key: cord-0808169-eowr4ng9 authors: Nightingale, Adrian M.; Hassan, Sammer-ul; Makris, Kyriacos; Bhuiyan, Wahida T.; Harvey, Terry J.; Niu, Xize title: Easily fabricated monolithic fluoropolymer chips for sensitive long-term absorbance measurement in droplet microfluidics date: 2020-08-21 journal: RSC advances DOI: 10.1039/d0ra05330a sha: b80c3f3a2e687e7de91736d135a56012fca236c2 doc_id: 808169 cord_uid: eowr4ng9 Maintaining a hydrophobic channel surface is critical to ensuring long-term stable flow in droplet microfluidics. Monolithic fluoropolymer chips ensure robust and reliable droplet flow as their native fluorous surfaces naturally preferentially wet fluorocarbon oils and do not deteriorate over time. Their fabrication, however, typically requires expensive heated hydraulic presses that make them inaccessible to many laboratories. Here we describe a method for micropatterning and bonding monolithic fluoropolymer flow cells from a commercially available melt-processable fluoropolymer, Dyneon THV 500GZ, that only requires a standard laboratory oven. Using this technique, we demonstrate the formation of complex microstructures, specifically the fabrication of sensitive absorbance flow cells for probing droplets in flow, featuring path lengths up to 10 mm. The native fluorous channel surface means the flow cells can be operated over extended periods, demonstrated by running droplets continuously through a chip for 16 weeks. Droplet ow, in which a liquid phase travels as a succession of discrete self-contained droplets carried by a ow of (typically uorous) oil, has the advantage of removing Taylor dispersion, enhancing mixing, 1 preventing channel clogging, 2 and can be used to isolate individual molecules or cells. 3 A requirement for robust and resilient droplet ow is that channel walls must be consistently preferentially wetted by the continuous (oil) phase. If the droplet phase wets a section of wall the resulting pinning causes cross-contamination between droplets and a decrease in the uniformity of droplet size and composition. 4 For the uorous oils typically used as continuous phase in microuidics, this necessitates uorous channel surfaces. If non-uorous materials are used for chip fabrication (e.g. poly(dimethyl siloxane), poly(methyl methacrylate), glass, cyclic olen copolymer, etc.) additional surface treatments are required to render the channels uorous. This adds an additional process step and yields a surface which can degrade if, for example, using elevated temperatures, 5 or performing experiments over multiple days and weeks. 6, 7 Chips fabricated from uoropolymers which feature native uorous surfaces solve this problem, however fabrication of monolithic chips from common uoropolymers (e.g. PTFE, FEP, PFA) is difficult due to poor suitability for direct machining, and high melting temperatures (e.g. 325 C for PTFE, 315 C for PFA), that mean expensive specialised equipment is required for moulding procedures. 8, 9 Consequently researchers oen opt to assemble uidic manifolds from off-the-shelf uoropolymer capillary tubing 6,7,10 as a more user-friendly option for long-term experimentation. In such systems uidic architectures cannot be arbitrarily designed however, meaning complex structures such as the extended path length ow cells needed for sensitive absorbance measurement are unobtainable. Optical absorption is one of the most extensively used analytical techniques as it is widely applicable, requires simple components, is label-free, is insensitive to matrix effects, and can draw on a large library of established assays. It is challenging to implement in microuidics however, as the sensitivity of the measurement is directly proportional to the optical path length through the uid. The simplest optouidic geometries, where light is transmitted across the microuidic channel, result in path lengths, and hence sensitivities, approximately two orders of magnitude lower than typical benchtop systems which have a standard path length of 10 mm. Consequently, several techniques have been developed to boost microuidic path lengths 11 such as cavity-enhanced optics, [11] [12] [13] liquid waveguiding, 14 and Z-or U-shaped ow cells. [15] [16] [17] These techniques are routinely used in single-phase ow systems and extra considerations must be taken when applying them to droplet ow where lensing at the oil/aqueous interface can divert light away from the detector. Recently Yang et al. 18 successfully measured droplet absorbance in ow and gained a 5.3-fold increase in absorbance path length relative to standard channel width, by squeezing droplets through narrow Zshaped ow cells. By ensuring the ow cell volume was lower than that of the droplets they eliminated liquid-liquid interface lensing, with each droplet transition including a period where the droplet lled the ow cell and the main oil/aqueous interfaces were outside the light path. This system gave a signicant increase in measurement sensitivity, however the use of a chip material which required surface modication means it is not ideally-suited to long-term droplet-based experimentation. 19 Here we describe an easy method for fabricating monolithic uoropolymer chips that offer increased optical path lengths and can be operated for months at a time. This was achieved using a commercially available melt-processable uoropolymer, Dyneon THV 500GZ, and a new, simpler bonding method that obviates the need for expensive heated hydraulic presses previously reported for fabrication of uoropolymer chips. 8, [20] [21] [22] The chips offer optical path lengths of up to 10 mm, the same as a standard benchtop spectrophotometer, and can be operated over multiple months without any degradation of channel surface and successfully maintaining consistent droplet ow. This opens up the possibility of long-term droplet-based experimentation that uses absorbance or indeed other techniques that require bespoke uidic architectures. To form the native-uorous absorption ow cells we microfabricated structures in Dyneon THV 500GZ (3M), a co-polymer made from tetrauoroethylene, hexauoropropylene, and vinylidene uoride monomers. Like all uoropolymers it is solvent resistant and hydrophobic (water contact angle 99 AE 2 ) 20 which is a requirement for stable oil/aqueous segmented ow. It is low cost ($V50 per kg), optically transparent, and crucially its relatively low melting temperature for a uoropolymer (165 C) means it can be easily melt-processed using a standard laboratory oven with no need for the expensive hydraulic presses that feature in previous reports describing monolithic Teon chips. 8, 9, 22 Microstructures were fabricated in Dyneon THV using a replica moulding strategy as illustrated in Fig. 1 . The overall process involved using a microstructured poly(methyl methacrylate) (PMMA) master (Fig. 1a) to cast an intermediate poly(dimethylsiloxane) (PDMS) mould (Fig. 1b) which was then used to form the nal Dyneon THV chip (Fig. 1c) , in a method similar to that previously proposed by Begolo et al. 20 The PMMA master was formed by milling microchannels into a 2 mm sheet of black PMMA (Sheet Plastics, Leicestershire, UK) using a LPKF Protomat S100 micromill (bits from ACS Industries Ltd, UK). Any standard microuidic mould fabrication technique could be used (e.g. stereolithography, 3D printing) but here we chose micromilling as it produces high aspect ratio channels and vertical walls that, with smoothing, are highly suitable for optical applications. 23 Aer milling, the mould was treated with chloroform vapour to re-melt the channel surfaces, remove all tool marks and yield an optically smooth surface (described in more detail in the ESI †). 23, 24 The smoothed PMMA master was then placed in a 3D-printed support (Fig. 1d , Veroclear, Connex Objet500), covered in PDMS (Fig. 1e , Dowsil Sylgard 184, elastomer : curing agent 20 : 1), degassed and cured (65 C, >2 hours). The use of the 3D-printed support here ensured that the resulting PDMS mould had side walls to hold the Dyneon THV pellets during the next stage and determines the nal thickness of the Dyneon THV substrate (3 mm). Aer curing, the PDMS mould was removed and lled with an excess of Dyneon THV pellets. To ensure the nal chip was at (important for later bonding), a $200 g aluminium block was placed on top, with a layer of 0.5 mm thick silicone (Silex Ltd, UK, 40 shore) placed between to allow easy removal aer casting (Fig. 1f ). This assembly was then le overnight in an oven at 190 C (Thermo Scientic Heraeus) during which time the Dyneon THV melted and conformed to the PDMS mould (Fig. 1g) . In contrast to previous reports describing microfabrication using Dyneon THV 20,21 we found that a vacuum oven was not required. Aer cooling, the PDMS mould was peeled from the solid Dyneon THV chip (Fig. 1c ) and then reused. PDMS moulds could typically be used 3-4 times before becoming brittle and tearing. For reproducible bonding in the next stage it is important that the compressive force, generated by the thermal expansion of the Dyneon THV and the tightening of the clamp bolts, is identical from chip-to-chip. Therefore, to ensure a uniform and The micromilled PMMA is placed in a 3D-printed support (d) and filled with liquid PDMS (e). The PDMS is cured and then removed to yield a mould (b). The PDMS mould is filled with Dyneon THV pellets, and a silicone sheet and aluminium weight placed on top (f). The Dyneon THV is melted (g) and, when cooled, removed to yield the final micropatterned substrate (c). reproducible compression from thermal expansion Dyneon THV substrates must be of reproducibly uniform thickness, hence the importance of using the aluminium weight during Dyneon THV casting ( Fig. 1f and g) . Additionally, as later described, the clamp bolts must be lightly tightened using a torque screwdriver so that the same compressive force can be applied each time. The microchannels were sealed using a method previously described for bonding FEP or PFA 8 (see Fig. 2 ). This method is cheaper, simpler, and more widely accessible than the previously reported Dyneon THV bonding methods 20,21 which require the use of expensive heated hydraulic presses. In our method, the microstructured Dyneon THV substrate was brought together with an identically sized blank Dyneon THV sheet (Fig. 2a) . The Dyneon THV parts were clamped between two steel plates using nuts and bolts, with 0.5 mm sheets of silicone (Silex Ltd, UK, 40 shore) placed between the Dyneon THV and steel (Fig. 2b ) so that the chip could be easily removed at the end of the process. The nuts and bolts were lightly tightened to a torque of 0.2 Nm using a torque screwdriver (Q-Torq PRIME 150 FH) so that the Dyneon THV substrates were rmly and reproducibly contacted together but weren't appreciably compressed by the tightening of the bolts. The whole assembly was then placed in a 160 C oven (just below the Dyneon THV's melting temperature of 165 C) and le overnight. During heating the thermal expansion of the Dyneon THV provided the compression required to fuse the two pieces, while the nite expansion meant that the channels were not appreciably deformed, as is observed when using a constant pressure. 8 When the assembly had been recovered from the oven, it was le to cool and then the nished chip extracted (Fig. 2c) . Finally, to allow easy introduction and removal of uid, PTFE tubing was inserted into recesses at each end of the main channel and xed using epoxy glue (Araldite 2012). To ascertain whether the Dyneon THV chips could be used to make long path length (multi-mm) ow cells for absorption measurement of droplets, we rst created a Dyneon THV chip featuring an array of concatenated Z-shaped ow cells with increasing path lengths from 1.7 to 10 mm (Fig. 3a) . In each case light was directed into, and collected from, the ow cell using bre optics (320 mm outer diameter, 250 mm core, Thorlabs) which sat in milled recesses (340 mm square cross section). Fibre optics were inserted into each recess until they abutted the end, with the bre optic tting snugly within the recess. The alignment of the bre optics and the uidic channels are ensured as both the recesses and channels were simultaneously milled on the same master mould. The cross section of the main uidic channel was 250 mm width by 500 mm height in each case, and the 90 turns within each "Z" were fabricated with a Tshape at each end to reduce droplet curvature at the point of light ingress/exit and hence loss of light due to lensing. Each turn of the Z featured exaggerated smoothed corners to ensure each droplet passed smoothly without breaking up. Away from the chip, the bre optics were interfaced with LEDs (Cree CLM4B-GKW-CWBYA693, Farnell Onecall) and light-to-voltage converters (TSL257, Texas Advance Optical Solutions, Farnell Onecall) using bespoke 3D-printed couplers (printed in black poly(lactic acid) on an Ultimaker 3 fused deposition modelling printer, 3D CAD design les included in ESI †). Micropatterned structures were imaged using an Amscope SM-2T trinocular microscope with a Thorlabs DCC1240M USB camera. The z-dimensions of the micropatterned structures were measured by surface prolometry using a Proscan 2200 (Scantron Ltd) with a S12/1400 chromatic sensor (STIL). The sensor has a range of 1400 mm, working distance of 12.2 mm and spot size of 2.6 mm. Scans were performed with measurement steps of 5 mm in both the x-and y-dimensions. Channel cross-sections of completed Dyneon THV chips were imaged by rst cutting open a chip using a single edge razor blade (VWR) and hammer, and then slicing a sliver of the cross section using an fresh razor blade. The resulting cross section sliver was imaged using an Olympus IX81 inverted microscope and QImaging optiMOS camera, and dimensions quantied using pre-calibrated Olympus cellSens soware. Unless otherwise stated, water was ultrapure grade (18.2 MU, Barnstead EASYpure RODI) and all chemicals were obtained from Sigma Aldrich, UK. A modied Griess assay for nitrite and nitrate measurement was formulated as previously described. 10,25 Briey, 1.25 g of vanadium(III) chloride (99.0%, Alfa Aesar, UK) was added to a 250 ml volumetric ask along with 50 ml of ultrapure water to form a dark brown solution. 15 ml of concentrated (37%) hydrochloric acid was added, causing the solution to turn dark turquoise, then 1.25 g of sulfanilamide ($99.0%) and 0.125 g of N-(1-naphthyl)ethylenediamine dihydrochloride (>98%) were added, dissolved, and the solution nally made up to the volumetric mark using ultrapure water. A 100 mM stock solution of sodium nitrite was made by dissolving 1.725 g of sodium nitrite ($99.0%) in ultrapure water in a 250 ml volumetric ask and then diluted as required to make up lower concentrations. Fluorinert FC40 oil was obtained from Acota Ltd, UK. All uids were pumped using peristaltic pumps built inhouse. 25, 26 For initial ow cell testing, droplets were generated in a separate PDMS-based T-junction chip and then owed into the Dyneon THV chip. The droplet generation chip was fabricated using standard replica moulding methods, as previously reported. 25 Droplets were generated using the anti-phase peristaltic pumping method, 26 whereby the oil and aqueous phases are delivered in time-separated alternate pulses, meaning droplet size, composition, and generation frequency is mechanically determined by the design of the pump and is independent of oil/aqueous interfacial tension. Replica moulding relies on all features being faithfully reproduced in each individual moulding stage. To assess the delity of replication, a specic ow cell (highlighted by dashed box in Fig. 3a) was measured in each substrate (PMMA, PDMS, Dyneon THV) in the x-y plane using bright-eld microscopy ( Fig. 3b-d) and in the z-direction using optical prolometry (Fig. 3e and f) . The x-y feature denition for each mould (Fig. 3b and c) and nal Dyneon THV substrate (Fig. 3d ) match closely, with the only visual difference being the inversion of the PDMS mould (Fig. 3c ). Fig. 3e shows the feature heights for the ow cell as measured in the Dyneon THV substrate, with the corresponding PMMA and PDMS measurements shown in ESI Fig S1. † A 2dimensional prole along the central axis of the ow cell (dashed line in Fig. 3e ) encompassing the main channel, bre optic recess and substrate surface, is shown in Fig. 3f along with the equivalent proles for the PMMA and PDMS moulds, with the PDMS prole inverted for easier comparison. The proles match well indicating the topology of the PMMA master was faithfully replicated in both the PDMS mould and the nal Dyneon THV substrate. Aer bonding the features showed minimal deformation as shown, for example, by the cross section of the main uidic channel in Fig. 3g . The potential of the replica moulding technique to replicate much ner features is apparent when imaging substrates cast from an unsmoothed PMMA master, where all the tooling marks (normally removed by solvent smoothing) are visible in the nished Dyneon THV substrate (see ESI Fig. S2 †) . The ability of the ow cells to deliver accurate absorbance measurements was assessed by generating coloured droplets off-chip, and then owing them through the chip. The colour of the droplets was generated by implementing a colourimetric Fig. 4 Optical measurement of droplets passing through the chip shown in Fig. 3(a) . Transmitted light signal measured as three coloured droplets and accompanying oil segments pass through the 1. assay for nitrite. Each droplet contained an equal volume of nitrite standard and Griess reagent, which reacted to form a purple coloured diazonium product with an absorbance maximum at $525 nm. The droplets were generated using our previously-reported anti-phase peristaltic pumping approach, 26 whereby oil and aqueous phases are supplied in time-separated pulses. In this way droplet size is determined solely by the volume supplied in each aqueous pulse and allowed us to easily ensure that droplets could be generated of pre-determined sizes (1.6 ml) that could ll every ow cell. The droplets passed through the chip without breakup and lled each channel (representative image shown in ESI Fig. S3 †) . This is important as an accurate absorbance measurement requires the droplet to completely ll the ow cell at some point during its transition, thus removing potential interference from lensing at the oil/droplet interface. As the droplet ow passed through each ow cell the transmitted light exhibited a characteristic waveform (Fig. 4a-d) with high light transmission when oil lled the ow cells, and lower levels when the coloured droplets lled the ow cell and absorbed a proportion of the light. Increasing path length from 1.7 to 10 mm (Fig. 4a-d) caused greater decreases in light levels in keeping with the Beer-Lambert law: where A is the absorbance, 3 is the molar extinction coefficient, c is the concentration of the absorbing species, and l is the optical path length. The shape of the waveform also changedfrom having long plateaus (periods where a single uid phase exclusively occupies the ow cell) and sharp transitions between these plateaus (Fig. 4a) to shorter plateaus and structured transitions (Fig. 4d) . This is consistent with the increasing ow cell volume causing shorter periods during which each segment (oil or aqueous) can ll the whole ow cell, and longer periods when the oil/aqueous interface travels through the ow cell. The structured, stepwise nature of the transitions in longer ow cells is consistent with the pulsed peristaltic pumping moving the droplets through in discrete steps, and can be correlated to pump rotation speed and pulse timing (data not shown). To demonstrate the increased measurement sensitivity with increasing path length in more detail, we ran different concentrations of nitrite through the system and obtained separate calibration curves for ow cells with path lengths ranging from 1.7 to 10 mm (Fig. 4e) . In each case a linear response was obtained, with the gradient (corresponding to measurement sensitivity) increasing with path length. The sensitivity (gradient) is dened by the Beer-Lambert law as 3l and hence should vary linearly with path length. This was found to be the case (see Fig. 4f ) and the gradient, corresponding to 3, was 13 060 M À1 cm À1 which is consistent with our previous testing using the same assay in short path length ow cells. 10 The increased path lengths demonstrated here increase sensitivity in colourimetric assays and, by maximising signal : noise ratio, lead to increased precision and lower limits of detection. 27 Longer path lengths will also reduce the measurement ceiling, but shorter ow cells can be used in combination with longer ow cells 28, 29 to maximise the measurable range. The use of a uoropolymer as the chip material means that droplets can, in principle, ow through the chip indenitely without fear of droplets pinning to the walls, and causing subsequent cross-contamination and disordered ow. 4 To test this, we fabricated a chip where droplets could be continuously and indenitely generated and owed through a 10 mm This journal is © The Royal Society of Chemistry 2020 RSC Adv., 2020, 10, 30975-30981 | 30979 absorbance cell. The chip (Fig. 5a ) was designed to be representative of a device that might be used for colourimetric assays in droplet ow, hence it not only included an optical ow cell but also a T-junction for droplet generation, serpentine delay channels, and a recess for a thermistor to monitor chip temperature (Fig. 5a) . To increase the residence time in the serpentine delay section, whilst also ensuring the droplets lled the ow cell, the cross section of the uidic channel was larger for the serpentine section than the ow cell: (500  580 mm vs. 300  300 mm width  height, see Fig. 5b ). This meant that as the droplets moved into the ow cell they approximately tripled in length to ensure that the ow cell was completely lled (as shown in Fig. 5c-f , and ESI video SV1 †). As before, the chip was supplied with uid using a peristaltic pump generating droplets every 9 s with volumes of 1.5 ml. Each of the three aqueous inlets was supplied with dyed water to generate droplets that were clearly discernible, and so that any pinned aqueous uid could be visibly identied. On exiting the chip, the droplet ow was collected in a sample tube where the uids gravimetrically separated before being recycled (as illustrated in Fig. 5a ), ensuring the system could be run indenitely without manual intervention. The setup was le running with a computer-controlled microscope periodically taking images (every 15 minutes) and videos of the chip (initially every day, then every week). The system ran continuously for over 16 weeks, at which point the experiment was ended due to laboratory shutdown accompanying the 2020 global coronavirus pandemic. Over time the droplet size decreased by approximately 20% due to compression of the peristaltic pump tubing and hence a reduction in the volume of uid delivered in each pulse (see e.g. Fig. 6a vs. Fig. 6h ), but crucially the droplets continued to ow without wetting the chip wall. This is shown in the representative images taken aer 0, 1, 2, 4, 7, 10, 13 and 16 weeks (Fig. 6 ) and in videos of the ow taken aer 1, 2, 4, 6, 8, 10, 13 and 16 weeks (ESI video SV2 †) where the droplets can be seen to be uniformly sized with no evidence of residual aqueous uid on the channel walls. The absorbance ow cell was still performing well aer the 16 week period, producing a uniform reproducible waveform signal (ESI, Fig. S4 †) consistent with droplets of identical size passing through cleanly and lling the light path during each transition. This shows that the chip can be condently used over multi-month periods without droplet pinning or breakup. Here we have shown a simple method to fabricate 10 mm path length absorbance ow cells, the standard path length used in benchtop spectrophotometers, in monolithic uoropolymer chips. These allow droplets to be measured with high sensitively and can be used over multi-month periods. It should be noted that these structures have not been extensively optimised, so while the droplets used here are relatively large (>1 ml) it will be possible to target smaller volumes by reducing cross section area of the ow cells' uidic channel. The sensitive and robust measurement of droplet absorbance has direct implications on droplet microuidic systems that use or could use absorbance measurement in long-term experimentation, with the increase in sensitivity allowing lower detection limits and increased precision. This, in turn, increases the range of potential applications and analytes for absorbance-based droplet microuidic systems. 7,10 More generally, however, this shows how arbitrary microuidic architectures can be easily implemented in monolithic uoropolymer chips without need for expensive laboratory equipment, and opens up for a range of different analytical methods and functionalities to be robustly addressed with droplet-based methods. There are no conicts to declare. Reactions in Droplets in Microuidic Channels A stable droplet reactor for high temperature nanocrystal synthesis Droplet microuidic technology for single-cell high-throughput screening Droplet connement and leakage: causes, underlying effects, and amelioration strategies High-Temperature Microuidic Synthesis of CdSe Nanocrystals in Nanoliter Droplets Whole Teon valves for handling droplets Lifetime of Phosphorescence from Nanoparticles Yields Accurate Measurement of Concentration of Oxygen in Microdroplets, Allowing One To Monitor the Metabolism of Bacteria Whole-Teon microuidic chips An automated Teon microuidic peptide synthesizer A Droplet Microuidic-Based Sensor for Simultaneous in situ Monitoring of Nitrate and Nitrite in Natural Waters Cavity-enhanced optical methods for online microuidic analysis On-chip cavity-enhanced absorption spectroscopy using a white light-emitting diode and polymer mirrors Optouidic marine phosphate detection with enhanced absorption using a Fabry-Pérot resonator Long pathlength absorbance spectroscopy: trace analysis of Fe Performance of an in-plane detection cell with integrated waveguides for UV/vis absorbance measurements on microuidic separation devices Microuidic colourimetric chemical analysis system: application to nitrite detection Inlaid microuidic optics: absorbance cells in clear devices applied to nitrite and phosphate detection A High-Sensitivity, Integrated Absorbance and Fluorescence Detection Scheme for Probing Picoliter-Volume Droplets in Segmented Flows Droplet microuidics for microbiology: techniques, applications and challenges New family of uorinated polymer chips for droplet and organic solvent microuidics Aqueous and Nonaqueous Electrochemical Sensing on Whole-Teon Chip Reduction of surface roughness for optical quality microuidic devices in PMMA and COC Droplet Interfaced Parallel and Quantitative Microuidic-Based Separations Nitrate measurement in droplet ow: gas-mediated crosstalk and correction Phased peristaltic micropumping for continuous sampling and hardcoded droplet generation Detection limits of chemical sensors: applications and misapplications Lab-on-Chip Measurement of Nitrate and Nitrite for In Situ Analysis of Natural Waters A Labon-Chip Analyzer for in situ Measurement of Soluble Reactive Phosphate: Improved Phosphate Blue Assay and Application to Fluvial Monitoring