key: cord-0061285-3azdgqi2 authors: Al Saqr, Ahmed; Khafagy, El-Sayed; Alalaiwe, Ahmed; Aldawsari, Mohammed F.; Alshahrani, Saad M.; Anwer, Md. Khalid; Khan, Salman; Lila, Amr S. Abu; Arab, Hany H.; Hegazy, Wael A. H. title: Synthesis of Gold Nanoparticles by Using Green Machinery: Characterization and In Vitro Toxicity date: 2021-03-22 journal: Nanomaterials (Basel) DOI: 10.3390/nano11030808 sha: e9064e80998a4bf7b7b04cf925fcf99781b47e6a doc_id: 61285 cord_uid: 3azdgqi2 Green synthesis of gold nanoparticles (GNPs) with plant extracts has gained considerable interest in the field of biomedicine. Recently, the bioreduction nature of herbal extracts has helped to synthesize spherical GNPs of different potential from gold salt. In this study, a fast ecofriendly method was adopted for the synthesis of GNPs using fresh peel (aqueous) extracts of Benincasa hispida, which acted as reducing and stabilizing agents. The biosynthesized GNPs were characterized by UV–VIS and Fourier transform infrared spectroscopy, transmission electron microscopy (TEM), and dynamic light scattering. In addition, the in vitro antibacterial and anticancer activities of synthesized GNPs were investigated. The formation of gold nanoparticles was confirmed by the existence of a sharp absorption peak at 520 nm, corresponding to the surface plasmon resonance (SPR) band of the GNPs. TEM analysis revealed that the prepared GNPs were spherical in shape and had an average particle size of 22.18 ± 2 nm. Most importantly, the synthesized GNPs exhibited considerable antibacterial activity against different Gram-positive and Gram-negative bacteria. Furthermore, the biosynthesized GNPs exerted remarkable in vitro cytotoxicity against human cervical cancer cell line, while sparing normal human primary osteoblast cells. Such cytotoxic effect was attributed to the increased production of reactive oxygen species (ROS) that contributed to the damage of HeLa cells. Collectively, peel extracts of B. hispida can be efficiently used for the synthesis of GNPs, which can be adopted as a natural source of antimicrobial and anticancer agent. The increasing antimicrobial resistance has become one of the major public health challenges especially in the era of decreased discovery of new safe antimicrobial agents [1, 2] . Several approaches have been exploited to renew the available antimicrobial chemotherapeutic options [3] [4] [5] . Currently, nanotechnology holds promise as an emerging technology for developing new antimicrobial agents with expanding properties such as efficient targeting, improvement of pharmacokinetic profile, and reduction of toxicity [5, 6] . Gold nanoparticles (GNPs) are emerging materials that exhibit optical and electrical characteristics distinct from those of traditional materials and show promising potential for Staphylococcus aureus (ATCC 25923), Eschrichia coli (ATCC 25922), Salmonella abony (ATCC BAA-2162), and Klebsiella pneumonia (ATCC 13883) were used to test the antibacterial activity of GNPs. The bacterial strains were cultivated and maintained at 37 • C on MH agar media. The normal human primary osteoblasts and human cervical cancer cells (HeLa) were supplied from National Centre for Cell Science (NCCS), Pune, India. The cell lines were grown as monolayer in MacCoy's and DMEM media with supplementation of 10% fetal bovine serum and 1% actinomycin. The cell lines were subcultured and maintained under a humidified atmosphere at 37 • C. Fresh peel of B. hispida were collected, rinsed repeatedly with distilled water to remove any impurities from their surfaces. Then, the fresh peel was cut into small pieces, ground with double distilled water using pestle mortar placed in a tray filled with ice to avoid protein denaturation. The mixture was filtered using the Whatman ® Grade 42 filter paper followed by centrifugation at 6000 rpm for 15 min. The supernatant was collected, filtered and finally the aqueous was stored at 4 • C for further use in the synthesis of GNPs. Gold nanoparticles were synthesized by the reduction method using 1 mM aqueous gold salt solution. Briefly, equal volumes of gold salt solution and aqueous peel extracts were mixed together to give a final volume of 30 mL. The mixture was held at 40 • C for 24 h. Upon incubation, the solution color changes from light green to ruby red, indicating the completion of reaction. The mixture was then filtered using a 2 µm syringe filter and unbound proteins were separated by precipitation with absolute ethanol. Finally, the obtained gold nanoparticles were kept at 4 • C for further experiments. The reduction of gold salts into gold nanoparticles was confirmed by using dualbeam UV-VIS spectroscopy (Shimadzu dual-beam spectrophotometer UV-1601 PC Series, Shimadzu, Tokyo, Japan) operated at a resolution of 1 nm in the range of 200 to 800 nm. This technique depends on color change owing to the reduction of metal salts to biosynthesized gold nanoparticles. The hydrodynamic radius of the prepared nanoparticles was estimated by dynamic light scattering (DLS). Both particle size and zeta potential were measured using a Zetasizer Nano-ZS (ZEN3600 Malvern Instrument Ltd., Malvern, UK). Transmission electron microscopy was adopted to investigate the morphology and size of the gold nanoparticles. One drop of GNPs suspension was distributed onto carboncoated TEM copper grids followed by analysis on a Tecnai G2 Spirit transmission electron microscope equipped with a BioTwin lens configuration (Hillsboro, OR, USA), operated at an accelerating voltage of 80 kV. FTIR spectroscopy was used to trace the existence of different functional groups at the surface of GNPs. The spectrum was obtained by a Perkin-Elmer Spectrum FTIR system (PerkinElmer Inc., Waltham, MA, USA) at the range of 650-4000 cm −1 . The antibacterial activities of synthesized GNPs were evaluated against various Gramnegative and Gram-positive bacterial strains. Synthesized GNPs were dispersed in phosphate buffer saline (PBS) and the prepared solutions were used at pH 7.2. To determine the ability of synthesized GNPs to inhibit bacterial growth, the agar diffusion method was used according to the Clinical Laboratory and Standards Institute Guidelines (CLSI 2015) [38] . Standardized suspensions of the tested strains (equivalent to the 0.5 McFarland) were prepared from overnight cultures in TSB and swabbed over the surface of Müeller-Hinton agar plates. Equal amounts of GNPs (10 µg/mL) and PBS as negative control were added to the wells made in MH agar plates. The experiment was carried out in triplicate and the plates were incubated at 37 • C overnight and the diameters of inhibition zones were measured. The minimum inhibitory concentrations (MICs) of synthesized GNPs against tested bacterial strains were determined using the broth microdilution method according to CLSI (2015) [4]. Aliquots of GNPs were serially diluted in 96-well microtiter plates containing TSB medium to achieve a range of concentrations (0.1-120 µg/mL). Aliquots (10 µL) from prepared standard suspensions of tested strains, which were cultured overnight in TSB and their optical densities were adjusted to OD600 of 0.4 (2 × 10 5 CFU/mL), were added to each well. The MICs were the lowest concentrations of synthesized GNPs that completely inhibited the bacterial growth after incubation at 37 • C for 20 h and the bacterial cells were viably counted from each well. Meanwhile, the lowest concentrations of GNPs that showed no visible growth upon subculturing onto fresh medium were considered minimum bactericidal concentrations (MBCs) [38] . Colistin sulfate was used as a positive control, sterile PBS was involved as a negative control, and the experiment was repeated in triplicate. To assess the cytotoxic effects of GNPs against cancerous (HeLa; human cervical cancer cells) and normal human primary osteoblasts, MTT cytotoxicity colorimetric assay was performed [36] . Briefly, the cells (1 × 10 4 cells per well) were plated in a 96-well plate and incubated for 24 h at 37 • C. The cell lines were treated with GNPs at different concentrations ranging from 0.62 to 20 µg/mL in triplicates and incubated for 48 h. Ten µL of the MTT reagent (0.5 mg/mL) was then added to each well and the plates were further incubated for 4 h. Then, 150 µL DMSO was added to each well to solubilize formazan crystals. Cell viability was quantified by measuring the optical densities (OD) at 570 nm with a reference filter of 655 nm using a Microplate Reader (BIORAD-680). The untreated HeLa cells were pretreated GNPs (at their IC 50 ) and were incubated at 37 • C in 5% CO 2 . At 48 h post incubation, gross morphological changes in the cells were observed using an inverted phase contrast microscope (Nikon ECLIPSE Ti-S, Tokyo, Japan). DAPI (4 , 6-diamidino-2-phenylindole), a fluorescent nuclear dye was used to assess the apoptotic potential at IC 50 concentrations of GNPs on HeLa cell line [36] . An inverted fluorescence magnifying microscope (Nikon ECLIPSE Ti-S, Japan) was utilized to capture images of stained cells. The intensities of fluorescence in treated HeLa cells with GNPs in IC 50 in comparison to untreated cells were measured by J-image program. The mean signal intensities and standard deviations for at least 50 treated cells were calculated. In order to detect the effect of GNPs on ROS production, treated and untreated HeLa cells with GNPS in IC 50 for 48 h at 37 • C were stained with fluorogenic reagent H2DCFDA [39] . An inverted fluorescence magnifying microscope (Nikon ECLIPSE Ti-S, Japan) was used. The intensities of fluorescence in GNPs (IC 50 ) treated HeLa cells in comparison to untreated cells were measured by the J-image program. The mean signal intensities and standard deviations for at least 50 treated cells were calculated. In this study, B. hispida was used as both a reducing and stabilizing agent, and HAuCl 4 (1 mM) acted as the gold precursor. It was proposed that aqueous peel extract triggers the formation of GNPs by the aid of its reducing enzymes as well as capping agents like secondary metabolites, which synergistically reduce AuCl 4 (+3 oxidation state) into Au (0 oxidation state). The reduction of HAuCl4 was visibly detected by color change of B. hispida peel extract from green into ruby red color, confirming the formation of GNPs. The surface plasmon resonance (SPR) represents a peculiar phenomenon to noble metal nanoparticles that contributes to intense electromagnetic fields on the particle surface, which in turn increases all radiative properties such as scattering and absorption [40] . Herein, therefore, the formation of GNPs was confirmed by UV-VIS spectra ( Figure 1A ). Sharp absorption peaked at 520 nm, corresponding to the surface plasmon resonance (SPR) band of the GNPs [41] . However, no obvious peak was observed for B. hispida peel extract. The average particle size and particle size distribution profile of the prepared GNPs were determined using the dynamic light scattering (DLS) technique. As shown in Figure 1B , GNPs had an average particle size of 70 nm with a polydispersity index (PDI) of 0.219, indicating homogenous size distribution. The zeta potential of GNPs was also investigated ( Figure 1C ). Generally, a zeta value of ±20 mV is needed for colloidal stability of nanoparticles [42] . The zeta potential of the prepared GNPs was −26 mV, indicating high stability of the particles. No signs of agglomeration or clumping were observed in the aqueous dispersion of GNPs upon storage at room temperature, presumably due to the electrostatic repulsive forces between the nanoparticles, which hinder nanoparticles from getting closer to each other. The average particle size and particle size distribution profile of the prepared GNPs were determined using the dynamic light scattering (DLS) technique. As shown in Figure 1B , GNPs had an average particle size of 70 nm with a polydispersity index (PDI) of 0.219, indicating homogenous size distribution. The zeta potential of GNPs was also investigated ( Figure 1C ). Generally, a zeta value of ±20 mV is needed for colloidal stability of nanoparticles [42] . The zeta potential of the prepared GNPs was -26 mV, indicating high stability of the particles. No signs of agglomeration or clumping were observed in the aqueous dispersion of GNPs upon storage at room temperature, presumably due to the electrostatic repulsive forces between the nanoparticles, which hinder nanoparticles from getting closer to each other. TEM analysis was adopted to investigate the morphology, shape, and size of GNPs. TEM micrographs ( Figure 1D ) depicted that GNPs were spherical in shape and uniformly distributed without significant agglomeration. The average size of GNPs determined by TEM was 22.18 ± 2 nm, which was comparatively smaller than that determined by the DLS technique. The particle size estimated by TEM represents the exact diameter of particles as measured in the dry state, while the size determined by the DLS technique is a hydrodynamic diameter (hydrated state). Consequently, the particles will show larger hydrodynamic volume due to the solvent effect in the hydrated state [43] . FTIR spectroscopy was performed to determine the potential functional groups in the synthesized GNPs ( Figure 1E ). The spectra of GNPs showed characteristic absorption peaks at 1639 cm −1 corresponding to C=O groups. A medium-wide shoulder, corresponding to amide I linkage and amide II band, was observed at 1455 cm −1 due to carboxyl stretch and N-H twist in the amide bond of the proteins, which were capped, or surface modified on the GNPs [44] . The peak at 3285 cm −1 was due to the N-H stretch vibration, which depends on the strength of hydrogen bonding rather than backbone confirmation [45] . In addition, ether and alcohol groups (C-O-C/C-OH) C-O stretching, and C-N (aliphatic amine) stretching vibration were observed at 1083 cm −1 . To ensure the antibacterial activities of GNPs, it was tested against various bacterial strains Gram-negative Escherichia coli (E. coli), Salmonella abony (S. abony), and Klebsiella pneumonia (K. pneumonia) and Gram-positive Staphylococcus aureus (S. aureus). The tested strains were selected to represent different bacterial machineries that harbor different arsenals of virulence factors, besides their noticeable pathogenies and high prevalence in our life [46, 47] . Initial findings revealed the ability of GNPs to diffuse in agar and inhibit bacterial growth (Figure 2 ). GNPs inhibited the growth of E. coli, S. abony, K. pneumonia, and S. aureus at concentrations MIC 50 21.6, 20.2, 13.8, and 26.9 µg/mL, respectively ( Figure 3) . Furthermore, the MBC values of GNPs against E. coli, S. abony, K. pneumonia, and S. aureus strains were determined to be 80.8, 84.5, 65.5, and 111.5 µg/mL, respectively. Similar findings were shown by Soliman et al. who verified the potent antibacterial activity of silver nanoparticles prepared by aqueous B. hispidia extract against different pathogenic bacteria [36] . Nevertheless, it appeared that silver nanoparticles exerted superior antibacterial activity against different pathogenic bacteria, compared to GNPs. The enhanced antibacterial activity of silver nanoparticles might be ascribed to the inherent antimicrobial properties of silver ions, compared to gold ions [48] . Gold has been appreciated as the inorganic antibacterial agent of choice to combat infections and spoilage since ancient times. In the current study, GNPs inhibited a broad spectrum of bacteria, this owed to several mechanisms. In addition to high penetrative 46, 47] . Moreover, new approaches were developed to improve the distribution, penetration, targeting, and pharmacokinetics of antimicrobial drugs; one of these is drug nanoparticle formulations [36, 38] . Metallic nanoparticles were employed for delivering antimicrobials efficiently, showing a magnificent enhancement in targeting and improvement of pharmacokinetics [5, 6, 8, 9, 28, 49] . Moreover, metallic nanoparticles were shown to have antimicrobial activities, and efficiently synergized the antimicrobial activity of natural product [6, 13, 14] . Gold has been appreciated as the inorganic antibacterial agent of choice to combat infections and spoilage since ancient times. In the current study, GNPs inhibited a broad spectrum of bacteria, this owed to several mechanisms. In addition to high penetrative power of GNPs, they target bacterial cell membrane, cell wall, DNA, and proteins [12, 24, 36, 50] . It has been repeatedly reported that GNPs can generate pits in bacterial membrane and cell wall. It was shown that GNPs can target cell membrane subcellular compartments, creating pits and leading to cellular decomposition and death. Furthermore, GNPs destroy the glycan N-acetylglucosamine and N-acetylmuramic acid linkage and create a link between the peptide surface and glycan ports of the cell wall, resulting in pit generation in cell walls [51] . In addition to cidal targeting of GNPs to cellular membrane and cell wall, GNPs have been demonstrated to target more bacterial targets as respiratory chain dehydrogenases and bacterial chromosome [9, 12, 52] . Moreover, the ability of metallic nanoparticles to release reactive oxygen species (ROS), which slow the oxidation of liberated gold ions, confers an additional biocidal activity [9, 53] . In this study, the toxic effects of GNPs were evaluated on cancer HeLa cells and normal osteoblasts cell line using MTT assay. The cell viability was screened at different GNPs concentrations (0.62, 1.25, 2.5, 5, 10, and 20 µg/mL). As shown in Figure 4 , HeLa cells rapidly lose their viability upon incubation with GNPs at a concentration range of 0.62 to 20 µg/mL. The estimated IC 50 value of GNPs on HeLa cells was 2.25 µg/mL. Of interest, GNPs were found to be less cytotoxic against primary osteoblasts, even at higher acceptable biological limit (20 µg/mL). Cancer selectivity of GNPs might be ascribed to the preferential uptake of GNPs by cancer cells compared to normal cells, apparently due to atypical metabolism and increased proliferation rate of cancer cells, compared to the longer doubling time of normal osteoblasts (>96 h) [54, 55] . Similar findings were reported by Soliman et al. who emphasized the potent cytotoxic effect of silver nanoparticles prepared by aqueous extract of B. hispida against HeLa cancer cells, compared to normal osteoblasts [36] . In this study, the toxic effects of GNPs were evaluated on cancer HeLa cells and normal osteoblasts cell line using MTT assay. The cell viability was screened at different GNPs concentrations (0.62, 1.25, 2.5, 5, 10, and 20 µg/mL). As shown in Figure 4 , HeLa cells rapidly lose their viability upon incubation with GNPs at a concentration range of 0.62 to 20 µg/mL. The estimated IC50 value of GNPs on HeLa cells was 2.25 µg/mL. Of interest, GNPs were found to be less cytotoxic against primary osteoblasts, even at higher acceptable biological limit (20 µg/mL). Cancer selectivity of GNPs might be ascribed to the preferential uptake of GNPs by cancer cells compared to normal cells, apparently due to atypical metabolism and increased proliferation rate of cancer cells, compared to the longer doubling time of normal osteoblasts (>96 h) [54, 55] . Similar findings were reported by Soliman et al. who emphasized the potent cytotoxic effect of silver nanoparticles prepared by aqueous extract of B. hispida against HeLa cancer cells, compared to normal osteoblasts [36] . Figure 4 . Assessment of GNPs cytotoxicity and determination GNPs IC50 on cancer cells. Normal human primary osteoblasts and human cervical cancer cell (HeLa cells) were plated overnight at a density of 1 × 10 4 cell per well in a 96-well plate at 37 °C. The normal or cancer cells were treated with different concentrations of GNPs and the in vitro cytotoxicity was evaluated using MTT assay. The inhibition percentages were calculated relative to negative control and IC50 was the GNPs concentration, which inhibits 50% of HeLa cells. The experiment was conducted in triplicate and the data shown are the means ± standard errors. HeLa cells with 70% confluence were co-incubated with or without GNPs at IC50 concentration for 48 h. The phase-contrast microscopic images exhibited morphological changes in HeLa cells ( Figure 5B ) in contrast to control untreated normal cells ( Figure 5A ). Several notable changes in shape (turning into circular), loss of membrane integrity, Figure 4 . Assessment of GNPs cytotoxicity and determination GNPs IC 50 on cancer cells. Normal human primary osteoblasts and human cervical cancer cell (HeLa cells) were plated overnight at a density of 1 × 10 4 cell per well in a 96-well plate at 37 • C. The normal or cancer cells were treated with different concentrations of GNPs and the in vitro cytotoxicity was evaluated using MTT assay. The inhibition percentages were calculated relative to negative control and IC 50 was the GNPs concentration, which inhibits 50% of HeLa cells. The experiment was conducted in triplicate and the data shown are the means ± standard errors. HeLa cells with 70% confluence were co-incubated with or without GNPs at IC 50 concentration for 48 h. The phase-contrast microscopic images exhibited morphological changes in HeLa cells ( Figure 5B ) in contrast to control untreated normal cells ( Figure 5A ). Several notable changes in shape (turning into circular), loss of membrane integrity, clumping of cells, condensation of cytoplasm, and inhibition of cells growth were observed in treated HeLa cells. It is widely recognized that nanomaterials could efficiently interact with cancerous cells [6, 14] . Many reports have demonstrated the impact of particle size, morphology, surface charge, functional surface modification, and different types of cells on cellular uptake of GNPs and their subcellular distribution [56] [57] [58] . Furthermore, various strategies have been established, exploiting the physiochemical properties of GNPs themselves (passive targeting) or employing active targeting moieties to ensure efficient intracellular delivery of GNPs to cancer cells [59, 60] . In this study, the mode of cellular internalization and, subsequently, the interaction with nuclear material, were evaluated by utilizing a DAPI fluorescent dye ( Figure 5C,D) . HeLa cells treated with or without GNPs (at IC 50 value) were incubated for 48 h at 37°C and stained by the DAPI dye. Compared to untreated cells, HeLa cells treated with GNPs induced potent apoptotic effects as manifested by condensed chromatin and dark blue fluorescent consolidated nuclei, which might be ascribed to the expanded cell membrane penetrability [61] . The experiment was conducted in triplicate and the fluorescence intensities were measured; Student's t-test (Graphpad Prism 8 software) was used to compare between the fluorescence intensities in HeLa cells treated or untreated with GNPs in IC 50 ( Figure 5E ). Significantly, the fluorescence intensities were decreased (p < 0.0001) in treated cells in comparison to untreated cells, indicating GNPs apoptotic effects due to consolidation of HeLa cells' nuclei. clumping of cells, condensation of cytoplasm, and inhibition of cells growth were observed in treated HeLa cells. It is widely recognized that nanomaterials could efficiently interact with cancerous cells [6, 14] . Many reports have demonstrated the impact of particle size, morphology, surface charge, functional surface modification, and different types of cells on cellular uptake of GNPs and their subcellular distribution [56] [57] [58] . Furthermore, various strategies have been established, exploiting the physiochemical properties of GNPs themselves (passive targeting) or employing active targeting moieties to ensure efficient intracellular delivery of GNPs to cancer cells [59, 60] . In this study, the mode of cellular internalization and, subsequently, the interaction with nuclear material, were evaluated by utilizing a DAPI fluorescent dye ( Figure 5C,D) . HeLa cells treated with or without GNPs (at IC50 value) were incubated for 48 h at 37 ℃ and stained by the DAPI dye. Compared to untreated ROS-mediated toxicity is one of the mechanisms by which nanomaterials act as anticancer agents [3, 7, 10, 12] . The generated oxidative pressure due to overproduction of ROS leads to enhancement of apoptosis, resulting in considered anticancer activity of GNPs [6, 9, 50 ]. In the current study, the intracellular ROS generation in HeLa cells treated with GNPs, was estimated using an oxidation-sensitive fluorogenic marker, H2DCFDA, ( Figure 5F ,G). Intense fluorescence signals, along with vandalized morphological structure, were observed in HeLa cells treated with GNPs, indicating ROS induced plasma membrane disruption. On the other hand, control (untreated) cells did not show any remarkable fluorescence and retained their natural morphology. The experiment was conducted in triplicate and the fluorescence intensities were measured; Student's t-test (Graphpad Prism 8 software) was used to compare between the ROS production in HeLa cells treated or untreated with GNPs in IC 50 ( Figure 5H ). The production of intracellular ROS was significantly increased in HeLa cells treated with GNPs in IC 50 compared to untreated cells. GNPs ability to penetrate and efficiently distribute inside cancer cells targeting their genomic content was documented [23] [24] [25] 50] . In this study, we found that GNPs were efficiently accumulated in cancer cells' nuclei and increased the production of ROS, which can induce considerable anticancer activity. In the current study, we report a simple one-step ecofriendly method for the synthesis of GNPs using B. hispida peel extract as a reducing and stabilizing agent. The formation of GNPs was detected by color change from light green to ruby red and was confirmed by the existence of a characteristic absorption peak at 520 nm. The biosynthesized GNPs were able to inhibit the growth of various Gram-positive and Gram-negative bacterial strains with comparable competency. In addition, GNPs showed potent cytotoxic effect against HeLa cancer cell line, without exerting remarkable toxicity against normal human osteoblast cell line. Such potent cytotoxic effect was linked with a significant destruction of nuclei of cells and an increase in ROS production in cancer cells. Collectively, our results suggest that B. hispida peel extract can be efficiently utilized for green synthesis of GNPs, which can be used as a natural antibacterial and anticancer agent. However, further studies are warranted to evaluate the in vivo activities of GNPs prior to offering them as a broad platform in the field of medicine, either alone or as carriers to other drugs. The data presented in this study are available on request from the corresponding author. Discovery research: The scientific challenge of finding new antibiotics Promising antibiofilm agents: Recent breakthrough against biofilm producing methicillinresistant Staphylococcus aureus Gold-nanoparticles coated with the antimicrobial peptide esculentin-1a(1-21)NH 2 as a reliable strategy for antipseudomonal drugs Nanomaterials 2021 Sitagliptin" as a novel virulence attenuating agent in Serratia marcescens Topical antimicrobial peptide formulations for wound healing: Current developments and future prospects Antimicrobial activity and toxicity of gold nanoparticles: Research progress, challenges and prospects Biomedical applications of gold nanoparticles Synthesis of silver nanostructures with controlled shapes and properties Antimicrobial gold nanoclusters: Recent developments and future perspectives Medicinal chemistry of gold anticancer metallodrugs Antiviral potential of nanoparticles-Can nanoparticles fight against coronaviruses? Nanomaterials Intrinsic therapeutic applications of noble metal nanoparticles: Past, present and future Gold nanoparticles: Recent advances in the biomedical applications Antimicrobial activity of gold nanoparticles and ionic gold Gold nanoparticles in cancer therapy Fabrication of gold nanoparticles for targeted therapy in pancreatic cancer Targeted delivery of gemcitabine to pancreatic adenocarcinoma using cetuximab as a targeting agent Gold nanoparticles: A new X-ray contrast agent Neo-adjuvant chemotherapy alone or with regional hyperthermia for localised high-risk soft-tissue sarcoma: A randomised phase 3 multicentre study Nanoshell-enabled photothermal cancer therapy: Impending clinical impact Estimation of tumour dose enhancement due to gold nanoparticles during typical radiation treatments: A preliminary Monte Carlo study Gold nanoparticles as novel agents for cancer therapy A gold(I) complex containing an oleanolic acid derivative as a potential antiovarian-cancer agent by inhibiting TrxR and activating ROS-mediated ERS Synthesis and evaluation of gold(III) complexes as efficient DNA binders and cytotoxic agents A new rhodium(I) NHC complex inhibits TrxR: In vitro cytotoxicity and in vivo hepatocellular carcinoma suppression Recent advances of gold compounds in anticancer immunity The biological activity of auranofin: Implications for novel treatment of diseases Gold complexes for therapeutic purposes: An updated patent review Green synthesis of metallic nanoparticles and their prospective biotechnological applications: An overview Biosynthesis of nanoparticles using eco-friendly factories and their role in plant pathogenicity: A review Preparation of gold nanoparticles using Salicornia brachiata plant extract and evaluation of catalytic and antibacterial activity Biogenic gold nanoparticles synthesis mediated by Mangifera indica seed aqueous extracts exhibits antibacterial, anticancer and anti-angiogenic properties Synthesis of gold nanoparticles using mimosa tenuiflora extract, assessments of cytotoxicity, cellular uptake, and catalysis Benincasa hispida (Thunb.) Cogn.): A potential source for valuable nutrients and functional foods Anxiolytic evaluation of Benincasa hispida (Thunb) Cogn. fruit extracts. Iran Therapeutic applications of biostable silver nanoparticles synthesized using peel extract of Benincasa hispida: Antibacterial and anticancer activities Neuropharmacological effects of methanolic extracts of Rubusfruticosus L. Turk Abd El-Hamid, M.I. Thymol nanoemulsion: A new therapeutic option for extensively drug resistant foodborne pathogens Identification of ROS using oxidized DCFDA and flow-cytometry Gold nanoparticles: Optical properties and implementations in cancer diagnosis and photothermal therapy Green synthesis of gold nanoparticles by Allium sativum extract and their assessment as SERS substrate Synthesis of silver nanoparticles via green method using ultrasound irradiation in seaweed Kappaphycus alvarezii media Studies on green synthesized silver nanoparticles using Abelmoschus esculentus (L.) pulp extract having anticancer (in vitro) and antimicrobial applications Mangifera indica leaf-assisted biosynthesis of well-dispersed silver nanoparticles Synthesis of mercaptothiadiazole-functionalized gold nanoparticles and their self-assembly on Au substrates Repurposing anti-diabetic drugs to cripple quorum sensing in Pseudomonas aeruginosa Ciprofloxacin interferes with Salmonella typhimurium intracellular survival and host virulence through repression of Salmonella pathogenicity island-2 (SPI-2) genes expression Silver as an antimicrobial: Facts and gaps in knowledge Size and shape-dependent cytotoxicity profile of gold nanoparticles for biomedical applications Gold nanoparticles in diagnostics and therapeutics for human cancer The systematic evaluation of size-dependent toxicity and multi-time biodistribution of gold nanoparticles Antibacterial activity and mechanism of silver nanoparticles on Escherichia coli Surface capping and size-dependent toxicity of gold nanoparticles on different trophic levels Selective cytotoxicity of green synthesized silver nanoparticles against the MCF-7 tumor cell line and their enhanced antioxidant and antimicrobial properties Characterization of hTERT-immortalized osteoblast cell lines generated from wild-type and connexin43-null mouse calvaria Strategies in the design of gold nanoparticles for intracellular targeting: Opportunities and challenges Uptake and intracellular fate of surface-modified gold nanoparticles Determining the size and shape dependence of gold nanoparticle uptake into mammalian cells Active targeting of gold nanoparticles as cancer therapeutics Surface modification of gold nanoparticles with neuron-targeted exosome for enhanced blood-brain barrier penetration Cisplatin bioconjugated enzymatic GNPs amplify the effect of cisplatin with acquiescence The current work was supported by Taif University Researchers Supporting Project number (TURSP-2020/29), Taif University, Taif, Saudi Arabia (to Hany H. Arab). The authors declare no conflict of interest.