key: cord-0019714-l8lipdmr authors: Jara, Nicole; Milán, Nataly S.; Rahman, Ashiqur; Mouheb, Lynda; Boffito, Daria C.; Jeffryes, Clayton; Dahoumane, Si Amar title: Photochemical Synthesis of Gold and Silver Nanoparticles—A Review date: 2021-07-29 journal: Molecules DOI: 10.3390/molecules26154585 sha: 3415b184e3d10aa4fa4df172ce362e3a2917a23c doc_id: 19714 cord_uid: l8lipdmr Nanomaterials have supported important technological advances due to their unique properties and their applicability in various fields, such as biomedicine, catalysis, environment, energy, and electronics. This has triggered a tremendous increase in their demand. In turn, materials scientists have sought facile methods to produce nanomaterials of desired features, i.e., morphology, composition, colloidal stability, and surface chemistry, as these determine the targeted application. The advent of photoprocesses has enabled the easy, fast, scalable, and cost- and energy-effective production of metallic nanoparticles of controlled properties without the use of harmful reagents or sophisticated equipment. Herein, we overview the synthesis of gold and silver nanoparticles via photochemical routes. We extensively discuss the effect of varying the experimental parameters, such as the pH, exposure time, and source of irradiation, the use or not of reductants and surfactants, reagents’ nature and concentration, on the outcomes of these noble nanoparticles, namely, their size, shape, and colloidal stability. The hypothetical mechanisms that govern these green processes are discussed whenever available. Finally, we mention their applications and insights for future developments. Nanoparticles (NPs) have unique chemical and physical properties compared to their bulk counterpart due to their high surface area and outstanding electronic, optical, magnetic, and catalytic properties, to name a few [1] [2] [3] [4] . The production of valuable nanoparticles for targeted applications is currently a fast-growing field of research [1, 5, 6] . Due to the ever-growing and sustained demand for nanomaterials, new and efficient synthesis methods are devised, including physical, chemical, and biological methods [6] [7] [8] [9] . Inorganic NPs are commonly synthesized via three different approaches [10] [11] [12] [13] . Biological methods rely on biomolecules [14] [15] [16] [17] , plants [18] , fungi [19, 20] , yeast [21] [22] [23] , algae [24] [25] [26] [27] [28] , and living cells and organisms [29, 30] to promote the synthesis of NPs [4, 31, 32] . On the other hand, physical methods often involve specialized equipment [33] [34] [35] , while chemical routes usually require numerous chemicals [36] [37] [38] [39] . To avoid using chemical compounds and generating harmful by-products, interest in developing environmentally friendly methods, such as nanoparticle photoinduced synthesis, is increasing [40] [41] [42] [43] . In addition to being easy and simple to implement, the photoinduced method is, in many ways, a green process that relies on biological extracts [44] , biomolecules [45, 46] , and restricted use of chemicals [47] as the reducing agent and/or the stabilizer rather than harmful substrates. Moreover, it diminishes or eliminates the generation of waste and hazardous by-products [42, 48, 49] . Depending on the starting material, the photoinduced synthesis can be classified as photophysical if a bulk material is downsized to nanomaterials (top-down pathway) or photochemical when atoms and molecules are assembled to build up the nanoparticles (bottom-up pathway) [42, [49] [50] [51] [52] , as indicated in Figure 1 . The photochemical synthesis method has comparative advantages, such as rigorous irradiation control, room temperature operation, simple and inexpensive equipment, and does not require highly skilled personnel [40, [53] [54] [55] [56] . Nanoparticle use in various fields has gained steady, growing attention, and metallic nanoparticles are no exception [57] [58] [59] [60] . Metallic nanoparticles have a diameter between 1to a few hundred nanometers [61] and exhibit outstanding electronic, optical [62] , and physicochemical [3] properties that are unique from their bulk crystal form [61, 63, 64] . In the past decades, silver NPs (Ag NPs) and gold NPs (Au NPs) have been extensively studied [65] . They have size-and shape-dependent properties that enable their application in numerous biological and biomedical areas [66] [67] [68] [69] , such as biosensing [70] , drug delivery [71, 72] , medical imaging [65] , and pharmaceutics [73] . Due to their antimicrobial activity [57] , they are also exploited in wound dressing and healing [74] . Au NPs have superior surface plasmon resonance (SPR) properties [11] , versatile surface bioconjugation [75, 76] , high electron conductivity [1] , high colloidal stability [65] , and low toxicity [72, 77] . Likewise, Ag NPs possess unique SPR band [78] , optical properties [79, 80] , good electrical conductivity, chemical stability, and catalytic properties [81] in addition to excellent antibacterial activity [82, 83] . Over the years, Au NPs and Ag NPs have gained increasing importance and shown remarkable, versatile bioapplications. This review provides the readership an overview of the principal studies portraying the photochemical synthesis of Au NPs and Ag NPs using ultraviolet and visible light in addition to hypothetical mechanistic aspects, specific applications, and future developments. Photochemical processes have gained significant attention in the fabrication of metallic NPs due to the enhanced spatial and temporal control these techniques offer [49, 84] . A typical experiment exposes solutions containing the metal precursors to visible or ultraviolet (UV) light. Compared to other methods, such as chemical methods, photochemical routes in nanotechnology are advantageous as they avoid the use of toxic or harmful compounds, do not rely on expensive instrumentation or highly skilled personnel, and, most importantly, can be carried out at ambient conditions, i.e., room temperature and atmospheric pressure [40, 54, 56] . The fabrication of metallic NPs in solution uses several initial reagents, such as the metal precursor (salt or complex), reducing agent, and sometimes, stabilizing agent [85, 86] . The photochemical process begins with the reduction of the metal precursor, from n + valence (M n+ ) to its zero-valence state (M 0 ) by the photocatalyzed action of the reducing agent [49, 87] . The M 0 form nucleation centers or nuclei that subsequently grow and aggregate to give rise to metallic NPs [88] . Stabilizers and capping agents are of utmost importance since they are used to control the formation of homogenous metallic NPs of desired size and shape [89, 90] , prevent their agglomeration, and improve their colloidal stability [91] [92] [93] [94] . Among the capping agents, polymers are excellent for trapping and protecting the NPs against their oxidation and coalescence [66, 95] . Moreover, the different chemical structures of the polymers enable specific interactions with the metallic surface, triggering significant variations in the size and shape of the obtained metallic NPs [66] . Some studies have detailed the impact of various polymers on the characteristics of Ag NPs and Au NPs, such as poly(vinyl pyrrolidone) (PVP) [2, 96, 97] , polymethacrylate (PMA) [98] , poly-, mono-saccharides and proteins (chitosan, glucose, dextrose, gelatin) [41, 89, 94, 96] , sodium dodecyl sulfate (SDS) [99] , and natural rubber (NR) latex [66] . Additionally, the experimental parameters determine the NP features and morphology, namely, the use and nature of the stabilizers, pH of the reaction medium, precursor concentration, exposure time, and, importantly, light source and wavelength [100, 101] . Ultraviolet radiation is located between visible light and ionizing radiation. Its wavelength ranges from 100 nm to 400 nm and can be divided into three groups: UV-A (315-400 nm), UV-B (290-315 nm), and UV-C (100-290 nm) [2, 102] . As the energy is inversely proportional to the wavelength, UV-C radiation possesses the highest energy and can cause irreversible cell damage [102] . The use of a photosensitizer enhances light absorption by the reaction medium. UV light directed to photosensitizers in appropriate solvents generates radicals that are involved in the M n+ reduction process and subsequent formation of metallic NPs. The ketone family is, by far, the most frequently used photosensitizers in the synthesis of metallic NPs [49] . Under UV irradiation, ketones form ketyl radicals that act as reducing species. For instance, benzoin is a ketone that produces ketyl radicals by photolysis. A Norrish type 1 cut (α-cleavage) occurs in the benzoin, generating short-lived triplet ketyl radicals that concomitantly trigger the reduction of cationic noble metal precursor because of radical quenching. This efficiently converts metal ions into metallic NPs [7, 103] . UV irradiation sources are mercury lamps and UV light emitting diode (LED) mounted in photoreactors [95] . Under UV irradiation, the experimental parameters, such as the pH solution, illumination time, and reagents' concentration, impact the size and the shape of synthesized metallic NPs [91, 104] . For example, Gabriel et al. performed the synthesis of spherical Ag NPs on a chitosan/clay nanocomposite, using different concentrations of chitosan as the stabilizing agent [41] . At a low clay content, NPs of a more uniform size (2.7-6.3 nm) are obtained, while, at higher ones, aggregates and NPs of wider size distribution (2-20 nm) are obtained, but are formed faster. The UV photochemical synthesis of Au NPs is characterized by: (1) the use of lightabsorbing solutes and reagents is not always necessary, (2) the reduction of metal ions may occur without reducing agents, and (3) the photon-mediated generation of reducing equivalents is usually well-defined, giving a constant and predictable reduction rate. Furthermore, it does not require sophisticated instruments, making it a practical and low-cost method. Only a UV lamp is needed [47] . Au NPs can be isotropic (nanospheres) or anisotropic (nanorods, nanowires, nanoshells, etc.). Au nanospheres are characterized by the presence of a single SPR band whose maxi-mum is located at~520 nm while their nanorod counterpart exhibits two SPR absorption bands: the transversal mode (~520 nm) and the longitudinal mode whose position depends on their aspect ratio, that is, the ratio between their length to their width [46, [105] [106] [107] . During the synthesis of Au NPs, the morphology is primarily controlled by the pH of the reaction medium, precursor concentration, surfactant type, and irradiation time [46, 107] . To evaluate the pH influence on the formation of Au NPs, Rodriguez et al. used a UV lamp (256 nm) at various pH values and many reagents, such as the precursor (tetrachloroauric acid, HAuCl 4 ; silver nitrate, AgNO 3 ), cationic surfactant (hexadecyltrimethylammonium bromide, CTAB), acids (ascorbic and hydrochloric acids), base (ammonium hydroxide), acetone, and cyclohexane [107] . As a result, Au nanospheres predominate in basic solutions (pH = 9) and their UV-Vis spectrum presents one SPR band (515 nm). However, Au nanorods that display two SPR bands ( Figure 2A ) form in acidic solutions (pH = 3 or 5). Similar observations were made by Cheng et al. [108] . Au nanorods are formed at low pH, while the NPs become more spherical as the pH increases ( Figure 2B ). Following a similar methodology, Unal et al. screened the pH effect on the Au NP size using red cabbage extract, a renewable feedstock, as both the stabilizer and reducing agent. A pH of 2.5 yielded aggregated NPs of 5-70 nm in size while a pH of 11 produced stable, uniform NPs of 18-30 nm in size [109] . This is mainly due to the rapid nucleation occurring at basic pH yielding the isotropic growth of smaller nanostructures, while the acidic pH causes the nuclei to grow anisotropically [107] . These results highlight the importance of the pH reaction medium in controlling the NP size and shape. Tetrachloroauric acid (HAuCl 4 ) is the most used gold precursor [84] . The shape of Au NPs is sensitive to the precursor concentration; in addition, the presence of silver nitrate favors the formation of anisotropic NPs since silver ions are directly related to the appearance of the longitudinal SPR band. For instance, Sanabria-Cala et al. studied the influence of HAuCl 4 and AgNO 3 concentrations on Au NP morphologies using a 256 nm wavelength UV lamp and the cationic surfactant CTAB [110] . The results highlighted that (i) an increase in HAuCl 4 concentration decreases the growth of CTAB micelles and yields spherical nanoparticles ( Figure 2C ) and (ii) an increase in the concentration of silver nitrate supports the formation of anisotropic Au nanorods. Moreover, the nanoparticles tend to form nanospheres in excess of HAuCl 4 since there is not enough CTAB to form elongated micelles to induce the formation of nanorods [107] . Many photochemical methods require reducing and stabilizing agents, such as citric acid, Triton x-100, dendrimers, trisodium citrate, and PVP, among others [111, 112] . For instance, Shiraishi et al. studied the influence of the citric acid concentration on the size of Au NPs formed under UV irradiation (254 nm) [111] . Increasing citric acid concentration increases the Au NP formation yield as depicted by the intensity of the SPR band, located at~530 nm, that goes up, indicating a fast nucleation process and, consequently, the formation of tiny Au NPs ( Figure 3 ). On the other hand, UV irradiation can also be used as the sole reducing agent without any chemical or biological reductants. To that aim, Teixeira et al. relied on 254-nm UV radiation as the light source and polyethyleneimine (PEI) as the stabilizing agent [113] . Besides a stabilizing-free experiment (the control), the concentrations of HAuCl 4 (precursor) and PEI were varied ([PEI]:[HAuCl 4 ] of 5:1, 10:1, and 20:1) to study their impact on the NP size. Similar to the results discussed by Shiraishi et al. [111] , as the stabilizer to precursor concentration ratio increases, smaller spherical Au NPs are formed. Moreover, no NPs were obtained in the absence of PEI as this reagent plays an important role in the nucleation step during the NP formation. Surfactants, which also act as stabilizing agents, play a critical role in the synthesis of Au NPs because they template and control their growth and prevent their shape and size from evolving [88, 114, 115] . There are several types of surfactants, such as the anionic ones (SDS, sodium dodecylbenzene sulfonate (SDBS), etc.), the cationic ones (dodecyltrimethylammonium bromide (DTAB), cetyltrimethylammonium bromide (CTAB), alkyltrimethylammonium bromide, etc.), and the non-ionic analogs (Triton X-100, Tween X-80, hydrogenated castor oil (HCO), etc.) [114, 116] . The surfactant nature and structure affect the NP size. For example, Shang et al. produced Au NPs from HAuCl 4 and several surfactants [117] . Their results demonstrate that the NP size can be tuned by using different surfactants. Indeed, cationic surfactants favor the formation of large-sized Au NPs owing to their positively charged head that attracts the dissociated AuCl 4 − ions, whereas anionic surfactants produce smaller Au NPs, as their negatively charged head repels the dissociated AuCl 4 − ions, allowing only reduced Au atoms to enter the micelles, resulting in smaller Au NPs. Since many reductants and stabilizers are toxic and harmful to human health and the environment, eco-friendly compounds constitute a viable alternative in the fabrication of nanomaterials. This may consist, for instance, in using extracts from plant parts (fruits, stems, leaves, etc.) as the reducing and stabilizing agents [109, 118, 119] . Yulizar et al. used Polyscias scutellaria leaf extract under UV irradiation for 2 h to synthesize stable Au NPs of 5-20 nm in diameter [119] . Additionally, these NPs exhibited interesting catalytic activity in the reduction of methylene blue (MB) in the presence of sodium borohydride (NaBH 4 ). Similarly, Babu et al. reported the synthesis of Au NPs using the ethanolic extract of Bacopa monnieri leaves (BLE) under UV irradiation for 15 min [120] . Compared to the heating route, this method formed Au NPs from 1 mM of HAuCl 4 with 4% of BLE (400 µg) and was much faster: 15 min using UV light vs. 80 min by heating. Furthermore, UV light produced smaller Au NPs (11 nm) than by heating (21 nm). The UV-mediated photochemical synthesis of Ag NPs is a well-established method. It has three main features that fit the principles of Green Chemistry: (i) water is usually the solvent, (ii) environmentally benign reducing agents are used, and (iii) non-toxic capping agents ensure NP stability [121] . Most often, the experiments are carried out at room temperature and atmospheric pressure using common lab equipment. In most cases, silver nitrate (AgNO 3 ) is used as the precursor [122] [123] [124] , while polymers and green materials are used as stabilizers and plant extracts [118] as reducing agents. The pH of the reaction medium plays an important role in controlling the size of Ag NPs [125, 126] . Thus far, the formation of Ag NPs under UV irradiation has been limited to a narrow pH range [125] . Some studies suggest that the Ag NP size tends to decrease in alkaline media due to the rapid nucleation, while acidic media results in larger Ag NPs since the reaction rate is slower [127, 128] . Furthermore, the pH affects the absorption of light and the position of the localized SPR (LSPR) band [126, 129] . Babusca et al. synthesized Ag NPs via a two-step process: the aqueous mixture of AgNO 3 and trisodium citrate was heated then irradiated using a UV-C lamp (30 W) for 45 min [126] . The two-step process promotes the efficient synthesis of Ag NPs since the reduction of silver ions is totally completed during the first step. As a result, the pH slightly increased from 5 to 6 while the SPR band maximum blue-shifted from 425 nm to 418 nm, suggesting the formation of smaller Ag NPs; this corroborates studies that reported the influence of increasing pH on the narrowing and position of the Ag NP SPR band [129, 130] . Rheima et al. irradiated an aqueous solution of glucose (C 6 H 12 O 6 ), used as both the reducing and stabilizing agent, in the presence of the precursor, silver nitrate, with a mercury UV lamp (λ = 365 nm, 125 W) for 30 min to produce highly crystalline hexagonal and spherical Ag NPs with an average size of 20 nm [131] . Besides, Valandro et al. reported the use of other substances, such as 10-oxo-10H-di benzene thiopyran-3-4-dicarboximide chitosan (TXICh) and triethanolamine (TEOH), that act as both the reducing and stabilizing agent [94] . When a UV-LED (λ = 365 nm, 92 mW cm −2 ) irradiated for 4 h an AgNO 3 solution containing only TXICh, spherical, self-assembled Ag NPs of 2-24 nm in size are obtained ( Figure 4A,B) . On the other hand, a 15-min irradiation is sufficient to obtain stable, spherical Ag NPs with an average diameter of 2.5 nm when a mixture made of both TXICh and TeOH is used ( Figure 4C,D) . TEOH is a good hydrogen donor; therefore, it shortens the reduction time by adding more free radicals to the TXLCh-containing reaction medium. In addition to green reducing agents, such as plant extracts, polymers are also widely used to synthesize Ag NPs under UV irradiation. In the presence of PVP, known to be a good protective agent and NP aggregation inhibitor, Radoń and Łukowiec irradiated AgNO 3 solution using UV light (λ = 365 nm) for 10 min [132] . When PVP was the reducing agent, the produced Ag NPs were cubes, rods, and spheres with an average size of 50.3 ± 27.5 nm. However, using chloramine T (Cl-T) as the reducing agent at a concentration of 0.25 g L −1 resulted in unstable and irregular Ag NPs with a mean size of 11.7 ± 7.2 nm. As Cl-T concentration increases, large and stable Ag NPs are formed. Finally, the Ag NPs ability to reduce methylene blue as a function of the reducing agent was investigated. Cl-T-synthesized Ag NPs were found to be the best catalyst with a first-order rate constant over catalyst mass (K = k/m) of 8.34 g −1 s −1 vs. 6.3 g −1 s −1 for PVP. Various studies showed that a reducing agent is not always required for the UVmediated synthesis of metallic NPs. For instance, Huang and Yang used only the precursor (AgNO 3 ) and aqueous laponite as the colloidal stabilizer [133] . This solution was irradiated by 0.362 mW cm −2 of UV light for 1, 3, 18, 46, and 93 h. In the case of 3 h UV irradiation, the obtained Ag NPs were 60-110 nm nanoprisms and pentagons. The 18 h UV exposure resulted in no nanoprisms and significantly decreased mean nanocrystal size when compared to the 3 h UV irradiation. The shortest irradiation time (1 h) yielded larger Ag NPs that lacked colloidal stability. Darroudi et al. used gelatin as the green stabilizer with AgNO 3 as the precursor under UV-irradiation for 48 h [89] . The color changed from yellow to dark brown, depicting the Ag NP formation as the irradiation time increased ( Figure 5A ). The Ag NPs were analyzed by TEM and UV-Vis spectroscopy. TEM images show a mean Ag NP size of 35.82 nm at 6 h irradiation, 18.84 nm at 24 h, and 20.99 nm at 48 h ( Figure 5B ). As UV irradiation time increases, the NP size decreases. Furthermore, UV-Vis spectroscopy, used to study the NP colloidal stability, shows that 3 months after their synthesis, the Ag NPs had a slight SPR red shift and absorbance decrease, highlighting their long-term stability ( Figure 5C ). Over the last 2 decades, the photochemical synthesis of bimetallic silver-gold NPs has witnessed limited developments when compared to their monometallic counterparts. A few recent works rely on visible light [134, 135] , but the very vast majority of designed protocols use UV irradiation to produce bimetallic Ag-Au NPs. The photochemically produced mono-metallic NPs may serve as a template, therefore forming the core, for the growth of the other metal, forming the shell. The shell formation might happen under light (e.g., UV) irradiation [136] or simply owing to galvanic exchange [134] . These bimetallic NPs may form spheres [137] , decahedrons [134] , mixed nanostructures [138] , and nanodendrites [139] . In terms of composition, these NPs can consist of alloys [137, 140] , nanotwins [137, 141] , core-shell structures [136, [142] [143] [144] [145] [146] [147] , and hollow NPs [148] . Mallik et al. were most likely the first to describe, in 2001, the photochemical synthesis of spherical, bimetallic Au core -Ag shell NPs via a seed-mediated procedure under UV irradiation [88] . More recently, Kazancioglu et al. reported the fabrication of bimetallic Au-Ag alloy nanoparticles of less than 10 nm under UV irradiation using 2-thioxanthone thioacetic acid-dioxide as a novel photoinitiator; these hybrids possess interesting catalytic activity [140] . This work constitutes a follow-up to a previous study carried out by the same group [53] . After obtaining alginate beads modified with Ag NPs and Au NPs owing to the action of cyclic UV irradiation (10 min ON/10 min OFF for 40 min), Saha et al. achieved the deposition of gold on Ag NPs (Au@Ag NPs) and silver on Au NPs (Ag@Au NPs) [147] . These hybrids were tested for surface-enhanced Raman spectroscopy (SERS) applications. Besides, Korir et al. obtained Au-Ag nanotwins via a two-step photochemical process in the presence of 1% chitosan [141] . First, Au seeds were synthesized starting from chloro(dimethyl sulfide)gold(I) (the precursor) under a medium-pressure mercury vapor lamp (Source 1: 40-48% UV + 40-43% visible) irradiation for 60-90 min or under UVA irradiation for 6 min. Then, AgNO 3 was added, and the mixture was irradiated using Source 1 for 5-30 min. This resulted in small, isotropic Au-Ag nanotwins of~30 nm in size. To obtain anisotropic Au-Ag nanotwins bigger than 70 nm, the Au seed solution should be irradiated for 120 min. Table 1 summarizes the available precursors, reducing agents, and stabilizers used to photochemically synthesize Au NPs and Ag NPs, the NP features (size and shape), and relevant information regarding the pH and UV irradiation (time of exposure, wavelength, power, and source). Visible light is defined as the radiation that excites the human visual system. Although its spectrum ranges vary, as they depend on the amount of radiant energy that reaches the retina, 360-400 nm is considered to be the lower limit and 760-830 nm to be the upper limit. Visible light is found in greater abundance in the solar spectrum that reaches the Earth's surface, compared to UV and infrared lights [150, 151] . This light can be exploited in the photochemical processes as sunlight, artificial white light, and monochromatic light (e.g., blue light, red light, etc.). Sunlight is the largest source of renewable and clean energy; it is non-toxic and nonpolluting, and does not leave traces in chemical processes [152] . Photo-assisted synthesis is an efficient method to produce NPs, particularly in the case of solar light, which is directly exploited as it is free, non-toxic, environmentally friendly, renewable, shortens reaction time, and produces NPs with controlled and desired characteristics [87, 153, 154] . Similar to UV-initiated experimental protocols, Ag NPs and Au NPs can be synthesized using sunlight as an inducing light source [155] . For instance, Annadhasan et al. carried out the synthesis of Au NPs using sunlight and N-cholyl-I-valine (NaValC) as both the stabilizing and reducing agent at basic pH (pH = 9) [45] . Au NP formation was completed within~20 min under sunlight irradiation; a typical SPR band of spherical NPs with a maximum at~524 nm was recorded. Following a similar methodology, Pienpinijtham et al. synthesized Au NPs of different shapes (triangles, hexagons, and polygons) using starch as the reducing and stabilizing agent under sunlight irradiation for 5 days [156] . A spectrophotometric absorbance at 315 nm, which corresponds to the ion transfer from chlorine to gold in the mixture, was observed within the first day. This band disappeared over the following days and was replaced by a broad SPR band with a maximum absorbance greater than 500 nm, which indicated the formation of Au nanostructures. The same study reported that no nanostructures were formed in the absence of sunlight although, in dark, the reaction lasted 7 days; this highlights the essential role played by this irradiation in forming NPs [156] . Several manuscripts have described the synthesis of Ag NPs using sunlight. For instance, Tang et al. reported the formation of anisotropic Ag NPs using sunlight [157] . Furthermore, sunlight irradiation has been shown to promote a fast reduction process, resulting in a higher yield when compared to control experiments in the dark. Some procedures relying on sunlight can be performed without the presence of any reducing moieties [6, 45, 155, 158] . SDS is an example of a surfactant used in the synthesis of Ag NPs starting from an AgNO 3 aqueous solution under sunlight irradiation of~50.3 mW cm −2 intensity for 1 h at room temperature [155] . The Ag NP formation started soon after the experiment was launched; the first color change was observed 5 min after exposure and continued steadily. However, exposure times longer than 5 h did not bring further changes. In comparison, the control experiment in the dark did not yield any color change nor Ag NP formation, highlighting the key role played by sunlight in this process [155, 158, 159] . The literature details the synthesis of Ag NPs using plant extracts as the reducing agent, such as ginger rhizome extract, and AgNO 3 as the precursor under sunlight irradiation. Using 5 mL ginger extract (5%) in 95 mL of 1 mM AgNO 3 under sunlight exposure, a rapid color change from yellow to dark brown occurred within 2 h, indicating the formation of spherical Ag NPs [87] . This holds great promise for the large-scale synthesis of Ag NPs using a free energy source, sunlight, and minimal plant material. Besides, the synthesis of Ag NPs using Azadirachta indica leaf extract under 1 h sunlight irradiation and the effect of extract amount on Ag NP features have been reported [160, 161] . When the amount of leaf extract was 1, 2, and 3 mL, the size of the synthesized nanocrystals decreased from 107 to~89, and~76 nm, respectively [160] . This trend corroborates what was extensively reviewed in the literature [162] . Mankad et al. showed that extending the irradiation time (5, 10, 15 , and 20 min) resulted in faster processes as the color change (from yellow to reddishbrown) intensified, obtaining the smallest NP size (~68 nm) with 5 mL of leaf extract and the longest sunlight exposure [161] . The use of Piper longum catkin extract for the synthesis of Ag NPs has attracted increasing attention [163] [164] [165] . Sunlight irradiation triggers the rapid formation of 15-40 nm Ag NPs [164] . Papaya extract promotes the synthesis of Ag NPs of 35-50 nm in size when exposed to sunlight irradiation for 15 min [166] , while pomelo peel extract (PPE) yields Ag NPs of 20-30 nm in diameter when sunlight-irradiated for 30 min [158] . The authors proposed that blue light plays the main role in reducing Ag + ions by inducing the tautomerization of the flavonoids in PPE, releasing the reactive hydrogen atoms responsible for the reduction. The authors also emphasized that using sunlight resulted in faster synthesis than heating. Other studies shed light on the effects of solar irradiation intensity on Ag NP formation kinetics. For instance, Wei et al. produced Ag NPs when the reaction medium containing AgNO 3 and Bacillus amyloliquefaciens cell-free extracts were subjected to different intensities of solar irradiation (3×, 4×, 5×, and 7× 10 4 l×) for 100 min [167] . The reduction process was evidenced by the appearance of a light brown color after only 1 min, then yellow, and finally orange-red after 100 min irradiation. The Ag NP formation was confirmed using UV-Vis spectroscopy, which showed an SPR maximum at 423 nm. The obtained Ag NPs were circular and triangular and~15 nm in size regardless of the light intensity. However, the maximum SPR peak intensity increased when the light intensity increased, highlighting the direct relationship between light intensity and Ag NP formation kinetics and yield. Jia et al. irradiated an aqueous solution containing AgNO 3 , sodium citrate, and sodium borohydride with a sodium lamp (70 W, 589 nm) [168] . TEM images show the morphology changes. Before irradiation, the NPs were spherical, with a diameter of 2-15 nm. After 1 h, small triangular Ag NPs (T-Ag NPs) were visible and, after 3.5 h, truncated triangular NPs with 40-100 nm in edge length were observed. Finally, at 5 h, the NPs became more truncated and showed a disk-like shape ( Figure 6A ). Moreover, Nguyen et al. varied the pH and irradiation source during the photochemical synthesis of T-Ag NPs [169] . The results showed that the absorption peaks were between 520 nm and 580 nm at pH 11-12. On the other hand, a peak at 650 nm, characteristic of T-Ag NPs, was observed at pH 9. Besides a dark control, different irradiation sources were used, such as a sodium lamp (λ = 589 nm), a UV-C lamp (λ = 254 nm), and a solar lamp (full spectrum light) for 180 min ( Figure 6B ). In the dark or under UV light exposure, only~2 nm and~6 nm Ag NPs, respectively, were formed. Under solar lamp illumination, several morphologies were obtained with a mean size of~7 nm, while using the sodium lamp yielded T-Ag NPs of 28 nm in edge length. Rahman et al. used algal production platforms to synthesize Ag NPs facilitated by visible light [17, 30, 170] . As a result, visible light has a direct effect on the formation of Ag NPs when mediated by the extracellular polymeric substances (EPS) of the green microalga Chlamydomonas reinhardtii [17] . The light-dependent nature of this process was revealed by the acidification of the reaction media that only occurred under light irradiation. Moreover, increasing light intensity induced the pH to further decrease and the Ag NP production rate to increase. This led to a constitutive relationship between photons and Ag NP production rate. Additionally, a hypothetical biosynthesis mechanism based on light-independent adsorption of Ag + by the EPS biomolecules and photocatalytic reduction of Ag + to its metallic counterpart, i.e., Ag 0 , was proposed. It was further established that (i) the EPS could maintain their bioreductive capabilities in the dark; however, photon energy is required for their activation, and (ii) the increase in SPR band intensity of the as-produced Ag NPs is related to the light input, while the final yield is related to the EPS concentration ( Figure 7 ). Several studies have also explored the biosynthesis of Ag NPs and Au NPs under visible light exposure, especially using the photosynthetic machinery and pigments of living organisms and microbes [8, [171] [172] [173] . For instance, extracted C-phycocyanin pigment from cyanobacteria has been reported to promote the formation of Ag NPs only under light illumination [174] . Additionally, intact chloroplasts harvested from microorganisms and plants have been successfully used to synthesize Ag NPs, Au NPs, and bimetallic Ag-Au alloy NPs; however, they all require light input [175, 176] . Shabnam et al. reported that, under light irradiation, photosynthetic electron transport in the thylakoids/chloroplasts reduced Au 3+ to Au 0 to promote the formation of Au NPs [175] . The group reported 5-20 nm sized Au NPs formed via a light-driven electron transport mechanism that uses light energy to transport electrons from water molecules to different organelles within the cell [175, 176] . While the reductive capacities of chloroplasts are evidently understood, how light input affects the specific roles played by the many other green parts of organisms during the NP formation is yet to be investigated [29] . Table 2 depicts the photochemical synthesis of Ag NPs and Au NPs; it summarizes the available precursors, reducing agents, and stabilizers used, the NP features (size and shape), and relevant information regarding the pH and visible light irradiation (time of exposure, wavelength, power, and source). * When the stabilizer is the same as the reducing agent. Metallic NPs have been used in medical applications due to their versatility and unique characteristics, such as biocompatibility, colloidal stability, optical properties, straightforward surface functionalization, among others [181, 182] . Due to their large surface area, it is possible to load large amounts of drugs onto NPs to design NP-based drug delivery systems that reduce the risk of side effects, target the desired part of the body, and increase the efficiency of the drug. For instance, Au NPs have been widely used for cancer treatment [181, 182] . Similar to their analogs obtained via other approaches, photochemically produced Ag NPs and Au NPs possess useful physico-chemical and biological properties that have enabled them to be applied in countless fields, such as nanomedicine, catalysis, and environment. For instance, Dizman et al. used photochemically synthesized Au NPs to deliver doxorubicin (Dox) to treat leukemia. Using MTT assay, the authors determined that the cytotoxicity of these nanoplatforms, made of Au NPs loaded with 5 µL of Dox, was higher in the case of cancer cells when compared to normal cells, making them a potential candidate for cancer treatment [183] . Similar results were obtained by Licciardi et al. who relied on spherical Au NPs conjugated with inulin folate (INU-FA) and loaded with Dox to treat breast cancer cells [184] . The use of visible and UV light enabled size control during the synthesis of Ag NPs, promoting the formation of small-sized NPs and avoiding the formation of aggregates [41, 153] . The small size of Ag NPs makes them more effective against bacteria. The oxidation of silver atoms at the NP surface triggers the release of Ag + ions that interact with bacterial proteins and enzymes, which inactivate and interrupt the cell metabolic processes yielding the cell lysis; this effect becomes even stronger when smaller NPs are used [185] . Ag NPs present high toxicity against some bacteria, such as Escherichia coli [20, 41] and B. subtilis [65] . Therefore, these Ag NPs may be used as nano-coatings in surgical devices and implants and as antibacterial agents in wound-healing bandages. Surface-enhanced Raman spectroscopy (SERS) is a powerful technique that allows the detection of trace amounts of various substances of interest in different fields, such as medicine, chemical analysis, and environmental safety [186, 187] . Noble metallic NPs, especially those made of gold and silver, are among the best substrates for SERS [147] . For example, Xu et al. deposited Au NPs, synthesized via a photochemical process, on the surface of zinc oxide nanorods (ZnO NRs) to form ZnO@Au NRs as a substrate for SERS in the detection of methylene blue to a detection limit as low as 0.8 µg L −1 , demonstrating their potential to detect organic pollutants in wastewater [188] . Similarly, Zhou et al. used a 6-day sunlight exposure to produce Au nanosheets for SERS applications. Most importantly, they found that~50 nm is the optimal thickness of Au nanosheets for SERS applications [189] . Numerous reports describe the use of Au NPs and Ag NPs to detect and biosense viruses [190, 191] , pathogens [192] , DNA [193, 194] , pesticides [187] , and toxins [195] . Taking advantage of the good electrochemical activity of Au NPs combined with the high specific surface area of ZnO NRs, Xu et al. relied on the photochemical synthesis to develop a sensor of densely deposited Au NPs on the surface of ZnO NRs to detect nitric oxide (NO) released by human umbilical vein endothelial cells (HUVEC) [196] . For environmental detection, Çinko et al. designed, via a photochemical process, Au NPs/polymer nanocomposite films capable of detecting benzene, toluene, and xylene vapors [197] . Besides, water-stable, blue-fluorescent silver nanoclusters (Ag NCs) are used in the stable and sensitive detection of hydrogen peroxide (H 2 O 2 ) [198] . To prepare this fluorescent probe, glutathione (GSH), used as a capping agent, reacted with Ag + under UV irradiation to yield Ag NCs. As a result, a response time of 2 s is achieved in the detection of H 2 O 2 , whose monitoring is of utmost importance in biological and chemical systems. Moreover, Ag NPs produced under sunlight irradiation can be used for the colorimetric detection of Hg 2+ with a linear range of 50 nM-500 µM, where a color change of the solution from dark brown to transparent was observed [199] . In addition, the SPR band intensity confirms the high selectivity and sensitivity of these Ag NPs for Hg 2+ detection. The applicability of Au NPs and Ag NPs in different areas, such as industry, medicine, and agriculture, has triggered a great interest for researchers to devise facile and innovative methodologies for controlled, reproducible, and scalable synthesis with acute environmental concerns. In this context, light-driven routes are of choice as they take advantage of UV and visible light to provide a clean and convenient method for the efficient and rapid synthesis of Au NPs and Ag NPs. In this article, we systematically reviewed the key parameters that materials scientists have considered in implementing their experiments towards the production of these noble metal NPs. As a consequence, reagent concentrations, type of light (natural vs. artificial, UV vs. visible, polychromatic vs. monochromatic), irradiation time, the use or lack of reducing/stabilizing agents, the reaction mixture pH, etc. are crucial parameters that greatly impact the characteristics of the obtained NPs, namely, their size, shape, and colloidal stability; the latter affecting greatly the properties (optical, catalytic, biological) that determine their bio-applications, such as biocidal activity, biosensing, drug delivery nanoplatforms, and catalysis, to name the most commonly reported applications in the literature. Future work should focus on the appropriate design of experiments to investigate the effect of varying several experimental parameters on the obtained NPs. To that end, scientists may rely on well-established designs of experiments (DoE) to produce NPs of desired compositions (e.g., metallic, oxides, chalcogenides, alloys) and features. Moreover, further surface functionalization of these photochemically obtained NPs should be investigated as a milestone towards their emerging, fast-growing, and diversifying bio-applications. Finally, the scalability of these photoprocesses using photobioreactors, such as the ones used in culturing microalgae, should be thoroughly examined, as this is another key criterion in the economic viability and cost-effectiveness of these green NP production routes. Synthesis Methods, Characterization Routes and Applications towards Drugs Fabrication and characterization of colloidal silver nanoparticle via photochemical synthesis Nanoparticles: Properties, applications and toxicities Green Biological Synthesis of Nanoparticles and Their Biomedical Applications Application of nanoparticles in percutaneous delivery of active ingredients in cosmetic preparations Sunlight mediated synthesis of silver nanoparticles using redox phytoprotein and their application in catalysis and colorimetric mercury sensing Photochemical synthesis of nano-and micro-crystalline particles in aqueous solutions Species selection for the design of gold nanobioreactor by photosynthetic organisms Stoichiometrically controlled production of bimetallic Gold-Silver alloy colloids using micro-alga cultures Methods and strategies for the synthesis of diverse nanoparticles and their applications: A comprehensive overview Recent biomedical applications of gold nanoparticles: A review An Overview of the Synthesis of Gold Nanoparticles Using Radiation Technologies Silver Nanoparticles: Synthesis and Application for Nanomedicine Sugar-Mediated Green Synthesis of Silver Selenide Semiconductor Nanocrystals under Ultrasound Irradiation High conversion synthesis of <10 nm starchstabilized silver nanoparticles using microwave technology Optimized production of antibacterial copper oxide nanoparticles in a microwave-assisted synthesis reaction using response surface methodology A Mechanistic View of the Light-Induced Synthesis of Silver Nanoparticles Using Extracellular Polymeric Substances of Chlamydomonas reinhardtii A green route to synthesis silver nanoparticles using Sargassum polycystum and its antioxidant and cytotoxic effects: An in vitro analysis Endophyte fungal isolate mediated biogenic synthesis and evaluation of biomedical applications of silver nanoparticles Fungal mediated synthesis of silver nanoparticles and evaluation of antibacterial activity Biosynthesis of silver nanoparticles using Saccharomyces cerevisiae Biosynthesis of Crystalline Silver and Gold Nanoparticles by Extremophilic Yeasts Nanoparticles Biosynthesized by Fungi and Yeast: A Review of Their Preparation, Properties, and Medical Applications Noble metal, oxide and chalcogenide-based nanomaterials from scalable phototrophic culture systems Microalgae: An outstanding tool in nanotechnology Algae-mediated biosynthesis of inorganic nanomaterials as a promising route in nanobiotechnology-A review Synthesis of bioactive silver nanoparticles using alginate, fucoidan and laminaran from brown algae as a reducing and stabilizing agent Design of magnetic akaganeite-cyanobacteria hybrid biofilms In Vivo Biosynthesis of Inorganic Nanomaterials Using Eukaryotes-A Review Biosynthetic Conversion of Ag + to highly Stable Ag 0 Nanoparticles by Wild Type and Cell Wall Deficient Strains of Chlamydomonas reinhardtii Biological synthesis of metallic nanoparticles Green Synthesis of Selenium and Tellurium Nanoparticles: Current Trends, Biological Properties and Biomedical Applications Electron-beam induced synthesis of nanostructures: A review Synthesis of Nanoparticles by Laser Ablation: A Review. KONA Powder Part A Review of Carbon Nanomaterials' Synthesis via the Chemical Vapor Deposition Review of the methodologies used in the synthesis gold nanoparticles by chemical reduction The polyol process: A unique method for easy access to metal nanoparticles with tailored sizes, shapes and compositions Metal oxides nanoparticles via sol-gel method: A review on synthesis, characterization and applications Conventional and Microwave Hydrothermal Synthesis and Application of Functional Materials: A Review Photochemical Reduction as a Green Method for the Synthesis and Size Control of Silver Nanoparticles in κ-Carrageenan Photochemical synthesis of silver nanoparticles on chitosans/montmorillonite nanocomposite films and antibacterial activity Photo-induced generation of size controlled Au nanoparticles on pure siliceous ordered mesoporous silica for catalytic applications Silver nanoparticles: Various methods of synthesis, size affecting factors and their potential applications-A review Photoinduced green synthesis of silver nanoparticles with highly effective antibacterial and hydrogen peroxide sensing properties Green synthesis of gold nanoparticles under sunlight irradiation and their colorimetric detection of Ni 2+ and Co 2+ ions Light-driven formation of gold/tryptophan nanoparticles Photochemical synthesis of colloidal gold nanoparticles Photochemical synthesis: Using light to build C-C bonds under mild conditions Light as a construction tool of metal nanoparticles: Synthesis and mechanism Solar Photochemical Synthesis: From the Beginnings of Organic Photochemistry to the Solar Manufacturing of Commodity Chemicals Silver and gold nanoparticles in silica matrices: Synthesis, properties, and application Challenges and opportunities in the bottom-up mechanochemical synthesis of noble metal nanoparticles Photochemical synthesis of nanocomposite thin films containing silver and gold nanoparticles with 2-thioxanthone thioacetic acid-dioxide and their role in photocatalytic degradation of methylene blue Green chemistry approach for the synthesis of gold nanoparticles with gum kondagogu: Characterization, catalytic and antibacterial activity Photochemical Synthesis of Silver Nanodecahedrons under Blue LED Irradiation and Their SERS Activity Original photochemical synthesis of Ag nanoparticles mediated by potato starch Recent advances in gold and silver nanoparticles: Synthesis and applications Green Synthesis of Metallic Nanoparticles and Their Prospective Biotechnological Applications: An Overview Unprecedented Dual Alignment Mode and Freedericksz Transition in Planar Nematic Liquid Crystal Cells Doped with Gold Nanoclusters Advances in gold nanoparticle-liquid crystal composites Photochemistry on Nanoparticles Bimetallic Nanoparticles: Enhanced Magnetic and Optical Properties for Synthesis and reactions of functionalised gold nanoparticles Unique Roles of Gold Nanoparticles in Drug Delivery, Targeting and Imaging Applications Noble Metal Nanomaterials: Synthetic Routes, Fundamental Properties, and Promising Applications Synthesis and characterization of silver nanoparticles in natural rubber Size-dependent electronic properties of nanomaterials: How this novel class of nanodescriptors supposed to be calculated? In vitro cytotoxicity and phototoxicity of surface-modified gold nanoparticles associated with neutral red as a potential drug delivery system in phototherapy Size Correlation of Optical and Spectroscopic Properties for Gold Nanoparticles Gold and Silver Nanoparticles in Sensing and Imaging: Sensitivity of Plasmon Response to Size, Shape, and Metal Composition Nanoparticles as Dental Drug-Delivery Systems Gold nanoparticles: Preparation, properties, and applications in bionanotechnology Silver nanoparticles: Synthesis methods, bio-applications and properties Antimicrobial Silver Nanoparticles for Wound Healing Application: Progress and Future Trends Immunological properties of gold nanoparticles Nanoparticles in biomedical applications Gold nanoparticles: Interesting optical properties and recent applications in cancer diagnostics and therapy A Review of Silver Nanoparticles: Research Trends, Global Consumption, Synthesis, Properties, and Future Challenges Predicting the Size of Silver Nanoparticles from Their Optical Properties Optical Properties of Reconfigurable Polymer/Silver Nanoprism Hybrids: Tunable Color and Infrared Scattering Contrast Green synthesis of silver nanoparticles using Terminalia cuneata and its catalytic action in reduction of direct yellow-12 dye A systematic review on silver nanoparticles-induced cytotoxicity: Physicochemical properties and perspectives Silver nanoparticles as antimicrobial agent: A case study on E. coli as a model for Gram-negative bacteria Photochemical routes to silver and gold nanoparticles A Novel Photosynthesis of Carboxymethyl Starch-Stabilized Silver Nanoparticles A review on radiation-induced nucleation and growth of colloidal metallic nanoparticles Sunlight mediated rapid synthesis of small size range silver nanoparticles using Zingiber officinale rhizome extract and its antibacterial activity analysis Seed-mediated successive growth of gold particles accomplished by UV irradiation: A photochemical approach for size-controlled synthesis Fabrication and Characterization of Gelatin Stabilized Silver Nanoparticles under UV-Light Photochemical Synthesis and Multiphoton Luminescence of Monodisperse Silver Nanocrystals Photochemical synthesis of polygonal gold nanoparticles Recent trends and methodologies in gold nanoparticle synthesis-A prospective review on drug delivery aspect Methods of Gold and Silver Nanoparticles Preparation Photochemical Synthesis of Ag and Au Nanoparticles Using a Thioxanthone Substituted Chitosan as Simultaneous Photoinitiator and Stabilizer A simple method to synthesize silver nanoparticles by photo-reduction Self-organization of silver nanoparticles during synthesis of Ag-Au nanoalloy by UV irradiation method Photochemical synthesis and self-assembly of gold nanoparticles Green synthesis of silver nanoparticles for ammonia sensing Superior bactericidal activity of SDS capped silver nanoparticles: Synthesis and characterization pH-controlled growth of triangular silver nanoprisms on a large scale Manipulation of the Growth of Gold and Silver Nanomaterials on Glass by Seeding Approach Impact of Silver Nanoparticles on the Ultraviolet Radiation Direct and Bystander Effects on TK6 Cell Line Green Routes to Noble Metal Nanoparticle Synthesis UV-induced synthesis, characterization and formation mechanism of silver nanoparticles in alkalic carboxymethylated chitosan solution Photochemical synthesis: Effect of UV irradiation on gold nanorods morphology Anisotropic growth of gold clusters to gold nanocubes under UV irradiation Effect of pH and chloroauric acid concentration on the geometry of gold nanoparticles obtained by photochemical synthesis Investigation of pH Effect on Gold Nanorod Synthesis One step preparation of stable gold nanoparticle using red cabbage extracts under UV light and its catalytic activity Merchan-Arenas, D. Gold Nanoparticles Formation Mechanism by Photochemical Synthesis Photoreductive synthesis of monodispersed Au nanoparticles with citric acid as reductant and surface stabilizing reagent A Review of Stabilized Silver Nanoparticles-Synthesis, Biological Properties, Characterization, and Potential Areas of Applications Photochemically-assisted synthesis of non-toxic and biocompatible gold nanoparticles Light-controlled synthesis of gold nanoparticles using a rigid, photoresponsive surfactant Photochemical synthesis of gold nanoparticles via controlled nucleation using a bioactive molecule The sequential intercalation of three types of surfactants into sodium montmorillonite Synthesis of gold nanoparticles by reduction of HAuCl 4 under UV irradiation UV-light mediated green synthesis of silver and gold nanoparticles using Cornelian cherry fruit extract and their comparative effects in experimental inflammation Green Method for Synthesis of Gold Nanoparticles Using Polyscias scutellaria Leaf Extract under UV Light and Their Catalytic Activity to Reduce Methylene Blue Synthesis of gold nanoparticles using ethonolic leaf extract of Bacopa monnieri and UV irradiation Completely "Green" Synthesis and Stabilization of Metal Nanoparticles Effects of ultraviolet light on silver nanoparticle mobility and dissolution Synthesis of PMA stabilized silver nanoparticles by chemical reduction process under a two-step UV irradiation DNA-Templated Photoinduced Silver Deposition The Effect of pH on the Size of Silver Nanoparticles Obtained in the Reduction Reaction with Citric and Malic Acids Two phase photochemical synthesis of silver nanoparticles and their impact on the chlorophylls Photo-irradiation induced green synthesis of highly stable silver nanoparticles using durian rind biomass: Effects of light intensity, exposure time and pH on silver nanoparticles formation Effects of pH, Electrolyte, Humic Acid, and Light Exposure on the Long-Term Fate of Silver Nanoparticles Citrate-silver nanoparticles and their impact on some environmental beneficial fungi Aljarrah, K. pH effect on the aggregation of silver nanoparticles synthesized by chemical reduction Synthesis of Silver Nanoparticles Using the UV-Irradiation Technique in an Antibacterial Application Silver nanoparticles synthesized by UV-irradiation method using chloramine T as modifier: Structure, formation mechanism and catalytic activity Preparation of silver nanoparticles in inorganic clay suspensions Laser assisted synthesis of anisotropic metal nanocrystals and strong light-matter coupling in decahedral bimetallic nanocrystals Flash light synthesis of noble metal nanoparticles for electrochemical applications: Silver, gold, and their alloys In situ photochemical generation of silver and gold nanoparticles on chitosan Photochemical synthesis of bimetallic and anisotropic Au-containing nanoparticles using a one-step protocol Photochemical formation of silver and gold nanostructures at the air-water interface and their electrocatalytic properties Laser-induced photochemical synthesis of branched Ag@Au bimetallic nanodendrites as a prominent substrate for surface-enhanced Raman scattering spectroscopy Photochemical synthesis of bimetallic gold/silver nanoparticles in polymer matrix with tunable absorption properties: Superior photocatalytic activity for degradation of methylene blue Facile Photochemical Syntheses of Conjoined Nanotwin Gold-Silver Particles within a Biologically-Benign Chitosan Polymer Photochemical synthesis of biopolymer coated Au core -Ag shell type bimetallic nanoparticles Photochemical Strategies for the Seed-Mediated Growth of Gold and Gold-Silver Nanoparticles Seed Mediated Formation of Bimetallic Nanoparticles by UV Irradiation: A Photochemical Approach for the Preparation of Keggin Ions as UV-Switchable Reducing Agents in the Synthesis of Au Core−Ag Shell Nanoparticles Synthesis and characterization of core-shell bimetallic nanoparticles for synergistic antimicrobial effect studies in combination with doxycycline on burn specific pathogens Alginate Gel-Mediated Photochemical Growth of Mono-and Bimetallic Gold and Silver Nanoclusters and Their Application to Surface-Enhanced Raman Scattering Synthesis of hollow bimetal particles based on silver and gold Chemical and photochemical formation of gold nanoparticles supported on viologen-functionalized SBA-Colloid Surf A Photocatalysis on supported gold and silver nanoparticles under ultraviolet and visible light irradiation Visible light photocatalysis as a greener approach to photochemical synthesis Size-controlled preparation of polyelectrolyte-protected gold nanoparticles by natural sunlight radiation Direct sunlight enabled photo-biochemical synthesis of silver nanoparticles and their Bactericidal Efficacy: Photon energy as key for size and distribution control Sun light mediated synthesis of gold nanoparticles as carrier for 6-mercaptopurine: Preparation, characterization and toxicity studies in zebrafish embryo model Green synthesis of silver nanoparticles using sunlight Micrometer-sized gold nanoplates: Starchmediated photochemical reduction synthesis and possibility of application to tip-enhanced Raman scattering (TERS) Sunlight-driven synthesis of anisotropic silver nanoparticles Sunlight-Driven Synthesis of Silver Nanoparticles Using Pomelo Peel Extract and Antibacterial Testing Sunlight-assisted synthesis of colloidal silver nanoparticles using chitosan as reducing agent Enhanced catalytic reduction of 4-nitrophenol and congo red dye by silver nanoparticles prepared from Azadirachta indica leaf extract under direct sunlight exposure Comparative studies of sunlight mediated green synthesis of silver nanoparaticles from Azadirachta indica leaf extract and its antibacterial effect on Xanthomonas oryzae pv. oryzae. Arab Biosynthesis of Inorganic Nanoparticles: A Fresh Look at the Control of Shape, Size and Composition Piper longum catkin extract mediated synthesis of Ag, Cu, and Ni nanoparticles and their applications as biological and environmental remediation agents Green synthesis of silver nanoparticles using Piper longum catkin extract irradiated by sunlight: Antibacterial and catalytic activity Synthesis, optimization and characterization of silver nanoparticles using the catkin extract of Piper longum for bactericidal effect against food-borne pathogens via conventional and mathematical approaches Green synthesis of silver nanoparticles using Carica Papaya fruit extract under sunlight irradiation and their colorimetric detection of mercury ions Synthesis of silver nanoparticles by solar irradiation of cell-free Bacillus amyloliquefaciens extracts and AgNO 3 A simple method to synthesize triangular silver nanoparticles by light irradiation Fast and simple synthesis of triangular silver nanoparticles under the assistance of light Individual and Combined Effects of Extracellular Polymeric Substances and Whole Cell Components of Chlamydomonas reinhardtii on Silver Nanoparticle Synthesis and Stability Recycling and adaptation of Klebsormidium flaccidum microalgae for the sustained production of gold nanoparticles A global approach of the mechanism involved in the biosynthesis of gold colloids using micro-algae Improvement of kinetics, yield, and colloidal stability of biogenic gold nanoparticles using living cells of Euglena gracilis microalga Screening of cyanobacteria and microalgae for their ability to synthesize silver nanoparticles with antibacterial activity Photosynthetic Electron Transport System Promotes Synthesis of Au-Nanoparticles Light Mediated Generation of Silver Nanoparticles by Spinach Thylakoids/Chloroplasts Sunlight mediated green synthesis of silver nanoparticles using Polygonatum graminifolium leaf extract and their antibacterial activity. Mater Sunlight-driven phytochemical synthesis of silver nanoparticles using aqueous extract of Albizia lebbeck (L.) Sunlight-mediated green synthesis of silver nanoparticles using Sida retusa leaf extract and assessment of its antimicrobial and catalytic activities Sunlight induced biosynthesis of silver nanoparticle from the bark extract of Amentotaxus assamica D.K. Ferguson and its antibacterial activity against Escherichia coli and Staphylococcus aureus Gold Nanoparticles for the Delivery of Cancer Therapeutics Therapeutic Nanoparticles and Their Targeted Delivery Applications Photochemically prepared monodisperse gold nanoparticles as doxorubicin carrier and its cytotoxicity on leukemia cancer cells Preparation and Characterization of Inulin Coated Gold Nanoparticles for Selective Delivery of Doxorubicin to Breast Cancer Cells Chitosan/silver nanocomposites: Synergistic antibacterial action of silver nanoparticles and silver ions Mesoporous silica supported orderly-spaced gold nanoparticles SERS-based sensor for pesticides detection in food Detection of Permethrin pesticide using silver nano-dendrites SERS on optical fibre fabricated by laser-assisted photochemical method Photochemical synthesis of ZnO@Au nanorods as an advanced reusable SERS substrate for ultrasensitive detection of light-resistant organic pollutant in wastewater Thickness-dependent SERS activities of gold nanosheets controllably synthesized via photochemical reduction in lamellar liquid crystals Gold-Nanorod-Based Sensing of Sequence Specific HIV-1 Virus DNA by Using Hyper-Rayleigh Scattering Spectroscopy Biomedical Science to Tackle the COVID-19 Pandemic: Current Status and Future Perspectives Colorimetric biosensing of pathogens using gold nanoparticles Dissecting the Effect of Salt for More Sensitive Label-Free Colorimetric Detection of DNA Using Gold Nanoparticles Colorimetric detection based on gold nano particles (GNPs): An easy, fast, inexpensive, low-cost and short time method in detection of analytes (protein, DNA, and ion) Optical Aggregation of Gold Nanoparticles for SERS Detection of Proteins and Toxins in Liquid Environment: Towards Ultrasensitive and Selective Detection Photochemical Synthesis of Shape-Controlled Nanostructured Gold on Zinc Oxide Nanorods as Photocatalytically Renewable Sensors In-situ photochemical synthesis of Au nanoparticles in polymer matrix with one-component thioxanthone disulfide for detection of benzene, toluene and xylene vapours Photochemical synthesis of glutathione-stabilized silver nanoclusters for fluorometric determination of hydrogen peroxide Green synthesis of silver nanoparticle for the selective and sensitive colorimetric detection of mercury (II) ion Funding: This research received no external funding. Informed Consent Statement: Not applicable. The authors declare no conflict of interest.Sample Availability: Not applicable.