key: cord-0031333-91p9qka3 authors: Baseer, Rasha A.; Dacrory, Sawsan; El Gendy, Mohamed A. M.; Ewies, Ewies F.; Kamel, Samir title: A biodegradable film based on cellulose and thiazolidine bearing UV shielding property date: 2022-05-12 journal: Sci Rep DOI: 10.1038/s41598-022-11457-5 sha: 59aa7383785ef88e55474ee46276b73daf0ffb23 doc_id: 31333 cord_uid: 91p9qka3 The current rationale is exploring new eco-friendly UV- shielding films based on cellulose and thiazolidine. Cellulose was oxidized to dialdehyde cellulose (DAC) and tricarboxy cellulose (TCC) by periodate and TEMPO/periodate/hypochlorite, respectively. While E-3-amino-5-(phenyldiazenyl)-2-thioxothiazolidin-4-one (TH) was synthesized by coupling diazonium salt with the 5-methylene of 2-thioxo-4-thiazolidinone. DAC was then coupled with TH via Schiff base reaction and incorporated onto TCC with different ratios to get UV-shielding films. (1)HNMR, infrared spectroscopy (FTIR), and thermal gravimetric analysis (TGA) were used to investigate the chemical structure of the synthesized materials. In addition, the films' morphology, thermal, mechanical, and UV-shielding properties were investigated. The UV-shielding studies revealed that the film with 10% DAC-TH has 99.88, 99.99, and 96.19% UV-blocking (UVB), UV-absorbance (UVA), and Ultra-violet protection (UPF), respectively. Moreover, the prepared films demonstrated promising antimicrobial activity against Escherichia coli, S. aureus, P. aeruginosa, and Candida albicans. Finally, the prepared films showed no cytotoxic effects on normal human skin fibroblast's HFB-4 cell line. For the last decades, polymer films have been widely applied as packaging materials in many primary industries such as food, drugs, and electronic devices for their significant low cost, lightweight, good elasticity, and high transmittance 1,2 . However, scientists have turned to create biodegradable materials with the mounting voices calling for environmental conservation and the trend to use friendly materials 3, 4 . These materials, obtained from renewable sources, are pure polymer, composite or blended products, and they could be classified as green polymer. Recently, cellulosic materials have emerged as a strong alternative to synthetic polymers due to their unique biocompatible, biodegradable, non-toxic, and allergen-free 5 . Depending on its functional group that can be inserted into its chains backbone via the suitable modification. It looks most promising material and plays an important role in many applications such as drug delivery 6 , conductive materials 7, 8 , Fertilizers agents 9 , and water treatment 10 . Dialdehyde cellulose (DAC) is the most widely utilized oxidized cellulose with highly reactive sites. Periodate is widespread to oxidize cellulose to dialdehyde cellulose 11, 12 . It oxidizes the vicinal hydroxyl groups of cellulose at C2 and C3 6 . In recent years, dialdehyde cellulose has received increasing attention as an ideal crosslinking agent whose aldehyde groups can crosslink with NH 2 of the amino acid via Schiff 's base interaction 7 . On the other hand, the building of UV-block cellulose films became an urgent need for further development and applications as biodegradable and eco-friendly UV-shielding materials 13, 14 . Many approaches have been performed to develop UV-shielding cellulose through thermal treatment technology, presented as a green and straightforward approach for preparing UV-block cellulose. However, this method depends on the yellow discoloration of cellulosic fibers during the treatment 15, 16 . Moreover, UV absorbers are considered the dominant technology to achieve high UV protection via incorporating them into cellulose films. In this context, the development of highly efficient cellulose-based UV-shielding films has the scientist's great attention 17 . Organic and inorganic UV-absorbers are mostly incorporated into cellulosic films to achieve UV protection depending on the type of functional group inserted in its chain backbone 13 www.nature.com/scientificreports/ On the other hand, heterocyclic compounds can be found in natural and synthetic materials and are mainly known for their significant UV-absorbing property [18] [19] [20] . 3-amino-2-thioxothiazolidin-4-one, commonly known as rhodanine, has a broad spectrum of biological activities demonstrating antiseptic, anti-inflammatory, antiparasitic, antifungal, antidiabetic, antiviral, and antineoplastic activity [21] [22] [23] . Many studies were performed on rhodanine derivatives to prove antimicrobial activity 24, 25 . Also, their azo dyes derivatives are used as a spectrophotometric chemosensor for Fe 3+26 with optical properties 27 . Based on this survey herein, we aim to synthesize E-3-amino-5-(phenyldiazenyl)-2-thioxothiazolidin-4-one (TH) and couple it with dialdehyde cellulose (DAC) to exploit the dual π bond of each of the aryl azo group, thioxothiazolidin-4-one, and the aldehyde oxime of DAC resulted from Schiff base beside to the lone pair of nitrogen, sulfur, oxygen which overlap arising to the splitting of the originally degenerate n orbitals to promote high UV absorbance material. It is incorporated with different ratios into tricarboxylic cellulose (TCC) to formulate biodegradable and antibacterial film with UV-shielding and high safety when tested on normal human skin fibroblasts viability. The mechanical, morphology, UV-absorbance and thermal properties of the produced film have been evaluated. Materials. Bleached bagasse pulp was supplied from Quena Company of Paper Industry, Egypt, with chemical composition, cellulose (96%), hemicellulose (3%), and lignin (3%). Dulbecco's modified Eagle's medium (DMEM), [3-(4,5-dimethylthiazol-2-yl)-2,3-diphenyltetra zoliumbromide] (MTT), Sodium meta periodate (NaIO 4 ), NaBr, and 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO) were purchased from OXFORD LAB FINE CHEM LLP (Navghar, Vasai East, Maharashtra, India). Penicillin-streptomycin, amphotericin B, trypsin/EDTA solution, L-glutamine, and fetal bovine serum (FBS) were obtained from Invitrogen (Carlsbad, CA, USA). Doxorubicin HCl (Adricin ® ) was purchased from EBEWE Pharma (Unterach, AUSTRIA). Tissue culture flasks and tissue culture plates were purchased from Cole-Parmer(UK). All chemicals and reagents were used in analytical grade without any purification required before use. In a reaction vessel, 5.1 mmol of sodium nitrite solution was dropped wisely for 10 min to the cooled solution of aniline (5 mmol) and 25 mL of aqueous hydrochloric acid solution (12 M, 32.19 mmol) . The produced diazonium chloride was preserved at 0-5 °C; after that, an ethanolic solution (25 ml) of 2-thioxo-4-thiazolidinone (5 mmol) and sodium acetate (5 mmol) was added dropwise over 20 min. The resulting sludge mixture was stirred for 2 h at 5 °C before remaining standing overnight. The obtained dark brown precipitate (TH) was filtered, washed with water many times, and recrystallized by hot ethanol as shown in Fig. 2 28 , MS m/z: 252 (81%). Oxidation of cellulose to dialdehyde cellulose (DAC). Dialdehyde cellulose was prepared by oxidation of cellulose by sodium periodate under the effect of a microwave. Briefly, in 20 ml distilled water 1.5 g of cellulose was dispersed, followed by adding 2 g of sodium periodate, and pH was adjusted to 3. The precursor was transferred to the domestic microwave (power 800 W) for 1.5 min. The oxidized product (dialdehyde cellulose) was filtered, washed with ethanol several times, and dried 29 . The yield was calculated and it was 75% based on the weight of cellulose. Schiff 's base reaction was used to calculate the aldehyde content of the oxidized cellulose, wherein aldehyde groups reacted with hydroxylamine hydrochloride forming an oxime. Va identifies the volume of alkali solution expended during the titration (in liter). The volume of 1.0 M sodium hydroxide solution consumed was presented as Vc, and the same concentration of cellulose solution at pH 5.0 was used as a blank (in liter) 5 : In which CNaOH = 1.0 M, m denotes the dry mass of DAC (0.3 g) used during the experiment, and M denotes the molecular mass of the cellulose repeating unit (162). Oxidation of cellulose to tricarboxylic cellulose (TCC). Cellulose was oxidized to tricarboxy cellulose through three steps; In the first step; to water-dispersed cellulose (5 g/ 500 mL), 0.08 g (0.5 mmol) of TEMPO reagent and 0.8 g (8 mmol) sodium bromide were added, followed by 50 mL (10%) of sodium hypochlorite solution and adjusting the pH to 10with stirring overnight. At the end of the reaction, the solution was neutralized and centrifuged at 7000 rpm, and washed with water. Finally, it was dialyzed for 1 week against water to complete the TEMPOoxidized cellulose purification process. In the second step, sodium periodate was added to suspend TEMPOoxidized cellulose (1% consistency). To prevent the photo-induced decomposition of the periodate, the reaction container was wrapped with aluminum foil. After 3 h, the reaction was terminated by adding ethylene glycol, washed with distilled water, and filtered, giving dialdehyde carboxy cellulose. In the third step, a mixture of acetic acid (20%) and sodium chlorite solution was added slowly to a suspended dialdehydecarboxy cellulose (4.5% consistency), giving yellowish color and stirring for 48 h at ambienttemperature. Eventually, the induced tricarboxy cellulose (TCC) was In the third step, a mixture of acetic acid (20%) and sodium chlorite solution was slowly added to a suspended dialdehydecarboxy cellulose (4.5%), producing a yellowish colour and stirring for 48 h at room temperature. Eventually, the induced tricarboxy cellulose (TCC) was scrubbed with deionized water and filtered. TCC carboxylate content was calculated using the electric conductivity titration method by merging 50 mg of the dried sample with 0.01 M HCl (15 mL) and deionized water (20 ml). The mixture was stirred to achieve a well-dispersed suspension. Titration with 0.01 M NaOH aqueous www.nature.com/scientificreports/ solution was performed on the dispersed solution. The drastic shift in conductivity deduced the carboxylate content of TCC (C (mmol/g)) using the following Eq.: where V1and V0 represent the volumes of NaOH solution before and after titration, CNaOH is the concentration of NaOH solution, and m is the weight of the dried sample 30, 31 . A suspended solution of DAC (1 g/ 20 ml distilled water) was added to a solution of TH (1 mol/ 30 ml of ethanol) and refluxed for 2 h with stirring. The resulted orange precipitate (DAC-TH) was filtered, washed several times with diluted ethanol, and dried at 80ºC for 24 h (yield ~ 60%). Preparation of TCC/DAC-TH film. Different ratios of DAC-TH (2.5, 5, 7, and 10% based on the total weight of the film) were added into an aqueous dispersion TCC solution with drops of the glycerol as a plasticizer followed by sonication for 10 min, 30% P. The resulting TCC/DAC-TH suspension was poured into Teflon dishes and dried at 60 °C for 24 h. Characterization. FTIR spectra were performed on a Beckman infrared spectrophotometer PU 7712 using a KBr disk (United States). The scans recorded were the average of 100 scans and the selected spectral range between 500 and 4000 cm −1 . The 1 HNMR spectra were measured on Bruker AVANCE 400 MHz spectrometer (Bruker) with a 5 mm BBFO probe using deuterated dimethyl sulfoxide (DMSO-d6) as the solvent (Germany). Morphological studies have been measured using a scanning electron microscope (SEM) (Hitachi High Technologies America, Schaumburg, IL). The thermal behavior (TGA/DSC) is performed via (Perkin Elmer thermogravimetric analyzer (Waltham, Massachusetts, USA) under nitrogen conditions heating rate was 10 °C/min from 50 to 500 °C. The mechanical properties of the prepared films were investigated using Universal Testing Machine model 4201 from Instron 33 . The stress-strain curve of films was tested on 6 cm film bars (width 15 mm; length 20 mm) with a Lloyd instrument (Lloyd Instruments, West Sussex, United Kingdom) with5-N load cell measurements at ambient temperature. The UV-blocking properties of the TCC/DAC-TH films were performed by measuring their absorbance and total transmittance with a Shimadzu UV-3600 spectrometer from 200 to 2500 nm (UV-Vis-NIR spectrum, Japan). The T (UVA)and T (UVB) of the TCC/DAC-TH films were calculated using the following equations 14 : The UV-protection factors (UPF) of films were measured by the AATCC 183-2010 using a UV-vis spectrophotometer, where T λ is the light transmittance of TCC/DAC-TH films. The air was used as the control reference. UPF was measured from the transmission spectra of the films in the range of 290-400 nm using the following equation 34 : where E(λ) is the relative erythemal spectral effectiveness, S(λ) is the solar spectral irradiance in Wm −2 nm −1 . The values were provided by the National Oceanic and Atmospheric Administration database (NOAA)), T(λ) is the spectral transfer of the data taken from UV spectrophotometric tests, and Δ(λ) is the variation among observable wavelengths. Evaluation of the antibacterial activities. Using nutrient broth medium, the microbial activity of TCC/ DAC-TH films was quantified against I Gram-negative bacteria: Escherichia coli (NCTC-10416); (ii) Grampositive bacteria: Staphylococcus aureus (NCTC-7447); and (iii) unicellular fungi: Candida albicans (NCCLS 11). according to Hamed et al. 35 .The inhibition percentages were calculated for the crude antimicrobial material using the serial dilution method via colony formation unite (CFU) technique according to the procedure described by Abdelraof et al. 36 . Cell culture and determination of cell viability. Human skin fibroblastsHFB-4 cell line was obtained from the Egyptian National Cancer Institute, Cairo University, Egypt. The cells were maintained in DMEM media supplemented with 10% heat-inactivated FBS, 2 mMl L-glutamine, 100 IU/mL penicillin, 100 μg/mL streptomycin, and 0.25 μg/mL amphotericin B. Cultures were grown in 75cm2 tissue culture flasks at 37 °C in a humidified incubator with 5% CO2 and subcultured every 3-5 days. Cells were treated with increasing concentrations of each treatment. As previously described, viability was calculated by monitoring the ability of reducing enzymes existing in viable cells to convert MTT to formazan Ethical approval. The cell experiments were consistent with the protocols adopted by the local ethical committee (Ethical Committee of National Research Centre). Chemistry. As presented in Fig. 1 TCC/DAC-TH film was prepared in several steps and evaluated as a UV-shielding, where the assumed synthetic mechanisms of TH, DAC, DAC-TH, and TCC/DAC-TH films are outlined in Figs. 2, 3, 4 . TH was synthesized from the reaction of the diazonium salt with the 5-methylene of 2-thioxo-4-thiazolidinone through a coupling reaction (Fig. 2) with a yield of 81%. As apparent in Fig. 3 , DAC has successfully synthesized via periodat oxidation with dialdehyde content 60%. As is well known, reactive aldehyde functionalities can exist as hydrates, hemialdals, and hemiacetals 32 . The intra-chain and intra-anhydroglucose unit hemiacetal structure are feasible among C2/C6 and C3/C6 and hemialdal C2/C3 38 . In addi- www.nature.com/scientificreports/ tion, DAC-TH was prepared via a Schiff base reaction as presented in Fig. 3 . An amine reacted with a carbonyl compound (DAC) via nucleophilic addition, and then dehydration formed hydrated cellulose aldehyde. Also, according to a previous study, Scheme 3 defines the suggested mechanism of formation of TCC with carboxyl contents of 2 ± 0.3 mmol/g 30 . In the presence of sodium bromide and sodium hypochlorite, TEMPO performs as a mediator as selectively oxidation of the primary hydroxyl groups (C6). After that, hydroxyl groups in C2 and C3 were oxidized to the aldehyde groups using periodate, which further oxidized to generate TCC. The afforded TH, DAC, and DAC-TH were confirmed by 1 HNMR and FT-IR (Fig. 5 ). As evident, 1 Fig. 5 shows significant FTIR spectra for TH, DAC, DAC-TH, TCC, and TCC/DAC-TH film. FTIR spectra of DAC, TH, and DAC-TH reveal a band at 3320 cm −1 related to (OH) for both DAC and DAC-TH 39 , a band at 3300 cm −1 assigned to (NH 2 ) of TH 40 , a band at 2943 cm −1 corresponding to (C-H vibration), 1680 cm −1 regarding C=O stretching δ-lactam, the band at 1630 cm −1 is due to C=O in DAC, due to hemiacetal bond formation (between aldehyde groups and their adjacent hydroxyl groups OH), so sometimes this peak can be very small and hidden due to presence DAC in the hydrated form 41, 42 . The band at 1610 cm −1 regarding to both (N=N) and (C=N) 43 , 1360 cm −1 for C-N, 1230 cm −1 for C=S 43 and 1030 cm −1 related to -C-O-C pyranose ring skeletal vibration 44 . Also, bands at 1733, 1615, 1230, and 1024 cm −1 attributed to stretching δ-lactam, carboxylate groups, C=S, and -C-O-C pyranose ring skeletal vibration, respectively 40,44 (Fig. 5 ). Thermogravimetric analysis. The thermogravimetric analysis (TGA) of TCC films with 0, 2.5, and 10% DAC-TH is presented in Fig. 6 . As apparent, three stages of degradation are observed for both TCC and TCC/10%DAC-TH. At the first stage of TCC thermal degradation, the wt loss is about 7% at 68-169 °C, attributed to water evaporation. The second stage is the degradation initiation temperature of TCC, which occurs from 169-330 °C and the wt loss is 47% due to the formation of CO 2 , H 2 O, and CO 35 . Finally, the residual solid www.nature.com/scientificreports/ at 190-232 °C due to DAC oxime azo degradation, 36% wt loss at 232,311 °C to the formation of CO 2 , H 2 O, and CO. The final TCC/2.5% DAC-TH residual solid is about 15% at 311-600 °C. cal structure of DAC fiber, TCC, and TCC/DAC-TH films are characterized via scanning electron spectroscopy (SEM). As presented in Fig. 7 , DAC fiber seems like a hair cluster structure, while TCC film showed a smooth surface. Furthermore, TCC/DAC-TH film showed a rough, thick layer of DAC-TH with semi-uniform dispersion. On the other side, the existence of DAC-TH was confirmed by Energy Dispersive X-ray spectroscopic analysis (EDX). EDX ensures the significant elements of DAC-TH, where the EDX analysis of TCC/showed two signals related to N and S opposite what TCC/DAC-TH film presents. Mechanical properties. The ability of films to withstand external stress is one of the essential features of films, and mechanical properties control this ability Fig. 8 shows the stress/strain curves of TCC/DAC-TH films with different ratios of DAC-TH that were investigated at room temperature. As it seems, increasing DAC-TH ratios decreases the tensile strength and elongation of the prepared films. For example, tensile strength and elongation of TCC film were 6.5 MPa and 4 mm and decreased to 2.5 MPa and 2 mm, respectively, with the addition of DAC-TH. It may be attributed to crosslinking formation between TCC and DAC-TH that causes structure deformation; as a result, the crystallinity of the films decreases. UV-shielding performance. UV absorbers have been widely used for UV-shielding improvement of films as the indispensable demand in several packaging industries [47] [48] [49] . As previously known, heterocyclic compounds have significant UV absorption properties 20, 34, 50 . Therefore, TH has been used to graft DAC and incorporated the resulted DAC-TH into TCC with different ratios to evaluate their UV-shielding features. Figure 9a presents the UV absorbance of TH and DAC-TH in DMSO using a Shimadzu UV-vis-2401 PC from 200-700 nm. It is known that the absorption spectrum of azobenzene and its derivatives shows three major absorption regions accordingly to the basis of Molecular Orbital Theory (MO) 51 . Where the solution of TH and DAC-TH showed main absorption peaks at 296and 427 nm for both of them due to π → π * transition and locally excited π i → π j * transition in benzene rings. Moreover, the two nitrogen atoms of the azo group exhibit two lone-pair orbitals that overlap, arising from the splitting of the originally degenerate n orbitals where the higher and lower energy orbitals are symmetric combination (ns) antisymmetric combination (n a ), respectively. Eventually, TH and DAC-TH solutions exhibit absorption bands at 479and 487 nm, respectively, which may be attributed to the n s→ π i transition 52 , where it seems weak for DAC-TH, maybe back to the overlap results from the aldehyde oxime of DAC. The films' UV absorbance and transmittance curves are shown in Fig. 9b ,c, which clarify the impact of increasing the DAC-TH ratio on the UV shielding properties. According to the equations, the transmittance of UV-A (320-400) and UV-B (280-320) were implemented to explore UV Shielding properties. The obtained results indicated that TCC/DAC-TH films showed an excellent UV shielding capacity at which the film with the highest DAC-TH ratio (10%) has the highest UV transmittance of UVA (99.99%) and UVB (99.88%). Therefore, DAC-TH has excellent sensitivity toward UV light and can absorb light ranging from 200 to 400 nm. On the other side, the film's transparency descends with increasing the DAC-TH ratio. On the other hand, the UV-protection (UPF) study of TCC/DAC-TH films agrees with the UV-shielding study. As clear in Fig. 10 , DAC-TH addition shows UV protection compared without DAC-TH. Herein, TCC/ DAC-TH film of 10% DAC-TH has excellent UV protection according to standard methods. The evolution of UPF values between 0-50 while between 15-24 is good, 25-39 is very good, and > 40 is excellent UV protection. Evaluation of the antibacterial activities. The antimicrobial activity screening of thiazolidine derivatives against common bacteria and fungi revealed a high inhibition effect 53, 54 . Consequently, the thiazolidine derivative such as TH was coupled with DAC giving DAC-TH, and to formulate this derivative, it was loaded onto TCC to give films. The efficiency of antimicrobial activity of TCC/DAC-TH films with different ratios of DAC-TH on Escherichia coli, S. aureus, and Candida albicans has been distinguished by the CFU technique as described previously (Table 1 ). In this respect, TCC film without DAC-TH did not show any antimicrobial effect. In contrast, TCC films with DAC-TH had an antimicrobial effect for all tested microorganisms, which was due to TH being characterized by antimicrobial activity. Dandia et al. recommended that N-C-S linkage is responsible for the antifungal activity of thiazolidine derivatives 55 . Moreover, increasing DAC-TH content in TCC films inhibited the growth of bacteria and fungi. In contrast, with the same DAC-TH content in films, the films have a highly inhibited effect on Escherichia coli than Staphylococcus aureus. The rate of inhibition of fungi (Candida albicans) was higher than that of bacteria. The results showed that the 10% DAC-TH content inhibited 72, 64, and 66% of Escherichia coli, Staphylococcus aureus, and Candida albicans. Determination of cell viability. To test whether the prepared films can affect cell viability, we chose human skin fibroblasts HFB-4 cells. HFB-4 cells have been used previously to study the harmful effect of UV radiation and to detect the role of UV protecting agents 56 . As indicated in Fig. 11 , all prepared films and TCC showed no cytotoxicity up to 100 mcg/mL when incubated with HFB-4 cells for 24 h. In contrast, DAC-TH showed moderate cytotoxicity that was statistically significant compared to vehicle-treated cells starting from 25 mcg/mL (Fig. 7a) . Photographs were captured for all treatments at 100 mcg/mL, and the positive control, doxorubicin, after 24 h incubation period that reflected the safety of all the prepared film formulations (Fig. 11b) . www.nature.com/scientificreports/ In conclusion, a new antimicrobial/ UV protection film based on cellulose and E-3-amino-5-(phenyldiazenyl)-2-thioxothiazolidin-4-one was successively prepared. In addition to film preparation, the properties of the films, such as UV protection, mechanical, thermal, and biological, were studied. A high degree of UV protection appeared with 10% dialdehyde cellulose. The prepared films have demonstrated significant antibacterial activities and did not affect the cell viability of human skin fibroblasts. Thus, this product is synthetically important and possesses a wide range of promising applications like food packaging, skincare materials, and electronic device coating. Aluminium oxide barrier films on polymeric web and their conversion for packaging applications Polymer-silicate nanocomposities: Package material for nanodevices as an EMI shielding Novel biodegradable polymer films based on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and Ceiba pentandra natural fibers for packaging applications Recent advances in the sustainable design and applications of biodegradable polymers A new approach for antimicrobial and antiviral activities of biocompatible nanocomposite based on cellulose, amino acid and graphene oxide Biocompatible hydrogel based on aldehyde-functionalized cellulose and chitosan for potential control drug release Functionalization and cross-linking of carboxymethyl cellulose in aqueous media Potential anticorrosive performance of green and sustainable inhibitor based on cellulose derivatives for carbon steel Cellulose-based hydrogels as smart, green and controllable nitrogenous fertilizers releasing agents Physically-crosslinked hydroxyethyl cellulose-g-poly (acrylic acid-co-acrylamide)-Fe 3+ /silver nanoparticles for water disinfection and enhanced adsorption of basic methylene blue dye Effects of periodate oxidation on cellulose polymorphs Development of mesoporous foam based on dicarboxylic cellulose and graphene oxide for potential oil/water separation Binary strengthening and toughening of mxene/cellulose nanofiber composite paper with nacre-inspired structure and superior electromagnetic interference shielding properties Highly transparent graphene oxide/cellulose composite film bearing ultraviolet shielding property Effects of drying-induced fiber hornification on enzymatic saccharification of lignocelluloses Thermally-induced cellulose nanofibril films with near-complete ultraviolet-blocking and improved water resistance Preparation and anti-UV property of modified cellulose membranes for biopesticides controlled release Synthesis of reactive UV absorbers, derivatives of monochlorotriazine, for improvement in protecting properties of cellulose fabrics Application of benzotriazole reactive UV absorbers to cellulose and determining sun protection of treated fabric spectrophotometrically Synthesis of novel heterocyclic imine type UV absorbers for application on cotton based textile materials 5-Ene-4-thiazolidinones-An efficient tool in medicinal chemistry Green, three component highly efficient synthesis of 2-amino-5, 6, 7, 8-tetrahydro-4-H-chromen-3-carbonitriles in water at ambient temperature Simple, three-component, highly efficient green synthesis of thiazolo [3, 2-a] pyridine derivatives under neat conditions Antibacterial properties of 5-substituted derivatives of rhodanine-3-carboxyalkyl acids Microwave assisted synthesis of 3-[alpha]-carboxy ethylrhodanine derivatives and their in vitro antibacterial activity Synthesis and antibacterial activity of rhodanine-based azo dyes and their use as spectrophotometric chemosensor for Fe3+ ions Second-order non-linear optical properties of new organic conjugated molecules Über Isonitrosoacetanilide und deren Kondensation zu Isatinen Antimicrobial activity, DFT calculations, and molecular docking of dialdehyde cellulose/graphene oxide film against Covid-19 Novel method of preparation of tricarboxylic cellulose nanofiber for efficient removal of heavy metal ions from aqueous solution Development of dielectric film based on cellulose loaded nano-silver and carbon for potential energy storage Review: Periodate oxidation of wood polysaccharides-Modulation of hierarchies In situ synthesis of Fe3O4@ cyanoethyl cellulose composite as antimicrobial and semiconducting film Modified cotton fabrics with poly (3-(furan-2-carboamido) propionic acid) and poly (3-(furan-2-carboamido) propionic acid)/gelatin hydrogel for UV protection, antibacterial and electrical properties Enhancement of multifunctional properties of leather surface decorated with silver nanoparticles (Ag NPs) Green synthesis of bacterial cellulose/bioactive glass nanocomposites: Effect of glass nanoparticles on cellulose yield, biocompatibility and antimicrobial activity Induction of quinone oxidoreductase 1 enzyme by Rhazya stricta through Nrf2-dependent mechanism Determination of molar mass distributions of highly oxidized dialdehyde cellulose by size exclusion chromatography and asymmetric flow field-flow fractionation Preparation and properties of cellulose nanocrystals: rods, spheres, and network. Carbohyd The Handbook of Infrared and Raman Characteristic Frequencies of Organic Molecules Physicochemical characterization of novel Schiff bases derived from developed bacterial cellulose 2, 3-dialdehyde Modification of carboxymethyl cellulose through oxidation Flow injection analysis of mercury using 4-(dimethylamino) benzaldehyde-4-ethylthiosemicarbazone as the ionophore of a coated wire electrode Thermo-responsive cellulose-based material with switchable wettability for controllable oil/water separation Preparation of dicarboxyl cellulose nanocrystals from agricultural wastes by sequential periodate-chlorite oxidation Thermal decomposition of dialdehyde cellulose and its nitrogen-containing derivatives Coupled heat, mass and momentum transport in swelling cellulose based materials with application to retorting of paperboard packages Preparation of UV absorbent films using polylactic acid and grape syrup for food packaging application New UV absorber for PET packaging: Better protection with less discoloration Triazole ultraviolet absorbers with enrichment performance for material surfaces protection from ultraviolet rays The electronic spectra of azobenzene derivatives and their conjugate acids Studies on the UV-vis absorption spectra of azo dyes: Part 25. 11For Part 24 see Mustroph 4-Thiazolidinone-A biologically active scaffold Synthesis and antimicrobial activities of 5-arylidene-thiazolidine-2,4-dione derivatives Efficient microwave enhanced regioselective synthesis of a series of benzimidazolyl/triazolyl spiro [indolethiazolidinones] as potent antifungal agents and crystal structure of spiro Evaluation of natural bioactive-derived punicalagin niosomes in skin-aging processes accelerated by oxidant and ultraviolet radiation. Drug Des The authors thank the National Research Centre for the financial support. Also, they thank Dr. Mohamed Hasanin, Department of Cellulose and Paper, National Research Centre, Egypt, for carrying out the antimicrobial screening experiment. The manuscript was written through the contributions of all authors. All authors have approved the final version of the manuscript. Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). Open access funding is provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). The authors declare no competing interests. Correspondence and requests for materials should be addressed to R.A.B. or S.D.Reprints and permissions information is available at www.nature.com/reprints.Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.