key: cord-0023747-4yjo82dv
authors: Singh, Reetika; Hano, Christophe; Tavanti, Francesco; Sharma, Bechan
title: Biogenic Synthesis and Characterization of Antioxidant and Antimicrobial Silver Nanoparticles Using Flower Extract of Couroupita guianensis Aubl.
date: 2021-11-13
journal: Materials (Basel)
DOI: 10.3390/ma14226854
sha: 430da94412f655e5ba9ab96e8212ec7a44a97a25
doc_id: 23747
cord_uid: 4yjo82dv

Couroupita guianensis Aubl. is an important medicinal tree. This tree is rich in various phytochemicals, and is therefore used as a potent antioxidant and antibacterial agent. This plant is also used for the treatment of various diseases. Here, we have improved its medicinal usage with the biosynthesis of silver nanoparticles (AgNPs) using Couroupita guianensis Aubl. flower extract as a reducing and capping agent. The biosynthesis of the AgNPs reaction was carried out using 1 mM of silver nitrate and flower extract. The effect of the temperature on the biosynthesis of AgNPs was premeditated by room temperature (25 °C) and 60 °C. The continuous stirring of the reaction mixture at room temperature for approximately one hour resulted in the successful formation of AgNPs. A development of a yellowish brown color confirmed the formation of AgNPs. The efficacious development of AgNPs was confirmed by the characteristic peaks of UV–Vis, X-ray diffraction (XRD) and Fourier transform infrared (FT-IR) spectroscopy spectra. The biosynthesized AgNPs exhibited significant free radical scavenging activity through a DPPH antioxidant assay. These AgNPs also showed potent antibacterial activity against many pathogenic bacterial species. The results of molecular dynamics simulations also proved the average size of NPs and antibacterial potential of the flower extract. The observations clearly recommended that the green biosynthesized AgNPs can serve as effective antioxidants and antibacterial agents over the plant extract.

Nanotechnology is a well-recognized and exponentially growing field with potential applications in the medical and non-medical field [1] [2] [3] [4] [5] . The wide range of applications of nanotechnology include device technology, medicine, medical imaging, drug delivery, food technology and environmental aspects [6] . Nanotechnology is a growing field that makes an impact in all provinces of human life [7] , dealing with the synthesis, development and applications of a variety of nanoparticles (NPs). Usually, NPs are produced using noble metals, such as gold, silver, platinum, etc., employing a variety of physiochemical methods [8, 9] ; however, these methods are not eco-friendly [10, 11] . The controlled biosynthesis of metal nanoparticles offers a significant effect by providing a definite size and morphology of NPs, which is different from results obtained by physicochemical methods. These NPs may be defined as particles whose sizes range from 1-100 nm. There is an urgent need to develop a sustainable method for the synthesis of NPs that does not employ noxious chemicals, in order to decrease the toxic residues released into the 

The C. guianensis flowers were collected from JNTBGRI campus, Palode, Trivendrum, Kerala, India. All of the chemicals used in the study were of analytical grade and purchased from Sigma-Aldrich. Millipore distilled water was used for the experiments. All of the experiments were performed in triplicates.

Fully blossomed mature flowers were collected from mature tree grown up to 50-60 ft. To remove the dust particles, the flowers were washed properly under running tap water and also rinsed two times by using Millipore distilled water. Flowers were dried under shade condition for 4-5 days and oven dried for 2-3 h at 40-45 °C. A mechanical grinder was used to make the coarse powder from dried flowers. A Soxhlet apparatus was used for the extraction, following same process as mentioned by Singh and Kumari [44] .

A total of 100 mg of extracts was dissolved in 40 mL Millipore distilled water (MDW) and boiled for 2 min. This preparation was filtered using Whatman no. 1 filter paper and used for nanoparticle synthesis.

Synthesis of AgNPs was performed using green synthesis method. In brief, for the synthesis of AgNPs, 45 mL of freshly prepared aqueous solution of silver nitrate (AgNO3, 1 mM) was mixed with 5 mL of plant extracts (PE). The biosynthesis of AgNPs was carried out at room temperature (25 °C) and 60 °C in order to observe the effect of temperature on the synthesis of AgNPs.

UV-Vis spectroscopic analysis of biosynthesized AgNPs was performed by continuous scanning from 350 to 700 nm (Thermo-Scientific-Evolution-201, Waltham, Massachusetts) and 1 mM silver nitrate solution was used for the baseline correction.

X-ray diffraction (XRD) analysis of purified AgNPs was performed using XRD-6000 X-ray diffractometer (Shimadzu, Kyoto, Japan). XRD machine was operated at a voltage of 40 kV and a current of 30 mA, with Cu Kα radiation in θ-2θ configurations. The average size of AgNPs was calculated using the Debye-Scherrer equation by determining the width of the (1 1 1) Bragg reflection [45] . 

The C. guianensis flowers were collected from JNTBGRI campus, Palode, Trivendrum, Kerala, India. All of the chemicals used in the study were of analytical grade and purchased from Sigma-Aldrich. Millipore distilled water was used for the experiments. All of the experiments were performed in triplicates.

Fully blossomed mature flowers were collected from mature tree grown up to 50-60 ft. To remove the dust particles, the flowers were washed properly under running tap water and also rinsed two times by using Millipore distilled water. Flowers were dried under shade condition for 4-5 days and oven dried for 2-3 h at 40-45 • C. A mechanical grinder was used to make the coarse powder from dried flowers. A Soxhlet apparatus was used for the extraction, following same process as mentioned by Singh and Kumari [44] .

A total of 100 mg of extracts was dissolved in 40 mL Millipore distilled water (MDW) and boiled for 2 min. This preparation was filtered using Whatman no. 1 filter paper and used for nanoparticle synthesis.

Synthesis of AgNPs was performed using green synthesis method. In brief, for the synthesis of AgNPs, 45 mL of freshly prepared aqueous solution of silver nitrate (AgNO 3 , 1 mM) was mixed with 5 mL of plant extracts (PE). The biosynthesis of AgNPs was carried out at room temperature (25 • C) and 60 • C in order to observe the effect of temperature on the synthesis of AgNPs.

UV-Vis spectroscopic analysis of biosynthesized AgNPs was performed by continuous scanning from 350 to 700 nm (Thermo-Scientific-Evolution-201, Waltham, MA, USA) and 1 mM silver nitrate solution was used for the baseline correction.

X-ray diffraction (XRD) analysis of purified AgNPs was performed using XRD-6000 X-ray diffractometer (Shimadzu, Kyoto, Japan). XRD machine was operated at a voltage of 40 kV and a current of 30 mA, with Cu Kα radiation in θ-2θ configurations. The average size of AgNPs was calculated using the Debye-Scherrer equation by determining the width of the (1 1 1) Bragg reflection [45] .

Formation of AgNPs was also confirmed using FTIR analysis. UV-vis and XRD analysis showed almost similar results for both preparations of nanoparticles (25 • C and 60 • C). The further analysis was performed with AgNPs synthesized at 25 • C only. AgNPs synthe- sized at room temperature (25 • C) were characterized using an FTIR (Bruker-Alpha, V70, Palaiseau, France) spectrometer. For the characterization, the fine powder of nanoparticles was analyzed using FTIR (in the range of 500-4000 cm −1 ) to study the biomolecules present as capping agents on silver NPs surface.

Antioxidant activity of PE and AgNPs was calculated following the method used by Singh et al. (2021) with slight modification [17] . In brief, different concentrations of PE and AgNPs (5%, 10%, 15%, 20%, 25%, 30%, 35% and 40%) were mixed well with freshly prepared DPPH (1 mL, 0.004% in absolute methanol) solution. This reaction mixture was incubated at room temperature for 30 min in dark. DPPH solution was used as control and ascorbic acid was used as standard. The absorbance was recorded at 517 nm using UV-vis spectrophotometer (Thermo-Scientific Evolution-201). The antioxidant activity was expressed as the percentage of inhibition, which was calculated using the following formula:

Percentage of antioxidant activity = Ac − As Ac × 100 (1) where Ac is the absorbance of control and As is the absorption of experimental sample.

The antibacterial activity of extract, AgNO 3 and AgNPs synthesized at 25 • C was evaluated using disc diffusion method against Morganella spp., Salmonella typhimurium, Enterobacter faecalis, Citrobacter spp. and Gonococci spp. [46] . Pure young cultures of bacteria were obtained by sub-culturing bacterial species on MHA (Mueller-Hinton agar) medium. The agar plates were swabbed using swab stick with bacterial suspension (0.5 McFarland's). The extract, AgNO 3 and AgNPs solutions (5 µL of each) were dropped on sterile discs (5 mm). AgNO 3 was used as a control. These cultured plates were incubated at 37 • C in the incubator (Heratherm Compact Thermo Scientific, Illkirch, France) for 24 h. The inhibition zone (around the disc, mm) was measured using ordinary scale.

The experiments were performed in triplicate. The statistical analysis was performed using XL-stat_2018 (Addinsoft, Paris, France).

In order to confirm experimental results, we employed computer-aided molecular dynamics simulations to obtain the atomistic structure of AgNPs and its XRD spectra profile. To build the AgNP, we employed a melt-and-quench protocol that showed good performance in the description of bulk materials [47, 48] . The starting system is made up of 4000 randomly displaced Ag atoms inside a cubic box with 15 nm in size. The system is heated up to 2500 K in order to obtain a liquid system that completely loses the memory of the initial state. The liquid phase is maintained for 10 ns. Then, the system is gradually cooled down to 300 K with a cooling rate of 5 K/ps, which is a good compromise between accuracy and a quite low computational cost [48] . In the last step, the system is simulated at the constant temperature of 300 K for 10 ns in order to let the system be rearranged at ambient temperature. AgNP representations in the liquid and solid state are reported in Figure 2 . This approach is different from the experimental approach, which is computationally too heavy to simulate, whereas the melt-and-quench protocol gives a realistic description of the AgNP structure and of several other systems [47, 49, 50] . The force field employed to simulate the AgNP formation is based on the embedded-atom model (EAM) obtained from the work of Kang et al. [50] for Ag and Cu bulk systems. This AgNP preparation had an approximate diameter of 4.5 nm with a spherical shape, which indicated that it was a good model to accurately describe the AgNP atomistic structure and its interactions with the molecules in the plant extract. force field employed to simulate the AgNP formation is based on the embedded-atom model (EAM) obtained from the work of Kang et al. [50] for Ag and Cu bulk systems. This AgNP preparation had an approximate diameter of 4.5 nm with a spherical shape, which indicated that it was a good model to accurately describe the AgNP atomistic structure and its interactions with the molecules in the plant extract. To load the AgNP with the molecules commonly found in the plant extract of C. guianensis, we chose five molecules whose atomistic structures are reported in Figure 2 : Couroupitine A, indigo, idirubin, nerol and isatin [51] . The structure of the AgNP obtained in the first step was inserted into the center of an empty cubic box that was 9 nm in size. Then, 30 replicas of each molecule were randomly inserted into the simulation box, ensuring that they were not in contact with the AgNP. The obtained box was then filled with SPC water [52] . The system was simulated at 300 K for 100 ns while the Ag atoms positions were kept frozen, as was carried out previously [51] [52] [53] [54] . The Gromos 54a7 force field was employed for the simulation of the adsorption of molecules over the AgNP surface [55] [56] [57] . The parameters for the molecules were retrieved from the Automated Topology Builder (ATB) [58] and the parameters for the AgNP were obtained from the work of Heinz et al. [59] . The combination of these parameters has already been employed with good results for Au and Ag NPs [51] [52] [53] [54] 60] . All simulations were performed with the LAMMPS package [61] and the timestep used was 0.1 fs. The temperature was controlled using a Nose-Hoover thermostat with a coupling time of 10 fs.

To simulate the interactions of the loaded AgNP with the C. guianensis molecules with the S. typhimurium bacteria, we built a simulation box containing the ST50 outer membrane protein of S. typhimurium and the loaded AgNP, placing it over the extracellular domain, as shown in Figure 2E . The atomistic structure of the ST50 outer membrane protein of S. typhimurium was retrieved from the PDB [62] (ID: 5BUN) [63] . The simulation was performed with the same parameters employed to load the AGNP with the plant extract molecules, without any bias that drives the interactions between the AgNP and the ST50 protein.

The XRD pattern was computed using the PLUMED package [64] and XRD script developed by Lodesani et al. [65] . To load the AgNP with the molecules commonly found in the plant extract of C. guianensis, we chose five molecules whose atomistic structures are reported in Figure 2 : Couroupitine A, indigo, idirubin, nerol and isatin [51] . The structure of the AgNP obtained in the first step was inserted into the center of an empty cubic box that was 9 nm in size. Then, 30 replicas of each molecule were randomly inserted into the simulation box, ensuring that they were not in contact with the AgNP. The obtained box was then filled with SPC water [52] . The system was simulated at 300 K for 100 ns while the Ag atoms positions were kept frozen, as was carried out previously [51] [52] [53] [54] . The Gromos 54a7 force field was employed for the simulation of the adsorption of molecules over the AgNP surface [55] [56] [57] . The parameters for the molecules were retrieved from the Automated Topology Builder (ATB) [58] and the parameters for the AgNP were obtained from the work of Heinz et al. [59] . The combination of these parameters has already been employed with good results for Au and Ag NPs [51] [52] [53] [54] 60] . All simulations were performed with the LAMMPS package [61] and the timestep used was 0.1 fs. The temperature was controlled using a Nose-Hoover thermostat with a coupling time of 10 fs.

To simulate the interactions of the loaded AgNP with the C. guianensis molecules with the S. typhimurium bacteria, we built a simulation box containing the ST50 outer membrane protein of S. typhimurium and the loaded AgNP, placing it over the extracellular domain, as shown in Figure 2E . The atomistic structure of the ST50 outer membrane protein of S. typhimurium was retrieved from the PDB [62] (ID: 5BUN) [63] . The simulation was performed with the same parameters employed to load the AGNP with the plant extract molecules, without any bias that drives the interactions between the AgNP and the ST50 protein.

The XRD pattern was computed using the PLUMED package [64] and XRD script developed by Lodesani et al. [65] .

The results showed the successful formation of AgNPs from the flower extract of C. guianensis. The formation of AgNPs was confirmed through the following observations:

The formation of AgNPs began just after mixing the flower extract into the AgNO 3 solution (1 mM). After the addition of extracts, the AgNO 3 began changing its color from colorless to yellowish brown in approximately 10-15 min, and, finally, the solution turned from a light brown to dark brown color in approximately 40-45 min at room temperature. A yellowish color appeared in 5-10 min and a dark brown color appeared within 30 min at a high temperature (60 • C). Color changes were more intense at the higher temperature than at room temperature ( Figure 3 ). The pH value of AgNPs was measured to be 7.5 and 7.1 at 25 • C and 60 • C, respectively. The results obtained from the MDS showed that the bare AgNP in the solid phase assumed a spherical shape, with an internal and surface atom geometry consisting of well-ordered structures, such as the (111), (200) 

The results showed the successful formation of AgNPs from the flower extract of C. guianensis. The formation of AgNPs was confirmed through the following observations:

The formation of AgNPs began just after mixing the flower extract into the AgNO3 solution (1 mM). After the addition of extracts, the AgNO3 began changing its color from colorless to yellowish brown in approximately 10-15 min, and, finally, the solution turned from a light brown to dark brown color in approximately 40-45 min at room temperature. A yellowish color appeared in 5-10 min and a dark brown color appeared within 30 min at a high temperature (60 °C). Color changes were more intense at the higher temperature than at room temperature ( Figure 3 ). The pH value of AgNPs was measured to be 7.5 and 7.1 at 25 °C and 60 °C, respectively. The results obtained from the MDS showed that the bare AgNP in the solid phase assumed a spherical shape, with an internal and surface atom geometry consisting of well-ordered structures, such as the (111), (200) and (220). 

A UV-visible spectral analysis of the mixed solution (flower extract and AgNO3) was also performed to confirm the formation of AgNPs. The characteristic surface plasmon resonance (SPR) absorption band of biosynthesized AgNPs was obtained as 432 nm and 444 nm for the reaction carried out at 60 °C and 25 °C, respectively ( Figure 3 ).

XRD analysis was also performed to observe the formation of AgNPs. The outcome of the XRD analysis of the NPs showed strong peaks corresponding to (111) 

A UV-visible spectral analysis of the mixed solution (flower extract and AgNO 3 ) was also performed to confirm the formation of AgNPs. The characteristic surface plasmon resonance (SPR) absorption band of biosynthesized AgNPs was obtained as 432 nm and 444 nm for the reaction carried out at 60 • C and 25 • C, respectively (Figure 3 ). Figure 4D demonstrates the XRD spectrum obtained from the MDS for the liquid AgNP, solid AgNP, the molecules in the solution without the AgNP and the molecules adsorbed on the AgNP. By a visual inspection of the computer simulation results, AgNPs in the liquid phase were completely disordered, as confirmed by the XRD spectra of Figure 4D . When the system was cooled down to 25 °C, the AgNPs assumed a spherical shape while maintaining a crystalline order. It was interesting to note that the AgNPs exhibited a marked peak at 2θ = 38, which is consistent with the (111) geometry that has been visually observed from MD simulations and found by XRD experiments. This main peak was characterized by a very steep slope at 2θ = 35, corresponding to the (111) surface, and a broader shoulder at 2θ = 42, which was associated with the (200) structures, as observed in Figure 4C . The XRD spectrum obtained from the MDS was not as accurate as that experimentally obtained, due to the small size of the system being taken into account, and the broadening observed is related to the two peaks that are close to each other. Moreover, the peak at 2θ = 65 was found to correspond to the (220) surface, confirming the experimental finding that the green synthesized AgNPs assumed a crystal-like structure.

The AgNPs covered by molecules showed a similar XRD spectra with respect to the base AgNPs, but the main peak at 2θ = 38 was lower, with the shoulder at 2θ = 42 more pronounced, as experimentally observed in the FT-IR analysis of AgNPs.

FT-IR studies of AgNPs were carried out to recognize the possible biomolecules responsible for the reduction of the Ag+ ions and the capping of the bioreduced AgNPs biosynthesized by C. guianensis flower extracts. The FT-IR spectrum of AgNPs synthesized at 25 °C is presented in Figure 5 . Various peaks of FT-IR represent different functional groups. Biosynthesized AgNPs have shown absorption peaks in regions that are already related to the presence of polyphenols capped by AgNPs [10] . The FT-IR spectra had major vibration modes at 677, 1043, 1111, 1377, 1631, 2140, 2349, 2866 and 2935. All of these spectra signified different functional groups. The results of the FT-IR analysis suggested the existence of different groups of various secondary metabolites. Figure 4D demonstrates the XRD spectrum obtained from the MDS for the liquid AgNP, solid AgNP, the molecules in the solution without the AgNP and the molecules adsorbed on the AgNP. By a visual inspection of the computer simulation results, AgNPs in the liquid phase were completely disordered, as confirmed by the XRD spectra of Figure 4D . When the system was cooled down to 25 • C, the AgNPs assumed a spherical shape while maintaining a crystalline order. It was interesting to note that the AgNPs exhibited a marked peak at 2θ = 38, which is consistent with the (111) geometry that has been visually observed from MD simulations and found by XRD experiments. This main peak was characterized by a very steep slope at 2θ = 35, corresponding to the (111) surface, and a broader shoulder at 2θ = 42, which was associated with the (200) structures, as observed in Figure 4C . The XRD spectrum obtained from the MDS was not as accurate as that experimentally obtained, due to the small size of the system being taken into account, and the broadening observed is related to the two peaks that are close to each other. Moreover, the peak at 2θ = 65 was found to correspond to the (220) surface, confirming the experimental finding that the green synthesized AgNPs assumed a crystal-like structure.

The AgNPs covered by molecules showed a similar XRD spectra with respect to the base AgNPs, but the main peak at 2θ = 38 was lower, with the shoulder at 2θ = 42 more pronounced, as experimentally observed in the FT-IR analysis of AgNPs.

FT-IR studies of AgNPs were carried out to recognize the possible biomolecules responsible for the reduction of the Ag+ ions and the capping of the bioreduced AgNPs biosynthesized by C. guianensis flower extracts. The FT-IR spectrum of AgNPs synthesized at 25 • C is presented in Figure 5 . Various peaks of FT-IR represent different functional groups. Biosynthesized AgNPs have shown absorption peaks in regions that are already related to the presence of polyphenols capped by AgNPs [10] . The FT-IR spectra had major vibration modes at 677, 1043, 1111, 1377, 1631, 2140, 2349, 2866 and 2935. All of these spectra signified different functional groups. The results of the FT-IR analysis suggested the existence of different groups of various secondary metabolites. 

The results of the antioxidant assay showed a significant free radical scavenging activity of PE and AgNPs. AgNPs exhibited a higher antioxidant potential when compared to the antioxidant potential of the flower extract. The antioxidant activity of AgNPs increased from 5-20% of concentrations, whereas the antioxidant activity increased from 5-25% in the case of the flower extract. The maximum antioxidant activity (70.35%) was observed in NPs, whereas, in the case of the flower extract, the maximum antioxidant activity was 28.50% (Table 1) . After 20% of the sample concentration, the antioxidant activity begins to decrease with high concentrations in AgNPs, and begins to decrease after 25% in the plant extract sample.

For comparison, the antioxidant activity acquired for AgNO3 (5%) was 34.81 ± 0.50%, whereas the antioxidant activity of the standard antioxidant butylated hydroxyanisole (BHA, 50 µM) was 68.12 ± 1.27%, which was slightly lower than that obtained using 20% of AgNPs. 

The results of the antioxidant assay showed a significant free radical scavenging activity of PE and AgNPs. AgNPs exhibited a higher antioxidant potential when compared to the antioxidant potential of the flower extract. The antioxidant activity of AgNPs increased from 5-20% of concentrations, whereas the antioxidant activity increased from 5-25% in the case of the flower extract. The maximum antioxidant activity (70.35%) was observed in NPs, whereas, in the case of the flower extract, the maximum antioxidant activity was 28.50% (Table 1) . After 20% of the sample concentration, the antioxidant activity begins to decrease with high concentrations in AgNPs, and begins to decrease after 25% in the plant extract sample. For comparison, the antioxidant activity acquired for AgNO 3 (5%) was 34.81 ± 0.50%, whereas the antioxidant activity of the standard antioxidant butylated hydroxyanisole (BHA, 50 µM) was 68.12 ± 1.27%, which was slightly lower than that obtained using 20% of AgNPs.

A significant bacterial growth inhibition activity was observed from the AgNPs. A higher bacterial growth inhibition was observed from the AgNPs when compared to the plant extract (PE) and AgNO 3 ( Table 2 and Figure 6 ). The maximum growth inhibition was observed against S. typhimurium (16.86 mm) . Similar values of the growth inhibition zone have been observed for Escherichia coli (7.5 mm) and Bacillus subtilis (7 mm) for citrate-synthesized AgNPs [32, 33] . 

A significant bacterial growth inhibition activity was observed from the AgNPs. A higher bacterial growth inhibition was observed from the AgNPs when compared to the plant extract (PE) and AgNO3 (Table 2 and Figure 6 ). The maximum growth inhibition was observed against S. typhimurium (16.86 mm) . Similar values of the growth inhibition zone have been observed for Escherichia coli (7.5 mm) and Bacillus subtilis (7 mm) for citrate-synthesized AgNPs [32, 33] . To understand the interaction between the loaded AgNP and the S. typhimurium bacteria, we simulated the ST50 outer membrane protein, which was a channel protein for S. typhimurium. This protein contained an outer membrane (OM) domain with a β-barrel shape with three extracellular loops that open to create a flux from the periplasma to the extracellular medium [63] . We observed that these three loops fluctuated before the binding with the AgNP and exhibited a flexible structure, as shown in Figure 7 . When the AgNP interacted with the ST50 OM domain, two of the three loops in contact with the NP assumed a closed conformation, and they remained in that closed position due to the binding of the AgNP, which prevented them from opening by closing the gate. To understand the interaction between the loaded AgNP and the S. typhimurium bacteria, we simulated the ST50 outer membrane protein, which was a channel protein for S. typhimurium. This protein contained an outer membrane (OM) domain with a β-barrel shape with three extracellular loops that open to create a flux from the periplasma to the extracellular medium [63] . We observed that these three loops fluctuated before the binding with the AgNP and exhibited a flexible structure, as shown in Figure 7 . When the AgNP interacted with the ST50 OM domain, two of the three loops in contact with the NP assumed a closed conformation, and they remained in that closed position due to the binding of the AgNP, which prevented them from opening by closing the gate. 

Color changes in the reaction mixture (AgNO3 solution + PE) confirmed the synthesis of nanoparticles [10, 17] . The color of the reaction mixture solution changed from colorless to yellowish, then to yellowish brown and finally to dark brown. The synthesis of AgNPs at room temperature takes more time when compared to the 60 °C [17] , which may be due to the high temperature that speeds up the process. Some previous reports have explained that color changes in the solution showed the presence of AgNPs due to the excitation of surface plasmon vibrations [32, 33, 66] . A smaller size of NPs was achieved due to the rapid consumption of the reactants [67] . For the synthesis of AgNPs, the flower extracts of C. guianensis acted as a reductant for AgNO3, and, finally, AgNPs synthesis took place. The characteristic absorption spectrum from the UV-Vis spectrum analysis also confirmed the synthesis of AgNPs. The metal nanoparticles, such as silver, have free electrons, which contribute to the SPR absorption band [68] . A higher absorbance peak was obtained from AgNPs formed at 60 °C, which showed that a higher number of nanoparticles were synthesized at 60 °C. Similar UV-Vis absorption spectrum investigations have also been reported by several researchers [16, 17, 32, 33, 36] and the broadening of Bragg's peaks also confirmed the nanoparticles synthesis. From the XRD study, both types of AgNPs (synthesized at 20 °C and 60 °C) showed an almost equal broadening of Bragg's peaks, revealing that an almost equal size of nanoparticles is present in both solutions. Similar results of XRD spectrum patterns have been reported by many researchers [10, 13, 17, 32, 33] . The XRD peaks were very strong and indicated that the AgNPs were synthesized in a nano-regime with a crystalline nature, where the surfaces have a predominant (111) structure, as also confirmed by the MDS analysis. A similar pattern of XRD peaks was also reported when using other plants [69, 70] . Kumar et al. [42] synthesized AgNPs with a size of 17 nm using the C. guianensis flower buds extract. Their findings suggested that the XRD spectrum contained more peaks that belonged to several crystallographic planes. This indicates that our AgNPs were more uniform from a structural point of view and suggests that smaller AgNPs synthesized with C. guianensis extracts have a higher degree of crystallinity with respect to bigger ones.

The FT-IR spectrum showed the presence of various functional groups and also exposed the existence of various phytochemicals in the flower extracts. A similar pattern of vibration bands has been reported in other plants [17, 18, 70, 71] . The FT-IR spectrum band at 677, 1111 cm −1 represents the vibration of C=C alkenes and the presence of the methoxy group (-OCH3). The band at 1043 cm −1 was assigned for the C-N (amines) stretch vibration of the proteins. The band at 1377 cm −1 represents the N=O symmetry stretching, which is typical of the nitro compound. The band at 1631 cm −1 relates to C-N and C-C stretching, indicating the presence of proteins. The spectrum peaks of 2140 and 2349 

Color changes in the reaction mixture (AgNO 3 solution + PE) confirmed the synthesis of nanoparticles [10, 17] . The color of the reaction mixture solution changed from colorless to yellowish, then to yellowish brown and finally to dark brown. The synthesis of AgNPs at room temperature takes more time when compared to the 60 • C [17] , which may be due to the high temperature that speeds up the process. Some previous reports have explained that color changes in the solution showed the presence of AgNPs due to the excitation of surface plasmon vibrations [32, 33, 66] . A smaller size of NPs was achieved due to the rapid consumption of the reactants [67] . For the synthesis of AgNPs, the flower extracts of C. guianensis acted as a reductant for AgNO 3 , and, finally, AgNPs synthesis took place. The characteristic absorption spectrum from the UV-Vis spectrum analysis also confirmed the synthesis of AgNPs. The metal nanoparticles, such as silver, have free electrons, which contribute to the SPR absorption band [68] . A higher absorbance peak was obtained from AgNPs formed at 60 • C, which showed that a higher number of nanoparticles were synthesized at 60 • C. Similar UV-Vis absorption spectrum investigations have also been reported by several researchers [16, 17, 32, 33, 36] and the broadening of Bragg's peaks also confirmed the nanoparticles synthesis. From the XRD study, both types of AgNPs (synthesized at 20 • C and 60 • C) showed an almost equal broadening of Bragg's peaks, revealing that an almost equal size of nanoparticles is present in both solutions. Similar results of XRD spectrum patterns have been reported by many researchers [10, 13, 17, 32, 33] . The XRD peaks were very strong and indicated that the AgNPs were synthesized in a nanoregime with a crystalline nature, where the surfaces have a predominant (111) structure, as also confirmed by the MDS analysis. A similar pattern of XRD peaks was also reported when using other plants [69, 70] . Kumar et al. [42] synthesized AgNPs with a size of 17 nm using the C. guianensis flower buds extract. Their findings suggested that the XRD spectrum contained more peaks that belonged to several crystallographic planes. This indicates that our AgNPs were more uniform from a structural point of view and suggests that smaller AgNPs synthesized with C. guianensis extracts have a higher degree of crystallinity with respect to bigger ones.

The FT-IR spectrum showed the presence of various functional groups and also exposed the existence of various phytochemicals in the flower extracts. A similar pattern of vibration bands has been reported in other plants [17, 18, 70, 71] . The FT-IR spectrum band at 677, 1111 cm −1 represents the vibration of C=C alkenes and the presence of the methoxy group (-OCH 3 ). The band at 1043 cm −1 was assigned for the C-N (amines) stretch vibration of the proteins. The band at 1377 cm −1 represents the N=O symmetry stretching, which is typical of the nitro compound. The band at 1631 cm −1 relates to C-N and C-C stretching, indicating the presence of proteins. The spectrum peaks of 2140 and 2349 proved the presence of alkynes N=C=O and O=C=O, respectively. The vibration bands of 2935 and 2866 have shown the presence of a -C-H-stretching of aromatic rings and the C-O group, respectively. Most of the vibration bands were similar to those in previous reports [17, 18, 70, 71] . The results of the FT-IR study proved the presence of various phytochemical groups in C. guianensis flower extracts. The presence of various characteristic functional groups may be responsible for the medicinal properties of C. guianensis.

C. guianensis is an important medicinal plant that is traditionally used for the treatment of various diseases due to its antioxidant and antimicrobial activities [34, 72] . Here, we decided to reconsider the traditional uses of the C. guianensis flower extract by using it for the green biosynthesis of AgNPs for evaluating their antioxidant and antimicrobial activities. Previous works of Khatoon et al. [32, 33] showed that both Ag and Au NPs obtained from trisodium citrates as reducing agents have a good antimicrobial activity against bacteria and fungal cells. They observed that the citrate-synthesized AgNPs and AuNPs have an inhibition zone from 4 mm to 8 mm depending on the bacterial strain and on the method employed to produce the NPs [32, 33] , and their values are in good agreement with our results when using AgNO 3 . After the synthesis with the flower extract, a higher antioxidant activity was observed from our biosynthesized AgNPs due to the mixed potential of silver and the flower extract. A DPPH radical is typically used to calculate the presence of the antioxidants of a sample/material, expressed as its percentage of free DPPH radical scavenging activity [10] . The flower extract of C. guianensis is a rich source of various phytochemicals, especially the phenolics, flavonoids and alkaloids, such as indigo, indirubin and couroupitne A [73, 74] . In the green biosynthesis method of AgNPs, flavonoids act as major capping agents that result in an increase in the antioxidant activity of AgNPs [10, 17, 75] . Our results suggest that the molecules found in the plant extract cover the AgNP surface, increasing its antibacterial activity. A high antioxidant activity of many plant-based green synthesized AgNPs has been reported by many researchers [5, 16, 17, 19] . Our AgNPs exhibited a higher bacterial growth inhibition in comparison to the plant extract and AgNO 3 against all of the selected bacteria. A similar bacterial growth inhibition was observed in the AgNPs of Carissa carandas and the plant extract of Sapinus mukorossi [17, 76] . The antibacterial activity indicated that AgNPs biosynthesized using the C. guianensis flower extract were more likely to inhibit the growth of Gram-negative bacteria, especially against S. typhi. We observed that the antibacterial activity of AgNPs was enhanced by the molecules present in the PE that cap the AgNP surface during the synthesis process [13, 23, 25] . The results suggested that the antibacterial activity of AgNPs could be caused by the destruction of the microbial cell membrane [13, 25] . We observed that loaded AgNPs could spontaneously bind to the ST50 protein of S. typhi, acting as a stopper that closes the channel. However, further studies are required to improve the antibacterial efficacy of AgNPs.

In this work, the Couroupita guianensis flower extract was successfully used for the biosynthesis of AgNPs. The formation of AgNPs was confirmed through UV-Vis spectrum analysis, FTIR analysis and XRD studies, and in conjunction with computer MDS. Green biosynthesized AgNPs have shown significant antioxidant and antibacterial activities. These AgNPs were more likely to inhibit the growth of Gram-negative bacteria, specifically against S. typhi. The antioxidant potential of these AgNPs can be used for scavenging several free radicals. However, an extensive research is required, especially in in vivo conditions, in order to find out the accurate dose and toxicity assessment of AgNPs before clinical practice of these nanoparticles. Moreover, future work may also be accompanied with the identification of end-capping phytocompounds responsible for these biological activities. 

The data presented in this study are available on request from the corresponding author.

Green Chemistry and the Health Implications of Nanoparticles

Advances in Nanomaterials as Novel Elicitors of Pharmacologically Active Plant Specialized Metabolites: Current Status and Future Outlooks

Chapter 5-Nanomaterials for cosmeceuticals: Nanomaterials-induced advancement in cosmetics, challenges, and opportunities

An Overview of the Applications of Nanomaterials and Nanodevices in the Food Industry

The Current Trends in the Green Syntheses of Titanium Oxide Nanoparticles and Their Applications

Low-Cost and Eco-Friendly Phyto-Synthesis of Silver Nanoparticles Using Cocos Nucifera Coir Extract and Its Larvicidal Activity

Synthesis and Characterization of Silver Nanoparticles Using Gmelina Asiatica Leaf Extract against Filariasis, Dengue, and Malaria Vector Mosquitoes

Formation of Colloidal Silver Nanoparticles Stabilized by Na + -Poly(Gamma-Glutamic Acid)-Silver Nitrate Complex via Chemical Reduction Process

Self-Assembly of Silver Nanoparticles in a Polymer Solvent: Formation of a Nanochain through Nanoscale Soldering

Synthesis of Bio-Mediated Silver Nanoparticles from Silybum Marianum and Their Biological and Clinical Activities

Biogenic Synthesis and Characterization of Antimicrobial and Antiparasitic Zinc Oxide (ZnO) Nanoparticles Using Aqueous Extracts of the Himalayan Columbine (Aquilegia pubiflora)

Extracellular Synthesis of Silver Nanoparticles by a Silver-Tolerant Yeast Strain MKY3

Melatonin-Enhanced Biosynthesis of Antimicrobial AgNPs by Improving the Phytochemical Reducing Potential of a Callus Culture of Ocimum basilicum L. Var. Thyrsiflora

Rapid Synthesis of Silver Nanoparticles Using Culture Supernatants of Enterobacteria: A Novel Biological Approach

The Green Synthesis, Characterization and Evaluation of the Biological Activities of Silver Nanoparticles Synthesized from Iresine Herbstii Leaf Aqueous Extracts

Antioxidant and Antibacterial Activity of Silver Nanoparticles Synthesized by Cestrum Nocturnum

Green Biosynthesis of Silver Nanoparticles Using Leaf Extract of Carissa carandas L. and Their Antioxidant and Antimicrobial Activity against Human Pathogenic Bacteria

Green Synthesis of Silver Nanoparticles from Leaf Extract of Mimusops elengi, Linn. for Enhanced Antibacterial Activity against Multi Drug Resistant Clinical Isolates

Biosynthesis of Silver Nanoparticles Using Alternanthera sessilis (Linn.) Extract and Their Antimicrobial

Green Synthesis of Silver Nanoparticles Using Azadirachta Indica Aqueous Leaf Extract

Fabrication of Alginate Fibers Loaded with Silver Nanoparticles Biosynthesized via Dolcetto Grape Leaves (Vitis vinifera Cv.): Morphological, Antimicrobial Characterization and In Vitro Release Studies

Photo-Irradiation Based Biosynthesis of Silver Nanoparticles by Using an Ever Green Shrub and Its Antibacterial Study

Biosynthesis of Silver Nanoparticles by Bamboo Leaves Extract and Their Antimicrobial Activity

Intrinsic Therapeutic Applications of Noble Metal Nanoparticles: Past, Present and Future

Plasma-Enhanced Deposition of Silver Nanoparticles onto Polymer and Metal Surfaces for the Generation of Antimicrobial Characteristics

Metal-Based Therapy in Traditional and Modern Medicine Systems

More than Just Simple Natural Antioxidants: Oxidative Stress, Aging and Age-Related Diseases. Medicines 2020

Biomedical Applications of Green Synthesized Nanoparticles

Antibiotic Resistance in Staphylococcus Aureus. Current Status and Future Prospects

Escherichia coli Virulence Factors

The Global Preclinical Antibacterial Pipeline

Comparative Study of Antifungal Activity of Silver and Gold Nanoparticles Synthesized by Facile Chemical Approach

Antibacterial and Antifungal Activity of Silver Nanospheres Synthesized by Tri-Sodium Citrate Assisted Chemical Approach

Qualitative characterization of phytochemicals and in vitro antimicrobial evaluation of leaf extract of couroupita guianensis aubl-A threatened medicinal tree

Comparative Antioxidant and Antimicrobial Studies of Cold and Hot Bark Hydromethanolic Extract of Couroupita Guianensis Aubl

Standardization and Anti Bacterial Activity of Couroupita guianensis Fruit Pulp Extract

Evaluation of the Immunomodulatory Activity of the Methanolic Extract of Couroupita Guianensis Aubl. Flowers in Rats

Free Radical Scavenging Activity and Qualitative Analysis of Polyphenols by RP-HPLC in the Flowers of Couroupita Guianensis Abul

Extraction of Indigo Dye from Couroupita Guianensisand Its Application on Cotton Fabric

Recognition of Natural Products as Potential Inhibitors of COVID-19 Main Protease (Mpro): In-Silico Evidences

Natural Product-Derived Phytochemicals as Potential Agents against Coronaviruses: A Review

Evaluation of Silver Nanoparticles Synthetic Potential of Couroupita guianensis Aubl

Green Synthesis of Silver Nanoparticles from Couroupita Guianensis Aubl. Flower Petal Extract and Its Antimicrobial Activity

Comparative Determination of Phytochemicals and Antioxidant Activity from Leaf and Fruit of Sapindus mukorrossi Gaertn-A Valuable Medicinal Tree

Determination of Nanocrystal Sizes: A Comparison of TEM, SAXS, and XRD Studies of Highly Monodisperse CoPt3 Particles

Antimicrobial Efficacy of Callus and In Vitro Leaf Extracts of Sapindus Mukorossi Gaertn

Hierarchical Short-and Medium-Range Order Structures in Amorphous GexSe1-x for Selectors Applications

Cooling Rate and Size Effects on the Medium-Range Structure of Multicomponent Oxide Glasses Simulated by Molecular Dynamics

Properties Calculations of Silica-Based Glasses by Atomistic Simulations Techniques: A Review

Atomistic Modeling of the Cu-Zr-Ag Bulk Metallic Glass System

Indigo as a Plant Growth Inhibitory Chemical from the Fruit Pulp of Couroupita guianensis Aubl

Flexible Simple Point-Charge Water Model with Improved Liquid-State Properties

Computational Insights into the Binding of Monolayer-Capped Gold Nanoparticles onto Amyloid-β Fibrils

Disclosing the Interaction of Gold Nanoparticles with Aβ(1-40) Monomers through Replica Exchange Molecular Dynamics Simulations

Atomistic Simulations of Coating of Silver Nanoparticles with Poly(Vinylpyrrolidone) Oligomers: Effect of Oligomer Chain Length

Protonation-Dependent Adsorption of Polyarginine onto Silver Nanoparticles

Definition and Testing of the GROMOS Force-Field Versions 54A7 and 54B7

An Automated Force Field Topology Builder (ATB) and Repository: Version 1.0

Accurate Simulation of Surfaces and Interfaces of Face-Centered Cubic Metals Using 12−6 and 9−6 Lennard-Jones Potentials

Computational Insight into the Interaction of Cytochrome C with Wet and PVP-Coated Ag Surfaces

Fast Parallel Algorithms for Short-Range Molecular Dynamics

The Protein Data Bank

Crystal Structure of an Antigenic Outer-Membrane Protein from Salmonella Typhi Suggests a Potential Antigenic Loop and an Efflux Mechanism

PLUMED 2: New Feathers for an Old Bird

Exploring the Crystallization Path of Lithium Disilicate through Metadynamics Simulations

Role of Halide Ions and Temperature on the Morphology of Biologically Synthesized Gold Nanotriangles

Rapid Biological Synthesis of Silver Nanoparticles Using Plant Leaf Extracts

The Effect of Gain and Absorption on Surface Plasmons in Metal Nanoparticles

Synthesis of Silver Nanoparticles Using Croton Sparsiflorus Morong Leaf Extract and Their Antibacterial and Antifungal Activities

Characterization of Silver Nanoparticles Synthesized Using Urtica dioica Linn. Leaves and Their Synergistic Effects with Antibiotics

Biosynthesis of Silver Nanoparticles Using Carissa carandas Berries and Its Potential Antibacterial Activities

A First Survey on the Medicinal Plants of the Chazuta Valley (Peruvian Amazon)

Chemical Examination of the Flowers of Couroupita guianensis Aubl

Chemical Examination of Couroupita guianensis Aubl

Nanoparticles Synthesis and Nanotechnological Applications of Sapindus Species

Free Radicals Scavenging Activity and Antimicrobial Potential of Leaf and Fruit Extracts of Sapindus mukorossi Gaertn. against Clinical Pathogen

The authors declare no conflict of interest.