key: cord-0697896-titv8rld authors: Chandra, Subhash; Jagdale, Pravin; Medha, Isha; Tiwari, Ashwani Kumar; Bartoli, Mattia; Nino, Antonio De; Olivito, Fabrizio title: Biochar-Supported TiO(2)-Based Nanocomposites for the Photocatalytic Degradation of Sulfamethoxazole in Water—A Review date: 2021-11-18 journal: Toxics DOI: 10.3390/toxics9110313 sha: ddd35b290fbaaa9013904955bf02b1249c64163e doc_id: 697896 cord_uid: titv8rld Sulfamethoxazole (SMX) is a frequently used antibiotic for the treatment of urinary tract, respiratory, and intestinal infections and as a supplement in livestock or fishery farming to boost production. The release of SMX into the environment can lead to the development of antibiotic resistance among the microbial community, which can lead to frequent clinical infections. SMX removal from water is usually done through advanced treatment processes, such as adsorption, photocatalytic oxidation, and biodegradation. Among them, the advanced oxidation process using TiO(2) and its composites is being widely used. TiO(2) is a widely used photocatalyst; however, it has certain limitations, such as low visible light response and quick recombination of e(−)/h(+) pairs. Integrating the biochar with TiO(2) nanoparticles can overcome such limitations. The biochar-supported TiO(2) composites showed a significant increase in the photocatalytic activities in the UV-visible range, which resulted in a substantial increase in the degradation of SMX in water. The present review has critically reviewed the methods of biochar TiO(2) composite synthesis, the effect of biochar integration with the TiO(2) on its physicochemical properties, and the chemical pathways through which the biochar/TiO(2) composite degrades the SMX in water or aqueous solution. The degradation of SMX using photocatalysis can be considered a useful model, and the research studies presented in this review will allow extending this area of research on other types of similar pharmaceuticals or pollutants in general in the future. Water is an important resource for the living of animals, aquatic life, and human beings. During past decades, a continuous increase in the worldwide population and industrial activities have rapidly increased the water demand among the communities. Therefore, it is very much necessary to fulfil the water demand among the communities while maintaining the ecological balance [1] . However, due to the rapid industrialization and change in living style, the water quality in the natural resources such as rivers, lakes, and groundwater has substantially deteriorated due to the release of the pollutants [2, 3] . In recent years, the production of antibiotics from pharmaceutical industries and their consumption by humans and animals has significantly increased due to the frequent endemic and pandemic episodes such as COVID-19, Ebola, and Swine flu [4, 5] . The high material for TiO 2 nanoparticles was reportedly done to increase the adsorption of SMX onto the micro-and mesopores of biochar, reduce the band energy gap, and reduce the chances of the recombination of e − /h + pairs due to the high semi-conductor activity of the material [37] . The motivation for writing a review on the photocatalytic degradation of SMX in water using the biochar-TiO 2 composite material lies in the fact that, till now, various reviews have been published on the photocatalytic degradation of dyes, organic pollutants, and other antibiotics. However, not a single review is available particularly focusing on the speciation of SMX in water and its photocatalytic degradation using the biochar-supported TiO 2 composite. The objectives of this paper are to review the following: (i) Synthesis methods of biochar-supported TiO 2 nanoparticles; (ii) The effect of the integration of biochar with TiO 2 particles in terms of changes in the physicochemical properties and increase in the photocatalytic response under UV-visible light; (iii) Delineate the photochemistry of SMX in water and its major sources into the environment; (iv) Delineate the chemical pathways and mechanisms involved during the photocatalytic degradation of SMX in water using the biochar-supported TiO 2 nanoparticles. Previous study results indicated that the application of TiO 2 -biochar composite showed up to 90% removal of SMX from the aqueous solution via photocatalysis under UV-visible radiation [38] . Another study showed that more than 80% of SMX was removed from the aqueous solution having high chemical oxygen demand via photocatalysis using the TiO 2 /biochar composite material [39] . Avramiotis and co-workers [40] developed a procedure to oxidize sulfamethoxazole through the activation of the persulfate by a pre-synthesized rice husk biochar, and they focused the study on the crucial activity of either electron transfer/singlet oxygen control and surface-bound radicals. In another recent work [41] , in which SMX was indicated as a dangerous and recalcitrant pollutant, this antibiotic was degraded by the surface coating of a ceramic membrane by a photo-Fenton catalyst, and the degradation reached up to 90%. In a similar work carried out by Liu and co-workers [42] , sulfonamide antibiotics were degraded efficiently using a combination of persulfate and UV irradiation. Vignati et al. [43] proved that ZnO can accelerate the photocatalytic degradation of Spiramycin in urban wastewater, and they carried out an in-depth study of the kinetics of the degradation and toxicity of the metabolites. In another work [44] , the photocatalytic degradation of tetracycline hydrochloride under visible light irradiation using a newly synthesized photocatalyst MVO 4 /g-C 3 N 4 (M = La, Ga) prepared by a hydrothermal method was investigated. There are various point and non-point sources of SMX in rivers and other water resources. The major sources of SMX (antibiotic) into water are illustrated graphically in Figure 1 . The primary sources of this molecule into the water resources can be classified into five different groups: (i) effluent wastes from hospitals, (ii) effluent waste from pharmaceutical industries, (iii) effluent waste from the water treatment plant, (iv) effluent waste from aquaculture system and livestock farming, and (v) effluent and leachates from sanitary landfills [45] . The concentration of SMX in the river stream and water reportedly varies from ng/L to mg/L [45] . The SMX from the aquaculture system and livestock farming mostly come into the river stream through the disposal of wastewater generated from the farms directly into the river. The concentration of SMX from aquaculture systems (fish and shrimp) and livestock farms (pig and poultry) reportedly varies from 10 µg/L to 7 mg/L as reported in the water samples collected from shrimp ponds and canals nearby the livestock farming in Vietnam [46, 47] . Untreated sewage is another source of SMX into the water as, during the heavy rainfall, untreated sewage, due to having limited hydraulic capacity, finds its way into the freshwater line. The concentration of SMX from the sewage discharge reportedly varies from ng/L up to 60 µg/L, as indicated by the data of the analysis of water samples from the sewage line discharge and freshwater streams within its nearby areas [48] . Apart from that, the presence of SMX in the effluent of wastewater treatment plants was also observed in the water samples, as reported in studies conducted in different countries [49, 50] . The concentration of this compound in the effluent of sewage treatment plants reportedly varies from 226 to 3000 ng/L as per the data obtained from different studies conducted in China, Vietnam, and the Philippines [47, 51, 52] . Leachate from landfills is another major source of SMX discharge into the surface and groundwater. However, very little information and understanding of the mechanism is available regarding the fate and transport of this compound from the landfill sites. The concentration of SMX in the leachates reportedly varies from 6.4 to 8488 ng/L based on the data gathered from the studies conducted in the landfill sites of China and Singapore [53, 54] . Moreover, the effluent waste from the pharmaceutical industries and hospital wastes are categorized as one of the direct sources of SMX and other antibiotics into the water. Previous studies carried out in the cities of China and Vietnam indicated the presence of SMX and other antibiotics in wastewater generated from hospitals and pharmaceutical industries [55, 56] . The typical concentration of SMX in the wastewater generated from the pharmaceutical industry and hospitals reportedly varied from 320-2910 ng/L based on the data of the studies done earlier in China and Vietnam [55, 57] . Toxics 2021, 9, x FOR PEER REVIEW 4 o mg/L as reported in the water samples collected from shrimp ponds and canals near the livestock farming in Vietnam [46, 47] . Untreated sewage is another source of SMX in the water as, during the heavy rainfall, untreated sewage, due to having limited hydrau capacity, finds its way into the freshwater line. The concentration of SMX from the sewa discharge reportedly varies from ng/L up to 60 μg/L, as indicated by the data of the an ysis of water samples from the sewage line discharge and freshwater streams within nearby areas [48] . Apart from that, the presence of SMX in the effluent of wastewa treatment plants was also observed in the water samples, as reported in studies conduct in different countries [49, 50] . The concentration of this compound in the effluent of sewa treatment plants reportedly varies from 226 to 3000 ng/L as per the data obtained fro different studies conducted in China, Vietnam, and the Philippines [47, 51, 52] . Leacha from landfills is another major source of SMX discharge into the surface and groundwat However, very little information and understanding of the mechanism is available regar ing the fate and transport of this compound from the landfill sites. The concentration SMX in the leachates reportedly varies from 6.4 to 8488 ng/L based on the data gather from the studies conducted in the landfill sites of China and Singapore [53, 54] . Moreov the effluent waste from the pharmaceutical industries and hospital wastes are categoriz as one of the direct sources of SMX and other antibiotics into the water. Previous stud carried out in the cities of China and Vietnam indicated the presence of SMX and oth antibiotics in wastewater generated from hospitals and pharmaceutical industries [55, 5 The typical concentration of SMX in the wastewater generated from the pharmaceuti industry and hospitals reportedly varied from 320-2910 ng/L based on the data of t studies done earlier in China and Vietnam [55, 57] . Sulfamethoxazole (SMX) and tetracycline are widely used antibiotics, which a mostly used for the treatment of human beings and animals [58] . These antibiotics a usually detected in wastewater, surface water, and groundwater in the detection range ng L −1 to μg L −1 [59, 60] . Specifically, sulfamethoxazole (SMX), which comes under t chemical class of sulfonamide compounds, is an antimicrobial drug with broad-spectru activity against gram-positive and negative bacteria [61] . The pharmaceutical waste, which the antibiotic is a part, is usually hydrolyzed in water. The understanding of t degree and behavior of hydrolysis of antibiotics is of prime concern to understand th stability and non-biodegradability in the environment [62] . Sulfamethoxazole possess Sulfamethoxazole (SMX) and tetracycline are widely used antibiotics, which are mostly used for the treatment of human beings and animals [58] . These antibiotics are usually detected in wastewater, surface water, and groundwater in the detection range of ng L −1 to µg L −1 [59, 60] . Specifically, sulfamethoxazole (SMX), which comes under the chemical class of sulfonamide compounds, is an antimicrobial drug with broad-spectrum activity against gram-positive and negative bacteria [61] . The pharmaceutical waste, of which the antibiotic is a part, is usually hydrolyzed in water. The understanding of the degree and behavior of hydrolysis of antibiotics is of prime concern to understand their stability and non-biodegradability in the environment [62] . Sulfamethoxazole possesses good chemical stability in the environment, which allows it to resist metabolic processes and natural degradation [63] . The SMX usually absorbs the incident radiation light in the wavelength range of 250 to 300 nm, which also varies with respect to the change in the surface charge density on the SMX as the pH of the aqueous solution varies from acidic to alkaline [64] . The absorbance range reportedly shifted towards a higher wavelength side (up to 300 nm) as the pH of the aqueous solution was reduced to 1 from 10 ( Figure 2 ) [64] . The pH of the solution plays a key role in the photocatalytic decomposition of SMX in water, as the SMX degradation rate reportedly was decreased with the increase in the pH value of the aqueous solution, as shown in Figure 3a [28] . The SMX mostly exists in the anionic form if pH > 5.6, and in the neutral form if pH lies between 1.85-5.6 ( Figure 3b ), as the pK a1 and pK a2 values of SMX was reported to be about 1.85 and 5.60, respectively [28, 64] . The photolytic degradation of SMX is very difficult as it cannot be completely mineralized during oxidation [28] . Previous studies elucidated the photocatalytic oxidation mechanism of SMX and the formation of intermediatory transformation products (TPs) [28, 64] . The detailed mechanism of SMX photodegradation in the presence of reactive oxygen species (ROS), i.e., •OH radical is shown in Figure 4 . It can be observed from the figure that SMX formed its isomerization intermediatory product and is denoted by P 254. Subsequently, with the addition of •OH radical, the SMX is degraded to an intermediatory product denoted by 270 c. Thereafter, the addition of • · OH radical to the transformation product (TP) defined as 270 c led to the demethylation process, which resulted in the formation of a new TP denoted by P 288. Subsequently, the breakage of the N-O bond and the removal of the carboxylic group from P 288 lead to the formation of another TP denoted by P 246. Additionally, the release of N-O and C-C bonds from P 288 formed another intermediatory product or TP denoted by P 198. The cleavage of the S-N bond from the SMX structure was reportedly occurred after reacting with an •OH free radical following the binding of N to an H atom, which leads to the formation of another TP called 3-amino 5-methylisoxazole denoted as P 99 [64] . The isomerized product of SMX is denoted by P 254, which, after reacting with •OH free radical, leads to the scission of S-N bond from P 254 that leads to the formation of a TP denoted by P 174. The P 174 on further oxidation with ROS leads to the formation of two new TPs denoted as P 158 and P 95, respectively, following the loss of C-N and C-S bonds. Toxics 2021, 9, x FOR PEER REVIEW 5 of 20 good chemical stability in the environment, which allows it to resist metabolic processes and natural degradation [63] . The SMX usually absorbs the incident radiation light in the wavelength range of 250 to 300 nm, which also varies with respect to the change in the surface charge density on the SMX as the pH of the aqueous solution varies from acidic to alkaline [64] . The absorbance range reportedly shifted towards a higher wavelength side (up to 300 nm) as the pH of the aqueous solution was reduced to 1 from 10 ( Figure 2 ) [64] . The pH of the solution plays a key role in the photocatalytic decomposition of SMX in water, as the SMX degradation rate reportedly was decreased with the increase in the pH value of the aqueous solution, as shown in Figure 3a [28] . The SMX mostly exists in the anionic form if pH > 5.6, and in the neutral form if pH lies between 1.85-5.6 ( Figure 3b ), as the pKa1 and pKa2 values of SMX was reported to be about 1.85 and 5.60, respectively [28, 64] . The photolytic degradation of SMX is very difficult as it cannot be completely mineralized during oxidation [28] . Previous studies elucidated the photocatalytic oxidation mechanism of SMX and the formation of intermediatory transformation products (TPs) [28, 64] . The detailed mechanism of SMX photodegradation in the presence of reactive oxygen species (ROS), i.e., •OH radical is shown in Figure 4 . It can be observed from the figure that SMX formed its isomerization intermediatory product and is denoted by P 254. Subsequently, with the addition of •OH radical, the SMX is degraded to an intermediatory product denoted by 270 c. Thereafter, the addition of •֗ OH radical to the transformation product (TP) defined as 270 c led to the demethylation process, which resulted in the formation of a new TP denoted by P 288. Subsequently, the breakage of the N-O bond and the removal of the carboxylic group from P 288 lead to the formation of another TP denoted by P 246. Additionally, the release of N-O and C-C bonds from P 288 formed another intermediatory product or TP denoted by P 198. The cleavage of the S-N bond from the SMX structure was reportedly occurred after reacting with an •OH free radical following the binding of N to an H atom, which leads to the formation of another TP called 3-amino 5-methylisoxazole denoted as P 99 [64] . The isomerized product of SMX is denoted by P 254, which, after reacting with •OH free radical, leads to the scission of S-N bond from P 254 that leads to the formation of a TP denoted by P 174. The P 174 on further oxidation with ROS leads to the formation of two new TPs denoted as P 158 and P 95, respectively, following the loss of C-N and C-S bonds. Titanium oxide (TiO 2 ) is a conventionally used a very common type of photocatalytic material reported in many of the earlier studies for the photocatalytic oxidation/reduction of the pollutants in the aqueous solution due to having a very stable chemical structure and non-toxicity [65] . Despite having photocatalytic properties and stable structure, nowadays, TiO 2 nanoparticles are not commonly used for the photocatalytic oxidation of pollutants in water. The reason behind its limited use for photocatalytic actions can be linked to its high bandgap (3.20 eV) and very narrow light absorbance in the ultraviolet-visible (UV-visible) range (200-400) [65, 66] . Hence, TiO 2 nanoparticles were reportedly chemically integrated with various materials, such as Zn nanoparticles, graphene, carbon nanotubes (CNT), activated carbon, and biochar, to reduce the band energy gap and increase the UV-visible absorbance range [67] [68] [69] [70] . Among the above-reported supporting materials to synthesize the TiO 2 composite, biochar has gained much attention due to its sustainability and low cost compared to the other reported materials. Moreover, the biochar-based nanoparticles reportedly have varieties of tunable functional groups, high chemical and thermal stability, and high electrical conductivity that, when integrated with the TiO 2 nanoparticles, can reduce the bandgap and quick recombination of e − /h + pairs during photocatalysis [38] . The biochar-supported TiO 2 composite can be developed using various physical, chemical, and thermal methods whose details are comprehensively covered in the subsequent sub-sections. Sol-gel is the most widely used method reportedly used for the synthesis of biocharsupported TiO 2 nanocomposites ( Figure 5A ) [71] [72] [73] . In this method, the biomass is converted to biochar through the pyrolysis process [36] , and then, the produced biochar is chemically treated with some weak acids, such as acetic or acrylic acid, to increase the surface oxides and reduce its pH [74, 75] . Subsequently, the acid-treated biochar is then mixed with the slurry containing TiO 2 nanoparticles in ethanol. The entire slurry mixture is then filtered through 0.22 µm filter paper to separate solid from liquid fraction. The solid fraction of the slurry is then calcinated in the temperature range of 500-700 • C to produce a highly stable biochar-supported TiO 2 nanocomposite [76, 77] . In the calcination process, the calcination temperature plays an important role, as heating the biochar TiO 2 mixture above 700 • C reportedly changes the TiO 2 crystal structure from anatase to rutile form [77] . The thermal polycondensation process is also known as the single-step heating process to produce biochar-supported TiO2 nanoparticles, as illustrated in Figure 5C [79, 80] . In this method, the biomass is initially mixed with some precursor such as melamine or polysaccharide agar to increase its thermal response during the calcination process. After that, the resultant biochar is mixed in a diluted ethanol solution containing titanium butyrate. The resulting solution mixture is oven-dried and then subjected to the calcination process under an ammonia gas environment to decrease the band energy gap and improve the visible light response of the biochar-supported TiO2 nanocomposite during the photocatalysis process [76, 80] . Solvothermal is the combination of hydrothermal treatment and dry heating process that facilitates the growth of TiO2 crystals onto the biochar's surface, as shown in Figure 5D . In this method, the biomass is dispersed into an ethanol solution containing titanium isopropoxide in different (w/w) ratios, such as 1:1 or 1:2, and then, the entire mixture containing biochar particles and titanium isopropoxide is subjected to a hydrothermal process in the temperature range of 160-175 °C for a duration of 12-14 h [71, 72] . Subsequently, the solids are separated from the mixture solution through the filtration process. The collected solid particles are washed several times with distilled water and then subjected to a calcination process in the temperature range of 600-700 °C for 6-8 h. The resultant is usually termed as biochar-supported TiO2 nanocomposite particles [73] . The ultrasound method is similar to the sol-gel method with the addition of an extra process of ultrasonication. The sonication of the pristine biochar with TiO 2 in the organic aqueous solution is done to promote the impregnation of TiO 2 nanoparticles into the pore of the porous biochar structure, which, upon calcination, reportedly provides a surface for TiO 2 crystal growth [78] . The detailed procedure of the synthesis of biochar-supported TiO 2 nanocomposite using the ultrasound method is illustrated in Figure 5B . Briefly, the biomass is converted to biochar through the pyrolysis process. The produced biochar after the crushing and sieving process is mixed with the Titanium isopropoxide and 2-propanol solution in a certain weight-by-volume ratio, and then, the mixture is subjected to the ultrasonication process for around 1-2 h. The ultrasonication of biochar and Titanium isopropoxide is done to break the biochar particles to nanoscale and to produce cracks on its surface, in which, subsequently, the TiO 2 nanoparticles are reportedly embedded [76] . The TiO 2 -embedded biochar nanoparticles are then calcinated in the temperature range of 500-700 • to start the nucleation of TiO 2 crystals within the cracks present in the biochar particles to produce a biochar-supported TiO 2 nanocomposite material. The thermal polycondensation process is also known as the single-step heating process to produce biochar-supported TiO 2 nanoparticles, as illustrated in Figure 5C [79, 80] . In this method, the biomass is initially mixed with some precursor such as melamine or polysaccharide agar to increase its thermal response during the calcination process. After that, the resultant biochar is mixed in a diluted ethanol solution containing titanium butyrate. The resulting solution mixture is oven-dried and then subjected to the calcination process under an ammonia gas environment to decrease the band energy gap and improve the visible light response of the biochar-supported TiO 2 nanocomposite during the photocatalysis process [76, 80] . Solvothermal is the combination of hydrothermal treatment and dry heating process that facilitates the growth of TiO 2 crystals onto the biochar's surface, as shown in Figure 5D . In this method, the biomass is dispersed into an ethanol solution containing titanium isopropoxide in different (w/w) ratios, such as 1:1 or 1:2, and then, the entire mixture containing biochar particles and titanium isopropoxide is subjected to a hydrothermal process in the temperature range of 160-175 • C for a duration of 12-14 h [71, 72] . Subsequently, the solids are separated from the mixture solution through the filtration process. The collected solid particles are washed several times with distilled water and then subjected to a calcination process in the temperature range of 600-700 • C for 6-8 h. The resultant is usually termed as biochar-supported TiO 2 nanocomposite particles [73] . Titanium dioxide is the most commonly used photocatalytic material reportedly being used for the photocatalytic degradation of pollutants in water under an advanced oxidation process (AOP). The pollutants are degraded by the charged radicals generated from TiO 2 when illuminated under light with a wavelength less than 400 nm, as shown in Figure 6a . However, the use of TiO 2 as a photocatalytic material for the oxidation/reduction of pollutants has certain limitations, such as a narrow photocatalytic activity region (λ < 400 nm), i.e., the very limited photocatalytic activity of the materials within the wavelength of the visible range (401-700 nm) (Figure 6b ), quick recombination of e − /h + pairs due to having large energy bandgap (~3.20 eV), very poor affinity towards organic pollutants, such as antibiotics, and the problem of agglomeration [74] . Hence, to overcome the limitations, the combination of the TiO 2 nanoparticles with a sustainable porous carbon material called Toxics 2021, 9, 313 9 of 20 "biochar" to produce biochar-supported TiO 2 nanocomposite for enhanced photocatalytic activities was mooted in the earlier studies [75, 76] . from TiO2 when illuminated under light with a wavelength less than 400 nm, as shown in Figure 6a . However, the use of TiO2 as a photocatalytic material for the oxidation/reduction of pollutants has certain limitations, such as a narrow photocatalytic activity region (λ < 400 nm), i.e., the very limited photocatalytic activity of the materials within the wavelength of the visible range (401-700 nm) (Figure 6b ), quick recombination of e − /h + pairs due to having large energy bandgap (~3.20 eV), very poor affinity towards organic pollutants, such as antibiotics, and the problem of agglomeration [74] . Hence, to overcome the limitations, the combination of the TiO2 nanoparticles with a sustainable porous carbon material called "biochar" to produce biochar-supported TiO2 nanocomposite for enhanced photocatalytic activities was mooted in the earlier studies [75, 76] . The rationale behind the integration of biochar particles with TiO2 nanoparticles can be linked to the fact that the presence of biochar with TiO2 nanoparticles reportedly increased the adsorption of pollutants on the composite's surface, thereby increasing the photocatalytic degradation rates. Moreover, the biochar addition to the TiO2 nanoparticles reportedly increased the available electrons in the conduction band to generate charged oxygen and hydroxyl radicals through the reduction and oxidation process, respectively, due to the availability of free electrons on the biochar's surface [70] . The major changes observed after the integration of biochar with the TiO2 nanoparticles were the change in the morphological structure, UV-visible absorbance range, and mineralogical structures, as shown in Figures 7 and 8 . It can be observed from Figure 7 that the biochar has a porous carbon structure that, after integration with TiO2 particles, provided a nucleation site during the calcination process within the pores for the crystallization of TiO2 nanoparticles within the biochar's pore structure that can be seen in the form of granules on the biochar's surface [38] . Additionally, the diffraction peaks at 2θ angles of 25.3, 37.8, 48.1, and 54.1 in the biochar-supported TiO2 reportedly indicate the presence of anatase TiO2 within the biochar structure, which confirms the successful integration of TiO2 in the biochar structure [38] . Further, the peaks at the 2θ angles of 62.5 and 70° are reportedly due to the presence of carbonates and CaO in the biochar's structure [64] . The UV-visible absorbance The rationale behind the integration of biochar particles with TiO 2 nanoparticles can be linked to the fact that the presence of biochar with TiO 2 nanoparticles reportedly increased the adsorption of pollutants on the composite's surface, thereby increasing the photocatalytic degradation rates. Moreover, the biochar addition to the TiO 2 nanoparticles reportedly increased the available electrons in the conduction band to generate charged oxygen and hydroxyl radicals through the reduction and oxidation process, respectively, due to the availability of free electrons on the biochar's surface [70] . The major changes observed after the integration of biochar with the TiO 2 nanoparticles were the change in the morphological structure, UV-visible absorbance range, and mineralogical structures, as shown in Figures 7 and 8 . It can be observed from Figure 7 that the biochar has a porous carbon structure that, after integration with TiO 2 particles, provided a nucleation site during the calcination process within the pores for the crystallization of TiO 2 nanoparticles within the biochar's pore structure that can be seen in the form of granules on the biochar's surface [38] . Additionally, the diffraction peaks at 2θ angles of 25.3, 37.8, 48.1, and 54.1 in the biochar-supported TiO 2 reportedly indicate the presence of anatase TiO 2 within the biochar structure, which confirms the successful integration of TiO 2 in the biochar structure [38] . Further, the peaks at the 2θ angles of 62.5 and 70 • are reportedly due to the presence of carbonates and CaO in the biochar's structure [64] . The UV-visible absorbance (Figure 8a) showed that the TiO 2 did not show any absorbance in the visible range (λ = 400-700 nm) but showed an absorbance of 1.4 (A.U) within the UV range (λ = 200-400 nm). However, the UV-visible absorbance of biochar-supported TiO 2 showed a significant increase in the absorbance within both UV and visible light range unlike only in the UV range, as shown by the TiO 2 nanoparticles. Apart from that, by increasing the pyrolysis temperature of the biochar from 550 to 700 • C, the UV-visible range light absorbance in the biochar-supported TiO 2 nanocomposite was significantly increased due to an increase in the available free electrons in the biochar structure [78, 79] . The highresolution transmission electron microscopy (HRTEM) image of the biochar-supported TiO 2 nanocomposite reportedly showed the presence of anatase TiO 2 on the carpet-like biochar's surface [78] . The HRTEM image (Figure 8b ) confirmed the proper integration of TiO 2 particles within the biochar's structure. Thus, it can be observed that the integration of TiO 2 nanoparticles with the biochar's structure significantly changed the chemical characteristics of the resulting biochar-supported TiO 2 nanocomposite. This makes it an efficient photocatalytic material for the photocatalytic degradation of the pollutants in the aqueous solution by increasing the light absorbance range, decreasing the e − /h + recombination, reducing the band energy gap, and increasing the surface interaction of the pollutants with the nanocomposite surface, thereby increasing its photocatalytic activity. mission electron microscopy (HRTEM) image of the biochar-supported TiO2 nanocomposite reportedly showed the presence of anatase TiO2 on the carpet-like biochar's surface [78] . The HRTEM image (Figure 8b ) confirmed the proper integration of TiO2 particles within the biochar's structure. Thus, it can be observed that the integration of TiO2 nanoparticles with the biochar's structure significantly changed the chemical characteristics of the resulting biochar-supported TiO2 nanocomposite. This makes it an efficient photocatalytic material for the photocatalytic degradation of the pollutants in the aqueous solution by increasing the light absorbance range, decreasing the e -/h + recombination, reducing the band energy gap, and increasing the surface interaction of the pollutants with the nanocomposite surface, thereby increasing its photocatalytic activity. The removal of SMX using various techniques such as ozonation, reverse osmosis, membrane filtration, adsorption, biological treatments, and advanced oxidation has been mooted in the previous studies [61, [80] [81] [82] [83] [84] [85] . Among them, the advanced oxidation process is an emerging technique for the removal of the antibiotic from water due to the low cost of material synthesis, simple operation, and high efficiency of removal [86] . The removal efficiency of the wastewater containing SMX using the biochar-supported TiO2 and its The removal of SMX using various techniques such as ozonation, reverse osmosis, membrane filtration, adsorption, biological treatments, and advanced oxidation has been mooted in the previous studies [61, [80] [81] [82] [83] [84] [85] . Among them, the advanced oxidation process is an emerging technique for the removal of the antibiotic from water due to the low cost of material synthesis, simple operation, and high efficiency of removal [86] . The removal efficiency of the wastewater containing SMX using the biochar-supported TiO 2 and its comparison with respect to the only TiO 2 under UV light source, without any photocatalyst under UV light, and without any catalyst under simulated sunlight is shown in Figure 9 . It can be evinced from the figure that SMX degradation under simulated sunlight and UV light source without any addition of photocatalyst was very appreciable (20-50%) [87] . However, the removal efficiency of SMX with the addition of TiO 2 as a photocatalytic material under UV light illumination was increased to up to 60%. Furthermore, this removal efficiency was substantially increased to more than 90% when the solvent was mixed with biochar-supported TiO 2 composite photocatalytic material, indicating the higher photocatalytic activity of the biochar-TiO 2 composite compared to the only TiO 2 particles. Moreover, it can also be observed that the SMX was photo catalytically removed in the presence of COD in the solvent, whose removal percentage was also reportedly increased from 42 to 60% with the addition of biochar-TiO 2 compared to the singularly applied TiO 2 particles. Thus, the above result suggested that the removal efficiency of SMX was not compromised due to the presence of other organic and inorganic pollutants under photocatalytic degradation. In Table 1 , the data related to the photocatalytic removal of SMX from the water using the biochar-TiO2 composite, TiO2-CNT composite, and other TiO2 nanocomposites are given. It can be observed from the table that among all the listed TiO2 composites, the maximum removal efficiency of SMX from the water was shown by the biochar-TiO2 composite (91.27%) produced using the sol-gel method under the UV range (200-400 nm), followed by ZnO-TiO2 biochar composite (81.21%) and the multiwalled carbon nanotube (MWCNT)/TiO2 composite (90%). The reduced graphene oxide (RGO)/TiO2 showed a removal efficiency of 77.27% for the SMX removal from water or aqueous solution. Apart from the above-mentioned TiO2 composites, all the other forms of TiO2 composites, such as Cu-TiO2, clay-TiO2, and TiO2-borosilicate composites, reportedly showed a relatively lower SMX removal efficiency in water or aqueous solution (70-80%, Table 1 ). Moreover, it can also be observed that the photocatalytic removal efficiency of SMX using biochar/TiO2 was significantly (p < 0.05) decreased from 91.27 to 40.58% with the increase in the pH of the aqueous solution from 4 to 10.77. The decrease in the photocatalytic removal efficiency of SMX using the biochar/TiO2 composite with the increase in the pH of the aqueous solution can be linked to the pKa values of the SMX and biochar/TiO2 composite. The SMX reportedly has two pKa values (pKa = 1.7 and pKa = 5.6), which suggests that the SMX remained in the cationic form if the pH of the solution is less than 1.7 and in the In Table 1 , the data related to the photocatalytic removal of SMX from the water using the biochar-TiO 2 composite, TiO 2 -CNT composite, and other TiO 2 nanocomposites are given. It can be observed from the table that among all the listed TiO 2 composites, the maximum removal efficiency of SMX from the water was shown by the biochar-TiO 2 composite (91.27%) produced using the sol-gel method under the UV range (200-400 nm), followed by ZnO-TiO 2 biochar composite (81.21%) and the multiwalled carbon nanotube (MWCNT)/TiO 2 composite (90%). The reduced graphene oxide (RGO)/TiO 2 showed a removal efficiency of 77.27% for the SMX removal from water or aqueous solution. Apart from the above-mentioned TiO 2 composites, all the other forms of TiO 2 composites, such as Cu-TiO 2 , clay-TiO 2 , and TiO 2 -borosilicate composites, reportedly showed a relatively lower SMX removal efficiency in water or aqueous solution (70-80%, Table 1 ). Moreover, it can also be observed that the photocatalytic removal efficiency of SMX using biochar/TiO 2 was significantly (p < 0.05) decreased from 91.27 to 40.58% with the increase in the pH of the aqueous solution from 4 to 10.77. The decrease in the photocatalytic removal efficiency of SMX using the biochar/TiO 2 composite with the increase in the pH of the aqueous solution can be linked to the pKa values of the SMX and biochar/TiO 2 composite. The SMX reportedly has two pKa values (pKa = 1.7 and pKa = 5.6), which suggests that the SMX remained in the cationic form if the pH of the solution is less than 1.7 and in the anionic form if the pH > 5.6 units [89] . Additionally, the pKa value of the biochar/TiO 2 composite was 6.1, indicating that the surface of biochar/TiO 2 composite remained positively charged if the pH of the solution remained below 6.1; otherwise, it was negatively charged [90] . Hence, in the acidic pH condition (pH = 4), the biochar/TiO 2 surface remained positively charged, which might have electrostatically attracted the negatively charged structure of SMX on its surface for adsorption. After adsorption of the SMX on the biochar/TiO 2 surface, the SMX is reportedly degraded by the •OH radical produced via photocatalysis of the biochar/TiO 2 composite. The integration of biochar as a supportive material with the TiO 2 reportedly helps the photocatalytic degradation of organic pollutants in two ways: firstly, by providing the adsorption sites on its porous surface due to the availability of pores and high specific surface area, and secondly, having the ability to prevent the recombination of e − and h + pair due to having an abundance of π-electrons and low energy bandgap that eventually promotes the generation of •OH from the catalyst [91] . The detailed mechanism of SMX photocatalytic degradation in the aqueous solution is illustrated in Figure 9 . The biochar/TiO 2 photocatalytic composite reportedly photogenerates a h + and e − pair upon incidence with high photon energy that is sufficient enough to excite the h + and e − pair from the valance to conduction band. The photogenerated h + is freely available on the surface of TiO 2 , which, upon reaction with H 2 O, reportedly produces •OH radical [92] . Similarly, the freely available e − in the conduction band of TiO 2 reportedly reacts with O 2 to generate O 2 − [93, 94] . The detailed reactions to produce •OH and O 2 − are given in Equations (1)-(6) [88] . Both of the radicals, i.e., OH and O 2 − , reportedly have a very strong ability to oxidize the SMX and its intermediates to some inorganic forms [88] . The chemical reactions depicting the photocatalytic generation of •OH and O 2 − are given in Equations (1)-(6) as follows [77] : The generated •OH and O 2 − radicals oxidize the SMX in the aqueous solution through three different pathways: hydroxylation, the opening of the isoxazole ring, and cleavage of the S-N bond [87] . Several intermediates produced during the photochemical degradation of SMX in water through •OH and O 2 − radicals have been identified using HPLC chromatogram in a previous study [88] . During the hydroxylation process, the hydroxyl radical •OH reportedly attacks the benzene ring, isoxazole ring, and the amine group in the SMX. The detailed mechanism of the photochemical degradation of SMX in water or aqueous solution is illustrated in Figure 10 . From the figure, it can be observed that the SMX, upon oxidation by the hydroxyl radical (•OH), deteriorates in three different ways. First is the hydroxylation process, in which a hydroxyl group is attached to the carbon ring, the isoxazole ring, and relaces the amine group in the carbon ring, leading to the formation of three intermediates C1, C2, and C3 with m/z values of 269.81 and 254.81, respectively. The intermediate C1 upon further oxidation by the •OH leads to the formation of a stable product denoted by C5 with an m/z value of 227.95. Moreover, the further oxidation of C2 and C3 intermediates leads to the attachment of the oxygen group in the isoxazole ring, resulting in the formation of another two intermediates, namely C4 and C5 with m/z values of 287.33 and 269.82, respectively. These intermediates (C4 and C5) upon further oxidation by •OH radical reportedly cause the cleavage of the isoxazole ring from the carbon ring attached through the link of the sulphate group, resulting in the formation of stable end products denoted as C7 and C8 with m/z values of 174.83 and 144.84, respectively [88] . Besides this, there are two more ways through which the SMX oxidizes to the stable end products. Firstly, through the cleavage of S-N bond in the SMX due to oxidation by •OH radical that leads to the formation of end-product denoted by C9 with an m/z value of 99.20. O2 -+ H2O → •OH2 + O2 - •OH2 + H2O + e -→ H2O2 + OH - The generated •OH and O2 -radicals oxidize the SMX in the aqueous solution through three different pathways: hydroxylation, the opening of the isoxazole ring, and cleavage of the S-N bond [87] . Several intermediates produced during the photochemical degradation of SMX in water through •OH and O2 -radicals have been identified using HPLC chromatogram in a previous study [88] . During the hydroxylation process, the hydroxyl radical •OH reportedly attacks the benzene ring, isoxazole ring, and the amine group in the SMX. The detailed mechanism of the photochemical degradation of SMX in water or aqueous solution is illustrated in Figure 10 . From the figure, it can be observed that the SMX, upon oxidation by the hydroxyl radical (•OH), deteriorates in three different ways. First is the hydroxylation process, in which a hydroxyl group is attached to the carbon ring, the isoxazole ring, and relaces the amine group in the carbon ring, leading to the formation of three intermediates C1, C2, Besides this, a separate comparison has been discussed with respect to the synthesis techniques used for the synthesis of AC, biochar, reduced graphene oxide (rGO), and metal-doped TiO 2 based photocatalysts and the effect of the various synthesis methods on the surface area and removal efficiency of various antibiotics (Table 2 ). It can be observed from the table that various synthesis methods, such as sol-gel, solvothermal, ultrasound method, thermal treatment, and hydrothermal methods, were used to synthesize AC, biochar, and metal-doped TiO 2 photocatalysts. Among the reported methods, it was found that the AC-based TiO 2 composite developed through the sol-gel method showed the highest removal efficiency of antibiotics (Tetracycline), followed by the rGO/TiO 2 composite developed through the hydrothermal method. Subsequently, the BC/Zn/TiO 2 and BiOBr/BC composites developed through the solvothermal method have shown high antibiotic removal efficiency of 96.8 and 92%, respectively. Conversely, the least organic pollutant removal was shown by the BC-TiO 2 composite developed through the ultrasoundpromoted wet impregnation method. Moreover, an interesting result was observed that the photocatalytic degradation of antibiotics was not much influenced by the surface area of the photocatalyst; rather, it depends on the synthesis method, the doping material being utilized for the development of the photocatalyst, as well as the pore volume of the photocatalyst. As far as the synthesis cost is concerned concerning the efficiency of the photocatalysts, it is beyond the scope of the present work. However, based on the technical methods and efficiency of the processes, it can be said that the sol-gel and hydrothermal are the most efficient and suitable methods to synthesize nanoscale photocatalysts having very high efficiency for the degradation of antibiotics in water. In the current perspective, the following conclusions can be deduced from the review: (1) The use of a biochar-supported TiO 2 composite for the photocatalytic degradation of antibiotics is an attractive method due to its high efficiency and low cost of operation compared to the existing treatment processes. (2) The integration of biochar with the TiO 2 nanoparticles increased photocatalytic degradation of SMX by increasing its photocatalytic response in the UV-visible range (200-700 nm) and the interaction of SMX with the TiO 2 through the adsorption onto the biochar/TiO 2 composite interface. (3) The biochar-supported TiO 2 composite can remove up to more than 95% of SMX in the aqueous solution within the UV range and up to 75% efficiency in the visible range. (4) Unlike the doped photocatalyst, the biochar-supported TiO 2 nanoparticles degrade the sulfamethoxazole both by adsorption and photocatalysis process and could also be used for the photocatalytic degradation of other antibiotics. (5) The •OH free radical is the prime key component that degrades the sulfamethoxazole through the oxidation or reduction process. In the future, more studies focusing on the application of biochar-supported TiO 2 composites for the photocatalytic degradation of antibiotics in the natural water stream under sunlight irradiation are required. Moreover, future studies should pay more attention to enhancing the adsorption capacity of biochar by doping it with certain metal or non-metal elements to increase the adsorption of anionic antibiotics onto the biochar-TiO 2 surface to increase the photocatalytic degradation. Additionally, more studies are required focusing on the photocatalytic degradation of SMX using a biochar/TiO 2 composite in real water under open sunlight as very limited studies are available delineating the photocatalytic degradation mechanism of SMX using the biochar/TiO 2 composite. Multi-criteria decision-making methods to address water allocation problems: A systematic review Potential Impacts of Climate and Land Use Change on the Water Quality of Ganga River around the Industrialized Kanpur Region Assessment of the groundwater suitability for irrigation near Al Kufa City and preparing the final water quality maps using spatial distribution tools Environmental side effects of the injudicious use of antimicrobials in the era of COVID-19 Antibiotics and antimicrobial resistance in the COVID-19 era: Perspective from resource-limited settings A survey of sub-inhibitory concentrations of antibiotics in the environment Chemical Fate and Partitioning Behaviour of Antibiotics in the Aquatic Environment-A Review First insight into the occurrence, spatial distribution, sources, and risks assessment of antibiotics in groundwater from major urban-rural settings of Pakistan Typical antibiotics in the receiving rivers of direct-discharge sources of sewage across Shanghai: Occurrence and source analysis Sulfamethoxazole biodegradation and biotransformation in the water-sediment system of a natural river Sorption-Desorption Behavior of Atrazine in Soils Irrigated with Reclaimed Wastewater Cellular toxicity of sulfamethoxazole reactive metabolites-I. Inhibition of intracellular esterase activity prior to cell death Identification and determination of metabolites and degradation products of sulfonamide antibiotics Occurrence and fate of antibiotics in the Seine River in various hydrological conditions Trends in antibiotic resistance genes occurrence in the Haihe River Input of pharmaceuticals through coastal surface watercourses into a Mediterranean lagoon Biodegradation and reversible inhibitory impact of sulfamethoxazole on the utilization of volatile fatty acids during anaerobic treatment of pharmaceutical industry wastewater Sulfamethoxazole, tetracycline and oxytetracycline and related antibiotic resistance genes in a large-scale landfill Enhancement of ionizing radiation-induced catalytic degradation of antibiotics using Fe/C nanomaterials derived from Fe-based MOFs Performance assessment of the combined treatment for oxytetracycline antibiotics removal by sonocatalysis and degradation using Pseudomonas aeruginosa Removal of sulfamethoxazole and trimethoprim from reclaimed water and the biodegradation mechanism Removal of sulfamethoxazole from water via activation of persulfate by Fe 3 C@NCNTs including mechanism of radical and nonradical process Removal of sulfamethoxazole and sulfapyridine by carbon nanotubes in fixed-bed columns Potential risks from UV/H 2 O 2 oxidation and UV photocatalysis: A review of toxic, assimilable, and sensory-unpleasant transformation products Contaminants of emerging concern: A review of new approach in AOP technologies Photocatalytic degradation of sulfamethoxazole by hierarchical magnetic ZnO@g-C 3 N 4 : RSM optimization, kinetic study, reaction pathway and toxicity evaluation Photocatalytic degradation of sulfamethoxazole in aqueous suspension of TiO 2 Photocatalytic oxidation of sulfamethoxazole in the presence of TiO 2 : Effect of matrix in aqueous solution on decomposition mechanisms Photocatalytic degradation of amoxicillin, ampicillin and cloxacillin antibiotics in aqueous solution using UV/TiO 2 and UV/H 2 O 2 /TiO 2 photocatalysis An overview on limitations of TiO 2 -based particles for photocatalytic degradation of organic pollutants and the corresponding countermeasures Development of modified N doped TiO 2 photocatalyst with metals, nonmetals and metal oxides Microporous and Mesoporous Materials The study of Iron (III) and nitrogen co-doped mesoporous TiO 2 photocatalysts: Synthesis, characterization and activity Synthesis and characterization of Ag-TiO 2 -CNT nanoparticle composites with high photocatalytic activity under artificial light Toxicology of nanoparticles of ZnO, CuO and TiO 2 to yeast Saccharomyces cerevisiae Photocatalytic degradation of methyl orange by Ag/TiO 2 /biochar composite catalysts in aqueous solutions Influence of temperature and duration of pyrolysis on the property heterogeneity of rice straw biochar and optimization of pyrolysis conditions for its application in soils Biochar as an Electron Shuttle between Bacteria and Fe (III) Minerals Heterogeneous photocatalytic degradation of sulfamethoxazole in water using a biochar-supported TiO 2 photocatalyst Promoting charge separation of biochar-based Zn-TiO 2 /pBC in the presence of ZnO for efficient sulfamethoxazole photodegradation under visible light irradiation Oxidation of sulfamethoxazole by rice husk biocharactivated persulfate. Catalysts Enhanced degradation of sulfamethoxazole (SMX) in toilet wastewater by photo-fenton reactive membrane filtration Enhanced degradation of sulfonamide antibiotics by UV irradiation combined with persulfate Photocatalytic ZnO-assisted degradation of spiramycin in urban wastewater: Degradation kinetics and toxicity Synthesis of a Novel Photocatalyst MVO 4 /g-C 3 N 4 (M = La, Gd) with Better Photocatalytic Activity for Tetracycline Hydrochloride Degradation under Visible-Light Irradiation Antibiotics in surface water of East and Southeast Asian countries: A focused review on contamination status, pollution sources, potential risks, and future perspectives Residues of selected antibiotics in water and mud from shrimp ponds in mangrove areas in Viet Nam Ubiquitous occurrence of sulfonamides in tropical Asian waters Occurrence and risk assessment of multiple classes of antibiotics in urban canals and lakes in Hanoi Occurrence and distribution of pharmaceuticals in wastewater from households, livestock farms, hospitals and pharmaceutical manufactures Occurrence and Removal of Veterinary Antibiotics in Livestock Wastewater Treatment Plants Antibiotics in wastewater of a rural and an urban hospital before and after wastewater treatment, and the relationship with antibiotic use-a one year study from Vietnam Occurrence and sources of antibiotics and their metabolites in river water, WWTPs, and swine wastewater in Jiulongjiang River basin, south Relationships between Antibiotics and Antibiotic Resistance Gene Levels in Municipal Solid Waste Leachates in Shanghai Antibiotics in wastewater from multiple sources and surface water of the Yangtze River in Chongqing in China Investigation of antibiotics in health care wastewater in Ho Chi Alder, A.C. Occurrence, fate and antibiotic resistance of fluoroquinolone antibacterials in hospital wastewaters in Hanoi Occurrence of antibiotic residues and antibiotic-resistant bacteria in effluents of pharmaceutical manufacturers and other sources around Hanoi Sulfamethoxazole contamination of a deep phreatic aquifer Adsorption characteristics of sulfamethoxazole and metronidazole on activated carbon Study of the toxicity of sulfamethoxazole and its degradation products in water by a Thaibioluminescence method during application of the electro-Fenton treatment A review on contamination and removal of sulfamethoxazole from aqueous solution using cleaner techniques: Present and future perspective Hydrolysis of sulphonamides in aqueous solutions Occurrence and Sorption Behavior of Sulfonamides, Macrolides, and Trimethoprim in Activated Sludge Treatment Photocatalytic degradation of sulfamethoxazole in aqueous solution using a floating TiO 2 -expanded perlite photocatalyst Environmental Science Water Research & Technology supported Mg(OH) 2 /bentonite composite Recent developments in titanium oxide-based photocatalysts Physicochemical and Engineering Aspects Preparation of graphene-TiO 2 composite by hydrothermal method from peroxotitanium acid and its photocatalytic properties Photocatalytic degradation of an azo-dye on TiO 2 /activated carbon composite material Enhanced visible-light photocatalytic activity of copper-doped titanium oxide-zinc oxide heterojunction for methyl orange degradation A novel TiO 2 /biochar composite catalysts for photocatalytic degradation of methyl orange Nanocrystalline carbon-TiO 2 hybrid hollow spheres as possible electrodes for solar cells General Selective phenol hydrogenation in aqueous phase on Pd-based catalysts supported on hybrid TiO 2 -carbon materials Recent progress in biochar-supported photocatalysts: Synthesis, role of biochar, and applications Preparation of visible light-activated titania photocatalyst by mechanochemical method Sewage sludge-derived TiO 2 /Fe/Fe 3 C-biochar composite as an efficient heterogeneous catalyst for degradation of methylene blue Preparation of TiO 2 supported on MDF biochar for simultaneous removal of methylene blue by adsorption and photocatalysis A Comparative Evaluation of TiO 2 Suspension Coating Techniques: A Novel Technique to Achieve Optimal Thickness and Uniformity of Photocatalytic Film Dual functionality of TiO 2 /biochar hybrid materials: Photocatalytic phenol degradation in liquid phase and selective oxidation of methanol in gas phase Effect of feedstock and pyrolysis temperature on properties of biochar governing end-use efficacy Synthesis of a novel core-shell-structure activated carbon material and its application in sulfamethoxazole adsorption The effects of activated carbon surface features on the reactive adsorption of carbamazepine and sulfamethoxazole Removal of ronidazole and sulfamethoxazole from water solutions by adsorption on granular activated carbon: Equilibrium and intraparticle diffusion mechanisms Adsorption characteristics of diclofenac and sulfamethoxazole to graphene oxide in aqueous solution A comparative adsorption study of sulfamethoxazole onto graphene and graphene oxide nanosheets through equilibrium, kinetic and thermodynamic modelling Ultra-high adsorption of tetracycline antibiotics on garlic skin-derived porous biomass carbon with high surface area Advanced Oxidation Processes for the Removal of Antibiotics from Water. An Overview Determination and toxicity evaluation of the generated products in sulfamethoxazole degradation by UV/CoFe 2 O 4 /TiO 2 TiO 2 supported on reed straw biochar as an adsorptive and photocatalytic composite for the efficient degradation of sulfamethoxazole in aqueous matrices A new method to determine the generation of hydroxyl radicals in illuminated TiO 2 suspensions Enhancement of photocatalytic activity of TiO 2 by immobilization on activated carbon for degradation of pharmaceuticals Photoinduced decomposition of nitrate in drinking water in the presence of titania and humic acids Sonocatalytic degradation of ciprofloxacin using synthesized TiO 2 nanoparticles on montmorillonite Comparative study of diethyl phthalate degradation by UV/H 2 O 2 and UV/TiO 2 : Kinetics, mechanism, and effects of operational parameters Novel anti-fouling Fe 2 O 3 /TiO 2 nanowire membranes for humic acid removal from water Reduced graphene oxide−TiO 2 /sodium alginate 3-dimensional structure aerogel for enhanced photocatalytic degradation of ibuprofen and sulfamethoxazole Novel Magnetic Carbon Nanotube-TiO 2 Composites for Solar Light Photocatalytic Degradation of Pharmaceuticals in the Presence of Natural Organic Matter Solar-active clay-TiO 2 nanocomposites prepared via biomass assisted synthesis: Efficient removal of ampicillin, sulfamethoxazole and artemether from water Photocatalytic degradation of a mixture of eight antibiotics using Cu-modified TiO 2 photocatalysts: Kinetics, mineralization, antimicrobial activity elimination and disinfection Sulfamethoxazole Removal in Membrane-Photocatalytic Reactor System-Experimentation and Modelling Sulfamethoxazole photocatalytic degradation in a continuous flow reactor using artificial radiation Enhanced removal of sulfamethoxazole by a novel composite of TiO 2 nanocrystals in situ wrapped-Bi 2 O 4 microrods under simulated solar irradiation Sol-gel synthesis of new TiO 2 /activated carbon photocatalyst and its application for degradation of tetracycline Effect of activating agent on the properties of TiO 2 /activated carbon heterostructures for solar photocatalytic degradation of acetaminophen Biomass Assisted Synthesis of 3D Hierarchical Structure BiOX(X Cl, Br)-(CMC) with Enhanced Photocatalytic Activity Biochar-TiO 2 magnetic nanocomposites for photocatalytic solar-driven removal of antibiotics from aquaculture effluents Removal of antibiotics, antibiotic-resistant bacteria and their associated genes by graphene-based TiO 2 composite photocatalysts under solar radiation in urban wastewaters Bismuth impregnated biochar for efficient estrone degradation: The synergistic effect between biochar and Bi/Bi 2 O 3 for a high photocatalytic performance Novel BiOBr by compositing low-cost biochar for efficient ciprofloxacin removal: The synergy of adsorption and photocatalysis on the degradation kinetics and mechanism insight Construction of novel biochar supported copper tungstate nanocomposites: A fruitful divergent catalyst for photocatalysis and electrocatalysis Data Availability Statement: Not applicable. The authors declare no conflict of interest.