area. If this were so, irrelevant peptides would also give strong electrochemical signals. However, as Figure 2d shows, irrelevant peptides do not give strong signals with the imprinted electrode, showing that increased surface does not give a larger signal from non-specific binding and that the WS 2 /pKIPs-coated electrodes are selective for the imprinted target. Figure S2c plots the AC impedance measurements of WS 2 -doped pKIPs and NIPs in buffer, peptide K and CRP 1.0 pg/mL solutions. The resistance of pKIPs was almost the same as that of NIPs, but decreased upon the rebinding of pK and CRP. Finally, Figure S2d presents the reusability of the WS 2 /pKIPs-coated electrodes. One of those electrodes was used to measure the relative peak current changes of a 1.0 pg/mL solution of CRP, rinsed, and then reused five times. There was only a small deterioration in the response on the fifth and sixth usage. Finally, the pKIP-coated electrode was integrated into an extended-gate FET as shown in Scheme 1. The drain current was measured as a function of drain voltage (Figure 3a ) for both WS 2 -doped pKIPs and WS 2 -doped NIPs at 1.0 pg/mL CRP concentration and in buffer alone. By repeating the measurement with several different CRP concentrations, a calibration curve of drain current (above buffer only) vs. CRP concentration was constructed, Figure 3b . Interestingly, the electrochemical response (sensitivity) of pK on WS 2 /pKIP-coated electrodes is higher on the FET platform than in the cyclic voltammogram in Figure 3a . The calibration curve (Figure 3b ) on the FET platform was then used to make measurements of the real serum sample. The sensing range is from 1.0 fg/mL to 1.0 ng/mL, which is comparable with the MIPs using PC analogs as functional monomers (e.g., 2-acryl amidoethyldihydrogen phosphate [14] or 4NPPC/polyethylene glycol 400 dimethacrylate [15] , which gave sensing ranges of 0.07-8.50 and 5-120 µg/mL, respectively, using differential pulse voltammetry or circular dichroism). Other imprinted CRP sensor approaches include whole CRP imprinted coupled with gold-platinum bimetallic nanomaterials to enhance the sensor's surface area and catalytic activity. This sensor had a large range (0.1-500 nM or 12 ng/mL-60 µg/mL) but a much higher limit of detection than the sensor in this work [28] . A graphdiyne-based CRP MIPs biosensor performed with a very broad detection range from 10 −5 to 10 3 ng/mL [29] . The WS 2 /pKIP-coated electrode in this work outperforms (in sensitivity) a CRP immunosensor (with sensing range 0.01-1000 ng/mL), which uses antibodies to recognize target molecules [30] . Moreover, our recent study shows that the effect of doping of MIPs with a very small percentage of an MXene (e.g., Ti 2 C at 0.1 wt% in the preparation solution) can give an electrochemical sensing range from 0.1 to 10,000 fg/mL [31] . The doping of WS 2 nanoflakes in this work may further extend the sensing range. Table 1 shows measurements on a real serum sample. A peak current change of 694.2 ± 1.2 µA was found, which converts to a CRP concentration of around 2.28 ± 0.12 µg/mL. The CRP concentration in the serum sample was checked using ELISA, indicating that the pKIP FET measurement had an accuracy of approximately 96%. We constructed a sensitive FET-based sensor for CRP, using peptide epitope imprinting (imprinting a peptide rather than a whole protein). This approach obviates the need to use ligand-mimicking functional monomers in the MIP composition. Flaked tungsten disulfide was used as a dopant in the recognition polymer, which was seen to increase both the response and the useful sensing range. The sensor proved to be sensitive and accurate on real serum when compared to ELISA results. Such economic approaches to biomarker sensing may be cost-effective for future home-care diagnostic systems, which can be integrated with a potentiostat [32] and a microfluidic device [33] or for wearable biosensor devices. We constructed a sensitive FET-based sensor for CRP, using peptide epitope imprinting (imprinting a peptide rather than a whole protein). This approach obviates the need to use ligand-mimicking functional monomers in the MIP composition. Flaked tungsten disulfide was used as a dopant in the recognition polymer, which was seen to increase both the response and the useful sensing range. The sensor proved to be sensitive and accurate on real serum when compared to ELISA results. Such economic approaches to biomarker sensing may be cost-effective for future home-care diagnostic systems, which can be integrated with a potentiostat [32] and a microfluidic device [33] or for wearable biosensor devices. Supplementary Materials: The following are available online at https://www.mdpi.com/article/ 10.3390/bios12010031/s1, Figure S1 : SEM images of 90 nm WS 2 (0.5 wt%) doped (a) NIPs, and (b) peptide K-imprinted poly(AN-co-MSAN)-coated electrodes before template removal (a,b), after template removal (c,d), and after rebinding peptide K (e,f); Figure S2 : The electrochemical response of (a) WS 2 /NIPs and (b) WS 2 /pKIPs-coated electrodes in buffer, 1.0 pg/mL of pK or CRP. The responses were then fit with Randles-Sevcik equation for the solution at 25 • C, ip = 268,600 n 3/2 AD 1/2 Cv 1/2 . (c) AC impedance measurements for WS 2 /NIPs-and WS 2 /pKIPs-coated electrodes in buffer, 1.0 pg/mL of pK or CRP solutions. (d) The reusability of the WS 2 /NIPs and WS 2 /pKIPs-coated electrodes. The electrode was used to measure a 1.0 ng/mL solution of CRP, rinsed and reused for five cycles. The authors confirm that the data supporting the findings of this study are available within the article and its Supplementary Materials. The authors declare no conflict of interest. C-reactive protein and clinical outcomes in patients with COVID-19 Targeting cardiovascular inflammation: Next steps in clinical translation C-reactive protein as an indicator of sepsis Rutgeerts, P. C-reactive protein as a marker for inflammatory bowel disease Protein in the Prediction of Rheumatoid Arthritis in Women What are the Optimal Cutoff Values for ESR and CRP to Diagnose Osteomyelitis in Patients with Diabetes-related Foot Infections? Activation of C-reactive protein proinflammatory phenotype in the blood retinal barrier in vitro: Implications for age-related macular degeneration CRP-induced levels of oxidative stress are higher in brain than aortic endothelial cells Brain tight junction protein expression in sepsis in an autopsy series Handbook of Molecular Imprinting: Advanced Sensor Applications The physiological structure of human C-reactive protein and its complex with phosphocholine C-reactive protein thin-film molecularly imprinted polymers formed using a micro-contact approach C-Reactive protein-directed immobilization of phosphocholine ligands on a solid surface Multiwalled carbon nanotubes embedded molecularly imprinted polymer-modified screen printed carbon electrode for the quantitative analysis of C-reactive protein Point-of-care protein sensing platform based on immuno-like membrane with molecularly-aligned nanocavities The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets Electronics and optoelectronics of two-dimensional transition metal dichalcogenides Controlled growth of high-quality monolayer WS2 layers on sapphire and imaging its grain boundary Recent advances in two-dimensional transition metal dichalcogenides for biological sensing Recent advances on TMDCs for medical diagnosis Doping of transition metal dichalcogenides in molecularly imprinted conductive polymers for the ultrasensitive determination of 17β-estradiol in eel serum Transition metal dichalcogenides to optimize the performance of peptide-imprinted conductive polymers as electrochemical sensors Extended-gate field-effect transistor (EG-FET) with molecularly imprinted polymer (MIP) film for selective inosine determination Epitope imprinting of alpha-synuclein for sensing in Parkinson's brain organoid culture medium Electrochemical sensing of urinary progesterone with molecularly imprinted poly(aniline-co-metanilic acid)s Electrosynthesis of Nanostructured, Imprinted Poly(hydroxymethyl 3,4-ethylenedioxythiophene) for the Ultrasensitive Electrochemical Detection of Urinary Progesterone Electrochemical Based C-Reactive Protein (CRP) Sensing Through Molecularly Imprinted Polymer (MIP) Pore Structure Coupled with Bi-Metallic Tuned Screen-Printed Electrode A graphdiyne-based protein molecularly imprinted biosensor for highly sensitive human C-reactive protein detection in human serum ZnO/porous carbon composite from a mixed-ligand MOF for ultrasensitive electrochemical immunosensing of C-reactive protein Doping of MXenes enhances the electrochemical response of peptideimprinted conductive polymers for the recognition of C-Reactive protein Integrated potentiostat for electrochemical sensing of urinary 3-hydroxyanthranilic acid with molecularly imprinted poly Molecularly imprinted electrochemical sensing of urinary melatonin in a microfluidic system