key: cord-0032737-49e13i98
authors: Edis, Zehra; Bloukh, Samir Haj; Sara, Hamed Abu; Azelee, Nur Izyan Wan
title: Antimicrobial Biomaterial on Sutures, Bandages and Face Masks with Potential for Infection Control
date: 2022-05-10
journal: Polymers (Basel)
DOI: 10.3390/polym14101932
sha: e393a05d99f052ec853c4155186dcc698cdcaf01
doc_id: 32737
cord_uid: 49e13i98

Antimicrobial resistance (AMR) is a challenge for the survival of the human race. The steady rise of resistant microorganisms against the common antimicrobials results in increased morbidity and mortality rates. Iodine and a plethora of plant secondary metabolites inhibit microbial proliferation. Antiseptic iodophors and many phytochemicals are unaffected by AMR. Surgical site and wound infections can be prevented or treated by utilizing such compounds on sutures and bandages. Coating surgical face masks with these antimicrobials can reduce microbial infections and attenuate their burden on the environment by re-use. The facile combination of Aloe Vera Barbadensis Miller (AV), Trans-cinnamic acid (TCA) and Iodine (I(2)) encapsulated in a polyvinylpyrrolidone (PVP) matrix seems a promising alternative to common antimicrobials. The AV-PVP-TCA-I(2) formulation was impregnated into sterile discs, medical gauze bandages, surgical sutures and face masks. Morphology, purity and composition were confirmed by several analytical methods. Antimicrobial activity of AV-PVP-TCA-I(2) was investigated by disc diffusion methods against ten microbial strains in comparison to gentamycin and nystatin. AV-PVP-TCA-I(2) showed excellent antifungal and strong to intermediate antibacterial activities against most of the selected pathogens, especially in bandages and face masks. The title compound has potential use for prevention or treatment of surgical site and wound infections. Coating disposable face masks with AV-PVP-TCA-I(2) may be a sustainable solution for their re-use and waste management.

The COVID-19 pandemic presented the most serious challenge for mankind in this century and exacerbated another "silent pandemic" of antimicrobial resistance (AMR) [1] . The severity of the COVID-19 crisis was elevated by insufficient health care support, supply shortages of personal protective equipment and existing antimicrobial resistance [1] [2] [3] [4] [5] . Resistant ESKAPE (Enterococcus faecium, Staphylococcus aureus, Klebsiella pneumoniae, Acinetobacter baumannii, Pseudomonas aeruginosa, Enterobacter spp., and Escherichia coli) pathogens augmented morbidity and mortality rates [4] [5] [6] [7] [8] [9] . ESKAPE pathogens are increasingly resistant to common antibiotics, drugs and antimicrobials due to inadequate utilization of antimicrobial agents [1, [3] [4] [5] [6] [7] [8] [9] . Global overuse of antimicrobials in hospital settings without proper surveillance during the COVID-19 pandemic escalated AMR dramatically [1] . Public and health sector settings are steadily encroached by such resistant, opportunistic absolute ethanol and ultrapure water were used. All reagents were of analytical grade and were employed as delivered.

We were kindly provided with leaves of an Aloe vera (Aloe barbadensis Miller) plant from the botanical garden of Ajman University at beginning of December between 8 and 9 am. The leaves were immediately taken to the research laboratory of the College of Pharmacy and Health Sciences. The leaves with a size between 35 to 50 cm were cleaned by tissue and then washed with water to remove dust and soil. Afterward, the clean leaves were rinsed several times with distilled water, pure ethanol, ultrapure water and dried carefully. The AV leaves were cut with a sterile knife to scrap the mucilaginous gel out. This pure gel was mixed at maximum speed for 20 min and centrifuged at 4000 rpm for 40 min (3K 30; Sigma Laborzentrifugen GmbH, Osterode am Harz, Germany). The supernatant with a light-yellow color was filled immediately into a brown bottle with a screw cap and stored in darkness at 3 • C.

The stock solution AV-PVP is prepared by adding 2 mL pure AV gel into 2 mL of a solution of 1 g polyvinylpyrrolidone K-30 (PVP) in 10 mL distilled water under continuous stirring at room temperature (RT). For the preparation of AV-PVP-TCA, first 0.148 g TCA is dissolved in 10 mL ethanol. Then, 2 mL of this solution is added to AV-PVP under continuous stirring at RT. After that, iodine solution is obtained by dissolving 0.05 g of iodine in 3 mL ethanol in a covered beaker at RT under stirring. An amount of 1 mL of this iodine solution is added to AV-PVP-TCA under continuous stirring at RT for the preparation of AV-PVP-TCA-I 2 .

The title compounds were analyzed by SEM/EDS, Raman Spectroscopy, UV-vis, FTIR and X-ray diffraction (XRD). These investigations confirmed the composition of our biomaterials.

The scanning electron microscopy (SEM) and the energy-dispersive X-ray spectroscopy (EDS) analyses were performed with VEGA3 from Tescan (Brno, Czech Republic) at 15 kV by. AV-PVP-TCA-I 2 was diluted by adding one drop into distilled water and positioning it on a carbon-coated copper grid. After drying the sample, it was coated with gold through the Quorum Technology Mini Sputter Coater. SEM and EDS analyses were used to determine the morphology and elemental composition of the sample, respectively.

The formulations AV-PVP-TCA and AV-PVP-TCA-I 2 were analyzed by UV-vis spectrophotometry. The investigation was performed by a UV-Vis spectrophotometer model 2600i from Shimadzu (Kyoto, Japan) in the wavelength range of 195 to 800 nm.

The biohybrid AV-PVP-TCA-I 2 underwent Raman analysis on a RENISHAW (Gloucestershire, UK) equipped with an optical microscope room at RT. The sample was placed into a cuvette (1 cm × 1 cm) and put in front of the laser beam. The solid-state laser beam had an excitation of 785 nm and was directed onto the sample by the 50× objective lens of a confocal microscope with a spot diameter of 2 microns. The scattered light was collected by a CCD-based monochromator with a spectral range of between 50 and 3400 cm −1 . The spectral resolution was −1 cm −1 , the output power was 0.5%, and the integration time was −30 s. 

The FTIR analysis of the formulations AV-PVP-TCA and AV-PVP-TCA-I 2 was conducted on an ATR IR spectrometer equipped with a Diamond window (Shimadzu, Kyoto, Japan). Both formulations were freeze dried and analyzed in the range between 400 to 4000 cm −1 .

The X-ray diffraction analysis was performed by a XRD from BRUKER (D8 Advance, Karlsruhe, Germany). The formulation AV-PVP-TCA-I 2 was analyzed by Cu radiation with a wavelength of 1.54060, coupled Two Theta/Theta, time/step of 0.5 s and a step size of 0.03.

The antimicrobial testing was performed with the reference microbial strains of S. pneumoniae ATCC 49619, S. aureus ATCC 25923, E. faecalis ATCC 29212, S. pyogenes ATCC 19615, Bacillus subtilis WDCM 0003 Vitroids, P. mirabilis ATCC 29906, E. coli WDCM 00013 Vitroids, P. aeruginosa WDCM 00026 Vitroids, K. pneumoniae WDCM 00097 Vitroids and C. albicans WDCM 00054 Vitroids. These reference strains were kept at −20 • C. The inoculation was performed by adding the fresh microbes to MHB. These suspensions were kept at 4 • C until needed.

The inhibitory action of AV-PVP-TCA-I 2 against nine reference bacterial strains (S. pneumoniae ATCC 49619, S. aureus ATCC 25923, S. pyogenes ATCC 19615, E. faecalis ATCC 29212, and B. subtilis WDCM 00003, P. mirabilis ATCC 29906, P. aeruginosa WDCM 00026, E. coli WDCM 00013 and K. pneumoniae WDCM 00097) was compared to the antibiotic gentamicin (positive control). The antifungal activity of the title compound was tested on C. albicans WDCM 00054 in comparison to the antibiotic nystatin (positive control). The negative controls of ethanol and water showed no susceptibility and were not mentioned further. The antimicrobial tests on discs, bandages, surgical face masks and sutures were repeated three times. The average of the independent experiments was presented in this investigation.

The zone of inhibition plate method was used to investigate the susceptibility of the selected pathogens toward AV-PVP-TCA-I 2 [93] . We suspended the selected bacterial strains in 10 mL MHB and incubated at 37 • C for 2 to 4 h. C. albicans WDCM 00054 was incubated on Sabouraud Dextrose broth at 30 • C. The microbial cultures were adjusted to 0.5 McFarland standard. The disposable, sterilized Petri dishes with MHA were uniformly seeded with 100 µL microbial culture with sterile cotton swabs and dried for 10 min to be used for the antimicrobial testing.

The antimicrobial testing was performed against the antibiotic discs of gentamycin and nystatin following the recommendations of the Clinical and Laboratory Standards Institute (CLSI) [94] . Sterile filter paper discs were coated for 24 h with 2 mL of AV-PVP-TCA-I 2 (11 µg/mL, 5.5 µg/mL, 2.75, and 1.38 µg/mL). After removing the discs from the solution, we dried the discs for 24 h under ambient conditions. C. albicans WDCM 00054 was incubated for 24 h at 30 • C on agar plates. The diameter of the zone of inhibition (ZOI) was measured with a ruler to the nearest millimeter. The antimicrobial properties of AV-PVP-TCA-I 2 are evident from the diameters of the clear inhibition zone around the disc. No inhibition zone confirms the resistance of the microorganisms.

We utilized SPSS software (version 17.0, SPSS Inc., Chicago, IL, USA) in our statistical analysis. The data are represented as mean values. The statistical significance between groups is calculated by one-way ANOVA. Any value of p < 0.05 was considered statistically significant.

AMR is a growing concern, and it increasingly endangers the existence of mankind, in particular [1] . Worldwide, the unjustified use of antimicrobials during the COVID-19 pandemic elevated the AMR crisis [1] . ESKAPE pathogens develop resistance against common antimicrobials, exacerbating the morbidity and mortality rates [1, [3] [4] [5] [6] [7] [8] [9] . Nosocomial infections in hospital settings aggravated the suffering and fatality during the recent COVID-19 pandemic [1] [2] [3] 5, 6] . Even community-acquired infections caused by multi-drugresistant microorganisms impacted global health due to antibiotic overuse, increasing costs and durations of treatments [1, 3, 4, 9] . The recent COVID-19 pandemic highlighted the need for strategic solutions to overcome AMR. Confusion, misinformation, lockdowns, disruption of transport chains and supply shortages were some of the early markers of the pandemic [3] . Resource management and alternative solutions to the shortages are eminent in times of crisis and beyond [3] .

The availability of antimicrobials and personal protective equipment can be a means of survival. Disinfectants are needed for inanimate surfaces in all indoor and outdoor settings, for contact-killing surfaces and as disinfectants on skin [3, 11] . Preservatives are used in different health care, pharmaceutical or cosmetic products to mitigate microbial contamination. Incorporating antimicrobials on bandages, wound dressing materials and surgical sutures leads to effective prevention and treatment of SSI, as well as wound infections [11, [48] [49] [50] [51] [52] [53] [54] [55] .

Health authorities enforced the use of face masks to mitigate viral transmission and droplet movement [73] [74] [75] [76] [77] [78] . However, the growing number of disposed masks presents a serious source of waste and pollution [72, 73] . The COVID-19 public health measures are going to be lifted as soon as the number of cases declines globally. The recommendations of social distancing, personal hygiene and wearing of face masks must be carried on in the future during known seasonal flu outbreaks. The incorporation of inhibitory biomaterials on surgical face masks can aid the prevention and treatment of upper respiratory tract infections as well [48] [49] [50] [51] [52] [53] [54] [55] . The antiviral, anti-coronavirus activities of plant secondary metabolites are reported in previous studies and include AV, as well as several polyphenols and hydroxycinnamic acids [67] [68] [69] [70] [71] . These properties can be utilized to elevate the antiviral barrier function of face masks and their re-use. Spraying or coating face masks with antimicrobial, natural biomaterials is a sustainable solution for the planet [73] [74] [75] [76] [77] [78] . Antimicrobial, non-toxic agents can be utilized to disinfect and re-use masks [73] [74] [75] [76] [77] [78] . At the same time, it presents a solution for low-income populations and households under economic strain. Furthermore, the re-use of face masks can effectively alleviate the supply shortage problems Polymers 2022, 14, 1932 7 of 29 in different areas globally. Antimicrobial application on face mask materials can ameliorate viral transmission processes more effectively for a longer time.

Antimicrobial agents must be sustainable and impervious to microbial resistance mechanisms. AMR is a global concern and needs to be addressed by the development of new antimicrobial agents. Plant phytochemicals are suitable candidates in the AMR challenge [44, 45] . Phytochemicals and their synergistic mechanisms have assisted the survival of plants against microbes since their existence [44, 45] . The antimicrobial, antiinflammatory activities of plant constituents, such as polyphenols and hydroxycinnamic acids, have been utilized since the history of mankind [46, 47] .

Our title compound AV-PVP-TCA-I 2 fits into the category of antimicrobial plant biomaterials and consists of TCA, PVP, AV, as well as iodine [39] [40] [41] [42] [95] [96] [97] [98] [99] . We used iodine, TCA and AV in our study to investigate the antimicrobial action against 10 selected pathogens. Iodine is a iodophor, which is most stable in form of "smart" triiodide species [34, 36, 41, 42, [100] [101] [102] [103] [104] . TCA, its derivatives and related AV bioconstituents, especially cinnamic acid, aloin, acemannan, aloe-emodin, pyrogallol, hesperidine, aloesin, 10-O-β-d-glucopyranosyl-aloenin and rhein increased biological activities due to their synergistic mechanisms [36, 39, 41, 42, [53] [54] [55] [56] [57] [58] [59] [60] [61] [62] [63] [64] [65] [66] 98, 99] . TCA and its hydroxycinnamic derivates in AV have abilities to permeate cell membranes of Gram-positive pathogens, resulting in cell membrane disruptions and changes [46] . The -COOH group within TCA and AV polyphenols is weakly acidic [46, 98] . Therefore, these compounds diffuse easily through the cell membranes and increase pH levels in the cytoplasm, leading to cell death [46, 47] . The secondary and tertiary structures of proteins are unfolded due to the formation of hydrogen bonding. This can occur through the interaction between hydroxyl, carbonyl and carboxylate groups within TCA and AV components with the functional groups of proteins, outer membrane and cell wall components of the microorganisms [46] . The tertiary structure is unfolded by interactions of carboxylate groups by ion-ion-electrostatic interactions, resulting in disturbances in the salt bridges. Phenolic groups in TCA and the AV biocomponents interfere in the hydrophobic interactions between close, nonpolar phenyl and alkyl groups [46, 47] . The covalent disulfide S-S linkages between the amino acids responsible for folding the tertiary structure of proteins are reduced to S-H groups by plant biomaterials in AV [12] . AV plant bio-compounds are oxidized by transforming their hydroxyl units to carbonyl groups [46, 47] . We aimed to employ in our investigations sustainable, natural, plant-based solutions capable of acting as "smart" triiodide reservoirs [36, 39, 41, 42] . Such triiodides are stable iodine moieties within the PVP matrix and are released upon contact with the microbial units. AV-PVP-TCA-I 2 formulations can be promising antimicrobial biomaterials.

The analytical results of AV-PVP-TCA-I 2 confirmed the antimicrobial properties, the formulation characteristics and sample constituents.

Electron Microscope (SEM) and Energy-Dispersive X-ray Spectroscopic (EDS) Analyses. The morphology and composition of AV-PVP-TCA-I 2 was investigated by SEM and EDS analyses (Figure 1 ).

The title compound AV-PVP-TCA-I 2 reveals an amorphous morphology with interesting thread-or barrel-like forms surrounded by semi-crystalline, white patches ( Figure 1a) . The EDS shows carbon as the main component with 81%, followed by oxygen (6.7%) and iodine (2.5%) (Figure 1b) . Chlorine, potassium and copper are originating from the AV biocompounds. Aluminum and gold appear due to their use during the preparation of the samples for the SEM analysis. The samples were coated with gold. The title compound AV-PVP-TCA-I2 reveals an amorphous morphology with interesting thread-or barrel-like forms surrounded by semi-crystalline, white patches ( Figure  1a ). The EDS shows carbon as the main component with 81%, followed by oxygen (6.7%) and iodine (2.5%) ( Figure 1b) . Chlorine, potassium and copper are originating from the AV biocompounds. Aluminum and gold appear due to their use during the preparation of the samples for the SEM analysis. The samples were coated with gold.

We investigated the antimicrobial activities of AV-PVP-TCA-I2-impregnated medical sutures, bandages and face masks. Sterile, braided surgical PGA sutures were dip coated with our formulations and analyzed by SEM/EDS techniques ( Figure 2 ). Figure 2a depicts the same plain PGA suture from our previous investigations [31] . Impregnating the suture with AV-PVP-Sage-I2 (11 µg/mL) results in a fully coated, homogenous surface (Figure 2b ). Crystalline depositions are distributed throughout the surface of the braided suture ( Figure 2b ). The EDS of the impregnated suture shows only the expected composition of carbon (61%), oxygen (30.8%), potassium (3.9%), chlorine (3.2%) and iodine (1.1%) (Figure 2c ). This result proves the coating process and enables these sutures for their possible use in the prevention of surgical site infections.

Plain medical face masks with and without AV-PVP-TCA-I2 (11 µg/mL) coating are depicted in Figure 3 . The title compound AV-PVP-TCA-I2 reveals an amorphous morphology with interesting thread-or barrel-like forms surrounded by semi-crystalline, white patches ( Figure  1a) . The EDS shows carbon as the main component with 81%, followed by oxygen (6.7%) and iodine (2.5%) (Figure 1b) . Chlorine, potassium and copper are originating from the AV biocompounds. Aluminum and gold appear due to their use during the preparation of the samples for the SEM analysis. The samples were coated with gold.

We investigated the antimicrobial activities of AV-PVP-TCA-I2-impregnated medical sutures, bandages and face masks. Sterile, braided surgical PGA sutures were dip coated with our formulations and analyzed by SEM/EDS techniques ( Figure 2 ). Figure 2a depicts the same plain PGA suture from our previous investigations [31] . Impregnating the suture with AV-PVP-Sage-I2 (11 µg/mL) results in a fully coated, homogenous surface (Figure 2b ). Crystalline depositions are distributed throughout the surface of the braided suture ( Figure 2b ). The EDS of the impregnated suture shows only the expected composition of carbon (61%), oxygen (30.8%), potassium (3.9%), chlorine (3.2%) and iodine (1.1%) (Figure 2c ). This result proves the coating process and enables these sutures for their possible use in the prevention of surgical site infections.

Plain medical face masks with and without AV-PVP-TCA-I2 (11 µg/mL) coating are depicted in Figure 3 . [31] . Impregnating the suture with AV-PVP-Sage-I 2 (11 µg/mL) results in a fully coated, homogenous surface (Figure 2b ). Crystalline depositions are distributed throughout the surface of the braided suture ( Figure 2b ). The EDS of the impregnated suture shows only the expected composition of carbon (61%), oxygen (30.8%), potassium (3.9%), chlorine (3.2%) and iodine (1.1%) (Figure 2c ). This result proves the coating process and enables these sutures for their possible use in the prevention of surgical site infections.

Plain medical face masks with and without AV-PVP-TCA-I 2 (11 µg/mL) coating are depicted in Figure 3 . Figure 3b reveals depositions on the surface of the surgical masks. The EDS of the impregnated mask material reveals the expected compositions of carbon (82.6%), oxygen (9.8%), iodine (6,4%), calcium (0.7%) and potassium (0.5%) (Figure 3c ). The plain mask depicts some rough areas, while the dip-coated mask has a smoother surface and has small aggregations on few fibers ( Figure 3 ). These depositions formed during the drying process of the coating agent. Otherwise, there is no change in the mask material related to porosity, shape and arrangement of the fibers (Figure 3b ). Such small changes will not aggravate the filtering and breathability properties of the face mask. The results may enable the use of our title material as a coating agent for face masks. (Figure 3c ). The plain mask depicts some rough areas, while the dip-coated mask has a smoother surface and has small aggregations on few fibers ( Figure 3 ). These depositions formed during the drying process of the coating agent. Otherwise, there is no change in the mask material related to porosity, shape and arrangement of the fibers (Figure 3b ). Such small changes will not aggravate the filtering and breathability properties of the face mask. The results may enable the use of our title material as a coating agent for face masks.

Medical bandage material was impregnated with AV-PVP-TCA-I2 (11 µg/mL) and analyzed by SEM/EDS techniques ( Figure 4 , Supplementary Files S1 and S2). The bandage material showed two different patterns in area1 (coiled) and area 2 (ordered) in the EDS (Figure 4 , Supplementary Files S1 and S2). The bandage was uniformly coated with the title compound and showed the expected composition of elements ( Figure  4 ). The coiled area of the bandage adsorbed more iodine than the ordered part, with 35% and 6.9%, respectively ( Figure 4 ). Again, carbon was the most abundant element, with 51.7 and 69% in the coiled and ordered structures of the bandage material. The SEM of the dip-coated bandage also shows small depositions due to the drying process, but no morphological changes to the fibers (Supplementary Files S1 and S2). The results encourage the use of the impregnated bandage for the prevention and possible treatment of wound infections.

The homogenous coating of the face mask material, sutures and bandages enables its potential use as an antimicrobial coating agent on these materials (Figures 2 and 3 , Figure 3b reveals depositions on the surface of the surgical masks. The EDS of the impregnated mask material reveals the expected compositions of carbon (82.6%), oxygen (9.8%), iodine (6,4%), calcium (0.7%) and potassium (0.5%) (Figure 3c ). The plain mask depicts some rough areas, while the dip-coated mask has a smoother surface and has small aggregations on few fibers ( Figure 3 ). These depositions formed during the drying process of the coating agent. Otherwise, there is no change in the mask material related to porosity, shape and arrangement of the fibers (Figure 3b ). Such small changes will not aggravate the filtering and breathability properties of the face mask. The results may enable the use of our title material as a coating agent for face masks.

Medical bandage material was impregnated with AV-PVP-TCA-I2 (11 µg/mL) and analyzed by SEM/EDS techniques ( Figure 4 , Supplementary Files S1 and S2). The bandage material showed two different patterns in area1 (coiled) and area 2 (ordered) in the EDS ( Figure 4 , Supplementary Files S1 and S2). The bandage was uniformly coated with the title compound and showed the expected composition of elements ( Figure  4 ). The coiled area of the bandage adsorbed more iodine than the ordered part, with 35% and 6.9%, respectively ( Figure 4 ). Again, carbon was the most abundant element, with 51.7 and 69% in the coiled and ordered structures of the bandage material. The SEM of the dip-coated bandage also shows small depositions due to the drying process, but no morphological changes to the fibers (Supplementary Files S1 and S2). The results encourage the use of the impregnated bandage for the prevention and possible treatment of wound infections.

The homogenous coating of the face mask material, sutures and bandages enables its potential use as an antimicrobial coating agent on these materials (Figures 2 and 3 , The bandage material showed two different patterns in area1 (coiled) and area 2 (ordered) in the EDS ( Figure 4 , Supplementary Figures S1 and S2). The bandage was uniformly coated with the title compound and showed the expected composition of elements ( Figure 4 ). The coiled area of the bandage adsorbed more iodine than the ordered part, with 35% and 6.9%, respectively ( Figure 4 ). Again, carbon was the most abundant element, with 51.7 and 69% in the coiled and ordered structures of the bandage material. The SEM of the dip-coated bandage also shows small depositions due to the drying process, but no morphological changes to the fibers (Supplementary Figures S1 and S2 ). The results encourage the use of the impregnated bandage for the prevention and possible treatment of wound infections.

The homogenous coating of the face mask material, sutures and bandages enables its potential use as an antimicrobial coating agent on these materials (Figures 2 and 3 , Supplementary Figures S1 and S2 ). Further investigations about the stability of the coated surfaces and the effective duration of inhibitory action are needed to judge the future applications of our title compound.

The EDS verifies the purity and composition of our title formulation AV-PVP-TCA-I 2 (Figures 1-4) . Chlorine, potassium and copper were also present in our previous study with AV-PVP-I 2 and originate from the AV biocomponents [41] .

The iodine moieties were available in every EDS of the analyzed samples (Figures 1-4 , Supplementary Figures S1 and S2 ).

Raman spectroscopic analysis of AV-PVP-TCA-I 2 is shown in Figure 5 .

Supplementary Files S1 and S2). Further investigations about the stability of the coated surfaces and the effective duration of inhibitory action are needed to judge the future applications of our title compound.

The EDS verifies the purity and composition of our title formulation AV-PVP-TCA-I2 (Figures 1-4) . Chlorine, potassium and copper were also present in our previous study with AV-PVP-I2 and originate from the AV biocomponents [41] .

The iodine moieties were available in every EDS of the analyzed samples (Figures 1-4, Supplementary Files S1 and S2).

Raman spectroscopic analysis of AV-PVP-TCA-I2 is shown in Figure 5 . Table 1 ). Table 1 ). The Raman spectrum verifies the presence of linear, "smart" triiodide ions as a major component in the AV-PVP-TCA-I 2 formulation, in agreement with our previous investigations ( Figure 5 , Table 1 ) [36, 39, 41, 42] .

Symmetrical, "smart" triiodide ions (I-I-I − ) are represented by strong Raman shifts around 91 cm −1 , followed by 100 and 112 cm −1 originating from symmetrical vibrations ν 1s ( Figure 5 , Table 1 ). Symmetrical triiodides appear at Raman shifts around 100-115 cm −1 . According to Yushina et al., triiodides appear at 100-120 cm −1 , bound I 2 at 140-180 cm −1 and pentaiodides at 140-160 cm −1 [100] . The absorption mode at 112 cm −1 appears in our previous works of AV-PVP-Sage-I 2 at 110 cm −1 [42] . The slight increase from 110 to 112 cm −1 confirms a blue shift with stronger bonds in the title formulation with TCA compared to the Sage biohybrid due to noncovalent interactions and the molecular surroundings of the compounds ( Figure 5 , Table 1 ) [42, 100] .

However, the Raman spectrum of AV-PVP-TCA-I 2 shows further medium to very weak absorption peaks related to asymmetrical triiodide ions (I-I . . . I − ). Savastano et al. and Xu et al. report strong symmetric stretching modes related to slightly nonlinear, symmetrical linear triiodide ions at 110 and 111 cm −1 , respectively [23, 30] . Weak to very weak absorption signals at 145 and 152 cm −1 confirm asymmetric vibrations, respectively. Accordingly, a medium-sized peak at 144 cm −1 was also available in our previous investigation of AV-PVP-Sage-I 2 ( Figure 5 , Table 1 ) [42] . The peak at 152 cm −1 was accompanied by weak to very weak asymmetric stretching modes ν as at 222 and 334 cm −1 , respectively [42] . The I 3 − bands have overtones in the form of increasingly weak vibrational stretching modes at 238 and 325 cm −1 ( Figure 5 , Table 1 ). The weak symmetric stretching mode at 221 cm −1 supports the linear structure, according to Savastano et al. [30] . The same Raman shift is available within the broad band in our formulations with TCA and Sage [42] . Ordinartsev et al. assign Raman modes at 116 and 235 cm −1 to centrosymmetric, symmetrical triiodide ions (I-I-I) [15] . Our compound shows similar symmetric stretching modes confirming the linear structure of the triiodide ions ( Figure 5 , Table 1 ) [15] . The TCA compound reveals a very low absorption intensity compared to the Sage compound, which indicates that the triiodide ions are, in the majority, linear and symmetric rather than nonlinear [42] . However, both compounds also contain slightly nonlinear, symmetrical triiodides accompanied by asymmetric triiodide ions. The title compound presents a broad, weak band between 200 and 400 cm −1 ( Figure 5 , Table 1 ).

Unsymmetrical triiodide ions are Raman active because they are slightly nonlinear and show absorption modes at 60, 85 and 160 cm −1 [30] . The same absorption bands are available in the title compound with strong-to medium-sized Raman shifts at 62, 84 and 160 cm −1 with lower intensity in comparison to the Sage formulation ( Figure 5 , Table 1 ) [30, 42] . The strong Raman shift at 62 cm −1 is assigned to a hot band transition related to the ν 2 symmetric stretching ( Figure 5 , Table 1 ) [30] . Table 1 ). The medium-sized shoulder at 84 cm −1 belongs to stretching vibrations in I 2 . . . I − moieties [30] . The I 2 -unit within I . . . I . . . I − is confirmed by the medium shoulders at 168 and 170 cm −1 ( Figure 5 , Table 1 ) [30, 42] .

Apart from triiodide units, characteristic absorption bands for pentaiodide ions could be assigned to 148, 157 and 165 cm −1 ( Figure 5 , Table 1 ). Pentaiodide ions consist of [I 2 . . . I 3 − ] units and, therefore, are detected related to molecular iodine and triiodide ions. The availability of I 5 − -units seems to be manifested by the high absorption intensities and broadness of these bands between 140 and 175 cm −1 ( Figure 5 , Table 1 ). Nevertheless, these bands are expected to be the overtones of the triiodide ions. Pentaiodide ion absorptions are usually detected around 137-147 cm −1 and 167 cm −1 [25, 82, 101] . The weakness of the absorption intensities is another indicator for the absence of pentaiodide ions. At the same time, free iodine is represented by a medium-sized shoulder at 171 cm −1 and further weak to very weak symmetric stretching modes up to 176 cm −1 in AV-PVP-TCA-I 2 ( Figure 5 , Table 1 ) [42, [102] [103] [104] . The previous investigation with AV-PVP-Sage-I 2 was devoid of absorption modes around 172 cm −1 and free iodine molecules [42, [102] [103] [104] .

The strong presence of the iodine moieties overshadows further signals in the Raman spectrum and impedes full characterization ( Figure 5, Supplementary Figure S3 ). AV biocompounds and TCA show different weak absorptions at higher Raman shifts in accordance to previous investigations [59, [105] [106] [107] . Weak, broad bands originating from hydroxyl groups are available around the broad band between 3175 and 3400 cm −1 (Supplementary Figure S3 ). The weak bands around 3045 and 3070 cm −1 are due to aliphatic and aromatic, unsaturated C-H stretching modes, respectively (Supplementary Figure S3 ) [59] . The Raman spectrum is also overshadowed by the strong absorption intensities of TCA from 1050 to 2050 cm −1 in AV-PVP-TCA-I 2 (Supplementary Figure S3 ). Aromatic and aliphatic -C=C-group stretching modes are available in TCA and the title compound AV-PVP-TCA-I 2 around 1603 and 1645 cm −1 in the form of strong, sharp signals, respectively (Supplementary Figure S3 ) [59] . Both Raman shifts have elevated intensity in AV-PVP-TCA-I 2 compared to TCA alone (Supplementary Figure S3) .

The deformation and stretching vibrations of unsaturated (C-H) are available in a broad band around 1200-1650 cm −1 with a maximum intensity at 1376 cm −1 (Supplementary Figure S3 ) [59] . The stretching vibration (C-C ring ) at 1376 cm −1 in AV-PVP-TCA-I 2 appears in TCA with higher intensity at 1371 cm −1 (Supplementary Figure S3) [59, 105, 106] . The lower intensity and blue shift in the title compound confirms the inclusion of TCA within AV-PVP-TCA-I 2 (Supplementary Figure S3 ). This Raman shift is assigned by de Souza et al. to the carboxylate ion [106] . The carbonyl groups -C=O within -COOH are more complexed in AV-PVP-TCA-I 2 by the interaction with PVP, iodine and AV biomolecules. This is also verified by the related Raman shifts for TCA and AV-PVP-TCA-I 2 at 1888 and 1848 cm −1 , respectively (Supplementary Figure S3) [59, 105] . The -C=O stretching modes show a red shift toward 1848 cm −1 with increased intensity in AV-PVP-TCA-I 2 (Supplementary Figure S3 ). A sharp stretching mode at 2018 cm −1 is originating from C-C 6 H 5 vibrations (Supplementary Figure S3 ) [59] . The aromatic ring breathing mode is seen around 1002 and 1029 cm −1 (Supplementary Figure S3 ) [59] . Very weak modes around 847 and 874 cm −1 are due to the aliphatic C-COOH vibrations (Supplementary Figure S3 ) [59] .

AV naturally contains TCA and acemannan [41] . Acemannan is indicated in the Raman spectrum of AV-PVP-TCA-I 2 through the acetylation degree, with absorptions around 1740 cm −1 (Supplementary Figure S3) [42] . The glycosidic O-C-O stretching vibrational modes appear around 1664 cm −1 [41] . In this work, the Raman shifts at 1602 and 1648 cm −1 in TCA and AV-PVP-TCA-I 2 overshadow the glycosidic stretching modes of O-C-O groups within acemannan (Supplementary Figure S3) . The title compound presents higher absorption intensities for the same modes. This indicates a larger size of molecules compared to pure TCA and confirms the encapsulation of TCA.

According to Hanai et al., the Raman spectrum for cis-CA and TCA shows Raman shifts at 1632 and 1637 cm −1 related to the C=C-stretching vibration [59] . TCA is easily changed due to UV photoisomerization to cis-CA [58, 59, 107] . We propose the existence of a mixture between cis-CA and TCA in our title compound AV-PVP-TCA-I 2 due to shifts at 1643 and 1645 cm −1 [58, 59, 107] .

The Raman spectrum proves the purity of the sample AV-PVP-TCA-I 2 through the absence of unrelated Raman shifts (Supplementary Figure S3 ).

The UV-vis spectrum of the two samples AV-PVP-TCA and AV-PVP-TCA-I 2 is shown in Figure 6 .

at 1643 and 1645 cm −1 [58, 59, 107] .

The Raman spectrum proves the purity of the sample AV-PVP-TCA-I2 through the absence of unrelated Raman shifts (Supplementary File S3).

The UV-vis spectrum of the two samples AV-PVP-TCA and AV-PVP-TCA-I2 is shown in Figure 6 . Table  2 ). Table 2 ).

The UV-vis spectrum of AV-PVP-TCA-I 2 confirms the composition of the sample. The UV-visible spectrum of AV-PVP-TCA-I 2 reveals absorption peaks of molecular I 2 (207 and 210 nm), iodide ions (202 nm) and triiodide ions (290 and 359 nm) ( Figure 6 , Table 2 ). Iodide ions, iodine molecules and triiodide ions are detected in accordance with previous investigations ( Figure 6 , Table 2 ) [15, 22, 23, 25, 27, 30, 33, 34, 36, 41, 42, [89] [90] [91] [100] [101] [102] [103] [104] . The bands at 290 and 359 nm depict a higher availability of symmetrical, linear triiodide ions (I-I-I − ) compared to asymmetric triiodide ions and iodine. The predominance of "smart" triiodide ions was confirmed by the Raman spectrum ( Figure 5 , Table 1 ). The very weak absorption intensity at 359 nm is expected to be an overtone to triiodide ions instead of being an indicator of pentaiodide units.

The biohybrids AV-PVP-Sage-I 2 and AV-PVP-I 2 reveal comparable UV-vis absorptions to the title compound (Table 2) [41, 42] . The iodine moieties appear in the UV-vis spectrum at similar wavelengths. The triiodides absorb in the Sage formulation at 291 and 359 nm (Table 2 ) [42] . The basic biohybrid AV-PVP-I 2 has absorption peaks at 291 and 358 nm [41] . These triiodides are "smart" triiodides with [I-I-I] units consisting of pure halogen bonding [33, 34, 36, 41, 42] . "Smart" triiodides are more stable and have enhanced antimicrobial activities [33, 34, 36, 41, 42] . They release iodine molecules in a controlled manner when the complexes are deformed due to electrostatic interaction with the microbial cell membranes [33, 34, 36, 41, 42] . Hence, the PVP in the biohybrid AV-PVP-TCA-I 2 complexes iodine moieties similar to the previous investigations [41, 42] . The formula PVP-I 2 can be used as PVP-I 3 − according to previous reports [16] [17] [18] [19] [20] [21] 23, 41, 42] . After one-month storage of AV-PVP-TCA-I 2 , the resulting UV-vis spectrum did not show any difference compared to the UV-vis spectrum of the fresh sample. Table 2 . UV-vis absorption signals in the samples AV-PVP-TCA (1), AV-PVP-TCA-I 2 (2), AV-PVP (3), AV-PVP-I 2 (4), PVP-I 2 (5) and [58] (nm). Enhanced interactions between the iodine moieties, AV biocomponents, TCA molecules and the PVP are expressed by the UV-vis spectrum of the title compound. The broadening also refers to the increased hydrogen bonding within the sample AV-PVP-TCA-I 2 . In comparison to the PVP-I 2 (black curve), the title compound shows increased absorption intensities for triiodides at 290 nm, while the band at 359 nm is decreased ( Figure 6 , Table 2 ). TCA molecules have strong absorptions in the region between 203 to 219, as well as 270 to 290 nm [58] [59] [60] . These overlap with the absorption bands of the iodine moieties and impede further clarifications ( Figure 6 , Table 2 ). The absorption bands of TCA are represented by strong bands at 210, 212, 278, 283 and 286 nm [58] [59] [60] . The addition of iodine leads to a hyperchromic effect, which coincides with increased availability of chromophores and conjugated systems. The mentioned bands increase in intensity in the title compound AV-PVP-TCA-I 2 , indicating the liberation of TCA and further AV components from the encapsulation by PVP ( Figure 6 , Table 2 ). The freed molecules perform hydrogen bonding, resulting in higher intensity and broadened bands in the spectrum of AV-PVP-TCA-I 2 ( Figure 6 , Table 2 ).

PVP shows strong absorption at 203-219 and 305 nm ( Figure 6 , Table 2 ) [22, 23, 41, 42] . Iodine moieties and TCA overshadow the region between 203 to 219 nm, but the shoulder at 305 nm can be observed easily in the UV-visible spectrum ( Figure 6 , Table 2 ). Starting with PVP-I 2 (black curve), the intensity of the shoulder at 305 nm increases from AV-PVP-TCA to AV-PVP-TCA-I 2 ( Figure 6 , Table 2 ).

The vibrational mode for -C=O can be observed in PVP-I 2 at 221 nm and undergoes a blue shift toward 215 nm in AV-PVP-TCA ( Figure 6 , Table 2 ) [22, 23, 41, 42] . The addition of iodine into the latter compound results in a red shift, with increased absorption intensity at 217 nm ( Figure 6 , Table 2 ). In comparison with AV-PVP-TCA, this bathochromic effect means for AV-PVP-TCA-I 2 an increase in chromophores and conjugated systems related to -C=O, as well as less encapsulation and decreased hydrogen bonding. Adding iodine into the system liberates TCA and the AV components from the encapsulation by PVP. Their -C=O bonds absorb at higher intensities, while PVP encapsulates the iodine units.

The biohybrid, as well as AV-PVP-TCA-I 2 , shows higher absorbance between the wavelength range of 240 to 320 nm compared to our previously reported complex AV-PVP-Sage-I 2 [42] . This hyperchromic effect reveals the existence of more π-electrons in the title compound. This means an increase in conjugation, less complexation, less encapsulation and less hydrogen bonding. TCA aromatic rings absorb around 277 nm and are, together with the AV aromatic biocomponents, the reason for the broad signal between 260 to 320 nm in the UV-vis spectrum. TCA has an absorption maximum at λ-max = 274 nm, with additional absorption peaks at 215 and 204 nm in accordance with previous investigations ( Figure 6 , Table 2 ) [58] [59] [60] . However, TCA overshadows the UV-vis spectrum and makes further clarifications about AV biocomponents difficult ( Figure 6 , Table 2 ). According to Saleh et al., cis-CA absorbs at 255 nm [58] . The additional shoulder at 256 nm in AV-PVP-TCA-I 2 may be related to cis-CA as a UV-induced photoisomerization of TCA ( Figure 6 ) [58, 59, 107] . Therefore, we may confirm a mixture between TCA and cis-CA in the sample after iodination. The same result was obtained during the discussion of the Raman spectra (Supplementary Figure S3) . The broadness of the absorption band in the UV-vis around 260 to 320 nm for both of the compounds AV-PVP-TCA and AV-PVP-TCA-I 2 may even suggest the availability of cis-CA before iodination.

The FTIR analysis of AV-PVP-TCA and AV-PVP-TCA-I 2 augments the small differences between the two samples clearly (Figure 7, Supplementary Figure S2 ). The title compounds AV-PVP-TCA-I 2 and AV-PVP-TCA reveal a similar pattern in the transmission spectrum (Figure 7 ). The iodinated biomaterial shows intense broadening and higher absorption intensity in two regions. These are evident around 3308, 1632, 1639, 1649 and 1655 cm −1 , being related to stretching vibrations of -COOH, -C=O (-COOH) and C=C groups, respectively (Figure 7 , Table 3 ) [39, 41, 42, 59, [108] [109] [110] .

The addition of iodine into AV-PVP-TCA produces shifts in the vibrational bands from 1646, 1651 and 1656 cm −1 toward 1632 cm −1 , 1639 cm −1 and 1655 cm −1 , respectively ( Figure 7 , Table 3 ) [59] . The blue shift from 1646 to 1632 cm -1 is related to the C=C bonds within TCA after iodine addition ( Table 3 ). The C=O of TCA underwent a small shift from 1656 to 1655 cm -1 after iodination ( Table 3 ). The carbonyl group in PVP, which is responsible for complexing iodine moieties, showed a blue shift from 1651 to 1639 cm -1 after the addition of iodine (Table 3) [19, 22, 59] . The blue shifts are due to the interaction of iodine with the C=O groups of PVP, verifying the encapsulation of the polyiodide ions by the PVP polymer matrix. This is also confirmed by a blue shift of the vibrational band related to PVP amide groups from 1292 to 1288 cm -1 after iodination (Table 3 ) [19] . The broadening, coupled with the increase in absorption intensities, indicates a higher availability of -C=C-, carboxyl and carbonyl groups originating from the released TCA and AV biocomponents. These molecules interact with the light and engage in hydrogen bonding. Adding molecular iodine also triggers oxidation reduction reactions. Iodine is reduced to iodide-ions, while the hydroxyl groups of AV biocomponents are oxidized to carbonyl groups. The encapsulation of PVP increases with the addition of iodine (Figure 7 , Table 3 ). The FTIR analysis reveals striking similarities to our previous investigations (Figure 7 , Table 3 ) [41, 42] . AV-PVP-TCA and its iodinated formulation AV-PVP-TCA-I 2 absorb in the same wavelength regions as in our previous reports (Figure 7 , Table 3 ) [41, 42] . AV biocomponents are available in the FTIR spectrum (Figure 7) . Acemannan is one of the major components in AV and can be detected by the O-C-O acetyl stretching at 1275 cm −1 in both FTIR spectra (Figure 7, Supplementary Figure S4 ) [41] . The small intensity peak at 1113 cm −1 is originating from aloin and is reduced in intensity after adding I 2 because it is also more encapsulated by the PVP complex [41, 42] . The complexation of iodine moieties also releases other molecules previously complexed by the PVP backbone ( Figure 7 , Table 3 ) [41, 42] . This finding is manifested in AV-PVP-TCA-I 2 by the increased band intensities and broadening between 3100 and 3600 cm −1 (Figure 7 , Table 3 ) [41, 42] . This proves a higher interaction of the light with more released -COOH-groups, which connect after their release from the PVP carbonyl oxygen atoms with other biomolecules through hydrogen bonding. The same increase in intensity occurs for the bands of the carbonyl-C=O stretching vibration ( Figure 6) . The band appears in AV-PVP-TCA at 1646 cm −1 with lower intensity and undergoes a red shift, coupled with an increase in intensity toward 1632 cm −1 in the iodinated title compound. The increased intensity is proof of the release from encapsulation from PVP after adding iodine (Figure 7 , Table 3 ) [41, 42] . At the same time, this indicates the increase in -C=O groups as a result of oxidation (Figure 7 , Table 3 ) [41, 42] . Hydroxyl groups within the AV biocompounds are oxidized, while iodine is reduced into iodide ions. The red shift toward 1632 cm −1 underlines the process of more hydrogen bonding and increased interactions between the newly formed -C=O groups and other moieties within the sample (Figure 7 , Table 3 ) [41, 42] .

As previously reported, adding iodine leads to a hypsochromic effect because of complexation of triiodide ions into the PVP matrix [16] [17] [18] [19] [20] [21] 23, 41, 42] . This complexation reduces the number of π-electrons and conjugation systems, which leads to more hydrogen bonding [41, 42] . Once molecular iodine is added into the formulation, it is reduced by AV biocomponents to iodide, while the phytochemical functional groups are oxidized and partly released from the PVP matrix [39, 41, 42] . Triiodide ions form hydrogen bonding to carbonyl groups within PVP [16] [17] [18] [19] [20] [21] 23, 41, 42] . The released AV phytochemicals result in higher absorption intensities for -COOH, -OH, -C=O, -C=C-and -C-O in AV-PVP-TCA-I 2 (Figure 7 , Table 3 ) [41, 42] .

The FTIR spectrum reveals bands for PVP carbonyl groups at 1651 and 1639 cm −1 for AV-PVP-TCA and AV-PVP-TCA-I 2 , respectively ( Figure 7 , Table 3 ) [41, 42] . This red shift indicates a stronger encapsulation of the carbonyl groups of PVP after addition of iodine, resulting in less hydrogen bonding with the AV biocomponents and TCA. Again, this proves a partial release of those components by replacement with iodine moieties. The same peak is observed for the Sage formulations at 1650 cm −1 for PVP [41, 42] . The stretching vibration of -C-O appears for TCA at 1290 cm −1 before and at 1289 cm −1 with higher intensity after adding iodine. This also confirms the partial release of TCA molecules after adding iodine (Figure 7 , Table 3 ) [41, 42] . The methylene groups of PVP are usually located around 2700 to 2900 cm −1 for PVP [41, 42, 108, 109] . In our title compounds, the bands are available at 2990/2989 cm −1 (C-H) a , 2953 (CH 2 ) and 2839 (C-H) s (Figure 7 , Table 3 ) [41, 42, 108, 109] . However, their intensities are reduced after iodine addition. This proves higher involvement of PVP entities in complexation in AV-PVP-TCA-I 2 , in accordance with previous investigations (Figure 7 , Table 3 ) [41, 42] . The same results can be observed for C-C and CH 2 rocking vibrational bands at 1014 cm −1 (Figure 7 , Table 3 ). The absorption intensity of this band is highly reduced in the title compound AV-PVP-TCA-I 2 , confirming the higher coiled structure of the PVP (Figure 7 , Table 3 ). Our previously investigated compounds AV-PVP-Sage-I 2 , AV-PVP-I 2 , AV-PVP-I 2 -Na and pure PVP show the same band at 1017 cm −1 [41, 42, 108] . The red shift from 1017 to 1016/1014 cm −1 proves higher complexation in our title compounds AV-PVP-TCA/AV-PVP-TCA-I 2 in comparison to pure PVP and our previous investigations [41, 42, 108] . The encapsulation of iodine moieties leads to a coiled structure of PVP, which reduces the absorption intensities of the backbone carbon chain of the polymer.

According to Hanai et al., cis-CA shows an absorption peak for the C=C-stretching vibrations at 1631 cm −1 , which is comparable to our result of 1632 cm −1 in Figure 7 ( Table 3 ) [59] . This can confirm the availability of cis-CA in our sample after iodination due to UV-induced photoisomerization (Figure 7 , Table 3 ).

In general, incorporating iodine into the system partially releases TCA and AV biocompounds from the PVP matrix. TCA and AV components appear in the FTIR spectrum of the iodinated title compound with higher absorbance. These molecules show higher intensities in the spectrum through their available functional groups, chromophores and increased abilities to form hydrogen bonding. The increase in absorption intensities is manifested by the AV-PVP-TCA-I 2 FTIR spectrum around 3308 (-O-H and -COOH), 1632 (asymmetric C=O from -COOH) and 1641 cm -1 (C=C) (Figure 7 , Table 3 ). The bands originate from TCA and the main AV component aloin. Further indicators are the vibrational stretching bands around 1343 and 1314 cm -1 (both C-C) (Figure 7 , Table 3 ). The C-O vibrational stretching bands at 1289, 1275, 1223, 1205, 1073 and 1064 cm -1 show higher absorbances compared to their counterparts in the AV-PVP-TCA compound.

As a result, iodine addition intensifies the -OH, -COOH, -C-O and -C=O interaction of de-complexed TCA and AV biocomponents. At the same time, higher encapsulation of iodine by the PVP backbone leads to lower intensity bands of -CH and -CH 2 groups. The FTIR spectrum proves the purity of the synthesized biohybrids AV-PVP-TCA and AV-PVP-TCA-I 2 (Figure 7 , Table 3 ).

The XRD analysis of AV-PVP-TCA-I 2 reveals sharp diffraction peaks originating from AV, TCA, PVP and iodine (Figure 8 ). The two main peaks at 2θ = 17, 19° and smaller peaks at 11 and 15° belong to TCA, while others at 11 and 20° are due to PVP [41, [95] [96] [97] [98] [99] [100] . Further peaks reveal crystalline behavior at 2θ = 10, 15, 16, 19, 20, 21 and 22° [41,95-100] . The small broad bands from 2θ = 20° to 30° indicate the formation of amorphous phases after the deposition of polyiodide species into the PVP matrix ( Figure 8 ). Iodide moieties are encapsulated into the PVP backbone and cause small but broad amorphous regions below the sharp peaks at 22.8, 23.8, 25.5, 27 and 30 ( Figure 8 , Table 4 ). 

AV-PVP- Table 4 ). The decrease in peak intensities related to PVP and their shift toward 2Theta values of 11 • and 20 • confirm the higher encapsulation of polyiodides in the title compound compared to AV-PVP-I 2 alone. The addition of TCA into the system clearly induced a higher crystallization degree, lower intensities and sharp peaks (Figure 8 , Table 4 ).

The purity of our title compound AV-PVP-TCA-I 2 is confirmed by the XRD analysis ( Figure 8 , Table 4 ).

Iodine and TCA are represented according to our previous studies and other investigations around 24-46 2Theta degrees [41, [95] [96] [97] . The intermediate peaks around 23, 24, 26, 27 and 30 degrees (2Theta) are followed by very weak to weak signals at 37 and 46 degrees, respectively ( Figure 8 , Table 4 ). These signals appear in previous investigations and confirm the iodine within our sample [41, 95, 97] . Figure 8 and Table 4 indicate the related strong and intermediate peaks of the crystalline TCA at 2Theta degrees of 10, 23 and 25, 29, respectively ( Figure 8 , Table 4 ) [96] . These are accompanied by several other weak peaks at 2Theta 19, 20, 27, 32, 34 ( Figure 8 , Table 4 ) [96] . AV biocomponents are indicated by intermediate peaks at 2Theta degrees of 16 and 22 in AV-PVP-TCA-I 2 (Figure 8 , Table 4 ), which are all available in previous investigations as well [41, 98, 99] . The title compound AV-PVP-TCA-I 2 has a higher crystalline character in comparison to our previous investigation of AV-PVP-I 2 , AV-PVP-NaI and AV-PVP-Sage-I 2 [41, 42] . The higher crystallinity in AV-PVP-TCA-I 2 is due to the higher presence of TCA in the formulation compared to the other bio-hybrids [41, 42] . The sample shows crystalline character in the SEM of the surgical suture ( Figure 2 ). The same result was obtained in the XRD analysis with sharp, distinct peaks for AV, TCA, iodine and PVP (Figure 8 , Table 4 ) [41,98-100].

Disc diffusion assay against 10 reference microorganisms was used to investigate the antimicrobial activities of AV-PVP-TCA and AV-PVP-TCA-I 2 . The utilized Gram-positive bacteria were S. pneumonia ATCC 49619, S. aureus ATCC 25923, S. pyogenes ATCC 19615, E. faecalis ATCC 29212 and B. subtilis WDCM0003. Gram-negative bacteria included the strains E. coli WDCM 00013 Vitroids, P. mirabilis ATCC 29906, P. aeruginosa WDCM 00026 Vitroids and K. pneumonia WDCM00097 Vitroids. C. albicans WDCM 00054 Vitroids, which were used to test the antifungal activities of our biomaterial. The antimicrobial properties of our bio-compounds were compared to the positive controls, gentamicin and nystatin. Methanol, ethanol and water were the negative controls. They showed no zone of inhibition (ZOI) and were excluded from Table 5 . Table 5 . Antimicrobial testing of antibiotics (A), AV-PVP-TCA-I 2 by disc dilution studies (1,2,3), suture (S), bandage (B) and mask (M). ZOI (mm) against microbial strains by diffusion assay. Our title biohybrid AV-PVP-TCA-I 2 shows remarkable antimicrobial properties of impregnated discs, sutures, bandages and face masks ( Table 4 ). The tests were performed on discs at concentrations of 11, 5.5 and 2.75 µg/mL. Sutures, bandages and masks were treated with a concentration of 11 µg/mL. The highest inhibition zones were achieved, in general, against the fungal reference strain C. albicans WDCM 00054, followed by Grampositive and, finally, Gram-negative bacterial strains.

C. albicans WDCM 00054, S. aureus ATCC 25923, S. pneumoniae ATCC 49619 and E. coli WDCM 00013 were more susceptible toward AV-PVP-TCA-I 2 than their respective antibiotic positive controls (Table 3) . AV-PVP-TCA-I 2 inhibits C. albicans WDCM 00054 at concentrations of 11 and 5.5 µg/mL with 46 and 25 mm stronger than nystatin (Table 5, Figure 9a ). WDCM 00054  NY  16  46  25 13 * 17 55 54 + Disc diffusion studies (6 mm disc impregnated with 2 mL of 11 µg/mL (1), 2 mL of 5.5 µg/mL (2) and 2 mL of 2.75 µg/mL (3) of AV-PVP-TCA-I2. A = G Gentamicin (30 µg/disc). NY (Nystatin) (100 IU). Suture (S), bandage (B) and mask (M) impregnated with 2 mL of 11 µg/mL AV-PVP-TCA-I2. Gray shaded area represents Gram-negative bacteria. 0 = Resistant. * Further dilution to 1.38 µg/mL yielded ZOI = 9 mm. No statistically significant differences (p > 0.05) between row-based values through Pearson correlation.

Our title biohybrid AV-PVP-TCA-I2 shows remarkable antimicrobial properties of impregnated discs, sutures, bandages and face masks ( Table 4 ). The tests were performed on discs at concentrations of 11, 5.5 and 2.75 µg/mL. Sutures, bandages and masks were treated with a concentration of 11 µg/mL. The highest inhibition zones were achieved, in general, against the fungal reference strain C. albicans WDCM 00054, followed by Grampositive and, finally, Gram-negative bacterial strains.

C. albicans WDCM 00054, S. aureus ATCC 25923, S. pneumoniae ATCC 49619 and E. coli WDCM 00013 were more susceptible toward AV-PVP-TCA-I2 than their respective antibiotic positive controls (Table 3) . AV-PVP-TCA-I2 inhibits C. albicans WDCM 00054 at concentrations of 11 and 5.5 µg/mL with 46 and 25 mm stronger than nystatin (Table 5, Figure 9a ). (Table 5 , Figure 9c ). The Gram-negative reference strains follow with P. aeruginosa WDCM 00026 (13/12 mm), K. pneumoniae WDCM 00097 (13/10 mm) and E. coli WDCM 00013 (13/0 mm) at concentrations of 11 and 5.5 µg/mL, respectively (Table 5, Figure 9 ).

The disc diffusion tests revealed strong antifungal activity of AV-PVP-TCA-I2 against C. albicans WDCM 00054. The next most susceptible microorganism is the Gram-positive bacteria S. aureus ATCC 25932. Intermediate antibacterial activity against further Grampositive and Gram-negative species K. pneumoniae WDCM 00097, P. aeruginosa WDCM 00026 and E. coli WDCM 00013 are manifested as well (Table 5, Figure 9 ).

The promising results in the disc diffusion studies tempted us to investigate AV-PVP-TCA-I2 on surgical sutures as potential preventive agents against surgical site infections. Figure 9c ). The Gram-negative reference strains follow with P. aeruginosa WDCM 00026 (13/12 mm), K. pneumoniae WDCM 00097 (13/10 mm) and E. coli WDCM 00013 (13/0 mm) at concentrations of 11 and 5.5 µg/mL, respectively (Table 5, Figure 9 ).

The disc diffusion tests revealed strong antifungal activity of AV-PVP-TCA-I 2 against C. albicans WDCM 00054. The next most susceptible microorganism is the Gram-positive bacteria S. aureus ATCC 25932. Intermediate antibacterial activity against further Grampositive and Gram-negative species K. pneumoniae WDCM 00097, P. aeruginosa WDCM 00026 and E. coli WDCM 00013 are manifested as well (Table 5, Figure 9 ).

The promising results in the disc diffusion studies tempted us to investigate AV-PVP-TCA-I 2 on surgical sutures as potential preventive agents against surgical site infections. We coated braided PGA surgical sutures with the title compound. The inhibitory activity on surgical sutures was tested against the same 10 reference strains (Table 5, Figure 10 ).

The inhibitory zones around the sutures follow the same trends displayed by the disc diffusion studies on sterile discs. The dip-coated sutures showed extraordinary antifungal activity against C. albicans WDCM 00054, with an inhibition zone of 17 mm (Table 5 , Figure 10 ). The Gram-positive pathogen, S. aureus ATCC 25,932 (7 mm), is followed by S. pyogenes ATCC 19615 (4 mm), B. subtilis WDCM 00003 (4 mm), S. pneumoniae ATCC 49619 and E. faecalis ATCC 29212 (both 3 mm) ( Figure 10 , Table 5 ). The two Gram-negative pathogens, P. aeruginosa WDCM 00026 and K. pneumoniae WDCM 00097, revealed inhibition zones of 2 mm against AV-PVP-TCA-I 2 ( Figure 10 , Table 5 ). We coated braided PGA surgical sutures with the title compound. The inhibitory activity on surgical sutures was tested against the same 10 reference strains (Table 5, Figure 10 ). The inhibitory zones around the sutures follow the same trends displayed by the disc diffusion studies on sterile discs. The dip-coated sutures showed extraordinary antifungal activity against C. albicans WDCM 00054, with an inhibition zone of 17 mm (Table 5, Figure  10 ). The Gram-positive pathogen, S. aureus ATCC 25,932 (7 mm), is followed by S. pyogenes ATCC 19615 (4 mm), B. subtilis WDCM 00003 (4 mm), S. pneumoniae ATCC 49619 and E. faecalis ATCC 29212 (both 3 mm) ( Figure 10 , Table 5 ). The two Gram-negative pathogens, P. aeruginosa WDCM 00026 and K. pneumoniae WDCM 00097, revealed inhibition zones of 2 mm against AV-PVP-TCA-I2 ( Figure 10 , Table 5 ).

We impregnated sterile face masks with the biomaterial AV-PVP-TCA-I2 to investigate the potential antimicrobial action on masks. The process can potentiate the re-use of masks during any pandemic. This will ensure safety, sustainability and waste reduction. Communities without adequate resources could solve this issue by re-using face masks after treatment with our biocompatible, non-toxic title compound.

The antimicrobial tests on face masks against the same 10 reference strains delivered the same trends. AV-PVP-TCA-I2 is a strong antifungal agent against C. albicans WDCM 00054 (54 mm) (Table 5, Figure 11 ). Table 5 ). The three Gram-negative pathogens, K. pneumoniae WDCM We impregnated sterile face masks with the biomaterial AV-PVP-TCA-I 2 to investigate the potential antimicrobial action on masks. The process can potentiate the re-use of masks during any pandemic. This will ensure safety, sustainability and waste reduction. Communities without adequate resources could solve this issue by re-using face masks after treatment with our biocompatible, non-toxic title compound.

The antimicrobial tests on face masks against the same 10 reference strains delivered the same trends. AV-PVP-TCA-I 2 is a strong antifungal agent against C. albicans WDCM 00054 (54 mm) (Table 5, Figure 11 ).

The highest susceptibility against our title compound is shown by the Gram-positive S. aureus ATCC 25932 (35 mm), followed by S. pneumoniae ATCC 49619 (20 mm), E. faecalis ATCC 29212 (20 mm), S. pyogenes ATCC 19615 (19 mm) and B. subtilis WDCM 00003 (16 mm) ( Figure 11 , Table 5 ). The three Gram-negative pathogens, K. pneumoniae WDCM 00097, P. aeruginosa WDCM 00026 and E. coli WDCM 00013, displayed against AV-PVP-TCA-I 2 inhibition zones of 21, 20 and 16 mm, respectively ( Figure 10 , Table 5 ).

We coated braided PGA surgical sutures with the title compound. The inhibitory activity on surgical sutures was tested against the same 10 reference strains (Table 5, Figure 10 ). The inhibitory zones around the sutures follow the same trends displayed by the disc diffusion studies on sterile discs. The dip-coated sutures showed extraordinary antifungal activity against C. albicans WDCM 00054, with an inhibition zone of 17 mm (Table 5, Figure  10 ). The Gram-positive pathogen, S. aureus ATCC 25,932 (7 mm), is followed by S. pyogenes ATCC 19615 (4 mm), B. subtilis WDCM 00003 (4 mm), S. pneumoniae ATCC 49619 and E. faecalis ATCC 29212 (both 3 mm) ( Figure 10 , Table 5 ). The two Gram-negative pathogens, P. aeruginosa WDCM 00026 and K. pneumoniae WDCM 00097, revealed inhibition zones of 2 mm against AV-PVP-TCA-I2 ( Figure 10 , Table 5 ).

We impregnated sterile face masks with the biomaterial AV-PVP-TCA-I2 to investigate the potential antimicrobial action on masks. The process can potentiate the re-use of masks during any pandemic. This will ensure safety, sustainability and waste reduction. Communities without adequate resources could solve this issue by re-using face masks after treatment with our biocompatible, non-toxic title compound.

The antimicrobial tests on face masks against the same 10 reference strains delivered the same trends. AV-PVP-TCA-I2 is a strong antifungal agent against C. albicans WDCM 00054 (54 mm) (Table 5, Figure 11 ). Table 5 ). The three Gram-negative pathogens, K. pneumoniae WDCM We tested the impregnated sterile cotton bandages with AV-PVP-TCA-I 2 and tested them against the same 10 microorganisms. Our compound can be potentially used as a strong microbial agent in the treatment of wounds and wound infections. The results show strong antifungal activities against C. albicans WDCM 00054, with inhibition zone of 55 mm (Table 5, Figure 12 ). 00097, P. aeruginosa WDCM 00026 and E. coli WDCM 00013, displayed against AV-PVP-TCA-I2 inhibition zones of 21, 20 and 16 mm, respectively ( Figure 10 , Table 5 ).

We tested the impregnated sterile cotton bandages with AV-PVP-TCA-I2 and tested them against the same 10 microorganisms. Our compound can be potentially used as a strong microbial agent in the treatment of wounds and wound infections. The results show strong antifungal activities against C. albicans WDCM 00054, with inhibition zone of 55 mm (Table 5, Figure 12 ). Table 5 ).

The three Gram-negative bacteria, K. pneumoniae WDCM 00097, E. coli WDCM 00013 and P. aeruginosa WDCM 00026, revealed inhibition zones of 28, 26 and 20 mm, respectively ( Figure 12 , Table 5 ).

The highest inhibitory action was achieved by AV-PVP-TCA-I2 against the fungal strain C. albicans WDCM 00054 with a ZOI = 46 mm compared to nystatin with 16 mm (Table 5) . We used the same method and concentration in our previous work with AV-PVP-Sage-I2 and reported an alleviated susceptibility of C. albicans WDCM 00054 with 52 mm [42] . The inhibitory action is similar or slightly weaker when the formulation contains TCA instead of Sage. The same result is seen in slightly weaker inhibition zones against S. aureus ATCC 25923 with 17, 13 and 11 mm (Table 5 ). In comparison, the Sage formulation showed inhibition zones of 20, 15 and 14 mm against the same pathogen [42] . The spore forming B. subtilis WDCM 0003 is slightly more inhibited by the title formulation with TCA in comparison to the Sage formulation (Table 5 ) [42] . When TCA replaces Sage in the formulation at a concentration of 11 µg/mL, the susceptibility of the Gram-positive S. pyogenes ATCC 19615 is slightly higher with 16 mm compared to 14 mm [42] . The Gramnegative, multi-drug-resistant P. aeruginosa WDCM 00026 is inhibited by AV-PVP-TCA-I2 with 13 and 12 mm, while it is resistant against AV-PVP-Sage-I2 (Table 5) [42, 46] . The same pathogen shows augmented susceptibility against AV-PVP-TCA-I2 on dip-coated sutures as well (Table 5 ) [42] . All Gram-positive pathogens and C. albicans WDCM 00054 were more inhibited on AV-PVP-TCA-I2-coated sutures compared to AV-PVP-Sage-I2-coated ones (Table 5 ) [42] . C. albicans WDCM 00,054 was inhibited by AV-PVP-TCA-I2-coated suture with 17 mm, while the Sage-formulation-coated suture resulted in 15 mm (Table 5 ) [42] . We also soaked the bandages and surgical face masks with our formulation AV-PVP-TCA-I2. The impregnated cotton bandages and face masks showed high antimicrobial activity against C. albicans WDCM 00054, followed by the Gram-positive pathogen S. aureus ATCC 25932 and the Gram-negative K. pneumoniae WDCM 00097 (Table 5 , Figures 11 and  12 ). Table 5 ).

The three Gram-negative bacteria, K. pneumoniae WDCM 00097, E. coli WDCM 00013 and P. aeruginosa WDCM 00026, revealed inhibition zones of 28, 26 and 20 mm, respectively ( Figure 12 , Table 5 ).

The highest inhibitory action was achieved by AV-PVP-TCA-I 2 against the fungal strain C. albicans WDCM 00054 with a ZOI = 46 mm compared to nystatin with 16 mm (Table 5) . We used the same method and concentration in our previous work with AV-PVP-Sage-I 2 and reported an alleviated susceptibility of C. albicans WDCM 00054 with 52 mm [42] . The inhibitory action is similar or slightly weaker when the formulation contains TCA instead of Sage. The same result is seen in slightly weaker inhibition zones against S. aureus ATCC 25923 with 17, 13 and 11 mm (Table 5 ). In comparison, the Sage formulation showed inhibition zones of 20, 15 and 14 mm against the same pathogen [42] . The spore forming B. subtilis WDCM 0003 is slightly more inhibited by the title formulation with TCA in comparison to the Sage formulation (Table 5 ) [42] . When TCA replaces Sage in the formulation at a concentration of 11 µg/mL, the susceptibility of the Gram-positive S. pyogenes ATCC 19615 is slightly higher with 16 mm compared to 14 mm [42] . The Gramnegative, multi-drug-resistant P. aeruginosa WDCM 00026 is inhibited by AV-PVP-TCA-I 2 with 13 and 12 mm, while it is resistant against AV-PVP-Sage-I 2 (Table 5) [42, 46] . The same pathogen shows augmented susceptibility against AV-PVP-TCA-I 2 on dip-coated sutures as well (Table 5 ) [42] . All Gram-positive pathogens and C. albicans WDCM 00054 were more inhibited on AV-PVP-TCA-I 2 -coated sutures compared to AV-PVP-Sage-I 2 -coated ones (Table 5 ) [42] . C. albicans WDCM 00,054 was inhibited by AV-PVP-TCA-I 2 -coated suture with 17 mm, while the Sage-formulation-coated suture resulted in 15 mm (Table 5 ) [42] . We also soaked the bandages and surgical face masks with our formulation AV-PVP-TCA-I 2 .

The impregnated cotton bandages and face masks showed high antimicrobial activity against C. albicans WDCM 00054, followed by the Gram-positive pathogen S. aureus ATCC 25932 and the Gram-negative K. pneumoniae WDCM 00097 (Table 5 , Figures 11 and 12 ).

In conclusion, the synergistic action of the Sage biocompounds in the biohybrid AV-PVP-Sage-I 2 achieves slightly higher inhibition zones for C. albicans WDCM 00054 and S. aureus ATCC 25932 in comparison to AV-PVP-TCA-I 2 at the same concentration in disc diffusion studies [42] . However, the title compound AV-PVP-TCA-I 2 is effective against P. aeruginosa WDCM 00026, while the Sage formulation fails to inhibit this multidrug-resistant pathogen on disc diffusion studies [42] . The AV-PVP-TCA-I 2 impregnated sutures were more effective than the ones coated with AV-PVP-Sage-I 2 against Grampositive bacteria and C. albicans WDCM 00054 [42] . These results encourage the use of AV-PVP-TCA-I 2 on sutures, bandages and face masks against C. albicans WDCM 00054, Gram-positive S. aureus ATCC 25932, Gram-negative P. aeruginosa WDCM 00026 and K. pneumoniae WDCM 00097.

The susceptibility of the tested microorganisms against our biomaterial AV-PVP-TCA-I 2 reveals similar patterns to previously reported biomaterials AV-PVP-I 2 and AV-PVP-Sage-I 2 [41, 42] . The highest susceptibility was showcased by C. albicans WDCM 00054, followed by high to intermediate inhibition of the Gram-positive pathogens (Table 5) . Gram-negative microorganisms displayed the lowest inhibition zones due to their higher negatively charged, complicated outer cell membrane with porin channels. This confirms the antimicrobial action of molecular iodine, which does not go through porin channels like its hydrophilic iodide and triiodide counterparts. Iodine is released from triiodide ions, which are encapsulated by the PVP complex [41, 42, 46] . The release occurs through deformation of the PVP complex through dipol-dipol interactions of TCA and AV biocomponents [41, 42, 46] . Remarkably, the results show higher susceptibility of the multidrug-resistant P. aeruginosa WDCM 00026 against AV-PVP-TCA-I 2 in comparison to the Sage formulation (Table 5 ) [42, 46] . The title formulation seems to be able to avoid the efflux pumps within Gram-negative, motile bacilli. P. mirabilis ATCC 29906 is a swarming bacillus with several flaggellae. P. mirabilis ATCC 29906 shows resistance against both of our formulations, AV-PVP-TCA-I 2 and AV-PVP-Sage-I 2 ( Table 5 ) [42] .

In general, the fungi C. albicans WDCM 00054 is highly susceptible, followed by Grampositive and lastly Gram-negative bacteria. The bacterial morphology rules susceptibility of the studied microorganisms against AV-PVP-TCA-I 2 and our previous compounds in the same patterns [41, 42] . Cocci, non-motile, Gram-positive, higher agglomerated clusters (S. aureus), chains (E. faecalis, S. pyogenes) and pairs (S. pneumoniae) are more susceptible than motile, Gram-negative pathogens (Table 5 ) [41, 42] . Fungus and Gram-positive microorganisms of our selection have less complicated outer cell membrane structures and are therefore more vulnerable toward AV-PVP-TCA-I 2 [8, 11, 41, 42, 44, 47, [110] [111] [112] . The thick peptidoglycan layers of Gram-positive pathogens are crosslinked with peptide bridges, which possibly form hydrogen bonding, dipol-dipol and electrostatic interactions with components in our title formulation through TCA, AV and PVP [8, 11, 36, 39, 41, 42, 44, 47, [110] [111] [112] . These interactions deform the complex AV-PVP-TCA-I 2 and result in the release of molecular iodine from the "smart" triiodides reservoir [36, 39, 41, 42] . Iodine compromises the cell membranes, leads to cell leakage, diffuses easily through the cell membranes and causes cell death by inhibiting important cell functions [17, 18, 36, 39, 41, 42] .

In conclusion, the biomaterial is a strong antifungal agent on bandages, discs, sutures and masks against C. albicans WDCM 00054. All the tested materials exhibited highest inhibitory action against the Gram-positive pathogen S. aureus ATCC 25932 and other tested bacterial strains. Intermediate to high inhibitory action is recorded with the Gram-negative pathogens, K. pneumoniae WDCM 00097, E. coli WDCM 00013 and P. aeruginosa WDCM 00026. P. mirabilis ATCC 29906 showed resistance in all the investigations.

Our title compound AV-PVP-TCA-I 2 is a combination of affordable, commonly used and well-known non-toxic antimicrobial agents. Coating common gauze bandages and surgical sutures with AV-PVP-TCA-I 2 can mitigate or even prevent surgical site and wound infections. The work is based on our previous investigations [36, 39, 41, 42] . Impregnating face masks with AV-PVP-TCA-I 2 can potentially reduce the viral load in the area between the mask and the face during its use. AV-PVP-TCA-I 2 can deactivate common microorganisms, moisturize skin and tissues and alleviate the filtering properties of the mask fibers. The formulation AV-PVP-TCA-I 2 may potentially support the community during pandemics, crises, shortages of antimicrobial disinfectants and reduce the need for disposing face masks after single use. The components are readily available for any individual and can be produced in households. Further investigations are needed to confirm the suggested uses and other biological activities of the formulation.

Iodine-based disinfectants and antiseptics are impervious to AMR and can play a strategic role against resistant, opportunistic pathogens. Biomaterials consisting of iodine and plant biocompounds have enhanced inhibitory action against a variety of microorganisms. These microbicidal formulations can be employed as disinfectants on inanimate surfaces to mitigate community-and hospital-acquired infections, as well as antiseptics on skin tissues. Coating sutures, wound dressing materials and gauze bandages can alleviate the development of SSI and wound infections. Surgical face masks are needed in the prevention of microbial infections through air droplets. Single-use, disposable face masks already place a huge burden on the environment, resources and low-income populations. Impregnating face masks with antimicrobial formulations can alleviate viral transmission and ameliorate sustainability. The title compound AV-PVP-TCA-I 2 showed excellent antifungal and good to intermediate antibacterial activities against our selection of Gram-positive-and Gram-negative reference strains, respectively. AV-PVP-TCA-I 2 inhibits C. albicans WDCM 00054 remarkably on sutures, bandages and face masks with a ZOI of 17, 55 and 54 mm, respectively. Gram-positive S. aureus ATCC 25932, Gram-negative P. aeruginosa WDCM 00026 and K. pneumoniae WDCM 00097 are also strongly susceptible on bandages and face masks. Therefore, the title compound has the potential to be used as an infection control agent against the mentioned pathogens. The composition and morphology of the title compound was verified by analytical methods. Our results confirm AV-PVP-TCA-I 2 as a strong antifungal agent against C. albicans. The title compound is an alternative in the prevention or treatment of infectious diseases on inanimate surfaces, face masks, sutures and bandages. Further investigations are needed to confirm the intended uses and other biological activities.

Supplementary Materials: The following supporting information can be downloaded at: https: //www.mdpi.com/article/10.3390/polym14101932/s1, Figure S1 : EDS of Bandage (coiled part), Figure S2 : EDS of Bandage (ordered fibers part), Figure S3 : Raman analysis full spectrum of AV-PVP-TCA-I2, Figure S4 : FTIR spectrum of AV, Figure S5 : FTIR spectrum of PVPI.

The silent pandemic: Emergent antibiotic resistances following the global response to SARS-CoV-2

Critical supply shortages-The need for ventilators and personal protective equipment during the COVID-19 pandemic

A Look behind the Scenes at COVID-19: National Strategies of Infection Control and Their Impact on Mortality

Emerging Strategies to Combat ESKAPE Pathogens in the Era of Antimicrobial Resistance: A

The microbial coinfection in COVID-19

Bacterial and fungal co-infection in individuals with coronavirus: A rapid review to support COVID-19 antimicrobial prescribing

A Review of Streptococcus pyogenes: Public health risk factors, prevention and control

Fungal Colonization and Infections-Interactions with Other Human Diseases

Attributable deaths and disability-adjusted life-years caused by infections with antibiotic-resistant bacteria in the EU and the European Economic Area in 2015: A population-level modelling analysis

Persistence of coronaviruses on inanimate surfaces and their inactivation with biocidal agents

Approaches for Mitigating Microbial Biofilm-Related Drug Resistance: A Focus on Micro-and Nanotechnologies

Iodine Chemistry and Applications

Encapsulating a high content of iodine into an active graphene substrate as a cathode material for high-rate lithium-iodine batteries

A chain-type diamine strategy towards strongly anisotropic triiodide of DMEDA·I 6

Crystal structure of new formamidinium triiodide jointly refined by single-crystal XRD, Raman scattering spectroscopy and DFT assessment of hydrogen-bond network features

Molecular iodine/polymer complexes

Polymer-Iodine Complexes: An Update

Antimicrobial properties of iodine based products

Iodine complexed poly(vinylpyrrolidone) plasma polymers as broad spectrum antiseptic coating

Povidone iodine in wound healing: A review of current concepts and practices

Povidone-Iodine-Based Polymeric Nanoparticles for Antibacterial applications

Insights into the molecular interaction between poly(vinylpyrrolidone)-iodine disinfection system and polypropylene microplastics in aquatic environment

Investigating the Complexation and Release Behaviors of Iodine in Poly(vinylpyrrolidone)-Iodine Systems through Experimental and Computational Approaches

Anti-microbial and skin wound dressing application of molecular iodine nanoparticles

Antimicrobial Hexaaquacopper(II) Complexes with Novel Polyiodide Chains

Structure and Antimicrobial properties of bis(1,4,7,10-tetraoxacyclododecane-κ 4 O,O ,O ,O )cesium pentaiodide, C 16 H 32 CsI 5 O 8

Crystalline Iodine Complexes of Amorphous Poly(vinyl acetate) as Studied by X-ray Diffraction, Vibrational Spectroscopy, and Computer Simulation

X-ray study of Poly(vinyl Alcohol)-Iodine complex prepared from the dilute iodine solution as a hint to know the inner structure of polarizer

Template self-assembly of polyiodide networks

Genesis of Complex Polyiodide Networks: Insights on the Blue Box/I − /I 2 Ternary System

Preparation and structural and spectroscopic characterization of a pentaiodide

Theoretical Modeling of Electronic Structures of Polyiodide Species Included in α-Cyclodextrin

Halogen bonding in Crystal structure of bis(1,4

Preparation and structural and spectroscopic characterization of triiodides [M(12-crown-4)2]I3 with M = Na and Rb

Anion composed of two asymmetric triiodide moieties: A competition between halogen and hydrogen bond

Treatment data using a topical povidone-iodine antiseptic in patients with superficial skin abscesses

Antimicrobial Properties of Lepidium sativum L. Facilitated Silver Nanoparticles

Smart" antimicrobial nanocomplexes with potential to decrease surgical site infections (SSI)

Green Synthesis of Potent Antimicrobial Silver Nanoparticles Using Different Plant Extracts and Their Mixtures

Facile Synthesis of Antimicrobial Aloe Vera-"Smart

Facile Synthesis of Bio-Antimicrobials with

Polymer sutures for simultaneous wound healing and drug delivery-A review

Antibacterial activity of medicinal plants against ESKAPE: An update

Synergistic Mechanisms of Constituents in Herbal Extracts during Intestinal Absorption: Focus on Natural Occurring Nanoparticles

Biocide Potentiation Using Cinnamic Phytochemicals and Derivatives

New Nanotechnologies for the Treatment and Repair of Skin Burns Infections

The place of biomaterials in wound healing

Wound dressings: Current advances and future directions

Composites Based on Gellan Gum, Alginate and Nisin-Enriched Lipid Nanoparticles for the Treatment of Infected Wounds

Multifunctional Nanofibrous Dressing with Antimicrobial and Anti-Inflammatory Properties Prepared by Needle-Free Electrospinning

Composite wound dressings of pectin and gelatin with Aloe vera and curcumin as bioactive agents

Aloe vera gel: Effective Therapeutic Agent against Multidrug-Resistant Pseudomonas aeruginosa Isolates Recovered from Burn Wound Infections

Anti-fungal bandages containing cinnamon extract

Alleviating the toxicity concerns of antibacterial cinnamon-polycaprolactone biomaterials for healthcare-related biomedical applications

Trans-Cinnamaldehyde Exhibits Synergy with Conventional Antibiotic against Methicillin-Resistant Staphylococcus aureus

Encapsulation of Cinnamic Acid by Cucurbit [7]uril for Enhancing Photoisomerization

A comparative vibrational and NMR study of cis-cinnamic acid polymorphs and trans-cinnamic acid

Self-Assemblies Based on Traditional Medicine Berberine and Cinnamic Acid for Adhesion-Induced Inhibition Multidrug-Resistant Staphylococcus aureus

Pharmacological Update Properties of Aloe Vera and its Major Active Constituents

Extraction, Purification, Structural Characteristics, Biological Activities and Pharmacological Applications of Acemannan, a Polysaccharide from Aloe vera: A Review

Evaluation of anti-infective potencies of formulated aloin A ointment and aloin A isolated from Aloe barbadensis Miller

Direct Spectrophotometric Determination of Hesperidin in Pharmaceutical Preparations

Aloe-emodin inhibits Staphylococcus aureus biofilms and extracellular protein production at the initial adhesion stage of biofilm development

Characterization and Topical Study of Aloe Vera Hydrogel on Wound-Healing Process

Aloe Polysaccharides Inhibit Influenza A Virus Infection-A Promising Natural Anti-flu Drug

Mirbella Cáceres-Farfán, M. In vitro evaluation of anthraquinones from Aloe vera (Aloe barbadensis Miller) roots and several derivatives against strains of influenza virus

Potential use of polyphenols in the battle against COVID-19

Polyphenols vs. Coronaviruses: How Far Has Research Moved Forward? Molecules 2020

Natural product-derived phytochemicals as potential agents against coronaviruses: A review

Protective Face Masks: Current Status and Future Trends

Microplastics waste in environment: A perspective on recycling issues from PPE kits and face masks during the COVID-19 pandemic

Copper-Coated Polypropylene Filter Face Mask with SARS-CoV-2 Antiviral Ability

Prospect of Biobased Antiviral Face Mask to Limit the Coronavirus Outbreak

Antibacterial Activity and Protection Efficiency of Polyvinyl Butyral Nanofibrous Membrane Containing Thymol Prepared through Vertical Electrospinning

Non-Woven Infection Prevention Fabrics Coated with Biobased Cranberry Extracts Inactivate Enveloped Viruses Such as SARS-CoV-2 and Multidrug-Resistant Bacteria

Application of Electrospun Nonwoven Fibers in Air Filters

Face Masks to Combat Coronavirus (COVID-19)-Processing, Roles, Requirements, Efficacy, Risk and Sustainability

Cinnamic acid derivatives as promising building blocks for advanced polymers: Synthesis, properties and applications

Preparation and characterization of ferulic acid-modified water soluble chitosan and poly (γ-glutamic acid) polyelectrolyte films through layer-by-layer assembly towards protein adsorption

Evaluation of Antimicrobial and Anti-Biofilm Formation Activities of Novel Poly (vinyl alcohol) Hydrogels Reinforced with Crosslinked Chitosan and Silver Nano-Particles

Advancement of Biomaterial-Based Postoperative Adhesion Barriers

Release Performance of Biodegradable/Cytocompatible Agarose-Polyethylene Glycol-Polycaprolactone Amphiphilic Co-Network Gels

Degradable/cytocompatible and pH responsive amphiphilic conetwork gels based on agarose-graft copolymers and polycaprolactone

Silver-loaded carboxymethyl cellulose nonwoven sheet with controlled counterions for infected wound healing

Self-Assembly of Partially Alkylated Dextran-graft-poly[(2-dimethylamino)ethyl methacrylate] Copolymer Facilitating Hydrophobic/Hydrophilic Drug Delivery and Improving Conetwork Hydrogel Properties

Mesoporous Silica and Titania-Based Materials for Stability Enhancement of Polyphenols

Molecular iodine is not responsible for cytotoxicity in iodophors

Iodide and triiodide anion complexes involving anion-π interactions with a tetrazine-based receptor

Iodine binding and release from antimicrobial hemostatic polymer foams

Assembling Polyiodides and Iodobismuthates Using a Template Effect of a Cyclic Diammonium Cation and Formation of a Low-Gap Hybrid Iodobismuthate with High Thermal Stability

Single-disk antibiotic-sensitivity testing of staphylococci: An analysis of technique and results

Performance Standards for Antimicrobial Disk Susceptibility Testing

Research on the preparation and antibacterial properties of 2-Nthiosemicarbazide-6-O-hydroxypropyl chitosan membranes with iodine

Evaluation of Antioxidant Ability In Vitro and Bioavailability of trans-Cinnamic Acid Nanoparticle by Liquid Antisolvent Precipitate

Situ Generation of Bimetallic Nanoparticles in Cotton Fabric Using Aloe Vera Leaf Extract, as a Reducing Agent

Effect of PVA Blending on Structural and Ion Transport Properties of CS: AgNt-Based Polymer Electrolyte Membrane

Preparation and characterization of Aloe vera acetate and electrospinning fibers as promising antibacterial properties materials

Spectral and Thermal Properties of

Facile fabrication of cellulose membrane containing polyiodides and its antibacterial properties

Effect of KI Concentration in Correcting Tank on Optical Properties of PVA Polarizing Film

Raman spectroscopy study of new thia-and oxazinoquinolinium triodides

Modern level for the prediction of properties of iodine-containing organic compounds: Iodine forming halogen bonds

Theoretical and Microbiological Study of trans o-Coumaric Acid and Alkali Metal o-Coumarates

López-Tocón, I. Comparative Performance of Citrate, Borohydride, Hydroxylamine and β-Cyclodextrin Silver Sols for Detecting Ibuprofen and Caffeine Pollutants by Means of Surface-Enhanced Raman Spectroscopy

Bioactivity: Phenylpropanoids' best kept secret

Intermolecular Interactions and the Release Pattern of Electrospun Curcumin-Polyvinyl (pyrrolidone) Fiber

Quantitative Analysis of Copolymers and Blends of Polyvinyl Acetate (PVAc) Using Fourier Transform Infrared Spectroscopy (FTIR) and Elemental Analysis (EA)

Preparation of Aloe vera mucilage-ethyl vanillin Nano-emulsion and its characterization. Mater

Melnick and Adelberg's Medical Microbiology

The authors deeply appreciate and thank Sohaib Naseem Khan from Ajman University for providing the FTIR analysis, his continuous support and valuable input during the investigations. We are grateful to Hussain Alawadhi, Mohammad Shameer, Muhammed Irshad and Fatima Mohammed Abla from Sharjah University for providing the SEM, XRD, Raman and EDS analyses. We thank Irina Yushina for her valuable input regarding the UV-vis and Raman analysis. We thank Iman Haj Bloukh from Ajman University and Ibrahim Haj Bloukh from Ajman University for their support and input during the investigations. We are grateful to the artist "@art_by_amie" and Iman Haj Bloukh for preparing digital art images as graphical abstracts.

The authors declare no conflict of interest.Polymers 2022, 14, 1932