key: cord-0067436-adi8p7b6 authors: Löbel, Martin; Lindner, Thomas; Mehner, Thomas; Rymer, Lisa-Marie; Björklund, Stefan; Joshi, Shrikant; Lampke, Thomas title: Microstructure and Corrosion Properties of AlCrFeCoNi High-Entropy Alloy Coatings Prepared by HVAF and HVOF date: 2021-09-09 journal: J Therm Spray Tech DOI: 10.1007/s11666-021-01255-2 sha: e7939067aae304817840550799bec2813a639f13 doc_id: 67436 cord_uid: adi8p7b6 High-entropy alloys (HEAs) represent an innovative development approach for new alloy systems. These materials have been found to yield promising properties, such as high strength in combination with sufficient ductility as well as high wear and corrosion resistance. Especially for alloys with a body-centered cubic (bcc) structure, advantageous surface properties have been revealed. However, typical HEA systems contain high contents of expensive or scarce elements. Consequently, applying them as coatings where their use is limited to the surface represents an exciting pathway enabling economical exploitation of their superior properties. Nevertheless, processing conditions strongly influence the resulting microstructure and phase formation, which in turn has a considerable effect on the functional properties of HEAs. In the presented study, microstructural differences between high-velocity oxygen fuel (HVOF) and high-velocity air fuel (HVAF) sprayed coatings of the alloy AlCrFeCoNi are investigated. A metastable bcc structure is formed in both coating processes. Precipitation reactions are suppressed by the rapid solidification during atomization and by the relatively low thermal input during spraying. The coating resistance to corrosive media was investigated in detail, and an improved passivation behavior was observed in the HVAF coatings. The multi-principal group of high-entropy alloys (HEAs) has gained extensive research interest. Their properties mainly stem from the ability to form simple solid solutions, preferably with body-centered cubic (bcc) or face-centered cubic (fcc) structure. Despite their complex composition, usually comprised of at least four elements with approximately equimolar composition, the formation of complex and brittle phases can be suppressed. Furthermore, improved properties could be achieved by minor elemental additions of non-metallic elements (Ref 1). Extensive investigations revealed an interesting combination of properties, e.g., high hardness and strength in combination with high ductility, which make these alloys promising for structural applications. Additionally, a high wear resistance under various loads and conditions was determined (Ref 2, 3) . These properties also make HEAs feasible for coating applications, where the required quantities of these materials can be significantly reduced by limiting them to the surface. Thermally sprayed HEA coatings have been produced utilizing various feedstock production routes and coating processes ( Ref 4, 5) . The best results in terms of homogeneity and defect reduction have been achieved by processing gas-atomized feedstock using high-kinetic energy thermal spray processes ( Ref 6, 7) . One such This article is an invited paper selected from presentations at the 2021 International Thermal Spray Conference, ITSC2021, that was held virtually May 25-28, 2021 due to travel restrictions related to the coronavirus (COVID- 19) pandemic. It has been expanded from the original presentation. industrially well-established process is high-velocity oxygen fuel (HVOF) thermal spraying, which enables the deposition of coatings with low porosity and oxide content. A further advancement of this process is high-velocity air fuel (HVAF) thermal spraying, where the combustion temperature is reduced by utilizing air in place of oxygen for fuel combustion. In this way, the formation of oxides and thermal degradation of the feedstock, e.g., metals or cemented carbides, can be avoided (Ref 8, 9) . This process had not yet been considered for HEAs. The most important base alloy system of HEAs is CrMnFeCoNi and its manganese-free derivative CrFe-CoNi, both forming single-phase fcc structures (Ref 10). The influence of various additional alloying elements has been investigated. The addition of aluminum clearly affects the phase formation, microstructure, and properties. For the equimolar alloy AlCrFeCoNi, a single-phase bcc structure is formed in the as-cast condition ( Ref 11) . The investigation of alternative production routes and heat treatments has revealed the formation of an additional fcc and tetragonal r-phase depending on the manufacturing conditions ( Ref 12, 13) . Furthermore, detailed investigations on sintered and cast AlCrFeCoNi alloys detected the presence of a disordered bcc phase, in addition to the chemically ordered bcc (B2) phase ( Ref 14, 15) . The phase formation in dependence of the production route and heat treatment distinctly influences the hardness and wear resistance ( Ref 16, 17) . Apart from microstructure, phase formation, and mechanical properties, the corrosion behavior of the alloy system AlCrFeCoNi and other HEAs has also been investigated. The corrosion resistance of cast, sintered, and additively manufactured HEAs in NaCl and H 2 SO 4 electrolytes has been assessed ( Ref 18, 19) . Investigation of spark plasma sintered AlCrFeCoNi in 0.5 M H 2 SO 4 by Zhou et al. revealed distinct passivation. Subsequent annealing was found to impair the corrosion resistance due to the formation of additional phases and hence a more heterogeneous condition ( Ref 20) . Detailed investigations by Parakh et al. on AlCrFeCoNi showed a distinct influence of the phase fraction (bcc and fcc phases), grain size, and dislocation density on the pitting resistance as tested in 3.5 wt.% NaCl electrolyte ( Ref 21) . Thermally sprayed AlCrFeCoNi coatings produced by atmospheric plasma spraying (APS) were investigated by Mu et al. in 3.5 wt.% NaCl electrolyte, revealing a high corrosion resistance. The formation of a passive film, which is comprised of Cr and Fe oxides, could be proven despite the relatively heterogeneous condition due to feedstock oxidation during thermal spraying ( Ref 22) . Investigations of laser cladded coatings in 0.6 M NaCl electrolyte also clearly showed passivation and an improved corrosion resistance in comparison to the stainless steel AISI 304L (EN 1.4306) ( Ref 23) . Due to the promising reported corrosion properties as mentioned above, the alloy AlCrFeCoNi was selected for this study. The high-kinetic energy processes of HVOF and HVAF thermal spraying have been selected to enable the deposition of dense coatings with low in situ oxidation during spraying. The influence of the coating process on the formed microstructure and resulting properties was investigated. Furthermore, detailed studies to determine resistance to pitting and passivation behavior have been conducted using NaCl and H 2 SO 4 electrolytes. Feedstock powder of the equimolar alloy was produced by NANOVAL GmbH & Co. KG (Berlin, Germany) using inert gas atomization and air classification. For the HVOF thermal spray process, the fraction of -45 ?15 lm was used, whereas a fraction of -33 ?15 lm was used for the HVAF coating process. The resulting particle size distribution was measured by laser diffraction analyses using a Cilas 920 device (Cilas, Orléans, France). Mild steel substrates (EN 1.0045) with [40 mm and 6 mm thickness were prepared by grit blasting prior to coating using Alodur EK F 24 blasting media (-850 ?650 lm) with a pressure of 2.5 bar under an angle of 70°. The HVOF coatings were deposited by a K2 liquid-fueled system (GTV Verschleißschutz GmbH, Luckenbach, Germany), employing the parameters summarized in Table 1 . The HEA AlCrFeCoNi powder was also sprayed using a HVAF coating process. For this purpose, a M3 TM -HVAF spray system (Uniquecoat, Oilville, VA, the USA) was employed. Mild steel substrate specimens in the form of [25 mm round coupons of 6 mm thickness were mounted on a horizontal rotating fixture and sprayed with parameters summarized in Table 2 . As depicted in the table, a Cross-sections of the feedstock and coatings were prepared by standard metallographic procedures and investigated by scanning electron microscopy (SEM) using a LEO 1455VP microscope (Zeiss, Jena, Germany) operated with an acceleration voltage of 25 kV. For visualization of material contrast, a backscattered electron (BSE) detector was used. The chemical composition was determined by coupled energy-dispersive x-ray spectroscopy (EDS) using a calibrated EDS GENESIS (EDAX, Mahwah, NJ, the USA) system for standardless quantitative measurements. Therefore, area analyses at a magnification of 500x have been performed. For both coating types, a measurement area of approximately 40,000 lm 2 was investigated. At least three measurements have been conducted to determine the average value. For the conducted measurements, a standard deviation in the range of ± 0,1-0,2 at.% occurred. Furthermore, the porosity was determined by optical microscopy image analyses using a GX51 microscope (Olympus, Shinjuku, Japan) and the Stream software (Olympus, Shinjuku, Japan). Ten images, which were taken with a magnification of 500x, have been considered to determine the average and standard deviation. X-ray diffraction (XRD) measurements were conducted to determine the phases formed using a D8 Discover diffractometer (Bruker, Billerica, MA, the USA). For all investigations, a diffraction angle range (2h) of 20°to 130°w as considered using Co Ka radiation. The roughness (R a , R z ) of the coatings in the as-sprayed condition was determined by tactile measurements using a Hommel-Etamic T8000 device (Jenoptik, Villingen-Schwenningen, Germany) according to ISO 4288 ( Ref 24) . Across the coating cross-sections, the coating microhardness value (HV 0.1) was determined with a Wilson Tukon 1102 device (Buehler, Uzwil, Switzerland). Ten measurements have been considered to calculate the average value and standard deviation. Prior to the corrosion investigations, the surface of the coatings was ground down to Grit 4000 (US#1200). For the investigation of pitting resistance and passivation behavior, potentiodynamic polarization curves were recorded in 0.5 M NaCl and 0.05 M H 2 SO 4 aerated electrolytes. A circular sample surface with a diameter of 10 mm was investigated. For all measurements, a three-electrode arrangement with a Pt sheet (2 9 2 cm 2 ) as a counter electrode was used. A reference electrode Ag/AgCl (saturated KCl) as well as a Haber-Luggin capillary was applied. The tests were conducted at room temperature with a PS6 potentiometer (Sensortechnik Meinsberg, Meinsberg, Germany). At least three measurements were made for each coating and test condition. The test parameters are summarized in Table 3 . The corrosion potential (E corr ) and the corrosion current density (i corr ) were determined by fitting the Butler-Volmer equation in the proximity of E corr . Therefore, a range of approximately ± 20 mV around E corr has been considered. For the investigation of the predominant corrosion mechanisms, potentiodynamic polarization measurements were conducted and interrupted at a defined current density of 2 mA/cm 2 to enable direct comparability. The surface of the samples was investigated with a VHX 500 digital microscope (Keyence, Osaka, Japan) to evaluate the corrosion mechanisms. The morphology and microstructure of the feedstock powders were investigated. Typical images of particle cross-sections obtained using a BSE detector for material contrast visualization are shown in Fig. 1 . A predominantly spherical morphology can be observed for the feedstock, which is typical for gas-atomized powder. Within bigger particles, a dendritic structure is formed. However, no distinct material contrast occurs, which indicates that there is no deviation of the local chemical The cross-section microstructures of the coatings were investigated by SEM. Typical microstructures are shown in Fig. 2 . At low magnification, a lamellar structure can be observed in the AlCrFeCoNi coating produced by HVOF. Oxide lamellae and pores are partially formed between the spray particles. Image analyses revealed a porosity of 0.6 ± 0.2%. In accordance with the feedstock powder, a dendritic structure can be observed at higher magnification within single spray particles. However, no distinct material contrast occurs. For the coatings produced by HVAF, no distinct oxide lamellae are formed due to the reduced thermal input in the coating process and the corresponding suppression of oxygen pick-up during spraying. In addition, the porosity is reduced in comparison to the HVOF coatings to a value of 0.3 ± 0.1%. At higher magnification, the dendritic structure of the feedstock powder particles can be observed. The chemical composition of the powder and coatings was measured by EDS. The results are summarized in Table 4 . In comparison to the nominal composition, no significant deviation appears to occur during the atomization to produce the feedstock powder. The processing by HVOF and HVAF thermal spraying also causes no significant changes in composition. The phase constitution of the feedstock and coatings was analyzed by XRD. The resulting diffractograms are shown in Fig. 3 . The diffraction peaks of the atomized powder can be assigned to a bcc phase. The superstructure peak at a diffraction angle of 36.3°({100} peak) indicates the formation of a chemically ordered B2 structure. The formation of this primary phase is in accordance with previous investigations on arc-melted alloys of the same composition, which revealed the formation of a single-phase bcc (B2) structure as well (Ref 11). The cooling conditions in arc-melting and atomization processes suppress the formation of additional phases, which have been detected for alternative production routes and additionally heat-treated material (Ref 12, 13) . The processing of the feedstock by HVOF or HVAF thermal spraying also causes no changes in the phase composition. A bcc (B2) phase has been determined in all conditions. The evaluation of the lattice parameter revealed a value of a = 2.87 Å for all states. No influence of the production route on the lattice parameter could be observed due to the low thermal input of both coating processes. The influence of the production route on the resulting surface properties was investigated. The roughness values of the coatings are summarized in Fig. 4 . Roughness values of R a : 4.6 ± 0.1 lm and R z : 31.4 ± 1.1 lm have been determined for the HVOF coating, whereas processing of the feedstock with reduced particle size by HVAF results in decreased roughness values of R a : 4.0 ± 0.2 lm and R z : 27.4 ± 2.0 lm. Therefore, the effort for mechanical finishing of the coatings can be reduced. Microhardness measurements revealed values of 600 ± 50 HV 0.1 for the HVOF coatings. For the coatings produced by HVAF, an increased microhardness of 680 ± 20 HV 0.1 was determined. This behavior might be caused by the finer powder fraction, resulting in a decreased grain size. Furthermore, the standard deviation is reduced, indicating the formation of a more homogeneous coating in the case of HVAF. This further corroborates the results from J Therm Spray Tech the microstructural investigations discussed above, where a lower content of oxide lamellae and porosity is present. The corrosion and passivation behavior was investigated by potentiodynamic polarization tests using NaCl and H 2 SO 4 electrolytes. Typical potentiodynamic polarization curves are shown in Fig. 5 . No passivation of both coating types can be observed for the measurements in 0.5 M NaCl For investigations to gain insight into the corrosion mechanisms, the surface of the specimens was examined after they were subjected to corrosion testing, which has been interrupted at a current density of 2 mA/cm 2 . Light microscopic images of the sample surface are shown in Fig. 6 . For both coating types tested in NaCl electrolyte pitting corrosion occurs at low current densities. Cracks and localized corrosion attack can be observed. However, investigation of cross-sections reveals that these are limited to the surface. For low current densities, no penetration of the electrolyte or delamination of the coating could be observed. With increasing current density, extensive delamination and coating failure occurred. In contrast to previous investigations on APS coatings of the same composition, there is no passivation for the investigated test conditions ( Ref 22) . Light microscopic images of the sample surface after corrosion investigation in H 2 SO 4 electrolyte are shown in Fig. 6(b) . Both coating types revealed no distinct corrosion reactions, although the specimens were subjected to corrosion well past the passive region. For specimens investigated in the full potential range (-1000 to ?1800 mV) in H 2 SO 4 , neither severe corrosion attack nor delamination could be observed. Only a thin layer at the surface is affected. Previous potentiodynamic investigation of the spark plasma sintered HEA AlCrFeCoNi in H 2 SO 4 electrolyte revealed a distinct passivation, although a multiphase microstructure was formed due to the different production conditions ( Ref 20) . The average characteristic values for both corrosion types are summarized in Table 5 . The comparison of both coating types tested in NaCl electrolyte reveals a slightly nobler E corr for the HVOF coating. However, i corr is reduced by a factor of two for the HVAF coating. The investigation of the passivation behavior in H 2 SO 4 electrolyte reveals distinct differences between both coating types. While E corr is not significantly affected by the coating type, i corr is distinctly reduced for the HVAF coating. Furthermore, the passivation current density is reduced as well. In the passive region, the HVAF coatings show a lower mean current density (0.013 vs. 0.073 mA/cm 2 ) compared to the HVOF coatings, which indicates the formation of a denser and more protective passive layer. For both coating types, a slight increase in current density with increasing potential can be observed in the passive region. This might be caused by the roughening of the surface due to the corrosion process, which results in a larger surface and hence increased current. The pitting potential is not significantly influenced by the coating process (947 vs. 957 mV), which seems to be determined by the chemistry of the coating. Inert gas-atomized feedstock of the HEA AlCrFeCoNi was successfully processed by HVOF and HVAF thermal spraying. Due to the low thermal input, the bcc (B2) structure can be retained in both coating types. The content of pores and oxides is reduced in the HVAF coatings. Furthermore, the roughness of the HVAF coatings in the as-sprayed condition is reduced in comparison to the HVOF coatings. Hardness measurements revealed an increased hardness for the HVAF coatings, which is also affected by the processing of feedstock with a reduced particle size. Detailed investigations of the corrosion behavior have been conducted to determine the resistance against pitting and the passivation behavior. Therefore, potentiodynamic polarization tests in NaCl and H 2 SO 4 electrolyte have been conducted. No passivation was observed in both coating types when tested in NaCl electrolyte. However, the corrosion current density is distinctly reduced for the HVAF coatings. Investigation of the passivation behavior in H 2 SO 4 electrolyte also reveals significant differences between both coating types. While a passive region can be observed J Therm Spray Tech in both coating types, the passivation current density and the current density in the passive region are distinctly reduced in case of the HVAF coating. This indicates an improved passivation behavior and the formation of a denser and more protective passive layer. The coating process of HVAF thermal spraying shows a high potential for the processing of HEAs, enabling the production of coatings with reduced structural defects and increased hardness. Due to the high cooling speeds in the atomization process, a metastable single-phase state is adjusted for the equimolar AlCrFeCoNi powder. This state is retained for the HVOF and HAVF coatings because of the low thermal input in the coating process. In comparison with coatings produced by HVOF thermal spraying, the corrosion resistance in both NaCl and H 2 SO 4 electrolytes is improved for the HVAF coatings. the Free State of Saxony, is gratefully acknowledged. The authors thank Elke Benedix for the corrosion investigations, Christian Loos and Paul Seidel for metallographic preparation and assistance with optical microscopy image analyses, and Morgan Uland for English proofreading. Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons. org/licenses/by/4.0/. Funding Open Access funding enabled and organized by Projekt DEAL. High-Entropy Alloys High-Entropy Alloys: Fundamentals and Applications New Multiphase Compositionally Complex Alloys Driven by the High Entropy Alloy Approach Thermal Spray High-Entropy Alloy Coatings: A Review High Entropy Alloy Coatings and Technology Microstructure and Wear Resistance of AlCoCrFeNiTi High-Entropy Alloy Coatings Produced by HVOF, Coatings Wear Behavior of HVOF-Sprayed Al 0.6-TiCrFeCoNi High Entropy Alloy Coatings at Different Temperatures Advanced Coatings by Thermal Spray Processes ASM Handbook: Volume 5 A Thermal Spray Technology Single-phase High-entropy Alloys -A Critical Update Influence of Titanium on Microstructure, Phase Formation and Wear Behaviour of AlCoCrFeNiTi x High-Entropy Alloy Heat Treatment Impacts the Micro-structure and Mechanical Properties of AlCoCrFeNi High Entropy Alloy Effect of Heat Treatment on the Phase Evolution and Mechanical Properties of Atomized AlCoCrFeNi High-entropy Alloy Powders Phase Separation in Equiatomic AlCoCrFeNi High-entropy Alloy Phase Composition of Al x FeNiCrCo High Entropy Alloys Prepared by Sintering and Arc-melting Methods Microstructure evolution and Mechanical Properties of Atmosphere Plasma Sprayed AlCoCrFeNi High-entropy Alloy Coatings Under Post-annealing Microstructure and Wear Behavior of the High-Velocity-Oxygen-Fuel Sprayed and Spark Plasma Sintered High-Entropy Alloy AlCrFeCoNi Corrosion of High Entropy Alloys, npj Mater. Degrad Corrosion Mechanism of an Equimolar AlCoCrFeNi High-Entropy Alloy Additively Manufactured by Electron Beam Melting, npj Mater. Degrad Mechanical and Corrosion Properties of AlCoCrFeNi High-Entropy Alloy Prepared by Spark Plasma Sintering Effect of Crystal Structure and Grain Size on Corrosion Properties of AlCoCrFeNi High Entropy Alloy Frictional Wear, and Corrosion Behavior of AlCoCrFeNi High-Entropy Alloy Coatings Synthesized by Atmospheric Plasma Spraying Evolution of Microstructure, Mechanical and Corrosion Properties of AlCoCrFeNi High-entropy Alloy Prepared by Direct Laser Fabrication Geometrical Product Specifications (GPS) -Surface texture: Profile method -Rules and procedures for the assessment of surface texture Acknowledgments The financial support of this work by the German Research Foundation (Deutsche Forschungsgemeinschaft/DFG), project number La-1274/54-1, as well as Sächsische Aufbaubank-Förderbank/SAB-100382175 by the European Social Fund ESF and