key: cord-0066250-ffivf6je authors: Andrzejczuk, Mariusz; Lewandowska, Małgorzata; Latuch, Jerzy; Kurzydłowski, Krzysztof Jan title: Multiscale characterization of nanostructured Al–Si–Zr alloys obtained by rapid solidification method date: 2011-08-01 journal: J Mater Sci DOI: 10.1007/s10853-011-5487-7 sha: 91187a393aa324df8f8be2dad2f9accb83c537e9 doc_id: 66250 cord_uid: ffivf6je Properties of engineering metallic alloys (e.g., fracture toughness, corrosion resistance) are often limited by the presence of primary intermetallic particles which form during conventional solidification. Rapid solidification brings about much more homogenous amorphous and/or nanocrystalline structure with reduced density of primary particles. Rapidly solidified thin ribbons obtained by melt spinning are usually considered as intrinsically homogenous. However, due to different cooling conditions at the wheel surface and on the side exposed to the ambient environment, structure of such ribbons may vary significantly across its thickness. The materials studied in this study were 30–40 μm thickness ribbons of nanocrystalline hyper- and hypo-eutectic Al–Si–Zr alloys produced by melt-spinning method. Transmission electron microscopy and high resolution scanning transmission electron microscopy were used to characterize the structure homogeneity across the ribbons. Thin foils for transmission observations were prepared by focused ion beam system. Microstructural observations confirmed nanocrystalline character of Al–Si–Zr alloys. However, these observations revealed inhomogeneity of the structure across the ribbon width. Al-Si alloys have low weight, high strength, relatively low coefficient of thermal expansion and high wear resistance, which make them suitable for a number of applications [1] . Unfortunately, the conventional way of solidification of these alloys leads to coarse microstructure with relatively large brittle Si particles, which deteriorate the mechanical properties, in particular reduce plasticity and fracture toughness [2] . Rapid solidification (RS) is in general one of the efficient ways of microstructure homogenizing and refinement of metals and alloys [3] . It can be implemented in a number of techniques, including melt spinning which is one of the most popular for thin flat elements [4] . The RS route was used to obtain highly uniform nanostructures in a number of alloys, which brought about excellent mechanical and anti-corrosion properties [5] . In the case of Al-Si alloys, these properties depend also on the content of transition and rare earth elements [6, 7] . In this context, it was reported that Zr addition refines grain size and results in enhanced mechanical properties due to the formation of intermetallic particles [8] . Microstructure features of RS alloys are routinely studied/ controlled via Transmission Electron Microscopy, TEM. In the case of RS ribbons, such observations are usually performed using thin foils cut parallel to the ribbon surface, with little attention paid to the possible variation of the micro/ nano-structure as a function of the distance from the surface [2, 9] . Such an assumption is intuitively backed-up by the small thickness of the RS ribbons. On the other hand, there is a clear difference in cooling rates at wheel and air side, which may result in a significant difference near to these two surfaces of the ribbons. In this study, an attempt has been made to investigate the relevance of such differences using as an example hypo and hypereutectic Al-Si-Zr alloys. The motivation for the investigation was possible consequences of the structure differentiation for further processing of ribbons, in particular for consolidation in bulk nanocrystalline samples. Two ternary Al-Si-Zr alloys with 0.5% of Zr and different content of Si (Al 90.5 Si 9 Zr 0.5 and Al 84.5 Si 15 Zr 0.5 ) were prepared by arc melting of pure elements in argon atmosphere. The melt was ejected onto copper wheel rotating with a speed of 50 ms -1 that provides fast quenching. The obtained ribbons were 2-3 mm wide and 30-40 lm thick. The microstructure of the alloys was characterized by TEM JEOL 1200 with accelerating voltage 120 kV. The nanostructure analyses were performed with high resolution scanning transmission electron microscopy (HR-STEM) Hitachi HD-2700 equipped with energy-dispersive X-ray analysis (EDX) and operating at 200 kV. This microscope has also high angle annular dark field (HAADF) detector, which worked with collecting angle from 70 to 370 mrad that enable obtaining images with composition contrast. Specimens for HR-STEM and TEM observations were prepared in the form of thin foils with the thickness less than 100 nm by a single focused ion beam (FIB) system (Hitachi FB-2100) by lift-out preparation technique. These specimens were perpendicular to the ribbons surface to allow for through-thickness characterization of the ribbons. The microstructure of ribbons at wheel and air surfaces was observed in FIB (secondary electron mode) thanks to strong crystallographic contrast. These observations were carried out on as-melt-spun surfaces (without chemical etching). The obtained microstructures were quantitatively described in terms of grain size and shape. The grain size was determined using the equivalent diameter d, defined as the diameter of a circle with the same area that surface area of the grain. The average equivalent diameter E(d), and the coefficient of variation, CV(d), defined as the ratio of the standard deviation to the mean value, were determined. The shape of the grains was determined using the elongation parameter, defined as the ratio of the maximum diameter to the equivalent diameter of given grain d max /d. The ribbons were also investigated via X-ray diffraction (XRD), using CuK a radiation, from the air side, as it is a standard technique for their indirect characterization. Microscopic observations were carried out using FIB system to examine the structure of as-received ribbons on the wheel and air side. Based on such observations it has been found that these two sides of the melt-spun ribbons differ in their microstructures (Fig. 1) . On the air side, regular grains with well-defined grain boundaries are visible for both the alloys investigated here. Different contrast of grains is related to their various crystallographic orientations. The size and shape of these grains change with the alloy composition. In the case of Al 90.5 Si 9 Zr 0.5 , the average equivalent diameter of the grains is 270 nm whereas for Al 84.5 Si 15 Zr 0.5 it equals to 190 nm (Table 1) . It should be noted that the distribution functions of the size of individual grains are relatively wide, as indicated by the coefficient of variation reaching the value of 0.5. The average elongation factor close to 1.5 indicates slight elongation of grains. On the wheel side, the structure features grains of similar geometry, however, with 'diffused grain boundaries' (they look thick with dark contrast). As a result, the structure might be considered two-phased one, with second phase forming the grain boundaries. It should be noted that the fraction of 'grain boundary phase' is much higher in the case of Al 84.5 Si 15 Zr 0.5 alloy. The dark contrast, visible especially in Fig. 1d is related to small size of different oriented crystallites. The non-homogeneity of the microstructure across the ribbons thickness are also clearly seen in TEM images obtained for the samples cut with FIB, as shown in Fig. 2 . The microstructure close to the wheel side consists of equiaxial grains with 'diffused grain boundaries' (Fig. 2a (bottom) , c). The measured size of Al grain is around 300 nm for both alloys and well corresponds to that estimated from FIB images. This indicates that the grains on the wheel side have regular shape in three dimensions. The wheel side zone of equi-axial grains is limited to about 20 lm in thickness. In contrast to the geometry of grains at the wheel side, in the areas close to the air side, elongated columnar aluminium grains, perpendicular to the surface are observed (Fig. 2a (top), b) . These elongated grains have few hundreds of nanometer in width which well corresponds to the size of grains observed in FIB on the air side of the ribbon. The length of columnar grains is up to 10 lm. A selected area electron diffraction (SAED) pattern taken from the area of 3 lm in diameter, close to the air side of rapidly solidified Al 84.5 Si 15 Zr 0.5 , is given as an inset in Fig. 2b . The figure shows spots of Al phase and rings of silicon phase. Such a diffraction pattern indicates relatively coarse aluminium grains and nanocrystalline silicon phase. Element mapping by energy-dispersive X-ray spectrometry (EDS) from the area close to the wheel side have shown that grain boundaries feature higher silicon content (Fig. 3) . Grain interiors are rich in aluminium with homogenous distribution of Si. It should also be noted that analysed signal for zirconium is very weak, so we can not definitely say that distribution of zirconium is homogeneous. More detailed investigations, at higher magnifications, revealed that the 'grain boundary phase' on the wheel side consists of homogenously distributed Si-rich nanoprecipitates embedded in Al matrix (Fig. 4) . Their diameter does not exceed 50 nm. No precipitates have been observed inside equi-axial grains. Such a structure (aluminium primary grains with eutectic consisting of Si nano-precipitates embedded in Al matrix) revealed for both alloys is typical for hypoeutectic solidification although Al 84.5 Si 15 Zr 0.5 alloy has hypereutectic composition and during traditional casting solidifies as hypereutectic. The difference comparing to conventional casting is the size of Si precipitates (few microns for conventional and nanometric for RS). A HR-STEM image of a Si nano-precipitate with [110] zone axis is presented in Fig. 5 . The image reveals multitwin structure of the precipitates, typical for RS of Al-Si alloys [10] . Nanosized precipitates are also observed on the air side (Fig. 6) . However, at this side, they are located not only at grain boundaries but also homogenously spaced inside columnar grains. The size of precipitates in this case is similar to the size of Si nanoprecipitates on the wheel side of the ribbons and does not exceed 50 nm. Observations under higher magnification (Fig. 6b , c) indicate that nano-precipitates on air side differ in their chemical composition. It is clearly visible in the HAADF-STEM image (Fig. 6c) where the contrast is related to chemical composition-brighter regions contain heavier elements. Precipitates located at the boundaries of columnar grains are brighter that suggests higher concentration of Si. It should be noted that the precipitates at grain boundaries are larger than those inside grains. Observations in BF-STEM mode (Fig. 6b ) revealed fine areas with darker contrast, which are weakly visible in HAADF-STEM mode. It might indicate that these areas are Al nanocrystals embedded in supersaturated aluminium matrix. Similar precipitates of fcc a-Al were observed in rapidly solidified Al-Si-Cu-Mg alloys [11] . The lattice parameters of a-Al phase estimated from the XRD pattern for both alloy, (Al 90.5 Si 9 Zr 0.5 -0.40357 nm, Al 84.5 Si 15 Zr 0.5 -0.40370 nm) is smaller than that of pure aluminium (0.40497 nm). This suggests relatively high Si content in a-Al phase, as the lattice parameter of a-Al decreases linearly with increasing silicon content in solid solution [12] . The difference of lattice parameter in two alloys is negligible. High resolution, multi-technique characterization of the rapidly solidified ribbons of Al-Si-Zr alloys has revealed their complex nano-and micro-structure with clearly defined wheel and air sub-layers. The wheel sub-layer features equiaxial Al grains 300 nm in diameter with Si nanoparticles embedded in Al matrix in grain boundaries (inter-grain phase). The air side sub-layer reveals columnar Al grains with nanoparticles homogenously distributed in the grain interiors. It should be noted that only minor differences in the structure of the ribbons were observed, despite the fact that the investigated alloys had hypo-and hyper-eutectic chemical compositions. The results reported here give a new insight into nanostructure of RS Al-Si alloys which are routinely studied via observations on in-plane thin foils providing simplified image of the true structure. Similarly, XRD studies do not account for the complexity of the structure of such materials. The new comprehensive description presented here can be also used to characterize the structure of RS alloys with other chemical compositions which are often considered as homogenous through the thickness. XRD pattern of as-melt-spun Al 90.5 Si 9 Zr 0.5 and Al 84.5 Si 15 Zr 0.5 ribbons Acknowledgements This study was carried out within a NANO-MET project financed under the European Funds for Regional Development (Contract No. POIG.01.03.01-00-015/08).Open Access This article is distributed under the terms of the Creative Commons Attribution Noncommercial License which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.