key: cord-0073370-6fquy9dv authors: Oliani, Washington Luiz; Pusceddu, Fabio Hermes; Parra, Duclerc Fernandes title: Silver-titanium polymeric nanocomposite non ecotoxic with bactericide activity date: 2022-01-12 journal: Polym Bull (Berl) DOI: 10.1007/s00289-021-04036-7 sha: 4843346113ffdbbdc992a840c698122f8e67e900 doc_id: 73370 cord_uid: 6fquy9dv In view of the intense interest in applications of silver nanoparticles in products for the medical field and in food preservation packaging due to their antimicrobial properties, the ecotoxicology of silver nanocomposites was evaluated in films. Test with the sea urchin Echinometra lucunter, to evaluate embryonic development and contamination by the action of silver and titanium nanoparticles in polyethylene nanocomposite films presents new results. The silver nanoparticle’s stability in polymeric materials can be enhanced by adding carriers, such as titanium dioxide and montmorillonite clay (MMT) without to producing one unfriendly material. For this research, low-density polyethylene (LDPE)/linear low-density polyethylene (LLDPE) were used processed in a twin-screw extruder, followed by gamma irradiation with 25 kGy and characterized by ecotoxicology assays, field emission scanning electron microscopy (FESEM), scanning electron microscopy and energy dispersive spectroscopy (SEM–EDX), differential scanning calorimetry (DSC), thermogravimetric analysis (TG), Raman spectroscopy (SERS) and mechanical properties. The antibacterial properties of the LDPE films were investigated against Escherichia coli and Staphylococcus aureus. The gamma irradiation had an important effect in the synthesis of silver nanoparticles resulting in bactericidal activity and the death of 100% of the tested bacteria. The evaluation of the environment was considered with the ecotoxicological investigation carried out. The results indicated that the polymeric films with silver nanoparticles and TiO(2) do not contaminate the environment and neither interfere with the larval development of Echinometra lucunter. The obtained materials can be used in various applications with antimicrobial properties. [Image: see text] The diversity of polymers and the different factors that control metallic nanoparticles' properties result in many technical applications for nanocomposites. The current nanocomposites present a relatively easy technology of preparation and application with low cost to produce new materials in substitution of available products [1, 2] . With the emergence of pathogenic bacterial strains resistant to one or more antibiotics, the medicine needs new disinfection systems. Metallic nanoparticle systems are one of the most promising systems for fulfilling this function [3] [4] [5] [6] . Antimicrobial materials are not only used in medical applications, such as catheters [7] and prostheses [8] , but also in food packaging [9, 10] and in paint industry [11] among others. One must be aware of the different public sectors where there is the possibility of proliferation of bacteria and fungi, such as hospitals, schools, offices, etc., where infectious diseases can be transmitted through surfaces [12] . In our days, plastics more than ever constitute these surfaces. Among the polyolefins, LDPE has important properties: low (weight, temperature toughness, density, moisture absorption), great mechanical properties, good processability, high stiffness in molded parts, tear-resistance besides being recyclable [13] [14] [15] [16] [17] [18] . For these properties, LDPE has a wide field of applications in which the biocidal activity can be added based on many examples of polymers cited in the literature. For example, the Polyvinyl butyral (PVB) with different types of nanoparticles showed antibacterial properties. It gained mechanical resistance compared to conventional polymers [19] . Polyacrylonitrile nanocomposite (PAN) films containing silver nanoparticles developed as multifunctional film matrix with has biocidal activity [20] . In parallel, direct surfaces treatment of as for PP (amphiphilic polymer) of PP-g-PEG sheets having embedded metal nanoparticles were synthesized with antibacterial efficiency [6] . Investigation of it on biomaterials, as the literature reports, showed the efficacy in preventing infection of a newly developed PP-g-PEG and Ag-PPg-PEG polymer-coated shunt catheters. Especially Ag-PP-g-PEG polymer coating was effective to prevent implant-related infections in the central nervous system in rats [21] . Another example is the study of PET-g-MAA fibers coated with AgNPs that had an antimicrobial effect on both bacterial species (E. coli and S. aureus). The synthesized material was obtained easily and cheaply with surface-bound Ag + ions converted to AgNPs (silver nanoparticles) without using any chemical reducing agents and had no cytotoxicity effects on L929 fibroblast cells [22] . Silver nanoparticles coated with poly(styrene-g-soybean oil) graft copolymers using soy oil macroperoxide as a nanosilver carrier. The polyolefin became an efficient bactericide, in addition to producing nanocomposites with fluorescence properties, making them promising materials [11] . PET fabrics knew for not preventing the growth of microorganisms, when PET surfaces were firstly modified by MAA grafting and HMDA attaching, and after modified by silk Sirina-AgNPs immobilization. It was found that the PET S-AgNPs had antimicrobial activity on both gramnegative and gram-positive bacteria [23] . The number of applications for AgNPs increases exponentially, including nanosilver in association with other metallic nanoparticles [24] . With this, the search for new antimicrobial and antiviral materials becomes timely and eminet, including in the fight against Covid 19 [25, 26] . Silver and titanium nanoparticles are known for their biomedical properties in common uses [27] . TiO 2 is an antimicrobial agent effective in bacterial cells, fungi, algae, and viruses. Its photodegradation is due to the high oxidizing action and hydroxyl radicals (OH*) species in oxidation systems. The photocatalytic property of TiO 2 is manifested under ultraviolet light. The doping of Ag nanoparticles in TiO 2 not only increases the photocatalytic activity of titania, but also promotes properties of antibacterial activity for the material in the absence of ultraviolet light [28] . The improved photocatalytic activity of Ag/TiO 2 thin film for disinfection can be attributed to the higher production rate of ROS reactive species, compared to TiO 2 [29] . The addition of clay-like montmorillonite strengthens the polymeric compound favoring the nucleation of silver nanoparticles. The parallel stacked layered clay structure facilitates the controlled diffusion of silver nanoparticles [30] . The creation of a biocidal material with slow release of silver species can prolong the biocidal activity [31, 32] . At the cellular level, many mechanisms of AgNPs toxicity were reported. This includes the generation of reactive oxidative species (ROS), DNA damage, and cytokine induction during in vitro studies [33] . On the surfaces, the dissolution of AgNPs releases silver ions that trigger the inactivation of respiratory enzymes, interrupt electron transport, and alter the permeability of the bacterial membrane and viral protein wrap, which causes the death of cells [29] . In contrast to the benefits, it can increase the disposal of nanoparticles into the environment. Consequently, it is necessary to be very careful with the application of nanomaterials, as the beneficial properties derived from them can be lost due to inadequate use in biological systems [27] in which cytotoxicity testing [34] and ecotoxicity testing [35] are of great importance. In this context, the literature also describes the interest in ecotoxicology tests for the evaluation of nanocomposites. The sea urchin Echinometra lucunter, which populates all the Brazilian coast, is used in ecotoxicology tests due to the sensitivity of the early embryonary stages for numerous laboratories of marine coast. For pollutants present in seawater, even in very low concentrations, bioassays routinely use sea urchin larvae embryos to assess water quality [36] [37] [38] . For these senses, in present work on LDPE nanocomposites proposed the investigation of ecotoxicity of the material in urchin larvae. The innovative aspect of our study is to improve antimicrobial properties to the surface of LDPE nanocomposites by gamma irradiation, as an effective process for totally reducing metallic ions simultaneously to sterilization without chemicals. Evaluation of nanocomposites activity evolving the irradiation for efficient silver nanoparticles on TiO 2 carrier reduced the formation of agglomerates, consequently, improved bactericidal efficiency. Synthesis of silver nanoparticles and titanium: PVP solution was prepared in deionized water heated at 60 ºC, followed by AgNO 3 solubilization with constant agitation. Subsequently, the solution was followed by addition of titanium (IV) isopropoxide and MMT clay. Sonication was carried out for 30 min to reduce and stabilize the silver under titanium nanoparticles. The equipment used for disruption of agglomerates of silver and titanium nanoparticles in PVP solution was the Eco-Sonics ultrasound, with a working frequency of 60 kHz and output with a maximum intensity of 350 Watts. The polyethylene composites (LDPE/LLDPE 90:10 wt%) were processed in a twin-screw extruder (Haake, Model Rheomex PTW 16/25), with the following processing conditions: the temperature profile (feed to die) was 160 to 190 °C, with a speed of 100 rpm. From five different nanocomposites of polyethylene LDPE/LLDPE films, PENC1 to PENC3 were obtained under those conditions containing nanosilver-titanium/MMT in different ratios. The films, PENC4 and PENC5 were, finally, irradiated under air at room temperature, in a 60 Co gamma source, at a dose rate of 5 kGy h −1 . The total dose absorbed was 25 kGy (monitored by a Harwell Red Perspex 4034 dosimeter), Fig. 1 . According to the literature, the polyethylene montmorillonite nanocomposites prepared with the addition of powder from sonication process showed improvement of the dispersion compared with non-treated ones [39] . The use of ultrasound is one important tool in nanoparticles research as reported by [38] that confirmed increasing of the surface content of Ag on TiO 2 [40] . The formulation of polyethylene nanocomposite (PENC) is shown in Table 1 . Simplified Scheme 1 of the preparation process of polyethylene nanocomposite represents the polymer matrix of the polyethylene being irradiated with gamma rays. The distribution of the clay is preferably exfoliated and the AgNPs@TiO 2 are anchored in LDPE/LLDPE matrix. Specimens of Echinometra lucunter were collected at Santos Bay, SP/Brazil. After the collection, the sea urchins were transported in cool boxes to the UNISANTA-Ecotoxicology Laboratory and placed in 500 L tanks with aerated seawater before testing. The gametes were obtained by KCl (0.5 M) injection according to standard [41] . As soon as the organisms started releasing the gametes, they were targeted for the fertilization procedure. These experiments are internationally accepted as suitable for toxicity, hazard, or risk assessments [36, 37, 41] , and have been employed to better understand negative effects on reproduction of an organism broadly recommended for water bioassays. The short-term chronic toxicity tests with Echinometra lucunter were carried out according to the procedure described by USEPA with adaptations [41] , sea urchin embryos are exposed to a specimen of the PENC = Polyethylene-Nanocomposite-Films samples. After the exposure period, the number of larvae that showed normal and anomalous development is evaluated. The dilution water used in the experiments, both for obtaining gametes and for preparing controls and elutriate samples, was prepared by diluting sea salt (Red-sea®) in distilled water, in concentrations of 30 to 36 ppm, followed by filtration in cellulose membrane with 0.22 µm porosity. The experiments were conducted in test tubes containing 10 mL of the test solution. For each treatment, four replicates were used, where about 300 eggs were inserted, and the set was kept for 36 to 42 h (until observes the Initial formation of the embryos) in an incubator chamber with a constant temperature of (26 ± 1) ºC and a photoperiod of 16 h/8 h (light-dark). After the exposure period, the test was ended by adding of 0.5 mL of borax-buffered formaldehyde to all replicates. Subsequently, the content of each replica was observed using a Sedgewick-Rafter microscope. The first 100 embryos were counted and their degree of development was assessed. Embryos that reached a well-developed pluteus larva stage were considered normal, while those that presented morphological changes and/or developmental delay were considered affected. The test was considered valid when ≥ 80% of larvae are successfully developed in the control. The results of the chronic toxicity tests were submitted to the variance analysis method (ANOVA). First, the data were analyzed for normality and homogeneity of variance by the Chi-square and Bartlett´s methods, respectively. Subsequently, the data were submitted to the analysis of variance method (ANOVA-p < 0.05) using the Dunnett method. The cell suspension concentration of the inoculum used for tests was (2.4 × 10 5 CFUmL −1 ) for Staphylococcus aureus (ATCC 6538P) and (2.7 × 10 5 CFUmL −1 ) for Escherichia coli (ATCC 8739) for each tested step. The procedure was performed separately for each microorganism. Control and test surfaces are inoculated with microorganisms, in triplicate, and then the microbial inoculum is covered with a thin, sterile film. Covering the inoculum spreads it, prevents it from evaporating, and ensures close contact with the antimicrobial surface. The samples of the PENCs films, (40 × 40) mm 2 , were deposited in a sterile Petri dish inoculated on the surface of 50 mL of a suspension of each organism. All samples were incubated for 24 h at 37 ºC [42] . The specimens were fixed in a sample holder and covered with Au/Pd for test. The acceleration rating used was 10 kV and the equipment was FESEM, JEOL, JSM-6701F-Japan. The samples were fixed in a sample holder and covered with Au/Pd and analyzed using a Hitachi TM3000, coupled with a Bruker Quantax 70 for the collection of energy-dispersive X-ray spectroscopic information. The EDS analysis was carried out at 15 kV and the acquisition period was 90 s. The thermal properties of the nanocomposite films were verified in the Mettler Toledo DSC 822 e equipment. Samples weighing 10 to 15 mg were placed into an aluminum pan. The samples were heated from − 20 ºC to 220 ºC and kept at 220 ºC for 5 min. After this isothermal process, the samples were cooled to − 20 ºC and then heated to 220 ºC. The heating rate consists of 10 ºC min −1 in a nitrogen atmosphere. The melting temperature (T m ) and degree of crystallinity (X c ) were calculated with the following Eq. (1): The value of ΔH f is melting enthalpy of the sample, ΔH 0 was taken for 100% crystalline LDPE, which is assumed to be 280 kJkg −1 [43, 44] , and P was the fraction content of LDPE in the sample. TG curves were acquired in the equipment TGA/SDTA 851-Mettler-Toledo. Samples of 10 to 15 mg were placed into an alumina pan, under a nitrogen atmosphere of 50 mLmin −1 , and heated from 25 up to 600 °C, at heating rate of 10°Cmin −1 . Raman analysis was performed using the Raman laser 785 nm, InPhotonics equipment. The mechanical properties of tensile stress and elongation at rupture followed ASTM-D882-18 [45] . The tests were performed on an Instron 5567 machine at a rate of 50 mm min −1 speed and equipped with pneumatic claws. Dimensions of the test specimens were (70 × 10) mm and 0.08 µm thick. Five specimens were tested for the mechanical properties of each composite formulation. Research on the toxicity of NPs can be investigated from two points of view: health and environmental hazard [46] . Morphological properties of the AgNPs influence their biocidal activity, for example: size, shape, and surface coating. It is important to note that same property also influences the cito and ecotoxicity of the AgNPs. These properties of AgNPs, combined with their high production volume, are a stimulus for research on the impact and harmfulness of silver nanoparticles [47, 48] . There is concern about increasing the use of manufactured nanomaterials, for example, TiO 2 and AgNPs, and their possible release into the environment via wastewater treatment plants. It poses a potential threat for aquatic organisms, and its effect on the ecosystem is of great importance for environmental risk assessment. Figure 2 shows the larval development of Echinometra lucunter exposed to different polyethylene nanocomposite films. Results of the embryo larval bioassay using E. lucunter are shown in Fig. 2 . In all nanocomposite polyethylene films containing silver and titanium nanoparticles, satisfactory larval development was observed in the ecotoxicity tests, above the control value sample (PE0). With those results, it was verified that the normal development of E. lucunter larvae was not affected by silver and titanium nanoparticles of the PENC nanocomposite films. The interesting result illustrated in Fig. 3 is that all nanocomposite films were effective in reducing E. coli and S. aureus. The nanocomposite polyethylene films showed significant results against the bacteria S. aureus and E. coli. Regarding PENC3 compounds with 1 wt% of silver particles and titanium, is remarkable a significant antimicrobial activity against S. aureus with antimicrobial activity values of 1.27 and 1.11 for E. coli, respectively (see Table 2 ). In addition, the results of the sample irradiated with 25 kGy, PENC4, showed a very significant antimicrobial activity for S. aureus, 3.04, and E. coli, 2.94, and also for the PENC5 sample S. aureus 2.85 and E. coli 2.71. The results of logarithmic reduction, are very expressive for the irradiated samples PENC4 and PENC5 that presented values 2.85 for S. aureus and 2.71 for E. coli. The high visible light photocatalytic activity of the Ag/TiO 2 /MMT is ascribed owing to the increase in surface-active centers and the localized surface plasmon effect of the silver nanoparticles. Under visible light irradiation, the electrons generated on the silver nanoparticles from the plasmon excitation are transferred to the neighboring TiO 2 particles, which function as the photocatalytic centers [49] . The release of Ag + present in the polymer surface depends on the diffusion of water molecules coming from the bacteria medium into the surface of particles [50] . Highly non-polar polymers such as allows the diffusion of those water molecules on interface through holes or micron-scale defects [51] . Gamma irradiation induces ionization and excitation of the water molecules, generating radiolytic molecular and radical species such as solvated electrons, hydroxyl radicals, and hydrogen atoms. The solvated electrons and hydrogen atoms reduce the metal ions to metal atoms, which coalesce to form more nanoparticles [52] . Polymeric nanocomposites irradiated with gamma radiation acquire more comprehensive biocidal properties compared to non-irradiated ones. The nanocomposite is effective against tested pathogenic microorganisms due to its high surface area and reduction in aggregates size due to the gamma rays [53] in surface of the carrier TiO 2 /MMT to perform a more stable bactericide activity. It was possible to identify the presence of silver and titanium nanoparticles by EDX analysis. The distribution of silver and titanium in the films surfaces was homogeneous. The micrograph showed in Fig. 4 , in nanometric scale indicates the presence of silver and titanium nanoparticles in spherical format and with dimensions from 53.2 to 91.1 nm. Figure 4 shows the FESEM micrographs of the nanocomposite film PENC1. The deposition of AgNPs on TiO 2 enhances the photocatalytic activity of titania and also imparts biocidal properties to the modified material, according to the literature [54] . In other work, the PP-AgNPs showed antibacterial activity toward E. coli and S. aureus via the release of oxygen reactive species and Ag ion diffusion mechanism; thus, the inhibition rates enhanced, potentializes the biocidal effect [55] , corroborating with our research work. Figures 5 and 6 show the SEM micrographs of the nanocomposite film PENC1 and PENC2. Energy-dispersive X-ray spectroscopy (EDX) was used to analyze the elementary constituents of the PENC thin films. Figure 5 displays the spectrum of PENC films obtained by elemental microprobe analysis of EDX. The results showed that titanium at a concentration of 1.27% and silver at 0.17% were the principal elements of PENC films. EDX analysis also confirmed the presence of elemental silver at a concentration of 0.13%, titanium 0.46%, and silicon 0.16% as measured on thin film surfaces. The metal elements have a uniform distribution which favors the biocidal interaction by contact with bacteria. The DSC results concerning on the Tm 2 and X C results are presented in Table 3 and refers to the DSC curves, Fig. 7 . [56] corroborate with that idea and the silver incorporation in MMT plays an important role in the crystallinity degree of PENC that increases when added Ag-MMT. Another important aspect reported by Ghosh et al. [57] is that crystallinity affects the permeability of the nanocomposite films, the permeability decreases with increasing of the crystallinity. The TG results indicated decomposition (T onset ) of the samples, Table 4 . From the information obtained in Table 4 , it can be seen that the temperature of degradation (T onset ) increased with the addition of inorganic particles For PENC4 and PENC5, both irradiated at 25 kGy is verified that radiation contributes to increasing of the thermal stability probable to efficiently reduction of silver avoiding aggregates of nanoparticles Ag/TiO 2 , and a slight formation of crosslink which corroborates with higher values of T onset . Analyzing the Raman spectrum of polyethylene nanocomposite films PENC, Fig. 8 , some results were significant and corroborated with the presence of nanoparticles in the films. The broad band with peaks at 385 and 670 cm −1 are associated with two-phonon states in a TiO 2 crystal. The 822 cm −1 lines are associated with the Eu(LO)-vibration TiO 2 crystal band [58] . Raman spectra measured the Si-Si phonon line position by deconvoluting the spectra into crystalline 520 cm −1 [59] . [60] , 882 cm −1 Si-O stretching [61] , and 1436 cm −1 band is associated with amino group [62] . The spectra in 1300 cm −1 CH 2 -Si wagging modes [63] , 968 and 1164 cm −1 ν(SiOSi) [64] . The peak appearing at 659 cm −1 is attributed to the presence of PVP stabilized silver nanoparticles [65] . The broad and intense peak at 1589 cm −1 was attributed to the enhancement of Raman lines by carbon polymeric segments absorbed on silver oxide [66] . Figure 9 shows the recorded tensile strength and tensile strain (elongation) results of the films. The PE0 and PENC4 samples showed very close tensile stress at yield values, 20 and 17 MPa, but tensile strain at break with little variation 127 and 115%. The other PENC1, 2, 3, and 5 samples showed very significant values of tensile strain at break ranging from 218 to 352%. These polyethylene nanocomposites films having silver nanoparticles and titanium dioxide synthesized showed antibacterial efficiency. All samples showed expressive values of microorganisms death by contact, using the Escherichia coli and Staphylococcus aureus, mainly in the irradiated samples PENC4 and PENC5. Polyethylene films (LDPE/LLDPE) using Ag/TiO 2 /MMT nanocomposites obtained via extrusion have biocidal properties and can be promising materials in medical applications, food packaging to prevent bacterial contamination. We highlighted that the films presented very significant elongation values concerning pure LDPE. It is essential The stress-strain curves of PENC films to consider that the silver nanoparticles and titanium dioxide used to manufacture of polyethylene films did not interfere as contaminants in the ecotoxicity tests with Echinometry lucunter since the larval development was normal. The nanocomposites were effective against tested pathogenic microorganisms due to the efficiency of irradiation in the reduction of ions to nanosilver in the TiO 2 / MMT surface with the consequence of total bacteria death, reaching values close to zero. Reduction in aggregates size due to the gamma irradiation of the surface films performed a more stable bactericide activity. The obtained materials can be used in various applications with antimicrobial functions. Polymer/metal nanocomposites for biomedical applications Antimicrobial polymers with metal nanoparticles Antibacterial activity of silver nanoparticles: a surface science insight Effects of weathering on mechanical, antimicrobial properties and biodegradation process of silver loaded TPE compounds Development of environmentally safe biodegradable, antibacterial surgical sutures using nanosilver particles Synthesis, characterization, and antibacterial activity of metal nanoparticles embedded into amphiphilic comb-type graft copolymer Enhanced antibacterial and antiadhesive activities of silver-PTFE nanocomposite coating for urinary catheters Silver nanocoating technology in the prevention of prosthetic joint infection Synthesis of polyethylene/silica-silver nanocomposites with antibacterial properties by in situ polymerisation Silver nanoparticles as an effective disinfectant: a review High fluorescence emission silver nano particles coated with poly(styrene-g-soybean-oil) graft copolymers: Antibacterial activity and polymerization kinetics Photocatalytic TiO 2 nanoparticles enhanced polymer antimicrobial coating Effect of ultrasonic irradiation on low-density polyethylene molecular structure Melt elongation flow behaviour of LDPE/ LLDPE blends Structural, thermal, and gas transport properties of HDPE/LLDPE blend-based nanocomposites using a mixture of HDPE-g-MA and LLDPE-g-MA as compatibilizer A facile evaluation on melt crystallization kinetics and thermal properties of low-density polyethylene (LDPE)/recycled polyethylene terephthalate (RPET) blends Biomedical applications of polyethylene Polietileno: principais tipos, propriedades e aplicações. Polímeros: Ciência e Tecnologia Quantitative evaluation of antibacterial activities of nanoparticles (ZnO, TiO 2 , ZnO/TiO 2 , SnO 2 , CuO, ZrO 2 , and AgNO 3 ) incorporated into polyvinyl butyral nanofibers Development of multifunctional polyacrylonitrile/silver nanocomposite films: antimicrobial activity, catalytic activity, electrical conductivity, UV protection and SERS-active sensor The efficacy of silver-embedded polypropylene-grafted polyethylene glycol-coated ventricular catheters on prevention of shunt catheter infection in rats In situ synthesis of silver nanoparticles on modified poly(ethylene terephthalate) fibers by grafting for obtaining versatile antimicrobial materials Coating of modified poly(ethylene terephthalate) fibers with sericin-capped silver nanoparticles for antimicrobial application AgNPs@ ZnO hybride nanoparticles infused thermoplastic polyester elastomer and their biocide effect Antibacterial properties of silver doped titania AgNPs polypropylene gel films thermal study and antibacterial activity A facile strategy for the construction of TiO2/Ag nanohybrid-based polyethylene nanocomposite for antimicrobial applications Improved microbial growth inhibition activity of bio-surfactant induced Ag-TiO 2 core shell nanoparticles Antiviral and antibacterial effects of silver doped TiO 2 prepared by the peroxo sol gel method Silver-clay nanohybrid structure for effective and diffusion controlled antimicrobial activity Incorporation of silver in montmorillonite-type phyllosilicates as potential antibacterial material Montmorillonite reinforced polymer nanocomposite antibacterial film Nanotoxicity: Prevention and antibacterial applications of nanomaterials. Toxicity of silver and other metallic nanoparticles Fabrication of polypropylene/silver nanocomposites for biocidal applications Silver nanoparticles: Behaviour and effects in the aquatic environment First steps towards Echinometra lucunter embryo cryopreservation Harmful effects of cocaine by product in the reproduction of sea urchin in different ocean acidification scenarios Recent developments and practical feasibility of polymer-based antifouling coatings Dispersion and exfoliation of nanoclays in itaconic acid funcionalized LDPE by ultrasound treatment Ultrasound assisted synthesis of Ag-decorated TiO 2 active in visible light Short-term methods for estimating the chronic toxicity of effluents and receiving waters to west coast marine and estuarine organisms Antibacterial products -Test for antibacterial activity and efficacy Polymer Handbook Kinetics of crystallization from the melt and chain folding in polyethylene fractions revisited: theory and experiment Standard test method for tensile properties of thin plastic sheeting Silver nanoparticles -Fabrication. Characterization and applications, assessment of nanotoxicity and safety profiles of silver nanoparticles. IntechOpen A systematic review of evidence for silver nanoparticle-induced mitochondrial toxicity Proteomic profile of the hard corona of charged polystyrene nanoparticles exposed to sea urchin Paracentrotus lividus coelomic fluid highlights potential drivers of toxicity Montmorillonite supported Ag/TiO 2 nanoparticles: an efficient visible-light bacteria photodegradation material The antimicrobial efficacy of polyamide 6/silver nano and microcomposites Water diffusion into transcrystalline layers on polypropylene Synthesis of silver nanoparticles deposited on silica by gamma-irradiation and preparation of PE/Ag nano compound masterbatches Handbook of immunological properties of engineered nanomaterials Preparation and characterization of titania-coated polystyrene spheres and hollow titania shells Enhanced antibacterial and food simulant activities of silver nanoparticles/polypropylene nanocomposite films Development of long-term antimicrobial poly (ε-caprolactone)/silver exchanged montmorillonite nanocomposite films with silver ion release property for active packaging use Physico-mechanical, rheological and gas barrier properties of organoclay and inorganic phyllosilicate reinforced thermoplastic films Two-phonon hyper-Raman scattering and polariton spectra in rutile crystal Raman spectroscopy of β-doped microcrystalline silicon films Application of portable Raman instruments for fast and non-destructive detection of minerals on outcrops In: Density functional theoretical study on surface-enhanced Raman spectroscopy of CH 2 /NH 2 Wagging Modes in p-π conjugated molecules on noble metal surfaces Spectroscopic properties of inorganic and organometallic compounds Sonochemical immobilization of silver nanoparticles on porous polypropylene Ultrasound irradiation coating of silver nanoparticles on ABS sheet surface The authors acknowledge financial support for this work from CNEN-IPEN, CLA-IPEN, and CCTM-IPEN, for microscopy analysis (FESEM and SEM-EDX), Multipurpose Gamma Irradiation Facility at the Radiation Technology Center-CTR-IPEN and ControlBio by biocide testing. Publisher's Note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.