key: cord-0027658-o4fuw693 authors: Smirnova, Olga M.; Menendez Pidal, Ignacio; Alekseev, Aleksandr V.; Petrov, Dmitry N.; Popov, Mikhail G. title: Strain Hardening of Polypropylene Microfiber Reinforced Composite Based on Alkali-Activated Slag Matrix date: 2022-02-21 journal: Materials (Basel) DOI: 10.3390/ma15041607 sha: 6e3dd544b25ba26178d861d6e2027c42f88da707 doc_id: 27658 cord_uid: o4fuw693 A comparative study of the fracture features, strength and deformation properties of pseudo strain-hardening composites based on alkali-activated slag and Portland cement matrices with polypropylene microfiber was carried out. Correlations between their compositions and characteristics of stress–strain diagrams under tension in bending with an additional determination of acoustic emission parameters were determined. An average strength alkali-activated slag matrix with compressive strength of 40 MPa and a high-strength Portland cement matrix with compressive strength of 70 MPa were used. The matrix compositions were selected for high filling the composites with polypropylene microfiber in the amount of 5%-vol. and 3.5%-vol. ensuring the workability at the low water-to-binder ratios of 0.22 and 0.3 for Portland cement and alkali-activated slag matrices, respectively. Deformation diagrams were obtained for all studied compositions. Peaks in the number of acoustic signals in alkali-activated slag composites were observed only in the strain-softening zone. Graphs of dependence of the rate of acoustic events occurrence in samples from the start of the test experimentally prove that this method of non-destructive testing can be used to monitor structures based on strain-hardening composites. Recently attention is paid to the development of new compositions of cement matrices and the use of modified multicomponent fibers in strain-hardening cement composites subjected to static and dynamic loads [1] [2] [3] [4] since construction practice shows a high demand for mineral composites with special deformation characteristics [5] [6] [7] [8] . The important advantages of such composites are the significant increase (up to 40% or more) of the value of tensile stresses corresponding to the sample destruction compared with the value of tensile stresses corresponding to the first microcrack and sufficiently large relative deformations of cement composite under uniaxial tension (up to values of several percent) due to a significant increase of the volume of microcracking before destruction [9] [10] [11] . A high relative deformation of up to 5% is the result of the sequential formation of multiple, densely spaced microcracks under increasing uniaxial tensile loading [12] . This behavior of the material under tension is achieved by fulfilling a number of micromechanical conditions for the formation of microcracks, their propagation and overlap with fibers [13] [14] [15] . This cement composite can be used not only as the main material in structures but also as thin reinforcing layers for repairing and strengthening the existing The microfiber manufacturers can add fillers and other modifying additives that lead to a change of properties of PP microfiber. PP microfibers properties of the above-cited papers are presented in Table 1 . A method is needed to assess the strength and deformation properties of the material in the structure under operating conditions [43] [44] [45] . The analysis of deformation curves and acoustic emission parameters can be used to evaluate the destruction of composites. Acoustic emission (AE) testing is a technique to detect the formation and growth of cracks both on the surface and inside the material. Crack formation and propagation in brittle materials are combined with a local rapid release of stored strain energy. The resulting elastic waves propagate through the material and can be detected by piezoelectric sensors on the surface. The characteristics of the elastic waves and hence the electric signals from the sensors depend on the crack type and the acoustic properties of the material [46] . Analysis of the signal parameters (e.g., amplitude and average frequency) makes it possible to classify the cracks, e.g., as described in papers [47] [48] [49] . In combination with the stressstrain curves one can draw conclusions about the destruction mechanism of SHCCs [46, 50] . The aim of the paper is to study the strain-hardening behavior under tension in bending of composites based on inorganic binders with polypropylene microfiber with the additional determination of acoustic emission parameters. Ordinary Portland cement (CEM I 42.5) was used for the study. The microfillers were obtained by grinding quartz sand and marking it as A1.5 (D 50 = 1.5 µm) and A4 (D 50 = 4 µm). The ground quartz sands with different fineness were marked as A1.5; A4; A15. The properties of polypropylene (PP) microfiber are presented in Table 2 . Mix proportions are presented in Tables 3 and 4 . The compositions based on Portland cement differed in the microfiber amount. The compositions based on alkali-activated slag binder differed in the water-to-binder ratio. The workability of the fresh mixture decreases with an increase in the microfiber quantity. Summarizing the experience of other scientists and own experience it is advisable to develop new compositions of strain-hardening of inorganic composite according to the scheme in Figure 1 . Development of new strain-hardening inorganic composite can be in mixture composition and in manufacturing technology. In study of mixture compositions the following results were obtained: the use of microfiber in the amount of 2% by volume or more [51] [52] [53] [54] [55] ; the use of rheologically active mineral additives in cement matrices with a superplasticizer to ensure workability at low W/C ratio and at high microfiber amount [56, 57] ; the use of mineral additives that improve workability and setting time in alkali-activated slag matrices [58] [59] [60] [61] ; the use of quartz sand with a low fineness modulus as a fine aggregate to obtain a homogeneous matrix and ensure a dense and uniform contact of matrix with the microfiber surface [62] [63] [64] [65] [66] [67] [68] . Manufacturing technology takes into account: the sequence of addition of components into a mixture [69] [70] [71] [72] [73] ; mixing modes [62, [74] [75] [76] [77] . It is shown in papers [1] [2] [3] 62] that it is necessary to increase the matrix density to achieve strain-hardening in composites with hydrophobic microfiber. An increase in density can be achieved by reducing the water-to-cement ratio using a superplasticizer and rheologically active mineral additives. High filling with microfiber can be achieved by justifying the choice of the type of concrete mixer [68] [69] [70] [71] , the sequence of addition of components [72] [73] [74] , and the speed and duration of mixing [62, [75] [76] [77] . A laboratory automatic mixer for mortars from Tinius Olsen was used to prepare the mixtures ( Figure 2 ). It has three mixing modes with different speeds. At first, the fresh mixture was made without fiber. In both cases at preparing the cement matrix or the slag-alkali matrix, the fresh mixtures were obtained with high fluidity despite the low values of the water-to-cement ratio. This was achieved by taking into account the recommendations from Figure 1 . Then the PP microfiber was added and the mixer was started at the second speed for 180 s. Composition of matrices with maximum microfiber quantity (5.5 and 3.5%) was selected taking into account the mixture workability. The spread diameter of mixtures on the shaking table was 160 mm after 15 shakes. volume or more [51] [52] [53] [54] [55] ; the use of rheologically active mineral additives in cement matrices with a superplasticizer to ensure workability at low W/C ratio and at high microfiber amount [56, 57] ; the use of mineral additives that improve workability and setting time in alkali-activated slag matrices [58] [59] [60] [61] ; the use of quartz sand with a low fineness modulus as a fine aggregate to obtain a homogeneous matrix and ensure a dense and uniform contact of matrix with the microfiber surface [62] [63] [64] [65] [66] [67] [68] . Manufacturing technology takes into account: the sequence of addition of components into a mixture [69] [70] [71] [72] [73] ; mixing modes [62, [74] [75] [76] [77] . It is shown in papers [1] [2] [3] 62] that it is necessary to increase the matrix density to achieve strain-hardening in composites with hydrophobic microfiber. An increase in density can be achieved by reducing the water-to-cement ratio using a superplasticizer and rheologically active mineral additives. High filling with microfiber can be achieved by justifying the choice of the type of concrete mixer [68] [69] [70] [71] , the sequence of addition of components [72] [73] [74] , and the speed and duration of mixing [62, [75] [76] [77] . A laboratory automatic mixer for mortars from Tinius Olsen was used to prepare the mixtures ( Figure 2 ). It has three mixing modes with different speeds. volume or more [51] [52] [53] [54] [55] ; the use of rheologically active mineral additives in cement matrices with a superplasticizer to ensure workability at low W/C ratio and at high microfiber amount [56, 57] ; the use of mineral additives that improve workability and setting time in alkali-activated slag matrices [58] [59] [60] [61] ; the use of quartz sand with a low fineness modulus as a fine aggregate to obtain a homogeneous matrix and ensure a dense and uniform contact of matrix with the microfiber surface [62] [63] [64] [65] [66] [67] [68] . Manufacturing technology takes into account: the sequence of addition of components into a mixture [69] [70] [71] [72] [73] ; mixing modes [62, [74] [75] [76] [77] . It is shown in papers [1] [2] [3] 62] that it is necessary to increase the matrix density to achieve strain-hardening in composites with hydrophobic microfiber. An increase in density can be achieved by reducing the water-to-cement ratio using a superplasticizer and rheologically active mineral additives. High filling with microfiber can be achieved by justifying the choice of the type of concrete mixer [68] [69] [70] [71] , the sequence of addition of components [72] [73] [74] , and the speed and duration of mixing [62, [75] [76] [77] . A laboratory automatic mixer for mortars from Tinius Olsen was used to prepare the mixtures ( Figure 2 ). It has three mixing modes with different speeds. A cement mixture with 2.5% vol. of PP microfiber is shown in Figure 3 . This cement mixture was very fluid and made it possible to increase the microfiber amount up to 5.5% by volume. At first, the fresh mixture was made without fiber. In both cases at preparing the cement matrix or the slag-alkali matrix, the fresh mixtures were obtained with high fluidity despite the low values of the water-to-cement ratio. This was achieved by taking into account the recommendations from Figure 1 . Then the PP microfiber was added and the mixer was started at the second speed for 180 s. Composition of matrices with maximum microfiber quantity (5.5 and 3.5%) was selected taking into account the mixture workability. The spread diameter of mixtures on the shaking table was 160 mm after 15 shakes. A cement mixture with 2.5% vol. of PP microfiber is shown in Figure 3 . This cement mixture was very fluid and made it possible to increase the microfiber amount up to 5.5% by volume. Figure 3 . Workability of cement mixture with 2.5% vol. of PP microfiber. The study to determine the mechanical properties was carried out using the MTS 816 servo-hydraulic system that tests samples at compression and three-point bending ( Figure 4 ). Three specimens were tested for each bath at the age of 28 days. The cube samples had a side of 7.07 cm; the beam samples had dimensions of 4 × 4 × 16 cm. The study to determine the mechanical properties was carried out using the MTS 816 servo-hydraulic system that tests samples at compression and three-point bending ( Figure 4 ). Three specimens were tested for each bath at the age of 28 days. The cube samples had a side of 7.07 cm; the beam samples had dimensions of 4 × 4 × 16 cm. At first, the fresh mixture was made without fiber. In both cases at preparing the cement matrix or the slag-alkali matrix, the fresh mixtures were obtained with high fluidity despite the low values of the water-to-cement ratio. This was achieved by taking into account the recommendations from Figure 1 . Then the PP microfiber was added and the mixer was started at the second speed for 180 s. Composition of matrices with maximum microfiber quantity (5.5 and 3.5%) was selected taking into account the mixture workability. The spread diameter of mixtures on the shaking table was 160 mm after 15 shakes. A cement mixture with 2.5% vol. of PP microfiber is shown in Figure 3 . This cement mixture was very fluid and made it possible to increase the microfiber amount up to 5.5% by volume. Figure 3 . Workability of cement mixture with 2.5% vol. of PP microfiber. The study to determine the mechanical properties was carried out using the MTS 816 servo-hydraulic system that tests samples at compression and three-point bending ( Figure 4 ). Three specimens were tested for each bath at the age of 28 days. The cube samples had a side of 7.07 cm; the beam samples had dimensions of 4 × 4 × 16 cm. The calculation of the specific fracture work was performed as the ratio of the area under the deformation curve to sample volume. Strain-hardening after the formation of the first microcrack was defined as the difference between the strength corresponding to the sample destruction and the strength corresponding to the first microcrack. A set of equipment was used to study the acoustic emission (AE) of samples consisting of the following main parts: MTS 816 servo-hydraulic system; ErgoTech acoustic emission control system; data collection and processing system, and specialized ASC software. The ErgoTech acoustic rock emission system makes it possible to study the processes of micro-and macro-cracking in rocks under complex loading conditions using acoustic emission sensors. The ErgoTech acoustic emission control system includes a measuring unit with sensors; an acoustic signal preamplifier ( Figure 5 ) for signal amplification and transmission to the information acquisition system; a unit for generating, collecting and processing acoustic signals. emission sensors. The ErgoTech acoustic emission control system includes a m unit with sensors; an acoustic signal preamplifier ( Figure 5 ) for signal amplifica transmission to the information acquisition system; a unit for generating, collec processing acoustic signals. The data collection and processing system, as well as the specialized softwar company, are designed for automated control of the process of data registration fr sors in the mode of constant and trigger control, waveform configuration, digit processing and filtering, localization and visualization of the received data in g and digital form. The data collection and processing system is made in the fo server. The type of sensor was a piezoelectric inducer with a 1.3 MHz resonant fr (Ergotech manufacturer). Preamplifier type was ASC Pulser Amplifier (PAD-006 and upper thresholds were 100 kHz and 2 MHz, accordingly. Calibration of sen performed by the Ergotech manufacturer. Calibration by the Nelson method (fra the lead) was performed before the tests. The mechanical properties of four types of composites are summarized in including the compressive strength and the tensile strength in bending at the a days. The data collection and processing system, as well as the specialized software of ASC company, are designed for automated control of the process of data registration from sensors in the mode of constant and trigger control, waveform configuration, digital signal processing and filtering, localization and visualization of the received data in graphical and digital form. The data collection and processing system is made in the form of a server. The type of sensor was a piezoelectric inducer with a 1.3 MHz resonant frequency (Ergotech manufacturer). Preamplifier type was ASC Pulser Amplifier (PAD-006). Lower and upper thresholds were 100 kHz and 2 MHz, accordingly. Calibration of sensors was performed by the Ergotech manufacturer. Calibration by the Nelson method (fracture of the lead) was performed before the tests. The mechanical properties of four types of composites are summarized in Table 5 including the compressive strength and the tensile strength in bending at the age of 28 days. The results of Table 5 show that the increase of PP microfiber amount from 4.4% to 5.5% by volume in cement composites led to a decrease in bending strength. This contradicts the well-known pattern that the bending strength increases with increasing the microfiber quantity. However, this pattern has been stated for microfiber quantity in the range from 0 to 2.5% by volume [15, 64] . If polypropylene microfiber is used in larger quantities (5.5% by volume) the interface area between microfiber and matrix increases and, possibly, the strength of the contact zone between microfiber and cement matrix begins to prevail. The surface of PP microfiber is hydrophobic so there is no chemical interaction between the surface of this fiber and the cement matrix. In this case, the strength of the contact zone between the PP microfiber and cement matrix is due to friction forces. Hence, the strength of the contact zone between the microfiber and cement matrix, with the increase of PP microfiber amount, affects the bending strength corresponding to the first microcrack in the matrix, namely, reducing it. Accordingly, the bending strength of the 6 Mix with 5.5% fiber is lower than the bending strength of the 2 Mix with 4.4% fiber as shown in Figures 6 and 7 . The strain-hardening zone appears on the curves of both mixes. However, this zone in samples of the 6 Mix is of interest because the bending strength corresponding to the sample destruction exceeds the bending strength corresponding to the first microcrack. The results of Table 5 show that the increase of PP microfiber amount from 4.4% to 5.5% by volume in cement composites led to a decrease in bending strength. This contradicts the well-known pattern that the bending strength increases with increasing the microfiber quantity. However, this pattern has been stated for microfiber quantity in the range from 0 to 2.5% by volume [15, 64] . If polypropylene microfiber is used in larger quantities (5.5% by volume) the interface area between microfiber and matrix increases and, possibly, the strength of the contact zone between microfiber and cement matrix begins to prevail. The surface of PP microfiber is hydrophobic so there is no chemical interaction between the surface of this fiber and the cement matrix. In this case, the strength of the contact zone between the PP microfiber and cement matrix is due to friction forces. Hence, the strength of the contact zone between the microfiber and cement matrix, with the increase of PP microfiber amount, affects the bending strength corresponding to the first microcrack in the matrix, namely, reducing it. Accordingly, the bending strength of the 6 Mix with 5.5% fiber is lower than the bending strength of the 2 Mix with 4.4% fiber as shown in Figures 6 and 7 . The strain-hardening zone appears on the curves of both mixes. However, this zone in samples of the 6 Mix is of interest because the bending strength corresponding to the sample destruction exceeds the bending strength corresponding to the first microcrack. The results show a contradictory pattern in the case of composites with alkali-activated slag matrix (compositions 3 and 4) . The bending strength decreases with the decrease of the water-to-binder ratio at a constant microfiber amount according to Table 5 and Figures 8 and 9 . However, the strain-hardening zone appears in composition 4 with The results show a contradictory pattern in the case of composites with alkali-activated slag matrix (compositions 3 and 4) . The bending strength decreases with the decrease of the water-to-binder ratio at a constant microfiber amount according to Table 5 and Figures 8 and 9 . However, the strain-hardening zone appears in composition 4 with W/B = 0.22, which is more pronounced compared to the zone on the deformation curve of composition 3 with W/B = 0.3, namely, the bending strength corresponding to sample destruction exceeds the bending strength corresponding to the first microcrack. Thus, strain-hardening behavior in which the strength value corresponding to sample destruction exceeds the strength value corresponding to the first crack appears in the studied alkali-activated slag matrix of medium strength with the decrease of the water-to-binder ratio up to 0.22. crease of the water-to-binder ratio at a constant microfiber amount according to Table 5 and Figures 8 and 9 . However, the strain-hardening zone appears in composition 4 with W/B = 0.22, which is more pronounced compared to the zone on the deformation curve of composition 3 with W/B = 0.3, namely, the bending strength corresponding to sample destruction exceeds the bending strength corresponding to the first microcrack. Thus, strainhardening behavior in which the strength value corresponding to sample destruction exceeds the strength value corresponding to the first crack appears in the studied alkaliactivated slag matrix of medium strength with the decrease of the water-to-binder ratio up to 0.22. Thus, the effect of the PP microfiber amount and the water-to-binder ratio is studied in this paper. Analysis of sample destruction showed that the characteristics of deformation curves significantly depend on the compositions. In general, the low-strain hardening composites and the high-strain hardening composites can be distinguished depending on the nature of deformation [78] . When operating construction structures made on the basis of strain-hardening composites reliable methods of monitoring changes in mechanical and deformation properties are needed, for example, the acoustic emission method. Flow characteristics, such as the number of signals and activity are used to describe the patterns of AE behavior during sample loading [79, 80] . The signal number of AE is registered for a certain time interval that counts from the beginning of observation. The activity is a derivative of the number of signals in time. Activity shows an increase in the number of AE signals registered per unit of time. The linkage of the flow characteristics of acoustic emission with the loading process has been studied and is shown in Figures 10 and 11 for a sample of cement-based composite with 4.4% vol. of PP microfiber and for a sample of slag-alkali-based composite with Thus, the effect of the PP microfiber amount and the water-to-binder ratio is studied in this paper. Analysis of sample destruction showed that the characteristics of deformation curves significantly depend on the compositions. In general, the low-strain hardening composites and the high-strain hardening composites can be distinguished depending on the nature of deformation [78] . When operating construction structures made on the basis of strain-hardening composites reliable methods of monitoring changes in mechanical and deformation properties are needed, for example, the acoustic emission method. Flow characteristics, such as the number of signals and activity are used to describe the patterns of AE behavior during sample loading [79, 80] . The signal number of AE is registered for a certain time interval that counts from the beginning of observation. The activity is a derivative of the number of signals in time. Activity shows an increase in the number of AE signals registered per unit of time. The linkage of the flow characteristics of acoustic emission with the loading process has been studied and is shown in Figures 10 and 11 for a sample of cement-based composite with 4.4% vol. of PP microfiber and for a sample of slag-alkali-based composite with 5.5% vol. of PP microfiber, respectively. The diagrams "load-strain on the traverse" are shown in Figures 10a and 11a . The load speed is shown in Figures 10b and 11b up to the deformation equal to 5 mm or up to the moment of sample destruction. The number of recorded acoustic signals per second in the time interval at which the load speed is indicated is shown in Figures 10c and 11c . The total number of acoustic signals from the start of the test is shown in Figures 10d and 11d . Each of the presented materials has deformation features. The strain-hardening zone is observed on the deformation diagram of cement composite with 5.5% vol. of PP microfiber. A sharp increase in the number of acoustic signals is observed at the beginning and end of the strain-hardening zone in Figure 11b ,c. A strain-hardening zone is almost absent in cement composite with 4.4% vol. of PP microfiber. Several splashes of acoustic signals are observed in this sample only in the strain-softening zone. Stable relationships between mechanical and AE parameters are observed in the above dependencies despite significant differences in the mechanical characteristics of the studied cement-based composites. The relationship of flow characteristics of the acoustic emission with the loading curve has been studied and is shown in Figures 12 and 13 for alkali-activated slag based composites with 3.5% vol. of PP microfiber and with different W/C ratios. The diagrams "load-strain on the traverse" are shown in Figures 12a and 13a . The load speed is shown in Figures 12b and 13b up to the deformation equal to 5 mm or up to the moment of sample destruction. The number of recorded acoustic signals per second in the time interval at which the load speed is indicated is shown in Figures 12c and 13c . The total number of acoustic signals from the start of the test is shown in Figures 12d and 13d. 15, x FOR PEER REVIEW 10 of 23 Flow characteristics, such as the number of signals and activity are used to describe the patterns of AE behavior during sample loading [79, 80] . The signal number of AE is registered for a certain time interval that counts from the beginning of observation. The activity is a derivative of the number of signals in time. Activity shows an increase in the number of AE signals registered per unit of time. The linkage of the flow characteristics of acoustic emission with the loading process has been studied and is shown in Figures 10 and 11 for a sample of cement-based composite with 4.4% vol. of PP microfiber and for a sample of slag-alkali-based composite with 5.5% vol. of PP microfiber, respectively. The diagrams "load-strain on the traverse" are shown in Figures 10a and 11a . The load speed is shown in Figures 10b and 11b up to the deformation equal to 5 mm or up to the moment of sample destruction. The number of recorded acoustic signals per second in the time interval at which the load speed is indicated is shown in Figures 10c and 11c . The total number of acoustic signals from the start of the test is shown in Figures 10d and 11d . Each of the presented materials has deformation features. The strain-hardening zone is observed on the deformation diagram of cement composite with 5.5% vol. of PP microfiber. A sharp increase in the number of acoustic signals is observed at the beginning and end of the strain-hardening zone in Figure 11b ,c. A strain-hardening zone is almost absent in cement composite with 4.4% vol. of PP microfiber. Several splashes of acoustic signals are observed in this sample only in the strain-softening zone. Stable relationships between mechanical and AE parameters are observed in the above dependencies despite significant differences in the mechanical characteristics of the studied cement-based composites. The relationship of flow characteristics of the acoustic emission with the loading curve has been studied and is shown in Figures 12 and 13 for alkali-activated slag based composites with 3.5% vol. of PP microfiber and with different W/C ratios. The diagrams "load-strain on the traverse" are shown in Figures 12a and 13a . The load speed is shown in Figures 12b and 13b up to the deformation equal to 5 mm or up to the moment of sample destruction. The number of recorded acoustic signals per second in the time interval at which the load speed is indicated is shown in Figures 12c and 13c . The total number of acoustic signals from the start of the test is shown in Figures 12d and 13d . A smaller number of acoustic signals by 3-4 times is typical for samples on alkaliactivated slag binder. Peaks in the number of acoustic signals in these samples were observed only in the strain-softening zone. Graphs of dependence of the occurrence rate of acoustic signals (the first derivative) in the sample from the start of the test, obtained in the work, experimentally prove that this method of non-destructive testing can be used to monitor structures based on strainhardening composites operating in difficult conditions. These graphs make it possible to use the AE method to estimate the residual resource of the material during deformation. In further studies linking the AE parameters with microscopic fracture parameters, it is necessary to formulate a number of diagnostic AE indicators for monitoring and evaluating the resource of material. Each of the presented materials has deformation features. The strain-hardening zone is observed on the deformation diagram of cement composite with 5.5% vol. of PP microfiber. A sharp increase in the number of acoustic signals is observed at the beginning and end of the strain-hardening zone in Figure 11b ,c. A strain-hardening zone is almost absent in cement composite with 4.4% vol. of PP microfiber. Several splashes of acoustic signals are observed in this sample only in the strain-softening zone. Stable relationships between mechanical and AE parameters are observed in the above dependencies despite significant differences in the mechanical characteristics of the studied cement-based composites. The relationship of flow characteristics of the acoustic emission with the loading curve has been studied and is shown in Figures 12 and 13 for alkali-activated slag based composites with 3.5% vol. of PP microfiber and with different W/C ratios. The diagrams "load-strain on the traverse" are shown in Figures 12a and 13a . The load speed is shown in Figures 12b and 13b up to the deformation equal to 5 mm or up to the moment of sample destruction. The number of recorded acoustic signals per second in the time interval at which the load speed is indicated is shown in Figures 12c and 13c . The total number of acoustic signals from the start of the test is shown in Figures 12d and 13d . A smaller number of acoustic signals by 3-4 times is typical for samples on alkaliactivated slag binder. Peaks in the number of acoustic signals in these samples were observed only in the strain-softening zone. Graphs of dependence of the occurrence rate of acoustic signals (the first derivative) in the sample from the start of the test, obtained in the work, experimentally prove that this method of non-destructive testing can be used to monitor structures based on strainhardening composites operating in difficult conditions. These graphs make it possible to use the AE method to estimate the residual resource of the material during deformation. In further studies linking the AE parameters with microscopic fracture parameters, it is necessary to formulate a number of diagnostic AE indicators for monitoring and evaluating the resource of material. The characteristics of the studied materials obtained from deformation curves are presented in Table 6 . According to the study of beam samples in three-point bending with controlled deformations, it was found that the frequency of occurrence of acoustic events is associated with the deformation curve. The recorded acoustic signals can be combined into seven groups depending on the stage of sample deformation as shown in Figures 14 and 15 . These seven groups are outlined with red lines that limit the areas where the values of the number of acoustic signals per second are grouped. At the initial stage of loading, as the traverse displacement increases, the accumulation of stresses occurs in the stretched and The characteristics of the studied materials obtained from deformation curves are presented in Table 6 . According to the study of beam samples in three-point bending with controlled deformations, it was found that the frequency of occurrence of acoustic events is associated with the deformation curve. The recorded acoustic signals can be combined into seven groups depending on the stage of sample deformation as shown in Figures 14 and 15 . These seven groups are outlined with red lines that limit the areas where the values of the number of acoustic signals per second are grouped. At the initial stage of loading, as the traverse displacement increases, the accumulation of stresses occurs in the stretched and compressed zone of a beam-sample. The periodic appearance of signals is typical for this zone (1). Zones 1 and 2 have a very conditional separation and are determined by the nature of deformation of a beam-sample at the initial stage during compression and stretching deformations in a matrix. The duration of signal registration is determined by the fracture work and the elasticity modulus of the material. A drastic increase of acoustic events per second is observed in zone (3), while the size of this zone is associated with the potential for strain-hardening. The formation of microcracks begins and for this reason the dependence of "stress-strain" becomes nonlinear. The frequency of signals per unit of time in this zone indicates the trajectory of destruction: with an instantaneous burst of a series of signals the destruction occurs according to a fragile scenario, with a periodic, prolonged appearance of signals, the destruction occurs with the involvement of microfiber and the development of plastic deformations. The development of cracks acquires an unstable, avalanche-like character during the transition from zone 3 to zone 4. An increase of acoustic events per unit of time is observed in the deformation area from zone 4 to zone 6, which is probably due to more intensive crack development. Characteristically, this phenomenon is observed for beam-samples of all mixes with the same deflection in the range from 1.2 to 2.2 mm. Zone 7 is characterized by a more intense release of signals in a sample, which has a more fragile destruction trajectory. This can probably be explained by the interaction of matrix particles with each other, while a sample that has collapsed along a plastic trajectory involves microfibers more effectively. stretching deformations in a matrix. The duration of signal registration is determined by the fracture work and the elasticity modulus of the material. A drastic increase of acoustic events per second is observed in zone (3), while the size of this zone is associated with the potential for strain-hardening. The formation of microcracks begins and for this reason the dependence of "stress-strain" becomes nonlinear. The frequency of signals per unit of time in this zone indicates the trajectory of destruction: with an instantaneous burst of a series of signals the destruction occurs according to a fragile scenario, with a periodic, prolonged appearance of signals, the destruction occurs with the involvement of microfiber and the development of plastic deformations. The development of cracks acquires an unstable, avalanche-like character during the transition from zone 3 to zone 4. An increase of acoustic events per unit of time is observed in the deformation area from zone 4 to zone 6, which is probably due to more intensive crack development. Characteristically, this phenomenon is observed for beam-samples of all mixes with the same deflection in the range from 1.2 to 2.2 mm. Zone 7 is characterized by a more intense release of signals in a sample, which has a more fragile destruction trajectory. This can probably be explained by the interaction of matrix particles with each other, while a sample that has collapsed along a plastic trajectory involves microfibers more effectively. The proposed approach in substantiating the selected zones makes it possible to obtain tools for indirect inspection and monitoring of building structures, as well as to predict and control the stages of crack development in the bent elements of the structures. The use of strain-hardening composites based on inorganic binders is actually in structures for which the presence of a strain-hardening zone on the deformation curve of material is of priority importance compared to the value of compressive or bending strength. Walling of mine workings can be one of the areas of application. Often, sprayed concrete with steel mesh reinforcement is used to fasten support. The sprayed concrete The proposed approach in substantiating the selected zones makes it possible to obtain tools for indirect inspection and monitoring of building structures, as well as to predict and control the stages of crack development in the bent elements of the structures. The use of strain-hardening composites based on inorganic binders is actually in structures for which the presence of a strain-hardening zone on the deformation curve of material is of priority importance compared to the value of compressive or bending strength. Walling of mine workings can be one of the areas of application. Often, sprayed concrete with steel mesh reinforcement is used to fasten support. The sprayed concrete support repeats the shape of the mine surface. Dispersed reinforcement with metal or synthetic fiber is performed to improve the mechanical properties of the sprayed concrete support. The main requirement for the mechanical behavior of fiber-reinforced sprayed concrete for walling mine workings is imposed on the post peak zone. The value at which the structure completely loses its ability to resist the load and its destruction occurs are taken as the value of the maximum bearing capacity of the support. Multiple cracking of concrete requires the development of non-destructive methods of structural control in difficult operating conditions [81, 82] . The main advantages when using the fiber-reinforced spray concrete for walling the mine workings are as follows [83] [84] [85] [86] [87] [88] : fibers in a large amount contribute to the appearance of strain-hardening of material after the formation of microcracks under external loading; -mechanical properties of lining increase under complex loading since reinforcement is carried out in all directions of walling; -residual strength of fiber-reinforced spray concrete is higher than the strength of ordinary concrete; -connectivity of sprayed concrete with the rock contour increases since there are no voids that can form between the rock contour and the sprayed concrete in the case of mesh reinforcement; -ensuring the strength properties of concrete under elevated temperature [89, 90] . It should be noted that the cost of fiber-reinforced concrete increases significantly with the increase of microfiber amount. The use of ground slags and affordable polypropylene microfiber can solve this problem. Further research should be carried out in order to develop new compositions of strain-hardening composites with inorganic binders based on by-products of the industry including the possibility of applying mixtures using shotcrete technology. Strength and deformation properties of pseudo strain-hardening composites based on inorganic binders with polypropylene microfiber under compression and tension in bending with the additional determination of the quantity of acoustic emission signals were carried out. The following new knowledge is obtained in the work: new compositions of strain-hardening material with alkali-activated slag matrix; data on the value of strainhardening in composites with polypropylene microfiber depending on its quantity and water-to-binder ratio, and data on the number of acoustic signals when approaching the ultimate strength and in the area of residual strength. A high-strength Portland cement matrix with compressive strength of 70 MPa and alkali-activated slag matrix with a compressive strength of 40 MPa were used. The matrix compositions were selected for high filling the composites with polypropylene microfiber in the amount of 5.5% vol. and 3.5% vol. for Portland cement and alkali-activated slag binder, respectively. Recommendations for the development of new strain-hardening composites with good workability are given. The increase of PP microfiber amount from 4.4% to 5.5% by volume in Portland cement composites led to a decrease in bending strength. The strain-hardening zone appears on the deformation curves of both mixes. However, this zone in samples with 5.5% vol. of PP microfiber is of interest because the bending strength corresponding to sample destruction exceeds the bending strength corresponding to the first microcrack. The results show a contradictory pattern in the case of composites with alkali-activated slag matrix. The bending strength decreases with the decrease of the water-to-binder ratio from 0.3 to 0.22 at the constant microfiber amount of 3.5%. The strain-hardening zone appears in composition with W/B = 0.22, which is more pronounced compared to the zone on the deformation curve of composition with W/B = 0.3, namely, the bending strength corresponding to sample destruction exceeds the bending strength corresponding to the first microcrack. Hydrophobic PP microfibers, in large amounts, reduce the compressive and tensile strength in bending. However, the use of these microfibers in large quantities makes it possible to obtain significant strain-hardening, which is of priority in some areas of construction, for example, in walling of mine workings. The acoustic emission method was used to assess the destruction of composites. A smaller number of acoustic signals, by 3-4 times, was observed for alkali-activated slag composites. Peaks in the number of acoustic signals in these samples were observed only in the strain-softening zone. The recorded acoustic signals can be combined into seven groups depending on the stage of sample deformation. The proposed approach in substantiating the selected zones makes it possible to obtain tools for indirect inspection and monitoring of building structures. Effect of fiber properties and matrix composition on the tensile behavior of strainhardening cement-based composites (SHCCs) subject to impact loading An experimental investigation of the behavior of strainhardening cement-based composites (SHCC) under impact compression and shear loading Increasing the Fatigue Resistance of Strain-Hardening Cement-Based Composites (SHCC) by Experimental-Virtual Multi-Scale Material Design Fibers and their properties for concrete reinforcement Experimental Investigation of Concrete Transverse Deformations at Relatively High Loading Rates for Interpretation of High Strength Concrete Behavior Prediction of the stress state of the shotcreting support under repeated seismic load Study of the stress-strain state in the sub-rectangular tunnel Flexural Behavior of Two-Span Continuous CFRP RC Beams Effects of supplementary cementitious materials and curing condition on mechanical properties of ultra-high-performance, strain-hardening cementitious composites Strain-rate effects on the tensile behavior of strain-hardening cementitious composites Rheological Model to Describe the Cyclic Load-Bearing Behaviour of Strain-Hardening Cement-Based Composites (SHCC) On engineered cementitious composites (ECC) a review of the material and its applications Structural phenomenon based theoretical model of concrete tensile behavior at different stress-strain conditions Strengthening of concrete structures with composite based on carbon fiber Improving the structural characteristics of heavy concrete by combined disperse reinforcement High-strength high-ductility Engineered/Strain-Hardening Cementitious Composites (ECC/SHCC) incorporating geopolymer fine aggregates Mechanical behaviour of strain hardening cement-based composites under impact loading Effect of nano silica on concrete bond strength modes of failure Nano-Modified Concrete as Repair Material in Cold Weather Technological Properties of Self-Compacting Concrete Mixtures with Ground Quartz Sand Physicochemical studies of the structure of energy-saving compositions based on slags The Influence of the Environment on the Properties of Hybrid Cement-Based Concrete with Steel and Air-Cooled Slags Bulk utilization of industrial waste (bauxite residue) of red mud concrete Adhesion between silica surfaces due to hydrogen bonding To the question of fiber reinforcement of concrete Design of strain hardening cement-based composites with alkali treated natural curauá fiber A Study on the Mechanical Characteristics of Glass and Nylon Fiber Reinforced Peach Shell Lightweight Concrete Effect of incorporation of rice husk ash instead of cement on the performance of steel fibers reinforced concrete Tensile behaviour of strain-hardening cement-based composites (SHCC) with steel reinforcing bars On the use of limestone calcined clay cement (LC3) in high-strength strain-hardening cement-based composites (HS-SHCC) Microorganism, Carriers, and Immobilization Methods of the Microbial Self-Healing Cement-Based Composites: A Review The Mechanism of a Penetrative Action for Portland Cement-Based Waterproofing Compositions Preliminary evaluation of the feasibility of using polypropylene fibres from COVID-19 single-use face masks to improve the mechanical properties of concrete Microstructural behaviour and shrinkage properties of high-strength fiber-reinforced seawater sea-sand concrete Polypropylene fiber-based strain-hardening cementitious composites Tensile properties of strain-hardening cementitious composites containing polyvinyl-alcohol fibers hybridized with polypropylene fibers Hydration characteristics of low carbon cementitious materials with multiple solid wastes Performance investigation of demolition wastes-based concrete composites Potential Energy Savings from Circular Economy Scenarios Based on Construction and Agri-Food Waste in Italy High performance cementitious composite from alkaliactivated ladle slag reinforced with polypropylene fibers Strain hardening polypropylene fiber reinforced composite from hydrated ladle slag and gypsum The effect of hybridization and geometry of polypropylene fibers on engineered cementitious composites reinforced by polyvinyl alcohol fibers Estimation of Post-Cracking Dissipation Capabilities of Fiber Reinforced Concretes in Three Point Bending Test Monitored with Application of Digital Image Correlation System Analysis and Prediction of Sulfate Erosion Damage of Concrete in Service Tunnel Based on ARIMA Model Prediction of spatial stress-strain behavior of physically nonlinear soil mass in tunnel face area Acoustic emission for characterising the crack propagation in strainhardening cement-based composites (SHCC) Crack classification in concrete based on acoustic emission Quantitative evaluation of fracture processes in concrete using signal-based acoustic emission techniques Classification of cracking mode in concrete by acoustic emission parameters Characterizing the crack development in strain-hardening cement-based composites (SHCC) by means of acoustic emission Experimental study of fiber-reinforced concrete structures A Taguchi approach for study on impact response of ultra-high-performance polypropylene fibrous cementitious composite Link of Self-Compacting Fiber Concrete Behaviors to Composite Binders and Superplasticizer Development of fiber reinforced self-compacting concrete (FRSCC): Towards an efficient utilization of quaternary composite binders and fibers Mechanical properties of fiber-reinforced concrete using composite binders Low-Clinker cements with low water demand Influence of ground granulated blast furnace slag properties on the superplasticizers effect El'shaeva, D. The Influence of Composition and Recipe Dosage on the Strength Characteristics of New Geopolymer Concrete with the Use of Stone Flour Effects of Steel Fibers (SF) and Ground Granulated Blast Furnace Slag (GGBS) on Recycled Aggregate Concrete Fiber-reinforced alkali-activated concrete: A review Low-permeability fiber-reinforcement concrete of composite binder Tensile behavior of high-strength strain-hardening cementbased composites (HS-SHCC) made with high-performance polyethylene, aramid and PBO fibers Development of classification of rheologically active microfillers for disperse systems with portland cement and super plasticizer Fiber concrete for industrial and civil construction The effect of mechanical-thermal synergistic activation on the mechanical properties and microstructure of recycled powder geopolymer Effect of Amount of Fibre and Damage Level on Service Life of SFR Recycled Concrete in Aggressive Environment Sustainability levels in comparison with mechanical properties and durability of pumice high-performance concrete Optimisation of GBFS, Fly Ash, and Nano-Silica Contents in Alkali-Activated Mortars Experimental study regarding the influence of fibre to matrix compatibility on general performance of Fibre Engineered Cementitious Materials (FECM) Natural fibre rebar cementitious composites Effect of high-calcium basalt fiber on the workability, mechanical properties and microstructure of slag-fly ash geopolymer grouting material Experimental and informational modeling study of sustainable self-compacting geopolymer concrete CO2 Emission Optimization of Concrete-Filled Steel Tubular Rectangular Stub Columns Using Metaheuristic Algorithms Effect of Low-Modulus Polypropylene Fiber on Physical and Mechanical Properties of Self-Compacting Concrete. Case Stud Life cycle assessment on construction and demolition waste: A systematic literature review Green concrete based on quaternary binders with significant reduced of CO2 emissions Experimental Research on Mechanical and Permeability Properties of Nylon Fiber Reinforced Recycled Aggregate Concrete with Mineral Admixture Damage investigation of ultra high performance concrete under direct tensile test using acoustic emission techniques Control of inhomogeneous materials strength by method of acoustic emission Quality control of hardening technologies using the acoustic emission method Concrete cracks detection and monitoring using deep learning-based multiresolution analysis Wavelet-based multiresolution analysis coupled with deep learning to efficiently monitor cracks in concrete Ion flotation of rare-earth metals with sodium dodecyl sulfate Evaluation of Industrial by-products as pozzolans: A road map for use in concrete production. Case Stud. Constr Alternative non-destructive method for strength testing of structural concrete Diagnostics and regulation of rheological characteristics for injection mortars by electromechanical sensors Efficiency of stabilization of slag suspensions by polycarboxylate Parametric Studies of the Load Transfer Platform Reinforcement Interaction with Columns Development and strength assessment of sustainable high strength fiber reinforced concrete. Mater Structural response of self-compacting concrete beams under elevated temperature. Mater Informed Consent Statement: Informed consent was obtained from all subjects. The authors declare no conflict of interest.