key: cord-0029769-nt0bwpzz authors: Zare, Alireza; Behaein, Saeed; Moradi, Mahmoud; Hosseini, Zahra title: Application of a dual functional blocking layer for improvement of the responsivity in a self-powered UV photodetector based on TiO(2) nanotubes date: 2022-03-29 journal: nan DOI: 10.1039/d2ra00379a sha: cfbcbad7c74f0298ee5d0ce1b1ab47b5debcfea5 doc_id: 29769 cord_uid: nt0bwpzz A layer of graphene quantum dots (GQDs) was applied on the photoanode of a self-powered photoelectrochemical (PEC) UV photodetector based on TiO(2) nanotubes (NTs). The GQDs layer acted as a dual functional layer and improved the photodetector performance by both UV light absorption and blocking the charge carriers recombination at the photoanode/electrolyte interface. The short circuit current density (Jsc) and thereby the responsivity of the PEC UV photodetector was enhanced by 473%. The highest value of the responsivity in this work obtained for the PEC UV photodetector with the dual functional GQDs layer was as much as 42.5 mA W(−1). This value is far better than previously reported responsivities of the PEC devices based on TiO(2) NTs as a photoanode. This high responsivity was obtained under the illumination of a very low intensity UV light (365 nm, 2 mW cm(−2)) and 0 V bias. Moreover, the sensitivity of the PEC UV photodetector with the dual functional GQDs layer has been improved by 345%, which is almost 3.5 times higher compared to the sensitivity of its counterpart without the GQDs coating. The devices with the dual functional GQDs layer present a splendid repeatability and stability. The rise time and the decay time of this device were measured to be 0.73 s and 0.88 s under the on/off switching UV LEDs, respectively. The electrochemical impedance spectroscopy (EIS) results prove the role of the GQDs layer as an effective blocking layer on the photoanode, hindering the charge carrier recombination at the photoanode/electrolyte interface. This study shows that application of the dual functional GQDs layer in the PEC UV photodetector based on TiO(2) NTs is an effective approach for improving the responsivity and sensitivity of a self-powered PEC UV PD, which brought us the possibility of detecting low UV index radiation and using the self-powered photodetectors in cutting-edge wearable electronic devices for the aim of health, safety and environmental monitoring. The process of detecting ultraviolet (UV) light has always been critical in scientic applications and several industries such as UV communication, environmental monitoring, biomedical and chemical analysis. 1-4 Recently, optoelectronic wearable devices with the intentions of health, safety and environmental monitoring are becoming more and more popular. Thus, a device with the capability of working without any external bias voltage, namely a self-powered photodetector and the ability of detecting low intensity UV light as well, is essential. So far, several types of self-powered photodetectors have been developed. Xu et al. reported a self-powered UV photodetector based on p-CuZnS/n-TiO 2 . 5 Although it was designed to operate at 0 V bias for the aim of a wearable UV detection system, the responsivity of the device was rather low. Gao et al. developed a self-powered p-n heterojunction UV photodetector using nanorod arrays. 6 The device worked in a self-powered mode but still suffered from an insufficient photocurrent and thereby low responsivity. Another type of self-powered UV photodetector based on a p-n junction was revealed by Ning et al. which showed a very low responsivity of 1 mA W À1 at zero bias. 7 Despite the great diversity of developed self-powered UV photodetectors, still innovative and simple approaches need to be developed to improve the spectral responsivity of these devices as well as reducing the cost and fabrication difficulties. Among various types of self-powered UV photodetectors, photoelectrochemical (PEC) cells are of great interest owing to their ease of fabrication process and low cost. 8 Up to this point, several wide bandgap semiconductors including ZnO, SnO 2 , TiO 2 , etc., have been utilized in the PEC UV photodetectors. [9] [10] [11] The investigations conrm TiO 2 as an ideal candidate for the main UV absorption material in the PEC UV photodetectors and photocatalyst applications 12-14 due to their appropriate characteristics such as: wide bandgap, E g (anatase phase) ¼ 3.2 eV, superior chemical stability, no toxicity and environmental safety. [15] [16] [17] TiO 2 has been applied in PEC UV photodetectors in different structures, [18] [19] [20] among which, TiO 2 nanotube has gained much attention due to high surface area, proper charge carrier transport and inexpensive method of synthesis. [21] [22] [23] Li et al. manufactured a self-powered ultraviolet photodetector based on TiO 2 /Ag/ZnS nanotubes with the maximum photocurrent of 497 mA under UV illumination of 40 mW cm À2 and 0 V bias. 24 Chen et al. reported a self-powered UV photodetector with self-doping TiO 2 nanotube arrays which has gained the maximum photo responsivity of 22 mA W À1 . 25 Li et al. prepared a TiO 2 -graphene composite as the UV sensitive layer in a self-powered UV photodetector, which has the ability to reach the responsivity of 11 mA W À1 . 26 In the PEC UV photodetectors based on TiO 2 NTs, the tubes are responsible for UV light absorption. A full absorption of incident UV photons is necessary in a competent UV photodetector. Short TiO 2 NTs are not able to absorb UV photons efficiently. Therefore, application of long TiO 2 NTs seems to be essential for achieving enough light absorption and thereby obtaining high current and responsivity in the device. On the other hand, research shows that fabrication of defect free and long TiO 2 NTs is challenging. 27 Due to the longer TiO 2 NTs, the carrier transport path length is relatively longer and consequently the probability of emerging defects on their surface is much higher. Chances of electron-hole recombination are thus higher in longer TiO 2 NTs. In fact, there is usually a trade-off between light harvesting efficiency and carrier collection efficiency in the devices based on the TiO 2 NTs. One should use the shortest possible TiO 2 NTs to maximize the electron collection efficiency. This can be the reason that despite all the outstanding properties of TiO 2 nanotubes, low photo response and quantum efficiency limit the associated photodetectors' practical use in innovative optoelectronic devices. 10 Therefore, new practical strategies need to be applied to improve the responsivity of these devices. Herein, we introduce a unique idea of applying graphene quantum dots (GQDs) to the self-powered PEC UV photodetector based on TiO 2 NTs as a dual functional coating. A monolayer of GQDs which serves as both a light absorber and a blocking layer was used in the device. GQDs are sizedependent bandgap semiconductors with high carrier mobility and good chemical stability which have been used as the photo-sensitive material in different photoelectrochemical and photocatalytic applications. [28] [29] [30] The studies show that the relative position of the GQDs and TiO 2 energy levels guarantees the injection of the electrons from the conduction band (CB) of GQDs to the CB of TiO 2 . Therefore, in our PEC UV photodetectors, there are two active UV absorbing layer, i.e., TiO 2 and GQDs. The photogenerated electrons in the GQDs nally contribute in the current generation by getting injected into the CB of TiO 2 NTs and transferring to the external circuit. The GQDs also cover the surface defects of the TiO 2 NTs and block the recombination of the photogenerated electrons with the redox species in the electrolyte. Accordingly, our results show that compared to the photodetectors made with bare TiO 2 NTs, the device with GQDs reveals improved responsivity and sensitivity. What's more, our approach lets us skip the challenges of fabricating defect free, long TiO 2 NTs and provides the opportunity to make self-powered PEC UV photodetectors with high responsivity using shorter TiO 2 NTs. Considering the remarkable improvements achieved in the performance of the selfpowered photodetectors based on TiO 2 NTs, employing a proper blocking layer which also serves as a UV absorber layer is an effective practical procedure to develop the performance of the self-powered PEC UV photodetectors based on TiO 2 NTs. TiO 2 NTs were synthesized on Ti foil via a two-step anodization method. 0.25 mm thick titanium foil (99.7%; Sigma-Aldrich) with desired dimension were sonicated in ethanol, acetone and DI water to remove any unwanted substance on the surface of the Ti foil. A two-electrode electrochemical cell lled with electrolyte containing ethylene glycol solution of 0.3 wt% NH 4 F and 2 vol% H 2 O was used for the preparation of NTs on Ti foil. The Pt and Ti were used as counter and working electrodes respectively. The rst anodization step was done for 30 minutes under 60 V potential and 25 C temperature. To obtain a highly ordered TiO 2 NTs, the rst layer of NTs was peeled off the foil via sonication of the sample in DI water for 10 minutes. The second anodization step was performed in a new electrolyte solution at different times to get the desired NTs with different heights from approximately 3 to 20 mm. To attain the TiO 2 NTs in anatase phase, an annealing process of anodized samples was carried out in 450 C for 2 h. Hydrothermal method was used to prepare N-doped GQDs as it was reported in our previous work. 31 A mixture of 1.26 g citric acid monohydrate (Merck), 1.08 urea (Merck) and 30 mL H 2 O were stirred to get a fully clear solution. The prepared solution was then transferred into a 50 mL Teon lined autoclave and heated in an electric furnace in 200 C for 24 h. Aer the heating step, the nal yellow solution was centrifuged at 6000 rpm for 20 minutes. In the nal step, the separated GQDs powder was re-dispersed into DI water. Fluorine doped tin oxide (FTO)-coated transparent glass was used as counter electrode in the device. Platinized counter electrode was prepared by depositing Pt paste (Sharif Solar, Iran) onto the surface of the FTO glass using Dr Blade method. For the application of the blocking layer, the GQDs coated on the TiO 2 NTs by dip coating the NTs in GQDs solution for a specic time. Subsequently, the platinized FTO glass and the photoanode were sealed (with Surlyn spacer) with conductive side of the FTO facing inward. Finally, some I/I 3 À redox couple electrolyte (Sharif Solar, Iran) was injected into the space between two electrodes for providing ionic conductivity. The photodetectors made with and without GQDs blocking coating are labelled as GQD-TNT-PD and TNT-PD, respectively. The X-ray diffraction spectroscopy (XRD; D8-ADVANCE) with Cu k (1/4 1.540 A) radiation over Bragg angles ranging from 10 to 80 was performed to conrm the crystal structure of GQDs and TiO 2 NTs. The GQDs morphology was inspected using transmission electron microscope (TEM; Zeiss EM900). The surface morphology of TiO 2 NTs was analysed using eld emission scanning electron microscope (FESEM; MIRA3 TESCAN-XMU) and scanning electron microscope (SEM; TESCAN-Vega3) equipped with an energy-dispersive X-ray spectrometer (EDS) for elemental analysis. To characterize the functional groups on the surface of GQDs, a Fourier-transform infrared spectroscopy (FTIR; Tensor II, Bruker) was conducted. Raman spectroscopy (Raman; LabRam HR, Horiba) was used to verify the coverage of GQDs on the surface of TiO 2 NTs. The optical transmittance and absorbance of GQDs were analysed using UV-Vis dual-beam spectrophotometer (UV-1280). The photoluminescence spectroscopy (PL) of GQDs is carried out by Agilent G9800A. UV-Vis diffused reectance spectroscopy (DRS) was performed to conrm the absorbing performance of GQDs by Avantes-Avaspec-2048 device. HITACHI 8WF8T5, 365 nm was used as the UV light source. 360 nanometre wavelength light emitting diodes were used as the switching UV source. All the photocurrent measurements and EIS spectroscopy were done by an Auto Lab electrochemical workstation (AUTO LAB PGSTAT302N) and Keithley Ampere meter 6487. The yellow aqueous GQDs solution, which is the nal product of previously described hydrothermal process, was analysed with TEM to determine the shape and size of the GQDs. As it is shown in Fig. 1a the GQDs are spherical particles with sizes less than 20 nm. The XRD pattern of the aqueous GQDs solution is demonstrated in ESI, Fig. S1 . † A broad diffraction peak at around 2q ¼ 25 is obvious which is corresponding to (002) crystal phase of graphite. Another broad peak at about 2q ¼ 9 which is attributed to the (001) plane of graphitic nitride carbon can be seen in Fig. S1 †. 32, 33 The absorption ability of the GQDs in UV region was examined with optical absorbance spectra. Fig. 1b illustrates a broad absorption band in the UV region with a peak at about 320 nm for the GQDs. The broad and intense spectral absorption of the GQDs in the UV region conrms that the GQDs can serve as UV absorbing material in the UV photodetector. The PL spectra of the GQDs is exhibited in Fig. S2 . † The PL property of the GQDs guarantees the electron transfer to the neighboring TiO 2 NTs rather than thermal relaxation. To determine the functional groups on the surface of the GQDs, FTIR spectroscopy was utilized and the obtained spectrum is shown in Fig. 1c Fig. 2a typically shows the cross sectional FESEM image of the TiO 2 NTs prepared by anodization process at 60 V for 45 min. It is clear that highly ordered, closely and rmly packed tubes were obtained which create defect free paths for electrons. Fig. 2b shows the top-view of the NTs indicating a smooth top surface with average tube diameter of 100-130 nm and of course a great sublayer for the attachment of the GQDs. The SEM images of the TiO 2 NTs in different lengths and full information about the anodization parameters are provided in Fig. S3 and Table S1 . † Additionally, XRD spectrum (Fig. S4 †) conrms the Fig. S4 † are all indexed to anatase phase of TiO 2 (JCPDS card #41-2127). 35 Coating the TiO 2 NTs with the GQDs was performed by the immersion of the TiO 2 NTs photoanode in the GQDs solution for a specic time. Fig. 2c shows the structural morphology of the TiO 2 NTs coated with the GQDs. The presence of the GQDs on the surface of the TiO 2 NTs is obvious and there is no change in the structural morphology of the TiO 2 NTs aer the GQDs coating. The energy-dispersive Xray spectroscopy (EDS mapping) was used for elemental characterization of the GQDs coated TiO 2 NTs. The EDS mapping picture of C element (Fig. 2d) proves complete loading and uniform coverage of the TiO 2 NTs surface with the GQDs. The inset of Fig. 2d shows the EDS mapping picture of C element on the pure TiO 2 NTs. The C element which is present on the surface of the uncoated TiO 2 NTs is from the environmental pollution and its concentration on the TiO 2 NTs surface is signicantly low compared to the C element concentration of the TiO 2 NTs surface aer the GQDs coating. The Raman spectra of the pure TiO 2 NTs and the GQDs coated TiO 2 NTs are compared in Fig. 3a . According to the symmetry group analysis, a few clear characteristic peaks can be seen centered at 144 cm À1 , 369 cm À1 , 515 cm À1 and 637 cm À1 which are denoted to the active modes of the pure anatase TiO 2 . Yet, two more peaks shown in Fig. 3a inset, centred at 1386 cm À1 and 1537 cm À1 in the spectra of the GQDs coated TiO 2 NTs, are related to the active Raman modes of the GQDs and again a verication of the GQDs coverage on the NTs sample. 36 Despite the fact that the TiO 2 NTs serve as an efficient UV light absorber, here the decorating GQDs on the NTs surface are also accountable material which absorb UV photons. The relative position of the energy levels for the different parts of the photodetector is demonstrated in Fig. 3b . When the device is exposed to UV radiation, the UV photons will be absorbed by both TiO 2 NTs and the GQDs and excite the electrons to the corresponding CBs. According to Fig. 3b , the existed electrons in the CB of GQDs will be injected into the CB of the TiO 2 NTs due to the lower energy band of the NTs compared to the GQDs. The injected electrons along with the photogenerated electrons in the TiO 2 NTs, contribute to the current ow by traveling through the NTs and the external circuit, until they reach the counter electrode. Transferring of electrons from the counter electrode to the electrolyte and the regeneration of the GQDs happens through electrolyte oxidation and reduction activities. For the purpose of achieving the best photo current and photo responsivity together with fast response, optimization of the TiO 2 NTs height and also the GQDs loading time on the NTs surface has been done. In the very rst step, a few numbers of the PEC UV photodetectors with bare TiO 2 NTs as photoanode and also different tube height from 3 to 20 nm were assembled and their detecting performance under UV illumination of 365 nm and 2 mW cm À2 power intensity was examined. The SEM image of different TiO 2 NTs are exhibited in Fig. S3 . † It is clear that the TiO 2 NTs are ordered well on the Ti foil through the anodization process and the NTs length has been increased by increasing the anodization time. According to Fig. S5 and Table S2 , † the maximum photo responsivity of 13.5 mA W À1 achieved by application of approximately 15 mm long TiO 2 NTs in photoanode of the PEC UV photodetector. As it is shown in Table S2 , † gradual increase in tube length resulted in an increase in the photocurrent density and thereby the photo responsivity. Excessive increase in tube length longer than 15 mm will cause a decrease in the photocurrent. This can be attributed to the longer electron path length which increases the chance of electron-hole recombination before the injection of electrons to the FTO. In order to guring out the appropriate time for the GQDs loading on the NTs surface, several numbers of photoanode with 7.5 and 15 mm long TiO 2 NTs were synthesized and immersed in the GQDs solution. A variety of PEC UV photodetectors were assembled using GQDs coated photoanodes with different immersion time intervals. Their detecting performance were analysed under UV light (365 nm, 2 mW cm À2 ). As demonstrated in Fig. S6 and Table S3 , † the optimum time for the GQDs loading on 7.5 mm long NTs is 9 days. As a matter of fact, longer loading time of the GQDs on the NTs surface will bring about the higher amounts of GQDs adsorbed on the NTs surface which resulted in an increment of the UV photons absorption and thereby higher photocurrent generation in the device. Extending immersion time more than 9 days results in a decrease in the photocurrent and deteriorates the detecting performance. The decrease in the photocurrent is due to the excessive accumulation of the GQDs on the NTs surface. In this condition, electrons are more likely to be trapped in the thick layer of the GQDs and also the chance of recombination is greater. We did the same experiments with 15 mm long NTs, up to 20 days, in order to nd the optimum immersion time for the GQDs loading. The results (Fig. S7 †) show that long NTs need a very long time for the GQDs coating. But we did not perform the experiments for longer times as we believe such long loading time is not practical from industrial point of view. Fig. 4a , b and Table 1 show the photocurrent of TNT-PD and GQD-TNT-PD devices, in both dark and under illumination condition (365 nm, 2 mW cm À2 ). As it is shown in Table 1 , the TNT-PD or GQD-TNT-PD devices with 15 mm long NTs have higher photocurrent compared to their counterparts made with 7.5 mm long NTs. Longer NTs provide higher surface area for the UV light absorption or the GQDs adsorption compared to the shorter ones, which results in higher responsivity in both TNT-PD and GQD-TNT-PD devices. Before coating the TiO 2 NTs with the GQDs, the photo responsivity of the 15 mm TNT-PD device is around 111% higher than the photo responsivity of the 7.5 mm TNT-PD device. With the application of the dual functional blocking layer, the photocurrent density in the photodetectors made with 7.5 and 15 mm long NTs increased by 473% and 348% respectively. Therefore, the difference between the photo responsivity of devices made with 7.5 and 15 mm long NTs decreases to 56% aer application of the GQDs coating. The increase in the photocurrent aer the application of the GQDs can be attributed to the higher light harvesting in both devices. When using GQDs, both TiO 2 NTs and the GQDs contribute in the light absorption. Therefore, the electron-hole generation is higher when using the GQDs in the device. We compared the diffuse reection spectra (DRS) of two photoanodes, with and without the GQDs. The spectra shown in Fig. S8 , † indicate that no more light scattering happens when using the GQDs coating on the TiO 2 NTs. Thus, light trapping cannot be the cause for the increased photocurrent of devices with GQD. Moreover, by application of the GQDs coating, the photo sensitivity of the PEC UV photodetectors increased by 345.7% and 171.2% when using 7.5 and 15 mm TiO 2 NTs in the device, respectively. Although a higher amount of photocurrent has been achieved by application of 15 mm NTs in the photoanode, the percentage of photo sensitivity increment is relatively low. This can be ascribed to the higher dark current in the PEC UV photodetector made by the 15 mm NTs. In the anodization process for the preparation of longer TiO 2 NTs, the upper parts of the tubes remain in the uoride-containing electrolyte for longer times. Therefore, chances of chemical etching and formation of holes and defects on the surface of NTs increases. 27 Thus, the PEC UV photodetector made by the 15 mm NTs have higher dark currents and thereby lower sensitivity. In order to obtain a deep insight into time response, stability and performance repeatability of the PEC UV photodetectors, photo response switching behaviour has been measured under illumination of on/off switching UV LEDs (360 nm, 5 mW cm À2 , 6.17 mW cm À2 and 7.12 mW cm À2 ) and 0 V bias for the photodetectors made with 7.5 mm TiO 2 NTs. The on/off switching time intervals are 15 seconds. As it is demonstrated in Fig. 5a , the photocurrent of the PEC UV photodetector made by 7.5 mm TiO 2 NTs grows to a steady value under UV illumination. Aer switching off the UV LEDs, the photocurrent returns to the initial state in a very short time. The 4 repeated cycles indicate the reproducible characteristics of the device. In addition, the photocurrent rises as the incident photon ux increases. It is noteworthy that the increment of photocurrent is an outcome of the improved electron-hole pair generation due to an increase in incident photon ux. A similar behaviour is seen in the photo response switching plots of the GQD-TNT-PD made with 15 mm TiO 2 NTs. The plots are shown in Fig. S9 . † The photocurrent of the GQD-TNT-PD device was measured under different low intensity UV light. As it is shown in Fig. 5b , there is an almost linear relation between the photocurrent and the incident UV photons power intensity. This behaviour conrms that this device is applicable for detection of low intensity UV light in the self-powered mode which is an essential behaviour in many applications. For instance, as a practical method for detecting virus and bacteria, the low intensity ultraviolet emission from the biological substances need to be detected. 37, 38 More information about the switching performance of the other assembled PEC UV photodetectors is available in the ESI, Fig. S9 . † Generally, the response speed of the device is an important factor in photodetectors. Fig. 5c Aiming for a deep understanding of electron transfer between interfaces, EIS was performed on the TNT-PD and the GQD-TNT-PD devices and the Nyquist plots are shown in Fig. 6a . It is quite accepted that the semicircle in the region of mid-frequencies in the Nyquist plot is affiliated with the impedance which is attributed to the charge recombination at electrolyte/photoanode interface. 24 The impedance spectrum of the equivalent electrical circuit illustrated in Fig. 6b has been tted to the Nyquist plots associated to the TNT-PD and the GQD-TNT-PD devices. The components in electrical circuit are standing for the charge transfer resistance and the capacitance of different interfaces existed in the device. For instance, R rc and CPE rc are related to the charge transfer resistance and the capacitance at the photoanode/electrolyte interface. A bigger semicircle diameter means bigger R rc which suppress interfacial electron recombination at the mentioned interface. The obtained values for the components of the electrical circuit are reported in Table S4 . † Application of the dual functional GQDs blocking layer brings about a signicant increase of 289% in R rc in the photodetector made by 7.5 mm TiO 2 NTs. It is concluded that the dual functional GQDs blocking layer suppresses the charge recombination at the photoanode/electrolyte interface efficiently. The EIS Nyquist plots for the PEC UV photodetectors made with 15 mm TiO 2 NTs are available in Fig. S10 . † Comparing the amount of R rc for the TNT-PD devices made with 7.5 and 15 mm TiO 2 NTs, one can see that the amount of R rc is lower for the TNT-PD device made with 15 mm TiO 2 NTs, which implies the higher charge recombination in this device compared to its counterpart made by 7.5 mm TiO 2 NTs. This behaviour explains the higher dark current and lower sensitivity of devices made by the 15 mm TiO 2 NTs compared to the devices made by 7.5 mm TiO 2 NTs. Therefore, the strategy of utilizing the GQDs coating as a dual functional layer, which can both increase the light harvesting efficiency and decrease the recombination in the device, would be considered as an efficient, practical and low-cost strategy for improving the performance of the self-powered PEC UV photodetectors. We presented the application of a GQDs inside a PEC UV photodetector based on TiO 2 NTs as a dual functional layer. The GQDs prepared by hydrothermal method and adsorbed on the surface of the TiO 2 NTs through the carbonyl, carboxyl and hydroxyl (Fig. 1c) groups present on their surfaces as it is shown in Fig. 2c . The GQDs improved the responsivity and sensitivity of the self-powered PEC UV photodetector by improving the UV light absorption and suppressing the charge carrier's recombination in the photodetector. An increment of 473% in photoresponsivity has been achieved by application of GQDs in the PEC UV photodetector. It is noteworthy that the device is able to detect low intensity UV radiation (2 mW cm À2 ) meanwhile operating without any bias (0 V). A high value of photoresponsivity about 42.5 mA W À1 has been achieved for the PEC UV photodetector, by using 15 mm TiO 2 NTs in photoanode and application of the GQDs dual-functional layer, which is significantly improved in comparison with other similar reported works reviewed in ESI, Table S5 . † A. Z. contributed to methodology, validation, investigation, writing original dra, visualization. S. B. contributed to methodology and investigation. M. M. contributed to writing, review and editing, supervision, funding acquisition. Z. H. contributed to conceptualization, methodology, validation, writing, review and editing, visualization, supervision, project administration, funding acquisition. There are no conicts to declare. for Smart Irradiation Monitoring Application Ultraviolet laser surface treatment for biomedical applications of b titanium alloys: Morphological and structural characterization CO 2 splitting by H 2 O to CO and O 2 under UV light in TiMCM-41 silicate sieve A Real-Time Wearable UV-Radiation Monitor based on a High-Performance p-CuZnS/n-TiO 2 Photodetector TiO 2 Nanorod Arrays Based Self-Powered UV Photodetector: Heterojunction with NiO Nanoakes and Enhanced UV Photoresponse Novel Transparent and Self-Powered UV Photodetector Based on Crossed ZnO Nanober Array Homojunction Photoelectrochemical Cells, Electrochem. Aspects Ionic Liq Photoluminescence and photoelectrochemical properties of nanocrystalline ZnO thin lms synthesized by spray pyrolysis technique Highperformance photoelectrochemical-type self-powered UV photodetector using epitaxial TiO 2 /SnO 2 branched heterojunction nanostructure Improved sensitivity in self-powered photoelectrochemical UV photodetector by application of graphene quantum dots Metal-semiconductor-metal TiO 2 ultraviolet detectors with Ni electrodes TiO 2 based metal-semiconductor-metal ultraviolet photodetectors Synthesis of mesoporous core-shell CdS@TiO 2 (0D and 1D) photocatalysts for solardriven hydrogen fuel production N-Doping of anodic TiO 2 nanotubes using heat treatment in ammonia Doped-TiO 2 : A Review A review on highly ordered, vertically oriented TiO 2 nanotube arrays: Fabrication, material properties, and solar energy applications Highly sensitive fastresponse UV photodetectors based on epitaxial TiO 2 lms An Interface Engineered Multicolor Photodetector Based on n-Si(111)/ TiO 2 Nanorod Array Heterojunction Electron mobility and injection dynamics in mesoporous ZnO, SnO 2 , and TiO 2 lms used in dyesensitized solar cells TiO 2 nanotubes: Synthesis and applications Smooth anodic TiO 2 nanotubes Ultraviolet photodetectors based on anodic TiO 2 nanotube arrays A selfpowered ultraviolet photodetector based on TiO 2 /Ag/ZnS nanotubes with high stability and fast response A High-Performance Self-Powered Uv Photodetector Based On Self-Doping Tio 2 Nanotube Arrays TiO 2 -graphene composite as an application of photoelectrochemical photodetectors with enhanced performances Self-organized TiO 2 nanotube arrays: Critical effects on morphology and growth Solution-processed graphene quantum dot deep-UV photodetectors Deep ultraviolet to near-infrared emission and photoresponse in layered n-doped graphene quantum dots Facile fabrication of NiTiO 3 / graphene nanocomposites for photocatalytic hydrogen generation Improvement of the current generation in silicon solar cells by utilizing graphene quantum dot as spectral converter A new uorescence probe comprising nitrogen-doped graphene quantum dots for the selective and quantitative determination of cerium(iv) Graphene quantum dot modied glassy carbon electrode for the determination of doxorubicin hydrochloride in human plasma A titanium dioxide/ nitrogen-doped graphene quantum dot nanocomposite to mitigate cytotoxicity: synthesis, characterisation, and cell viability evaluation The size and valence state effect of Pt on photocatalytic H2 evolution over platinized TiO 2 photocatalyst Facile one-step hydrothermal synthesis toward strongly coupled TiO 2 / graphene quantum dots photocatalysts for efficient hydrogen evolution Technology and equipment development in laser-induced uorescence-based remote and eld detection of biological aerosols Detection of Middle East respiratory syndrome coronavirus using reverse transcription loopmediated isothermal amplication (RT-LAMP)