key: cord-0684208-9xzwebiw
authors: Wang, Yong; Zhou, Youting; Chen, Yangjie; Yin, Zhihang; Hao, Juan; Li, Huiming; Liu, Kunping
title: Simple and sensitive nitric oxide biosensor based on the electrocatalysis of horseradish peroxidase on AuNPs@metal–organic framework composite-modified electrode
date: 2022-03-29
journal: Mikrochim Acta
DOI: 10.1007/s00604-022-05268-8
sha: d4fb6f551077ca39845c96c6b37bd9ad67fab2ec
doc_id: 684208
cord_uid: 9xzwebiw

Fe-based metal–organic framework (MIL-101(Fe)) was synthesized through a simple solvothermal synthesis and then used to prepare the AuNPs-decorated MIL-101(Fe) nanocomposite (APPPM(Fe)) by a multi-step layer-by-layer assembly process. Benefited from the porous structure of MIL-101(Fe) and the multilayer assemble process, the loading amount of AuNPs on APPPM(Fe) was enhanced and exhibited a fine biocompatible interface and high conductivity. Through the intense Au–S bond, high loading amount of horseradish peroxidase was immobilized on APPPM(Fe) and the native bioactivity of HRP was kept to realize its direct electrochemistry. From the electrochemical kinetics, the constructed biosensor displayed fast electron transfer and good electrocatalysis activity for the detection of nitric oxide (NO) with wide linear range from 0.033 to 5370 μM and a low detection limit of 0.01 μM (3 σ) as well as fine stability, reproducibility and specificity. According to results of real sample analysis, the proposed electrochemical biosensor offers fast and simple detection of NO in real serum. Therefore, the present strategy definitely provided a potential application prospect in NO clinic detection and disease therapy. GRAPHICAL ABSTRACT: [Image: see text] SUPPLEMENTARY INFORMATION: The online version contains supplementary material available at 10.1007/s00604-022-05268-8.

Nitric oxide (NO) is one of the important signaling molecules in all vertebrates, which can adjust neural activity and blood flow [1] . A series of diseases and multisystem symptoms were caused or affected by NO production or signal transduction disorders which often exhibited an abnormal NO level [2, 3] . Hence, it was an effective way to understand the disease process status through monitoring the NO level of patient. On the other hand, some NO-based therapy strategy had been gradually trying to apply in disease treatment based on the dynamic change characteristics of NO such as organic nitrate, sodium nitrate and inhaled nitric oxide (iNO) which had been used for the heart failure, pulmonary hypertension and COVID-19 [4] [5] [6] [7] [8] [9] [10] . In this situation, patient NO level monitor also was necessary for control the dosage of NO donor drugs because the exceeded NO will affect and even harm human body [11] . Therefore, it is necessary to develop a class of detection methods with high sensitivity, wide linear range and low detection limit for the detection of NO.

In the past decades, multiple analytical techniques have been developed for qualitative and quantitative analysis of NO or its derived oxides, for instance, high-performance liquid chromatography (HPLC) [12, 13] , gas chromatography-mass spectrometry (GC-MS) [14, 15] and spectrophotometry [16] [17] [18] . However, these methods still presented several shortcomings, including complex sample pretreatment, time-consuming, high detection limit and complex operation. As a comparison, the electrochemical sensor is a supplementary analysis tool for NO detection because of the simplicity, rapidity, high sensitivity, high selectivity and real-time monitoring. Moreover, combined with the good property of nanomaterial and fine specificity of biological enzyme, nanomaterial-based electrochemical biosensor had got more attentions and achieved more applications for the highly sensitive detection of target [19] [20] [21] [22] . Metal-organic frameworks (MOFs) are a new class crystalline porous nanomaterial with regular three-dimensional framework. Due to their novel properties such as high surface area, ordered porosity, low density and tunable structures, they had got more attention in separation, gas storage, heterocatalysis, sensing and drug delivery [23, 24] . Benefited from the porous structure of MOFs, more active metal nanoparticles could be loaded on the surface of MOFs which could improve the conductivity of MOFs and immobilized the biological enzyme to keep its native activity; hence, MOFs may be a fine substrate of electrochemical biosensor for sensitive NO detection [25] [26] [27] [28] [29] .

Herein, a simple and sensitive MOFs-based biosensing strategy was raised for the NO detection based on the electrocatalysis of horseradish peroxidase (HRP) (Scheme 1). In the strategy, Fe-based MOFs (MIL-101(Fe)) were synthesized through a simple solvothermal synthesis. After a multi-step layer-by-layer assembly process, AuNPs/PDDA/ PSS/PEI/MIL-101(Fe) (APPPM(Fe)), a AuNPs-decorated MIL-101(Fe) nanocomposite, was achieved and then used for the immobilization of HRP through the intense Au-S bond. Benefited from the multilayer assemble process, the loading amount of AuNPs and HRP on MIL-101(Fe) was enhanced and can provide a fine biocompatible interface and high conductivity of APPPM(Fe) which could keep native bioactivity of HRP, and the constructed biosensor (HRP/ APPPM(Fe)/GCE) displayed fast electron transfer and good electrocatalysis activity for the detection of NO with wide linear range and low detection limit as well as fine stability, reproducibility and specificity. Therefore, this work opened a new way for the clinical applications of MOFs in electrochemical biosensors.

Terephthalic acid (H 2 BDC, 99.0%) was purchased from Shanghai Titan Scientific Co., Ltd (Shanghai, China). Polyethylenimine (PEI, branched, Mw = 25,000), poly (sodium 4-styrenesulfonate) solution (PSS, 30 wt% in H 2 O, Mw = 70,000), poly (diallyldimethylammonium chloride) (PDDA, Mw = 200,000-350,000, 20 wt% in H 2 O), HAuCl 4 ·3H 2 O, L-ascorbic acid, 3-hydroxytyramine and uric acid were purchased from Sigma-Aldrich (Shanghai, China). NaNO 2 , glucose, citric acid, L-cysteine, FeCl 3 ·6H 2 O, MgSO 4 and NaNO 3 were purchased from Chengdu Kelong Co., Ltd (Chengdu, China). Horseradish peroxidase (HRP) was provided by Sangon Biotech Co., Ltd (Shanghai, China). All reagents were used without further purification, and experimental water was ultra-pure water with a resistance of 18.2 MΩ cm by a Milli Q system. The preparation of AuNPs was based on a previous method listed in the literature [30] .

Electrochemical measurements were performed on a CHI660 workstation (Shanghai Chenhua, China) with a conventional three-electrode system comprised of a platinum Scheme 1 Schematic representations of the preparation of APPPM(Fe) and the construction of the nitric oxide biosensor wire employed as the counter electrode, a saturated calomel electrode (SCE) as the reference electrode and a modified glassy carbon electrode (GCE) as the working electrode. Scanning electron microscopy (SEM, Thermo scientific Apreo 2C, America), Fourier transform infrared spectrometer (FT-IR, Nicolet iS10, Thermo Fisher, America) and UV-visible spectrophotometer (Shimadzu, Suzhou, China) were performed to characterize the nanomaterials.

The preparation of MIL-101(Fe) was based on the previous literature [31] . Next, 400 μL of PEI (20.0 mg mL −1 ) aqueous solution was added to 2.0 mL of as-prepared MIL-101(Fe) (3.0 mg mL −1 ). After shaking for 30 min, centrifugation with 10,000 rpm and three times of water washing were performed to separate the PEI functionalized MIL-101(Fe) (PEI/MIL-101(Fe)). Subsequently, 5 mg of PEI/MIL-101(Fe) was added into 3.0 mL PSS (w/v 0.5%) solution and shaken for 30 min. After centrifugation at 10,000 rpm for 10 min and washing with water, the obtained PSS/PEI/ MIL-101(Fe) was added into another 3.0 mL PDDA (w/v 0.5%) solution and then shaken for 30 min. By the similar centrifugation and water washing process, the PDDA/PSS/ PEI/MIL-101(Fe) was achieved. Next, the as-prepared electropositive PDDA/PSS/PEI/MIL-101(Fe) was transferred to 3.0 mL AuNPs solution followed with a 30-min shaking. After centrifugation and three times of water washing, the APPPM(Fe) composite was collected and re-dispersed in ultrapure water and stored in 4 °C for future use.

The GCE was first polished with 1.0, 0.3 and 0.05 μm alumina slurry successively, followed by ultrasonication thoroughly with ultrapure water and drying with nitrogen to get a mirror-like surface. Thereafter, 5.0 μL of the APPPM(Fe) (1.0 mg·mL −1 ) suspension was dropped onto the pre-treated GCE surface and dried naturally at room temperature. Finally, the electrode was immersed in 50 μL HRP (5.0 mg·mL −1 ) solution and stored at 4 °C for overnight to obtain the HRP/APPPM(Fe)/GCE-modified electrode. Before the as-prepared HRP/APPPM(Fe)/GCE biosensor was used for the detection, the modified electrode was rinsed with 1.0 mL of 0.10 M PBS (pH 7.4) for three times to remove loosely adsorbed HRP on the electrode surface.

All solutions for electrochemical analysis were N 2 -saturated, and we keep the N 2 atmosphere in whole measurement process. The direct electrochemistry of HRP/APPPM(Fe)/GCE was performed in 0.10 M PBS pH 7.4 by cyclic voltammetry (CV) in the potential range from -0.8 to 0.2 V. Moreover, the electrocatalysis of HRP/APPPM(Fe)/GCE electrodes to NO that comes from the disproportionation reaction of NaNO 2 was performed in 0.10 M pH 2.0 NaAc-HAc buffer solution in the potential range from -1.0 to 0.2 V with the scan rate of 0.1 V s −1 . For amperometric measurement (i-t curve), the potential parameters were set as -0.630 V and the sensitivity of method was set as 10 -6 . For real sample detection, 5.0 mL of 0.10 M pH 2.0 NaAc-HAc buffer solution was firstly added in a 10 mL electrolysis cell and purging by nitrogen under magnetic stirring. Meanwhile, the i-t curve electrochemical method was started to run to record the i-t curve until the i-t curve was steady to be a horizontal line and keeping 10 min. Then, 5 μL of the real sample was quickly added in the electrolysis cell. Finally, the current changing value in i-t curve after the adding of real sample was recorded to compute the NO concentration in real sample.

Characterization Different tools were used to characterize the morphology and composition of MIL-101(Fe). As can be seen from SEM image in Fig. 1A , MIL-101(Fe) presented a regular octahedron shape with relatively rough surface. From the EDS mapping of MIL-101(Fe) in Fig. 1B , the mean elements of MIL-101(Fe) were C, O and Fe with wt% of 63.19, 23.49 and 13.32, respectively. Moreover, according to the particle size distribution (measured from multiple SEM images) shown in the inset of Fig. 1B , the particle sizes of MIL-101(Fe) were mainly distributed in the range of 500-1100 nm. In addition, the XRD pattern of MIL-101(Fe) was also investigated as shown in Fig. 1C , and the main diffraction peaks were presented at 9.36°, 12.54°, 16.52°, 18.8° and 21.88° which revealed the successful formation of highly crystal MIL-101(Fe) and was corresponded to the previous study [32] . From the FT-IR of MIL-101(Fe) in Fig. 1D , the two strong absorption peaks at 1660 cm −1 and 1391 cm −1 indicated the existence of carboxyl group of H 2 DBC. The characteristic peaks at 1598 cm −1 and 1502 cm −1 were corresponded to the C = C skeleton vibration of the benzene ring and 749 cm −1 was contributed to the bending vibration peak of the C-H. More importantly, the peak at 554 cm −1 could be assigned to the absorption of Fe-O which also proved the success preparation of MIL-101(Fe) [33] .

To improve the conductivity of the nanomaterial and immobilize the HRP molecular to keep the native bioactivity, MIL-101(Fe) was modified with PEI, PSS and PDDA successively through a multi-step layer-by-layer assemble procedure and then decorated AuNPs on its surface to obtain the APPPM(Fe) composite. The assemble process of APPPM(Fe) was characterized by zeta potential, and the result was listed in Fig. S1 . It could be seen that the zeta potential of MIL-101(Fe) was 25.8 mV. After modified with PEI, the zeta potential of PEI/MIL-101(Fe) was increased to 37.7 mV due to the highly positive electricity of PEI. When negative PSS was warped on the surface of PEI/MIL-101(Fe), the zeta potential of PSS/PEI/MIL-101(Fe) changed to -35.8 mV. Then, followed with the modification of positive PDDA on the surface of PSS/PEI/ MIL-101(Fe), the zeta potential of PDDA/PSS/PEI/MIL-101(Fe) reversed to 33.0 mV due to the intense positive electricity. Finally, after the assemble of negative AuNPs on the surface of PDDA/PSS/PEI/MIL-101(Fe), the zeta potential of the obtained APPPM(Fe) changed to -4.9 mV. Thus, it was convinced that the assemble process was successful and AuNPs had been successfully decorated on PDDA/PSS/PEI/MIL-101(Fe) according to the above zeta potential characterization. From the SEM image of AuNPs@MIL-101(Fe) shown in Fig. 2A and inset, a large number of AuNPs were attached to the surface of MIL-101(Fe) without aggregation. Moreover, UV-Vis was also used to reflect the self-assemble process as shown in Fig. 2B . It could be seen that MIL-101(Fe) exhibited a strong and wide absorption band in the range of 220-500 nm. The absorption peaks at 247 nm and 396 nm with a slightly broad band were attributed to the characteristic absorption caused by ligand-to-metal charge transfer (LMCT) of O (II) → Fe (III), which confirmed the bonding of carboxylate oxygen to metal ion (curve a) [34] [35] [36] . And the characteristic absorption peak of AuNPs emerged at 518 nm caused by the surface plasma resonance (curve b). After the assemble of AuNPs on the MIL-101(Fe), the characteristic absorption peaks of MIL-101(Fe) and AuNPs were red-shifted to 435 and 558 nm, respectively (curve c), which was also the obvious evidence for the success of self-assemble process.

CV was employed to investigate the direct electrochemistry of HRP/APPPM(Fe)-modified electrode in 0.10 M pH 7.4 PBS buffer with a scan rate of 0.1 V s −1 . As shown in Fig. 3 , no obvious redox peaks could be observed in bare GCE (curve a), MIL-101(Fe)/GCE (curve b) and APPPM(Fe)/GCE (curve c) in the potential window of -0.8-0.2 V. However, after HPR was immobilized on the surface of APPPM(Fe)/GCE electrode, a pair of stable, definite and reversible redox peaks at -0.415 V and -0.350 V were observed (curve d). Moreover, the potential difference (△Ep), an important parameter equal to the difference between the reduction peak and oxidation peak, was calculated to be about 65 mV which confirmed a fast electron transfer process between HRP and the APPPM(Fe)/GCE-modified electrode. This result indicated that the APPPM(Fe) supplied a bio-compatible interface for the immobility of HRP to keep the native bioactivity of HRP.

In addition, the electrochemical kinetics was also investigated by scanning rate as shown in Fig. S2 which showed that the reaction process on the surface of this electrode belongs to the surface controlled quasi-reversible process. In accordance with Faraday's law, the surface concentration of electroactive HRP (Γ) at HRP/APPPM(Fe)/GCE was calculated according to the following equation [37, 38] :

where Ip is the reduction peak current, n is the number of electrons, A is the surface area of the electrode, v is the scan rate, and R, T and F are constants. The value of Γ was estimated to be 2.07×10 -10 mol cm −2 , which was much greater than the theoretical monolayer coverage of the HRP (1.89×10 -11 mol cm −2 ). This result hinted that HRP participated in the electron transfer process through multi-layer pattern on the AuNPs@MIL-101(Fe) composite film.

CV was applied to explore the electrocatalytic activity of HRP immobilized on the APPPM(Fe) nanocomposite for reduction of H 2 O 2 and nitric oxide. As could been in Fig. S3 , with addition of different concentrations of H 2 O 2 in 0.10 M pH 7.4 PBS buffer (curve a to g), HRP/APPPM(Fe)/GCE exhibited an increased cathode current response which indicated that HRP/APPPM(Fe)/GCE had fine electrocatalytic activity for H 2 O 2 . Moreover, the electrocatalytic activity of HRP/APPPM(Fe)/GCE to NO was also performed by adding of varying concentrations of NaNO 2 in 0.10 M pH 2.0 NaAc-HAc buffer as presented in Fig. 4A . When without any addition of NaNO 2 , only a pair of weak HRP redox peaks were observed at -0.150 and 0.210 V (curve a). However, when NaNO 2 was added in the acid buffer, NaNO 2 will experience a disproportionation reaction to release NO which could be catalyzed by the HRP on APPPM(Fe)/GCE and a well-defined cathode peak of NO at -0.630 V was emerged as well as the peak currents increased with the increase of NaNO 2 (curve b-d). Moreover, the electrocatalytic capacity of the APPPM(Fe)/GCE was also studied in 0.10 M pH 2.0 NaAc-HAc buffer containing NaNO 2 to compare with HRP/APPPM(Fe)/GCE. As shown in the inset of Fig. 4A , no any redox peaks were observed in the APPPM(Fe)/GCE which indicated that APPPM(Fe)/GCE had no electrocatalytic activity against NO (curve a). However, after the immobilization of HRP on APPPM(Fe), the obvious peak at -0.630 V proved the strong electrocatalytic ability of HRP/ APPPM(Fe)/GCE to NO (curve b).

As shown in Fig. 4B , the amperometric current-time curve was utilized to investigate the steady-state response of HRP/APPPM(Fe)/GCE with successive injection of NaNO 2 in a N 2 saturated NaAc-HAc buffer (0.10 M, pH 2.0) at an applied potential of -0.630 V. The calibration curve shown in the inset of Fig. 4B illustrated a good linear relationship between the amperometric response and NaNO 2 In addition, as listed in Table S1 compared with numerous typical nitrite detection methods reported in literatures, the traditional methods of HPLC and UV-Vis exhibited narrow linear range and high detection limit. For the spectrophotometry, it could achieve lower detection limit but still narrow linear range than HPLC. However, for electrochemical method, both detection limit and linear range were improved and achieved very good results. Compared with other amperometry, the as-prepared biosensor in this experiment displayed a higher sensitivity and wider linear range, which can be attributed to the large specific surface area of MIL-101(Fe) and the high biocompatible surface of APPPM(Fe) to immobilize HRP and keep its native bioactivity.

Stability, reproducibility and specificity were the important aspects for the performance evaluation of the modified electrode. Fig. S4 displayed the consecutive 50 cycle CV scan curves of HRP/APPPM(Fe)/GCE in 0.10 M pH 2.0 NaAc-HAc buffer containing 160 μM NaNO 2 . Results showed that the percentage ratio of peak current decreased only 6.55% after 50 cycle which hinted the excellent stability of the biosensor. The reproducibility of the biosensor was estimated by analysis five HRP/APPPM(Fe)/GCE in 0.10 M pH 2.0 NaAc-HAc buffer containing 400 μM NaNO 2 . Results indicated that the relative standard deviation (RSD) of the five current responses was 2.46% which proved the biosensor possessed a favorable reproducibility for NaNO 2 detection. For specificity, a series of interference, including ascorbic acid (100 μM), uric acid (100 μM), dopamine (100 μM), glucose (100 μM), citric acid (100 μM), L-cysteine (100 μM), MgSO 4 (100 μM), NaCl (100 μM) and NaNO 3 (100 μM), were selected to measure under same conditions and compared with NaNO 2 (10 μM). As shown in Fig. 5 , with an excess (tenfold) amount of the inferences, the biosensor response exhibited superior selectivity for NaNO 2 which was contributed to the selective catalysis of HRP to NO produced from the disproportionation reaction of NaNO 2 under acid environment. This result demonstrate that the as-prepared biosensor has a good selective for NaNO 2 and the series of interference coexisted in serum had no or 

The recovery experiment was carried out to evaluate the applied ability for real sample detection of the proposed biosensor. Three concentrations of 800, 1000 and 1200 μM of NaNO 2 standard solution were added into the undiluted serum sample (contained 82.3 μM of NO), respectively. Then 5 μL of above serum sample with standard addition was quickly added in the electrolysis cell which contained 5.0 mL of N 2 saturated 0.10 M pH 2.0 NaAc-HAc buffer solution and the i-t curve was measured using the proposed biosensor under the optimal condition. As listed in Table S2 , the three standard addition serum samples were measured three times and averaged, respectively. The recovery ranged from 91.1% to 105.7%, and the RSD was between 5.00% and 7.33%. Therefore, the constructed biosensor could be a good selection for NO detection in serum.

In conclusion, AuNPs-decorated metal-organic frameworks nanomaterial was successfully prepared and applied for HRP immobilization and biosensor construction. Due to the high conductivity and fine biocompatible interface which was beneficial to keep the native bioactivity of HRP, the proposed biosensor displayed a good electrocatalysis activity for the detection of NO with wide linear range and low detection limit as well as fine stability, reproducibility and specificity. According to the real sample analysis, the proposed electrochemical biosensor can realize the fast, simple detection of NO in real serum. Therefore, the present strategy definitely provided a potential application prospect in NO clinic detection and disease therapy.

The online version contains supplementary material available at https:// doi. org/ 10. 1007/ s00604-022-05268-8.

Revisiting the nitrite reductase activity of hemoglobin with differential pulse voltammetry

Sodium nitrite: The "cure" for nitric oxide insufficiency

Nitric oxide and cardiovascular and renal effects

Clinical use of inhaled nitric oxide: Local and systemic applications

Characterization of the role of nitric oxide and its clinical applications

Inhaled NO as a therapeutic agent

When to say no to inhaled nitric oxide in neonates?

Intensive care management of coronavirus disease 2019 (COVID-19): challenges and recommendations

Inhaled nitric oxide in mechanically ventilated patients with COVID-19

Inhaled high dose nitric oxide is a safe and effective respiratory treatment in spontaneous breathing hospitalized patients with COVID-19 pneumonia

Endothelial nitric oxide synthase activation is critical for vascular leakage during acute inflammation in vivo

Effective indirect enrichment and determination of nitrite ion in water and biological samples using ionic liquid-dispersive liquid-liquid microextraction combined with high-performance liquid chromatography

Analysis of nitrite and nitrate in biological samples using high-performance liquid chromatography

GC-MS approach revealing hidden nitrite reactions in hemolysate using 18 O-labelled nitrite and cysteine-based thiols

Determination of low level nitrite and nitrate in biological, food and environmental samples by gas chromatography-mass spectrometry and liquid chromatography with fluorescence detection

Estimation of nitrite in source-separated nitrified urine with UV spectrophotometry

Griess micro-assay for the determination of nitrite by combining fibre optics-based cuvetteless UV-Vis micro-spectrophotometry with liquid-phase microextraction

Development of a cloud point extraction and spectrophotometry-based microplate method for the determination of nitrite in human urine and blood

Electrochemical nitric oxide sensors for physiological measurements

Designing molecular materials and strategies for the electrochemical detection of nitric oxide, superoxide and peroxynitrite in biological systems

Recent advances in nanomaterial-based electrochemical sensing of nitric oxide and nitrite for biomedical and food research

Development of an electrochemical sensor for nitric oxide based on carbon paste electrode modified with Nafion, gold nanoparticles and graphene nanoribbons

Understanding the role of metal-organic frameworks in surface-enhanced Raman scattering application

Controllable design of tunable nanostructures inside metal-organic frameworks

Enhanced Fentonlike catalysis by iron-based metal organic frameworks for degradation of organic pollutants

Electrodeposition of gold nanoparticles on Cu-based metal-organic framework for the electrochemical detection of nitrite

A novel electrochemical sensor based on metal-organic framework for electro-catalytic oxidation of L-cysteine

Fabricated Metal-Organic Frameworks (MOFs) as luminescent and electrochemical biosensors for cancer biomarkers detection

Microcalorimetry-guided pore-microenvironment optimization to improve sensitivity of Ni-MOF electrochemical biosensor for chiral galantamine

Photoelectrochemical aptasensing of thrombin based on multilayered gold nanoparticle/ graphene-TiO 2 and enzyme functionalized graphene oxide nanocomposites

BbvCI powered DNA walking machinebased Zr-MOFs-labeled electrochemical aptasensor using Pt@ AuNRs/Fe-MOFs/PEI-rGO as electrode modification material for patulin detection

Selective removal of phosphate from aqueous solution by MIL-101(Fe)/bagasse composite prepared through bagasse size control

Encapsulation of K 6 P 2 W 18 O 62 into magnetic nanoporous Fe 3 O 4 /MIL-101 (Fe) for highly enhanced removal of organic dyes

Iron terephthalate metalorganic framework: Revealing the effective activation of hydrogen peroxide for the degradation of organic dye under visible light irradiation

A simple strategy for fabrication of Pd@MIL-100(Fe) nanocomposite as a visible-light-driven photocatalyst for the treatment of pharmaceuticals and personal care products (PPCPs)

Electronic and vibrational properties of a MOF-5 metalorganic framework: ZnO quantum dot behaviour

An amperometric hydrogen peroxide biosensor based on the immobilization of HRP on multi-walled carbon nanotubes/electro-copolymerized nano-Pt-poly(neutral red) composite membrane

The use of linear potential sweep voltammetry and of a.c. voltammetry for the study of the surface electrochemical reaction of strongly adsorbed systems and of redox modified electrodes

The authors acknowledge the support provided by Second Tibetan Plateau Scientific Expedition and Research Program (STEP) (No. 2019QZKK0201).

The authors declare no competing interests.