key: cord-0737484-h5ysxh1i authors: Endo, Tomonori; Gemma, Aki; Mitsuyoshi, Ryoto; Kodama, Hiroki; Asaka, Daiya; Kono, Midori; Mochizuki, Takeshi; Kojima, Hiromi; Iwamoto, Takeo; Saito, Saburo title: Discussion on effect of material on UV reflection and its disinfection with focus on Japanese Stucco for interior wall date: 2021-11-08 journal: Sci Rep DOI: 10.1038/s41598-021-01315-1 sha: ad988e15d54a766597a3ab284005a768f8683416 doc_id: 737484 cord_uid: h5ysxh1i Research has previously shown that ultraviolet light C (UV-C) can inactivate unexpected infection. However, this type of potential disinfection is dramatically reduced for the shadow area such as under desk or medical equipment. Because the UV-C reflectance ratio is low on the general wall surfaces. We compared Stucco against the other materials to investigate whether we could improve disinfection for the shadow area. The reflectance ratios of UV-C irradiation of each material were examined, with particular attention to the rates for the author’s Modified Stucco. To evaluate the disinfection effects of the UV-C reflective lighting, colonies of E. coli and of Staphylococcus hominis were cultured in an agar media and counted over a certain time period after applying UV-C irradiation from a sterilizing lamp onto the investigation materials. The author’s Modified Stucco, produced reflectance ratios that was 11 times that of white wallpaper. This demonstrated that the UV-C reflected on the Stucco wall having optimum components and their compositions inhibited the number of E. coli and S. hominis, resulting in significantly disinfection effects on white wallpapers. The space with Modified Stucco and then irradiated by a UV-C may give a strong disinfection effect. www.nature.com/scientificreports/ calcium hydroxide mined from limestone and distilled at the super high temperature of 900 ℃ or higher. In the past, fillers, such seaweed and fibers as were added, but in the present polymers are added as thickening agents. Most Stucco formulas are a mixture of natural materials. When the Stucco is applied to the wall surface, it begins to harden by absorbing CO 2 from the air through the chemical reaction Ca(OH) 2 + CO 2 → CaCO 3 + H 2 O. The Stucco continues to harden for at least 10 years, eventually becoming calcium carbonate (CaCO 3 ), a high-duty, limestone-like hard surface. For this reason, Stucco has historically been used for roof tiles and for both outer and inners walls requiring high strength 8, 9 . However, in the 1960s the Japanese economy grew rapidly and the use of Stucco in Japanese building practices fell due to a new dry construction method, which shortened the construction period, allowing for mass production and reduced costs. This construction trend changed Japanese inner wall materials from Stucco to white wallpaper or white paint. The use of Stucco decreased because the longer construction time and finishing time, which depended upon the techniques of Stucco artisans 6 . At present, the use of Stucco is mainly for special locations, such as in private homes and in hotels as wall art. The Stucco is a traditional material for inner walls in Japan as well as in foreign countries. In recent years, the use of Stucco for interior walls has received renewed attention. The Stucco used in historical buildings is not only artistic, but also has the advantage of strong wall strength and long service life. Recent studies have shown that Stucco walls absorb and release moisture from the atmosphere, thereby preventing rapid changes in room humidity 10, 11 . Humidity control is the most important strategy to reduce indoor fungal growth. A room with Stucco walls is reported to have a high anti-fungal effect due to humidity control 12 . Powder lime, with its strong alkaline properties, is used in many countries for the prevention and control of avian influenza virus 13 . Similarly, fine-grained lime Stucco walls have an antimicrobial activity under moist conditions. In contrast, grain wall materials with a surface of porous adsorbs bacteria and have no antimicrobial effect 14 . This antimicrobial effect of fine-grained Stucco walls would allow to be used in health care unit. Stucco walls also efficiently absorbs volatile organic compounds (VOCs) generated during construction associated sick building syndrome 15 . These functionalities of the Stucco are due to the porous mediums structure such as carbon-based adsorbent. In addition, Stucco is made of inorganic materials, so it has excellent fire resistance 16 . Stucco has the potential to make residence more comfortable and safer than conventional wallpaper or paint. Through this study of UV-C light irradiated onto a Stucco surface and the resulting reflected UV-C light waves released by the irradiated Stucco, it was shown that Stucco has a high UV-C reflectance ratio and that this reflected light has a high disinfection effect, compared to white wall papers and paints which are used for a general inner wall. In the hopes of increasing the reflectance ratio, this paper's authors altered conventional Stucco by creating a unique formula, thereby creating a Modified Stucco. This modified version of Japanese Stucco was compared favorably to the reflectance ratio of aluminum (aluminum foil), a material previously reported as having the highest UV-C reflectance ratio 17 . Powder materials and average diameters of their particles. The powder materials used for preparing the Modified Japanese Stucco, with the authors' unique composition and particle diameters, are as follows: calcium hydroxide (a generous gift from Nippon Plaster Co., Ltd. Tochigi, Japan), calcium carbonate in three different particle sizes (a generous gift from Nippon Plaster Co., Ltd. Tochigi, Japan), calcium hydroxide (Esukaron #2300, Sankyo Seifun Co., Ltd. Okayama, Japan), barium sulfate (022-00425, Fujifilm Wako Pure Chemical Co., Ltd. Osaka, Japan), barium sulfate (W-6, W-1, P-30, Takehara Kagaku Kogyo Co., Ltd. Hyogo, Japan). The diameters for the particles of the three types of calcium carbonate were provided by the maker. Those values were measured by a laser diffraction particle size analyzer (SALD-200V, Shimadzu Co., Ltd. Kyoto, Japan). The average diameters of the particles of microparticulate calcium carbonate and magnesium sulfate were measured by dynamic light scattering and zeta potential measurement systems (Zetasizer Nano ZS, Malvern Panalytical Ltd. Worcestershire, United Kingdom). (UV-Vis-NIR) spectrophotometer (UV-3600, Shimazu Co., Ltd. Kyoto, Japan), a source light was dispersed into monochrome light in the UV-C wavelengths through diffraction grating. The resulting UV to visible light (240-780 nm) irradiated the sample materials. The light reflected back from the surface of the sample materials was measured using the integrating sphere attachment of the spectrophotometer and the reflectance ratios were calculated. The UV-C reflectance ratios of Stucco with different mixing ratios and particle sizes of each material was measured. By changing formulation and particle size of CaCO 3 and BaSO 4 , we created a sample of Stucco using powder materials and thickener. Water was added to these material at room temperature to make a paste, which was applied to the plasterboard by an artisan. Based on these reflectance data, the Stucco was modified to improve the UV-C reflectance. The Modified Japanese Stucco prepared by this paper's authors was based on JIS A 6919 Japanese Industrial Standards (JIS) for Stucco 18 ("Supplementary data"). The irradiated materials on which UV-C reflectance ratios were measured are follows: aluminum foil (MY FOIL, UACJ Foil Co., Ltd. Tokyo, Japan), aluminum plate (N96620, Nippon Light Metal Co., Ltd. Tokyo, Japan), commercial Japanese Stucco (Shikkui Kurumu Uchi ® , Nippon Plaster Co., Ltd. Tochigi, Japan), white wallpaper (FE6716, Sangetsu Co., Ltd. Aichi, Japan), white paint (Suisei-Wide V, Nippe Home Products Co., Ltd. Tokyo, Japan), and the Modified Japanese Stucco blended by the authors. The other metals examined were stainless steel plate (SUS304 2B, Nippon Steel Stainless Steel Co., Ltd. Tokyo, Japan), and copper plate (C1100P, Mitsubishi Materials Corporation Co., Ltd. Tokyo, Japan). In addition, common Japanese cedar lumber, mortar and concrete were measured. www.nature.com/scientificreports/ Using a UV irradiance meter (UV-M02, Orc Manufacturing Co., Ltd. Tokyo, Japan), UV-C irradiance at the agar media after passing through various test boxes was also measured. The test boxes in which UV-C irradiance was measured are follows: aluminum foil (back side, matt), authors' Modified Stucco, commercial Stucco, and white wall paper. JM109 strain, Takara Bio Inc. Shiga, Japan), and Staphylococcus hominis (S. hominis). These are Gram-negative and Gram-positive bacteria with different bacterial cell wall structures. Instead of the pathogenic microorganisms that are problematic in hospitals, these bacteria were used as surrogate microorganisms for this study. S. hominis were collected by placing the standard agar media at 0.8 m height from the floor for 15 min. with careful aseptic handling, and by passive microbial sampling. The collected bacteria were cultured at 37 ℃ for 48 h. From the various cultured bacteria, S. hominis were identified by MALDI-TOF MS (autoflex speed™ MALDI-TOF/ TOF MS, Bruker Corp. Massachusetts, USA). off of each wall material were evaluated using a test wall, which simulated an inner wall (Fig. 1 ). These wall sections were uniformly coated or covered with each material. A light wave reflected 90° from the direct light wave of a UV-C germicidal lamp (power consumption 6 W, UV irradiance 19 μW cm −2 , 254 nm, Toshiba Lighting & Technology Co., Ltd. Kanagawa, Japan) irradiated the standard agar media (Trypto-Soya Agar, Petri dish diameter: 8 cm) which had been applied with either the E. coli or S. hominis. Then, the number of colonies that had cultured at 37 ℃ for 48 h. was counted to compare the disinfection effects. The materials used in this portion of the study were commercial Stucco, the Stucco with the formula created by the authors, and the aluminum foil. White wallpaper was used as a reference. The number of bacteria was prepared solution concentration (E. coli; 3.47 × 10 6 CFU/ml, S. hominis; 3.93 × 10 6 CFU/ml) and this solution was applied onto the standard method agar with 50 μl. Statistical analysis. Statistical analyses for disinfection effects of UV-C reflected irradiation were carried out using GraphPad Prism 9.1.0 software (GraphPad Software, Inc., San Diego, CA, USA). The quantitative data (n = 3) for disinfection are presented as mean ± standard deviation. The evaluation of the bactericidal effect of UV-C reflected lighting was analyzed by two-way ANOVA. The significance of the results of the analysis was defined as p < 0.05. Since we used several different sizes of calcium carbonate and barium sulfate particles, we measured the average diameter of these particle sizes (ps). The average diameters of the particles in CaCO 3 measured by particle size analyzer were 8.9 μm, 6.0 μm, 3.0 μm, and 1.0 μm, and described as CaCO 3 (ps = 8.9 μm), CaCO 3 (ps = 6.0 μm), CaCO 3 (ps = 3.0 μm), CaCO 3 (ps = 1.0 μm). The average diameters of the particles in barium sulfate were determined as 4.8 μm, 1.7 μm, 1.1 μm, 0.3 μm, and described as BaSO 4 (ps = 4.8 μm), BaSO 4 (ps = 1.7 μm), BaSO 4 (ps = 1.1 μm), BaSO 4 (ps = 0.3 μm). UV reflectance ratios for each material. As shown in Fig. 2 , the reflectance ratios of UV-C (254 nm) light for the aluminum foil (back side, matt), the aluminum foil (front side, shiny), the Japanese commercial Stucco, the aluminum plate, the white paint and the white wallpapers were, 75.7%, 65.9%, 38.3%, 32.2%, 6.7%, and 6.1%, respectively. The ratios of the stainless steel plate, copper plate, Japanese cedar lumber, mortar, and Fig. S1 ). Among the materials measured in this study, the aluminum foil (backside, matt) showed the highest reflectance ratio. Changes in UV-C reflectance ratios and irradiance of Stucco by changing composition ratio and material. To increase the reflectance ratio of the commercial Stucco, the composition and the average particle diameters were changed. Standard commercial Stucco has Ca(OH) 2 as a main component, CaCO 3 as the second highest ingredient, and smaller amounts of sand, fibers, and a thickening agent as miscellaneous ingredients. The basic components in the Stucco used in this study are mainly Ca(OH) 2 , CaCO 3 and a thickening agent. The UV-C reflectance ratios produced by changing the amount (%) of CaCO 3 are shown in Fig. 3a . The changes of the ratios produced by changing the average diameters of CaCO 3 particles at the fixed amount ratio (%) of CaCO 3 and Ca(OH) 2 are shown in Fig. 3b . The changes in ratios produced by replacing CaCO 3 with BaSO 4 were also examined (Fig. 4) . By increasing the amount (weight %) of CaCO 3 by 45%, 50%, 70%, 80%, and 90%, the UV-C (254 nm) reflectance ratios were 61.3%, 65.5%, 63.8%, 69.0%, and 71.5%, respectively (Fig. 3a) . By changing the average diameters of the CaCO 3 particles to 8.9 μm, 6.0 μm, 3.0 μm, and 1.0 μm, the respective reflectance ratios were 53.1%, 67.7%, 71.5%, and 73.4%, respectively (Fig. 3b) . By increasing the amount (weight %) of BaSO 4 from 0 to 5%, 25%, 60%, and 90%, the reflectance ratios of UV-C (254 nm) showed higher from 54.1 to 61.1%, 66.8%, 60.5%, and 77.2%, respectively (Fig. 4a) . By changing the average diameters of the BaSO 4 particles to 4.8 μm, 1.7 μm, 1.1 μm, 0.3 μm, the reflectance ratios were 59.6%, 65.7%, 70.1%, 77.2%, respectively (Fig. 4b) . According to JIS A 6919, the amount of Ca(OH) 2 should amount to more than a half of the total Stucco. In the Stucco composition based on Standards in Japan, JIS A 6919 (Ca(OH) 2 54%, CaCO 3 (ps = 8.9 μm) 45%, with other ingredients, including a 1% thickening agent), the UV-C (254 nm) reflectance ratio was 45.0%, showing a rate close to the commercial Stucco. In addition, in the authors' Modified Stucco composition, which we determined based on the characteristics of CaCO 3 and BaSO 4 stated above, that is, Ca(OH) 2 51%, BaSO 4 (ps = 0.3 μm) 25%, CaCO 3 (ps = 3.0 μm) 23% and 1% thickener, the UV-C reflectance ratio rose to 66.8% (Fig. 5) . Next, UV-C irradiance at a distance of 75 cm from the direct UV-C lamp was 30 μW cm −2 . In contrast, UV-C irradiance at the agar media after passing through a test box with aluminum foil (back side, matt), authors' Modified Stucco, commercial Stucco, and white wall paper was 148 μW cm −2 , 21 μW cm −2 , 6 μW cm −2 , and 1 μW cm −2 , respectively. Disinfection effects of UV-C reflected irradiation. The log reduction of E. coli and S. hominis in direct UV-C light was evaluated. The UV dose (Irradiance × exposure time) required to 5.928-log 10 reduction of E. coli was 3.6 mJ cm −2 . The UV dose required to 4.254-log 10 reduction of S. hominis was 18 mJ cm −2 ( Supplementary Fig. S2) . www.nature.com/scientificreports/ As shown in Fig. 6a, 1 .11-log 10 reduction of E. coli were found after 1 min of irradiation time onto the white wallpaper (the common inner wall material) and 3.96-log 10 reduction at 30 min. In contrast, we observed log reduction of E. coli at only 30 s of irradiation for the commercial Stucco, the aluminum foil and the authors' Modified Stucco (composed of Ca(OH) 2 51%, BaSO 4 (ps = 0.3 μm) 25%, CaCO 3 (ps = 3.0 μm) 23% and thickening stabilizer etc. 1%). We observed 4.6-log 10 reduction and 5.24-log 10 reduction, at 1 min for the authors' modified Stucco and the aluminum foil, showing the significant difference in disinfection effects compared to white wall paper (p < 0.001, p < 0.001, respectively). In the same experiment using the S. hominis, we observed more than 4-log reduction at 1 min for the aluminum foil, at 30 min for the originally created Stucco, at 90 min for the commercial Stucco. In contrast, we observed 2.84-log 10 reduction at 180 min for white wallpaper. At 5 min of UV irradiation, authors' Modified www.nature.com/scientificreports/ Stucco showed a significant difference in the disinfection effects compared to white wall paper (3.04-log 10 reduction, p < 0.001; Fig. 6b ). There is increasing interest in the role of disinfection for multi-drug antimicrobial resistanc 19 . Also, COVID-19, the novel pandemic infectious disease has become a worldwide issue and is recently reported to become a growing menace in the future 20 . UV disinfection has been reported to be effective in reducing of multi-drug resistant organisms 21 and COVID-19 22 . Since contamination of infectious microbes is noticeable at the bedsides and on the flooring under beds 23 , the risks posed by these microbes in healthcare environments has gained greater recognition. The infectious substances are diffused by contact with hands, transference from the floor to shoes, and the movement of people. Sterilizing the sites where the infectious microbes have spread is a basic countermeasure 24 and is expected to effectively inactivate the infectious agents. However, exposure to UV-C light, one method of microbe inactivation, may risk impairment of the skin and the eyes. Yet, UV-C lighting is reported for its usefulness 25, 26 because it shows the inactivation of microbes with high efficiency when the lighting is used safely 27 . In recently, UV-LED lighting (ultraviolet light emitting diode) is attracting attention in the food field 28 , an area of limited available microbe inactivation techniques, as well as the medical field. This study paid attention to Stucco, which has been a traditional Japanese wall material. Stucco walls are very pure white, make rooms bright, and their surface textures are artistic and very beautiful. Around the world, Stucco walls have had specific historical cultural uses. For example, Holy Trinity Cathedral in Chicago, with Stucco finishing on its brick construction, is known as historical architecture. This study was intended to demonstrate whether Stucco has a new value and highly effective functionality even in modern times in Japan. The aluminum wall surface (aluminum foil) showed the highest UV-C reflectance ratios among the materials measured in this study, as previously reported 17 . By analyzing the reflectance effect on experimental Stucco walls, the Stucco showed a high reflectance ratio not only in the visible region, but also notably in the UV-C region, as compared with the white wallpaper and white paint commonly used (Fig. 2) . The UV-C reflectance ratio of the commercial Stucco was 1.2 times that of the aluminum plate, 5.7 times that of the white paint, and 6.3 times that of the white wallpaper. Of special note is that the Stucco gave a reflectance ratio higher than the aluminum plate (Fig. 2) . For the purpose of investigate the reflectance ratio of the wall surface coated with Stucco, the weight % or particle size of CaCO 3 and BaSO 4 have been changed. By increasing the amount of CaCO 3 , the UV-C reflectance ratios increased (Fig. 3a) . In the same amount (weight %) of CaCO 3 , the smaller the average diameters of CaCO 3 particles were, the more the UV reflectance ratios rose (Fig. 3b) . By replacing CaCO 3 with BaSO 4 , a natural inorganic substance, and increasing the amount (weight percent) of BaSO 4 , the trend of a rise in the ratio of reflectance was shown (Fig. 4a) . When the average diameter of BaSO 4 particles was smaller, the UV-C reflectance ratio increased (Fig. 4b) . In short, CaCO 3 which is the second main component of the Stucco formula can be used to increase the reflectance ratio by reducing the particle size and increasing its weight percent. Alternatively, the reflectance ratio of the Stucco can also be more increased by using BaSO 4 , which is a smaller particle size and increasing its weight percent, instead of CaCO 3 . Stucco walls are almost composed of natural white inorganic materials. BaSO 4 is also a white natural mineral material, it has high chemical stability with a decomposition temperature of 1600 ℃ 29 , which is higher than CaCO 3 30 . BaSO 4 is safe and familiar to us because it is used in X-ray contrast media for the gastric. There would www.nature.com/scientificreports/ be no problem if BaSO 4 was added to Stucco as a substitute for CaCO 3 . However, the smaller particle size of the second component may cause cracks in the wall due to long-term vibration. This problem may be solved by adding fibers to the Stucco. In the Stucco formulated to be close to the reflectance of commercial Stucco (UV reflectance 45.0%, Fig. 5 ), the particle size of CaCO 3 was 8.9 μm. Therefore, UV reflectance may be increased by using CaCO 3 with smaller this particle size. As shown in Fig. 3b , the reflectance of CaCO 3 (ps = 8.9 μm) is 53.1%, so the reflectance may be increased instead of any particle size of same amount BaSO 4 (Fig. 4b) . No cracks appeared on the wall within 14 days of applying BaSO 4 (ps = 0.3 μm), while CaCO 3 (ps = 1.0 μm) caused cracks on the wall ( Supplementary Fig. S3 ). The authors considered these characteristics, one example of a modified Stucco was prepared by selecting more than half of Ca(OH) 2 , about a quarter of CaCO 3 (ps = 3.0 μm) was selected to prevent cracking, and about a quarter of BaSO4 (ps = 0.3 μm) was selected to improve reflectivity. The unique Stucco compositions reached UV-C reflectance ratios close to the level of aluminum foil (66.8%, Fig. 5 ). The author's Modified Stucco produced reflectance ratios that was 11 times that of white wallpaper. These results demonstrated that, by selecting an optimum composition and particle diameter of CaCO 3 or adding BaSO 4 , a Stucco wall surface can be used to show a very effective reflectance of UV-C light. In addition to increasing the UV reflectance, UV-C irradiance was high in proportion to UV-C reflectance. The author's modified Stucco had 21 times UV-C irradiance of white wall paper. In short, by increasing UV-C reflectance also made it possible to increase the UV-C irradiance. Improvement in UV irradiance of Stucco wall is more effective than UV reflectance ratio. The reason for effective increase in UV irradiance may be Stucco walls caused reflections and scattering of UV in space. This effect on UV irradiance may also be expected in the room with Stucco wall. Figure 6 . Log reduction (Log (N t /N 0 )) vs UV dose of UV-C reflected off various materials: the UV-C was irradiated to standard agar media applied with (a) E. coli and (b) S. hominis. UV dose is the UV intensity at a distance of 75 cm from the direct UV-C lamp (6 W, 254 nm). Data are presented as mean ± standard deviation. **p < 0.01, ***p < 0.001. www.nature.com/scientificreports/ We examined the disinfection effects against E. coli and S. hominis using the irradiation light waves of a UV-C germicidal lamp. More than 4 log reduction of E. coli and S. hominis required UV dose was 3.6 mJ cm −2 for E. coli and 18 mJ cm −2 for S. hominis. Comparing the UV resistance of E. coli and S. hominis to direct UV-C light, S. hominis required several times more UV dose than E.coli (Supplementary Fig. S2 ). As shown in Fig. 6 , both the Stuccos with the unique compositions created by the authors and the Japanese commercial Stucco significantly decreased the time to be sterilized compared with white wallpaper. The rapid decrease in the reflectance ratios of wallpaper and paint in the lights in UV region may be caused by the low transmittance of UV-C light through vinyl chloride 31 , a main component of wallpaper, and by the absorption of UV-C light by titanium dioxide 32 , used in the coloring of the paint. For the reasons stated above, the inactivation of infectants wanes substantially on the surface of objects irradiated by the reflection effect of UV-C light compared with direct UV-C lighting. UV-C light and wall coating materials which reflect UV-C light have been reported to reduce the inactivation time against microbes in a room 33 . Therefore, a room space which has both Stucco walls and a UV-C irradiation device are expected to reduce the time needed to inactivate infectious microbes more than other conventional ways, even against the shadows under desks and medical equipment. This information shows that this combination may be effective for inactivation of infectious substances on the space where the lights irradiated off the wall of objects or medical devices in the examination room of otolaryngology where a lot of those microbes may be found. The efficient inactivation of microbes in a short time may reduce the examination interval from one patient to the next. Since UV radiation over long intervals causes deterioration and discoloring of the resin in expensive medical devices, high radiation effects for a short time gives many benefits. Furthermore, Stucco has a history of longtime usage in many countries, so its applications are very beneficial. This study was performed in the limited area as a model experiment in the laboratory for the inactivation test only against E. coli, and S. hominis, which are surrogate microorganisms for pathogenic microorganisms. The challenge in the near future, is necessary to verify the improvement of disinfection effect against microbiological associated with HAI such as ESKAPE (Enterococcus faecium, Staphylococcus aureus, Klebsiella pneumoniae, Acinetobacter baumannii, Pseudomonas aeruginosa and species of Enterobacter) pathogens 34 , is to explore Stucco components showing high UV reflection rates, apply to the deep UV-LED which came into practical use recently, and investigate infectious substances in the real medical environment. CaCO 3 which is the second component of the Stucco can be increased the UV reflectance by increasing its weight percent with a small particle size of 3.0 μm. Alternatively, the UV reflectance of the Stucco can also be increased by using more BaSO 4 , which is a small particle size of 0.3 μm, instead of CaCO 3 . As an example of modified Stucco, selecting more than half of Ca(OH) 2 and about a quarter of CaCO 3 (ps = 3.0 μm), and about a quarter of BaSO 4 (ps = 0.3 μm) can significantly improve UV reflectance. The space coated optimized Stuccos showed an improvement of UV-C reflectance ratios close to that of aluminum foil (front surface, shine). Thus, when a UV-C light source is used in a room with Stucco walls which have been made with an optimum composition of elements, disinfection effects may be significantly obtained, not only under direct irradiation, but also from the irradiating light being reflected off the wall. Antimicrobial resistance Healthcare equipment as a source of nosocomial infection: A systematic review The role of the surface environment in healthcare-associated infections The effectiveness of UV-C radiation for facility-wide environmental disinfection to reduce health care-acquired infections Simplified modeling of E. coli mortality after genome damage induced by UV-C light exposure Reaffirm the functionality of the plasterd walls Calculation of k factor function for the carbonation process of lime-based plasters Lime mortars for the conservation of historic buildings Water vapor adsorption in porous building materials: Experimental measurement and theoretical analysis Comparison of moisture buffering properties of plasters in full scale simulations and laboratory testing Domestic environment: Indoor mycobiota as a public health risk factor. Environ. Mycol. Public Health Lime in the limelight Building materials vs. fungal colonization -model experiments Influence of eco-materials on Performance of lime-based mortars at elevated temperatures Reflectance and preparation of front surface mirrors for use at various angles of incidence from the ultraviolet to the far infrared Japanese pre-mixed lime plaster for interior finish (JIS A 6919) Controlling hospital-acquired infection: Focus on the role of the environment and new technologies for decontamination Confronting antimicrobial resistance beyond the COVID-19 pandemic and the 2020 US election Clinical and microbiological effect of pulsed xenon ultraviolet disinfection to reduce multidrug-resistant organisms in the intensive care unit in a Japanese hospital: A before-after study SARS-CoV-2 survival on surfaces and the effect of UV-C light Healthcare environments and spatial variability of healthcare associated infection risk: Cross-sectional surveys Best practice in healthcare environment decontamination Room decontamination with UV radiation Patient room decontamination against carbapenem-resistant enterobacteriaceae and methicillin-resistant staphylococcus aureus using a fixed cycle-time ultraviolet-C device and two different radiation designs A powerful technique for inactivating microorganisms and the related side effects to the skin Recent advances on the application of UV-LED technology for microbial inactivation: Progress and mechanism Barium sulfate Calcium carbonate Preparation, dielectric and optical properties of Cr 2 O 3 /PVC nanocomposite films Optimizing the benefits of TiO 2 in paints Rapid hospital room decontamination using ultraviolet (UV) light with a nanostructured UV-reflective wall coating Bad bugs, no drugs: No ESKAPE! An update from the Infectious Diseases Society of America Commercial Stucco, calcium hydroxide, and calcium carbonate were gifted by Nippon Plaster Co., Ltd of Japan. T.E. was involved in the conception and design of the study. T.E., A.G., R.M., H.K., D.A., M.K., T.M., H.K. and S.S. were involved in the acquisition of data. T.E. and A.G. analyzed and interpreted the data. T.E. drafted the article. All other authors critically revised the article for important intellectual content. All authors read and approved the final manuscript. T. Mochizuki and T. Endo are the co-inventor of the patent pending reflective Stucco. The other authors declare no potential conflict of interest. The online version contains supplementary material available at https:// doi. org/ 10. 1038/ s41598-021-01315-1.Correspondence and requests for materials should be addressed to T.E.Reprints and permissions information is available at www.nature.com/reprints.Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.