key: cord-0804862-hcxv5gdl
authors: Molan, Katja; Rahmani, Ramin; Krklec, Daniel; Brojan, Miha; Stopar, David
title: Phi 6 Bacteriophage Inactivation by Metal Salts, Metal Powders, and Metal Surfaces
date: 2022-01-21
journal: Viruses
DOI: 10.3390/v14020204
sha: 0fbcc2c64920a3bdeec109854529435c37950447
doc_id: 804862
cord_uid: hcxv5gdl

The interaction of phages with abiotic environmental surfaces is usually an understudied field of phage ecology. In this study, we investigated the virucidal potential of different metal salts, metal and ceramic powders doped with Ag and Cu ions, and newly fabricated ceramic and metal surfaces against Phi6 bacteriophage. The new materials were fabricated by spark plasma sintering (SPS) and/or selective laser melting (SLM) techniques and had different surface free energies and infiltration features. We show that inactivation of Phi6 in solutions with Ag and Cu ions can be as effective as inactivation by pH, temperature, or UV. Adding powder to Ag and Cu ion solutions decreased their virucidal effect. The newly fabricated ceramic and metal surfaces showed very good virucidal activity. In particular, 45%TiO(2) + 5%Ag + 45%ZrO(2) + 5%Cu, in addition to virus adhesion, showed virucidal and infiltration properties. The results indicate that more than 99.99% of viruses deposited on the new ceramic surface were inactivated or irreversibly attached to it.

Viruses can spread and contaminate surfaces by aerosols and droplets. The lack of effective virucidal strategies can often be due to a poor understanding of virus stability on different surfaces. In this work, we used the model Phi6 bacteriophage and checked its infectivity in contact with metal ions, metal and ceramic powders, as well as on different engineered surfaces. Phi6 virus has been extensively used as a surrogate for the study of enveloped RNA animal viruses [1] [2] [3] [4] [5] , including SARS coronaviruses [6, 7] . Similar to SARS-CoV-2, it is enveloped by a lipid membrane, has spike proteins, and is of similar size (80-100 nm) [8] [9] [10] [11] [12] .

Phi 6 stability to environmental factors in suspension, such as temperature, pH, RH, and light, has been determined [2, 7, [11] [12] [13] [14] [15] [16] [17] [18] . Much less, however, is known about phage stability in the presence of metal ions, metal powders, and ceramic or metal surfaces. For example, the virucidal effect of copper ions has been described against Phi6 as well as against influenza virus, norovirus, monkeypox, vaccinia virus, human immunodeficiency virus (HIV), SARS-CoV, and SARS-CoV-2 [19] [20] [21] [22] [23] [24] [25] [26] [27] [28] . Silver nanoparticles, on the other hand, have been shown to inhibit herpes simplex virus, human parainfluenza virus type 3, vaccinia virus, respiratory syncytial virus, Tacaribe virus, and hepatitis B virus [29] [30] [31] [32] [33] . Surprisingly, the mechanisms of action are still not well understood [34] . It has been shown that by binding to the surface of HIV-1 glycoproteins, silver nanoparticles destroy disulfide bonds [35] . Such destruction of viral surface glycoproteins has also been suggested for virucidal activity against influenza virus [36, 37] . There is one study of the silver

All virucidal experiments were performed with an overnight culture of Pseudomonas sp. (DSM 21482) and bacteriophage Phi6 obtained from Leibnitz-Institut (DSMZ-Deutsche Sammlung von Mikroorganismen und Zellkulturen GmbH, Braunschweig, Germany). Bacteria were cultured in Tryptic Soy Broth (TSB) medium at 28 • C and 180 rpm, overnight. For phage enrichment, 1% of the overnight bacterial culture was added to fresh TSB medium and grown to the exponential phase. Next, 1 mL of exponential-phase bacteria and 300 µL of Phi6 phage suspension were added to 30 mL of SM buffer, followed by incubation overnight at 50 rpm and 28 • C as described previously [50] . The enriched phage suspensions were centrifuged (13,000 rpm, 4 • C, 10 min), and the supernatant filtered through a 0.22 µm filter. To obtain a stock viral suspension with a titer of 10 10 -10 11 , the phage suspension was centrifuged at 100,000× g for 2 h at 4 • C. The phage stock was stored at 4 • C in SM buffer (7.5 pH) until further use. The virucidal effect was determined in terms of Plaque-Forming Units (PFU) before and after exposure of the virus particles for 15 min to different conditions/solutions/suspensions/material surfaces using the double-layer agar Viruses 2022, 14, 204 3 of 12 overlay plaque method [51] . Viral titer was calculated as [(PFU/volume of phage)*phage dilution]. All experiments were performed independently at least three times.

To determine viral titer after exposure of Phi6 to different physicochemical factors, phage suspensions were diluted in Phosphate-Buffered Saline (PBS, 7.4 pH), and viral titer was determined by the double-layer agar method [51] . To test the effect of temperature, 10 µL of phage suspension was added to 490 µL of PBS buffer in a microcentrifuge tube, mixed, and incubated for 15 min at different temperatures in a PCR cycler (Biometra Tone Series, Analytik Jena GmbH, Jena, Germany). To test the effect of pH, solutions with a pH ranging from 2 to 12.5 were prepared. To 490 µL of a solution with known pH, 10 µL of phage suspension was added, and the suspension was incubated for 15 min at room temperature without mixing under light conditions. The effects of relative humidity (RH) values were studied in a constant climatic chamber (Memmert, Schwabach, Germany) at 4 different temperatures (10, 19, 28 , and 33 • C) and 2 RH values (10% and 80%). In this experiment, 10 µL of the phage suspension was added to a microtiter plate and incubated for 24 h at given RH and temperature. Next, 100 µL of PBS solution was added to the wells and mixed with a pipette, and the suspension was transferred to a microcentrifuge tube containing 400 µL of PBS buffer to test for viral titer. To test the effects of ultrasound on phage stability, microcentrifuge tubes containing 490 µL of PBS and 10 µL of phage suspension were placed on ice for 10 min and then sonicated with a sonotrode pulse (3 mm probe at 12 microns of amplitude, 150 Watt Ultrasonic Disintegrator Mk2, MSE Scientific Instruments, Heathfield, UK) from 30 to 100 s. The effect of UV radiation was tested in an Ultraviolet Crosslinker chamber (Analytik Jena GmbH, Jena, Germany) in a 12-well titer plate containing 490 µL of PBS and 10 µL of phage suspension. Each column (3 wells) of the titer plate was irradiated with a different amount of energy, from 100 mJ/cm 2 to 1000 mJ/cm 2 .

Stock solutions of silver nitrate, iron sulphate, aluminum sulphate, copper sulphate, and nickel chloride (II) were prepared as 0.5 M solutions in Milli-Q water (5.5 pH). Metal salt concentrations in the range from 0.1 M to 0.001 M were prepared in MQ water. To 10 µL of the stock phage suspension, 490 µL of the solution with the tested metal ion concentration was added, and the mixture was incubated for 15 min at room temperature (without mixing, under light conditions). The virus titer was determined based on PFU using the double-layer agar method.

TiO 2 -ZrO 2 -Ag-Cu, TiO 2 -Ag-Cu, and Co28Cr6Mo powders were prepared as 0.5 M stock suspensions of the respective dopant metal ions in MQ water (5.5 pH). We prepared powder suspensions ranging from 0.001 to 0.25 M by diluting with Milli-Q water. To ensure better solubility, the powder suspensions were sonicated and vortexed before use. To 10 µL of the stock phage suspension, 490 µL of the tested metal and ceramic powder suspension was added, and the mixture was incubated for 15 min at room temperature (without mixing, under light conditions). To determine the virus titer, the solutions containing the phages were serially diluted, and the number of PFU was determined using the double-layer agar method.

The disks were prepared by spark plasma sintering (SPS, FCT Systeme GmbH, Effelder-Rauenstein, Germany) in vacuum chamber with a nitrogen flow. SPS is the most popular, advanced, and rapid sintering process in powder metallurgy (PM), which for metal alloys, metal matrix composites, and ceramics guarantees the highest consolidation and densification percentage. During SPS, a low-voltage pulsed electric current is imposed on the electrodes. Electrical discharges pass through the material powders which are enclosed inside a graphite mold. The combination of samples, pressure, sintering time, and temperature has a pivotal role in PM procedures. In our experiments approximately 15 g of each mixture was plasma-sintered for 20 min at a 50 MPa pressure. Temperature was 800 • C for TiO 2 + 10%Ag + 10%Cu, 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu ceramic disks, and 1000 • C for pre-alloyed gas-atomized Co28Cr6Mo metallic discs.

The protocol to test the virucidal effect on disk surfaces is schematically depicted in Figure 1 . Five droplets containing 10 µL of phage stock solution were placed on the disk surface and incubated for 15 min at room temperature (non-mixing, light conditions), after which the liquid was removed, and virus titer determined. After one min, the surface was swabbed with a cotton swab soaked in 100 µL PBS buffer and additionally with a dry cotton swab to collect the viruses on the surface completely. Both the moist and the dry swab were placed in a microcentrifuge tube containing 400 µL PBS and vigorously vortexed for 10 s to detach the virus particles from the swabs. Next, 100 µL of undiluted or 500 µL of diluted PBS virus suspensions were used to infect bacterial cells and to determine viral titers. To determine the residual viruses left on the swabs after detachment, both cotton swabs were placed on TSA agar plates and doused with soft agar containing an inoculum of bacteria. The TSA plates with cotton swabs were photographed and visually compared. Although swabbing removed most of the virus from the disk surface, strongly attached viruses could remain on the surface. To determine strongly attached infective viruses, the disks were sonicated in 1-5 mL of PBS buffer for 5 min in a sonication bath (ASonic Ultrasonic Cleaner, degas mode, water temperature 22 • C). In the next step, 500 µL of PBS solution with detached virus particles was used for viral titer determination. We checked independently the effect of the sonication bath on virus infectivity and determined that the applied sonication did not decrease the virus titer (see Table S1 ). The viral titers obtained after selective virus detachment form the surface were compared to those of the reference materials (TiO 2 anatase, steel 316 L).

The disks were prepared by spark plasma sintering (SPS, FCT Systeme GmbH, Effelder-Rauenstein, Germany) in vacuum chamber with a nitrogen flow. SPS is the most popular, advanced, and rapid sintering process in powder metallurgy (PM), which for metal alloys, metal matrix composites, and ceramics guarantees the highest consolidation and densification percentage. During SPS, a low-voltage pulsed electric current is imposed on the electrodes. Electrical discharges pass through the material powders which are enclosed inside a graphite mold. The combination of samples, pressure, sintering time, and temperature has a pivotal role in PM procedures. In our experiments approximately 15 g of each mixture was plasma-sintered for 20 min at a 50 MPa pressure. Temperature was 800 °C for TiO2 + 10%Ag + 10%Cu, 45%TiO2 + 5%Ag + 45%ZrO2 + 5%Cu ceramic disks, and 1000 °C for pre-alloyed gas-atomized Co28Cr6Mo metallic discs.

The protocol to test the virucidal effect on disk surfaces is schematically depicted in Figure 1 . Five droplets containing 10 µL of phage stock solution were placed on the disk surface and incubated for 15 min at room temperature (non-mixing, light conditions), after which the liquid was removed, and virus titer determined. After one min, the surface was swabbed with a cotton swab soaked in 100 µL PBS buffer and additionally with a dry cotton swab to collect the viruses on the surface completely. Both the moist and the dry swab were placed in a microcentrifuge tube containing 400 µL PBS and vigorously vortexed for 10 s to detach the virus particles from the swabs. Next, 100 µL of undiluted or 500 µL of diluted PBS virus suspensions were used to infect bacterial cells and to determine viral titers. To determine the residual viruses left on the swabs after detachment, both cotton swabs were placed on TSA agar plates and doused with soft agar containing an inoculum of bacteria. The TSA plates with cotton swabs were photographed and visually compared. Although swabbing removed most of the virus from the disk surface, strongly attached viruses could remain on the surface. To determine strongly attached infective viruses, the disks were sonicated in 1-5 mL of PBS buffer for 5 min in a sonication bath (ASonic Ultrasonic Cleaner, degas mode, water temperature 22 °C). In the next step, 500 µl of PBS solution with detached virus particles was used for viral titer determination. We checked independently the effect of the sonication bath on virus infectivity and determined that the applied sonication did not decrease the virus titer (see Table S1 ). The viral titers obtained after selective virus detachment form the surface were compared to those of the reference materials (TiO2 anatase, steel 316L). 

Contact angle measurements were performed using a mobile surface analyzer MSA (Krüss GmbH, Hamburg, Germany) equipped with a double-pressure dosing unit for hydrophobicity determination of the surface. Measurements were performed with 2 µL drops and 1 s of equilibration time under constant conditions. Deionized water and diiodomethane (CH2I2) served as test liquids with different polarities to calculate surface [52] [53] [54] . Surface free energy (SFE) as well as polar and dispersive components were calculated using Krüss Advance software v. 1.9.2.

Differences among disks surfaces were analyzed with ANOVA test. A p-value less than 0.05 was considered statistically significant. Statistical analysis was performed using SPSS version 28. Calculations and ANOVA tables are presented in Supplementary Materials (Tables S2 and S3 ).

In all experiments, we arbitrarily used a 4 logs reduction of virus titer as a measuring stick for efficient inactivation of virus [55, 56] . This implied 99.99% inactivation of the viruses.

The viability of Phi6 after treatment with various metal salt solutions at different concentrations is shown in Figure 2 . Inactivation corresponding to 99.99% was reached with 1 mM silver nitrate and ferrous sulphate, 10 mM aluminum sulphate, and 20 mM copper sulphate (Figure 2A-D) . Potassium dichromate and nickel sulphate had lower inactivation efficiencies; at the highest concentration tested (0.1 M), the virus titer decreased by approximately 3 or 1 log, respectively ( Figure 2E ,F). Since metal salt solutions are known to undergo hydrolysis, we measured the pH of the resulting solutions. In the case of iron and aluminum sulphate, a significant decrease in pH was measured with an increasing salt concentration. In these solutions, the pH decreased below pH 4, which could lead to a drastic inactivation of the virus ( Figure S1B ). In other metal ion solutions, the decrease of pH was less pronounced, or the solution pH did not change (i.e., silver nitrate). Compared to other physicochemical factors such as temperature, pH, relative humidity (RH), sonication, and UV radiation (Supplementary Material Figure S1A -E), metal salts of Ag, Cu, Fe, and Al could reach similar virus deactivation rates.

The virucidal effects of metal and ceramic powder suspensions are shown in Figure 3 . Treatment with the TiO 2 -ZrO 2 -Ag-Cu powder suspension had the strongest effect on Phi6 viral titer. Within the experimental error, 99.99% inactivation of the virus was achieved at a metal dopant concentration of 10 mM Ag and Cu ions ( Figure 3A ). The decrease of virus titer correlated with a decrease in pH. To obtain 4 logs decrease for the TiO 2 -Ag-Cu powder, a 25 mM concentration of Ag in Cu ions was needed ( Figure 3B ). At higher metal ions concentration, the number of infective virus particles decreased, although the pH remained unchanged. The metallic Co28Cr6Mo powder suspension ( Figure 3C ) had no significant effect on viral inactivation.

The inactivation of viruses on ceramic and metal composite disk surfaces was determined selectively. The inactivation of viruses suspended in a drop of liquid on disk surfaces is presented in Figure 4A , the inactivation of weakly attached viruses in contact with the disk surfaces in Figure 4B , and the inactivation of strongly attached viruses in Figure 4C . Viruses suspended in a drop of liquid in contact with the control steel disks had comparable viral titers to those of the control. However, there was significant virus inactivation in the drop of liquid in contact with TiO 2 anatase disks. A more pronounced virus inactivation was observed in droplets collected from TiO 2 + 10%Ag + 10%Cu disks (1.5 log decrease, p < 0.001), whereas a dramatic decrease of liquid volume was observed on 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu ceramic disk and Co28Cr6Mo metal disks. The two disks adsorbed all the added virus suspensions during the 15 min incubation (Video S1), 

The virucidal effects of metal and ceramic powder suspensions are shown in Figure  3 . Treatment with the TiO2-ZrO2-Ag-Cu powder suspension had the strongest effect on Phi6 viral titer. Within the experimental error, 99.99% inactivation of the virus was achieved at a metal dopant concentration of 10 mM Ag and Cu ions ( Figure 3A ). The decrease of virus titer correlated with a decrease in pH. To obtain 4 logs decrease for the TiO2-Ag-Cu powder, a 25 mM concentration of Ag in Cu ions was needed ( Figure 3B ). At higher metal ions concentration, the number of infective virus particles decreased, although the pH remained unchanged. The metallic Co28Cr6Mo powder suspension ( Figure 3C ) had no significant effect on viral inactivation. 

The virucidal effects of metal and ceramic powder suspensions are shown in Figure  3 . Treatment with the TiO2-ZrO2-Ag-Cu powder suspension had the strongest effect on Phi6 viral titer. Within the experimental error, 99.99% inactivation of the virus was achieved at a metal dopant concentration of 10 mM Ag and Cu ions ( Figure 3A ). The decrease of virus titer correlated with a decrease in pH. To obtain 4 logs decrease for the TiO2-Ag-Cu powder, a 25 mM concentration of Ag in Cu ions was needed ( Figure 3B ). At higher metal ions concentration, the number of infective virus particles decreased, although the pH remained unchanged. The metallic Co28Cr6Mo powder suspension ( Figure 3C ) had no significant effect on viral inactivation. To obtain the number of strongly attached viruses, the disks were put in a sonication bath after swabbing. The recovery of strongly attached viruses that were infective is shown in Figure 4C . From the control steel and TiO2 disks, we recovered 5.0 × 10 4 strongly attached infective viruses. Only a few strongly attached infective viruses were recovered from TiO2 + 10%Ag + 10%Cu and 45%TiO2 + 5%Ag + 45%ZrO2 + 5%Cu disks. The highest viral recovery was obtained from Co28Cr6Mo disks (4.3 × 10 5 ).

Surface free energy (SFE) can have a major effect on virus adhesion [57] . The SFE of different surfaces varied between 33.19 (± 1.38) mJ/m 2 and 55.20 (± 2.76) mJ/m 2 ( Table 1 ). The highest SFE was measured on the surface of porous Co28Cr6Mo, which also had the highest polar component. On all disks, the disperse component was the dominant component of SFE. Virus contact inhibition by different surfaces was tested by allowing viruses to adhere to the disk surfaces for 15 min after the liquid was removed. The weakly attached viruses were detached by swabbing the surfaces with wet and dry swabs. This simulated touching the surface with moist and dry fingers and possible virus transmission from the surface. The numbers of infective viruses recovered per control steel disk were in the order of 10 7 PFU/disk. Slightly lower numbers of infective viruses were determined on TiO 2 anatase ceramic surfaces. On the other hand, viral titers obtained from swabbing TiO 2 + 10%Ag + 10%Cu, 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu, and Co28Cr6Mo surfaces were significantly lower compared to those from control TiO 2 or steel disks (p < 0.001) ( Figure 4B) .

Although the majority of the swabbed viruses were detached from the cotton swabs and resuspended into PBS solution, some viruses remained attached to the swabs. This would lead to underestimation of the number of weakly attached viruses to a disk surface. To test this, we put swabs after resuspension in PBS on agar plates ( Figure 4D ). As expected, a substantial number of residual viruses remained attached to the swabs. The highest numbers of residual viruses were detected on swabs from steel and TiO 2 composite ceramic disk surfaces. On swabs collected from TiO 2 + 10%Ag + 10%Cu, 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu, and Co28Cr6Mo disks, considerably less residual infectious viruses were present (seen as individual plaques). To obtain the number of strongly attached viruses, the disks were put in a sonication bath after swabbing. The recovery of strongly attached viruses that were infective is shown in Figure 4C . From the control steel and TiO 2 disks, we recovered 5.0 × 10 4 strongly attached infective viruses. Only a few strongly attached infective viruses were recovered from TiO 2 + 10%Ag + 10%Cu and 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu disks. The highest viral recovery was obtained from Co28Cr6Mo disks (4.3 × 10 5 ).

Surface free energy (SFE) can have a major effect on virus adhesion [57] . The SFE of different surfaces varied between 33.19 (± 1.38) mJ/m 2 and 55.20 (± 2.76) mJ/m 2 ( Table 1 ). The highest SFE was measured on the surface of porous Co28Cr6Mo, which also had the highest polar component. On all disks, the disperse component was the dominant component of SFE. 

The interactions of phage particles with abiotic surfaces are usually understudied in the field of phage ecology. In this work, we examined the resistance of phage Phi6 to various physicochemical parameters, metal salts, ceramic powders, as well as composite ceramic and metal surfaces fabricated by spark plasma sintering (SPS) and/or selective laser melting (SLM) technology. The results showed that phage infectivity can be quickly decreased (during 15 min) by more than 4 logarithms in contact with various metal ions; this is generally considered a very good virucidal activity [55, 56] . More importantly, phage infectivity could decrease significantly on ceramic and metal surfaces doped with metals, which can provide new materials to control viruses.

The results imply that water solutions of Ag, Cu, Fe, Al, and Cr ions have a virucidal effect on Phi6. The loss of Phi6 infectivity associated with iron and aluminum sulphates is likely the consequence of a low pH due to metal ion hydrolysis [58] . For example, at a 10 mM concentration of iron and aluminum sulphates, the pH was below 4, with a significant detrimental effect on phage infectivity. On the other hand, the virucidal effect of Cu and Ag ions is well known [19] [20] [21] [22] 29, 30, 33] . It is interesting to note that the virucidal effect of silver nitrate was obtained without a significant pH drop. On the other hand, the virucidal effect of copper sulphate likely derived from a combination of Cu ions toxicity and low pH values. A concentration of 20 mM copper sulphate was required to achieve a 99.99% loss of Phi6 infectivity. This was higher than reported by Li et al. [21] , who showed that 5 mM copper sulphate reduced Phi6 virus titer by 4 logs, albeit after 180 min of incubation. When powder suspensions of TiO 2 + 10%Ag + 10%Cu were tested for virucidal activity, the activity was lower compared to that of pure ion solutions, suggesting lower ion activities in powder suspension compared to solutions. Still, the powder suspensions were able to reduce viral titers for more than 4 logs. In powder suspensions where TiO 2 was partially replaced with ZrO 2 , the virucidal activity was lower than in the TiO 2 + 10%Ag + 10%Cu suspension. On the other hand, in the Co28Cr6Mo powder suspension, there was no significant virucidal activity, suggesting that Co, Cr, and Mo ions have low virucidal activity. Consistently, we obtained appreciable Cr virucidal activity only at high ion concentrations (>100 mM).

In this work, new virucidal composite ceramic and metal materials were fabricated by selective laser melting and spark plasma sintering technology. Most notably, 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu and Co28Cr6Mo disks have porous features that allow the infiltration of the added virus particles. The infiltration on Co28Cr6Mo was completed in less than 5 s. The polar component of surface free energy of Co28Cr6Mo was very high, which may explain the ease with which water infiltrates the disk. Co28Cr6Mo is a prealloyed spherical-shaped powder, which is suitable for both SPS and SLM processes [59] . Its excellent biocompatibility and heat and oxidation resistance make it a great candidate for medical industry. The results of this study suggest that this material also has excellent virus infiltration and adsorption properties. The viruses strongly adhered to the interior of the material but could be removed with sonication. It is expected that sonication released viruses from the pore space. When PFU of viruses attached to the internal and external surfaces of Co28Cr6Mo disk were added together, the total number of PFU was still significantly lower than that in control steel disks, suggesting virucidal activity. On the other hand, the infiltration of a drop of viruses in 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu disk must have a different origin. The dispersive contribution to surface free energy was much higher. It is interesting to note that in TiO 2 -based ceramics, there was no infiltration. This suggest that the addition of bioinert ZrO 2 ceramic increased the porosity of TiO 2 -ZrO 2 composite ceramics. The mechanical properties of TiO 2 -ZrO 2 mixtures are influenced by the amount of TiO 2 and the sintering temperature, due to the lower melting point and density of TiO 2 compared to ZrO 2 [60] . However, compared to anatase TiO 2 , the ZrO 2 nanoparticles have more photocatalytic degradation capability, and the TiO 2 -ZrO 2 ceramic composite has improved phase stability [61] .

The newly fabricated 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu ceramic material showed combined virus adhesion, virucidal, and infiltration capability. The number of infective virus particles in this ceramic was significantly lower compared to that in the reference TiO 2 ceramic, which does not have inherent virucidal properties, although viruses can adhere to a TiO 2 surface ( Figure 4B ,C) [62] [63] [64] . If one assumes that the same number of viruses in a drop of virus suspension sedimented to the disk surface, irrespective of the surface chemistry, then the decreased number of infective viruses on fabricated surfaces indicates a virucidal contact effect of the new material. The virucidal effect is attributed to Ag and Cu doped ions. When 10 8 PFU were added to the 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu disk surface, most viruses infiltrated the disk. Approximately 10 4 virus PFU remained weakly attached to the external surface and could be swabbed, whereas 10 2 PFU were strongly attached. This suggests that 99.99% of viruses that were added to the surface were either irreversibly attached to the surface or inactivated, therefore possessing no threat to potential host cells.

Phage attachment to different surfaces and their inactivation can have a dramatic effect on virus reproduction success. Bacteriophages modify microbial communities by lysing hosts, transferring genetic material, and effecting lysogenic conversion. All this can be severely compromised when phage numbers decrease due to virucidal effectors in the environment or irreversible attachment to a surface. In addition, when phages are infiltrated in a material, they may fail to find host cells. For example, in a porous soil environment, up to 30% of volume available for viruses can be inaccessible for bacteria in the presence of a pore diameter less than 1 µm [65] . Similarly, attached viruses will be inaccessible for bacteria. Nevertheless, infiltrated or attached phages may retain their viability. In contrast, when phages are in contact with virucidal surfaces such as Cu-and Ag-doped ceramic surfaces, their infectivity can be drastically reduced.

Understanding phage stability in the environment is important as it determines phage ecology and phage reproductive success. Irreversibly attached phages, inactivated phages, or phages that enter pore spaces smaller than the size of bacterial hosts can no longer infect their bacterial host cells. We showed that inactivation of Phi6 in solutions with Ag and Cu ions can be as effective as inactivation by other environmental factors, such as pH, temperature, or UV. Adding Ag and Cu to powder suspensions decreases their virucidal effect. The new fabricated metal and ceramic surfaces with doped Ag and Cu ions allow very good virus infiltration and have virucidal activity, in particular 45%TiO 2 + 5%Ag + 45%ZrO 2 + 5%Cu, which in addition to promote irreversible virus adhesion, also has virucidal activity and favors virus infiltration.

Supplementary Materials: The following supporting information can be downloaded at: https: //www.mdpi.com/article/10.3390/v14020204/s1, Figure S1 : Effects of physicochemical factors on Phi6 inactivation; Table S1 : Phi6 viral titer before and after treatment in a ultrasonic bath; Table S2 : ANOVA for "Viruses in suspension"; Table S3 : ANOVA for "Weakly and strongly attached viruses". Video S1: Disk surface porosity. 

Physico-chemical characteristics of evaporating respiratory fluid droplets

Survival of the enveloped virus Phi6 in droplets as a function of relative humidity, absolute humidity, and temperature

Comparison of five bacteriophages as models for viral aerosol studies

Evaluation of Phi6 persistence and suitability as an enveloped virus surrogate

The use of bacteriophages of the family Cystoviridae as surrogates for H5N1 highly pathogenic avian influenza viruses in persistence and inactivation studies

Persistence of Bacteriophage Phi 6 on Porous and Nonporous Surfaces and the Potential for Its Use as an Ebola Virus or Coronavirus Surrogate

Survival of the enveloped bacteriophage Phi6 (a surrogate for SARS-CoV-2) in evaporated saliva microdroplets deposited on glass surfaces

Bacteriophage phi6: A Lipid-Containing Virus of Pseudomonas phaseolicola

Membrane fusion in prokaryotes: Bacteriophage phi 6 membrane fuses with the Pseudomonas syringae outer membrane

Bacteriophage phi 6 envelope elucidated by chemical cross-linking, immunodetection, and cryoelectron microscopy

Structural studies of the enveloped dsRNA bacteriophage phi 6 of Pseudomonas syringae by Raman spectroscopy. I. The virion and its membrane envelope

The origin of phospholipids of the enveloped bacteriophage phi6

Virion Structure and Composition

Comparative properties of bacteriophage phi6 and phi6 nucleocapsid

Survival of MS2 and Φ6 viruses in droplets as a function of relative humidity, pH, and salt, protein, and surfactant concentrations

Humid Air Decontamination of Aircraft Confirmed That High Temperature and High Humidity Are Critical for Inactivation of Infectious

Inactivation of Coronaviruses and Phage Phi6 from Irradiation across UVC Wavelengths

Blue light inactivation of the enveloped RNA virus Phi6

Mechanism of inactivation of bacteriophages by metals

Virus inactivation by copper or iron ions alone or in the presence of peroxide

Differential bacteriophage mortality on exposure to copper

The use of copper to help prevent transmission of SARS-coronavirus and influenza viruses. A general review

Metallic copper as an antimicrobial surface

Inactivation of norovirus on dry copper alloy surfaces

Can Copper Products and Surfaces Reduce the Spread of Infectious Microorganisms and Hospital-Acquired Infections? Materials

Novel antiviral characteristics of nanosized copper(I) iodide particles showing inactivation activity against 2009 pandemic H1N1 influenza virus

Aerosol and Surface Stability of SARS-CoV-2 as Compared with SARS-CoV-1

The chemotherapeutic activity of compounds of copper, rhodium and certain other metals in mice infected with neurovaccinia and ectromelia viruses

Antiviral activity of mycosynthesized silver nanoparticles against herpes simplex virus and human parainfluenza virus type 3

Silver nanoparticles inhibit vaccinia virus infection by preventing viral entry through a macropinocytosisdependent mechanism

Antiviral and Immunomodulatory Activity of Silver Nanoparticles in Experimental RSV Infection

Interaction of silver nanoparticles with Tacaribe virus

Silver nanoparticles inhibit hepatitis B virus replication

Inactivation of RNA and DNA viruses in water by copper and silver ions and their synergistic effect

Mode of antiviral action of silver nanoparticles against HIV-1

Comparison of the antiviral effect of solid-state copper and silver compounds

The Infectious Bronchitis Coronavirus Pneumonia Model Presenting a Novel Insight for the SARS-CoV-2 Dissemination Route

Hardness of multilayered ceramics. Ceram.-Matrix Compos

Indentation brittleness of ceramics: A fresh approach

Lightweight 3D printed Ti6Al4V-AlSi10Mg hybrid composite for impact resistance and armor piercing shielding

Perspectives of metal-diamond composites additive manufacturing using SLM-SPS and other techniques for increased wear-impact resistance

Silver Nanoparticles: Synthesis, Characterization, Properties, Applications, and Therapeutic Approaches

Comparison of mechanical and antibacterial properties of TiO 2 /Ag ceramics and Ti6Al4V-TiO 2 /Ag composite materials using combining SLM-SPS techniques

The survival and inactivation of enteric viruses on soft surfaces: A systematic review of the literature

Sanitizing agents for virus inactivation and disinfection

SARS-CoV-2 (COVID-19) inactivation capability of copper-coated touch surface fabricated by cold-spray technology

Metal nanoparticles: The protective nanoshield against virus infection

Silver nanoparticles are broad-spectrum bactericidal and virucidal compounds

Efficiency of Phage ϕ6 for Biocontrol of Pseudomonas syringae pv

Dispersion-Polar Surface Tension Properties of Organic Solids

Estimation of the Surface Free Energy of Polymers

Einige Aspekte der Benetzungstheorie und ihre Anwendung auf die Untersuchung und Veränderung der Oberflächene genschaften von Polymeren

Evaluation of the virucidal efficacy of disinfectant wipes with a test method simulating practical conditions

Guideline for testing chemical disinfectants regarding their virucidal activity within the field of human medicine

Virus adhesion to archetypal fomites: A study with human adenovirus and human respiratory syncytial virus

Aqueous Chemistry of Metal Cations: Hydrolysis, Condensation and Complexation

The impact resistance of highly densified metal alloys manufactured from gasatomized pre-alloyed powders

Sintered ZrO 2 -TiO 2 ceramic composite and its mechanical appraisal

Effects of ZrO 2 addition on phase stability and photocatalytic activity of ZrO 2 /TiO 2 nanoparticles

Antiviral surfaces and coatings and their mechanisms of action

Surface interactions and viability of coronaviruses

Surface adhesion of viruses and bacteria: Defend only and/or vibrationally extinguish also?! A perspective

Viruses in soil: Nano-scale undead drivers of microbial life, biogeochemical turnover and ecosystem functions

The authors declare no conflict of interest.