key: cord-0067751-z8v3safh
authors: Wang, Shu; Li, JianNa; Cao, Yihong; Gu, JingWei; Wang, YuanFeng; Chen, ShiGuo
title: Non-Leaching, Rapid Bactericidal and Biocompatible Polyester Fabrics Finished with Benzophenone Terminated N-halamine
date: 2021-09-20
journal: Adv
DOI: 10.1007/s42765-021-00100-z
sha: 9461636324eea86d2aa42fa9dc021d25efb1ef6b
doc_id: 67751
cord_uid: z8v3safh

Pathogenic bacteria can proliferate rapidly on porous fabrics to form bacterial plaques/biofilms, resulting in potential sources of cross-transmissions of diseases and increasing cross-infection in public environments. Many works on antibacterial modification of cotton fabrics have been reported, while very few works were reported to endow poly(ethylene terephthalate) (PET) fabrics with non-leaching antibacterial function without compromising their innate physicochemical properties though PET is the most widely used fabric. Therefore, it is urgent to impart the PET fabrics with non-leaching antibacterial activity. Herein, a novel N-halamine compound, 1-chloro-3-benzophenone-5,5-dimethylhydantoin (Cl-BPDMH), was developed to be covalently bonded onto PET fabrics, rendering non-leaching antibacterial activity while negligible cytotoxicity based on contact-killing principle. Bacterial was easily adhered to Cl-BPDMH finished PET fabrics, and then it was inactivated quickly within 10 s. Furthermore, the breaking strength, breaking elongation, tearing strength, water vapor permeability, air permeability and whiteness of Cl-BPDMH finished PET fabrics were improved obviously compared to raw PET fabrics. Hence, this work developed a facile approach to fabricate multifunctional synthetic textiles to render outstanding and rapid bactericidal activity without compromising their physicochemical properties and biocompatibility. SUPPLEMENTARY INFORMATION: The online version contains supplementary material available at 10.1007/s42765-021-00100-z.

Poly(ethylene terephthalate) (PET) fabrics have been widely used in our daily clothes due to their excellent strength, easy processability, quick drying, dimensional stability, and wrinkle resistance [1] . However, pathogenic bacteria can proliferate rapidly on porous PET fabrics to form bacterial plaques/biofilms, resulting in irreversibly damaging their appearance, adversely affecting human health, and increasing cross-infection in public environments [2] , since bacterial infection is one of the most serious threat to global safety especially drug-resistant bacteria [3] [4] [5] [6] . To endow fabrics with antibacterial activity, ciprofloxacin [7] , metal salts and nanoparticles [8] [9] [10] , metallic oxide [11] , rose Bengal [12] , chitosan [13] [14] [15] , betaine [16, 17] , surface stereochemistry [18] , quaternary ammonium salt(QAS) [19] [20] [21] . dopaminementhol [22] , guanidine [23, 24] , and N-halamine [25] [26] [27] have been developed, and impressive achievements have been gained. Among them, N-halamine has become a popular antimicrobial due to its remarkable antibacterial activity against wide-spectrum pathogens even drug-resistant pathogenic bacteria [25, 28] , rapidly inactivating bacteria [29] , and reproducible biocidal activity [30, 31] . Moreover, strenuous efforts have been made to develop N-halamine as disinfectants [32, 33] for water treatment [30] , food packaging [34, 35] , hydrogel [25] , and antibacterial fabrics [36, 37] . Siloxane [38] [39] [40] or epoxide [41] terminated N-halamines have been developed to fabricate antibacterial cotton fabrics through a powerful covalent-bonding method. Shu Wang and JianNa Li contributed equally to this work. The aforementioned strategies were suitable for natural fibers containing reactive NH 2 or OH group, while an effective finishing method to fabricate antibacterial PET fabrics without compromising their intrinsic physicochemical properties is still not satisfactory owing to no reactive group in the PET molecular skeleton [2] . To endow PET fabrics with permanent antibacterial, reactive NH 2 , COOH, and OH groups were introduced by local destruction of polymer chains, and then the antibacterial constituents were covalently bonded to the locally damaged PET molecular chain through surface coupling reaction [42] . However, those strategies would lead to significant decrease in the mechanical properties and surface roughness of PET fabrics [43] . Therefore, it is urgent to develop a convenient strategy to fabricate permanent antibacterial PET fabrics with well-preserved physicochemical properties. Recently, we developed a benzophenone terminated quaternary ammonium salt (BP-QAS) for PET fabric by a photochemical finishing method, rendering perdurable antibacterial, and anti-mite activities without compromising their physicochemical properties [2] . Therefore, the benzophenone terminated N-halamine may be an optimal antibacterial agent for durable antibacterial PET fabrics. However, hydrophilic surface is not suitable for protective textiles such as medical surgical masks and protective clothing with waterproof requirements.

Herein, 1-chloro-3-benzophenone-5,5-dimethylhydantoin (Cl-BPDMH) was developed to finish PET fabrics by covalent bond via a photochemical hydrogen abstraction reaction. The Cl-BPDMH finished PET fabrics exhibited (i) excellent bactericidal activities against Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus); (ii) greatly improved mechanical properties, softness, and air permeability; (iii) negligible cytotoxicity; (iv) rapidly attaching and killing bacteria; (v) well-preserved water vapor permeability and whiteness. This work proposed a potential avenue to develop non-leaching bactericidal synthetic fabrics with great potential applications including but not limited to water purification, masks, home textiles and protective clothing.

Materials 5,5-dimethylhydantoin (DMH, 99%), 4-(Bromomethyl) benzophenone (BP-Br, 99%), trichloroisocyanuric acid (TCCA, 99%), sodium hydroxide (NaOH, 99%), sodium hypochlorite (available chlorine ≥ 8.25%), sodium thiosulfate (Na2S2O3, 99%), and potassium iodide (KI, 99%) were purchased from Energy Chemical Co. Ltd., China. Ethyl acetate (EA, AR), hexane (AR), and acetone (AR) were purchased from Guangzhou Chemical Reagent Factory, China. 

The typical synthetic reaction of Cl-BPDMH was following. The intermediate product 3-benzophenone-5,5-dimethylhydantoin (BPDMH, a pale yellow powder) was obtained by a nucleophilic substitution reaction of 5,5-dimethylhydantoin and 4-(bromomethyl) benzophenone (BP-Br) under constant stirring at 80 °C for 24 h (yield, 65%). Then, the crude product Cl-BPDMH was prepared by the chlorination reaction of the BPDMH and trichloroisocyanuric acid under continuous stirring for 12 h at room temperature. And the final product Cl-BPDMH was obtained after being purified by silica gel column chromatography using petroleum ether as the eluent (yield, 84%).

The PET fabrics were finished with Cl-BPDMH as following. Typically, the commercial PET fabrics were sequentially immersed in acetone solution for 2 min and purified water for 5 min under ultrasonic vibration, after being dried in blast drying oven at 50 ℃, the clean PET fabrics (defined as raw PET) were obtained. The raw PET fabrics were completely immersed in finishing solution containing Cl-BPDMH (liquor ratio 6:1) at room temperature, then the PET fabrics were irradiated under mild light (1.5 mW, λ = 365 nm) for 1 min. Finally, the Cl-BPDMH finished PET fabrics were obtained after being washed with purified water and air-dried. The PET fabrics finished with different Cl-BPDMH content were defined PET-2 (20 mg/ml), PET-3 (30 mg/ml), and PET-4(40 mg/ml), respectively.

Fourier transform infrared (FTIR) spectra of BP-Br, MDH, BPDMH, and Cl-BPDMH were recorded on a Nicolet 6700 FTIR spectrometer with a scan range of 400-4000 cm −1 at a resolution of 4 cm −1 and 32 scans. The proton magnetic resonance ( 1 H-NMR) spectra of BPDMH and Cl-BPDMH were collected on a Bruker Avance-400 spectrometer at 400 MHz by using CDCl 3 and DMSO-d6 as solvents, respectively, and tetramethylsilane (TMS) was used as the internal standard. The morphologies of the raw PET and Cl-BPDMH finished PET fabrics were observed by field emission scanning electron microscope (FE-SEM, Hitachi SU-70). The chemical element compositions of the raw PET and Cl-BPDMH finished PET fabrics were determined by energy dispersive X-ray spectroscopy (EDS) elemental mapping. The oxidative chlorine content of Cl-BPDMH finished PET fabrics were determined by the iodimetric/thiosulfate titration method as compared with raw PET fabrics [44, 45] .

The tearing strength, bursting strength, breaking strength, breaking elongation, water contact angle (WCA), moisture permeability and air permeability of raw PET and PET-3 were characterized according to our previous work [16, 46] , and the detailed test processes were provided in supporting information. The whiteness of raw PET and PET-3 was evaluated by the AATCC 110-2015 test method on a WSB-3A Intelligent Whiteness tester.

The quantitative antibacterial activity of the Cl-BPDMH finished PET fabrics against E. coli and S. aureus was evaluated by flask oscillation method and the plate count method according to FZ/T 73,023-2006 standard [20] . The antibacterial kinetics were carried out using the above experimental operation method while the shaking time was replaced by other predetermined time. The diameters of the inhibition zone (DIZs) were measured by the agar plate diffusion method to evaluate release behavior of the antibacterial constituent from the Cl-BPDMH finished PET fabrics [17] . To investigate the washing durability of antibacterial activity, the antibacterial rates of PET-3 compared with raw PET (control) against E. coli and S.aureus after being washed for 5, 10 and 20 laundering times, respectively, were performed according to FZ/T 73,023-2006 standard method. Each experiment was carried out in triplicate and the mean results were reported for analysis [2] .

To further visualize the antibacterial process of the Cl-BPDMH finished PET-3 fabrics, E. coli was stained using the live/dead BacLight Bacterial Viability Kit [47, 48] . Afterward, the dynamic process of stained E.coli contacting with PET-3 fabrics compared with raw PET fabrics was observed by rotating confocal fluorescence microscope (Olympus IX explore SpinSR10 instrument). Living E.coli was green and dead E.coli was red.

The cytotoxicity of Cl-BPDMH finished PET fabrics was evaluated by a CCK-8 assay using NIH 3T3 mouse embryonic fibroblast cells, and rabbit skin irritation was carried out to evaluate their skin irritation according to our previous work [24] .

The Cl-BPDMH was synthesized by two step typical chemical reactions as showed in Fig. 1a . The FTIR spectra of DMH, BP-Br, BPDMH and Cl-BPDMH were shown in Fig. 1b . A peak at about 1650 cm −1 assigned to C=O characteristic peaks of diaryl ketone appeared in the FTIR spectra of BP-Br, BPDMH and Cl-BPDMH. While a peak at 3240 cm −1 assigned to the N-H characteristic peaks of Hein ring appeared in the FTIR spectra of DMI and BPDMH. Compared with BDMMH, a new peak at 752 cm −1 assigned to N-Cl group appeared and the characteristic peak of N-H group at 3240 cm −1 disappeared in the FTIR spectrum of the Cl-BPDMH [49] . The molecular structures of BPDMH and Cl-BPDMH were further confirmed by 1 H-NMR spectra (Fig. 1c, d) . 1 9H) . Therefore, we confirmed that the Cl-BPDMH was synthesized successfully. The Cl-BPDMH finished PET fabrics were fabricated by covalently binding Cl-BPDMH to raw PET fabrics though a facilely photochemical hydrogen abstraction reaction as showed in Fig. 2a . Compared to raw PET, the surface and cross-sectional morphology of PET-3 exhibited no obvious damage (Fig. 2b) , indicating that PET-3 fabrics could maintain their original structures well during the finishing process. Compared to raw PET fabric, a weak signal of Cl (0.12 wt%) ascribed to N-Cl bond appeared in PET-3 (Fig. 2b, insert figure) , and the oxidative chlorine content of the Cl-BPDMH finished PET fabrics increased from 0.067 to 0.18 wt% as the concentration of the finishing agent increased (Fig. 2c) . The distribution mapping of N and Cl elements (Fig. 2d) could be further confirmed that Cl-BPDMH was successfully bonded to the PET fabrics.

As shown in Fig. 3a , no live S.aureus could be observed when it was incubated with Cl-BPDMH finished PET fabrics for 24 h, while about 65% of live E.coli could be observed when it incubated with PET-2 for 24 h. Obviously, no live bacteria could be observed for both test bacteria when they incubated with PET-3 and PET-4 for 24 h.

The DIZs were all zero, and no live bacteria was existed under antibacterial PET fabrics (Fig. 3b) , indicating that no Cl-BPDMH was leached from the Cl-BPDMH finished PET fabrics. Therefore, the antibacterial mechanism of the Cl-BPDMH finished PET fabrics was proven to contact killing mechanism [28] by directly transferring the oxidative chlorine from N-halamine to bacterial receptors [31, 50] . Non-leaching characteristics of antibacterial fabrics usually exhibited long-lasting antibacterial activity [46] . The antimicrobial rates of PET-3 were higher than 99% against both S.aureus and E.coli after being washed for 5,10, and 20 laundering times, respectively (Fig. 3c) than that of Gram positive S.aureus [51] . Thus, the nonleaching Cl-BPDMH finished fabrics exhibited excellent antibacterial activity and PET-3 was selected as the following experimental sample.

To further visualize the process of bacteria contacting with PET-3, and its real bactericidal speed, the in-situ dynamic process of E.coli contacting with PET-3 compared with raw PET fabrics was observed by rotating confocal fluorescence microscope as shown in Fig. 3e . The ultra-high resolution fluorescence microscopy image of E.coli treated with raw PET was full of live bacterial (green). Interestingly, E.coli was inactivated (red) after contacting with PET-3 within 10 s. Therefore, bacteria can be easily adhered to Cl-BPDMH finished PET fabrics, thereby being inactivated quickly within a few seconds, further indicating the main antibacterial mechanism of the Cl-BPDMH finished PET fabrics was contact killing. Though antiviral activity was not provided here, and it would be carried out in the future, N-haloamines have been proved to have excellent antiviral activity [52] . Therefore, Cl-BPDMH finished PET fabrics have potential applications in quick sterilization, including but not limited to water purification, biochemical protective clothing, mask, food packaging, antibacterial textiles.

Mechanical property is one of the most critical requirements of the fabrics. Compared with the raw PET fabric, the breaking strength and breaking elongation, tearing strength and bursting strength of PET-3 all showed a general increase (Fig. 4a-d) . Specifically, the breaking strength increased by 8.3% in the warp direction from 1450.6 to 1570.3 N, and it increased by 38.5% in the weft direction from 511.7 to 708.4 N (Fig. 4a) . Additionally, the breaking elongation increased by 8.0% in the warp direction from 31.7 to 34.2%, and it increased by 69.22% in the weft direction from 11.3 to 19.2% (Fig. 4b) because the increase of the interaction between Cl-BPDMH and PET chains improved the portion of amorphous region [53] . The tearing strength of PET-3 increased by 10.1% in the warp direction from 15.4 to 17.0 N, and it increased by 20.5% in the weft direction from 7.0 to 8.5 N (Fig. 4c) . Therefore, the breaking strength, breaking elongation and tearing strength of PET-3 increased obviously compared with raw PET fabrics because the intermolecular forces could increase by introducing polar chlorine group [54] after binding Cl-BPDMH, and extracting an active hydrogen to generate free radicals by mild light irradiating on the surface of PET fabric for a short time would not damage to PET structure [53] . The bursting strength remained basically unchanged as compared with raw PET (Fig. 4d) The whiteness of Cl-BPDMH finished PET fabrics was well remained without obvious changes as compared with raw PET (Fig. 4f) . The water vapor transmission (Fig. 4g ) and air permeability (Fig. 4h ) of PET-3 both increased slightly may be the pore size of the Cl-BPDMH finished PET fabric were slightly increased during the finishing process, resulting in improving the ability of water vapor and air flow to penetrate the PET fabrics [2] . Compared to raw PET, the water contact angle (WCA) of PET-2, PET-3 and PET-4 all increased, meaning that Cl-BPDMH finished PET fabrics can improve the hydrophobicity of PET fabrics due to the mainly influence of the diaryl group (hydrophobic group) on the chain of Cl-BPDMH (Fig. 4i) , which was conducive to adhering bacteria, and thereby inactivated them quickly (Fig. 3e) . This strategy has obvious advantages over hydrophilic antibacterial surfaces for medical surgical clothing and masks with waterproof requirements.

Cytotoxicity of PET-2, PET-3 and PET-4 compared with raw PET were shown in Fig. 5a . After being co-cultured with PET fabrics for 24 h, the viability of NIH 3T3 cell treated with Cl-BPDMH finished PET fabrics showed a slight decrease. Interestingly, compared with raw PET fabrics, the cell viability of PET-2, PET-3 and PET-4 were all more than 95%. Almost no cell was inactivated (red) after incubated with both raw PET and PET-3 for 24 h compared with NIH 3T3 cell only (Fig. 5b) . Therefore, the Cl-BPDMH finished PET fabrics exhibited negligible cytotoxicity.

Raw PET and PET-3 were further exposed to the back of rabbit's skin to test their irritation responses. After being contacted for 12, 24, 48, and 72 h, respectively, no erythema and edema of rabbit's skin treated with both raw PET and PET-3 was found on (Fig. 5c) . Besides, no distinct histopathological abnormal was found in hematoxylin & eosin (H&E) stained images at any evaluated areas masked by raw PET and PET-3 (Fig. 5d) . 

Cl-CBPDMH was synthesized to fabricate non-leaching bactericidal PET fabrics by photocatalytic hydrogen abstraction reaction. The Cl-CBPDMH finished PET fabrics can inactivate bacteria within 10 s, indicating their outstanding bactericidal activity against both Gram-positive S.aureus and Gram-negative E.coli. Moreover, PET fabrics can maintain even improve their mechanical properties, comfort properties and biocompatibility after being finished with Cl-BPDMH. Therefore, the Cl-BPDMH was a preferred antimicrobial to fabricate excellent bactericidal PET fabrics while negligible toxicity. Selecting C-H bond as the modified active site, this strategy can be widely applied to finish synthetic fiber fabrics, including but not limited to polyester, polyamide, polypropylene, and polyacrylonitrile. This work can promote the development of permanent antibacterial finishing strategy of synthetic fibers. And Cl-BPDMH finished synthetic fiber fabrics has promising applications including but not limited to water purification, masks, and medical textiles, socks, curtains, carpet and so on.

The online version contains supplementary material available at https:// doi. org/ 10. 1007/ s42765-021-00100-z.

Fabrication of highly durable polysiloxane-zinc oxide (ZnO) coated polyethylene terephthalate (PET) fabric with improved ultraviolet resistance, hydrophobicity, and thermal resistance

Insight into multifunctional polyester fabrics finished by one-step eco-friendly strategy

Antibacterial drug discovery in the resistance era

In situ selfassembled polyoxotitanate cages on flexible cellulosic substrates: multifunctional coating for hydrophobic, antibacterial, and uvblocking applications

Antimicrobial properties and application of polysaccharides and their derivatives

-Oxazoline)-based functional peptide mimics: eradicating MRSA infections and persisters while alleviating antimicrobial resistance

Surfacetransformed osteoinductive polyethylene terephthalate scaffold as a dual system for bone tissue regeneration with localized antibiotic delivery

Silver-nanoparticle-colored cotton fabrics with tunable colors and durable antibacterial and self-healing superhydrophobic properties

Thermal, waterproof, breathable, and antibacterial cloth with a nanoporous structure

Synthesis of metal nanoparticles in metal-phenolic networks: Catalytic and antimicrobial applications of coated textiles

Low starch/corn silk/ ZnO as environmentally friendly nanocomposites assembling on PET fabrics

Green light-triggered antimicrobial cotton fabric for wastewater disinfection

Construction of durable antibacterial and anti-mildew cotton fabric based on P(DMDAAC-AGE)/Ag/ZnO composites

Nanocomposites based on chitosan/silver/clay for durable multi-functional properties of cotton fabrics

Progress and prospects in chitosan derivatives: Modification strategies and medical applications

Durable antibacterial and nonfouling cotton textiles with enhanced comfort via zwitterionic sulfopropylbetaine coating

Environmentally friendly antibacterial cotton textiles finished with siloxane sulfopropylbetaine

Stereochemical strategy advances microbially antiadhesive cotton textile in safeguarding skin flora

Supramolecular antibacterial materials for combatting antibiotic resistance

New insights into synergistic antimicrobial and antifouling cotton fabrics via dually finished with quaternary ammonium salt and zwitterionic sulfobetaine

Antibacterial modification of PET with quaternary ammonium salt and silver particles via electron-beam irradiation

One-step anti-superbug finishing of cotton textiles with dopamine-menthol

Inherent guanidine nanogels with durable antibacterial and bacterially antiadhesive properties

Guanidine-functionalized cotton fabrics for achieving permanent antibacterial activity without compromising their physicochemical properties and cytocompatibility

Engineering a multifunctional N-halamine-based antibacterial hydrogel using a super-convenient strategy for infected skin defect therapy

Porous antimicrobial starch particles containing N-halamine functional groups

Novel N-Br bond-containing N-halamine nanofibers with antibacterial activities

Chemical insights into antibacterial N-halamines

Ding B N-halamine functionalized electrospun poly(vinyl alcohol-co-ethylene) nanofibrous membranes with rechargeable antibacterial activity for bioprotective applications

Biocidal poly(styrenehydantoin) beads for disinfection of water

Novel quat/di-N-halamines silane unit with enhanced synergism polymerized on cellulose for development of superior biocidability

Novel N-halamine disinfectant compounds

Chemistry of N-bromamines and N-chloramines

Absorbent pads containing N-halamine compound for potential antimicrobial use for chicken breast and ground chicken

Rechargeable antibacterial N-halamine films with antifouling function for food packaging applications

Ren XH N-halamine modified mesoporous silica coated cotton as multipurpose protective fibrous materials

Electrospun composite nanofiber fabrics containing uniformly dispersed antimicrobial agents as an innovative type of polymeric materials with superior antimicrobial efficacy

Huang TS N-halamine/quat siloxane copolymers for use in biocidal coatings

Characterization and mechanism for the protection of photolytic decomposition of N-halamine siloxane coatings by titanium dioxide

Novel inorganic-based N-halamine nanofibrous membranes as highly effective antibacterial agent for water disinfection

Polymeric antimicrobial N-halamine epoxides

Environmentally friendly surface modification of polyethylene terephthalate (PET) fabric by low-temperature oxygen plasma and carboxymethyl chitosan

Construction of antibacterial poly(ethylene terephthalate) films via layer by layer assembly of chitosan and hyaluronic acid

Preparation, characterization and antibacterial properties of cellulose membrane containing N-halamine

Construction of chlorine labeled ZnO-chitosan loaded cellulose nanofibrils film with quick antibacterial performance and prominent UV stability

Non-leaching bactericidal cotton fabrics with well-preserved physical properties, no skin irritation and no toxicity

Bactericidal and antifouling electrospun PVA nanofibers modified with a quaternary ammonium salt and zwitterionic sulfopropylbetaine

Enhanced water-solubility, antibacterial activity and biocompatibility upon introducing sulfobetaine and quaternary ammonium to chitosan

Preparation of magnetically separable N-halamine nanocomposites for the improved antibacterial application

Novel porous chitosan/N-halamine structure with efficient antibacterial and hemostatic properties. Carbohyd Polym

Vancomycin-modified nanoparticles for efficient targeting and preconcentration of Gram-positive and Gramnegative bacteria

Progress and perspective of antiviral protective material

Radiation grafting of glycidyl methacrylate and divinylbenzene onto polyethylene terephthalate fabrics for improving anti-dripping performance

Chlorination of conjugated side chains to enhance intermolecular interactions for elevated solar conversion

Conflict of interest The authors declare that there is no financial and non-financial competing interest. His main research interests include smart and functional fibers/textiles, biomimetic materials/interfaces, super-wettable m a t e r i a l s , a n d b i o -/ medical-materials. Shiguo Chen received his BSc degree in chemistry from Jishou University in 2000, a PhD degree in polymer chemistry and physics from Sun Yat-sen University in 2005. He is now a professor of the College of Materials Science and Engineering at Shenzhen University. His research interests include structure-property-processing relationships, characterization techniques and applications of multifunctional fibers/ textiles/coatings, and bio-/ medical-materials.