key: cord-0023779-o8iy0faj authors: Ma, Qun; Liu, Lichao; Yang, Zeyue; Zheng, Peng title: Facile Synthesis of Peptide-Conjugated Gold Nanoclusters with Different Lengths date: 2021-11-02 journal: Nanomaterials (Basel) DOI: 10.3390/nano11112932 sha: f24a2536e4f80f4066293f621e606c5ff761b4df doc_id: 23779 cord_uid: o8iy0faj The synthesis of ultra-small gold nanoclusters (Au NCs) with sizes down to 2 nm has received increasing interest due to their unique optical and electronic properties. Like many peptide-coated gold nanospheres synthesized before, modified gold nanoclusters with peptide conjugation are potentially significant in biomedical and catalytic fields. Here, we explore whether such small-sized gold nanoclusters can be conjugated with peptides also and characterize them using atomic force microscopy. Using a long and flexible elastin-like polypeptide (ELP)(20) as the conjugated peptide, (ELP)(20)-Au NCs was successfully synthesized via a one-pot synthesis method. The unique optical and electronic properties of gold nanoclusters are still preserved, while a much larger size was obtained as expected due to the peptide conjugation. In addition, a short and rigid peptide (EAAAK)(3) was conjugated to the gold nanoclusters. Their Yong’s modulus was characterized using atomic force microscopy (AFM). Moreover, the coated peptide on the nanoclusters was pulled using AFM-based single molecule-force spectroscopy (SMFS), showing expected properties as one of the first force spectroscopy experiments on peptide-coated nanoclusters. Our results pave the way for further modification of nanoclusters based on the conjugated peptides and show a new method to characterize these materials using AFM-SMFS. Gold nanoparticles, particularly gold nanospheres [1] [2] [3] [4] [5] [6] [7] [8] (Au NSs, size < 200 nm) and gold nanoclusters [9] [10] [11] [12] [13] [14] [15] [16] [17] (Au NCs, size < 2 nm), have received growing attention in recent years because of their excellent optical and electronic properties [18] [19] [20] . Many biomoleculeconjugated Au NSs have been prepared, such as peptide, protein, and DNA, which have a potential use in many biomedical and biosensing applications [21] [22] [23] [24] [25] [26] [27] [28] [29] . Typically, the peptides are conjugated to the surface of gold nanoparticles through the Au-S bond which was formed between the cysteine and gold [30] [31] [32] [33] . So far, most peptide-conjugated nanoparticles are prepared by using the larger size Au NSs, while the peptide-conjugation of ultra-small Au NCs is relatively less. Considering the much larger size of peptides compared with the nanoclusters, the synthesis of peptide-coated nanoclusters may be complex. Moreover, many protein-conjugated Au NSs have been prepared with more diverse and powerful applications [8, [34] [35] [36] [37] [38] , which are typically directly immobilized by non-specific interactions [39, 40] . Here, the conjugation of a lengthy peptide on Au NSs can be the first step toward site-specific protein modification. By conjugating a proper peptide with a recognition site for enzymatic connection, a target protein can be further coated on the nanoclusters via an enzymatic ligation with the peptide, such as using sortase or asparaginyl ligase (AEP) [41] [42] [43] . Thus, we explore here whether such small-sized Au NCs can be conjugated with a long peptide, with the ultimate goal for site-specific protein immobilization on nanocluster. can be conjugated with a long peptide, with the ultimate goal for site-specific protein immobilization on nanocluster. Tow peptides with different lengths were used for conjugation ( Figure 1 ). First, a long and flexible elastin-like polypeptide (ELP), consisting of a repeat unit of Val-Pro-Gly-Xaa-Gly derived from human tropoelastin, was selected. Due to its unique thermos-responsive ability and low-mechanical strength, the ELP fragment has been used to synthesize smart-nanoparticle responsible for the change of temperature and be used as a soft linker for single-molecule studies [42, [44] [45] [46] [47] [48] [49] [50] . Specifically, a polypeptide of twenty ELP units, (ELP)20, was used here, which has nearly twenty times higher length than the nanocluster (~20 nm vs. 1 nm) with a high molecular weight (~10 kDa). Secondly, a rigid peptide (EAAAK)3 with a comparable length (~7.5 nm) as the nanoclusters was tested. Moreover, it is worth noting that (EAAAK)3 has been widely used as the scaffold in biomacromolecule conjugation [51] . Hydrogen tetrachloroaurate (III) trihydrate (HAuCl4·3H2O) was purchased from Alfa Aesar (Shanghai, China). Trisodium citrate dihydrate was purchased from Sinopharm Chemical Reagent Co. Ltd. (Shanghai, China). Peptide CCY(EAAAK)3 was synthesized using a solid-phase method (Sangon Biotech Co. Ltd., purity 95%) (Shanghai, China). Other reagents were purchased from Sangon Biotech Co. Ltd. (Shanghai, China). All reagents were used without further purification. Ultrapure water (18 MΩ cm −1 ) was obtained from a Millipore Milli-Q Advantage water purification system (Burlington, MA, USA). E. coil BL21 (DE3) and XL1-Blue cells were purchased from TransGen Biotech Co. Ltd. (Beijing, China). The glass coverslips were purchased from Sail Brand, China. The AFM cantilevers (MLCT-Bio-DC) were purchased from Bruker Corp (Billerica, MA, USA). Hydrogen tetrachloroaurate (III) trihydrate (HAuCl 4 ·3H 2 O) was purchased from Alfa Aesar (Shanghai, China). Trisodium citrate dihydrate was purchased from Sinopharm Chemical Reagent Co. Ltd. (Shanghai, China). Peptide CCY(EAAAK) 3 was synthesized using a solid-phase method (Sangon Biotech Co. Ltd., purity 95%) (Shanghai, China). Other reagents were purchased from Sangon Biotech Co. Ltd. (Shanghai, China). All reagents were used without further purification. Ultrapure water (18 MΩ cm −1 ) was obtained from a Millipore Milli-Q Advantage water purification system (Burlington, MA, USA). E. coil BL21 (DE3) and XL1-Blue cells were purchased from TransGen Biotech Co. Ltd. (Beijing, China). The glass coverslips were purchased from Sail Brand, China. The AFM cantilevers (MLCT-Bio-DC) were purchased from Bruker Corp (Billerica, MA, USA). The size and morphology of nanoparticles and clusters were observed using a JEOL JEM-2100 transmission electron microscope (Tokyo, Japan) at 200 kV and a Thermo Sci-Nanomaterials 2021, 11, 2932 3 of 11 entific Talos L120C TEM (Waltham, MA, USA) at 120 kV. Dynamic light scattering (DLS) was recorded at a wavelength of 659 nm and zeta potential experiments were conducted on 90 Plus/BI-MAS equipment (Brookhaven, NY, USA). The concentration of Au was determined by inductively coupled plasma mass spectrometry (Thermo X Series 2 ICP-MS, Waltham, MA, USA). The UV-Vis spectra were measured on an Ocean Optics Maya 2000 Pro spectrometer (Orlando, FL, USA). The fluorescence spectra were measured on a HORIBA Jobin Yvon Fluoromax-4 fluorescence spectrometer (Irvine, CA, USA). The concentrations of CCY(ELP) 20 and C-(ELP) 20 were determined using the Ellman method. The AFM experiments were performed on a Nanowizard4 AFM (JPK, Berlin, Germany). Mass spectrometric analyses were performed using an UltrafleXtreme MALDI-TOF mass spectrometer (Bruker Daltonics, Billerica, MA, USA) operating in linear positive ion mode with 2,5-Dihydroxybenzoic acid (DHB) as the matrix. ELP is the abbreviation of the elastin-like polypeptide. The genes of (ELP) 20 were purchased from Genscript (Nanjing, China). Construction of C-(ELP) 20 and CCY(ELP) 20 was in the expression vector pET-28a by standard molecular biology and PCR techniques. The plasmids were transformed and then overexpressed in E. coli BL21 (DE3) cells. The bacteria kept in the LB medium containing 50 µg mL −1 kanamycin were grown to an OD 600 = 0.6 and then were induced by 0.5 mM isopropyl β-D-thiogalactoside (IPTG) overnight at 18 • C. The cells were obtained by centrifugation at 9000 rpm for 5 min at 4 • C (Avanti JXN series, Beckman Coulter, Brea, CA, USA). The cells were redispersed in buffer (50 mM Tris, 100 mM NaCl, pH 7.0) and lysed via a high-pressure homogenization. The supernatants were mixed with Co-NTA affinity beads and then kept for 2 to 3 h after the centrifugation operation at 20,000 rpm for 30 min. The mixture was washed with buffer (20 mM Tris, 400 mM NaCl, 2 mM imidazole, pH 7.0) several times and eluted in buffer (20 mM Tris, 400 mM NaCl, 250 mM imidazole, pH 7.0) immediately. Citrate capped Au nanospheres were synthesized according to a previously published method [52] . Briefly, HAuCl 4 (1 mL, 25 mM) was injected into a boiling aqueous solution of sodium citrate (2.2 mM, 150 mL) under magnetic stirring. The solution was cooled to room temperature when the solution turned red. The concentration of Au (0.18 mM) was determined by ICP-MS. 1.5 mL of C-(ELP) 20 (1.3 µmoL) solution was added into the 20 mL Au-Cit solution dropwise [53] . The sample was stirred for three hours at room temperature. The product (ELP) 20 -Au NSs were collected by centrifugation and washed with buffer (50 mM Tris, 100 mM NaCl, pH 7.0) several times. Finally, the (ELP) 20 -Au NSs were dispersed in buffer (50 mM Tris, 100 mM NaCl, pH 7.0). Based on the quantity of the reactant HAuCl 4 and peptide, we estimated the concentration of NSs is 5 × 10 4 ppm with a cove rate of 5. First, CCY(ELP) 20 was obtained from C-(ELP) 20 using the standard molecular biology method. Then, (ELP) 20 -AuNCs were synthesized accordingly to the previously reported method. In a typical experiment, an aqueous solution of HAuCl 4 (70 µL, 25 mM) was added slowly to the CCY(ELP) 20 solution (1.7 mL, 1 mM) under vigorous stirring in a 5 mL flask. Then NaOH solution (300 µL, 0.5 M) was added to adjust the pH of the sample to 9. The mixture was reacted for 12 h in the dark. Finally, the product (ELP) 20 -Au NCs were purified by dialysis (Dialysis Membrane MWCO: 100 KD) against buffer (50 mM Tris, 100 mM NaCl, pH 7.0) for three days. Similarly, we estimated the concentration of NCs is 77.5 ppm with a cove rate of 37. The synthesis of (EAAAK) 3 -Au NCs was similar to (ELP) 20 -Au NCs. First, 3.4 mg peptide CCY(EAAAK) 3 was dissolved in 1.65 mL H 2 O. Next, an aqueous solution of HAuCl 4 (66 µL, 25 mM) was added slowly to the CCY(EAAAK) 3 solution (1 mM) under vigorous magnetic stirring in a 5 mL flask. Then NaOH solution (300 µL, 0.5 M) was added to adjust the pH of the sample to 13. The mixture was reacted for 12 h in the dark. Finally, the product (EAAAK) 3 -Au NCs were purified by dialysis (Dialysis Membrane MWCO: 10 KD) against H 2 O for three days. We estimated the concentration of NCs is 116 ppm with a cover rate of 38. To better demonstrate the synthesis and property of the (ELP) 20 -conjugated gold nanoclusters, we synthesized the (ELP) 20 -gold nanospheres with a larger particle size first for comparison. The Au-Cit NSs were synthesized by the classic method described above. The TEM picture ( Figure S1 ) showed that the Au-Cit NSs were monodispersed in water with an average diameter of 9 nm. Peptide C-(ELP) 20 was naturally produced using E. coli expression. The purified peptide showed an expected molecular weight of~10 kDa, verified by SDS-PAGE gel ( Figure S2 ). Then the (ELP) 20 -Au NSs were synthesized by the ligand-exchange method owing to the Au-S bond formation between cysteine residues in C-(ELP) 20 and Au-Cit NSs ( Figure 1a ). Dynamic light scattering (DLS) and zeta potential experiments were conducted to further prove its peptide conjugation on the nanospheres. The changes of hydrodynamic diameter distribution along with Zeta potential indicated that the conjugation of flexible peptide C-(ELP) 20 on the NSs is successful (Figure 2a,b) . In addition, the UV-Vis absorption spectroscopy showed that the surface plasmon resonance peak is red-shifted from 520 to 530 nm after being modified with peptide C-(ELP) 20 (Figure 2c ). The modified (ELP) 20 -Au NSs were well monodisperse without aggregation in buffer (50 mM Tris, 100 mM NaCl, pH 7.0) as shown in the TEM picture ( Figure 2d) . Furthermore, the morphology of the prepared (ELP) 20 -Au NSs experienced no change at all compared with the Au-Cit NSs ( Figure S1 ). Next, we explore whether the ultra-small Au nanocluster conjugated with the long peptide, CCY(ELP) 20 , can also be synthesized (Figures 1b, S3 and S4) . Here, the peptideconjugated gold nanoclusters were synthesized using a one-pot method, in which the formation of gold nanoclusters and the peptide conjugation were achieved at the same step. In short, the tyrosine in the CCY(ELP) 20 functioned as a reducing agent and participated in the formation of (ELP) 20 -Au NCs [10, 54] . Thus, the ELP peptide was conjugated in the same step. The details for the synthesis can be found above. As shown in Figure 3a , the solution of (ELP) 20 -Au NCs exhibited light yellow under room light and pink fluorescence under UV light, consistent with the formation of gold nanoclusters. Compared to Au NSs, luminescence is the unique property of Au nanoclusters. It is believed that the small size of the Au NSs (2 nm) is comparable to Fermi wavelength of electrons (<1 nm) and thus has a visible-to-near infrared fluorescence. It indicates the unique optical property of Au NCs is preserved after the conjugation of a long peptide. The negative-stain EM image and the histogram revealed the Au NCs with an average diameter of 1.29 nm (Figure 3b,c) . In addition, the aggregation state of CCY(ELP) 20 from the negative-stain EM image also confirmed the successful synthesis of the nanoclusters ( Figure S5 ). Moreover, DLS results of (ELP) 20 -Au NCs (Figure 3d ) showed that the hydrodynamic diameter was about 40 nm, much larger than the size observed with TEM. It agrees well with a long ELP peptide's conjugation and proves the CCY(ELP) 20 conjugation on the nanocluster. The (ELP) 20 -Au NCs showed a broad absorption band ranging from 250 nm to 800 nm with a small absorption peak located at 280 nm, which can be attributed to the absorption of tyrosine. The location of this peak and the absorption spectrum matched with CCY(ELP) 20 (Figure 3e ). The fluorescence excitation and emission spectra of CCY(ELP) 20 and (ELP) 20 -Au NCs were depicted in Figure 3f . The fluorescence emission spectra of (ELP) 20 -Au NCs ranged from 600 to 800 nm, with the emission peak locating at 659 nm when excited at 250 nm with the insertion of 300 nm optical filter in the excitation window. At the same time, the CCY(ELP) 20 exhibited almost negligible emission. In summary, all data proved that the (ELP) 20 -Au NCs are successfully synthesized. Moreover, the composition of the (ELP) 20 -Au NCs were characterized by using matrix-assisted laser desorption/ionization time of flight mass spectrometry (MALDI-TOF MS). The mass spectrum indicated that (ELP) 20 -Au NCs were mainly composed of Au 21 and Au 23 ( Figure S6 ). Next, we explore whether the ultra-small Au nanocluster conjugated with the long peptide, CCY(ELP)20, can also be synthesized (Figures 1b, S3 and S4) . Here, the peptideconjugated gold nanoclusters were synthesized using a one-pot method, in which the formation of gold nanoclusters and the peptide conjugation were achieved at the same step. In short, the tyrosine in the CCY(ELP)20 functioned as a reducing agent and participated in the formation of (ELP)20-Au NCs [10, 54] . Thus, the ELP peptide was conjugated in the same step. The details for the synthesis can be found above. As shown in Figure 3a , the solution of (ELP)20-Au NCs exhibited light yellow under room light and pink fluorescence under UV light, consistent with the formation of gold nanoclusters. Compared to Au NSs, luminescence is the unique property of Au nanoclusters. It is believed that the small size of the Au NSs (2 nm) is comparable to Fermi wavelength of electrons (<1 nm) and thus has a visible-to-near infrared fluorescence. It indicates the unique optical property of Au NCs is preserved after the conjugation of a long peptide. The negative-stain EM image and the histogram revealed the Au NCs with an average diameter of 1.29 nm (Figure 3b,c) . In addition, the aggregation state of CCY(ELP)20 from the negative-stain EM image also confirmed the successful synthesis of the nanoclusters ( Figure S5 ). Moreover, DLS results of (ELP)20-Au NCs (Figure 3d ) showed that the hydrodynamic diameter was about 40 nm, much larger than the size observed with TEM. It agrees well with a long ELP peptide's conjugation and proves the CCY(ELP)20 conjugation on the nanocluster. The (ELP)20-Au NCs showed a broad absorption band ranging from 250 nm to 800 nm with a small absorption peak located at 280 nm, which can be attributed to the absorption of tyrosine. The location of this peak and the absorption spectrum matched with CCY(ELP)20 ( Figure 3e ). The fluorescence excitation and emission spectra of CCY(ELP)20 and (ELP)20-Au NCs were depicted in Figure 3f . The fluorescence emission spectra of (ELP)20-Au NCs ranged from 600 to 800 nm, with the emission peak locating at 659 nm when excited at 250 nm with the insertion of 300 nm optical filter in the excitation window. At the same time, the CCY(ELP)20 exhibited almost negligible emission. In summary, all data proved that the In addition to the synthesis of a long (ELP)20-conjugated gold nanoclusters, we demonstrate the synthesis of another short peptide CCY(EAAAK)3 -conjugated nanoclusters (Figures 1c and S7) . The synthesis procedure is almost the same as the previous one, which can be found in Section 2.6. As shown in Figure 4a , the solution of (EAAAK)3-Au NCs appeared light brown under room light and pink fluorescence under UV light. TEM In addition to the synthesis of a long (ELP) 20 -conjugated gold nanoclusters, we demonstrate the synthesis of another short peptide CCY(EAAAK) 3 -conjugated nanoclusters (Figures 1c and S7) . The synthesis procedure is almost the same as the previous one, which can be found in Section 2.6. As shown in Figure 4a , the solution of (EAAAK) 3 -Au NCs appeared light brown under room light and pink fluorescence under UV light. TEM images showed the morphology and monodispersity of (EAAAK) 3 -Au NCs with an average diameter of 1.1 nm (Figures 4b,c and S8) . It is noted that the peptide was not detectable in TEM, and the value here reflects the diameter of the Au nanocluster core. Indeed, DLS results of (EAAAK) 3 -Au NCs (Figure 4d) showed an average diameter of~3 nm (Raw data in Table S1 ). Nevertheless, the detection limit of our DLS is 2 nm. Thus, the actual diameter may be biased and smaller than the apparent DLS result. The (EAAAK) 3 -Au NCs showed a broad absorption band ranging from 250 nm to 800 nm with a small absorption peak located at 273 nm, which is the characteristic absorption of tyrosine. The location of this peak and the absorption spectrum fitted with CCY(EAAAK) 3 (Figure 4e ). Figure 4f showed the fluorescence excitation and emission spectra of CCY(EAAAK) 3 and (EAAAK) 3 -Au NCs. The fluorescence emission spectra of (EAAAK) 3 -Au NCs ranged from 550 to 850 nm, with the emission peak at 660 nm when excited at 498 nm, similar to the preceding experimental results. The emission spectra of (EAAAK) 3 -Au NCs were shown in Figure S9 and the peak of emission spectrum peak was at 660 nm. Furthermore, the mass spectrum showed that (EAAAK) 3 -Au NCs mainly consisted of Au 16 and Au 21 ( Figure S10 ). To verify the differences between the two types of peptides-modified Au NCs, atomic force microscopy imaging and Young's modulus measurement experiments were conducted. Briefly, the Au NCs were dispersed on the mica evenly and immersed in the corresponding buffer. The Au NCs on the mica showed a distinct difference in the morphology and Young's modulus ( Figure 5 ) when compared with the substrate mica ( Figure S11 ). In addition, (ELP)20-Au NCs appeared larger in size and irregular in morphology in contrast with (EAAAK)3-Au NCs (Figure 5a,d) , which is possibly attributed to the larger molecular weight of CCY(ELP)20 than CCY(EAAAK)3. It is worth noting that the brighter particle in Figure 5d is the aggregation of the (EAAAK)3-Au NCs, which is caused by the addition of the adsorption buffer (KCl), which helps the adsorption of (EAAAK)3-Au NCs To verify the differences between the two types of peptides-modified Au NCs, atomic force microscopy imaging and Young's modulus measurement experiments were conducted. Briefly, the Au NCs were dispersed on the mica evenly and immersed in the corresponding buffer. The Au NCs on the mica showed a distinct difference in the morphology and Young's modulus ( Figure 5 ) when compared with the substrate mica ( Figure S11 ). In addition, (ELP) 20 -Au NCs appeared larger in size and irregular in morphology in contrast with Nanomaterials 2021, 11, 2932 7 of 11 (EAAAK) 3 -Au NCs (Figure 5a,d) , which is possibly attributed to the larger molecular weight of CCY(ELP) 20 than CCY(EAAAK) 3 . It is worth noting that the brighter particle in Figure 5d is the aggregation of the (EAAAK) 3 -Au NCs, which is caused by the addition of the adsorption buffer (KCl), which helps the adsorption of (EAAAK) 3 -Au NCs on the mica. Moreover, Young's modulus of (ELP) 20 -Au NCs measured is about 50 MPa, which is higher than the (EAAAK) 3 -Au NCs (~35 MPa) ( Figure 5 ). AFM imaging showed that the Au NCs were dispersed uniformly and in the state of a single nanoparticle (Figure 5a,d) . Based on this, we conducted the atomic force microscopybased single-molecule force spectroscopy (AFM-SMFS) experiment to pull the coated peptide ( Figure 6a) . First, the AFM tip approached and captured the peptide. Then the tip pulled the peptide vertically, leading to a length increment from the peptide extension. Finally, the peptide detached from the tip, and the detachment force was recorded. All corresponding force-extension curves on the (ELP) 20 In this work, we demonstrate the conjugation of a long and flexible peptide CCY-(ELP)20 on an ultra-small gold nanocluster via the one-pot synthesis. The nanocluster remains its unique optical property while the hydrodynamic diameter increases significantly due to the conjugated long peptide. Also, a short and rigid peptide-conjugated gold nanocluster is synthesized with the expected property, characterized by classic method and atomic force microscopy. Thus, we believe gold nanocluster is suitable for conjugation/functionalization with most peptide sequences, regardless of their size and length. And many previous works on peptide-conjugated nanoparticles can be adopted for nanocluster and may show better performance due to the smaller nanocluster size. In addition, the conjugated peptide may modify the properties of AuNCs. For example, the coated long peptide (ELP)20 may increase the contact area between the AuNCs and the surface, leading to increased friction and a modification of the tribological properties of the nanocluster. And the coated peptide may change the optical properties of the AuNCs if the peptide possesses additional optical properties. Moreover, the demonstration here may have great potentials for further modification of gold nanoclusters. Enzymes can recognize many specific peptide sequences for ligation, such as sortase and asparaginyl ligase OaAEP1 [42, 43, [55] [56] [57] , and the use of a suitable peptide as a linker for protein immobilization may allow further characterization by single-molecule force spectroscopy [58] [59] [60] [61] [62] [63] [64] [65] [66] , which may provide mechanical information about the nanocluster and immobilized protein [67] [68] [69] [70] [71] . Thus, by designing a proper peptide sequence for a first step peptide-conjugation, further functionalization and characterization of the nanoclusters can be possible [72] [73] [74] [75] [76] [77] . Supplementary Materials: The following are available online at www.mdpi.com/xxx/s1, Table S1 . Raw data of hydrodynamic diameter distribution of (EAAAK)3-Au NCs measured by DLS. Figure S1 . TEM image of Au-Cit NSs. Figure S2 . SDS-PAGE result of C-ELP20. Figure S3 . SDS-PAGE result of CCY(ELP)20. Figure S4 . MALDI-TOF MS result of CCY(ELP)20. Figure S5 . Low-magnified negative-stain EM image of (ELP)20-Au NCs. Figure S6 . MALDI TOF-MS result of (ELP)20-Au NCs. Figure S7 . MALDI-TOF MS result of CCY(EAAAK)3. Figure S8 . TEM image of (EAAAK)3-Au NCs. Figure S9 . The emission spectra of (EAAAK)3-Au NCs. Figure S10 . MALDI TOF-MS result of (EAAAK)3-Au NCs. Figure S11 . AFM imaging and Young's modulus measurement of mica substrate. In this work, we demonstrate the conjugation of a long and flexible peptide CCY-(ELP) 20 on an ultra-small gold nanocluster via the one-pot synthesis. The nanocluster remains its unique optical property while the hydrodynamic diameter increases significantly due to the conjugated long peptide. Also, a short and rigid peptide-conjugated gold nanocluster is synthesized with the expected property, characterized by classic method and atomic force microscopy. Thus, we believe gold nanocluster is suitable for conjugation/functionalization with most peptide sequences, regardless of their size and length. And many previous works on peptide-conjugated nanoparticles can be adopted for nanocluster and may show better performance due to the smaller nanocluster size. In addition, the conjugated peptide may modify the properties of AuNCs. For example, the coated long peptide (ELP) 20 may increase the contact area between the AuNCs and the surface, leading to increased friction and a modification of the tribological properties of the nanocluster. And the coated peptide may change the optical properties of the AuNCs if the peptide possesses additional optical properties. Moreover, the demonstration here may have great potentials for further modification of gold nanoclusters. Enzymes can recognize many specific peptide sequences for ligation, such as sortase and asparaginyl ligase OaAEP1 [42, 43, [55] [56] [57] , and the use of a suitable peptide as a linker for protein immobilization may allow further characterization by singlemolecule force spectroscopy [58] [59] [60] [61] [62] [63] [64] [65] [66] , which may provide mechanical information about the nanocluster and immobilized protein [67] [68] [69] [70] [71] . Thus, by designing a proper peptide sequence for a first step peptide-conjugation, further functionalization and characterization of the nanoclusters can be possible [72] [73] [74] [75] [76] [77] . Supplementary Materials: The following are available online at https://www.mdpi.com/article/10 .3390/nano11112932/s1, Table S1 . Raw data of hydrodynamic diameter distribution of (EAAAK) 3 -Au NCs measured by DLS. Figure S1 . TEM image of Au-Cit NSs. Figure S2 . SDS-PAGE result of C-ELP 20 . Figure S3 . SDS-PAGE result of CCY(ELP) 20 . Figure S4 . MALDI-TOF MS result of CCY(ELP) 20 . Figure S5 . Low-magnified negative-stain EM image of (ELP) 20 -Au NCs. Figure S6 . MALDI TOF-MS result of (ELP) 20 -Au NCs. Figure S7 . MALDI-TOF MS result of CCY(EAAAK) 3 . Figure S8 . TEM image of (EAAAK) 3 -Au NCs. Figure S9 . The emission spectra of (EAAAK) 3 -Au NCs. Figure S10 . Tumor targeting and imaging using cyclic rgd-pegylated gold nanoparticle probes with directly conjugated iodine-125 Thermally triggered in situ assembly of gold nanoparticles for cancer multimodal imaging and photothermal therapy Gold nanoparticles in chemical and biological sensing Gold nanoparticles for in vitro diagnostics A versatile surface bioengineering strategy based on mussel-inspired and bioclickable peptide mimic De novo design of polymeric carrier to photothermally release singlet oxygen for hypoxic tumor treatment Gold nanoclusters: Bridging gold complexes and plasmonic nanoparticles in photophysical properties Inorganic nanostructures with strong chiroptical activity Renal clearable catalytic gold nanoclusters for in vivo disease monitoring Rgd peptide-modified fluorescent gold nanoclusters as highly efficient tumor-targeted radiotherapy sensitizers One-pot synthesis of gd3+-functionalized gold nanoclusters for dual model (fluorescence/magnetic resonance) imaging Atomically precise colloidal metal nanoclusters and nanoparticles: Fundamentals and opportunities Bifunctional peptides that precisely biomineralize au clusters and specifically stain cell nuclei Heterogeneous cross-coupling over gold nanoclusters Atomically precise noble metal nanoclusters as efficient catalysts: A bridge between structure and properties DNA dumbbell and chameleon silver nanoclusters for mirna logic operations Nanoscale crystalline sheets and vesicles assembled from nonplanar cyclic π-conjugated molecules Peptide-coated platinum nanoparticles with selective toxicity against liver cancer cells Luminescent metal nanoclusters with aggregation-induced emission Ultra-small fluorescent metal nanoclusters: Synthesis and biological applications Designing a nanoparticle-containing polymeric substrate for detecting cancer cells by computer simulations Identifying reducing and capping sites of protein-encapsulated gold nanoclusters Nanomaterials 2021 Zwitterionic gel coating endows gold nanoparticles with ultrastability Peptide and protein modified metal clusters for cancer diagnostics Peptide modified gold nanoparticles for improved cellular uptake, nuclear transport, and intracellular retention Gold nanoparticles modulate the crosstalk between macrophages and periodontal ligament cells for periodontitis treatment Microwave-assisted synthesis of bsa-stabilized and hsa-protected gold nanoclusters with red emission Bio-ncs-The marriage of ultrasmall metal nanoclusters with biomolecules DNA templated metal nanoclusters: From emergent properties to unique applications Fabrication of peptide stabilized fluorescent gold nanocluster/graphene oxide nanocomplex and its application in turn-on detection of metalloproteinase-9 Luminescent gold nanoclusters for bioimaging applications Aprotinin encapsulated gold nanoclusters: A fluorescent bioprobe with dynamic nuclear targeting and selective detection of trypsin and heavy metal Discriminating single base pair mismatches in DNA using glutathionetemplated copper nanoclusters Green synthesis of protein-protected fluorescent gold nanoclusters (auncs): Reducing the size of auncs by partially occupying the ca2+ site by la3+ in apo-α-lactalbumin Engineering protein-gold nanoparticle/nanorod complexation via surface modification for protein immobilization and potential therapeutic applications Self-assembly of precision noble metal nanoclusters: Hierarchical structural complexity, colloidal superstructures, and applications Fgf21 trafficking in intact human cells revealed by cryo-electron tomography with gold nanoparticles Aggregation of protein therapeutics enhances their immunogenicity: Causes and mitigation strategies Protein-directed synthesis of highly fluorescent gold nanoclusters Tailored design of protein nanoparticle scaffolds for multivalent presentation of viral glycoprotein antigens Sortase-mediated quantifiable enzyme immobilization on magnetic nanoparticles Verification of sortase for protein conjugation by single-molecule force spectroscopy and molecular dynamics simulations Oaaep1-mediated enzymatic synthesis and immobilization of polymerized protein for single-molecule force spectroscopy Site-specific adsorption of gold nanoparticles coated with thermo-responsive peptides Mechanical polyprotein assembly using sfp and sortase-mediated domain oligomerization for single-molecule studies Elastin-like polypeptide linkers for singlemolecule force spectroscopy Bioorthogonal elastin-like polypeptide scaffolds for immunoassay enhancement Single-molecule force spectroscopy reveals that iron-ligand bonds modulate proteins in different modes Next generation methods for single-molecule force spectroscopy on polyproteins and receptor-ligand complexes Single-molecule force spectroscopy reveals that the fe-n bond enables multiple rupture pathways of the 2fe2s cluster in a mitoneet monomer Fusion protein linkers: Property, design and functionality Kinetically controlled seeded growth synthesis of citrate-stabilized gold nanoparticles of up to 200 nm: Size focusing versus ostwald ripening Synthesis, stability, and cellular internalization of gold nanoparticles containing mixed peptide−poly(ethylene glycol) monolayers Peptide protected gold clusters: Chemical synthesis and biomedical applications Enzymatic biosynthesis and immobilization of polyprotein verified at the single-molecule level Tailored polyproteins using sequential staple and cut Functional DNA structures and their biomedical applications Influence of fluorination on single-molecule unfolding and rupture pathways of a mechanostable protein adhesion complex Multistep protein unfolding scenarios from the rupture of a complex metal cluster cd3s9 Zheng, P. N501Y mutation of spike protein in sars-cov-2 strengthens its binding to receptor ace2 Biomechanical characterization of sars-cov-2 spike rbd and human ace2 protein-protein interaction Chemical unfolding of protein domains induces shape change in programmed protein hydrogels Heterogeneous and rate-dependent streptavidin-biotin unbinding revealed by high-speed force spectroscopy and atomistic simulations Towards unveiling the exact molecular structure of amorphous red phosphorus by single-molecule studies Quantifying thiol-gold interactions towards the efficient strength control Single molecule study of force-induced rotation of carbon-carbon double bonds in polymers Single molecule force spectroscopy reveals that a two-coordinate ferric site is critical for the folding of holo-rubredoxin Direct single-molecule quantification reveals unexpectedly high mechanical stability of vinculin-talin/alphacatenin linkages Maleimide-thiol adducts stabilized through stretching Single-molecule mechanics of catechol-iron coordination bonds Kin discrimination in social yeast is mediated by cell surface receptors of the flo11 adhesin family Quantifying the initial unfolding of bacteriorhodopsin reveals retinal stabilization Dissipative supramolecular polymerization powered by light A simple approach to bioconjugation at diverse levels: Metal-free click reactions of activated alkynes with native groups of biotargets without prefunctionalization Combination of click chemistry and enzymatic ligation for stable and efficient protein immobilization for single-molecule force spectroscopy Harvesting mechanical work from folding-based protein engines: From single-molecule mechanochemical cycles to macroscopic devices Mechanochemistry of an interlocked poly [2]catenane: From single molecule to bulk gel